Patent Application
20100266793
1. Technical Field
The disclosure relates to a housing and, particularly, to a housing for an electronic device.
2. Description of the Related Art
Electronic devices such as notebook computers, MP3 players, personal digital assistants, and mobile phones, are in common use. A pleasing appearance and finish, such as a metallic finish, are often important to users.
Accordingly, textured patterns or stripes are often formed on the exterior housing of such devices. Hair lines are commonly formed on metallic housings of materials such as magnesium alloy, aluminum, and stainless steel. However, such metallic housings are difficult to manufacture and at a high cost. Plastic housings are easily manufactured by injection molding and have a low cost, but lack the appeal of the metallic finish and texturing which can be difficult to directly form on the plastic housing.
Therefore, what is needed, is a housing that overcomes the limitations described.
The components in the drawing are not necessarily drawn to scale, the emphasis instead being placed upon clearly illustrating the principles of the present disclosure.
Referring to
The housing 10 may be a front cover, a back cover, a foldable cover or a slidable cover employed in many types of electronic devices.
The substrate 11 may be acrylonitrile butadiene styrene (ABS), polycarbonate (PC), polyphenylene sulfide (PPS), or any suitable combination thereof.
The supporting layer 13 can improve a hardness and a flatness of the substrate 11. The supporting layer 13 includes a prime layer 132 adjacent to the substrate 11, and an enhancing coating layer 134 formed on the prime layer 132.
The prime layer 132 enhances a bonding strength between the substrate 11 and the enhancing coating layer 134. The prime layer 132 may consist essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, black pigments, ethylene-acrylate copolymer, propylene glycol monomethyl ether acetate (PMA), and butyl ester. The black pigments may be carbon black. A thickness of the prime layer 132 may be from about 25 micrometers (μm) to about 50 μm. Defects formed on the substrate 11 such as pits and thin grooves during injection molding are masked by the prime layer 132, thus the flatness of the substrate 11 is improved.
The enhancing coating layer 134 has a relatively high hardness and may consist essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, pigments, ethylene-acrylate copolymer, PMA, and butyl ester. The enhancing coating layer 134 may further improve hardness and flatness of the substrate 11. A thickness of the enhancing coating layer 134 may be from about 15 μm to about 80 μm.
The hair line layer 15 is formed on the enhancing coating layer 134.
The decorative layer 17 may be a metallic coating layer in colors such as silver, gold, or other decorative finishes, achieving a metallic hair line layer 15. The decorative layer 17 may consist essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, ethylene-acrylate copolymer, PMA, butyl ester, and nano-aluminum oxide powder or nano-aluminum oxide flakes. In the illustrated embodiment, the decorative layer 17 consists essentially of acrylic resin and nano Al2O3 powder. A thickness of the decorative layer 17 may be from about 2 μm to about 7 μm.
The transparent protection layer 19 may consist essentially of acrylic resin and silicon oxide, and has a high bonding strength with the decorative layer 17. A thickness of the transparent protection layer 19 may be from about 20 μm to about 80 μm.
The substrate 11, as a main portion of the housing 10, is made of plastic material, thus the housing 10 is much cheaper than a metallic housing. The hair line layer 15 presents a pleasing metallic finish because the decorative layer 17 is a metallic enhancing coating layer.
It should be noted that if the substrate 11 has a good uniformity and hardness, the enhancing coating layer 134 may be omitted. In such a case, the hair line layer 15 is directly formed on the prime layer 132.
It should also be noted that if the substrate 11 has a good uniformity and a bonding strength between the substrate 11, and the enhancing coating layer 134 is sufficient, the prime layer 132 may be omitted.
Referring to
Beginning in step S201, a plastic substrate 11 is formed by injection molding.
In step S202, the supporting layer 13 is formed on the substrate 11, as follows. Primer is brushed on the substrate 11 and dried, such that the primer layer 132 is formed. Prime coating of the substrate 11 can be accomplished by spray coating. The primer may consist essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, black pigments, ethylene-acrylate copolymer, PMA, and butyl ester. The black pigments may be carbon black. The primer is dried at from about 50 degrees Celsius (° C.) to about 100° C., for about 10 minutes to 30 about minutes. An enhancing lacquer is coated on the primer layer 132, and may consist essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, pigments, ethylene-acrylate copolymer, PMA, and butyl ester. When the enhancing lacquer is dried, the enhancing coating layer 134 is formed on the primer layer 132. The enhancing laquer is dried at from about 50° C. to about 100° C., for about 10 minutes to about 30 minutes.
In step S203, the enhancing coating layer 134 is ground with a grinding wheel, so that a portion of the enhancing coating layer 134 forms the hair line layer 15. The grinding wheel may be made of cloth.
In step S204, a metallic color coating is coated on the hair line layer 15 and dried, thereby forming the decorative layer 17. The metallic color coating may consist essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, ethylene-acrylate copolymer, PMA, butyl ester, and nano-aluminum oxide powder or nano-aluminum oxide flakes. A thickness of the decorative layer 17 may be about 2 μm to about 7 μm. A method of coating the metallic color coating on the hair line layer 15 may be accomplished by spray coating. The dried temperature is from about 50° C. to about 100° C., the dried time is from about 10 minutes to about 30 minutes.
In step S205, a transparent coating is coated on the decorative layer 17 and dried, thereby forming a transparent protection layer 19. The transparent coating may consist essentially of acrylic resin and silicon oxide. The transparent coating can be spray coated on the decorative layer 17. The drying temperature is from about 50° C. to about 100° C., for about 10 minutes to about 30 minutes.
It may be noted that if the substrate 11 has a good uniformity and hardness, formation of the enhancing coating layer 134 in step S202 may be omitted.
It should also be noted that if the substrate 11 has a good uniformity and a bonding strength between the substrate 11 and the enhancing coating layer 134 is sufficient, formation of the prime layer 132 in step S202 may be omitted.
In one embodiment of a method of manufacturing a housing, a substrate is injection molded with a plastic material including ABS. A primer, coated on the substrate, consists essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, black pigments, ethylene-acrylate copolymer, PMA, and butyl ester. The primer coated on the substrate is dried for about 10 minutes to about 30 minutes at from about 50° C. to about 100° C., thereby forming a prime layer having a thickness of about 25 μm to about 50 μm. The prime layer may be ground with a grinding wheel, such that a portion of the prime layer forms a hair line layer. A metallic color coating, coated on the hair line layer, consists essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, ethylene-acrylate copolymer, PMA, butyl ester, and nano-aluminum oxide powder or nano-aluminum oxide flakes. The metallic color coating is dried for about 10 minutes to about 30 minutes at about 50° C. to about 100° C., thereby forming a decorative layer having a thickness of about 2 μm to about 7 μm. A transparent coating consisting essentially of acrylic resin and silicon oxide is coated on the decorative layer. The transparent coating is dried for about 10 minutes to about 30 minutes at about 50° C. to about 100° C., thereby forming a transparent protection layer having a thickness of about 20 μm to about 80 μm. The housing is thus complete.
In another embodiment of a method of manufacturing a housing, a substrate is injection molded of plastic material including PC. An enhancing lacquer, coated on the substrate, consists essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, pigments, ethylene-acrylate copolymer, PMA, and butyl ester. The enhancing lacquer coated on the substrate is dried for about 10 minutes to about 30 minutes at about 50° C. to about 100° C., thereby forming an enhancing coating layer having a thickness of about 25 μm to about 50 μm. The enhancing coating layer may be ground with a grinding wheel, such that a portion of the enhancing coating layer forms a hair line layer. A metallic color coating, coated on the hair line layer, consists essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, ethylene-acrylate copolymer, PMA, butyl ester, and nano-aluminum oxide powder or nano-aluminum oxide flakes. The metallic color coating is dried for about 10 minutes to about 30 minutes at about 50° C. to about 100° C., thereby forming a decorative layer having a thickness of about 2 μm to about 7 μm. A transparent coating consisting essentially of acrylic resin and silicon oxide is coated on the decorative layer. The transparent coating is dried for about 10 minutes to about 30 minutes at about 50° C. to about 100° C., thereby forming a transparent protection layer having a thickness of about 20 μm to about 80 μm. The housing is thus complete.
In yet another embodiment of a method of manufacturing a housing, a substrate is injection molded of a plastic material including ABS and PC. A primer, coated on the substrate, consists essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, black pigments, ethylene-acrylate copolymer, propylene glycol monomethyl ether acetate(PMA), and butyl ester is. The primer coated on the substrate is dried for about 10 minutes to about 30 minutes at about 50° C. to about 100° C., thereby forming a prime layer having a thickness of about 25 μm to about 50 μm. An enhancing lacquer, coated on the prime layer, consists essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, pigments, ethylene-acrylate copolymer, PMA, and butyl ester. The enhancing lacquer coated on the prime layer is dried for about 10 minutes to about 30 minutes at about 50° C. to about 100° C., thereby forming an enhancing coating layer having a thickness of minutes 25 μm to minutes 50 μm. The enhancing coating layer may be ground with a grinding wheel, such that a portion of the enhancing coating layer forms a hair line layer. A metallic color coating, coated on a hair line layer, consists essentially of acrylic resin, polyester resin, epoxy resin, amidocyanogen resin, ethylene-acrylate copolymer, PMA, butyl ester, and nano-aluminum oxide powder or nano-aluminum oxide flakes. The metallic color coating is dried for about 10 minutes to about 30 minutes at about 50° C. to about 100° C., thereby forming a decorative layer having a thickness of about 2 μm to about 7 μm. A transparent coating consisting essentially of acrylic resin and silicon oxide is coated on the decorative layer. The transparent coating is dried for about 10 minutes to about 30 minutes at about 50° C. to about 100° C., thereby forming a transparent protection layer having a thickness of about 20 μm to about 80 μm. The housing is thus complete.
A bonding strength of samples of the housing was evaluated after the transparent protection layer was formed. Bonding strengths of the samples of the housing were from about 4 B to about 3 B.
A pencil hardness of the samples of the housing was evaluated with a pencil after the transparent protection layer was formed. A pencil was applied on the surface of the housing at an angle of 45° with a force of 9.8 Newtons. The pencil hardness of the samples of the housing was from about 1 H to about 2 H.
A solvent resistance of the samples the housing was evaluated with a solvent resistance test after the transparent protection layer was formed. The housing was wiped 50 times according to the standard of ASTM (The American Society for Testing and Materials) D4752, and a resistance grade of the housing is 4.
An abrasion resistance of the samples the housing was evaluated with a Norman Abrasion test after the transparent protection layer was formed. When a force of 175 g gravity was used to polish the housing, no fish eyes or ripples appeared on the surface of the housing.
The test result shows that the housing has relatively high bonding strength, high solvent resistance, high hardness, and high abrasion resistance.
Finally, while various embodiments have been described and illustrated, the embodiments are not to be construed as being limited thereto. Various modifications can be made to the embodiments by those skilled in the art without departing from the true spirit and scope of the invention as defined by the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 200910301608.7 | Apr 2009 | CN | national |