Claims
- 1. A composition comprising:
- at least one rhodium or palladium compound or mixture thereof supported on a calcined, acidic, nickel and rare earth-treated crystalline zeolite; wherein the rare earth content of the calcined, acidic, nickel and rare earth-treated crystalline zeolite ranges from about 2 to about 25 percent by weight; and
- wherein the nickel content of the calcined, acidic, nickel and rare earth-treated crystalline zeolite ranges from about 0.01 to about 12 percent by weight.
- 2. The composition of claim 1 wherein the rhodium and/or palladium content ranges from about 0.01 to about 1 percent by weight.
- 3. The composition of claim 1 wherein the rhodium and/or palladium content ranges from about 0.05 to about 0.25 percent by weight.
- 4. The composition of claim 1 wherein the crystalline zeolite is selected from the group consisting of Type X and Type Y zeolites;
- wherein the rare earth metal and nickel compounds are selected from the group consisting of nitrates, bromides, acetates, chlorides, iodides, sulfates and mixtures thereof;
- wherein the rare earth metal is selected from the group consisting of cerium, lanthanum, praseodymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium and mixtures thereof, and
- wherein the rhodium and palladium compounds are selected from the group consisting of rhodium(III) acetylacetonate, rhodium(I) dicarbonyl chloride dimer, rhodium(III) nitrate, and rhodium(III) trichloride, palladium(II) acetylacetonate, palladium(II) chloride, palladium(II) iodide, palladium(II) nitrate and mixtures thereof.
- 5. The composition of claim 1 wherein the crystalline zeolite is the alkali metal form with the alkali metal content of the calcined, acidic, nickel and rare earth-treated crystalline zeolite in the range of from about 0.01 to about 2 percent by weight.
- 6. The composition of claim 1 wherein the crystalline zeolite is the alkali metal form with the alkali metal content of the calcined, acidic, nickel and rare earth-treated crystalline zeolite ranging from about 0.05 to about 1 percent by weight;
- wherein the rare earth content of the calcined, acidic, nickel and rare earth-treated crystalline zeolite ranges from about 5 to about 20 percent by weight; and
- wherein the nickel content of the calcined, acidic, nickel and rare earth-treated crystalline zeolite ranges from about 2 to about 7 percent by weight.
- 7. The composition of claim 1 wherein the crystalline zeolite is selected from the group consisting of Type X and Type Y zeolites; and
- the rhodium and palladium compounds are rhodium chloride and palladium chloride respectively, the nickel compound used to treat the crystalline zeolite is nickel chloride hexahydrate and the rare earth metal compound used to treat the crystalline zeolite is a mixture of the chlorides consisting of lanthanum, cerium, praseodymium, neodymium, samarium and gadolinium.
- 8. The composition of claim 1 treated with a halogen-containing compound in an amount sufficient to promote the formation of a desired cycloalkyl aromatic hydrocarbon when said composition is employed in a hydroalkylation reaction.
- 9. The composition of claim 8 wherein the halogen-containing compound is in an amount ranging from about 0.1 to about 100 milligrams of the elemental halogen per gram of said composition.
- 10. The composition of claim 8 wherein the halogen-containing compound is an organic halogen-containing compound and the amount of said organic halogen-containing compound ranges from about 0.5 to about 10 milligrams of the elemental halogen per gram of the catalyst employed.
- 11. The composition of claim 8 wherein the halogen-containing compound is selected from the group consisting of carbon tetrachloride, tetrachloroethylene, chloroform, bromoform, dichloromethane, difluoromethane, dibromomethane, fluoromethane, chloromethane, bromomethane, 1,4-dichlorobutane, 1,4-dibromobutane, 1-chlorobutane, 1-fluorobutane, 1-bromobutane, 1,2-dichloroethane, 1,2-dibromoethane, 2-chloropropane, acetyl chloride, acetyl bromide, acetyl iodide, bromochloromethane, 1-bromo-4-chlorobutane, 1-fluoro-4-chlorobutane, 1,2-dichloroethylene, 1,2-dibromoethylene and mixtures thereof.
- 12. A method for the preparation of a composition comprising:
- contacting a crystalline zeolite with an aqueous cation exchange solution comprising rare earth, nickel, and ammonium compounds to produce a zeolite having from about 2 to about 25 weight percent rare earth content and from about 0.01 to about 12 weight percent nickel content,
- removing the cation exchanged zeolite from said solution and washing said zeolite with water to remove excess ions;
- calcining said cation exchanged zeolite;
- cooling said calcined zeolite;
- impregnating said cation exchanged zeolite with a solution comprising at least one rhodium or palladium compound or mixture thereof in a suitable solvent; and
- removing said solvent by evaporation,
- wherein said cation exchanged zeolite is calcined and then cooled either before or after said rhodium or palladium compound or a mixture thereof is impregnated on said zeolite.
- 13. The method of claim 12 wherein said zeolite is selected from the group consisting of alkali metal Type X and Type Y zeolites;
- wherein the rare earth metal and nickel compounds are selected from the group consisting of nitrates, bromides, acetates, chlorides, iodides, sulfates and mixtures thereof;
- wherein the rare earth metal is selected from the group consisting of cerium, lanthanum, praseodymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium and mixtures thereof, and
- wherein the rhodium and palladium compounds are selected from the group consisting of rhodium(III) acetylacetonate, rhodium(I) dicarbonyl chloride dimer, rhodium(III) nitrate, and rhodium(III) trichloride, palladium(II) acetylacetonate, palladium(II) chloride, palladium(II) iodide, palladium(II) nitrate and mixtures thereof;
- wherein the weight ratio of ammonium compound to rare earth and nickel compounds combined ranges from about 0.05:1 to about 20:1;
- wherein said aqueous cation exchange nickel, rare earth and ammonium compound solution is contacted with said zeolite at a liquid hourly space velocity ranging from about 0.1 to about 0.5; and
- wherein after said zeolite is washed with water and prior to said calcination step, said zeolite is heated to a temperature ranging from about 100.degree. to 300.degree. C. to remove excess water and then the temperature is slowly raised to a temperature ranging from about 200.degree. to 550.degree. C. in order to calcine said zeolite and convert the ammonium cations to the hydrogen form.
- 14. The method of claim 13 wherein said composition is treated with hydrogen subsequent to calcination and to the removal by evaporation of the solvent for the rhodium and palladium compounds.
- 15. The method of claim 12 wherein the crystalline zeolite is selected from the group consisting of Type X and Type Y zeolites; and
- the rhodium and palladium compounds are rhodium chloride and palladium chloride respectively, the nickel compounds used to treat the crystalline zeolite is nickel chloride hexahydrate and the rare earth metal compound used to treat the crystalline zeolite is a mixture of the chlorides consisting of lanthanum, cerium, praseodymium, neodymium, samarium and gadolinium.
- 16. The method of claim 12 wherein the rhodium and palladium content of the impregnating solution is sufficient to provide a rhodium and palladium content of the cation exchanged zeolite ranging from about 0.01 to about 1 percent by weight.
- 17. The method of claim 12 wherein the rhodium and palladium content of the impregnating solution is sufficient to provide a rhodium and palladium content of the cation exchanged zeolite ranging from about 0.05 to about 0.25 percent by weight.
- 18. The method of claim 12 wherein the impregnated and calcined zeolite composition is treated with a halogen-containing compound in an amount sufficient to promote the formation of a desired cycloalkyl aromatic hydrocarbon when said composition is employed in a hydroalkyoation reaction.
- 19. The method of claim 18 wherein the halogen-containing compound is in an amount ranging from about 0.1 to about 100 milligrams of the elemental halogen per gram of said composition.
- 20. The method of claim 18 wherein the halogen-containing compound is an organic halogen-containing compound and the amount of said organic halogen-containing compound ranges from about 0.5 to about 10 milligrams of the elemental halogen per gram of the catalyst employed.
- 21. The method of claim 18 wherein the halogen-containing compound is selected from the group consisting of carbon tetrachloride, tetrachloroethylene, chloroform, bromoform, dichloromethane, difluoromethane, dibromomethane, fluoromethane, chloromethane, bromomethane, 1,4-dichlorobutane, 1,4-dibromobutane, 1-chlorobutane, 1-fluorobutane, 1-bromobutane, 1,2-dichloroethane, 1,2-dibromoethane, 2-chloropropane, acetyl chloride, acetyl bromide, acetyl iodide, bromochloromethane, 1-bromo-4-chlorobutane, 1-fluoro-4-chlorobutane, 1,2-dichloroethylene, 1,2-dibromoethylene and mixtures thereof.
Parent Case Info
This is a division, of application Ser. No. 767,413, filed Feb. 10, 1977 now U.S. Pat. No. 4,094,918.
US Referenced Citations (6)
Divisions (1)
|
Number |
Date |
Country |
Parent |
767413 |
Feb 1977 |
|