Patent Application
20130273392
An embodiment of the present invention relates to a hot-dip galvanized high strength steel sheet having improved formability and a manufacturing method thereof. The hot-dip galvanized high strength steel sheet also includes a galvanneald high strength steel sheet.
Priority is claimed on Japanese Patent Application No. 2010-281690, filed Dec. 17, 2010, the content of which is incorporated herein by reference.
The strength increase (high tension) of a steel sheet used is one of the most effective methods to achieve both weight saving and a collision safety for a vehicle body. Recently, a regulation regarding the collision safety represented by Euro-N-CAP has been stricter. In order to correspond to the regulation, addition of a stiffened member or the like is required, and thus, an increase in body weight is unavoidable. The increase in body weight results in a decrease in fuel efficiency. Accordingly, the increase in a utilization of an ultra-high strength material, in which a thickness is capable of being thinned while a strength of a part is maintained, has been more preferable. On the other hand, in order to achieve the weight saving of the part as much as possible, a shape of the part becomes complicated. Thereby, further improvement of forming workability is required in the steel sheet. Particularly, in most cases, a high strength thin steel sheet is applied to a portion, in which bending deformation is mainly performed, such as a side sill. Accordingly, it is important to estimate a hole expansibility which is an index indicating a bendability or local ductility as formability of the high strength thin steel sheet. Moreover, since corrosion resistance is also required in the member, a hot-dip galvanizing or a galvannealing is applied to the high strength steel sheet used.
However, in general, if the strength of the steel sheet is increased, it is known that the forming workability such as the bendability or the hole expansibility is deteriorated.
For example, in the related art, steel sheets having improved the hole expansibility are suggested in Patent Documents 1 to 3.
Since the high strength steel sheet has much content of an alloying element and the alloying element is concentrated in a center portion of a sheet thickness, the hole expansibility is deteriorated. However, there is no related art which discloses a hardness difference between a surface portion of the steel sheet and a center portion of the steel sheet. Moreover, since a MnS having a large size becomes a fracture origin at the time of molding, it is assumed that a precipitation state of the MnS influences formability. However, there is no related art which discloses the precipitation state of the MnS.
An object of an embodiment of the present invention is to solve the problems of the related art as described above, and to provide a hot-dip galvanized steel sheet having high strength and improved formability and a manufacturing method thereof.
The inventors eagerly reviewed a hot-dip galvanized high strength steel sheet having improved formability.
As a result, with respect to a steel sheet which is a DP (Dual Phase) steel having relatively low yield stress in high strength steel sheets and becomes a substrate of a hot-dip galvanized steel sheet, by controlling a total amount of a Si and a Al, which are components of the steel sheet, to a specific range and by controlling a hardness distribution of the steel sheet, the inventors found that a hot-dip galvanized high strength steel sheet is capable of obtaining more formability than the related art could be industrially manufactured.
In order to prevent problems such as a delayed fracture or secondary working embrittlement, it is preferable that the steel sheet be a DP steel which substantially does not include a residual austenite except for the residual austenite of approximately 5% by volume which is inevitably included.
Moreover, in the surface portion of the steel sheet and the center portion of the steel sheet, it is important to control the hardness of the martensite or the precipitation state of the MnS in the steel sheet.
The aspect of the present invention may be applied to a hot-dip galvanized high strength steel sheet having a tensile strength of 590 MPa to 1500 MPa. However, remarkable effects are exerted on the hot-dip galvanized high strength steel sheet having the tensile strength of approximately 980 MPa.
The gist of the present invention is as follows.
(1) According to an embodiment of the present invention, there is provided a hot-dip galvanized steel sheet including: a steel sheet; and a hot-dip galvanized layer arranged on the steel sheet, wherein a component of the steel sheet includes, by mass %, C: 0.05% to 0.13%, Si: 0.2% to 0.8%, Mn: 1.5% to 3.1%, P: 0.001% to 0.06%, S: 0.001% to 0.01%, N: 0.0005% to 0.01%, and Al: 0.1% to 0.7%, wherein the balance consisting of Fe and unavoidable impurities, wherein a Si content and an Al content by mass % satisfy the following Equation A, wherein a metallographic structure of the steel sheet includes a ferrite and a martensite, and wherein the metallographic structure satisfies the following Equation B when the number of a MnS per 0.1 mm2 on a surface portion of the steel sheet which is a region of ⅛ to 2/8 in a sheet thickness direction is n1, an average equivalent circle diameter of the MnS on the surface portion of the steel sheet is a hardness of the martensite of the surface portion of the steel sheet is H1 GPa, the number of the MnS per 0.1 mm2 on a center portion of the steel sheet which is a region of ⅜ to ⅝ in the sheet thickness direction is n2, an average equivalent circle diameter of the MnS on the center portion of the steel sheet is d2 μm, and the hardness of the martensite in the center portion of the steel sheet is H2 GPa.
0.5<Si+Al<1.0 (Equation A)
{(n2)2/3×d2}/{(n1)2/3×d1}×ln(H2/H1)<0.3 (Equation B)
(2) In the hot-dip galvanized steel sheet according to (1), the component of the steel sheet may further include by mass % at least one of B: 0.0005% to 0.002%, Mo: 0.01% to 0.5%, Cr: 0.01% to 0.5%, V: 0.001% to 0.1%, Ti: 0.001% to 0.1%, Nb: 0.001% to 0.05%, Ca: 0.0005% to 0.005%, and Rare Earth Metal: 0.0005 to 0.005%.
(3) In the hot-dip galvanized steel sheet according to (2), the steel sheet may be a cold rolled steel sheet.
(4) In the hot-dip galvanized steel sheet according to (1), the steel sheet may be a cold rolled steel sheet.
(5) In a manufacturing method of the hot-dip galvanized steel sheet according to any one of (1) to (4), when a total number of stands in a hot finish rolling is n stage and ri% is a rolling reduction of the ith stand, the hot finish rolling may satisfy the following Equation C.
(r1+r2+r3)/(rn-2+rn-1+rn)>1.6 (Equation C)
According to the hot-dip galvanized steel sheet related to the aspect of the present invention and the manufacturing method thereof, by controlling a total amount of the Si and the Al which are components of the steel sheet, to a specific range, and further by controlling the hardness of the martensite and the precipitation state of the MnS of the steel sheet in the steel sheet which becomes a substrate of the hot-dip galvanized steel sheet, a hot-dip galvanized steel sheet having the high strength and improved formability and a manufacturing method thereof is capable of being provided.
A hot-dip galvanized steel sheet according to an embodiment of the present invention includes a steel sheet which becomes a substrate and a hot-dip galvanized layer arranged on the steel sheet. Here, the hot-dip galvanizing also includes a galvannealing.
First, a numerical limit range regarding the base elements of the steel sheet which becomes a substrate and the reasons for the limit will be described. Here, the described % is mass %.
C: 0.05% to 0.13%
C (carbon) is an essential element in order to secure a strength and stabilize a martensite.
When the C content is less than 0.05%, the strength is not satisfied, and the martensite is not formed. Moreover, when the C content exceeds 0.13%, a hardness of the martensite becomes too high, a hardness difference between a soft phase and the martensite becomes too large, and thus, a hole expansibility is decreased, and the weldability is deteriorated.
Therefore, the C content is 0.05% to 0.13%, and is preferably 0.06% to 0.1%.
Si: 0.2% to 0.8%
Si (silicon) is an element which is added in order to secure the strength and a ductility.
When the Si content exceeds 0.8%, a phosphatability or a galvanizability is deteriorated. Accordingly, the Si content is set to 0.8% or less. Moreover, when the galvanizability is emphasized, the Si content is preferably 0.6% or less. Furthermore, the hole expansibility is improved due to multiple addition of Si and Al. However, when the Si content is less than 0.2%, the effect does not remarkably appear. Therefore, a lower limit of the Si content is 0.2%.
Mn: 1.5% to 3.1%
Mn (manganese) is an element which delays a generation of a carbide and stabilizes a ferrite in addition to securing the strength.
When the Mn content is less than 1.5%, strength is not satisfied, a formation of the ferrite is insufficient, and thus, the ductility is deteriorated. Moreover, when the Mn content exceeds 3.1%, the hardenability is increased more than necessary, and thus, the product quality is not stabilized. Furthermore, the ductility is also deficient.
Accordingly, the Mn content is 1.5% to 3.1%, and is preferably 1.8% to 2.8%.
P: 0.001% to 0.06%
P (phosphorus) is added as an element which increases the strength of the steel sheet, if necessary. However, if the additional amount of P is increased, an intergranular segregation occurs, and thus, local ductility and the weldability is deteriorated.
Accordingly, an upper limit of the P content is 0.06%. Moreover, a lower limit of the P content is 0.001%, the reason is because costs are increased on steel making process, if the P content is less than 0.001%. Preferably, the P content is 0.003% to 0.03%.
Al: 0.1% to 0.7%
Al (aluminum) is an element which promotes the generation of the ferrite and effectively acts on improvement of the ductility. In addition, Al is an element which does not deteriorate the phosphatability or the galvanizability, even if the additional amount of Al is large.
In order to improve the hole expansibility by a multiple addition of Si and Al, the Al content is 0.1% or more. However, if the additional amount of Al is increased, and causes the increase of inclusions such as an alumina, accordingly, the workability is deteriorated. Therefore, an upper limit of the Al content is 0.7%. Preferably, the upper limit is 0.15% to 0.6%.
In addition to the above-described base elements, the steel sheet may further include at least one of B, Mo, Cr, V, Ti, Nb, Ca, and Rare Earth Metal (REM) as selective elements. Hereinafter, the numerical limit ranges of the selective elements and the reasons for the limit will be described. Here, the described % is mass %.
B: 0.0005% to 0.002%
B (boron) may be added in order to secure the hardenability and increase effective Al due to a formation of BN. Moreover, the fraction of ferrite of DP steel is increased, and thus, a high elongation is capable of being secured. However, the metallographic structure is a laminated structure, and thus, the local ductility may be decreased. Due to addition of B, an aforementioned phenomenon is capable being prevented.
When the B content is less than 0.0005%, the effects are not exerted. When the B content exceeds 0.002%, the effects corresponding to the added amount are not exhibited.
Mo: 0.01% to 0.5%
Cr: 0.01% to 0.5%
Mo (molybdenum) and Cr (chromium) may be added so as to secure the strength and the hardenability.
When the Mo content and the Cr content are less than 0.01%, the effects are not exerted. When the Mo content and the Cr content exceed 0.5%, a ferrite generation is suppressed in the DP steel, and thus, the ductility is deteriorated. Moreover, the phosphatability or the galvanizability is deteriorated.
V: 0.001% to 0.1%
Ti: 0.001% to 0.1%
V (vanadium) and Ti (titanium) may be added so as to secure the strength.
When the V content and the Ti content are less than 0.001%, the effects are not exerted. When the V content and the Ti content exceed 0.1%, the weldability or the like is deteriorated.
Nb: 0.001% to 0.05%
Nb (niobium) may be added so as to secure the strength.
When the Nb content is less than 0.001%, the effects are not exerted. When the Nb content exceeds 0.05%, the effects are saturated.
Ca: 0.0005% to 0.005%
REM: 0.0005% to 0.005%
Ca (calcium) and REM may be added to suppress the generation of inclusions and to improve the hole expansibility.
When the Ca content and the REM content are less than 0.0005%, the effects are not exerted. When the Ca content and the REM content exceed 0.005%, the effects are saturated.
In addition to the elements, the steel sheet includes unavoidable impurities. Here, the unavoidable impurities show an auxiliary raw material such as steel scrap or elements such as S, N, Mg, Pb, Sb, Sn, Cd, Ni, or Cu which is inevitably mixed in a plating process.
For example, even when Sn or the like is included within a range of 0.01% or less, the effects of the present invention are not reduced. However, in order to sufficiently exert the effects of the present invention, it is preferable that the S content and the N content be limited as follows. Here, the described % is mass %.
S: 0.001% to 0.01%
S (Sulfur) is an element that unwelcomes to exist in the steel. S generates MnS, and thus, the local ductility and the weldability are deteriorated by it.
Accordingly, an upper limit of the S content is limited to 0.01%. Moreover, since costs in the steel making process are increased, if S is decreased in an unnecessary manner. Thus, a lower limit of the S content is 0.001%. Preferably, the S content is 0.002% to 0.005%.
N: 0.0005% to 0.01%
N (nitrogen) is an element which is inevitably included. However, if too much N is included, not only aging properties are deteriorated but also an amount of an MN precipitation is increased, and thus, the effects of Al addition are decreased.
Accordingly, an upper limit of the N content is limited to 0.01% or less. Moreover, if the N content is decreased in an unnecessary manner, since costs in the steel making process are increased, a lower limit of the N content is 0.0005% or more. Preferably, the N content is 0.001% to 0.005%.
Next, the numerical limit range regarding the total content of Si and Al will be described.
In order to increase the strength of the steel sheet, utilizations of only solid solution hardening or precipitation strengthening is insufficient, generally, in many cases, transformation strengthening is also used. Furthermore, since the controlling of a DP structure making, high elongation is obtained due to a soft ferrite phase, and the strength is secured due to a hard martensite phase.
However, in a case of the DP steel, if a hardness difference between the soft phase and the hard phase is increased, it is known that the hole expansibility is deteriorated. In order to improve this, there is a method which produces the decrease in hardness by tempering the martensite. However, the method is not sufficient enough. Particularly, in the DP steel which requires the tensile strength of 980 MPa or more, the strength may be deficient due to the tempering.
Thus, the inventors eagerly reviewed, and as a result, found that a steel sheet which has high strength and improved hole expansibility is obtained when the total amount of Si and Al by mass % satisfies the following Equation A.
0.5<Si+Al<1.0 (Equation A)
In evaluation of the strength and the formability, a value of λ×TS, which is the product of a hole expansion ratio: λ(%) and the tensile strength: TS (MPa), is used. Generally, the value is approximately 40,000% MPa. When the value of λ×TS is 60,000% MPa or more, it determined that the steel sheet has the high strength and improved formability.
Next, the metallographic structure of the steel sheet, which becomes a substrate of the hot-dip galvanized steel sheet according to the embodiment of the present invention, will be described.
In the metallographic structure of the steel sheet, the ferrite and the martensite are mainly included. This is because the steel sheet has improved balance between the strength and the ductility. Here, the ferrite includes a polygonal ferrite and a bainitic ferrite, and the martensite also includes a martensite obtained by performing tempering at a temperature of 600° C. or less in addition to a martensite obtained by general quenching. Even when the steel sheet subjected to tempering at the temperature of 600° C. or less is used as the substrate of the hot-dip galvanized steel sheet, the effects of the present invention are not changed.
The fraction of ferrite and the fraction of martensite are controlled according to the strength of the steel sheet. When TS is 500 MPa to 800 MPa, it is preferable that the fraction of the ferrite be 50 area % to 90 area % and the fraction of the martensite be 10 area % to 40 area %. When TS is 800 MPa to 1100 MPa, it is preferable that the fraction of the ferrite be 20 area % to 60 area % and the fraction of the martensite be 30 area % to 60 area %. When TS exceeds 1100 MPa, it is preferable that the fraction of the ferrite be 30 area % or less and the fraction of the martensite be 40 area % or more.
The steel sheet includes a bainite as the structure in addition to the ferrite and the marteniste. It is preferable that the fraction of bainite be 10 area % to 40 area %. Moreover, if an austenite remains in the structure, secondary working embrittlement or delayed fracture characteristics are deteriorated. Accordingly, it is preferable that residual austenite be not substantially included in the steel sheet except for residual austenite of approximately 5 volume % which inevitably exists.
In order to obtain high strength and sufficient hole expansibility (formability) in the steel sheet, the condition of the metallographic structure is needed to satisfy the following Equation B.
{(n2)2/3×d1}/(n1)2/3×d1}×ln(H2/H1)<0.3 (Equation B)
Here, the number of a MnS per 0.1 mm2 on a surface portion of the steel sheet which is a region of ⅛ to 2/8 in a sheet thickness direction is n1, an average equivalent circle diameter of the MnS is d1 (μm) and a hardness of the martensite of the surface portion of the steel sheet is H1 (GPa). Similarly, the number of the MnS per 0.1 mm2 on a center portion of the steel sheet which is a region of ⅜ to ⅝ in the sheet thickness direction is n2, the average equivalent circle diameter of the MnS is d2 (μm), and the hardness of the martensite in the center portion of the steel sheet is H2 (GPa).
The left side of the Equation B being less than 0.3 shows that the difference of the numbers of the MnS, the difference of the average equivalent circle diameters of the MnS, and the difference of martensite hardness in the surface portion of the steel sheet and the center portion of the steel sheet are qualitatively small. Generally, the values of the number of the MnS, the average equivalent circle diameter of the MnS, and the martensite hardness in the center portion of the steel sheet are larger than those in the surface portion of the steel sheet, and thus, the left side of the Equation B becomes 0.3 or more.
As shown in
The hardness of the martensite and the precipitation state of the MnS in the steel sheet are capable of being controlled by a manufacturing method described below. Furthermore, in order to more precisely control the hardness of the martensite and the precipitation state of the MnS in the steel sheet, it is preferable that the steel sheet be a cold rolled steel sheet in which cold rolling is also performed after hot rolling.
Moreover, if a value of EL×TS, which is the product of the elongation (EL) and TS, is 16,000% M Pa or more, since the formability is further improved, it is preferable that the value be 16,000% MPa or more.
As described above, by controlling the component and the metallographic structure of the steel sheet in the steel sheet which becomes the substrate of the hot-dip galvanized steel sheet, the hot-dip galvanized high strength steel sheet having high strength and improved formability are capable of being obtained.
Next, a manufacturing method of the hot-dip galvanized steel sheet according to the embodiment of the present invention will be described.
The manufacturing method may be performed by processes of a hot rolled steel sheet, a cold rolled steel sheet, and a plating steel sheet which are performed generally.
In a casting process, steel products are manufactured by casting of molten steel which satisfies the base elements, the selective elements, and the unavoidable impurities described above. The casting method is not particularly limited, and a vacuum casting method, a continuous casting method, or the like may be used.
In the hot rolling process, the hot rolling is performed by heating the steel products. In order to prevent a decrease of the workability due to apply of a strain to ferrite grains excessively, a finish rolling in the hot rolling is preferably performed at temperature of Ar3 (the temperature in which ferrite transformation starts at the time of cooling) or more. Moreover, since a recrystallized grain diameter after annealing coarsens more than necessary at too high temperature, the finish rolling in the hot rolling is preferably performed at a temperature of 940° C. or less.
At the time of the finish rolling in the hot rolling, when a rolling reduction at each stand satisfies a following Equation C, a high value of λ×TS is obtained.
(r1+r2+r3)/(rn-2+rn-1+rn)>1.6 (Equation C)
Here, the number of a total stands of the hot finish rolling is n stage and ri% is the rolling reduction of the ith stand.
As shown in
In order to securely obtain high strength and improved formability, it is preferable that (r1+r2+r3)/(rn-2+rn-1+rn)>1.9 be satisfied. Moreover, it is more preferable that (r1+r2+r3)/(rn-2+rn-1+rn)>2.0 be satisfied. On the other hand, due to limitations of a plant capacity, an upper limit of the value of (r1+r2+r3)/(rn-2+rn-1+rn) becomes 3.0.
Moreover, as shown in
Furthermore, if the value of EL×TS of the steel sheet is 16,000% MPa or more, since the hot-dip galvanized steel sheet is capable of being applied to an automotive members or the like in which strict workability is required, it is more preferable that the value of EL×TS be 16,000% MPa or more.
As a winding temperature of the steel sheet after the hot rolling is increased, recrystallization or grain growth is promoted, and the workability may be improved. However, as the winding temperature is increased, scales are generated, a pickling property is decreased. So, a ferrite and a pearlite are generated in layers, and thus, C is non-uniformly segregated. Accordingly, the winding temperature is set to 650° C. or less. On the other hand, if the winding temperature is too low, the steel sheet is hardened, and thus, a load at the time of cold rolling becomes high. Therefore, the winding temperature is set to 400° C. or more. Moreover, if necessary, the steel sheet after the hot rolling may be maintained at the winding temperature within a range of 1 hour or more and 24 hours or less. The steel sheet is maintained during the time, and thus, the metallographic structure of the hot rolling steel sheet is capable of being appropriately controlled.
If necessary, in a grinding process, in order to remove scales, surface grinding may be performed to the steel sheet after the hot rolling process. The grinding method is not particularly limited, and for example, a wire brush roll, an abrasive belt, a shot blasting, or the like may be used.
In a pickling process, the steel sheet after the hot rolling process or after the grinding process is pickled. The pickling method is not particularly limited, and an established pickling method which uses sulfuric acid, nitric acid, or the like may be used.
In a cold rolling process, the steel sheet after the pickling process is cold-rolled. The cold rolling method is not particularly limited. In the cold rolling, since shape correction of the steel sheet is difficult if the rolling reduction is low, the lower limit of the rolling reduction is preferably 30%. Moreover, if the rolling is performed at the rolling reduction exceeding 70%, due to an occurrence of cracks in an edge portion of the steel sheet and a deformation in the shape, the upper limit of the rolling reduction is preferably 70%.
In the cold rolled steel sheet which is manufactured through the hot rolling process and the cold rolling process described above, the hardness of the martensite and the precipitation state of the MnS in the steel sheet is more precisely controlled. Accordingly, the steel sheet is preferably used as the substrate of the hot-dip galvanized steel sheet.
In an annealing process, the steel sheet after the cold rolling process is annealed at the temperature of Ac1 (a temperature in which an austenite starts to be generated at the time of heating) or more and Ac3 (a temperature in which transformation from a ferrite to an austenite is completed at the time of heating)+100° C. or less. At the temperature less than Ac1, the structure is nonuniform. On the other hand, at the temperature exceeding Ac3+100° C., ferrite generation is suppressed due to coarsening of the austenite, and elongation characteristics are deteriorated. Moreover, from an economical aspect, the annealing temperature is preferably 900° C. or less. Moreover, during the annealing process, in order to make layered structures disappear, the steel sheet is needed to be maintained for more than 30 seconds. However, even when the steel sheet is maintained more than 30 minutes, the effects are saturated, and thus, the productivity is decreased. Accordingly, the maintaining duration is set to 30 seconds or more and 30 minutes or less.
In a cooling process, the steel sheet, which is heated within the temperature range in the annealing process, is cooled. A cooling end temperature is set to 600° C. or less. If the cooling end temperature exceeds 600° C., the austenite easily remains, problems about the secondary workability and the delayed fracture may easily occur. Furthermore, if necessary, at the cooling end temperature, the steel sheet after the annealing process may be maintained within a range of 10 seconds or more and 1000 seconds or less. According to the maintenance for the time, the metallographic structure of the steel sheet after the annealing process is capable of being appropriately controlled.
Moreover, in order to improve the hole expansibility and the brittleness, tempering treatment may be performed to the steel sheet at temperature of 600° C. or less after the cooling process, if necessary. Even when the tempering treatment is performed, effects of the present invention are not changed.
In a plating process, hot-dip galvanizing is performed to the steel sheet after the cooling process or the tempering treatment. A hot-dip galvanizing method is not particularly limited. Moreover, if necessary, an alloying treatment is performed, and thus, a galvannealing may be used.
Steel having the component composition shown in Table 1 was casted in a vacuum melting furnace. In Table 1, underlined numerical values indicate values outside the range of the present invention. The steel products were heated to 1200° C. and the hot rolling was performed. The finish rolling in the hot rolling was performed at 880° C. Moreover, in the hot finish rolling, the rolling reduction was controlled at each stand. After the hot finish rolling ends, the rolling steel sheet was cooled to 500° C. and was maintained for 1 hour at the temperature, and the winding heat treatment of the hot rolling was performed. The surface scales of the obtained hot rolled steel sheet were removed by grinding and pickling. Thereafter, the cold rolling was performed to the steel sheet. Annealing was performed to the steel sheet after the cold rolling for 60 seconds at 800° C. by using a continuous annealing simulator. Thereafter, the steel sheet was cooled at a temperature range of 400° C. to 600° C. and maintained for 10 seconds to 600 seconds at the temperature. Hot-dip galvanizing was performed to the steel sheet, and if necessary, some of the steel sheets were cooled down to a room temperature after being treated by the alloying treatment.
A tensile test and a hole expansion test were performed using the hot-dip galvanized steel sheet manufactured described above. When the product of the hole expansion ratio λ(%)×the tensile strength TS (MPa) was 60,000% MPa or more, it was determined that the steel sheet had high strength and improved formability. The tensile test was performed by JIS No. 5 specimen. The hole expansion test is performed by pushing a conical punch having a tip angle of 60° into a punched hole which is provided on the specimen and has an initial hole diameter d0: 10 (mm), and by expanding the punching hole. Moreover, the hole diameter d (mm) was measured at the time when cracks generated at a circumference of the punched hole penetrate in a sheet thickness direction of the specimen, and the hole expansion ratio λ was obtained by a following Equation D.
λ=[(d−d0)/d0]×100(%) (Equation D)
Here, d0=10 mm.
The metallographic structure of the hot-dip galvanized steel sheet manufactured as described above was observed by an optical microscope. An observed surface was a cutting section which was cut into a plane face along the sheet thickness direction so that a sheet width direction perpendicular to the rolling direction of the hot-dip galvanized steel sheet was the observed surface. The Ferrite was observed by NITAL etching and the martensite was observed by Le Pera etching method. A position of ¼ of the thickness of the steel sheet, which was positioned at the steel sheet side from an interface which was shown on the cutting section and was between the steel sheet and the hot-dip galvanized layer, was observed, and area fractions of the ferrite and the martensite were obtained. After the surface of the hot-dip galvanized steel sheet was ground in a parallel manner to the depth which was ¼ of the sheet thickness of the steel sheet, a polished surface was measured by an X-ray diffractometer, and thus, the volume faction of the austenite was obtained.
A galvanizing property was estimated by performing hot-dip galvanizing to the rolling steel sheet, which was subjected to annealing under the annealing conditions similar to the above-described conditions, using a hot-dip galvanizing simulator, and by visually confirming an attachment situation of the plating. A case where the plated surface was 90 area % or more and the galvanizing was uniformly attached was represented by “Good”, and a case where the plated surface was more than 10 area % and defects existed was represented by “Bad”. The results are shown in Table 2.
An observation of the precipitation state of MnS was performed by using a Field Emission-Scanning Electron Microscope (Fe-SEM). The observation was performed at the surface portion of the steel sheet which was ⅛ to 2/8 in the sheet thickness direction of the steel sheet from the interface, which was shown on the cutting section and between the steel sheet and the hot-dip galvanized layer, to the steel sheet side, and at the center portion of the steel sheet which was ⅜ to ⅝ in the sheet thickness direction of the steel sheet. A Magnification of the observation was set to 1,000 times, and an area of 0.12 mm×0.09 mm=0.01 mm2 was set to one observation visual filed. A total of 10 visual fields were observed, and the number of the MnS was measured. Here, a total of 10 visual fields for every area of 0.01 mm2 were observed, the total number was measured, and thus, the number of the MnS was represented by the number per 0.1 mm2. An equivalent circle diameter (μm) of the MnS was calculated by an image analysis software in which the equivalent circle diameters in the 10 visual fields were incorporated into the Fe-SEM, the average value in the 10 visual field was obtained, and thus, the average value was set to the average equivalent circle diameter (μm).
The hardness of the martensite was measured using a nanoindenter. Grains of the martensite, which existed on the surface portion of the steel sheet and the center portion of the steel sheet, were measured at total 30 points with intervals of 100 μm, and the average value was obtained. The results were shown in Table 3. In Table 3, underlined numerical values indicate values outside the range of the present invention.
As shown in Tables 1 to 3, No. 1 to 27, which are Examples, are hot-dip galvanized steel sheets which have improved the galvanizability, the high strength, and sufficient hole expansibility (formability).
On the other hand, Nos. 28 to 45, which are Comparative Examples, are hot-dip galvanized steel sheets outside the range of the present invention.
In Comparative Examples 28 and 29, since the C content is outside the range of the present invention, the value of λ×TS becomes less than 60,000% MPa.
In Comparative Example 30, since the Si content is outside the range of the present invention, the value of Si+Al by mass % also is outside the range of the present invention, and thus, the value of λ×TS becomes less than 60,000% MPa, and the galvanizing property is also not good.
In Comparative Example 31, since the Si content and the Mn content are outside the range of the present invention and the value of Si+Al by mass % also is outside the range of the present invention, the value of λ×TS becomes less than 60,000% MPa, and galvanizing property is also not good.
In Comparative Example 32, since the Mn content is outside the range of the present invention, the value of λ×TS becomes less than 60,000% MPa.
In Comparative Example 33, since the P content is outside the range of the present invention, the value of λ×TS becomes less than 60,000% MPa.
In Comparative Example 34, since the S content is outside the range of the present invention, the value of λ×TS becomes less than 60,000% MPa.
In Comparative Example 35, since the N content is outside the range of the present invention, the value of λ×TS becomes less than 60,000% MPa.
In Comparative Example 36, since the Al content is outside the range of the present invention, the value of λ×TS becomes less than 60,000% MPa.
In Comparative Examples 37 to 41, since the value of Si+Al by mass % is outside the range of the present invention, the value of λ×TS becomes less than 60,000% MPa.
In Comparative Examples 42 to 45, since the Equation B and the Equation C are not satisfied, the value of λ×TS becomes less than 60,000% MPa.
0.040
0.250
1.523
1.879
1.498
1.30
2.119
3.25
0.075
0.0210
0.003
1.923
2.133
0.120
0.270
0.920
1.150
2.070
0.400
0.31
1.43
0.31
1.43
0.36
1.24
According to the hot-dip galvanized steel sheet and the manufacturing method thereof of the aspects of the present invention, in the steel sheet which becomes a substrate of the hot-dip galvanized steel sheet, by controlling a total amount of Si and Al, which are components of the steel sheet, to a specific range, and by controlling the hardness of the martensite and a precipitation state of the MnS of the steel sheet, a hot-dip galvanized steel sheet having high strength and improved formability and a manufacturing method thereof is capable of being provided.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2010-281690 | Dec 2010 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2011/079045 | 12/15/2011 | WO | 00 | 6/12/2013 |