Hot rolled steel sheet for cold rolled steel sheet, hot rolled steel sheet for galvanized steel sheet, and method for producing the same

Abstract

A hot rolled steel sheet having a chemical composition containing, by mass %, C: 0.04% or more and 0.20% or less, Si: 0.7% or more and 2.3% or less, Mn: 0.8% or more and 2.8% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities. The microstructure of the hot rolled steel sheet includes ferrite and pearlites, in which the area ratio of the ferrite is 75% or more and less than 95%, the mean grain size of the ferrite is 5 μm or more and 25 μm or less, the area ratio of pearlite is 5% or more and less than 25%, the mean grain size of pearlite is 2.0 μm or more, and the mean free path of pearlite is 5 μm or more.

Description

FIELD OF THE INVENTION

The present invention relates to a hot rolled steel sheet for a cold rolled steel sheet and a hot rolled steel sheet for a galvanized steel sheet excellent in terms of formability and stability of material quality which can be suitably applied to automobile parts and a method for producing the hot rolled steel sheets.

BACKGROUND OF THE INVENTION

Nowadays, an increase in fuel efficiency is strongly required in order to decrease the CO₂ emission of automobiles due to growing awareness of the need to conserve the global environment. Accordingly, there is a trend towards decreasing the weight of automobiles by increasing the strength of the material of automobile bodies in order to decrease the thickness of the material. However, there is a concern that there may be a decrease in ductility due to the increase in the strength of steel sheets. Therefore, the development of a high strength and high ductility steel sheet is desired. In addition, there is a significant decrease in shape fixability due to an increase in the strength of a steel sheet and a decrease in the thickness of a steel sheet. In order to solve this problem, it is common practice to design a mold for press forming in anticipation of the amount of deformation which is expected to occur after the release of a workpiece from the mold. However, in the case where the tensile strength (TS) of a steel sheet varies, a shape defect occurs due to the deviation of the amount of deformation from that which is expected for a constant tensile strength, and a readjustment such as sheet-metal working of each workpiece is necessary after press forming in order to correct the shape of the workpiece, which results in a significant decrease in volume efficiency. Therefore, it is necessary to control the variability of the TS of a steel sheet to be as small as possible.

In order to increase the ductility of a high strength cold rolled steel sheet and a high strength galvanized steel sheet, various kinds of high strength steel sheets having a combined microstructure such as ferrite-martensite dual-phase steel and TRIP steel, which utilizes the transformation induced plasticity of retained austenite, have been developed.

For example, Patent Literature 1 discloses a steel sheet excellent in terms of ductility which can be used for a high strength cold rolled steel sheet and a high strength galvanized steel sheet, in which a chemical composition and the volume fractions of ferrite, bainitic ferrite, and retained austenite phases are specified. Patent Literature 2 discloses a method for producing a high strength cold rolled steel sheet, in which the variability of elongation in the width direction of the steel sheet is decreased. In addition, in the case of a hot rolled steel sheet, Patent Literatures 3, 4, and 5 disclose methods for producing high strength hot rolled steel sheets, in which cooling conditions in a hot rolling process are specified.

PATENT LITERATURE

• PTL 1: Japanese Unexamined Patent Application Publication No. 2007-182625
• PTL 2: Japanese Unexamined Patent Application Publication No. 2000-212684
• PTL 3: Japanese Patent No. 3119122
• PTL 4: Japanese Patent No. 3823338
• PTL 5: Japanese Unexamined Patent Application Publication No. 10-36917

SUMMARY OF THE INVENTION

Since the main object of the Patent Literature 1 is to increase the ductility of a high strength steel sheet, stability of material quality is not considered. In addition, since only the variability of total elongation (EL) in the width direction is mentioned in Patent Literature 2, the variability of material quality due to a chemical composition and producing conditions is not considered. Moreover, in any of Patent Literatures 1 and 2 described above, microstructure control at the hot rolling stage is not considered, and an increase in ductility and a decrease in the variability of ductility in the width direction have been intended by microstructure control after cold rolling. In addition, in Patent Literatures 3, 4, and 5, methods for producing hot rolled steel sheets excellent in terms of stretch flangeability are disclosed, but a hot rolled material to be used for producing a cold steel sheet or a hot rolled material to be used for producing a galvanized steel sheet is not considered. Therefore, there is a desire for the development of a hot rolled steel sheet for a cold rolled steel sheet and a hot rolled steel sheet for a galvanized steel sheet which are excellent in terms of formability and stability of material quality.

In view of the situation described above, the present invention aims to provide a hot rolled steel sheet having a TS of 540 MPa or more which can be used for producing a cold rolled steel sheet and a galvanized steel sheet excellent in terms of formability and stability of material quality and a method for producing the hot rolled steel sheet.

The present inventors diligently conducted investigations in order to obtain a hot rolled material for producing a cold rolled steel sheet and a galvanized steel sheet having a TS of 540 MPa or more and excellent in terms of formability and stability of material quality, and, as a result, found the following facts.

The control of a microstructure of the hot rolled steel sheet in which the variability of material quality is small has been aimed at by forming a microstructure mainly including ferrite and pearlite at the coiling stage in a hot rolling process so as to suppress the change of the microstructure due to transformation in the following cooling process. Moreover, the sufficient strength, an increase in the ductility of a cold rolled steel sheet and a galvanized steel sheet and a decrease in the variability of the material quality (the stability of material quality) of a cold rolled steel sheet and a galvanized steel sheet after the following annealing have been aimed at by controlling a thermal history from a finish rolling delivery temperature to a coiling temperature, in particular, a cooling rate, so as to form the microstructure of the steel sheet mainly include ferrite and pearlite and so as to control the mean grain sizes and the area ratios of the ferrite and pearlite and the dispersion state (mean free path) of the pearlite. As a result, the production of a hot rolled steel sheet for a cold rolled steel sheet and a hot rolled steel sheet for a galvanized steel sheet excellent in terms of formability and stability of material quality has become possible.

The present invention has been completed on the basis of the knowledge described above and includes the following characteristics.

[1] A hot rolled steel sheet for a cold rolled steel sheet, the hot rolled steel sheet having a chemical composition containing, by mass %, C: 0.04% or more and 0.20% or less, Si: 0.7% or more and 2.3% or less, Mn: 0.8% or more and 2.8% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities, and a microstructure of the hot rolled steel sheet including ferrite and pearlite, in which the area ratio of the ferrite is 75% or more and less than 95%, the mean grain size of the ferrite is 5 μm or more and 25 μm or less, the area ratio of the pearlite is 5% or more and less than 25%, the mean grain size of the pearlite is 2.0 μm or more, and the mean free path of the pearlite is 5 μm or more.

[2] The hot rolled steel sheet for a cold rolled steel sheet according to item [1], in which a difference in tensile strength between a portion at the center of the width of the hot rolled steel sheet and a position located at ⅛ of the sheet width from the edge in the width direction of the hot rolled steel sheet, is 30 MPa or less.

[3] The hot rolled steel sheet for a cold rolled steel sheet according to item [1], further containing, by mass %, at least one element selected from the group consisting of Cr: 0.05% or more and 1.0% or less, V: 0.005% or more and 0.5% or less, Mo: 0.005% or more and 0.5% or less, Ni: 0.05% or more and 1.0% or less, and Cu: 0.05% or more and 1.0% or less.

[4] The hot rolled steel sheet for a cold rolled steel sheet according to item [1] or [3], further containing, by mass %, at least one element selected from the group consisting of Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less, and B: 0.0003% or more and 0.0050% or less.

[5] The hot rolled steel sheet for a cold rolled steel sheet according to item [1] or [3], further containing, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

[6] The hot rolled steel sheet for a cold rolled steel sheet according to item [4], further containing, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

[7] A hot rolled steel sheet for a galvanized steel sheet, the hot rolled steel sheet having a chemical composition containing, by mass %, C: 0.04% or more and 0.20% or less, Si: 0.7% or more and 2.3% or less, Mn: 0.8% or more and 2.3% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities, and a microstructure of the hot rolled steel sheet including ferrite and pearlite, in which the area ratio of the ferrite is 75% or more and less than 95%, the mean grain size of the ferrite is 5 μm or more and 25 μm or less, the area ratio of the pearlite is 5% or more and less than 25%, the mean grain size of the pearlite is 2.0 μm or more, and the mean free path of the pearlite is 5 μm or more.

[8] The hot rolled steel sheet for a galvanized steel sheet according to item [7], in which a difference in tensile strength between a portion at the center of the width of the hot rolled steel sheet, and a position located at ⅛ of the sheet width from the edge in the width direction of the hot rolled steel sheet is 30 MPa or less.

[9] The hot rolled steel sheet for a galvanized steel sheet according to item [7], further containing, by mass %, at least one element selected from the group consisting of Cr: 0.05% or more and 1.0% or less, V: 0.005% or more and 0.5% or less, Mo: 0.005% or more and 0.5% or less, Ni: 0.05% or more and 1.0% or less, and Cu: 0.05% or more and 1.0% or less.

[10] The hot rolled steel sheet for a galvanized steel sheet according to item [7] or [9], further containing, by mass %, at least one element selected from the group consisting of Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less and B: 0.0003% or more and 0.0050% or less.

[11] The hot rolled steel sheet for a galvanized steel sheet according to item [7] or [9], further containing, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

[12] The hot rolled steel sheet for a galvanized steel sheet according to item [11], further containing, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

[13] A method for producing a hot rolled steel sheet for a cold rolled steel sheet, the method including:

hot rolling a steel slab having a chemical composition containing, by mass %, C: 0.04% or more and 0.20% or less, Si: 0.7% or more and 2.3% or less, Mn: 0.8% or more and 2.8% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities under the condition that a finish rolling delivery temperature is 850° C. or higher;

cooling the hot rolled steel sheet at a mean cooling rate of 20° C./s to 90° C./s in a temperature range from the finish rolling delivery temperature to 650° C.;

further cooling the hot rolled steel sheet at a mean cooling rate of 5° C./s to 35° C./s in a temperature range down to a coiling temperature; and

coiling the cooled steel sheet at a temperature of 470° C. to 640° C.

[14] The method for producing a hot rolled steel sheet for a cold rolled steel sheet according to item [13], wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Cr: 0.05%, or more and 1.0% or less, V: 0.005% or more and 0.5% or less. Mo: 0.005% or more and 0.5% or less, Ni: 0.05% or more and 1.0% or less, and Cu: 0.05% or more and 1.0% or less.

[15] The method for producing a hot rolled steel sheet for a cold rolled steel sheet according to item [13] or [14], wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less, and B: 0.0003% or more and 0.0050% or less.

[16] The method for producing a hot rolled steel sheet for a cold rolled steel sheet according to item [13] or [14], wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

[17] The method for producing a hot rolled steel sheet for a cold rolled steel sheet according to item [15], wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

[18] A method for producing a hot rolled steel sheet for a galvanized steel sheet, the method including:

hot rolling a steel slab having a chemical composition containing, by mass %, C: 0.04% or more and 0.20% or less, Si: 0.7% or more and 2.3% or less, Mn: 0.8% or more and 2.8% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities under the condition that a finish rolling delivery temperature is 850° C. or higher,

cooling the hot rolled steel sheet at a mean cooling rate of 20° C./s to 90° C./s in a temperature range from the finish rolling delivery temperature to 650° C.,

further cooling the hot rolled steel sheet at a mean cooling rate of 5° C./s to 35° C./s in a temperature range down to a coiling temperature, and

coiling the cooled steel sheet at a temperature of 470° C. to 640° C.

[19] The method for producing a hot rolled steel sheet for a galvanized steel sheet according to item [18], wherein the steel slab further contains, by mass %, at least one element selected the group consisting of Cr: 0.05% or more and 1.0% or less, V: 0.005% or more and 0.5% or less, Mo: 0.005% or more and 0.5% or less, Ni: 0.05% or more and 1.0% or less, and Cu: 0.05% or more and 1.0% or less.

[20] The method for producing a hot rolled steel sheet for a galvanized steel sheet according to item [18] or [19], wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less, and B: 0.0003% or more and 0.0050% or less.

[21] The method for producing a hot rolled steel sheet for a galvanized steel sheet according to item [18] or [19], wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

[22] The method for producing a hot rolled steel sheet for a galvanized steel sheet according to item [20], wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

Here, % used when describing a chemical composition of steel always represents mass % in the present specification.

In addition, in the present invention, “a galvanized steel sheet” collectively means a steel sheet which is coated with zinc by a galvanizing method regardless of whether or not the steel sheet is subjected to an alloying treatment after galvanizing has been performed. That is to say, galvanized steel sheets according to the present invention include both a galvanized steel, sheet (GI) which is not subjected to an alloying treatment and a galvannealed steel sheet (GA) which is subjected to an alloying treatment. In addition, in the present invention, hot rolled steel sheets for cold rolled steel sheets and hot rolled steel sheets for galvanized steel sheets include both cut steel sheets and coiled steel sheets (strips).

According to the present invention, a hot rolled steel sheet for a cold rolled steel sheet and a hot rolled steel sheet for a galvanized steel sheet excellent in terms of formability and stability of material quality can be obtained. Since a cold steel sheet and a galvanized steel sheet which are produced from the hot rolled steel sheet according to the present invention preferably have a TS of 540 MPa or more and are excellent in terms of formability and stability of material quality, an increase in fuel efficiency due to a decrease in the weight of automobile bodies can be realized by applying the steel sheets to, for example, the structural parts of automobiles.

DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION

Exemplary embodiments of the present invention will be described in detail hereafter.

By appropriately controlling the mean grain sizes and the mean area ratios of ferrite and pearlite of a microstructure of the hot rolled steel sheet, it has become possible to achieve good ductility after the following annealing has been performed. Moreover, it has been found that, by controlling the thermal history in hot rolling so as to control the mean grain size of ferrite and the mean grain size and the mean free path of pearlite in a microstructure of the hot rolled steel sheet, a microstructure of the hot rolled steel sheet in which pearlite is dispersed sparsely can be formed. Accordingly, the further increase in ductility and the further decrease in the variability of material quality (increase in stability of material quality) of a cold rolled steel sheet and a galvanized steel sheet which are produced by performing an annealing treatment afterward (hereinafter, a steel sheet which has been subjected to an annealing treatment will be also called “an annealed steel sheet”) can be achieved. That is to say, by considering microstructure control at the hot rolling stage, it has become possible to manufacture a cold rolled steel sheet and a galvanized steel sheet excellent in terms of formability and stability of material quality.

The facts described above are the technological characteristics which have been used to complete the present invention.

A chemical composition contains, by mass %, C: 0.04% or more and 0.20% or less, Si: 0.7% or more and 2.3% or less, Mn: 0.8% or more and 2.8% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities, and a microstructure of the hot rolled steel sheet includes ferrite and pearlite, in which the area ratio of the ferrite is 75% or more and less than 95%, the mean grain size of the ferrite is 5 μm or more and 25 μm or less, the area ratio of the pearlite is 5% or more and less than 25%, the mean grain size of the pearlite is 2.0 μm or more, and the mean free path of the pearlite is 5 μm or more.

(1) First, a chemical composition will be described.

C: 0.04% or More and 0.20% or Less

C is an element which is effective for forming an austenite phase and for increasing strength and ductility by forming a combined microstructure after annealing has been performed. In the case where the C content is less than 0.04%, it is difficult to obtain an annealed steel sheet with a sufficient strength. On the other hand, in the case where the C content is more than 0.20% excessively, mechanical properties of a welded part deteriorate due to a significant increase in the hardness of the welded part and heat affected zone, which results in a decrease in performances such as spot welding performance and arc welding performance. Therefore, the C content is set to be 0.04% or more and 0.20% or less, preferably 0.05% or more and 0.14% or less, more preferably 0.07% or more and 0.12% or less.

Si: 0.7% or More and 2.3% or Less

Si is an element which is effective for forming a ferrite, for solid solution strengthening of the ferrite of an annealed steel sheet, and for increasing the ductility of an annealed steel sheet. It is necessary that the Si content be 0.7% or more in order to improve the balance between the strength and ductility of an annealed steel sheet. In addition, Si is an element which is necessary to increase the stability of material quality, because Si promotes ferrite transformation at the hot rolling stage, which results in securing the desired mean grain size and area ratio of ferrite. However, in the case where the Si content is more than 2.3% excessively, red scale or the like occurs, which results in the deterioration of surface quality and the wettability and adhesiveness of coating. Therefore, the Si content is set to be 0.7% or more and 2.3% or less, preferably 0.9% or more and 2.0% or less, more preferably more than 1.2% and 2.0% or less.

Mn: 0.3% or More and 2.8% or Less

Mn is an element which is effective for forming an austenite phase and for securing a strength of an annealed steel sheet. It is difficult to secure the strength in the case where the Mn content is less than 0.8%. On the other hand in the case where the Mn content is more than 2.8% excessively ferrite transformation and pearlite transformation are delayed in hot rolling, which makes it difficult to obtain a desired mean grain size and area ratio of ferrite, resulting in a concern that there may be a decrease in the stability of material quality. In addition, since the alloying cost of Mn is increasing nowadays, excessively high Mn content causes an increase in cost. Therefore, the Mn content is set to be 0.8% or more and 2.8% or less, preferably 1.2% or more and 2.8% or less.

P: 0.1% or Less

Although P is an element which is effective for increasing the strength of steel, embrittlement due to grain boundary segregation is caused in the case where the P content is more than 0.1% excessively, which results in a decrease in impact resistance. In addition, alloying speed of a galvanized coating layer is significantly delayed in the case where the P content is more than 0.1%. Therefore, the P content is set to be 0.1% or less, preferably 0.02% or less. In addition, since P is an element which is effective for solid solution strengthening and may be added depending on a desired strength, it is preferable that the P content be 0.005% or more.

S: 0.01% or Less

Since S causes a decrease in impact resistance and a crack along the metal flow in a welded part as a result of forming inclusions such as MnS, it is preferable that the S content be as small as possible. The S content is set to be 0.01% or less from the viewpoint of producing cost, preferably 0.005% or less.

Al: 0.1% or Less

Since excessively high Al content causes a decrease in surface quality and formability due to an increase in oxide inclusions and an increase in cost, the Al content is set to be 0.1% or less, preferably 0.05% or less. In addition, since Al is an element which is effective for forming ferrite and improving the balance between strength and ductility, it is preferable that the Al content be 0.01% or more.

N: 0.008% or Less

Since N is the element which most significantly decreases the aging resistance of steel, it is preferable that the N content be as small as possible, and there is a significant decrease in aging resistance in the case where the N content is more than 0.008%. Therefore, the N content is set to be 0.008% or less, preferably 0.004% or less.

The remainder of the chemical composition consists of Fe and inevitable impurities. However, the alloying elements described below may be added as needed in addition to the composition described above.

At least one selected from the group consisting of Cr: 0.05% or more and 1.0% or less, V: 0.005% or more and 0.5% or less, Mo: 0.005% or more and 0.5% or less, Ni: 0.05% or more and 1.0% or less, and Cu: 0.05% or more and 1.0% or less

Since Cr, V, Mo, Ni, and Cu are elements which are effective for increasing the strength of steel, these elements may be added so as to increase the strength of steel as long as the contents of these elements are within the limitations according to the present invention. The effect for increasing the strength of steel can be realized in the case where the Cr content is 0.05% or more, the V content is 0.005% or more, the Mo content is 0.005% or more, the Ni content is 0.05% or more, or the Cu content is 0.05% or more. However, in the case where the Cr content is more than 1.0%, the V content is more than 0.5%, the Mo content is more than 0.5%, the Ni content is more than 1.0%, or the Cu content is more than 1.0%, the fraction of retained raicrostructures (described below) such as martensite becomes excessively large, which causes a concern that there may be a decrease in ductility due to a significant increase in strength. In addition, the excessively high contents of these elements cause an increase in cost. Therefore, in the case where these elements are added, the Cr content is set to be 0.05% or more and 1.0% or less, the V content is set to be 0.005% or more and 0.5% or less, the Mo content is set to be 0.005% or more and 0.5% or less, the Ni content is set to be 0.05% or more and 1.0% or less, and the Cu content is set to be 0.05% or more and 1.0% or less.

At least one selected from the group consisting of Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less, and B: 0.0003% or more and 0.0050% or less

Ti and Nb are elements which are effective for precipitation strengthening of steel. This effect is realized in the case where the Ti content is 0.01% or more, or the Nb content is 0.01% or more. However, in the case where the Ti content is more than 0.1% or the Nb content is more than 0.1% excessively, the fraction of retained microstructures such as a martensite becomes excessively large, which causes a concern that there may be a decrease in ductility due to a significant increase in strength, and which results in an increase in cost. Therefore, in the case where Ti or Nb is added, the Ti content is set to be 0.01% or more and 0.1% or less, or the Nb content is set to be 0.01% or more and 0.1% or less.

B is an element which is effective for increasing the strength of steel, and this effect is realized in the case where the B content is 0.0003% or more. However, in the case where the B content is more than 0.0050% excessively, the fraction of retained microstructures such as martensite becomes excessively large, which causes a concern that there may be a decrease in ductility due to a significant increase in strength. In addition, excessively high B content causes an increase in cost. Therefore, in the case where B is added, the B content is set to be 0.0003% or more and 0.0050% or less.

At least one selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less

Ca and REM are elements which are effective for decreasing the negative effect of sulfides on local ductility as a result of spheroidizing the shape of the sulfides. In order to realize this effect, it is necessary that the Ca content be 0.001% or more, or the REM content be 0.001% or more. However, in the case where the Ca content or the REM content is more than 0.005%, there is an increase in the amount of inclusions, which results in the occurrence of defects on the surface and the inside of a steel sheet. Therefore, in the case where Ca or REM is added, the Ca content is set to be 0.001% or more and 0.005% or less, or the REM content is set to be 0.001% or more and 0.005% or less.

(2) Secondly, a microstructure will be described.

The area ratio of ferrite of a microstructure of the hot rolled steel sheet: 75% or more and less than 95%

In order to obtain an annealed steel sheet with good ductility, it is necessary that the area ratio of ferrite of a microstructure of the hot rolled steel sheet be 75% or more, more preferably 78% or more. In addition, in order to obtain an annealed steel sheet with a sufficient strength, it Is necessary the area ratio of ferrite of a microstructure of the hot rolled steel sheet be less than 95%.

The area ratio of pearlite of a microstructure of the hot rolled steel sheet: 5% or more and less than 25%

In order to obtain an annealed steel sheet with good ductility, it is necessary that the area ratio of pearlite of a microstructure of the hot rolled steel sheet be 5% or more, more preferably 8% or more. In addition, in order to obtain an annealed steel sheet with sufficient stability of material quality, it is necessary the area ratio of pearlite of a microstructure of the hot rolled steel sheet be less than 25%.

The mean grain size of ferrite of a microstructure of the hot rolled steel sheet: 5 μm or more and 25 μm or less

In order to obtain an annealed steel sheet with good stability of material quality, it is necessary that the mean grain size of ferrite of a microstructure of the hot rolled steel sheet be 5 μm or more. In addition, in the case where the mean grain size of ferrite of the microstructure of the hot rolled steel sheet is more than 25 μm, it is difficult to obtain an annealed steel sheet with a desired strength. Therefore, it is necessary that the mean grain size of ferrite of a microstructure of the hot rolled steel sheet be 5 μm or more and 25 μm or less, preferably 8 μm or more and 20 μm or less.

The mean grain size of pearlite of a microstructure of the hot rolled steel sheet: 2.0 μm or more

In order to obtain an annealed steel sheet with good ductility, it is necessary that the mean grain size of pearlite of a microstructure of the hot rolled steel sheet be 2.0 μm or more, preferably 3.0 μm or more and 10 μm or less.

The mean free path of pearlite of a microstructure of the hot rolled steel sheet: 5 μm or more

In order to obtain an annealed steel sheet with good ductility and stability of material quality, it is necessary that the mean free path of pearlite of a microstructure of the hot rolled steel sheet be 5 μm or more, preferably 6 μm or more and 15 μm or less.

There is a case where, in addition to ferrite and pearlite, carbides such as a cementite and martensite, bainitic ferrite and retained austenite are formed as retained microstructures in a microstructure of the hot rolled steel sheet. It is preferable that the area ratio of these retained microstructures be 8% or less, and the effects of the present invention is not decreased as long as the area ratio is within this range. According to the present invention, it is possible to achieve benefits of the present invention, if the chemical composition of steel and the constitution of a metal microstructure (the area ratios and mean grain sizes of ferrite and pearlite and the mean free path of a pearlite) satisfy the requirement described above.

(3) A difference in tensile strength (absolute value) between a tensile strength in a portion at the center of the width of the hot rolled steel sheet and a tensile strength at a position located at ⅛ of the sheet width from the edge in the width direction of the hot rolled steel sheet: 30 MPa or less

In order to realize a decrease in the variability of material quality in the width direction of an annealed steel sheet (increase in the stability of material quality), it is effective to stabilize the material quality in the width direction of a hot rolled steel sheet. From the viewpoint of the stabilization of the material quality of an annealed steel sheet, it is preferable that a difference (absolute value) in tensile strength between a portion at the center of the width of the hot rolled steel sheet and a position located at ⅛ of the sheet width from the edge (edge portion) in the width direction of the hot rolled steel sheet (hereinafter, also called “position at ⅛ of width”) be 30 MPa or less.

In addition, it is more preferable that differences in yield stress (ΔYP) and total elongation (ΔEL) between a portion at the center of the width of the hot rolled steel sheet and a position located at ⅛ of the sheet width from the edge (edge portion) in the width direction of the hot rolled steel sheet be respectively 40 MPa or less and 4% or less from the viewpoint of stabilization of the material quality of an annealed steel sheet. The reason why the variability of material quality of the hot rolled steel sheet is evaluated at the two points, one of which is a portion at the center of the width of a hot rolled steel sheet and another is a position at ⅛ of width, is that, for example, in case where a difference in tensile strength between a portion at the center of the width of a hot rolled steel sheet and a position located at ¼ of the sheet width from the edge (edge portion) in the width direction of the hot rolled steel sheet (position at ¼ of width) is used, the material quality in the vicinity of the edge cannot be evaluated, accordingly, it is difficult to satisfactorily evaluate the stability of material quality in the width direction, but it is possible to appropriately evaluate the stability of the material quality of an annealed steel sheet by using a difference between a position located at ⅛ of the width, which is closer to the edge, and a portion at the center of the width.

(4) Subsequently, an embodiment of a method for producing the hot rolled steel sheet for a cold rolled steel sheet and the hot rolled steel sheet for a galvanized steel sheet according to embodiments of the present invention will be described.

The hot rolled steel sheet for a cold rolled steel sheet excellent in terms of formability and stability of material quality according to the present invention can be produced by hot rolling a steel slab having the chemical composition described above under the condition that a finish rolling delivery temperature is 850° C. or higher, by cooling the hot rolled steel, sheet at a mean cooling rate of 20° C./s to 90° C./s in a temperature range from the finish rolling delivery temperature to 650° C., by further cooling the hot rolled steel sheet at a mean cooling rate of 5° C./s to 35° C./s in a temperature range down to a coiling temperature, and by coiling the cooled steel sheet at a temperature of 470° C. to 640° C.

In addition, the hot rolled steel sheet for a galvanized steel sheet excellent in terms of formability and stability of material quality according to the present invention can be produced by hot rolling a steel slab having the chemical composition described above under the condition that a finish rolling delivery temperature is 850° C. or higher, by cooling the hot rolled steel sheet at a mean cooling rate of 20° C./s to 90° C./s in a temperature range from the finish rolling delivery temperature to 650° C., by further cooling the hot rolled steel sheet at a mean cooling rate of 5° C./s to 35° C./s in a temperature range down to a coiling temperature, and by coiling the cooled steel sheet at a temperature of 470° C. to 640° C.

Detailed description will be given hereafter.

Steel having a chemical composition described above is smelted by a well-known method, made into a slab by performing slabbing rolling or continuous casting, and made into a hot rolled steel sheet by performing hot rolling. Although there is no limitation on the heating conditions of the slab, it is preferable that the heating temperature be 1100° C. to 1300° C. Hot rolling is performed under the conditions described below.

A finish rolling delivery temperature: 850° C. or higher

In the case where the finish rolling delivery temperature is lower than 850° C., a microstructure, in which a ferrite is elongated in the rolling direction, is formed, which results in a decrease in the ductility and stability of the material of an annealed steel sheet. Therefore, the finish rolling delivery temperature is set to be 850° C. or higher, preferably 870° C. or higher.

Cooling at a mean cooling rate of 20° C./s to 90° C./s in a temperature range from the finish rolling delivery temperature to 650° C. (first cooling)

In the case where the mean cooling rate in a temperature range from the finish rolling delivery temperature to 650° C. is less than 20° C./s, ferrite transformation excessively progresses and a desired area ratio of a pearlite cannot be achieved, which results in a decrease in the ductility of an annealed steel sheet. In addition, in the case where the mean cooling rate is more than 90° C./s, ferrite transformation does not sufficiently progress in a microstructure of the hot rolled steel sheet and a desired mean grain size of ferrite and a desired mean free path of pearlite cannot be achieved, which results in a decrease in the ductility and stability of the material quality of an annealed steel sheet. Therefore, the mean cooling rate in a temperature range from the finish rolling delivery temperature to 650° C. is set to be 20° C./s to 90° C./s, preferably 30° C./s to 70° C./s.

Cooling at a mean cooling rate of 5° C./s to 35° C./s in a temperature range down to a coiling temperature (second cooling)

In the case where the mean cooling rate in a temperature range down to a coiling temperature after the first cooling has been finished is less than 5° C./s, ferrite transformation excessively progresses and a desired area ratio of a pearlite cannot be achieved, which results in a decrease in ductility. In addition, in the case where the mean cooling rate in a temperature range down to a coiling temperature after the first cooling has been finished is more than 35° C./s, bainite transformation progress after coiling has been finished, a desired area ratio and mean grain size of pearlite cannot be achieved, which results in a decrease in the ductility of an annealed steel sheet. Therefore, the mean cooling rate in a temperature range down to a coiling temperature is set to be 5° C./s to 35° C./s, preferably 10° C./s to 25° C./s.

Coiling Temperature: 470° C. to 640° C.

In the case where the cooing temperature is lower than 470° C., low-temperature transformation phases (hard phases) of martensite and bainite are contained in a large amount in a microstructure of the hot rolled steel sheet and a desired area ratio of a pearlite cannot be obtained, which results in a decrease in the stability of material quality of an annealed steel sheet due to the occurrence of uneven distribution of hardness in the width direction of the microstructure of the hot rolled steel sheet. In addition, in the case where the coiling temperature is higher than 640° C., there is an increase in the grain size of ferrite in a microstructure of the hot rolled steel sheet, it is difficult to achieve a desired strength of an annealed steel sheet. Therefore, the coiling temperature is set to be 470° C. to 640° C., preferably 480° C. to 620° C.

A cold rolled steel sheet is produced by pickling the hot rolled steel sheet obtained as described above by a commonly known method, optionally, as needed, by performing pretreatments such as degreasing, by cold rolling the pickled steel sheet, and by performing an annealing treatment on the cold rolled steel sheet. In addition, after the annealing treatment has been performed, a galvanized steel sheet is produced by performing a galvanizing treatment, and optionally, by further performing an alloying treatment. In addition, a galvanized steel, sheet may be produced, without performing cold rolling after pickling has been performed, by performing an annealing treatment, by performing a galvanizing treatment, and optionally, by further performing an alloying treatment. In the series of the heat treatments in the producing method according to the present invention, the steel sheet may be subjected to heat treatments in any kinds of equipment. It is preferable that cold rolling and an annealing treatment be performed under the conditions described below.

In the case where a cold rolling reduction ratio is less than 30%, the recrystallization of a ferrite is not promoted in an annealing treatment and non-recrystallized ferrite is retained, which may result in a decrease in the ductility of an annealed steel sheet. Therefore, it is preferable that the cold rolling reduction ratio be 30% or more. It is preferable that an annealing treatment is performed at a temperature of 750° C. to 900° C. for a duration time of 15 seconds to 600 seconds. This is because, in the case where the annealing temperature is lower than 750° C. or the duration time is less than 15 seconds with the annealing temperature of 750° C. to 900° C., non-recrystallized microstructure is retained, which may result in a decrease in ductility, and because, in the case where the annealing temperature is higher than 900° C. or the duration time is more than 600 seconds with the annealing temperature of 750° C. to 900° C., there is a significant growth of austenite grains, a non-uniform microstructure is finally formed, which may result in a decrease in the stability of material quality.

A steel sheet, may be subjected to skin pass rolling for the purposes of, for example, straightening the shape of the steel sheet after annealing has been performed in the case of a cold rolled steel sheet, after galvanizing has been performed in the case of a galvanized steel sheet (GI) which is not subjected to an alloying treatment, or after an alloying treatment has been performed in the case of an galvannealed steel sheet (GA).

EXAMPLES

Steels having the chemical compositions given in Table 1 with the balance being Fe and inevitable impurities were smelted in a revolving furnace and made into slabs by a continuous casting method. The obtained slabs were heated up to a temperature of 1200° C., subjected to hot rolling under the conditions that, the thicknesses of the hot rolled steel sheets were 2.3 to 4.5 mm and finish rolling delivery temperatures were those given in Table 2, subjected to cooling under the conditions given in Table 2, and coiled. Subsequently, the obtained hot rolled steel sheets were pickled, cold rolled and annealed at a temperature of 800° C., and, as needed, subjected to a galvanizing treatment, and optionally, further subjected to a alloying treatment of the galvanized layer so as to make cold rolled steel sheets (CR), galvanized steel sheets (GI), and galvannealed steel sheets (GA). Some of the hot rolled steel sheets were, without being cold rolled after pickling had been performed, subjected to annealing and galvanizing, and, optionally, further subjected to an alloying treatment of the galvanized layer so as to make galvanized steel sheets (GI) and galvannealed steel sheets (GA). A galvanizing bath having an Al content of 0.19 mass % was used for galvanized steel sheets (GI) and a galvanizing bath having an Al content of 0.14 mass % was used for galvannealed steel sheets (GA), where the bath temperature was 460° C. Galvannealed steel sheets (GA) were subjected to an alloying treatment at a temperature of 550° C. A coating weight was 45 g/m² per side (double-sided coating). The Fe content in the coating layer of galvannealed steel sheets (GA) was 9 mass % to 12 mass %.

TABLE 1
Steel	Chemical Composition (mass %)
Grade	C	Si	Mn	Al	P	S	N	Ni	Cu	Cr	V	Mo	Nb	Ti	B	Ca	REM	Note
A	0.089	1.52	1.48	0.031	0.015	0.0018	0.0032	—	—	—	—	—	—	—	—	—	—	Example
B	0.082	1.16	1.76	0.029	0.014	0.0017	0.0034	—	—	—	—	—	—	—	—	—	—	Example
C	0.113	1.36	1.96	0.032	0.020	0.0021	0.0038	—	—	—	—	—	—	—	—	—	—	Example
D	0.078	1.47	2.66	0.030	0.013	0.0020	0.0032	—	—	—	—	—	—	—	—	—	—	Example
E	0.086	1.38	1.38	0.031	0.018	0.0019	0.0035	—	—	0.19	—	—	—	—	—	—	—	Example
F	0.096	1.34	1.52	0.026	0.012	0.0018	0.0031	—	—	—	0.058	—	—	—	—	—	—	Example
G	0.090	1.41	1.34	0.030	0.013	0.0024	0.0030	—	—	—	—	0.12	—	—	—	—	—	Example
H	0.085	1.52	1.38	0.026	0.008	0.0019	0.0032	—	—	—	—	—	0.024	—	—	—	—	Example
I	0.089	1.46	1.39	0.029	0.011	0.0026	0.0029	—	—	—	—	—	—	0.022	0.002	—	—	Example
J	0.073	1.32	1.51	0.030	0.013	0.0023	0.0036	0.22	0.16	—	—	—	—	—	—	—	—	Example
K	0.093	1.46	1.55	0.026	0.009	0.0023	0.0031	—	—	—	—	—	—	—	—	0.002	0.001	Example
L	0.013	1.24	1.62	0.034	0.022	0.0022	0.0033	—	—	—	—	—	—	—	—	—	—	Comparative
																		Example
M	0.092	0.31	1.98	0.030	0.019	0.0024	0.0031	—	—	—	—	—	—	—	—	—	—	Comparative
																		Example
N	0.086	0.99	3.02	0.028	0.016	0.0019	0.0033	—	—	—	—	—	—	—	—	—	—	Comparative
																		Example
Under line: indicates a value out of range according to the present invitation

TABLE 2
		Finish	Mean Cooling Rate	Mean
		Rolling	from Finish Rolling	Cooling Rate from
		Delivery	Delivery Temperature	650° C. to Coiling	Coiling
	Steel	Temperature	to 650° C.	Temperature	Temperature
No.	Grade	° C.	(° C./s)	(° C./s)	° C.	Note
1	A	890	36.5	18.0	560	Example
2	A	890	40.5	20.0	530	Example
3	A	890	45.5	16.0	550	Example
4	A	890	42.5	22.0	540	Example
5	A	890	32.5	15.0	580	Example
6	A	890	38.5	18.0	520	Example
7	B	900	40.5	20.0	550	Example
8	C	890	45.5	15.0	540	Example
9	A	890	35.5	12.0	550	Example
10	B	880	34.5	18.0	550	Example
11	B	880	45.5	22.0	560	Example
12	B	880	55.5	21.0	560	Example
13	C	880	60.5	12.0	540	Example
14	C	880	55.5	15.0	540	Example
15	C	880	33.5	16.0	540	Example
16	D	870	31.5	20.0	570	Example
17	D	870	40.5	20.0	570	Example
18	D	870	55.5	18.0	570	Example
19	A	800	35.5	20.0	560	Comparative
						Example
20	A	890	150.0	18.0	550	Comparative
						Example
21	A	890	10.0	16.0	560	Comparative
						Example
22	A	890	36.5	50.0	530	Comparative
						Example
23	A	890	45.5	20.0	750	Comparative
						Example
24	A	890	50.5	18.0	400	Comparative
						Example
25	A	890	60.5	18.0	560	Example
26	E	890	55.5	12.0	520	Example
27	F	890	34.5	14.0	580	Example
28	G	890	45.5	20.0	570	Example
29	H	890	30.5	18.0	560	Example
30	I	890	30.5	16.0	550	Example
31	J	890	65.5	20.0	580	Example
32	K	890	40.5	22.0	550	Example
33	L	890	40.5	22.0	560	Comparative
						Example
34	M	890	35.5	19.0	520	Comparative
						Example
35	N	890	36.5	20.0	550	Comparative
						Example
Under line: indicates a value out of range according to the present invitation

Each of the area ratios of ferrite and pearlite of the obtained hot rolled steel sheets was derived by calculating the average of ten values of area ratios of each phase (ferrite or pearlite) which were calculated using Image-Pro, produced by Media Cybernetics, Inc., from the microstructure photographs which were taken using a SEM (scanning electron microscope) at a magnification of 2000 times in 10 microscopic fields of a position at ¼ of thickness (position located at ¼ of the thickness of the steel sheet from the surface of the steel sheet) of each sample which was prepared by polishing and etching, using a 3% nital solution, a cross section in the thickness direction which was parallel to the rolling direction of the steel sheet. In the microstructure photograph, ferrite is observed as a gray microstructure (base microstructure), and pearlite is observed as a layered microstructure of ferrite and cementite (white). Each of the mean grain sizes of ferrite and pearlite was derived as the average value of the equivalent circle diameters which were calculated from the areas of the grains of ferrite and pearlite which were obtained using Image-Pro described above. The mean free path of pearlite was derived using equation (1) below on the assumption that there was not a significant eccentricity in the distribution of pearlite grains as indicated by the coordinates (X-coordinate and Y-coordinate) of the barycenter of the pearlite grains which was obtained using Image-Pro described above. The remainder of the microstructure other than ferrite and pearlite was any of oxides such as cementite and martensite, bainitic ferrite and retained austenite.L_M=(d_M/2)(4π/3f)^1/3  (equation 1)

Here,

• L_M: the mean free path of a pearlite (μm)
• d_M: the mean grain size of a pearlite (μm)
• f: the area ratio of a pearlite (%)/100.

Tensile tests were carried out using the obtained cold steel sheets (CR), galvanized steel sheets (GI), and galvannealed steel sheets (GA). The tensile test was carried out using a JIS No. 5 tensile test piece, which was cut out of the steel sheet so that the tensile direction was at a right angle to the rolling direction of the steel sheet, in accordance with JIS Z 2241 (2010), and TS (tensile strength) and EL (total elongation) were determined. Ductility was evaluated using the value of TS×EL. Here, a case where the relationship TS×EL≥19000 MPa·% was satisfied was judged as satisfactory in the present invention.

The TS, yield stress (YP) and EL of the center and the position at ⅛ of width of the hot rolled steel sheet were determined by carrying out a tensile test using a JIS No. 5 test piece (with a tensile direction being at a right angle to the rolling direction) in the similar way as described above, and the differences in these values between the center of the width and the position at ⅛ of width (value for the center of the width−value for the position at ⅛ of width) were calculated and respectively represented by ΔTS, ΔYP, and ΔEL. Here, a case where the differences in these values between the center of the width and the position at ⅛ of width of the hot rolled steel sheet satisfy the relationships ΔTS=30 MPa, ΔYP≤40 MPa, and ΔEL≤4.0% was judged as a case where the stability of material quality is satisfactory in the present, invention.

In addition, the TS, yield stress (YP), and EL of the center and the position at ⅛ of width of the annealed steel sheet were determined, and the differences in these values between the center of the width and the position at ⅛ of width (value for the center of the width−value for the position at ⅛ of width) were calculated and respectively represented by ΔTS, ΔYP, and ΔEL. Here, a case where the differences in these values between the center of the width and the position at ⅛ of width of the annealed steel sheet satisfy the relationships ΔTS≤25 MPa, ΔYP≤35 MPa, and ΔEL≤3.5% was judged as a case where the stability of material quality is satisfactory in the present invention.

The results derived as described above are given in Tables 3 and 4.

TABLE 3
		Thickness				Mean	Mean	Mena
		of Hot		Area	Area	Grain	Grain	Free
		Rolled	Final	Ratio	Ratio	Size	Size	Path
	Steel	Sheet	Thickness	of F	of P	of F	of P	of P	Remainder of
No.	Grade	(mm)	(mm)	(%)	(%)	(μm)	(μm)	(μm)	Microstructure	Note
1	A	3.2	1.4	89	9	12.1	6.2	11.1	BF, θ	Example
2	A	3.2	1.4	90	8	11.4	5.6	10.5	BF, θ	Example
3	A	3.2	1.4	88	10	11.7	5.1	8.9	BF, θ	Example
4	A	2.3	0.8	89	9	10.1	4.2	7.6	BF, θ	Example
5	A	4.5	2.3	91	8	13.4	6.8	12.7	BF, θ	Example
6	A	3.2	3.2	91	8	11.4	5.4	10.1	BF, θ	Example
7	B	2.8	2.8	86	12	11.8	5.1	8.3	BF, θ	Example
8	C	2.6	2.6	83	16	10.1	4.8	7.1	BF, θ	Example
9	A	3.2	3.2	87	11	12.4	4.9	8.2	BF, θ	Example
10	B	3.2	1.4	85	13	10.6	4.6	7.3	BF, θ	Example
11	B	3.2	1.4	86	12	10.2	4.4	7.2	BF, θ	Example
12	B	3.2	1.4	87	11	11.4	4.7	7.9	BF, θ	Example
13	C	3.2	1.4	82	17	9.5	4.6	6.7	BF, M, RA, θ	Example
14	C	3.2	1.4	83	16	9.4	4.2	6.2	BF, M, RA, θ	Example
15	C	3.2	1.4	82	17	9.2	4.1	6.0	BF, M, RA, θ	Example
16	D	3.2	1.4	80	18	8.4	4.6	6.6	BF, M, RA, θ	Example
17	D	3.2	1.4	79	19	8.6	4.8	6.7	BF, M, RA, θ	Example
18	D	3.2	1.4	78	19	8.2	4.7	6.6	BF, M, RA, θ	Example
19	A	3.2	1.4	84	10	10.2	1.6	2.8	BF, θ	Comparative
										Example
20	A	3.2	1.4	77	11	3.1	2.4	4.0	BF, M, RA, θ	Comparative
										Example
21	A	3.2	1.4	94	3	10.4	3.6	9.3	BF, θ	Comparative
										Example
22	A	3.2	1.4	88	2	11.4	1.8	5.3	BF, M, RA, θ	Comparative
										Example
23	A	3.2	1.4	88	9	28.2	5.8	10.4	BF, θ	Comparative
										Example
24	A	3.2	1.4	84	3	11.5	3.8	9.9	BF, M, RA, θ	Comparative
										Example
25	A	3.2	1.4	88	9	12.1	5.4	9.7	BF, θ	Example
26	E	3.2	1.4	90	9	12.7	5.8	10.4	BF, θ	Example
27	F	3.2	1.4	88	10	12.2	5.9	10.2	BF, θ	Example
28	G	3.2	1.4	89	9	11.4	6.2	11.1	BF, θ	Example
29	H	3.2	1.4	90	9	12.6	6.2	11.1	BF, θ	Example
30	I	3.2	1.4	87	11	13.4	5.1	8.6	BF, θ	Example
31	J	3.2	1.4	88	10	13.8	5.4	9.4	BF, θ	Example
32	K	3.2	1.4	89	9	12.8	5.3	9.5	BF, θ	Example
33	L	3.2	1.4	96	1	12.0	1.7	6.4	BF, θ	Comparative
										Example
34	M	3.2	1.4	72	12	4.2	2.4	3.9	BF, M, RA, θ	Comparative
										Example
35	N	3.2	1.4	72	2	4.1	1.8	5.3	BF, M, RA, θ	Comparative
										Example
Under line: indicates a value out of range according to the present invention
F: ferrite, P: pearlite, BF: bainitic ferrite, M: martensite, RA: retained a austenite, θ: carbides such as cementite
CR: cold rolled steel sheet, GI: galvanized steel sheet, GA: galvannealed steel sheet

TABLE 4
		TS of	EL of	TS × EL of	Difference between	Difference between
		Annealed	Annealed	Annealed	Center and Position at 1/8 of	Center and Position at 1/8 of
	Steel	Sheet	Sheet	Sheet	Width of hot rolled Sheet	Width of Annealed Sheet	Steel
No.	Grade	(MPa)	(%)	(MPa • %)	ΔTS (MPa)	ΔYP (MPa)	ΔEL (%)	ΔTS (MPa)	ΔYP (MPa)	ΔEL (%)	Type	Note
1	A	624	33.1	20654	10	18	2.4	7	12	1.8	CR	Example
2	A	628	32.6	20473	11	19	2.8	7	12	2.0	GI	Example
3	A	609	33.2	20219	8	17	2.2	6	11	1.8	GA	Example
4	A	632	32.1	20287	13	16	2.0	9	14	1.6	GA	Example
5	A	607	37.2	22580	8	13	2.2	6	11	2.0	GA	Example
6	A	617	32.8	20238	10	14	2.4	8	13	2.2	GA	Example
7	B	612	33.4	20441	14	16	2.2	15	16	2.0	GA	Example
8	C	798	26.7	21307	19	20	2.4	18	21	2.2	GA	Example
9	A	610	33.4	20374	10	17	2.2	11	18	2.0	GI	Example
10	B	622	33.2	20650	15	16	2.2	11	16	1.4	CR	Example
11	B	618	33.1	20456	14	14	2.2	10	15	1.6	GI	Example
12	B	603	33.4	20140	13	13	2.4	10	15	1.4	GA	Example
13	C	808	25.8	20846	18	19	2.4	15	20	1.6	CR	Example
14	C	806	25.4	20472	17	19	2.6	16	21	1.9	GI	Example
15	C	786	26.4	20750	19	18	2.6	12	17	1.8	GA	Example
16	D	1012	19.1	19329	22	20	2.4	20	25	1.7	CR	Example
17	D	1008	19.4	19555	23	22	2.4	21	26	1.5	GI	Example
18	D	992	20.3	20138	21	20	2.0	20	25	1.9	GA	Example
19	A	602	26.8	16134	38	48	4.4	31	41	3.8	GA	Comparative
												Example
20	A	607	26.9	16328	42	46	4.6	34	44	3.7	GI	Comparative
												Example
21	A	608	26.3	15990	22	29	3.2	14	22	2.2	GI	Comparative
												Example
22	A	614	26.7	16394	23	28	3.3	15	23	2.1	GA	Comparative
												Example
23	A	521	33.7	17558	24	31	3.1	18	28	2.0	CR	Comparative
												Example
24	A	648	30.1	19505	41	47	4.6	31	41	3.7	GA	Comparative
												Example
25	A	630	32.4	20412	10	13	1.8	6	11	2.0	GI	Example
26	E	618	33.1	20456	10	15	2.4	7	12	1.8	CR	Example
27	F	620	33.2	20584	9	15	2.6	7	12	1.7	GI	Example
28	G	614	33.4	20508	11	13	2.4	6	11	1.5	GA	Example
29	H	610	33.0	20130	11	13	2.2	7	12	1.4	CR	Example
30	I	613	33.4	20474	10	12	2.0	6	11	1.2	GI	Example
31	J	614	33.7	20692	10	14	2.2	8	13	1.6	GA	Example
32	K	619	33.8	20922	9	13	2.2	9	14	1.8	CR	Example
33	L	502	32.4	16265	22	24	2.8	10	15	2.6	CR	Comparative
												Example
34	M	605	27.4	16577	44	43	4.6	32	41	3.9	GI	Comparative
												Example
35	N	762	25.1	19126	52	50	4.4	41	46	4.0	GA	Comparative
												Example

In the case of the examples of the present invention, the hot rolled steel sheets for a cold rolled steel sheet and the hot rolled steel sheets for a galvanized steel sheet had a TS of 540 MPa or more after the following annealing had been performed and were excellent in terms of ductility and stability of material quality. On the other hand, the comparative examples were poor in one or more of strength, ductility, and stability of material quality.

According to the present invention, a hot rolled steel sheet for a cold rolled steel sheet end a hot rolled steel sheet for a galvanized steel sheet excellent in terms of formability and stability of material quality can be obtained. A cold rolled steel sheet and a galvanized steel sheet which are produced from the hot rolled steel sheet according to the present invention can be applied, for example, to the structural parts of automobiles.

Claims

1. A method for producing a hot rolled steel sheet for cold rolling, the method comprising: hot rolling a steel slab having a chemical composition containing, by mass %, C: 0.04% or more and 0.20% or less, Si: 0.7% or more and 2.3% or less, Mn: 0.8% or more and 2.8% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities under the condition that a finish rolling delivery temperature is 850° C. or higher;cooling the hot rolled steel sheet at a first mean cooling rate of 20° C./s to 45.5° C./s in a temperature range from the finish rolling delivery temperature to 650° C.;subsequently, further cooling the hot rolled steel sheet at a second mean cooling rate of 5° C./s to 35° C./s in a temperature range from 650° C. down to a coiling temperature; andcoiling the cooled steel sheet at a temperature of 470° C. to 640° C.;wherein the first mean cooling rate is higher than the second mean cooling rate, andwherein an area ratio of a microstructure of the cooled steel sheet includes 75% or more and less than 95% of ferrite.

2. The method for producing a hot rolled steel sheet for cold rolling according to claim 1, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Cr: 0.05% or more and 1.0% or less, V: 0.005% or more and 0.5% or less, Mo: 0.005% or more and 0.5% or less, Ni: 0.05% or more and 1.0% or less, and Cu: 0.05% or more and 1.0% or less.

3. The method for producing a hot rolled steel sheet for cold rolling according to claim 1, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less, and B: 0.0003% or more and 0.0050% or less.

4. The method for producing a hot rolled steel sheet for cold rolling according to claim 1, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

5. The method for producing a hot rolled steel sheet for cold rolling according to claim 3, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

6. A method for producing a hot rolled steel sheet for galvanizing, the method comprising: hot rolling a steel slab having a chemical composition containing, by mass %, C: 0.04% or more and 0.20% or less, Si: 0.7% or more and 2.3% or less, Mn: 0.8% or more and 2.8% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities under the condition that a finish rolling delivery temperature is 850° C. or higher;cooling the hot rolled steel sheet at a first mean cooling rate of 20° C./s to 45.5° C./s in a temperature range from the finish rolling delivery temperature to 650° C.;subsequently, further cooling the hot rolled steel sheet at a second mean cooling rate of 5° C./s to 35° C./s in a temperature range from 650° C. down to a coiling temperature; andcoiling the cooled steel sheet at a temperature of 470° C. to 640° C.;wherein the first mean cooling rate is higher than the second mean cooling rate, andwherein an area ratio of a microstructure of the cooled steel sheet includes 75% or more and less than 95% of ferrite.

7. The method for producing a hot rolled steel sheet for galvanizing according to claim 6, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Cr: 0.05% or more and 1.0% or less, V: 0.005% or more and 0.5% or less, Mo: 0.005% or more and 0.5% or less, Ni: 0.05% or more and 1.0% or less, and Cu: 0.05% or more and 1.0% or less.

8. The method for producing a hot rolled steel sheet for galvanizing according to claim 6, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less, and B: 0.0003% or more and 0.0050% or less.

9. The method for producing a hot rolled steel sheet for galvanizing according to claim 6, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

10. The method for producing a hot rolled steel sheet for galvanizing according to claim 8, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

11. The method for producing a hot rolled steel sheet for cold rolling according to claim 2, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less, and B: 0.0003% or more and 0.0050% or less.

12. The method for producing a hot rolled steel sheet for cold rolling according to claim 2, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

13. The method for producing a hot rolled steel sheet for cold rolling according to claim 11, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

14. The method for producing a hot rolled steel sheet for galvanizing according to claim 7, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ti: 0.01% or more and 0.1% or less, Nb: 0.01% or more and 0.1% or less, and B: 0.0003% or more and 0.0050% or less.

15. The method for producing a hot rolled steel sheet for galvanizing according to claim 7, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

16. The method for producing a hot rolled steel sheet for galvanizing according to claim 14, wherein the steel slab further contains, by mass %, at least one element selected from the group consisting of Ca: 0.001% or more and 0.005% or less and REM: 0.001% or more and 0.005% or less.

17. The method for producing a hot rolled steel sheet for cold rolling according to claim 1, wherein the chemical composition contains, by mass %, C: 0.04% or more and 0.093% or less.