Patent Grant
8328931
The subject application is a National Phase of PCT/EP2010/068465 filed 30 Nov. 2010 which claims priority from Italian Application IT No. MI2009A002105 filed on 30 Nov. 2009, which is incorporated by reference.
The present invention relates to hydraulic binders, such as cements, which use a finely ground and activated granulated blast furnace slag of latent hydraulic activity.
Ground blast furnace slag is a by-product of cast iron production starting from iron minerals or scrap. In this process a liquid slag forms and floats on the molten metal, the slag containing lime, silica and other oxides such as MgO, which separate from the metal at temperatures exceeding 1900° C. This by-product is suddenly cooled to obtain a vitreous granulate with latent hydraulic properties.
The use of granulated blast furnace slag is permitted as a cement component by European Standard EN 197-1, type II (Portland slag cement) and III (blast furnace cement), up to a theoretical slag content of 95%. This high value is related to the potential hydraulicity of slag and its activability in cementitious mixtures which enable concretes to be produced for particular applications, for instance where high durability is required with low heat development or with low atmospheric CO2 emissions.
Specifically, EN 197-1 requires the following conditions to be satisfied: (CaO+MgO)/SiO2>1; CaO+MgO+SiO2>67% and vitreous mass greater than 67%.
Slag activation requires the addition of an activator chosen from alkalis, or sulphates, or calcium oxide, or chloride ion based alkaline salts, or it can also be implemented thermally. The ability to replace a Portland cement clinker with slag increases with the level of slag activation.
In general however the reactivity of cements of high slag content is considered to be too mild compared with cements of high clinker content; the high slag content is aimed at those applications in which the typical high activity of clinker would lead to excessive overheating of the final concrete article.
The availability of cements of high slag content with good mechanical characteristics would be desirable, in particular good compressive strength with quick curing. This property would also extend the application of high slag content cements to those sectors in which cements of high clinker content are currently used, as well as to structural applications in aggressive environments, or to road, railway or airport construction, or for large castings, or for castings in coastal localities.
In the known art, U.S. Pat. No. 6,409,820 describes a hydraulic binder comprising a slag, activatable with sulphates, and having a glass content or vitreous fraction greater than 93%, SiO2=34-40%, Al2O3>9%, CaO=34-37% by mass, and a (CaO+MgO)/(Al2O3+SiO2) ratio=0.88-0.98, hence less than 1, and a high content of sulphates, with CaSO4 variable between 12 and 20% by mass on the binder, as activators.
U.S. Pat. No. 6,409,820 shows in its experimental part that a similar slag composition in which however the components are only slightly varied such that the (CaO+MgO)/(Al2O3+SiO2) ratio=1.03, hence greater than 1, is not suitable for is forming a hydraulic binder of low clinker content that provides satisfactory final article properties, in particular compressive strength.
An object of the present invention is to provide a hydraulic binder of medium and high slag content instead of clinker in compliance with standard EN 197-1, in which Portland cement clinker is contained in a quantity equal to or greater than 5% by mass on the binder, which is able to form concrete articles of high mechanical performance with quick curing and of low environmental impact due to its moderate CO2 content.
A particular object of the present invention is to achieve said result while satisfying the requirements of standard EN 197-1, in particular for rapid hardening (R) strength classes.
An object of the present invention is also to provide this binder while maintaining the content of slag activators substantially low, within the limits allowed by standard EN 197-1 because if said content is high, various technical problems can arise as a result. In this respect, it is considered that, for example, the use of high amounts of alkali results in greater shrinkage with consequent increased risks of crack formation in concrete applications, greater undesirable reactivity towards aggregates, especially due to alkali-silica reaction, and the appearance of efflorescence in concrete. With regard to the use of large amounts of chloride ion based alkaline salts, this is considered to increase corrosion risks in reinforced concrete structures. With regard to the use of large amounts of sulphates, this is thought to lead to delayed expansion phenomena in the cured concrete article with possible disgregation of the article, or to detachment of structural parts.
A further object of the invention is to provide a high activity slag which can be used in Portland cement clinker or as an addition to the concrete.
This object is attained according to the present invention by a hydraulic binder comprising a ground blast furnace slag in a quantity between 30% and 95% by mass on the binder, Portland cement clinker in a quantity equal to or greater than 5% by mass on the binder and at least one sulphate as activator, characterised in that said slag has the following properties and composition by mass: grinding is fineness greater than 4000 cm2/g Blaine, glass content greater than 80%, SiO2 from 30 to 40%, Al2O3 from 9 to 13%, CaO from 34 to 42%, with a (CaO+MgO)/(Al2O3+SiO2) ratio greater than 1; and that said sulphate is contained in a total quantity, expressed as SO3, of between 0.6 and 4.5% by mass on the binder.
Preferably, said slag has a MgO content greater than 8% by mass.
Said sulphate is chosen as one or more of the following: CaSO4, Na2SO4, K2SO4. When the sulphate is CaSO4, it is either natural or is a product obtained by desulphurization processes, or is a mixture of the preceding, or is in the form of hydrated salt (hemihydrate).
The quantity of said activator in the binder is hence preferably chosen as follows: CaSO4 in the range between 0.3-5%, preferably 0.5-2.5%, by mass on the hydraulic binder; Na2SO4 in the range between 0.3-5%, preferably 0.5-2.5%, by mass on the hydraulic binder.
In one embodiment, said activator can comprise calcium oxide, present in the range between 0.3-5%, preferably 1-4%, by mass on the hydraulic binder.
In one embodiment, said slag in said hydraulic binder is ground to a fineness greater than 5000 cm2/g, while in a different preferred embodiment, it is ground to a fineness greater than 6000 cm2/g Blaine.
For the purposes of the present description, cementitious compositions mean cementitious mixes comprising at least said hydraulic binder, water and possibly one or more inert aggregates, and/or one or more mineral additions, and/or fibres for cements, and/or one or more conventional additives.
The term “hydraulic binder” means a material in powder form in the dry state which, when mixed with water, provides plastic mixtures able to solidify and harden with time. Cements mean in particular those included in European Standard EN 197-1.
Cementitious compositions are divided into pastes, i.e. compositions without inert aggregates, and conglomerates, i.e. compositions containing at least one inert aggregate. Conglomerates are divided into mortars (containing fine aggregates such as sand), and concretes (containing both fine aggregates and coarse aggregates such as gravel, pebbles and crushed stone, chosen for example from is those classified according to UNI EN 12620).
The present invention is particularly suitable for mortars and concretes.
A mineral addition means any type of finely divided inorganic material which can be added to the concrete to impart ideal mechanical strength and durability characteristics. The additions can be inert, pozzolanic or of latent hydraulic activity, these additions being for example chosen from those allowed by European Standard EN 206-1.
More particularly, the term “addition” means a finely divided activated ground slag. The slag based hydraulic binders of the present invention, when used as cements, give rise to the production of concretes in accordance with European Standard EN 206-1.
The quantities of these binders, per cubic metre of concrete, fall within the range of values commonly adopted for concretes while respecting the limiting values recommended for concrete composition and properties (EN 206-1). A concrete can be produced having a binder quantity greater than 100 kg/m3.
Even when the activated slag of the present invention is used as a concrete addition, a concrete can be produced conforming to European Standard EN 206 having an addition quantity greater than 10 kg/m3.
The characteristics and advantages of the present invention are described in greater detail in the following examples, given merely as non-limiting illustration of the present invention.
In the following examples 1, 2, 3, 4 and 5, three slags for hydraulic binders according to the present invention are identified as GGBFS1, GGBFS5 and GGBFS6, having the composition stated in the following Table 1.
Example 6 shows the results for applications in concrete.
Table 1 also shows for comparison purposes the compositions of slags not suitable for the present invention, namely: GGBFS2, GGBFS3 and GGBFS4, this latter corresponding to the aforesaid comparison slag of the known art described in U.S. Pat. No. 6,409,820.
In the described examples, hydraulic binders according to the present invention are used as cements. Cements according to the invention and comparison is cements were prepared as follows:
This ground Portland cement clinker with calcium sulphate and possible minor components is also a CEM I 52.5 R cement according to European Standard EN 197-1. Said possible minor components according to European Standard EN 197-1 are different from slag and clinker and are contained in a quantity less than 5% by mass on the sum of the clinker and slag quantities according to CEM I 52.5R.
90%
94%
85%
95%
10%
A cement was prepared having the following composition:
The following compressive strength results, Rc, were obtained:
A cement was prepared having the following composition:
The following compressive strength results, Rc, were obtained:
Rc after 7 days=31.1 MPa
Rc after 28 days=38.1 MPa
conforming to a CEM III/C 32.5R.
A cement was prepared having the following composition:
The following compressive strength results, Rc, were obtained:
A cement was prepared having the following composition:
The following compressive strength results, Rc, were obtained:
Table II shows the compressive strengths after 2 days (EN 196-1), i.e. Rc2days measured in MPa for two cements of the present invention (I1, I2) compared to cements not pertaining to the invention (C1, C2, C3, C4, C5), these cements being obtained from the slags GGBFS1, GGBFS2, GGBFS3, GGBFS5 as identified in Table I above. The grinding fineness values (Blaine cm2/g) are given next to each slag.
As can be deduced from the combined data of Table II, the cements C1, C2, C3, C4 and C5 do not pertain to the present invention because of the chemical composition of the slag (C2 C3) or the activator content (C1 C4) or the slag fineness (C3) or the slag content (C5).
The marked increase in the compressive strength of the cements of the present invention (I1 and I2) after 2 days i.e. Rc2days, compared to the cements C1, C2, C3, C4 and C5, is therefore apparent.
For the activators of the GGBFS1 slag in cement I1 of the present invention, also apparent was the effect of increasing compressive strength after 2 days with respect to the non-activated cement mixture C5.
Moreover, the cements produced according to the present invention did not generally show expansion phenomena in stability tests, and their ‘start of setting’ times were found to be greater than those of the reference cements as shown in Table III below, from which it can be concluded that mortar rheology was normal.
Cements of the invention were used to produce concrete.
The results of the experiments carried out are given in Table IV.
A concrete produced with a limestone cement CEM II/A-LL 42.5R was used as the reference.
It can be seen that the blast furnace cement of the invention enabled the rheological and mechanical characteristics to be in line with those obtained with limestone cement in relation to the relative cement strength classes.
In particular the cement produced with the CEM III/B 52.5N enabled better mechanical characteristics than the reference concrete to be achieved. In this latter case to obtain the consistency class S5 a higher a/c ratio had to be adopted (i.e. 0.41 instead of 0.39).
As is apparent from the preceding overall description, the invention therefore enables all the predetermined objects be effectively attained.
| Number | Date | Country | Kind |
|---|---|---|---|
| MI2009A2105 | Nov 2009 | IT | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2010/068465 | 11/30/2010 | WO | 00 | 5/29/2012 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2011/064378 | 6/3/2011 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2947643 | Kamlet | Aug 1960 | A |
| 6409820 | Novak | Jun 2002 | B1 |
| 8056631 | Garcia et al. | Nov 2011 | B2 |
| 8257488 | Garcia et al. | Sep 2012 | B2 |
| 20110136946 | Kono et al. | Jun 2011 | A1 |
| 20110259246 | Guynn et al. | Oct 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 2324486 | Apr 2002 | CA |
| 2080742 | Jul 2009 | EP |
| 59-091190 | May 1984 | JP |
| 2007-217197 | Aug 2007 | JP |
| 2010-285292 | Dec 2010 | JP |
| 2010-285465 | Dec 2010 | JP |
| WO-2011055063 | Jun 2011 | WO |
| WO-2011064378 | Jun 2011 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20120234209 A1 | Sep 2012 | US |