HUMIDITY SENSOR

Abstract

Humidity sensors may exhibit a relatively small amount of hysteresis and/or a faster response time. In some cases, a humidity sensor may include a polymeric humidity sensing layer disposed over an electrode layer. The polymeric humidity sensing layer may include a halogenated layer disposed over the polymeric humidity sensing layer. The polymeric humidity sensing layer may, for example, include a polyimide and the halogenated layer may include a monolayer or less than a monolayer of a halogenated material such as a fluorinated material.

Description

BACKGROUND

Capacitive and resistive type humidity sensors rely on the ability of the sensing material to quickly absorb and desorb water molecules. The absorbed moisture changes the physical properties of the sensing material either by changing its resistance, permittivity, or stress, which can each directly affect the electrical response of the sensor. Bulk polyimide films are often used as the humidity sensing material in many capacitive and resistive humidity sensors. However, humidity sensors using bulk polyimide films typically exhibit an inherent hysteresis due to the adsorption, absorption, diffusion, and desorption properties of the films. Also, such sensors often have a relatively large response time. What would be desirable is a humidity sensor that exhibits a relatively small amount of hysteresis (e.g. 2 Sigma hysteresis of 1% or less) and/or a faster response time.

SUMMARY

The disclosure generally relates to humidity sensors that exhibit a relatively small amount of hysteresis and/or a faster response time. In some cases, a humidity sensor may include a polymeric humidity sensing layer disposed over an electrode layer. The polymeric humidity sensing layer may include a halogenated layer disposed over the polymeric humidity sensing layer. In some instances, the polymeric humidity sensing layer may, for example, include a polyimide and the halogenated layer may include a monolayer or less than a monolayer of a halogenated material such as a fluorinated material.

In a particular example of the disclosure, a humidity sensor may include a substrate and an electrode layer that is supported by the substrate. In some cases, the electrode layer may define a first capacitive plate and a second capacitive plate. A non-halogenated humidity sensing layer may be disposed adjacent the electrode layer and may include a number of openings to increase an effective surface area of the non-halogenated humidity sensing layer. A halogenated layer may adjoin the non-halogenated humidity sensing layer.

In another example of the disclosure, a humidity sensor may include a substrate and an electrode layer that is supported by the substrate. In some cases, the electrode layer may define a first capacitive plate and a second capacitive plate. A polyimide humidity sensing layer may be disposed adjacent the electrode layer. In some instances, the polyimide humidity sensing layer includes a sensing surface and a thickness, and includes a number of openings formed within the sensing surface to increase an effective surface area of the sensing surface. In some cases, the sensing surface of the polyimide humidity sensing layer may be fluorinated to a depth that is less than the thickness of the polyimide humidity sensing layer, resulting in a fluorinated sensing surface.

In another example of the disclosure, a method of manufacturing a humidity sensor may include forming an electrode layer over a substrate. A non-halogenated polymeric material may be disposed over the electrode layer as a humidity sensing material. With the non-halogenated polymeric material disposed over the electrode layer, the non-halogenated polymeric material may be hydrogenated to increase the non-halogenated polymeric material's resistance to humidity sensing hysteresis.

The above summary of some embodiments is not intended to describe each disclosed embodiment or every implementation of the present disclosure. The Figures, and Detailed Description, which follow, more particularly exemplify some of these embodiments.

BRIEF DESCRIPTION OF THE FIGURES

The disclosure may be more completely understood in consideration of the following detailed description in connection with the accompanying drawings, in which:

FIG. 1 is a schematic cross-sectional side view of an illustrative humidity sensor in accordance with an embodiment of the disclosure;

FIG. 2 is a cross-sectional side view of an illustrative humidity sensor in accordance with an embodiment of the disclosure;

FIG. 3 is a top view of a plate-type humidity sensor, with the humidity sensing material not shown to reveal the electrodes;

FIG. 4 is a schematic cross-sectional side view of the humidity sensor of FIG. 3 taken along line A-A′, showing the humidity sensing material;

FIG. 5 is a schematic cross-sectional side view of the humidity sensor of FIG. 3 taken along line A-A′, after additional processing of the humidity sensing material;

FIG. 6 is a top view of the humidity sensor of FIG. 5;

FIG. 7 is an alternate top view of the humidity sensor of FIG. 5;

FIG. 8 is a top view of an interdigitated humidity sensor;

FIG. 9 is a schematic cross-sectional side view of the humidity sensor of FIG. 8 take along line B-B′;

FIG. 10 is an enlarged cross-sectional side view of a portion of FIG. 9 after additional processing of the humidity sensing material; and

FIG. 11 is a flow diagram illustrating an illustrative method for making a humidity sensor.

While the disclosure is amenable to various modifications and alternative forms, specifics thereof have been shown by way of example in the drawings and will be described in detail. It should be understood, however, that the intention is not to limit the disclosure to the particular embodiments described. On the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the disclosure.

DESCRIPTION

For the following defined terms, these definitions shall be applied, unless a different definition is given in the claims or elsewhere in this specification.

All numeric values are herein assumed to be modified by the term “about,” whether or not explicitly indicated. The term “about” generally refers to a range of numbers that one of skill in the art would consider equivalent to the recited value (i.e., having the same function or result). In many instances, the terms “about” may include numbers that are rounded to the nearest significant figure.

The recitation of numerical ranges by endpoints includes all numbers within that range (e.g. 1 to 5 includes 1, 1.5, 2, 2.75, 3, 3.80, 4, and 5).

As used in this specification and the appended claims, the singular forms “a”, “an”, and “the” include plural referents unless the content clearly dictates otherwise. As used in this specification and the appended claims, the term “or” is generally employed in its sense including “and/or” unless the content clearly dictates otherwise.

It is noted that references in the specification to “an embodiment”, “some embodiments”, “other embodiments”, etc., indicate that the embodiment described may include one or more particular features, structures, and/or characteristics. However, such recitations do not necessarily mean that all embodiments include the particular features, structures, and/or characteristics. Additionally, when particular features, structures, and/or characteristics are described in connection with one embodiment, it should be understood that such features, structures, and/or characteristics may also be used connection with other embodiments whether or not explicitly described unless clearly stated to the contrary.

The following detailed description should be read with reference to the drawings in which similar structures in different drawings are numbered the same. The drawings, which are not necessarily to scale, depict illustrative embodiments and are not intended to limit the scope of the disclosure. FIG. 1 is a schematic cross-sectional side view of an illustrative humidity sensor 10, showing particular features of the humidity sensor 10. The illustrative humidity sensor 10 includes a substrate 12, which in some instances may be a silicon substrate, although other substrates may be used. The illustrative humidity sensor 10 includes an electrode layer 14. As drawn, the humidity sensor 10 is a plate-style humidity sensor in which the electrode layer 14 includes a pair of capacitive plates 14a and 14b. In some cases, however, the humidity sensor 10 may be an interdigitated style humidity sensor in which the electrode layer includes a pair of interdigitated electrodes, or any other suitable humidity sensor configuration as desired.

The illustrative humidity sensor 10 further includes a humidity sensing material 16 that in some cases may include a first layer 18 and a second layer 20. In some cases, the first layer 18 may be a polymer such as but not limited to a polyimide, a parylene, a benzocyclobutene, and divinylsiloxane bis(benzocyclobutene). In some cases, the first layer 18 may be a polyimide and the second layer 20 may be a halogenated layer that is deposited onto the first layer 18. In some cases, the second layer 20 may be a fluorinated layer, although other halogens such as chlorine and bromine may also be used.

In some cases, the second layer 20 may not be a separate layer, but may instead represent a fluorination of at least part of an outer surface of the first layer 18. In some instances, for example, the humidity sensing layer 16 may include a sensing surface 22 and an overall thickness that is indicated on FIG. 1 as a dimension D₁. The second layer 20 may represent a halogenated portion of the first layer 18, and may have a thickness (or perhaps thought of as a halogenation depth) that is indicated as a dimension D₂. In some cases, the second layer 20 may represent a portion of the first layer 18 that has been fluorinated to a depth D₂ that is less than the thickness D₁ of the first layer 18.

In some cases, the second layer 20, representing a halogenation such as fluorination of the sensing surface, may be considered as forming a mono-layer or in some cases a partial mono-layer of the halogen such as fluorine. In some cases, the sensing surface 22 may, for example, be fluorinated by plasma deposition of C_xH_yF_z onto the polyimide humidity sensing layer 16, where x is an integer ranging from 1 to 4, y is an integer ranging from 0 to 2 and z is an integer ranging from 2 to 8. In some instances, the sensing surface 22 may be fluorinated via plasma deposition of one or more of CF₄, C₂F₆, C₄F₈, CHF₃ and CH₂F₂. In some cases, there may be some displacement of hydrogen within the sensing surface 22. In some cases, particularly during plasma deposition of C_xH_yF_z, there may be deposition of a heterogeneous mixture of fluorocarbons and hydrofluorocarbons on the sensing surface 22.

FIG. 2 is a side view of an illustrative humidity sensor 50. As illustrated, the humidity sensor 50 is a plate-style humidity sensor. The illustrative humidity sensor 50 includes a substrate 52 and a dielectric layer 54 disposed on the substrate 52. In some cases, the substrate 52 may be silicon and the dielectric layer 54 may, for example, be SiO₂. A porous platinum layer 56 forms a common plate that is shared by two series capacitors CX1 and CX2. Layer 58 is a patterned layer that forms the other plates of capacitors CX1 and CX2. For example, layer 58 may be patterned as illustrated in FIG. 3 to form a capacitor plate 58A for capacitor CX1 and a separate capacitor plate 58B for capacitor CX2. Capacitor plate 58A may be electrically connected to gold pad 64A and capacitor plate 58B may be electrically connected to gold pad 64B. In some cases, the layer 58 may be a titanium tungsten alloy. A passivation layer 60 may be formed over the porous platinum layer 56, and may be a polyimide, for example. A dielectric layer 62 is provided between the porous platinum layer 56 and the titanium tungsten alloy layer 58 and in some cases functions as the humidity sensing layer. The dielectric layer 62 may be halogenated or include a halogenated layer such as a fluorinated layer. Gold pads 64A and 64B permit electrical connections to be made to the humidity sensor 50.

FIGS. 3 through 10 provide additional examples of humidity sensors. FIG. 3 is a top view of a plate-type humidity sensor 30, with the humidity sensing material not shown to reveal the electrode layer 14, while FIG. 4 is a schematic cross-sectional side view of the humidity sensor of FIG. 3 taken along line A-A′, illustrating a sequence of the substrate 12, the electrode layer 14 and the humidity sensing material 16. FIG. 5 is a schematic cross-sectional side view of the humidity sensor of FIG. 3 taken along line A-A′, after additional processing of the humidity sensing material to create pores. In FIG. 5, openings 32 have been formed in the humidity sensing material 16 to increase the porosity and thus the effective surface area of the humidity sensing material 16. This may increase the sensitivity of the humidity sensor. FIG. 6 is a top view of the humidity sensor 30 of FIG. 5, illustrating that the openings 32 of FIG. 5 may include a plurality of pores 34 formed within the humidity sensing material 16. FIG. 7 is an alternate top view of the humidity sensor 30 of FIG. 5, illustrating that the openings 32 of FIG. 5 may include one or more elongated channels 36 formed within the humidity sensing material 16.

FIG. 8 is a top view of an interdigitated humidity sensor 40, while FIG. 9 shows a schematic cross-sectional side view of the interdigitated humidity sensor 40 of FIG. 8 taken along line B-B′ illustrating the sequence of a substrate 12, an electrode layer 14 and a humidity sensing material 16. As can be seen, in this example, the electrode layer includes two interdigitated electrodes. FIG. 10 is an enlarged cross-sectional side view of a portion of the interdigitated humidity sensor 40 of FIG. 9 after additional processing of the humidity sensing material 16. In FIG. 10, openings 42 have been formed in the humidity sensing material 16 to increase the porosity and thus the effective surface area of the humidity sensing material 16. This may increase the sensitivity of the interdigitated humidity sensor.

FIG. 11 is a flow diagram showing an illustrative method of manufacturing a humidity sensor such as the humidity sensor 10 (FIG. 1), the humidity sensor 30 (FIG. 3), the humidity sensor 40 (FIG. 8) or the humidity sensor 50 (FIG. 2). As generally indicated at block 70, an electrode layer may be formed over a substrate. In some cases, the electrode layer may be formed directly on the substrate while in other cases there may be one or more intervening layers. A non-halogenated polymeric layer may be disposed over the electrode layer, as generally seen at block 72. In some cases, the non-halogenated polymeric layer may be a non-halogenated polyimide layer. In some cases, as optionally shown at block 74, a plurality of openings, such as channels, pores or other void spaces, may be formed within the non-halogenated polymeric layer.

Next, as generally indicated at block 76, the non-halogenated polymeric layer may be halogenated. In some cases, halogenating the non-halogenated polymeric layer may include a chemical reaction and/or a thermal reaction, such as in a plasma environment. In some cases, halogenating the non-halogenated polymeric material may include an ion implantation process. In some cases, halogenating the non-halogenated polymeric material may include fluorinating the non-halogenated polymeric material, and may for example result in an organofluorine thin film disposed on the non-halogenated polymeric material.

In some cases, the humidity sensing material may include, beyond those already discussed, a polymer film (polyimides, benzocyclobutene, nylons, etc.), an organosilicate film (Si—O—C polymers, divinylsiloxane bis (benzocyclobutene), etc.), and/or an inorganic film that has been halogenated, such as with fluorine, chlorine or bromine, and/or coated with a halogenated thin film such as a perfluorocarbon or an organofluorine (CxFy) thin film. By halogenating and/or coating the humidity sensing material, the capacitive and/or resistive hysteresis effect of the humidity sensor may be diminished compared to a humidity sensor that uses an untreated humidity sensing material. In general, halogenating the humidity sensing material may make the humidity sensing material more hydrophobic, and thus less susceptible to hysteresis. Fluorination is a favorable method of halogenation due to the availability of a large number of fluorine sources within a typical microelectronics fabrication facility, although chlorine and bromine are also available for use. In some cases, the humidity sensing material may be first etched or otherwise processed to increase its effective surface area before halogenating and/or coating the humidity sensing material. It is contemplated that the halogenation may extend into etched pores, holes, trenches and/or other etched features.

As noted above, the humidity sensing material may include, for example, polyimide s, parylene s, benzocyclobutene s, polyethersulfone, celluloseacetatebutyrate, poly(methyl methacrylate), and/or any other suitable humidity sensing material. Such humidity sensing materials may be improved by modifying their surface. In some cases, the humidity sensing material may be improved by either directly halogenating the humidity sensing material or by depositing an organofluorine (CxFy) thin film on the humidity sensing material. The deposited organofluorine thin film may be on the order of a single monolayer to many monolayers, as desired. It is contemplated that other halocarbons such as haloalkanes may be used to form hydrophobic surfaces. This can be accomplished by one or a combination of chemical reaction, ion implantation and deposition.

The chemical reaction of fluorine with organic and organosilicate humidity sensing materials can be accomplished with a variety of chemicals. A simple way to create reactive fluorine is in a plasma environment using fluorine containing gases such as F₂, NF₃, anhydrous HF, SiF₄, ClF₃, and XeF₂. In some cases, these gases may be blended with inert diluents such as Ar, He, and N₂ to improve the production of fluorine radicals. Most plasma etch and plasma chemical vapor deposition systems control the temperature of the processed substrate in order to allow for control of the chemical reaction between the fluorine and the humidity sensing material. In some cases, downstream plasmas may be used to eliminate ion interactions with the substrate of the humidity sensor, thus allowing for purely chemical interactions. It is also possible to fluorinate surfaces of polymer films with XeF₂ vapors. The SPTS Xactix tool, for example, is specifically built for XeF₂ reactions and is used within MEMS manufacturing.

Ion implantation of fluorine and fluorinated species into the humidity sensing material is also contemplated. For the organic films, low energy ions may be used to keep the ions near the surface of the humidity sensing material. Ion implanters typically use BF₃ to implant boron. In fact, ions of BF₂ are implanted into the silicon. This can be done by plasma immersion ion implantation. One commercially available tool that produces low energy ions is the Varian VIISta PLAD. Higher energy ions are also possible with other implanters that are configured to directly implant F-ions or BF_x-ions into the humidity sensing material. Since these tools typically handle a fluorinated species they can also be plumbed with NF₃, SF₆, F₂, HF, and SiF₄. After implantation, the humidity sensing material can be annealed/heat treated in a conventional furnace to allow additional chemical reactions and diffusion of the fluorine.

Deposition of C_xF_y and C_xH_yF_z type materials is possible in plasma etch and plasma enhanced CVD tools. Under appropriate conditions, deposition of these species is possible with, for example, one or more of the following gases: CF₄, C₂F₆, C₄F₈, CHF₃, CH₂F₂, C₃F₈, C₄F₆, and C₅F₈. Additives and diluents may including O₂, He, N₂, Ar, H₂, NF₃, SF₆, XeF₂, ClF₃, F₂, SiF₄, and/or HF may be added to the fluorocarbon gases in order to modify the chemical species available for deposition. Other halocarbons can be formed by the above processes using other halogenated gases commonly found in a microelectronics or MEMS fabrication facility, such as HCl, Cl₂, HBr, ClF₃, HI, BCl₃, and BBr₃. In some cases, all three interactions may take place in plasma-based tools.

In one example of the disclosure, divinylsiloxane bis (benzocyclobutene) (DVS-bis-BCB) is etched in O₂+F₂ plasma which modifies the surface and bulk material properties of BCB. Optimizing the ratio of O₂ and F₂ may provide greater control of the etch rate of DVS-bis-BCB and the film thickness. DVS-bis-BCB has good adhesion properties and should adhere better than polyimide when exposed to chemical cleaners such as ammonia.

It should be understood that this disclosure is, in many respects, only illustrative. Changes may be made in details, particularly in matters of shape, size, and arrangement of steps without exceeding the scope of the disclosure. This may include, to the extent that it is appropriate, the use of any of the features of one example embodiment being used in other embodiments.

Claims

1. A humidity sensor comprising: a substrate;an electrode layer supported by the substrate, the electrode layer defining a first capacitive plate and a second capacitive plate;a polyimide humidity sensing layer adjacent the electrode layer, the polyimide humidity sensing layer including a sensing surface and a thickness, and further including a number of openings formed within the sensing surface to increase an effective surface area of the sensing surface; andthe sensing surface of the polyimide humidity sensing layer being fluorinated to a depth that is less than the thickness of the polyimide humidity sensing layer, resulting in a fluorinated sensing surface.

2. The humidity sensor of claim 1, wherein the fluorinated sensing surface is fluorinated by plasma deposition of CxHyFz onto the polyimide humidity sensing layer, where x is an integer ranging from 1 to 4, y is an integer ranging from 0 to 2 and z is an integer ranging from 2 to 8.

3. The humidity sensor of claim 2, wherein the CxHyFz comprises one or more of CF4, C2F6, C4F8, CHF3 and CH2F2.

4. The humidity sensor of claim 1, wherein the fluorinated sensing surface comprises a monolayer or a partial monolayer.

5. The humidity sensor of claim 1, wherein the fluorinated sensing surface comprises a heterogeneous mixture of fluorocarbons and hydrofluorocarbons.

6. The humidity sensor of claim 1, wherein the electrode layer is adjacent a first side of the polyimide humidity sensing layer, and a porous platinum layer is adjacent a second opposing side of the polyimide humidity sensing layer, wherein the porous platinum layer in combination with the first capacitive plate and the second capacitive plate form a first capacitor and a second capacitor.

7. A humidity sensor comprising: a substrate;an electrode layer supported by the substrate, the electrode layer defining a first capacitive plate and a second capacitive plate;a non-halogenated humidity sensing layer adjacent the electrode layer, the non-halogenated humidity sensing layer including a number of openings to increase an effective surface area of the non-halogenated humidity sensing layer; anda halogenated layer adjoining the non-halogenated humidity sensing layer.

8. The humidity sensor of claim 7, wherein the halogenated layer represents the halogenation of a surface portion of the non-halogenated humidity sensing layer.

9. The humidity sensor of claim 7, wherein the halogenated layer comprises an organofluorine monolayer.

10. The humidity sensor of claim 7, wherein the non-halogenated humidity sensing layer comprises one or more of a polyimide, a parylene, a benzocyclobutene, and divinylsiloxane bis(benzocyclobutene).

11. The humidity sensor of claim 7, wherein the non-halogenated humidity sensing layer comprises a polyimide.

12. The humidity sensor of claim 7, wherein the halogenated layer extends into the number of openings in the non-halogenated humidity sensing layer.

13. A method of manufacturing a humidity sensor, comprising: forming an electrode layer over a substrate;disposing a non-halogenated polymeric material over the electrode layer as a humidity sensing material; andwith the non-halogenated polymeric material disposed over the electrode layer, halogenating the non-halogenated polymeric material to increase the non-halogenated polymeric material's resistance to humidity sensing hysteresis.

14. The method of claim 13, further comprising forming a plurality of openings in the non-halogenated polymeric material before halogenating the non-halogenated polymeric material.

15. The method of claim 13, further comprising forming a plurality of pores in the non-halogenated polymeric material before halogenating the non-halogenated polymeric material.

16. The method of claim 13, wherein the non-halogenated polymeric material comprises polyimide.

17. The method of claim 13, wherein halogenating the non-halogenated polymeric material comprises a chemical reaction and/or a thermal reaction in a plasma environment.

18. The method of claim 13, wherein halogenating the non-halogenated polymeric material comprises an ion implantation process.

19. The method of claim 13, wherein halogenating the non-halogenated polymeric material comprises a deposition process.

20. The method of claim 13, wherein halogenating the non-halogenated polymeric material comprises forming an organofluorine thin film on the non-halogenated polymeric material.