Hydrocarbonylation/carbonylation of alkyl carboxylates

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to the hydrocarbonylation and/or carbonylation of alkyl carboxylates, in particular methyl carboxylates and alkyl acetates, in the presence of water. The subject process is, moreover, conveniently represented by the following equation:
R--CO--O--R'+CO+H.sub.2 .fwdarw.R'--CO--O--CH.sub.2 --R', R--CO--O--CH.sub.2 --R', R'--CH.sub.2 --OH, R'--CHO, R--CO--OH, R'--CO--OH. (1)
in which R represents a linear or branched chain alkyl radical having from 1 to 16 carbon atoms, a cycloalkyl radical having from 3 to 6 carbon atoms, a phenyl radical (C.sub.6 H.sub.5 --), a radical C.sub.6 H.sub.5 --C.sub.x H.sub.2x -- or a radical C.sub.x H.sub.2x+1 --C.sub.6 H.sub.4 --, with x being an integer ranging from 1 to 6 (1.ltoreq.x.ltoreq.6), and R' represents a linear or branched chain alkyl radical having from 1 to 5 carbon atoms or a radical C.sub.6 H.sub.5 --C.sub.x H.sub.2x --, with x being as above defined, it also being possible for R and R' to be identical.
The process according to this invention is admirably suited to the preparation of one or more of the compounds acetaldehyde, acetic acid, ethanol and ethyl acetate, from methyl carboxylates, and especially from methyl acetate.
2. Description of the Prior Art
Certain authors (compare Journal of the American Chemical Society, 100:19, 1978, pages 6,238-6,239) have reported that it is possible to prepare, in particular, ethyl acetate by the hydrocarbonylation of methyl acetate in the simultaneous presence of ruthenium, an iodine-containing promoter and a proton donor (which is either the HI initially employed in the reaction, or formed in situ from CH.sub.3 I, or a carboxylic acid).
However, the industrial-scale development of a technique of this type, the value of which is not contested in principle, is markedly compromised by the low activity of the catalyst system used.
It has recently been proposed (compare French Patent Application No. 78/20,843) to carry out such reaction in the presence of a cobalt salt and iodine. However, the high pressures required for the catalyst system to develop an acceptable activity hardly make it possible to envisage industrial development of such a process.
Parallel to this, examination of the specialized literature reveals that numerous attempts to hydrocarbonylate methanol in order to selectively obtain either acetaldehyde or ethanol have not resulted in satisfactory solutions. A survey of the various techniques proposed for this purpose can be found, for example, in the introductory portion of U.S. Pat. No. 4,133,966.
It is clearly apparent from this analysis that it would be desirable to have available an efficient process which makes it possible, if appropriate, to prepare aldehydes, carboxylic acids, "homologous" alcohols and, more particularly, alkyl carboxylates from their lower homologs. The term "homologous alcohol" is to be understood as connoting the alcohol R'--CH.sub.2 --OH shown in equation (1) above, which thus contains one carbon atom more than the alcohol (R'--OH) from which the starting ester is derived. A first category of alkyl carboxylates which can be obtained according to the present invention is represented by the formula R--CO--O--CH.sub.2 --R' in equation (1) above. This type of ester contains one carbon atom more than the starting ester and can thus be considered as a "higher homolog" of the starting ester. To simplify the account below, the alkyl carboxylates of the formula R'--CO--O--CH.sub.2 --R' shown in equation (1) above will also be referred to as "homologous esters".
SUMMARY OF THE INVENTION
Accordingly, and which is a major object of the present invention, a novel process is hereby provided which quite unexpectedly, enables hydrocarbonylation and/or carbonylation of alkyl carboxylates in an aqueous medium in order to obtain one or more of the compounds comprising the carboxylic acids, aldehydes, alcohols and homologous alkyl carboxylates, according to equation (1) above, in an extremely efficient manner, provided that the reaction is carried out in the presence of hydrogen, ruthenium, cobalt, at least one iodine-containing promoter and chromium (or a chromium compound).
DETAILED DESCRIPTION OF THE INVENTION
More particularly according to this invention, one of the essential constituents of the catalyst system consistent herewith is ruthenium. The precise form in which the ruthenium is employed in the reaction is not critical. Ruthenium carbonyls, such as Ru.sub.3 (CO).sub.12, [Ru(CO.sub.3 Br.sub.2 ].sub.2 and Ru(CO).sub.4 I.sub.2, and more generally any ruthenium compound which is capable of giving rise to, under the reaction conditions, the appearance of ruthenium carbonyls in situ, are particularly suitable for carrying out the subject process. Ruthenium metal in finely divided form, ruthenium tribromide, ruthenium triiodide, ruthenium carboxylates (in particular ruthenium acetate) and ruthenium acetylacetonate are exemplary in this respect.
The amount of ruthenium to be used is also not critical. As the proportion of ruthenium in the reaction medium has a beneficial influence on the reaction rate, it will be determined as a function of the rate which it will be judged suitable to attain.
In general, an amount ranging from 0.5 to 100 milligram atoms of ruthenium per liter of reaction medium (mg atoms/liter) affords satisfactory results. The reaction is preferably carried out with a proportion of ruthenium ranging from 1 to 50 mg atoms/liter of ruthenium.
The second essential, or critical constituent of the catalyst system is cobalt. Any source of cobalt which is capable of reacting with carbon monoxide in the reaction medium to provide cobalt carbonyl complexes can be used within the scope of the present process.
Examples of typical sources of cobalt are finely divided cobalt metal, inorganic salts, such as cobalt nitrate or carbonate, and organic salts, in particular carboxylates. Cobalt carbonyls or hydrocarbonyls can also be employed.
Cobalt formate, acetate and halides, and more particularly cobalt iodide, and dicobalt octacarbonyl are also exemplary of the cobalt derivatives suitable for carrying out the process according to the invention.
The precise amount of cobalt employed in the reaction too is not of fundamental importance. In general, the reaction is carried out with an amount of cobalt such that the atomic ratio Co/Ru ranges from 0.01 to 100 (0.01.ltoreq.Co/Ru.ltoreq.100). This ratio preferably ranges from 0.1 to 10.
The presence of an iodine-containing promoter is also required for carrying out the process according to the present invention. Free or combined iodine can be used for this purpose.
A first category of iodine-containing promoters suitable for carrying out the subject process consists of alkyl or acyl iodides of the respective formulae R"--I and R"--CO--I, in which R", which can be identical to or different from R', has the meaning given for R'. In this catetory, it is preferred to use alkyl iodides having a maximum of 4 carbon atoms and more particularly methyl or ethyl iodide.
A second category of iodine-containing promoters which can be used within the scope of the present process consists of ionic iodides, the cations of which are selected from among alkali metal cations, alkaline earth metal cations and the quaternary ammonium or phosphonium cations represented by the formulae I to III below: ##STR1## in which A represents a nitrogen or phosphorus atom, and R.sub.1, R.sub.2, R.sub.3 and R.sub.4, which can be identical or different, represent hydrogen or preferably organic radicals, the free valency of which is carried by a carbon atom, it optionally being possible for any two of these various radicals to together form a single divalent radical.
More specifically, R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are advantageously linear or branched chain alkyl radicals, cycloalkyl radicals, aralkyl radicals (for example, benzyl) or monocyclic aryl radicals, which have at most 16 carbon atoms and which, if appropriate, can be substituted by 1 to 3 alkyl radicals having from 1 to 4 carbon atoms, it optionally being possible for two of the radicals R.sub.1 to R.sub.4 to together form a single divalent alkylene or alkenylene radical containing 3 to 6 carbon atoms and, if appropriate, 1 or 2 ethylenic double bonds, and it being possible for the said radical to bear 1 to 3 alkyl substituents having from 1 to 4 carbon atoms. ##STR2## in which R.sub.5, R.sub.6, R.sub.7 and R.sub.8, which are identical or different, represent alkyl radicals having from 1 to 4 carbon atoms, it also being possible for one of the radicals R.sub.7 or R.sub.8 to represent hydrogen and it optionally being possible for R.sub.7 and R.sub.8 to together form a single divalent alkylene radical containing from 3 to 6 carbon atoms, for example, tetramethylene or hexamethylene; R.sub.6 and R.sub.7 or R.sub.8 can together form a single divalent alkylene or alenkylene radical containing 4 carbon atoms and, if appropriate, 1 or 2 ethylenic double bonds, the nitrogen atom then being included in a heterocyclic ring to form, for example, a pyridinium cation. ##STR3## in which R.sub.5 and A.sup.+ have the meaning given above, R.sub.9, which can be identical to R.sub.5, represents an alkyl radical having from 1 to 4 carbon atoms or a phenyl radical and y is an integer ranging from 1 to 10 (1.ltoreq.y.ltoreq.10) and preferably from 1 to 6 (1.ltoreq.y.ltoreq.6). The following are exemplary of quaternary ammonium iodides suitable for carrying out the present process: tetramethylammonium, triethylmethylammonium, tributylmethylammonium, trimethyl-(n-propyl)-ammonium, tetraethylammonium, tetrabutylammonium, dodecyltrimethylammonium, benzyltrimethylammonium, benzyldimethylpropylammonium, benzyldimethyloctylammonium, dimethyldiphenylammonium, methyltriphenylammonium, N,N-dimethyl-trimethyleneammonium, N,N-diethyl-trimethyleneammonium, N,N-dimethyltetramethyleneammonium, N,N-diethyl-tetramethyleneammonium, N-methylpyridinium, N-ethylpyridinium and N-methylpicolinium iodides.
The following are exemplary quaternary phosphonium iodides also suitable for carrying out the present process: tetramethylphosphonium, ethyltrimethylphosphonium, trimethylpentylphosphonium, octyltrimethylphosphonium, dodecyltrimethylphosphonium, trimethylphenylphosphonium, diethyldimethylphosphonium, dicyclohexyldimethylphosphonium, dimethyldiphenylphosphonium, cyclohexyltrimethylphosphonium, triethylmethylphosphonium, methyl-tri-(isopropyl)phosphonium, methyl-tri-(n-propyl)-phosphonium, methyl-tri-(n-butyl)-phosphonium, methyl-tris-(2-methylpropyl)-phosphonium, methyltricyclohexylphosphonium, methyltriphenylphosphonium, methyltribenzylphosphonium, methyl-tris-(4-methyl-phenyl)phosphonium, methyltrixylylphosphonium, diethylmethylphenylphosphonium, dibenzylmethylphenylphosphonium, ethyltriphenylphosphonium, tetraethylphosphonium, ethyl-tri-(n-propyl)-phosphonium, triethylpentylphosphonium, ethyltriphenylphosphonium, n-butyl-tri-(n-propyl)-phosphonium, butyltriphenylphosphonium, benzyltriphenylphosphonium, (.beta.-phenylethyl)-dimethylphenylphosphonium, tetraphenylphosphonium and triphenyl-(4-methylphenyl)-phosphonium iodides.
The precise nature of the quaternary ammonium or phosphonium cation is not of fundamental importance within the scope of the present process. The choice from among these compounds is governed more by considerations of a practical nature, such as solubility in the reaction medium, the availability and the convenience of use.
In this respect, the quaternary ammonium or phosphonium iodides represented either by the formula (I) in which any one of the radicals R.sub.1 to R.sub.4 is selected from among linear alkyl radicals having from 1 to 4 carbon atoms, or by the formulae (II) or (III) in which R.sub.5 or R.sub.6 is also an alkyl radical having from 1 to 4 carbon atoms, are particularly suitable.
Moreover, the preferred ammonium iodides are those in which the cations correspond to the formula (I) in which all the radicals R.sub.1 to R.sub.4 are selected from among linear alkyl radicals having from 1 to 4 carbon atoms, and in which at least three of same are identical.
Likewise, the preferred quaternary phosphonium iodides are those in which the cations correspond to the formula (I) in which any one of the radicals R.sub.1 to R.sub.4 represents a linear alkyl radical having from 1 to 4 carbon atoms, the other three radicals being identical and selected from among phenyl, tolyl or xylyl radicals.
The alkali metal iodides, in particular lithium, potassium and sodium iodides, constitute a preferred class of ionic iodides within the scope of the present invention. The quaternary phosphonium iodides, and more particularly those in which the cations correspond to the formula (I) above, in which one of the radicals R.sub.1 to R.sub.4 is an alkyl radical having from 1 to 4 carbon atoms, the other three radicals being identical and selected from among phenyl, tolyl or xylyl radicals, constitute another preferred class of ionic iodides which are particularly effective for carrying out the present invention.
Of course, hydriodic acid can also be used as the iodine-containing promoter; it is also possible to employ iodine-containing compounds such as CoI.sub.2, CrI.sub.2, CrI.sub.3 (9H.sub.2 O), RuI.sub.3 and Ru(CO).sub.4 I.sub.2, by themselves or, preferably, mixed with one or more iodine-containing promoters belonging to one or another of the aforenoted categories.
In general, the amount of iodine-containing promoter is such that the atomic ratio I/Ru is equal to at least 0.01; it serves no purpose to exceed a value of 2,000 for this ratio. This ratio advantageously ranges from 0.05 to 500.
According to a preferred embodiment of the subject process, an alkyl or acyl iodide (a member of the first category of iodine-containing promoters described above) is used simultaneously with an ionic iodide belonging to the second category of iodine-containing promoters mentioned above.
It too has been found that good results are obtained if an alkyl iodide (R"--I) is used simultaneously with an alkali metal iodide.
The simultaneous use of methyl iodide and an alkali metal iodide is particularly advantageous within the scope of the present process.
Another essential characteristic of the present invention is the use of chromium or a chromium compound. Although finely divided chromium metal and chromium hexacarbonyl can be used, it is preferred to use chromium salts in which the chromium is in an oxidation state (p) of more than zero (p>0), and which have the general formula Cr.sub.n.sup.p+ X.sub.q.sup.m-, in which q denotes the ratio (nxp)/m, m is equal to 1 or 2, p=2, 3, 4 or 6, n being equal to 1 or 2 and being selected as a function of the respective values of m and p such that q is an integer, and X.sup.m- is an anion selected from the group comprising OH.sup.-, Cl.sup.-, Br.sup.-, I.sup.-, O.sup.=, PO.sub.4.sup..ident., CH.sub.3 COCH.dbd.C(CH.sub.3)O.sup.-, HCOO.sup.-, C.sub.2 O.sub.4.sup.=, R.sup.10 --COO.sup.-, R.sup.10 --O.sup.-, NO.sub.3.sup.- and CO.sub.3.sup.=, R.sup.10 having the meaning given for R and it being possible for R.sup.10 and R to be identical or different; the chromium salts can be in hydrated form.
The precise nature of the anion X.sup.m- would not appear to be a fundamental parameter of the process according to this invention. The following are exemplary of chromium salts suitable for carrying out the present process: Cr(OH).sub.3, CrCl.sub.2, CrCl.sub.3.6H.sub.2 O, CrI.sub.2, CrBr.sub.2, CrI.sub.3.9H.sub.2 O, CrBr.sub.3.6H.sub.2 O, CrO.sub.3, Cr.sub.2 O.sub.3, CrPO.sub.4.6H.sub.2 O, Cr(OCOCH.sub.3).sub.3.H.sub.2 O, Cr(NO.sub.3).sub.3, CrCO.sub.3, Cr(OCOCH.sub.3).sub.2, Cr(OH) (HCO.sub.2).sub.2, Cr[CH.sub.3 COCH.dbd.C(CH.sub.3)O.sup.- ].sub.3 and CrC.sub.2 O.sub.4.H.sub.2 O.
According to a preferred embodiment of the invention, a chromium salt in which the chromium is in oxidation state 3 (p=3) is used. Chromium carboxylates, and more particularly acetates, are convenient to use and in this respect are recommended for carrying out the present invention.
The amount of chromium (or chromium compound) employed in the reaction is generally such that the atomic ratio Cr/Ru ranges from 0.5 to 500 (0.5.ltoreq.Cr/Ru.ltoreq.500). This ratio preferably ranges from 1 to 200.
According to the present invention, a mixture containing carbon monoxide and hydrogen is thus reacted with an alkyl carboxylate in the presence of water and the catalyst system defined above. In general, the water represents at least 1% by volume of the initial reaction medium and can be as high as 25% of the said volume. The reaction is advantageously carried out in the liquid phase under a pressure in excess of atmospheric. In general, it is carried out under a total pressure of at least 50 bars; a pressure of as much as 1,000 bars serves no purpose. To carry out the invention satisfactorily, a total pressure of 80 to 350 bars is recommended. The molar ratio of the carbon monoxide to the hydrogen can vary over wide limits.
If it is desired to assist the carbonylation of the starting material (the production of the carboxylic acid R'--CO--OH), the reaction is carried out with a mixture comprising a preponderant proportion of carbon monoxide and a small proportion of hydrogen; in general, a molar ratio CO/H.sub.2 of more than 5 leads to satisfactory results in this case.
If it is desired to assist the hydrocarbonylation of the starting material (the production of R'--CHO, R'--CH.sub.2 OH, R--CO--O--CH.sub.2 --R' and R'--CO--O--CH.sub.2 --R'), the reaction is carried out with a mixture containing carbon monoxide and hydrogen in a molar ratio CO/H.sub.2 ranging from 1/10 to 10/1 and preferably ranging from 1/5 to 5/1.
In all cases, substantially pure carbon monoxide and hydrogen, as available commercially, are employed. However, the presence of impurities, such as, for example, carbon dioxide, oxygen, methane and nitrogen, is not detrimental.
The reaction temperature is generally above 120.degree. C. However, it serves no purpose to exceed a temperature of 300.degree. C. Good results are obtained within the temperature range from 160.degree. to 250.degree. C.
As indicated in equation (1), the starting material is an alkyl carboxylate of the formula R--CO--O--R', in which R represents a linear or branched chain alkyl radical having from 1 to 16 carbon atoms, a cycloalkyl radical having from 3 to 6 carbon atoms, a phenyl radical (C.sub.6 H.sub.5 --), a radical C.sub.6 H.sub.5 --C.sub.x H.sub.2x -- or a radical C.sub.x H.sub.2x+1 --C.sub.6 H.sub.4 --, with x being an integer ranging from 1 to 6 (1.ltoreq.x.ltoreq.6), and R' represents a linear or branched chain alkyl radical having from 1 to 5 carbon atoms, it furthermore being possible for R and R' to be identical. R' is preferably a methyl radical. R is advantageously an alkyl radical having at most 4 carbon atoms or a radical C.sub.6 H.sub.5 --CH.sub.2 --. Alkyl acetates and benzoates, and more particularly methyl acetate and benzoate, are particularly suitable starting materials within the scope of the present invention.
Of course, the alkyl carboxylate (starting material) can be formed in situ from the corresponding carboxylic acid and alcohol of the formulae RCOOH and R'OH respectively.
It has also been determined that good results are obtained if the reaction medium also initially contains a carboxylic acid of the formula R'"COOH, in which R'" has the meaning given for R, it being possible for R'" and R to be identical or different. The initial reaction medium can contain up to 90% by volume of carboxylic acid (R'"COOH).
According to another preferred embodiment of the present process, the initial reaction medium contains from 1 to 20% by volume of water and from 5 to 50% by volume of carboxylic acid.
If the initial reaction medium contains a carboxylic acid (R'" COOH) which is different from the acid RCOOH from which the starting alkyl carboxylate is derived, the presence, among the reaction products, of the ester of the formula: R"' COOCH.sub.2 R', in which R' has the above meaning, is noted in certain instances.
If it is desired to carry out the reaction initially in the presence of a carboxylic acid (R'" COOH), acetic, propionic, butyric, benzoic or toluic acid is preferably used.
As indicated above, the present process has a particularly advantageous application in the preparation of one or more compounds selected from among acetaldehyde, acetic acid, ethanol and ethyl acetate, from methyl carboxylates and especially from methyl acetate.
As far as it is possible to determine, and without implying any limitation, the subject process which leads to the formation of the main products referred to above, can be directed towards the preferential production of one or other of the classes of products in question.
Thus, a reduction in the reaction temperature and/or in the proportion of hydrogen in the CO/H.sub.2 mixture is capable of assisting the production of acetic acid. (Of course, in the case where the starting material is methyl acetate, some of the acetic acid formed originates from the hydrolysis reaction of the starting material.) On the other hand, an increase in the reaction temperature and/or in the proportion of hydrogen in the CO/H.sub.2 mixture and, if appropriate, the presence of an increased proportion of ruthenium in the reaction medium seem to direct the reaction towards the preferential formation of ethyl acetate or ethanol.
An increase in the temperature and/or in the proportion of hydrogen in the CO/H.sub.2 mixture, coupled with a reduction in the reaction time, would tend to assist the production of acetaldehyde.
Thus, it is possible to obtain free acetaldehyde, namely, acetaldehyde which is not substantially converted to dimethylacetal, in contrast to that which occurs to a more or less marked extent when attempting to obtain this product starting from free methanol. Those skilled in the art will appreciate the fact that the recovery of the acetaldehyde from the reaction medium is facilitated, especially if the reaction is carried out in the presence of a heavy carboxylic acid, such as benzoic acid, and/or if a heavy methyl carboxylate (for example, methyl benzoate) is selected as the starting material.
Upon completion of the reaction, the products obtained can easily be separated, for example, by fractional distillation of the resulting mixture.

In order to further illustrate the present invention and the advantages thereof, the following specific examples are given, it being understood that same are intended only as illustrative and in nowise limitative.
In said examples which follow, the following technique was employed:
The alkyl carboxylate (starting material), the catalyst system, distilled water and, if appropriate, a carboxylic acid were introduced into a Z-8 CNDT 17-12 stainless steel autoclave (AFNOR Standard Specification) having a capacity of 250 ml. After closing the autoclave, a pressure of 140 bars (unless otherwise indicated) was established with the aid of a mixture of carbon monoxide and hydrogen in a fixed molar ratio, as indicated in each of the following examples.
Shaking by means of a reciprocating system was commenced and the autoclave was then heated to the selected temperature over the course of about 25 minutes.
The pressure in the autoclave then increased and was maintained substantially at the value indicated in each of the following examples by successively introducing additional amounts of the initial CO/H.sub.2 mixture. When the reaction time fixed for each example, at the indicated temperature, was reached, the heating and shaking were terminated. The autoclave was then cooled and degassed. After dilution, the resulting reaction mixture was analyzed by gas chromatography.
The results obtained are indicated in mols of products (in principle: acetaldehyde, ethanol, ethyl acetate and acetic acid) obtained per hour and per liter of reaction medium. The notation M/hour.times.liter is used for each product.
The results relating to the acetic acid include neither the amount of acetic acid which may have been introduced initially, nor the amount which was formed by hydrolysis of the methyl acetate (starting material).
Also, for a given product, Y indicates the selectivity of this product, relative to all of the products listed immediately above.
The degree of conversion, referred to as DC in the following text, is defined as being the ratio of the total number of mols of products in the list given above to the number of mols of methyl acetate introduced, reduced by the number of mols (of this starting material) hydrolyzed. (That fraction of the starting material hydrolyzed during an experiment can be measured by determining the methanol present in the liquid product obtained upon completion of the experiment).
EXAMPLE 1
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.22 mg atom of cobalt, in the form of cobalt acetate tetrahydrate;
(v) 1.30 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 8.34 mg atoms of chromium, in the form of chromium acetate; and
(vii) 30 mmols of sodium iodide.
After a reaction time of 20 minutes at 215.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/2 CO/H.sub.2 mixture, the formation of:
(1) 1.14 M/hour.times.liter of acetaldehyde (Y=15%);
(2) 1.64 M/hour.times.liter of ethanol (Y=22%);
(3) 2.96 M/hour.times.liter of ethyl acetate (Y=40%); and
(4) 1.64 M/hour.times.liter of acetic acid (Y=22%);
was determined (DC=24.9%).
EXAMPLE 2
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 77 ml of methyl acetate (964 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.22 mg atom of cobalt, in the form of cobalt acetate tetrahydrate;
(v) 1.30 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 17 mg of chromium, in the form of chromium acetate; and
(vii) 35 mmol of methyl iodide.
After a reaction time of 20 minutes at 215.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/2CO/H.sub.2 mixture, the formation of:
(1) 0.79 M/hour.times.liter of acetaldehyde (Y=11%);
(2) 1.05 M/hour.times.liter of ethanol (Y=15%);
(3) 2.23 M/hour.times.liter of ethyl acetate (Y=32%); and
(4) 2.89 M/hour.times.liter of acetic acid (Y=42%);
was determined (DC=23.7%).
EXAMPLE 3
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.22 mg atom of cobalt, in the form of cobalt iodide;
(v) 1.30 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 8.34 mg atoms of chromium, in the form of chromium acetate; and
(vii) 30 mmols of sodium iodide.
After a reaction time of 20 minutes at 215.degree. C., with the pressure in the autoclave being maintained at about 245 bars by periodically introducing additional amounts of a 1/2CO/H.sub.2 mixture, the formation of:
(1) 1.09 M/hour.times.liter of acetaldehyde (Y=13%);
(2) 1.66 M/hour.times.liter of ethanol (Y=20%);
(3) 3.33 M/hour.times.liter of ethyl acetate (Y=40%); and
(4) 2.18 M/hour.times.liter of acetic acid (Y=26%);
was determined (DC=27.5%).
EXAMPLE 4
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of ethyl acetate (791 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.42 mg atom of cobalt, in the form of cobalt iodide;
(v) 2.15 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 33.4 mg atoms of chromium, in the form of chromium acetate;
(vii) 7.34 mmols of methyl iodide; and
(viii) 15 mmols of sodium iodide.
After a reaction time of 85 minutes at 213.degree. C., with the pressure in the autoclave being maintained at about 230 bars by periodically introducing additional amounts of a 1/2CO/H.sub.2 mixture, 0.47 M/hour.times.liter of propanol was obtained.
EXAMPLE 5
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 90 ml of methyl acetate (1,125 mmols);
(ii) 10 ml of acetic acid (175 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.33 mg atom of cobalt, in the form of cobalt iodide;
(v) 1.32 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 3.52 mmols of methyl iodide; and
(viii) 12 mmols of methyltriphenylphosphonium iodide.
After a reaction time of 30 minutes at 214.degree. C., with the pressure in the autoclave being maintained at about 260 bars by periodically introducing additional amounts of a 1/2CO/H.sub.2 mixture, the formation of
(1) 2.02 M/hour.times.liter of acetaldehyde (Y=22%);
(2) 0.57 M/hour.times.liter of ethanol (Y=6%);
(3) 3.24 M/hour.times.liter of ethyl acetate (Y=35%); and
(4) 3.54 M/hour.times.liter of acetic acid (Y=38%);
was determined (DC=41.6%).
EXAMPLE 6
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 100 ml of methyl acetate (1,250 mmols);
(ii) 3 ml of water (170 mmols);
(iii) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(iv) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(v) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vi) 4.5 mmols of methyl iodide; and
(vii) 15 mmols of tetraethylammonium iodide.
After a reaction time of 35 minutes at 204.degree. C., with the pressure in the autoclave being maintained at about 260 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, the following were otained:
(1) 1.56 M/hour.times.liter of acetaldehyde (Y=36%);
(2) 1.65 M/hour.times.liter of ethyl acetate (Y=38%); and
(3) 1.16 M/hour.times.liter of acetic acid (Y=27%).
No ethanol was detected. (DC=16.9%).
EXAMPLE 7
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 50 ml of methyl acetate (626 mmols);
(ii) 50 ml of acetic acid (875 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 1 mmol of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
After a reaction time of 35 minutes at 204.degree. C. with the pressure in the autoclave being maintained at about 260 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, the formation of:
(1) 2.01 M/hour.times.liter of acetaldehyde (Y=70%);
(2) 0.07 M/hour.times.liter of ethanol (Y=2.4%); and
(3) 0.80 M/hour.times.liter of ethyl acetate (Y=28%);
was determined (DC=26.8%).
EXAMPLE 8
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 6 ml of water (340 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 4.56 mmols of methyl iodie; and
(viii) 15 mmols of tetraethylammonium iodide.
After a reaction time of 35 minutes at 204.degree. C., with the pressure in the autoclave being maintained at about 260 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, the formation of:
(1) 2.98 M/hour.times.liter of acetaldehyde (Y=62%);
(2) 0.09 M/hour.times.liter of ethanol (Y=1.9%);
(3) 0.46 M/hour.times.liter of ethyl acetate (Y=9.6%); and
(4) 1.25 M/hour.times.liter of acetic acid (Y=26%);
was determined (DC=27.9%).
EXAMPLE 9
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 1 mmol of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
A pressure of 70 bars was established with the aid of a 1/1CO/H.sub.2 mixture. The shaking was commenced and the autoclave was heated to 204.degree. C. The pressure in the autoclave was maintained at about 150 bars by periodically introducing additional amounts of the 1/1CO/H.sub.2 mixture. After a reaction time of 35 minutes at the temperature indicated, the formation of:
(1) 1.33 M/hour.times.liter of acetaldehyde (Y=40%);
(2) 0.49 M/hour.times.liter of ethyl acetate (Y=15%); and
(3) 1.54 M/hour.times.liter of acetic acid (Y=46%);
was determined.
Virtually no ethanol was detected. (DC=19.5%).
EXAMPLE 10
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 1 mmol of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
A pressure of 105 bars was established with the aid of a 1/2CO/H.sub.2 mixture. The autoclave was heated to 206.degree. C.; the pressure in the autoclave was maintained at about 205 bars by periodically introducing additional amounts of the above-mentioned CO/H.sub.2 mixture. After a reaction time of 35 minutes at the temperature indicated, the formation of:
(1) 1.95 M/hour.times.liter of acetaldehyde (Y=45%);
(2) 0.11 M/hour.times.liter of ethanol (Y=2.5%);
(3) 0.59 M/hour.times.liter of ethyl acetate (Y=14%); and
1.71 M/hour.times.liter of acetic acid (Y=39%);
was determined (DC=25.6%).
EXAMPLE 11
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 atoms of chromium, in the form of chromium acetate;
(vii) 1 mmol of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
An initial pressure of 105 bars was established with the aid of a 2/1CO/H.sub.2 mixture and the autoclave was heated to 204.degree. C. The pressure in the autoclave was maintained at about 205 bars by periodically introducing additional amounts of the above-mentioned CO/H.sub.2 mixture. After a reaction time of 35 minutes at the temperature indicated, the formation of:
(1) 2.07 M/hour.times.liter of acetaldehyde (Y=50%);
(2) 0.31 M/hour.times.liter of ethyl acetate (Y=7%); and
(3) 1.80 M/hour.times.liter of acetic acid (Y=43%);
was determined.
Virtually no ethanol is detected (DC=24.3%).
EXAMPLE 12
Using the autoclave and the procedure described above, and experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 1 mmol of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
After a reaction time of 35 minutes at 205.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, the formation of:
(1) 2.30 M/hour.times.liter of acetaldehyde (Y=60%);
(2) 0.38 M/hour.times.liter of ethyl acetate (Y=10%); and
(3) 1.13 M/hour.times.liter of acetic acid (Y=30%);
was determined.
Virtually no ethanol was detected (DC=22.2%).
EXAMPLE 13
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 90 ml of methyl acetate (1,125 mmols);
(ii) 10 ml of acetic acid (175 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.32 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 33.4 mg atoms of chromium, in the form of chromium acetate;
(vii) 4.4 mmols of methyl iodide; and
(viii) 12 mmols of sodium iodide.
After a reaction time of 20 minutes at 203.degree. C., with the pressure in the autoclave being maintained at about 240 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, the formation of:
(1) 2.35 M/hour.times.liter of acetaldehyde (Y=85%);
(2) 0.16 M/hour.times.liter of ethanol (Y=6%); and
(3) 0.27 M/hour.times.liter of ethyl acetate (Y=10%);
was determined (DC=8.3%).
EXAMPLE 14
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 1 mmol of methyl iodide; and
(viii) 12 mmols of sodium iodide.
After a reaction time of 35 minutes at 206.degree. C., with the pressure in the autoclave being maintained at about 255 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, the formation of:
(1) 2.49 M/hour.times.liter of acetaldehyde (Y=54%);
(2) 0.21 M/hour.times.liter of ethanol (Y=5%);
(3) 0.74 M/hour.times.liter of ethyl acetate (Y=16%); and
(4) 1.15 M/hour.times.liter of acetic acid (Y=25%);
was determined (DC=26.8%).
EXAMPLE 15
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 4.5 mmols of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
After a reaction time of 35 minutes at 205.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, the formation of:
(1) 2.51 M/hour.times.liter of acetaldehyde (Y=72%);
(2) 0.44 M/hour.times.liter of ethyl acetate (Y=13%); and
(3) 0.56 M/hour.times.liter of acetic acid (Y=16%);
was determined.
Virtually no ethanol was detected (DC=20.6%).
EXAMPLE 16
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 4.3 mmols of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
After a reaction time of 35 minutes at 190.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, the formation of:
(1) 2.65 M/hour.times.liter of acetaldehyde (Y=66%);
(2) 0.21 M/hour.times.liter of ethyl acetate (Y=5%); and
(3) 1.14 M/hour.times.liter of acetic acid (Y=29%);
was determined.
Virtually no ethanol was detected (DC=23.4%).
EXAMPLE 17
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 1.28 mg atoms of cobalt, in the form of cobalt iodide;
(v) 0.64 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 1 mmol of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
After a reaction time of 20 minutes at 203.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, the formation of:
(1) 3.99 M/hour.times.liter of acetaldehyde (Y=65%);
(2) 0.16 M/hour.times.liter of ethanol (Y=2.6%);
(3) 0.38 M/hour.times.liter of ethyl acetate (Y=5%); and
(4) 1.58 M/hour.times.liter of acetic acid (Y=26%);
was determined (DC=20.4%).
EXAMPLE 18
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.34 mg atom of cobalt, in the form of cobalt iodide;
(v) 1.97 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 33.4 mg atoms of chromium, in the form of chromium acetate;
(vii) 7.67 mmols of methyl iodide; and
(viii) 15 mmols of sodium iodide.
After a reaction time of 40 minutes at 215.degree. C., with the pressure in the autoclave being maintained at about 240 bars by periodically introducing additional amounts of a 1/2CO/H.sub.2 mixture, the formation of:
(1) 0.39 M/hour.times.liter of acetaldehyde (Y=7%);
(2) 0.99 M/hour.times.liter of ethanol (Y=17%);
(3) 4.13 M/hour.times.liter of ethyl acetate (Y=72%); and
(4) 0.26 M/hour.times.liter of acetic acid (Y=5%);
was determined (DC=38.5%).
EXAMPLES 19 TO 22
Using the autoclave and the procedure described above, a series of experiments was carried out on a charge containing:
(i) methyl acetate;
(ii) chromium, in the form of chromium acetate;
(iii) 20 ml of acetic acid (350 mmols);
(iv) 5 ml of water (280 mmols);
(v) 0.22 mg atom of cobalt, in the form of cobalt acetate tetrahydrate;
(vi) 1.31 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl; and
(vii) 17.5 mmols of methyl iodide.
All of these experiments were carried out at 214.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/2CO/H.sub.2 mixture. The reaction time was 20 minutes. The particular conditions and also the results obtained are reported in Table I below.
Control experiment (a) was carried out in the absence of chromium; the reaction time was 30 minutes.
TABLE I__________________________________________________________________________ Chromium Acetaldehyde Ethanol Ethyl acetate Acetic acid DCExample Methyl acetate in M/hour M/hour M/hour M/hour inNo. mmols ml mg atoms .times. liter Y (%) .times. liter Y (%) .times. liter Y (%) .times. liter Y (%) %__________________________________________________________________________a 977 78 0 -- -- 0.26 17 0.65 42 0.62 41 7.719 939 75 10 1.69 18 0.96 10 3.74 41 2.81 31 33.320 939 75 25 1.63 15 0.94 9 4.20 39 4.02 37 40.221 914 73 40 1.00 10 0.90 9 4.10 39 4.45 43 40.422 877 70 60 0.99 10 1.08 11 4.19 42 3.69 37 39.4__________________________________________________________________________
EXAMPLES 23 to 30
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.22 mg atom of cobalt, in the form of dicobalt octacarbonyl;
(v) 1.32 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 3.52 mmols of methyl iodide; and
(vii) 12 mmols of ionic iodide.
Control experiment (b) was carried out in the absence of chromium; in Example 23, chromium hexacarbonyl was introduced, and in the other examples, chromium acetate was introduced.
For all of these experiments, a 1/2CO/H.sub.2 mixture was used. The particular conditions and also the results obtained are reported in Table II below, in which Pt denotes the total pressure and T the reaction temperature.
TABLE II__________________________________________________________________________ Acetaldehyde Ethanol Ethyl acetate Acetic acidExample Chromium Pt T Time M/hour M/hour M/hour M/hour DCNo. mg/atoms (x) bars .degree.C. minutes .times. liter Y (%) .times. liter Y (%) .times. liter Y (%) .times. liter Y in__________________________________________________________________________ %b 0 Na 260 216 75 0.18 9 0.32 16 1.45 72 0.06 3 25.123 16.7 Na 260 210 40 0.34 12 0.41 15 1.63 60 0.35 13 18.224 8.3 Na 260 216 50 0.38 9 0.76 18 2.37 57 0.64 15 34.525 16.7 Na 240 215 40 0.55 12 0.73 15 3.47 73 -- -- 31.626 33.3 Na 260 218 30 0.77 10 0.80 10 4.09 51 2.41 30 40.327 16.7 A 250 216 30 1.02 12 0.91 11 4.22 51 2.16 26 41.628 16.7 B 250 216 35 1.15 18 0.62 10 2.63 42 1.82 29 36.229 16.7 Li 250 215 35 0.80 12 0.89 13 3.70 56 1.23 19 38.730 16.7 Cs 250 215 60 0.43 19 0.36 16 1.40 62 0.08 3 22.7__________________________________________________________________________ N.B. (x): nature of the cation of the ionic iodide. A: denotes the cation [CH.sub.3 (C.sub.6 H.sub.5).sub.3 P ##STR4##
EXAMPLES 31 to 35
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.22 mg atom of cobalt, in the form of cobalt iodide;
(v) 1.32 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 3.52 mmols of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
The reaction temperature was 215.degree. C. (unless otherwise indicated); the pressure in the autoclave was maintained at about 255 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture. The reaction time and also the results obtained for each experiment are reported in Table III below.
TABLE III__________________________________________________________________________ Acetaldehyde Ethanol Ethyl acetate Acetic acidExample Time M/hour M/hour M/hour M/hour DCNo. minutes .times. liter Y (%) .times. liter Y (%) .times. liter Y (%) .times. liter Y (%) %__________________________________________________________________________31 10 6.82 61 1.04 9 1.84 17 1.45 13 18.632 20 3.78 46 0.65 8 1.57 19 2.13 26 27.133 35 1.33 22 0.49 8 2.64 43 1.66 27 35.634x 35 2.18 35 0.30 5 0.81 13 2.86 47 27.435 50 1.2 27 0.30 7 1.51 34 1.42 32 36.9__________________________________________________________________________ x: this experiment was carried out at 205.degree. C.
EXAMPLES 36 to 38
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.64 mg atom of cobalt, in the form of cobalt iodide;
(v) triruthenium dodecacarbonyl, in the amount shown in Table IV below;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 2.27 mmols of methyl iodide; and
(viii) 15 mmols of tetraethylammonium iodide.
The results obtained after a reaction time of 35 minutes at 205.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/1CO/H.sub.2 mixture, are also reported in Table IV below.
In this series of experiments, virtually no ethanol was detected.
TABLE IV__________________________________________________________________________ Acetaldehyde Ethyl acetate Acetic acidExample Ru M/hour M/hour M/hour DCNo. mg atoms .times. liter Y (%) .times. liter Y (%) .times. liter Y (%) %__________________________________________________________________________36 0.17 2.04 68 0.29 10 0.69 23 17.637 0.33 2.30 60 0.41 11 1.12 29 22.338 0.65 2.94 77 0.46 12 0.39 10 22.2__________________________________________________________________________
EXAMPLE 39
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl benzoate (635 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.4 mg atom of cobalt, in the form of cobalt iodide;
(v) 2.35 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 33.4 mg atoms of chromium, in the form of chromium acetate;
(vii) 9.72 mmols of methyl iodide; and
(viii) 15 mmols of sodium iodide.
After a reaction time of 30 minutes at 214.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/2CO/H.sub.2 mixture, the formation of:
(1) 0.27 M/hour.times.liter of acetaldehyde;
(2) 1.78 M/hour.times.liter of ethanol;
(3) 2.52 M/hour.times.liter of ethyl acetate; and
(4) 0.57 M/hour.times.liter of ethyl benzoate;
was determined.
EXAMPLE 40
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl benzoate (635 mmols);
(ii) 21.4 g of benzoic acid (175 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.40 mg atom of cobalt, in the form of cobalt iodide;
(v) 2.34 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 33.4 mg atoms of chromium, in the form of chromium acetate;
(vii) 9.5 mmols of methyl iodide; and
(viii) 15 mmols of sodium iodide.
After a reaction time of 30 minutes at 215.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 1/2CO/H.sub.2 mixture, the formation of:
(1) 2.48 M/hour.times.liter of ethanol;
(2) 0.86 M/hour.times.liter of ethyl acetate;
(3) 0.83 M/hour.times.liter of acetic acid; and
(4) 1.46 M/hour.times.liter of ethyl benzoate;
was determined.
EXAMPLE 41
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 21.4 g benzoic acid (175 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.22 mg atom of cobalt, in the form of cobalt iodide;
(v) 1.30 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 16.7 mg atoms of chromium, in the form of chromium acetate;
(vii) 3.51 mmols of methyl iodide; and
(viii) 11.9 mmols of caesium iodide.
After a reaction time of 60 minutes at 214.degree. C., with the pressure in the autoclave being maintained at about 260 bars by periodically introducing additional amounts of a 1/2CO/H.sub.2 mixture, the formation of:
(1) 0.13 M/hour.times.liter of acetaldehyde;
(2) 0.73 M/hour.times.liter of ethanol;
(3) 2.22 M/hour.times.liter of ethyl acetate; and
(4) 0.02 M/hour.times.liter of ethyl benzoate;
was determined.
EXAMPLE 42
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 73 ml of methyl acetate (914 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 5 ml of water (280 mmols);
(iv) 0.22 mg atom of cobalt, in the form of cobalt acetate tetrahydrate;
(v) 0.65 mg atom of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 40 mg atoms of chromium, in the form of chromium acetate; and
(vii) 17.9 mmols of methyl iodide.
After a reaction time of 20 minutes at 214.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 13/1CO/H.sub.2 mixture, the formation of:
(1) 0.98 M/hour.times.liter of acetaldehyde (Y=32%);
(2) 0.031 M/hour.times.liter of ethanol (Y=1%);
(3) 0.052 M/hour.times.liter of ethyl acetate (Y=1.7%); and
(4) 2.02 M/hour.times.liter of acetic acid (Y=65%);
was determined (DC=11.3%).
EXAMPLE 43
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 0.6 ml of water (33 mmols);
(iv) 0.22 mg atom of cobalt, in the form of cobalt acetate tetrahydrate;
(v) 1.31 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl; and
(vi) 15 mg atoms of chromium, in the form of CrI.sub.3.9H.sub.2 O.
After a reaction time of 20 minutes at 214.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 2/1CO/H.sub.2 mixture, the formation of:
(1) 1.49 M/hour.times.liter of acetaldehyde (Y=18%);
(2) 0.65 M/hour.times.liter of ethanol (Y=8%);
(3) 3.55 M/hour.times.liter of ethyl acetate (Y=44%); and
(4) 2.4 M/hour.times.liter of acetic acid (Y=30%);
was determined (DC=29%).
EXAMPLE 44
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.22 mg atom of cobalt, in the form of cobalt acetate tetrahydrate;
(v) 1.31 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 15 mg atoms of chromium, in the form of CrI.sub.2 ; and
(vii) 30 mmols of sodium iodide.
After a reaction time of 20 minutes at 214.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 2/1CO/H.sub.2 mixture, the formation of:
(1) 1.00 M/hour.times.liter of acetaldehyde (Y=15%);
(2) 0.99 M/hour.times.liter of ethanol (Y=15%);
(3) 2.63 M/hour.times.liter of ethyl acetate (Y=41%); and
(4) 1.81 M/hour.times.liter of acetic acid (Y=28%);
was determined (DC=21.4%).
EXAMPLE 45
Using the autoclave and the procedure described above, an experiment was carried out on a charge consisting of:
(i) 80 ml of methyl acetate (1,000 mmols);
(ii) 20 ml of acetic acid (350 mmols);
(iii) 3 ml of water (170 mmols);
(iv) 0.22 mg atom of cobalt, in the form of cobalt acetate tetrahydrate;
(v) 1.31 mg atoms of ruthenium, in the form of triruthenium dodecacarbonyl;
(vi) 15 mg atoms of chromium, in the form of chromium hexacarbonyl;
(vii) 30 mg atoms of iodine; and
(viii) 30 mmols of sodium iodide.
After a reaction time of 20 minutes at 214.degree. C., with the pressure in the autoclave being maintained at about 250 bars by periodically introducing additional amounts of a 2/1CO/H.sub.2 mixture, the formation of:
(1) 1.10 M/hour.times.liter of acetaldehyde (Y=21%);
(2) 0.90 M/hour.times.liter of ethanol (Y=17%);
(3) 1.73 M/hour.times.liter of ethyl acetate (Y=34%); and
(4) 1.43 M/hour.times.liter of acetic acid (Y=28%);
was determined (DC=17.5%).
While the invention has been described in terms of various preferred embodiments, the skilled artisan will appreciate that various modifications, substitutions, omissions, and changes may be made without departing from the spirit thereof. Accordingly, it is intended that the scope of the present invention be limited solely by the scope of the following claims.

Number	Name	Date
4133966	Pretzer et al.	Jan 1979
4189441	Braca et al.	Feb 1980
4239924	Pretzer et al.	Dec 1980

Hydrocarbonylation/carbonylation of alkyl carboxylates

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (3)