Hot Forging Facility

Abstract

A hot forging facility enabling the manufacture of a hot forged product excellent in fatigue properties and cold workability is provided. A heating furnace for heating a steel material and a hot forging apparatus for perfonning forging of the heated steel material are sequentially arranged on a transport line. A partially cooling apparatus/apparatuses for partially cooling a forged product after hot forging is provided on an exit side of the hot forging apparatus.

Description

TECHNICAL FIELD

The present invention relates to a hot forging facility for manufacturing various hot forged products, of which typical examples includes machine structural components represented by, for example, steel-using automobile components such as suspension components including, for example, constant-velocity universal joints and hubs, and engine components such as crank-shafts.

BACKGROUND ART

According to a general practice, steel products for the use of, for example, automobile axle unit and engine components, are each manufactured in the manner that the product is hot forged, and thereafter is finished by a machining process (or, “machined and finished,” here-below). A manufacturing process for such a component is disclosed in, for example, Non-Patent Publication 1 (*1) listed below. The manufacturing process is carried out by processing steps representative of forging production processing steps. More specifically, a material is machined and heated, and thereafter, the thus-processed material is shaped or formed by a forging step, and by necessity, the formed material is heat treated.

Recently, it is increasingly demanded that products for the above-described use be improved in fatigue strength for implementation of, for example, compactness and thinning for weight reduction of automobiles using those products.

In Patent Publication 1 (*2) listed below, as a technique for increasing the fatigue strengths of hot forged products, there is disclosed a manufacturing method for a high fatigue strength hot forged product. According to the method, the entirety of a forged product is hardened or quenched after hot forging, and further, the matrix thereof is precipitation hardened by tempering processing.

Further, Patent Publication 2 (*3) listed below discloses a cooling apparatus operating such that cooling rate nonuniformity in the entirety of a forged product is eliminated, thereby to control the overall cooling rate for the product.

(*1) Non-Patent Publication 1: “Plastic Processing Technology Series 4: Forging”; The Japan Society for Technology of Plasticity, published by Corona

(*2) Patent Publication 1: Japanese Patent No. 3100492 (Publication)

(*3) Patent Publication 1: Japanese Patent No. 2936198 (Publication)

DISCLOSURE OF INVENTION

However, according to the method disclosed in Patent Publication 1, the component (product) itself is directly cooled after hot forging, such that the hardness of the entirety of the component is increased, and hence the workability of an area not requiring fatigue strength is reduced. More specifically, according to a general practice, a machine structural component for the above-described use is manufactured in the manner that the material is formed by hot forging into substantially the product shape, and thereafter, the entire surface of the hot forged product is machined and finished. As such, in the manufacture of a machine structural component of the above-described type, the machining process and surface abrading are indispensable. However, in the event that the hardness of the entirety of the component is increased, reduction in machinability inevitably poses a significant problem.

In addition, a manufacturing facility for implementing the above-described method requires a heating facility to provide separate quenching for the precipitation hardening treatment. As such, the facility is not preferable even from the viewpoint of energy saving.

Similarly, the technique described in Patent Publication 2 controls the cooling rate of the entirety of the workpiece, such that reduction in machinability poses a significant problem.

Under these circumstances, for the facility described in any one of Patent Publications 1 and 2, it is difficult to provide a hot forged product excellent in fatigue properties and cold workability. More specifically, it is difficult for the disclosed facility to provide such a hot forged product that has high fatigue strength, which is required from stress occurred in association with, for example, weight reduction and compactness of the forged product, relative to the forged product obtained from the conventional method, and that has high machinability not only for, of course, an area not requiring fatigue strength, but also for other areas when machining is performed after hot forging, thereby to making it possible to be easily finished.

Accordingly, an object of the present invention is to provide a hot forging facility enabling manufacturing of a hot forged product excellent in fatigue properties and cold workability.

In order to achieve the object, the inventors made extensive study and research, particularly, about execution of partial cooling after hot forging, and resultantly obtained knowledges (I) to (III) below.

(I) When a hardness increase rate of an area of a hot forged product reaches 10% or higher after partial cooling of a specifically fatigue-strength required area, the fatigue strength of the product as a component can be increased by 20% or higher.

(II) An area partially quenched by partial cooling is self-tempered by the quantity of holding heat of a non-cooled area. As a consequence, effectiveness equivalent to the effectiveness after the tempering process conventionally performed as the additional processing step can be obtained. In order to obtain the effectiveness, the tempering process has to be performed to satisfy a specific parameter.

(III) Consequently, the forged product does not have to be additionally tempered after being cooled to the ambient temperature, therefore making it possible to manufacture a high fatigue.strength component at low cost.

Further, in order to practical enforcement of the technique in accordance with the above-described knowledge, the inventors made extensive investigation regarding the configuration of a facility enabling manufacture on an industrial scale, and as a consequence, the inventors have developed the invention.

The present invention is based on the knowledge described above.

More specifically, essential configurations of the present invention are as follows.

(1) In a hot forging facility wherein a heating furnace for heating a steel material and a hot forging apparatus for performing forging of the heated steel material are sequentially arranged on a transport line, a partially cooling apparatus/apparatuses for partially cooling a forged product after hot forging is provided inside of and/or on an exit side of the hot forging apparatus.

(2) In a hot forging facility as described in (1), the partially cooling apparatus includes a nozzle for spraying cooling liquid towards a part of the forged product.

(3) In a hot forging facility as described in (1) or (2), at least one unit of the partially cooling apparatus is provided in a position along the transport line on an exit side of the hot forging apparatus.

(4) In a hot forging facility as described in any one of (1) to (3), a plurality of the partial cooling apparatuses are provided in positions along the transport line on an exit side of the hot forging apparatus.

According to the present invention, a facility for securely implementing the manufacture of a hot forged product excellent in fatigue properties and cold workability can be provided.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a conceptual diagram of a temperature history in heat recuperation.

FIG. 2 is a diagram showing the relationship between a parameter H and “(V₁-V₂)/V₂”.

FIG. 3 is a view showing the configuration of a hot forging facility.

FIG. 4 is a process view showing a procedure of hot forging.

FIG. 5 is a view showing a partially cooling apparatus.

REFERENCE NUMERALS

Reference numerals in FIGS. 3 to 5 are as follows:

• • 1 Heating furnace
  • 2 Steel material
  • 3 Transport line
  • 4 Hot forging apparatus
  • 5 Partially cooling apparatus
  • 20 Hot forged product
  • 20a Flange base portion
  • 20b axial end portion

BEST MODE FOR CARRYING OUT THE INVENTION

First, in order to obtain a hot forged product excellent in fatigue properties and cold workability, it is preferable that a hardened area is provided in a specifically fatigue-strength required area of a forged product by performing partial cooling after hot forging, and other areas are remained as an un-hardened area, in which a Vickers hardness V₁ of the hardened area, particularly, on a surface and a Vickers hardness V₂ of the un-hardened area satisfy an expression:

(V₁-V₂)/V₂:0.1˜0.8

More specifically, when the ratio “(V₁-V₂)/V₂” is less than 0.1, a strength increase of the hardened area is insufficient, such that sufficient strength improvement effectiveness cannot be obtained. On the other, hand, however, if the ratio “(V₁-V₂)/V₂” exceeds 0.8, then the hardness is excessively increased, thereby significantly reducing cold workability, such as machinability. Especially, since direct partial quenching is directly performed after hot forging, subsequent machining process is indispensable, so that it is recommended that the hardness ratio “(V₁-V₂)/V₂” is set to 0.8 or less. An optimal range of the ratio is from 0.2 to 0.6.

The hardened area having the hardness difference is structured from martensite and/or bainite. The un-hardened area is primarily structured from ferrite and/or pearlite, but, depending on the case, can partly be mixed with bainite.

Thus, the hot forged product is obtained through the direct partial quenching after hot forging, and then is formed into a machine structural component through a mechanical finishing process. In this case, hot forging refers to the step of performing forging by heating the material to a temperature of A_c3 or higher.

Manufacture conditions for manufacturing the hot forged product satisfying ratio “(V₁-V₂)/V₂:0.1˜0.8” will be described herebelow.

More specifically, following the general manufacturing method for components of the above-described type, the steel material is heated and fed into the hot forging apparatus. In the present case, however, it is essential that a partial cooling process is performed to cool down the forged product having been obtained as described above, from a temperature of A_c3 or higher to a temperature of Ac1-150° C. or lower at a rate of 20° C./s. More specifically, an area of the product required to have a high fatigue strength after hot forging is cooled down from a temperature of A_c3 or higher to a temperature of Ac1-150° C. or lower at a cooling rate of 20° C./s. Thereby, ferrite development or transformation during cooling can be suppressed, and the structure can be transformed to martensite and/or bainite.

Thus, partial cooling after hot forging is performed within the temperature range of from A_c3 or higher to A_c1-150° C. or lower. It is indispensable to perform cooling from A_c3 or higher in order to obtain a sufficient heat recuperation effect after cooling; and cooling is performed to A_c1-150° C. or lower is to suppress ferrite development or transformation.

The cooling rate within the temperature range is set to the cooling rate of 20° C./s in order to transform the structure into martensite and/or bainite while suppressing the ferrite transformation.

Thereafter, it is important to cause the component to be quenched by heat recuperation in accordance with the holding heat of the component within the temperature range not continually exceeding the A_C1 point. More specifically, when the quenching temperature associated with the heat recuperation exceeds the A_C1 point, the structure formed by partial quenching is retransformed into an austenite structure and is transformed into a ferrite-pearlite structure. To prevent this, it is important to cause the component to be quenched within the temperature range not exceeding the A_C1 point.

In the case of quenching using the heat recuperation, it is preferable that, during a time period from the instance of stop of cooling to the instance wherein the temperature reaches 300° C. in the stage of temperature falling after the heat recuperation, a parameter H defined by expression (1) below from an average temperature T_n(K) in units of a time period Δt_n (second) satisfy

65≦H≦85

H=log₁₀Σ10^fn  (1)

Where, f_n=logΔt_n−1.597×10⁴/T_n+100

FIG. 1 shows a temperature history in the event of heat recuperation of a partially cooled area. With reference to FIG. 1, an average temperature T_n(K) in each time period Δt_n is obtained from a cooling curve after stop of cooling, and the resultant value is adapted in expression (1), whereby the parameter H is defined. In this case, since the temperature T_n in the stage of self-tempering continually varies, the temperature is obtained by assuming Δt_n to 0.5 seconds or less.

FIG. 2 shows the relationship between the ratio “(V₁-V₂)/V₂” and the parameter H. As shown in FIG. 2, the parameter H and the hardness ratio are in a good interrelationship. When the parameter H is less than 65, the quenching effect is insufficient, the hardness ratio “(V₁-V₂)/V₂” exceeds 0.8, therefore posing the problem with the machinability. When the parameter H exceeds 85, the component is excessively softened to the extend that the ratio “(V₁-V₂)/V₂” is less than 0.1 at which fatigue strength improvement effects cannot be obtained.

As described above, in order to obtain the hot forged product excellent in fatigue properties and cold workability, partial cooling after hot forging has to be appropriately performed, preferably, in accordance with the parameter H. A hot forging facility for obtaining the product will be described in detail herebelow with reference to FIG. 3.

Referring to FIG. 3, numeral 1 represents a heating furnace for heating the steel material. A hot forging apparatus 4 is disposed on a transport line 3 of a heated steel material 2 extending toward an outlet side of the heating furnace 1. A partially cooling apparatus 5 is disposed in a position along the transport line 3 on an exit side of the hot forging apparatus 4.

In the hot forging apparatus 4, the heated steel material 2 is formed into a desired shape by die forging. For example, in the hot forging apparatus 4, through processing steps respectively shown in FIGS. 4(b) to 4(d), a steel material 2 shown in FIG. 4(a) is formed into a forged product 20 having a pre-finishing product shape.

Subsequently, a specified area of the forged product 20 is cooled in the partially cooling apparatus 5 disposed on the exit side of the hot forging apparatus 4. For example, as shown in FIG. 5, a plurality of nozzles 5a are provided towards the forged product 20 in a plurality of circumferentially equi-sectional positions of two portions, namely upper and lower portions, of the forged product 20. Cooling liquid is sprayed from the nozzles 5a towards, for example, flange base portions 20a of the forged product 20, thereby making it possible to perform localized cooling of the flange base portions 20a.

A partially cooling apparatus shown in FIG. 5 includes a turn table 6 that is used for placing the forged product 20 and that is turnable by a motor 8. The plurality of nozzles 5a are positioned and fixed to inject cooling water to the flange base portions 20a placed on the table 6. The nozzles 5a are each fluidly connected to a cooling water feed pipe 12. The cooling water feed pipe 12 is provided to include a booster pump 11 for feeding the cooling water, a flow regulation valve 10 for controlling the volume of injection, and a flowmeter 9 for monitoring the flow. Further, upper and lower cooling water partition plates 7a and 7b, respectively, are provided on upper and lower sides of the respective nozzle 5a. The respective plate is thus provided to locally cool only the flange base portions 20a of the forged product 20 and to thereby prevent other areas from being cooled. Either of the upper or lower cooling water partition plates 7a and 7b is formed from an annular partition plate to be capable of preventing even leakage of the cooling water to a not-to-be-cooled area of the forged product 20. Further, even for the turn table 6, a ceramic table is used to prevent dissipation of heat of a portion being in contact with the rotary table 6 of the forged product 20.

According to the partially cooling apparatus thus configured, when the cooling water is injected from the nozzles 5a while the turn table 6 is being turned, only the flange base portions 20a is cooled, but the other areas are not forcedly cooled. Consequently, only a locally cooled area, that is, the flange base portions 20a in the present example, can be quenched. After stop of cooling, then self-tempering is effected using heat transferred from non-locally cooled areas.

In this event, partial cooling is performed, preferably, by using the parameter H described above.

After the partial cooling, radiational cooling is effected. The radiational cooling can be effected either in a bucket (not shown) disposed to a terminal end of the transport line 3 or on the transport line 3.

By using the hot forging facility described above, cooling localized to the specified area can be securely effected on the hot forged product, consequently making it possible to manufacture the hot forged product satisfying “(V₁-V₂)/V₂=0.1˜0.8”.

In the example facility described above, while the single partially cooling apparatus 5 is provided in the position along the transport line 3, a plurality of partially cooling apparatuses 5 can be disposed along the transport line 3. In this case, a plurality of forged products can be partially cooled at substantially the same time, such that the partial cooling process can be implemented corresponding to the forging rate in the same line.

The nozzles 5a may be either a plurality of openings provided on an inner side of a ringular pipe or circumferential slit nozzles. For using the alternative nozzles, a non-turnable table may be used instead of the turn table 6. However, it is preferable that the turn table 6 be used to further improve uniformity. Further, the partition plate 7a is provided corresponding to an allowable level of the degree of temperature fall in the not-to-be-cooled area, but is not indispensable.

In the example described above, although the partially cooling apparatus 5 is disposed on the side downstream of the forging apparatus. However, the partially cooling apparatus 5 may be provided inside of the forging apparatus to be able to effect cooling immediately after forging. Further, the configuration may be such that, when performing forging at multiple passes, cooling is effected in any inter-pass stage.

EXAMPLES

Steels of chemical compositions shown in Table 1 are refined in a vacuum melting furnace, and are molded into 100 kg ingots. Subsequently, the respective ingot is formed into a 65 mm diameter steel bar by hot forging, and then the steel bar is led into the hot forging facility. First, the steel bar was heated up to 1200° C. in the heating furnace 1, and then was subjected to three hot forging steps as shown in FIGS. 4(b) to 4(d) in the hot forging apparatus 4. Thereby, a forged product 20 having a flange, as shown in FIG. 4(d), were formed. The forged product 20 was immediately transported into the partially cooling apparatus 5 shown in FIG. 5. Then, partial cooling localized to flange base portions 20a was effected by injecting the cooling water at a flow range of 10˜201/min, and then was subjected to radiational cooling. The start temperature of the partially cooled area was set to 780˜1150° C.

The respective hot forged product thus obtained was subjected structure observation, hardness measurement, and machining testing. For comparison, forged products were manufactured through a hot forging and air cooling process and hot forging and entire tempering process that have been conventionally generally used. In this case, after entire quenching, a tempering process was performed to satisfy a condition of “600° C. (tempering temperature)×1 hr.”

First, structure observation was carried in such a manner that structure observation samples, respectively, were cut out from a flange base portion 20a and axial end portion 20b of the respective hot forged product obtained, and “3 vol. % natal” etched microstructures thereof were observed using an optical microscope and an electronic microscope.

Vickers hardness measurement was carried out in such a manner that the Vickers hardness was measured at a 1-mm portions below a skin of each of the flange base portion 20a and the axial end portion 20b by applying a load of 300 g.

Machinability by machining (cutting) testing was evaluated by outer-circumference machining. More specifically, machining was carried with a carbide tool P10 at a cutting speed of 200 m/min, a cutting depth of 0.25 mm, and a feed of 0.5 mm/rev by spraying a lubricant, and the machinability was evaluated in terms of a time period required for machining the entirety of the respective component. More specifically, evaluation was made in terms of “(t2-t1)/t1,” where t2 is the required time relative to a time period t1 required for machining the respective material subjected to the conventional hot forging and air cooling process.

Thus, partial cooling was securely effected by use of the facility of the present invention. As a result, it was possible to obtain obtaining forged products in each of which the structure of a cooled area is formed from quenched martensite or bainite or a mixture thereof. In addition, and the structure of an area other than the cooled area is formed from ferrite-pearlite or from bainite, and the hardness ratio “(V₁-V₂)/V₂” is within the range of 0.14˜0.77. Further, the machinability evaluation results are each lower or equal to 1.2 times that of the conventionally processed material and less or equal to about ⅓ times that of the forged product subjected to the conventional entire quenching.

TABLE 1
Steel	Chemical Composition (mass %)	Transformation Point (° C.)
No.	C	Si	Mn	Mo	P	S	Al	Cu	Ni	Nb	Cr	Ti	V	B	Ca	Ac3	Ac1
1	0.54	0.23	0.83	—	0.014	0.015	0.026	—	—	—	0.20	—	—	—	—	771	724
2	0.31	0.22	0.64	—	0.014	0.008	0.021	—	—	—	—	—	—	—	—	807	723
3	0.53	0.69	0.8	—	0.015	0.015	0.019	—	0.05	—	0.16	—	0.03	—	—	795	736
4	0.45	0.66	0.55	0.36	0.010	0.010	0.030	0.16	0.21	0.021	—	0.015	0.02	0.002	0.004	817	733
5	0.51	0.76	0.62	0.54	0.021	0.009	0.025	0.31	—	—	—	—	—	—	—	816	738
Ac3 = 910 − 203{square root over ( )}C − 15.2Ni + 44.7Si + 104V + 31.5Mo
Ac1 = 723 − 10.7Mn − 16.9Ni + 29.1Si − 16.9Cr

	TABLE 2
		Hot	Cooling		Cooling	Heat
		Forging	Start	Cooling	Stop	Recuperation		Hardened	Un-hardened	Hardness	Machining
	Steel	Temp.	Temp.	Rate	Temp.	Max. Temp.		Area	Area	Increase	Time
No.	Type	(° C.)	(° C.)	(° C./s)	(° C.)	(° C.)	H	Structure	Hv	Structure	Hv	Rate (%)	Ratio	Remarks
1	1	1200	1100	35	203	560	80	M	332	F + P	234	42	1.1	Example of
														the invention
2		1200	1150	22	214	620	84	M	269	F + P	236	14	1.0	Example of
														the invention
3		1050	980	34	229	370	67	M	427	F + P	241	77	1.2	Example of
														the invention
4		950	870	60	220	520	78	M	346	F + P	236	47	1.1	Example of
														the invention
5		810	780	46	219	530	79	M	362	F + P	247	47	1.1	Example of
														the invention
6		1150	1100	38	340	550	81	B	301	F + P	243	24	1.0	Example of
														the invention
7		1150	1100	51	270	540	79	M + B	354	F + P	239	48	1.1	Example of
														the invention
8		1150	1100	0.5	—	—	—	—	—	F + P	231	—	1.0	Comparative
														Example:
														Conventional
														Process
9		1150	1100	36	Ambient	—	—	M	687	—	—	—	4.2	Comparative
					temp.									Example:
														Entire
														Quenching,
														Tempering
10	2	1100	1030	26	367	560	83	M	296	F + P	224	32	1.1	Example of
														the invention
11		1100	1030	0.7	—	—	—	—	—	F + P	226	—	1.0	Comparative
														Example:
														Conventional
														Process
12	3	1140	1050	27	260	530	81	M	342	F + P	267	28	1.2	Example of
														the invention
13		1140	1050	0.7	—	—	—	—	—	—	267	—	1.0	Comparative
														Example:
														Conventional
														Process
14	4	1080	1020	23	305	520	79	M	339	B	285	19	1.1	Example of
														the invention
15		1080	1020	0.6	—	—	—	—	—	—	279	—	1.0	Comparative
														Example:
														Conventional
														Process
16	5	1120	1080	42	237	530	76	M	319	B	264	21	1.1	Example of
														the invention
17		1120	1080	0.4	—	—	—	—	—	—	263	—	1.0	Comparative
														Example:
														Conventional
														Process

Claims

1-4. (canceled)

5. A hot forging facility wherein a heating furnace for heating a steel material and a hot forging apparatus for performing forging of the heated steel material are sequentially arranged on a transport line, having a partially cooling apparatus for partially cooling a forged product after hot forging, the partially cooling apparatus is provided at least inside of or on an exit side of the hot forging apparatus.

6. The hot forging facility according to claim 5, wherein the cooling apparatus includes a nozzle for spraying cooling liquid towards at least a portion of the forged product.

7. The hot forging facility according to claim 5, wherein at least one unit of the cooling apparatus is provided in a position along the transport line on an exit side of the hot forging apparatus.

8. The hot forging facility according to claim 7, wherein at least one unit of the cooling apparatus is provided in a position along the transport line on an exit side of the hot forging apparatus.

9. The hot forging facility according to claim 5, wherein a plurality of the cooling apparatuses are provided in positions along the transport line on an exit side of the hot forging apparatus.

10. The hot forging facility according to claim 6, wherein a plurality ofthe cooling apparatuses are provided in positions along the transport line on an exit side of the hot forging apparatus.

11. The hot forging facility according to claim 7, wherein a plurality ofthe cooling apparatuses are provided in positions along the transport line on an exit side of the hot forging apparatus.

12. The hot forging facility according to claim 8, wherein a plurality ofthe cooling apparatuses are provided in positions along the transport line on an exit side of the hot forging apparatus.

13. A hot forging facility comprising: a heating furnace that heats steel material; anda hot forging apparatus that forges the heated steel material sequentially arranged on a transport line, the hot forging apparatus having a cooling apparatus that partially cools forged products after hot forging is provided at least inside of or on an exit side of the hot forging apparatus.

14. The hot forging facility according to claim 13, wherein the cooling apparatus includes a nozzle for spraying cooling liquid towards at least a portion of the forged product.

15. The hot forging facility according to claim 13, wherein at least one unit of the cooling apparatus is provided in a position along the transport line on an exit side of the hot forging apparatus.

16. The hot forging facility according to claim 15, wherein at least one unit of the cooling apparatus is provided in a position along the transport line on an exit side of the hot forging apparatus.

17. The hot forging facility according to claim 13, wherein a plurality of the cooling apparatuses are provided in positions along the transport line on an exit side of the hot forging apparatus.

18. The hot forging facility according to claim 14, wherein a plurality of the cooling apparatuses are provided in positions along the transport line on an exit side of the hot forging apparatus.

19. The hot forging facility according to claim 15, wherein a plurality of the cooling apparatuses are provided in positions along the transport line on an exit side of the hot forging apparatus.

20. The hot forging facility according to claim 16, wherein a plurality of the cooling apparatuses are provided in positions along the transport line on an exit side of the hot forging apparatus.