Patent Application
20100279042
1. Technical Field
The present disclosure generally relates to housings and, particularly, to a housing for a portable electronic device and a method of manufacturing the housing.
2. Description of Related Art
Electronic devices such as notebook computers, MP3 players, personal digital assistants, and mobile phones are in common use. A pleasing appearance and finish, such as a metallic finish, are often important to users.
Accordingly, textured patterns or stripes are often formed on the exterior housing of such devices. Hair lines are commonly formed on metallic housings of materials such as magnesium alloy, aluminum, and stainless steel. However, such metallic housings are difficult to manufacture and at a high cost. Plastic housings are easily manufactured by injection molding and have a low cost, but lack the appeal of the metallic appearance and texturing which can be difficult to directly form on the plastic housing.
Therefore, what is needed, is a housing that overcomes the limitations described.
The components in the drawing is not necessarily drawn to scale, the emphasis instead being placed upon clearly illustrating the principles of the present disclosure.
Referring to
The metallic base 11 may be magnesium alloy, aluminum alloy, or any other metal.
The chemical plating layer 12 protects the metallic base 11 from oxidation, and improves coating performance of the metallic base 11. The chemical plating layer 12 may be mainly phosphate.
The prime layer 13 further protects the metallic base 11 from oxidation and corrosion. In the illustrated embodiment, the prime layer 13 includes a connecting layer 132 adjacent to the chemical plating layer 12, and a shielding layer 134 coated on the connecting layer 132.
The connecting layer 132 masks surface defects of the metallic base 11, and enhances bonding between the chemical plating layer 12 and the shielding layer 134. The connecting layer 132 may include polyester resin, epoxy resin, and pigments dispersed therein. The pigments may be carbon black, exhibiting favorable absorption of laser energy. The thickness of the connecting layer 132 may be about 25 micrometers (μm) to about 50 μm.
The shielding layer 134 further masks surface defects of the metallic base 11. The shielding layer 134 may include acrylic resin, polyester resin, epoxy resin, amino resin, acrylate copolymer, propylene glycol methyl ether acetate (PMA), butyl ester, and pigments dispersed therein. The pigments may be carbon black, exhibiting favorable absorption of laser energy. The thickness of the shielding layer 134 may be about 15 μm to about 20 μm.
The color coating layer 14 normalizes the surface of the metallic base 11 and provides a background color to the pattern 17. The color coating layer 14 may include acrylic resin, polyester resin, epoxy resin, amino resin, acrylate copolymer, PMA, butyl ester, and pigments dispersed therein. The pigments may be any desired color. The thickness of the color coating layer 14 may be about 15 μm to about 80 μm.
The decorative layer 15 may include acrylic resin, polyester resin, epoxy resin, amino resin, acrylate copolymer, PMA, butyl ester, pigments and aluminum oxide powder dispersed therein. The pigments and the aluminum oxide powder may be in a nanometer scale. The aluminum oxide powder provides metallic luster to the housing 10, and generates a light reflection effect to provide the pattern 17 with a stereoscopic appearance. The thickness of the decorative layer 15 may be about 2 μm to about 7 μm.
The pattern 17 is defined in the decorative layer 15 via laser engraving. In the illustrated embodiment, the pattern 17 extends through the decorative layer 15 to the color coating layer 14. Thus, the pattern 17 shows the color of the color coating layer 14. Alternatively, the pattern 17 may extend through the decorative layer 15 and the color coating layer 14 to the prime layer 13. Thus, the pattern 17 may show the color of the connecting layer 132 or the color of the shielding layer 134.
The transparent protection layer 16 protects the decorative layer 15 and the pattern 17 from abrasion, and improves glossiness of the housing 10. The transparent protection layer 16 may include acrylic resin, polyester resin, epoxy resin, amino resin, silicon dioxide, acrylate copolymer, PMA, and butyl ester. Thickness of the transparent protection layer 16 may be about 20 μm to about 80 μm.
Because the pattern 17 extends through the decorative layer 15 and shows the color of the color coating layer 14, when viewed from the front, the pattern 17 shows a color different from the decorative layer 15, thus the pattern 17 is conspicuously defined in the decorative layer 15. At the same time, the decorative layer 15 provides metallic luster to the housing 10, and generates a light reflection effect to enable the pattern 17 to exhibit a stereoscopic appearance. When viewed from the side, the pattern 17 may show changed color, due to the light reflection of the decorative layer 15 and the light refraction of the transparent protection layer 16.
In alternative embodiments, if the metallic base 11 has minimal surface defects, the connecting layer 132 or the shielding layer 134 may be omitted.
Referring to
The metallic base 11 may be manufactured by casting, forging, or extrusion molding.
The metallic base 11 is submerged in a chemical solution, such as a phosphate solution, forming the chemical plating layer 12 on a surface thereof.
The prime layer 13 is coated on the chemical plating layer 12. The prime layer 13 includes the connecting layer 132 and the shielding layer 134. A connecting coating is coated on the chemical plating layer 12 and dried, thereby forming the connecting layer 132. A shielding coating is then coated on the connecting layer 132 and dried, thereby forming the shielding layer 134. The connecting coating may include polyester resin, epoxy resin, and pigments dispersed therein. The connecting coating may be coated on the chemical plating layer 12 by spray coating. A drying temperature of the connecting coating is about 150 degrees Celsius (° C.) to about 200° C. A drying time of the connecting coating is about 10 minutes to about 30 minutes. The shielding coating may include acrylic resin, polyester resin, epoxy resin, amino resin, acrylate copolymer, PMA, butyl ester, and pigments dispersed therein. The shielding coating may be coated on the connecting layer 132 by spray coating. A drying temperature of the shielding coating is about 130° C. to about 180° C. A drying time of the shielding coating is about 10 minutes to about 30 minutes.
A color coating is coated on the shielding layer 134 and dried, thereby forming the color coating layer 14. The color coating may include acrylic resin, polyester resin, epoxy resin, amino resin, acrylate copolymer, PMA, butyl ester, and pigments dispersed therein. The color coating may be coated on the shielding layer 134 by spray coating. A drying temperature of the color coating is about 50° C. to about 180° C. A drying time of the color coating is about 10 minutes to about 30 minutes.
A decorative coating is coated on the color coating layer 14 and dried, thereby forming the decorative layer 15. The decorative coating may include acrylic resin, polyester resin, epoxy resin, amino resin, acrylate copolymer, PMA, butyl ester, pigments and aluminum oxide powder dispersed therein. The decorative coating may be coated on the color coating layer 14 by spray coating. A drying temperature of the decorative coating is about 50° C. to about 180° C. A drying time of the decorative coating is about 10 minutes to about 30 minutes.
The metallic base 11 is received in a laser engraver, and predetermined regions of the decorative layer 15 are engraved. The materials of the decorative layer 15 at the predetermined regions disintegrate due to the energy of the laser, thus defining the pattern 17 in the decorative layer 15. The power of the laser is adjusted to enable the pattern 17 to extend through the decorative layer 15.
A transparent coating is coated on the decorative layer 15 and dried, thereby forming the transparent protection layer 16. The transparent coating may include acrylic resin, polyester resin, epoxy resin, amino resin, silicon dioxide, acrylate copolymer, PMA, and butyl ester. The transparent coating may be coated on the decorative layer 15 by spray coating. A drying temperature of the transparent coating is about 50° C. to about 180° C. A drying time of the transparent coating is about 10 minutes to about 30 minutes.
Alternatively, the connecting layer 132 may be omitted, and the shielding layer 134 directly coated on the chemical plating layer 12, or shielding layer 134 may be omitted, and the color coating layer 14 directly coated on the connecting layer 132.
In one embodiment of the method of manufacturing a housing 10, a metallic base 11 is cast of magnesium alloy, and then submerged in a phosphate solution to form a chemical plating layer 12. A connecting coating is coated on the chemical plating layer 12 and dried for about 30 minutes, at about 150° C., thus forming a connecting layer 132 about 50 μm thick. A color coating is coated on the connecting layer 132 and dried for about 15 minutes, at about 100° C., thus forming a color coating layer 14 about 15 μm thick. A decorative coating is coated on the color coating layer 14 and dried for about 30 minutes, at about 50° C., thus forming the decorative layer 15 about 5 μm thick. A laser is irradiated on the predetermined regions of the decorative layer 15, thus defining a pattern 17 extending through the decorative layer 15. Finally, a transparent coating is coated on the decorative layer 15 and dried for about 10 minutes, at about 180° C., thus forming a transparent protection layer 16 about 50 μm thick.
In another embodiment of the method of manufacturing a housing 10, a metallic base 11 is forged of aluminum alloy. The metallic base 11 is then submerged in a phosphate solution to form a chemical plating layer 12. A shielding coating is coated on the chemical plating layer 12 and dried for about 10 minutes, at about 180° C., thus forming a shielding layer 134 about 15 μm thick. A color coating is coated on the shielding layer 134 and dried for about 30 minutes, at about 50° C., thus forming a color coating layer 14 about 80 μm thick. A decorative coating is coated on the color coating layer 14 and dried for about 10 minutes, at about 100° C., thus forming a decorative layer 15 about 7 μm thick. A laser is irradiated on the predetermined regions of the decorative layer 15, thus defining a pattern 17 extending through the decorative layer 15. Finally, a transparent coating is coated on the decorative layer 15 and dried for about 30 minutes, at about 50° C., thus forming a transparent protection layer 16 about 80 μm thick.
In yet another embodiment of the method of manufacturing a housing 10, a metallic base 11 is cast of magnesium alloy and then submerged in a phosphate solution to form a chemical plating layer 12. A connecting coating is coated on the chemical plating layer 12 and dried for about 10 minutes, at about 200° C., thus forming a connecting layer 132 about 25 μm thick. A shielding coating is coated on the connecting layer 132 and dried for about 30 minutes, at about 130° C., thus forming a shielding layer 134 about 20 μm thick. A color coating is coated on the shielding layer 134 and dried for about 10 minutes, at about 180° C., thus forming a color coating layer 14 about 30 μm thick. A decorative coating is coated on the color coating layer 14 and dried for about 15 minutes, at about 180° C., thus forming a decorative layer 15 about 2 μm thick. A laser is irradiated on the predetermined regions of the decorative layer 15, thus defining a pattern 17 extending through the decorative layer 15. Finally, a transparent coating is coated on the decorative layer 15 and dried for about 15 minutes, at about 100° C., thus forming a transparent protection layer 16 about 20 μm thick.
It is believed that the present embodiments and their advantages will be understood from the foregoing description, and it will be apparent that various changes may be made thereto without departing from the spirit and scope of the disclosure or sacrificing all of its material advantages.