Hydrofining employing treated alumina material in fixed beds

Abstract

A hydrotreating process comprises contacting a substantially liquid hydrocarbon-containing feed stream, which contains compounds of sulfur and metals (preferably Ni and/or V), in the presence of a fixed catalyst bed comprising (a) at least one layer of impregnated substantially spherical alumina-containing particles which have been prepared by a process comprising the steps of impregnating specific starting material with at least one dissolved magnesium compound and then heating the thus impregnated material at about 500.degree.-900.degree. C. for improved crush strength retention. In a preferred embodiment, the fixed catalyst bed further comprises at least one layer (b) of catalyst particles comprising a refractory inorganic carrier and at least one hydrogenation promoter. A composition of matter comprising the impregnated, spherical alumina-containing particles described above, and a process for preparing them are also provided.

Description

BACKGROUND OF THE INVENTION

This invention relates to the preparation of impregnated, substantially spherical alumina-containing particles having improved crush strength retention. In another aspect, this invention relates to a process for hydrotreating hydrocarbon-containing oils, which also contain sulfur and metal impurities, in the presence of a fixed bed comprising at least one layer of impregnated, substantially spherical alumina-containing particles. In still another aspect, this invention relates to the use of said at least one layer of impregnated, substantially spherical alumina-containing particles as support layer in a fixed catalyst bed. In a further aspect, this invention relates to a process for catalytically hydrotreating hydrocarbon-containing oils in the presence of water. In still another aspect, this invention relates to a fixed multi-layer hydrotreating catalyst bed system comprising at least one layer of substantially spherical alumina-containing particles.

Fixed beds of hydrotreating catalysts are used in many oil refineries. Examples of processes in which fixed hydrotreating (hydrofining) catalyst beds are used include hydrodenitrogenation hydrodesulfurization and hydrodemetallization of heavy oils. Generally, a layer of shaped, substantially inert ceramic particles at the bottom of the fixed bed reactor is used to support a column of one or more layers of hydrotreating catalyst. The same shaped, substantially inert material can also be employed as the top layer (i.e., above one or more layers of hydrotreating catalyst) or between layers of hydrotreating catalyst, so as to provide improved flow dispersion of feed oil passing downwardly through the fixed catalyst bed. More recently, promoted alumina spheres, which offer some catalytic activity, have been suggested as replacement for these substantially inert ceramic support particles which generally have little or no catalytic activity for hydrodesulfurization and -demetallization. However, there is an ever present need to develop improved substantially spherical alumina-containing support particles having higher crush strength and higher resistance to specific feed components, such as water, than those presently known, so as to employ these improved alumina-containing support particles under very severe hydrotreating conditions.

SUMMARY OF THE INVENTION

It is an object of this invention to provide impregnated, substantially spherical alumina-containing particles having high crush strength retention. It is another object of this invention to provide a process for making impregnated, substantially spherical alumina-containing particles having high crush strength retention. It is still another object of this invention to provide a process for hydrotreating substantially liquid hydrocarbon-containing feed streams employing a fixed catalyst bed comprising at least one layer of impregnated, substantially spherical alumina-containing particles having high crush strength retention. It is a further object of this invention to provide a process for hydrotreating substantially liquid hydrocarbon-containing feed streams in the presence of water and a fixed catalyst bed comprising at least one layer of impregnated, substantially spherical alumina-containing particles having high crush strength retention. It is still another object of this invention to provide a multi-layer catalyst bed comprising at least one layer of impregnated, substantially spherical alumina-containing particles having high crush strength retention (when exposed to oil and water under hydrotreating conditions). It is a still further embodiment of this invention to employ said multi-layer catalyst bed in said process for hydrotreating substantially liquid hydrocarbon-containing feed streams. Further objects and advantages will be apparent from the detailed description and the appended claims.

In accordance with this invention, a hydrotreating process comprises the step of contacting a substantially liquid (i.e., liquid at the hydrotreating conditions) hydrocarbon-containing feed stream, which also contains compounds of sulfur and metals, with a free hydrogen containing gas in the presence of a fixed catalyst bed comprising

(a) at least one layer of impregnated, substantially spherical alumina-containing particles,

under such hydrotreating conditions as to obtain at least one liquid hydrocarbon-containing product stream having lower concentrations of sulfur and metals than said hydrocarbon-containing feed stream;

wherein said impregnated, substantially spherical alumina-containing particles in catalyst layer (a) have been prepared by a process comprising the steps of

(A) impregnating (i) a starting material of substantially spherical alumina-containing particles, which have an initial average particle diameter of at least about 0.05 inch, an initial surface area (determined by the BET/N.sub.2 method; ASTM D3037) of at least about 20 m.sup.2 /g, an initial pore volume (determined by mercury intrusion porosimetry at a pressure ranging from 0to 50,000 psig) of at least about 0.1 cc/g, and an initial content of Al.sub.2 O.sub.3 of at least about 80 weight-%, with (ii) a solution (preferably aqueous) comprising at least one dissolved magnesium compound; and

(B) heating the material obtained in step (A) at a temperature in the range of from about 500.degree. to about 900.degree. C. for a period of time of at least 10 minutes, preferably for a period of time in the range of about 10 minutes to about 20 hours, under such heating conditions as to convert at least a portion of said at least one magnesium compound absorbed (taken up) in step (A) to magnesium oxide and to obtain a material having a higher retention of crush strength (measured after exposure for about 100 hours to a liquid hydrocarbon-containing stream which contains at least about 0.5 weight-% sulfur, under hydrotreating conditions at about 2250 psig total pressure, about 350 psig partial pressure of steam and about 700.degree. F.) than said starting material.

Preferably a drying step (A1) after step (A) is carried out, so as to remove at least a portion of water from the material obtained in step (A). In this preferred embodiment, step (B) is carried out with the product obtained in step (A1).

In one preferred embodiment, said metals in said liquid hydrocarbon-containing feed stream comprise at least one of nickel and vanadium, preferably about 3-500 ppmw Ni and about 5-1,000 ppmw V (ppmw=parts per million parts of feed stream). In another preferred embodiment, said substantially liquid hydrocarbon-containing feed stream also contains water (preferably about 0.5-10 volume-%). In a further preferred embodiment, steam is injected into the fixed catalyst bed during said contacting under hydrotreating conditions.

In a particularly preferred embodiment, said catalyst bed additionally comprises

(b) at least one layer of catalyst particles [i.e., hydrotreating catalyst particles; different from the particles in layer (a)] comprising a refractory inorganic carrier (preferably alumina) and at least one (i.e., one or a mixture of two or more) hydrogenation promoter selected from the group consisting of transition metals of Groups IIIB, IVB, VB, VIB, VIIB, VIII, IB and IIB of the Periodic Table (as defined in Webster's New Collegiate Dictionary, 1977) and compounds of these metals (preferably Y, La, Ce, Ti, Zr, Cr, Mo, W, Mn, Re, Ni, Co and Cu). The most preferred hydrogenation promoters include oxides and/or sulfides of Mo, Co, Ni and mixtures of two or more of these compounds. In addition to or in lieu of these hydrogenation promoters, one or more compounds of phosphorus can also be present in these catalyst particles.

Also in accordance with this invention, there is provided a composition of matter (suitable as a hydrotreating catalyst composition) comprising (preferably consisting essentially of) impregnated substantially spherical alumina-containing particles, having been prepared by the process comprising steps (A) and (B), and optionally also step (A1), as described above. Further in accordance with this invention, there is provided a process for preparing said composition of matter comprising steps (A) and (B), and optionally also step (A1), as described above.

Further in accordance with this invention, a fixed catalyst bed (preferably a hydrotreating catalyst bed) is provided comprising

(a) at least one catalyst bed layer of impregnated, substantially spherical alumina-containing particles of this invention, having been prepared by the process composing steps (A) and (B), and optionally also step (A1), as described above; and

(b) at least one catalyst bed layer of catalyst particles [preferably hydrotreating catalyst particles; different from the particles in layer (a)] comprising a refractory inorganic carrier material and a hydrogenation promoter, as defined above in the description of the hydrotreating process of this invention.

In one preferred embodiment of this invention, said impregnated, substantially spherical alumina-containing particles, which can be used in catalyst bed layer (a), also contain at least one compound of at least one element selected from the group consisting of Y, La, Ce, Ti, Zr, Cr, Mo, W, Mn, Re, Ni, Co, Cu, Zn and P, preferably oxide and/or sulfide of Mo and/or Co and/or Ni (more preferably containing about 0.1-2.0 weight-% Mo) as hydrotreating promoters. In a more preferred embodiment, the impregnating solution used in step (A) (described above in the description of the hydrotreating process) comprises at least one compound of at least one of the elements listed immediately above.

In a further preferred embodiment, said at least one catalyst bed layer (a) is located as support layer below said at least one catalyst bed layer (b). In a still further preferred embodiment, said at least one layer (a) is located on top of said at least one catalyst layer (b). In still another embodiment, one catalyst bed layer (a) is located below said catalyst bed layer (b) and another catalyst bed layer (a) is located above said catalyst bed layer (b). In a further embodiment, layer (a) is located between two layers (b). These configurations of catalyst bed layers described immediately above are preferably employed in the hydrotreating process of this invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the arrangement of a fixed multi-layer catalyst bed used for testing catalysts in hydrotreating processes.

FIG. 2 is a graph showing the dependence of crush strength (determined after use in hydrotreating test) of alumina-containing particles on the calcination temperature.

FIG. 3 exhibits pore distribution curves for several alumina-containing particles.

DETAILED DESCRIPTION OF THE INVENTION

(A) Hydrotreating Process

Any suitable hydrocarbon-containing feed stream, which is substantially liquid at the hydrotreating conditions and contains compounds of metals (in particular nickel and/or vanadium) and sulfur as impurities, can be employed in the hydrotreating process of this invention. Generally these feed streams also contain coke precursors (measured as Ramsbottom carbon) and nitrogen compounds as impurities. Suitable hydrocarbon-containing feed streams include crude oil (crude petroleum) and heavy fraction thereof, heavy oil extracts, liquid coal pyrolyzates, liquid products from coal liquification, liquid extracts and liquid pyrolyzates from tar sands, shale oil and heavy shale oil fractions. The process of this invention is particularly suited for treating heavy crudes and heavy petroleum residua, which generally have an initial boiling point (at atmospheric pressure) in excess of about 400.degree. F., preferably in excess of about 600.degree. F. These heavy oil feeds generally contain at least about 5 ppmw (parts by weight per million by weight of hydrocarbon-containing feed) vanadium (preferably 5-1000 ppmw V), at least about 3 ppmw Ni (preferably about 3-500 ppmw Ni), at least about 0.5 weight-% sulfur (preferably about 0.5-5.0 weight-% S), about 0.2-2.0 weight-% nitrogen, and about 1-20 weight-% Ramsbottom carbon residue (determined by ASTM D524). The API.sub.60 gravity (measured at 60` F.) of these feeds is generally about 5-30 (preferably about 8-25).

The substantially liquid hydrocarbon-containing feed stream can be substantially free of water but can, in a preferred embodiment, also contain at least about 0.3 weight-% water, generally about 0.3 to about 20 weight-% H.sub.2 O, preferably about 0.5 to about 10 weight-% H.sub.2 O, more preferably about 1.0 to about 5.0 weight-% H.sub.2 O. Water can be residual water which has not been removed from heavy crude oil, or water can be added as liquid water to the hydrocarbon-containing feed stream prior to its contact with the fixed catalyst bed, or water can be added as steam to the hydrocarbon-containing feed stream prior to its contact with the fixed catalyst bed, or water can be added as steam concurrently with the hydrocarbon-containing feed stream prior to its contact with the fixed catalyst bed. Some oil refineries use steam in this manner to alleviate coke deposition in the fixed catalyst bed and thus retard fouling and deactivation of the fixed catalyst bed. The hydrotreating process of this invention is particularly suited for feed streams that contain water because the alumina-containing particles in layer (a), in accordance with this invention, are particularly resistant to the detrimental effect of water during hydrotreating.

The hydrotreating process of this invention can be carried out in any apparatus whereby an intimate contact of the fixed hydrotreating catalyst bed with said hydrocarbon-containing feed stream and a free hydrogen containing gas is achieved, under such conditions as to produce a hydrocarbon-containing product having reduced levels of metals (in particular Ni and V) and sulfur. Generally, a lower level of nitrogen and Ramsbottom carbon residue and higher API gravity are also attained in this hydrotreating process. The hydrotreating process of this invention can be carried out as a batch process or, preferably, as a continuous down-flow process, more preferably in a tubular reactor containing one or more fixed catalyst beds (as will be described later) or in a plurality of fixed bed reactors in parallel or in series. The hydrocarbon-containing product stream can be distilled, e.g., in a fractional distillation unit, so as to obtain fractions having different boiling ranges.

Any suitable reaction time (contact time) between the fixed catalyst bed, the hydrocarbon-containing feed stream, the hydrogen-containing gas and, optionally, steam can be utilized. In general, the reaction time will be in the range of from about 0.05 hours to about 10 hours, preferably from about 0.4 to about 5 hours. In a continuous fixed bed operation, this generally requires a liquid hourly space velocity (LHSV) in the range of from about 0.10 to about 10 cc of feed per cc of catalyst per hour, preferably from about 0.2 to about 2.5 cc/cc/hr.

The hydrotreating process employing the fixed catalyst bed of the present invention can be carried out at any suitable temperature. The reaction temperature will generally be in the range of about 250.degree. C. to about 550.degree. C. and will preferably be in the range of about 300.degree. C. to about 450.degree. C. Higher temperatures do improve the removal of impurities but temperatures which will have adverse effects on the hydrocarbon containing feed stream, such as excessive coking, will usually be avoided. Also, economic considerations will usually be taken into account in selecting the operating temperature.

Any suitable pressure may be utilized in the hydrotreating process. The reaction pressure will generally be in the range from of about atmospheric pressure (0 psig) to up to 5,000 psig. Preferably, the pressure will be in the range of from about 100 to about 2500 psig. Higher pressures tend to reduce coke formation, but operating at high pressure may be undesirable for safety and economic reasons.

Any suitable quantity of free hydrogen can be added to the hydrotreating process. The quantity of hydrogen used to contact the hydrocarbon containing feed stream will generally be in the range of from about 100 to about 10,000 standard cubic feet H.sub.2 per barrel of hydrocarbon containing feed stream and will more preferably be in the range of from about 1,000 to about 5,000 standard cubic feed H.sub.2 per barrel of the hydrocarbon containing feed stream. Either pure hydrogen or a free hydrogen containing gas mixture (e.g., H.sub.2 and CH.sub.4, or H.sub.2 and CO, or H.sub.2 and N.sub.2) can be used.

If desired, the hydrotreating process of this invention may comprise the step of adding at least one added thermally decomposable metal compound into the hydrocarbon-containing feed stream prior to its being contacted with the catalyst composition of this invention. The metal in the added thermally decomposable metal compound is selected from compounds of metals of Group IIIB, IVB, VIB, VIIB, VIII, IB and IIB of the Periodic Table (as defined above). Preferred metals are molybdenum, tungsten, manganese, chromium, zirconium and zinc. Molybdenum is a particularly preferred metal which may be introduced as a carbonyl, acetate, acetylacetonate, carboxylate (e.g., octoate), naphthenate, mercaptide, dithiophosphate or dithiocarbamate. Molybdenum hexacarbonyl, molybdenum dithiophosphate and molybdenum dithiocarbamate are particularly preferred additives. The life of the catalyst composition and the efficiency of the demetallization process is improved by introducing at least one of the above-cited decomposable metal compounds into the hydrocarbon containing feed, which also contains metals such as nickel and vanadium. These additives can be added continuously or intermittently and are preferably added at a time when the catalyst composition of this invention has been partially deactivated so as to extend its life. Any suitable concentration of the additive may be added to the hydrocarbon containing feed stream to result in a concentration of the metal (preferably molybdenum) of said decomposable compounds in the range of from about 1 to about 1,000 parts per million by weight and more preferably in the range of about 5 to about 100 parts per million in said feed stream.

At least a portion of the hydrotreated product stream which has been produced in the process of this invention can subsequently be cracked, e.g., in a fluidized catalytic cracking unit, employing zeolite- or clay-containing cracking catalyst, under such conditions as to produce lower boiling hydrocarbon materals, such as gasoline and kerosene, suitable for use as fuels and other useful products. It is within the scope of this invention to hydrotreat the product stream having reduced contents of metals and sulfur in a second hydrotreating process using a different fixed catalyst bed, such as zinc titanate-supported Ni/MoO.sub.3 catalysts, for further removal of sulfur and other impurities (e.g., metals) before the product stream is introduced into a cracking reactor and treating under cracking conditions.

(B) Composition of Matter and Preparation Thereof

As has been described in the "Summary of the Invention", the impregnated, substantially spherical alumina-containing particles of this invention are prepared by a process comprising the steps of impregnating and then heating a suitable starting material under suitable conditions, so as to obtain a product having a specific set of properties. Any suitable substantially spherical alumina containing particles which have the following initial parameters can be used as said starting mateial for step (A): average particle diameter of at least about 0.05 inch, preferably in the range of from about 0.05 to about 1.5 inch, more preferably from about 0.1 to about 1.0 inches; surface area (determined by the BET/N.sub.2 method; ASTM D3037) of at least about 20 m.sup.2 /g, preferably in the range of from about 40 to about 600 m.sup.2 /g, more preferably in the range of from 100 to about 400 m.sup.2 /g; a pore volume, as determined by mercury intrusion porosimetry (carried out at room temperature and a mercury pressure varying from 0 psi to about 60,000 psi, using an Autopore 9200 instrument of Micromeritics, Norcross, GA), of at least about 0.1 cc/g, preferably in the range of from about 0.2 to about 1.0 cc/g., more preferably from about 0.3 to about 0.7 cc/g; and content of alumina, which generally is a mixture of gamma-alumina and amorphous alumina, of at least about 80 weight-% Al.sub.2 O.sub.3, preferably in the range of from about 90 to about 99 weight-% Al.sub.2 O.sub.3, more preferably from about 93 to about 98 weight-% Al.sub.2 O.sub.3. The preferred starting material has a normalized crush strength per particle, determined as side plate crush strength by means of a mechanical force gauge, such as the one described in Example I, of at least 100 lb. per inch diameter per particle, preferably in the range of from about 100 to about 400 lb. per inch diameter per particle; and a Na content of less than about 3.0 weight-%, more preferably less than about 1.0 weight-% Na, most preferably less than about 0.5 weight-% Na. A presently particularly preferred starting material is a commercially available spherical, alumina-containing Claus catalyst material that is marketed by the Aluminum Company of America, Pittsburgh, PA under the product designation of S-100 (see Example II).

Preparation step (A), as described above, can be carried out in any suitable manner. The solvent in the impregnating solution used in step (A) generally comprises water, and preferably consists essentially of water. Suitable solvents which can be used besides water are alcohols such as methanol, ethanol, ethylene glycol and the like, acetone, esters such as ethyl acetate and the like. However, these non-aqueous solvents are presently not preferred.

The solute in the impregnating solution used in step (A) can be any magnesium compound that is at least partially soluble in water or mixtures of two or more of these magnesium compounds. Non-limiting examples of suitable Mg compounds are Mg(NO.sub.3).sub.2, Mg(HCO.sub.3).sub.2, Mg(HSO.sub.4).sub.2, MgSo.sub.4, Mg acetate and the like, preferably Mg(NO.sub.3).sub.2. The concentration of the Mg compound in the impregnating solution generally is in the range of from about 10.sup.-4 to about 2.0 mol/l of Mg (i.e., g-atoms Mg contained in the dissolved Mg compound(s) per liter solution), preferably from about 0.01 to about 1.0 mol/l Mg.

The impregnation of the alumina-containing starting material with the impregnating solution in step (A) can be carried out in any suitable manner. Preferably, the starting material is soaked with the impregnating solution, more preferably with agitation such as mechanical stirring, for a period of time long enough (preferably about 0.5-3 days) to allow said at least one dissolved Mg compound to penetrate into the substantially spherical, alumina-containing particles of the starting material, more preferably to the core of these particles. Any suitable weight ratio of said starting material to the impregnating solution can be employed. Preferably, the weight ratio of said starting material to said impregnating solution will be in the range of from about 0.1:1 to about 2.0:1, more preferably from about 0.3:1 to about 1.2:1. Even though presently not preferred, other impregnating methods can be applied, such as spraying of the impregnating solution, which comprises at least one dissolved Mg compound, onto the substantially spherical, alumina-containing particles of the starting material.

Even though the material obtained in step (A) can be directly processed in step (B), it is presently preferred to substantially dry the impregnated material obtained in step (A) in drying step (A1). The drying step (A1) is generally carried out in air or an inert gas, at a temperature ranging from about 25.degree. C. to about 200.degree. C. (preferably 50.degree.-100.degree. C.) so as to remove the greatest portion of water from the mixture obtained in step (B). Vacuum conditions may be employed but are presently not preferred. The at least partially dried mixture generally contains less than about 20 weight-% water. The rate of drying is controlled so as to avoid surges of water vapor that can cause the impregnating solution to splatter and can cause the solute to excessively accumulate in surface regions of the solid particles. Depending on the drying temperature and specific drying conditions (such as extent of air movement; thickness of the solid layer to be dried), the drying time ranges generally from about 0.5 hour to about 100 hours, preferably from about 1 hour to about 30 hours.

The impregnated alumina-containing material obtained in step (A), or alternatively step (A1), is heated (calcined) at a temperature in the range of from about 500.degree. to about 900.degree. C., preferably from about 550.degree. to about 800.degree. C., more preferably from about 600.degree. to about 750.degree. C. The heating time is at least 10 minutes, preferably in the range of from about 10 minutes to 20 hours, more preferably from about 0.5 to about 10 hours. The pressure can be atmospheric (preferred) or subatmospheric or superatmospheric. The heating process can be carried out in a free oxygen containing gas atmosphere, such as air, or in an inert or in a reducing gas atmosphere. Presently heating in an O.sub.2 -containing gas is preferred. It is believed that heating in an O.sub.2 -containing gas insures that Mg compounds taken up by the starting material in step (A) is substantially converted to MgO in step (B). The gas atmosphere may contain water vapor, but the amount of water vapor should be minimized to less than about 10 volume percent.

Generally, the above-described heating (calcining) of the impregnated spherical, alumina-containing material results in a tolerable decrease in surface area, in a slight increase in total pore volume, but in a substantial increase of the pore volume in pores having a pore diameter in the 40-200 Angstroms (A) range. Preferably, the impregnated, substantially spherical alumina-containing particles in catalyst layer (a), obtained by the preparation process of this invention, have a pore volume of pores in the 40-200 A pore diameter range in excess of about 50%, more preferably from about 50 to about 90% of the total pore volume. Preferably, the total BET/N.sub.2 surface area of the impregnated, substantially spherical particles of this invention is in the range of from about 50 to about 300 m.sup.2 /g, and the total pore volume (determined by mercury porosimetry, discussed above) is in the range of from about 0.3 to about 0.8 cc/g. The Mg content of the calcined substantially spherical material of this invention preferably contains at least about 0.006 weight-% Mg (i.e., about 0.01 weight-% MgO), more preferably about 0.06 to about 6.0 weight-% Mg (i.e., about 0.1 to about 10 weight-% MgO), more preferably about 0.3 to about 4.0 weight-% Mg (i.e., about 0.5 to about 6.6 weight-% MgO).

The crush strength of the impregnated, substantially spherical alumina-containing particles of this invention is preferably measured after they have been used in a hydrotreating process in the presence of water, as has been described above and also in Example I, so as to determine the retention of initial crush strength under these severe hydrotreating conditions (about 2250 psi total pressure, about 400 psi partial pressure of steam, 700.degree. F., 100 hours; with at least about 0.5 weight-% sulfur in the hydrocarbon-containing feed). The thus determined crush strength generally exceeds 150 lb. per inch diameter per particle and preferably is in the range of about 150 to about 350 lb./inch/particle.

The impregnated, substantially spherical alumina-containing particles of this invention can be promoted with at least one element or compound at least one element (i.e., one or mixture of two or more) selected from the group consisting of Y, La, Ce, Ti, Zr, Hf, Cr, Mo, W, Mn, Re, Ni, Co, Cu, Zn, P (as phosphite and/or phosphate), preferably Mo, Ni and Co, more preferably Mo. The total promoter level generally is relatively low and suitably ranges from about 0.01 to about 3.0 weight-% of said at least one element, preferably from about 0.1 to about 2.0 weight-%, more preferably from about 0.2 to about 1.0 weight-% of said at least one element (most preferably Mo).

Any suitable technique for promoting the particles of this invention can be employed, preferably the impregnating solution used in step (A) contains one or more of the above-described promoters besides (NH.sub.4).sub.2 SO.sub.4. The thus obtained particles, which additionally contain at least one promoter compound, then undergo step (B), optionally after step (A1), as described above. It is, of course, possible (yet presently not preferred) to carry out step (A) without having any transition metal and/or phosphorus promoter compound present in the impregnating solution, and to impregnate the calcined material obtained in step (B) with a solution containing at least one promoter compound, followed by drying and calcining (preferably at about 500.degree.-900.degree. C.) of the thus twice-impregnated material (so as to at least partially convert the at least one transition metal compound to oxides of said metal). Generally the crush strength of the impregnated, substantially spherical alumina-containing particles is not substantially affected by the presence of one or more promoters.

(C) Fixed Catalyst Bed

In accordance with this invention, a fixed catalyst bed, suitable for hydrotreating substantially liquid hydrocarbon-containing feed streams which also contain sulfur and metal compounds (as has been described earlier for one embodiment of this invention), is provided comprising at least one layer (a) of the impregnated, substantially spherical alumina-containing material of this invention.

In a preferred embodiment of this invention the fixed catalyst bed comprises at least one layer (a), as described above, and at least one layer (b) of catalyst particles, different from those in layer (a). The catalyst particles in layer (b) generally comprise an inorganic refractory carrier. Non-limiting examples of such inorganic refractory carrier materials are those that comprise (preferably consist essentially of) alumina (preferred), aluminum phosphate, silica, titania, zirconia, zirconium phosphate, ceria, boria, magnesia, silica-alumina, titania-silica, titania-alumina. In addition to the carriers, the catalyst particles in catalyst bed layer (b) comprise at least one promoter selected from compounds of metals of Groups IIIB, IVB, VB, VIB, VIIB, VIII, IB and IIB of the Periodic Table. Presently preferred promoters are compounds of metals selected from the group consisting of Y, La, Ce, Ti, Zr, Cr, Mo, W, Mn, Re, Ni, Co and Cu, more preferably oxides and/or sulfides of these metals, most preferably Mo, Ni, Co, and mixtures of any of these metal oxides and sulfides. Phosphorus compounds of these metals can also be present. Generally the total level of promoter ranges from about 0.5 to about 30 weight-%, preferably from about 1 to about 15 weight-%, based on the elemental metal. Generally the BET/N.sub.2 surface area of the particles in layer (b) is in the range of from about 50 to about 500 m.sup.2 /g, and their pore volume (measured by mercury porosimetry) is in the range of from about 0.2 to about 2.0 cc/g.

The catalyst particles in layer (b) can be prepared by any suitable technique such as contacting of the carrier (preferably alumina) with one or more solutions containing one or more compounds of the promoter metals (plus, optionally, one or more compounds of phosphorus) and subsequent drying and calcining (this method presently being preferred) as has been described for promoted particles in layer (a); or by coprecipitation e.g., of hydrogels of alumina and promoter metal (e.g., Ni, Co, Mo), followed by drying and calcining. Suitable commercially avilable catalyst materials for layer (b) are described in Example I.

Layers (a) and (b) can be arranged in the fixed catalyst bed of this invention in any suitable manner. In one preferred embodiment layer (a) is placed as support layer below at least one catalyst layer (b). In another embodiment, layer (a) is placed as a cover layer on top of at least catalyst layer (b). In a further embodiment, layer (a) is placed between at least two catalyst layers (b). In a still further embodiment, in which at least three layers (a) and at least two catalyst layers (b) (which are different from each other) are employed, one layer (a) is placed on top of said at least two catalyst layers (b), one layer (a) is placed as interlayer between two different catalyst layers (b), and a third layer (a) is placed below said at least two lower catalyst layer (b). Another suitable catalyst bed arrangement is shown in FIG. I. The weight ratio of each catalyst layer (a) to each catalyst layer (b) is generally in the range of from about 1:100 to about 1:1, preferably from about 1:20 to about 1:5.

The dimensions of catalyst bed layer (a) comprising the substantially spherical alumina-containing particles obtained by the above-described heating process are not critical and depend on the dimension of the hydrotreating reactor that holds the fixed catalyst bed. Generally the height of each layer (a) ranges from about 1 to about 50 feet in commercial hydrotreating operations. It is within the scope of this invention to have additionally inert particles present (up to 50 weight-%) in layer (a), such as inert ceramic particles, in particular Denstone D-57. The height of each catalyst layer (b) can vary widely, depending on the particular reactor dimensions.

If desired, the fixed catalyst bed of this invention can be sulfided by treatment with a fluid stream that contains sulfur compounds, generally prior to said hydrotreating process. Non-limiting examples of such fluid streams are solutions or mercaptans, mercaptoalcohols, organic sulfides and organic disulfides in a suitable organic solvent (such as gas oil and other petroleum fractions), and gas streams that comprise H.sub.2 S, such as mixtures of H.sub.2 and H.sub.2 S. This sulfiding procedure is generally carried out at an elevated temperature (preferably at about 400.degree.-700.degree. F.) for a period of time sufficient (preferably from about 0.5-20 hours) so as to convert at least a portion of any compounds of one or more metals contained in particles of layer (b), and optionally also in particles of layer (a), to sulfides of said one or more metals.

In general, the fixed catalyst bed of this invention is utilized primarily for demetallization and desulfurization. The time in which the fixed catalyst bed of this invention will maintain its activity for the above process will depend upon the hydrotreating conditions and the composition of the hydrocarbon-containing feed. Generally, the temperature of the hydrotreating process is gradually increased to compensate for loss of catalyst activity due to fouling (e.g., due to deposition of coke and metals as the catalyst). The entire fixed catalyst bed or one or more layers of the fixed catalyst bed can, if desired, be regenerated when the catalytic activity has dropped below a desired level. Catalyst regeneration can be carried in-situ by discontinuing the flow of hydrogen and of the hydrocarbon-containing feed streams, purging the fixed bed reactor with an inert gas (e.g., N.sub.2), and then heating the fixed catalyst bed in a free oxygen-containing gas atmosphere (such as air), under such conditions as to remove carbonaceous materials and to at least partially convert sulfides of transition metals such as Mo, Co and/or Ni back to their oxides and/or phosphates. Preferably, however, the fixed bed layers are removed from the cooled hydrotreating reactor after said purging and are transferred to another reactor where the catalyst regeneration takes place. Generally the catalyst regeneration step is carried out at about 400.degree.-600.degree. C. and at a pressure of about 0-1,000 psig.

The following examples are presented in further illustration of the invention and are not to be considered as unduly limiting the scope of this invention.

EXAMPLE I

This example illustrates the evaluation of catalyst bed support particles in oil hydrotreating tests, in the presence of steam. The purpose of this evaluation procedure is to determine the hydrodemetallization activity and the retention of crush strength of these support particles under severe hydrotreating conditions, in the presence of steam.

The catalyst bed arrangement (simulating proportions of a typical refinery bed loading) which was used in the evaluation tests is shown in FIG. 1. The catalyst bed column had a diameter of about 0.75 inches. Particles A were substantially spherical alumina-containing particles, which can be any of the particles A1 through A15 described in more detail in Example II. Material B was a commercial alumina-supported hydrotreating catalyst comprising 0.9 weight-% Co, 0.5 weight-% Ni and 7.5 weight-% Mo, having a BET/N.sub.2 surface area of 174 m.sup.2 /g and a pore volume of 0.63 cc/g (measured by mercury intrusion porosimetry). Material C was a commercial alumina-based hydrotreating catalyst comprising 3.1 weight-% Ni, 7.9 weight-% Mo and 4.6 weight-% Ti having a BET/N surface area of 140 m.sup.2 -g and a pore volume (by Hg intrusion porosimetry) of 0.5 cc/g. Material D was a commercial alumina-based hydrotreating catalyst comprising 2.4 weight-% Co and 6.7 weight-% Mo, having a BET/N.sub.2 surface area of 290 m.sup.2 /g and pore volume (by Hg intrusion porosimetry) of 0.47 cc/g.

A heavy oil-water mixture containing about 4-8 volume-% H.sub.2 O was pumped to a metallic mixing T-pipe where it was mixed with a controlled amount of hydrogen gas. The heavy oil was a Maya 400F+ resid having an API.sup.60 gravity of 14.0, containing 3.8 weight-% sulfur and about 350 ppmw (Ni+V) (parts by weight of Ni+V per million parts by weight of oil feed). The oil/water/hydrogen mixture was pumped downward through a stainless steel trickle bed reactor which contained the multi-layer catalyst bed described above (see FIG. I). The tubular reactor was about 28.5 inches long, has an inner diameter of about 0.75 inches, and was fitted inside with a 0.25 inch O.D. axial thermocouple well. The reactor was heated by a 3-zone furnace. The reactor temperature was usually measured in four locations along the reactor bed by a traveling thermocouple that was moved within the axial thermocouple well.

Generally, the hydrotreating conditions were as follows: reaction temperature of about 690.degree.-710.degree. F.; liquid hourly space velocity (LHSV) of about 0.3 cc/cc catalyst/hour; about 2,250 psig total pressure; about 330-400 psig H.sub.2 O (steam) partial pressure; time on stream: about 100-200 hours. When it was desired to determine the desulfurization and demetallization activity of the catalyst bed, the liquid product was filtered through a glass filter and analyzed for sulfur, nickel and vanadium by plasma emission analysis.

After completion of the hydrotreating test, the reactor with catalyst bed was flushed with xylene so as to remove undrained oil. Thereafter, nitrogen gas was passed through the xylene-washed catalyst bed so as to dry it. The various catalyst layers were carefully removed. Particles A, B or C were tested for crush strength in a Mechanic Force Gauge D-75M of Hunter Spring, Division of Ametek, Hot Field, PA. A single sphere of A or B or C, the average diameter of which had been measured, was placed between the metal plates of D-75M, and the plates were slowly moved toward one another by means of an electric motor. The force applied to the plates was displayed by a gauge. The force necessary to fracture (crush) a catalyst sphere was recorded as the crush strength of the sphere. The normalized crush strength, defined as crush strength of a sphere divided by its average particle diameter (lb/sphere/inch diameter), was calculated.

EXAMPLE II

This example illustrates the preparation of the substantially spherical alumina-containing particles of this invention and of other alumina-containing catalyst bed particles.

Control Particles A1 were spherical, Co/Mo-promoted alumina particles, marketed by Shell Chemical Company, Houston, TX under the product designation "Shell 544", suitable as support balls for hydrotreating catalyst beds. Pertinent properties of Particles A1 were: diameter of 1/6 inch; cobalt content of 1.7 weight-%; molybdenum content of 5.3 weight-%; surface area of 300+ m.sup.2 /g; total pore volume of 0.47 cc/g; loss on ignition (LOI; weight loss when heated to 482.degree. C.) of 0.8 weight-%; compacted bulk density (compacted loading density) of about 0.83 g/cc; and side plate crush strength of 30+ lb/particle (i.e., about 190 lb/particle/inch diameter).

Control Particles A2 were substantially spherical, substantially unpromoted alumina-containing particles having an average particle diameter of 1/4 inch; a BET/N.sub.2 surface area of about 325 m.sup.2 /g; a total pore volume of about 0.50 cc/g; and average normalized individual ball crush strength of about 240 lb/particle/inch diameter (i.e., the actual crush strength of a 1/4" sphere was about 60 lb/particle); Al.sub.2 O.sub.3 content of about 94.6 weight-%; Na.sub.2 O content of about 0.35 weight-%; and LOI content (weight loss when heated from 250.degree. C. to 1200.degree. C.; a measure of hydroxyl content) of 5.0 weight-%. Particles A2 were supplied by Aluminum Company of America, Pittsburgh, PA under the product designation of S-100.

Control Particles A3 were obtained when Control Particles A2 were heated at about 650.degree. C. for about one hour.

Control Particles A4 were obtained by soaking 27.0 grams of Control Particles A2 with 50 cc of an aqueous solution containing 3.17 grams of dissolved Ca(NO.sub.3).sub.2.4H.sub.2 O for about 0.5-3 days, decanting excess solution, drying the thus impregnated particles and then calcining them at about 650.degree. C. for about 2 hours in air. Control Particles A4 contained about 1.6 weight-% CaO.

Control Particles A5 were prepared essentially in accordance with the procedure for Particles A4, except that 16.5 grams of Ca(NO.sub.3).sub.2.4H.sub.2 O (in 50 cc solution) were employed so as to provide particles containing about 8.0 weight-% CaO.

Invention Particles A6 were prepared essentially in accordance with the procedure for Particles A4, except that 3.4 grams of Mg(NO.sub.3).sub.2.6H.sub.2 O (in 50 cc solution) were employed (in lieu of dissolved Ca nitrate), so as to provide particles containing about 1.2 weight-% MgO.

Invention Particles A7 were prepared essentially in accordance with the procedure for Particles A4, except that 17.9 grams of Mg(NO.sub.3).sub.2.6H.sub.2 O (in 50 cc solution) were employed (in lieu of Ca nitrate), so as to provide particles containing about 5.6 weight-% MgO.

Control Particles A8 were obtained by soaking 27.0 grams of Control Particles A2 with 25 cc of an aqueous solution containing 0.82 grams of (NH.sub.4).sub.6 Mo.sub.7 O.sub.24.4H.sub.2 O for about 3 days, decanting excess solution, drying the impregnated particles at 120.degree. C. and calcining them in air at 650.degree. C. for 1 hour. Calcined Particles A8 contained 0.3 weight-% Mo.

Control Particles A9 were prepared essentially in accordance with the procedure for Particles A8, except that the aqueous impregnating solution additionally contained 0.184 grams ZnCl.sub.2. Calcined Particles A9 contained 0.3 weight-% Mo and about 0.2 weight-% ZnO.

Control Particles A10 were prepared essentially in accordance with the procedure for Particles A8, except that the aqueous impregnating solution additionally contained 1.84 grams ZnCl.sub.2. Calcined Particles A10 contained 0.3 weight-% Mo and about 2.3 weight-% ZnO.

Invention Particles A11 were prepared essentially in accordance with the procedure for Particles A8, except that the aqueous impregnating solution additionally contained 0.035 grams Mg(NO.sub.3).sub.2.H.sub.2 O. Calcined particles A11 contained 0.3 weight-% Mo and about 0.01 weight-% MgO.

Invention Particles A12 were prepared essentially in the same manner as Particles A11, except that 0.35 gram Hg(NO.sub.3).sub.2.H.sub.2 O was used. Calcined particles A12 contained 0.3 weight-% Mo and about 0.1 weight-% MgO.

Invention Particles A13 were prepared essentially in the same manner as Particles A11, except that 1.73 grams Mg(NO.sub.3).sub.2.H.sub.2 O were used. Calcined Particles A13 contained 0.3 weight-% Mo and about 0.6 weight-% MgO.

Invention Particles A14 were prepared essentially the same as Particles A13, except that calcined Particles A14 contained 0.3 weight-% Mo and about 1.2 weight-% MgO.

Invention Particles A15 were prepared essentially the same as Particles A13, except that calcined Particles A15 contained 0.3 weight-% Mo and about 5.6 weight-% MgO.

EXAMPLE III

This example illustrates the beneficial effect of the impregnation of spherical alumina particles with a Mg compound on the crush strength of the calcined particles, measured after hydrotreating in the presence of steam in accordance with the procedure described in Example I. Test results are summarized in Table I.

TABLE I__________________________________________________________________________ Weight-% Mo Additional Weight-% of Crush StrengthRun Particle in Particle Promoter Addit. Promoter.sup.1 (Lb Per Particle)__________________________________________________________________________1 (Control) A3 0 None -- 11.42 (Control) A4 0 CaO 1.6 16.03 (Control) A5 0 CaO 8.0 5.94 (Invention) A6 0 MgO 1.2 21.85 (Invention) A7 0 MgO 5.6 22.06 (Control) A8 0.3 None -- 14.77 (Control) A9 0.3 ZnO 0.2 13.58 (Control) A10 0.3 ZnO 2.3 14.99 (Invention) A11 0.3 MgO 0.01 16.710 (Invention) A12 0.3 MgO 0.1 17.611 (Invention) A13 0.3 MgO 0.6 15.7 (repeated: 24)12 (Invention) A14 0.3 MgO 1.2 30.813 (Invention) A15 0.3 MgO 5.6 31.1__________________________________________________________________________ .sup.1 given as weight% metal oxide (i.e. CaO or MgO or ZnO)

The above-described tests results clearly show that, surprisingly, the impregnation of spherical alumina-containing particles with a Mg compound was beneficial for the crush strength retention of calcined particles in hydrotreating test runs employing steam. This result is quite surprising because no such advantage of the impregnation of alumina-containing particles with compounds of Ca or Zn was observed. Furthermore, the average initial crush strength of calcined Mg-treated and untreated alumina-containing particles, i.e., the crush strength of those particles before use in hydrotreating tests employing steam was approximately the same: about 55 lb per 1/4 inch particle.

Additional tests showed that incorporating the Mg compound into Control Particles A3 or A8 by soaking with the impregnating solution (containing Mg nitrate), as described for Particles A6, A7 and A11-15, was more effective, in terms of crush strength (after hydrotreatment in the presence of steam) and also in terms of penetration of the Mg compound into the interior of the alumina-containing particles (as determined by electron microprobe analysis), than spraying of the impregnating solution into Particles A3 or A8. In the latter case, the Mg compound had penetrated in A3 or A8 particles at a depth of only up to about 2 microns from the surface; whereas soaking for about 1-3 days resulted in a substantially even distribution of the Mg compound substantially throughout the entire alumina-containing particles of this invention.

EXAMPLE IV

This example illustrates the effect of the heating (calcination) conditions on pertinent physical properties of alumina-containing spheres. A2 particles of about 1/8 inch diameter that had been impregnated with about 0.3 weight-% Mo were heated in air at temperatures ranging from 400.degree. C. to 900.degree. C. for about 1 hour, (so as to prepare Particles A8). The crush strength of the thus calcined particles (diameter: 1/8 inch) was determined in accordance with the procedure described in Example I. Tests results are summarized in Table II and are plotted in FIG. 2.

TABLE II______________________________________ Crush NormalizedCalcination Strength Crush StrengthTemp. (.degree.C.) (lb/Particle) (lb/Inch Diameter)______________________________________400 1.88 15.0500 3.42 27.4600 4.37 35.0700 4.80 38.4800 3.95 31.6900 1.65 13.2______________________________________

Data in Table II and FIG. 2 clearly show that maximum crush strength (after hydrotreating in the presence of steam) was attained when the alumina spheres (containing 0.3 weight-% Mo) were calcined at a temperature in the range of from about 550.degree. to about 800.degree. C., preferably from about 600.degree. to about 750.degree. C.

The effect of the calcination time, at a calcination temperature of 650.degree. C., is shown in Table III.

TABLE III______________________________________Calcination Crush Strength Crush StrengthTime (minute) (lb/Particle) (lb/Inch Diameter)______________________________________20 7.01 56.140 7.25 58.060 7.20 57.690 6.68 53.4120 6.41 51.3240 5.22 41.8______________________________________

Data in Table III show that a calcination time of about 20-90 minutes was suitable for 1/8 inch diameter alumina-containing Particles A8. Prolonged calcining had a detrimental effect.

Based on the above-described test results, it is concluded that the preferred heating conditions in step (A) for preparing the Mg-impregnated, substantially spherical alumina-containing particles of this invention will also comprise a temperature of about 550.degree.-800.degree. C. (more preferably about 600.degree.-750.degree. C.) and a heating time of about 20-90 minutes.

EXAMPLE V

The effect of the calcination temperature on the pore volume distribution of Particles A1, A2 and A3 was investigated. Pore volume and pore diameter of these particles were determined by measuring intrusion porosimetry (carried out at room temperature at a mercury ranging from 0 psi to 60,000 psi, using an Autopore 9200 instrument of Micromeritics, Norcross, GA). In FIG. 3, pore volume was plotted versus logarithm of pore diameter for A1, A2 and two A3 samples. FIG. 4 shows that A1 (Shell 544, as received; 1/6" diameter) and of A2 (Alcoa S-100, as received; 1/16" diameter) had very similar pore distributions, whereas the pore distributions of the two A3 samples (obtained by heating 1/16" A2 particles at 600.degree. C. and 800.degree. C., respectively, for about 3 hours), differed significantly from those of A1 and A2. The most significant changes that resulted when A2 (S-100) particles were heated to 600.degree. C. and 800.degree. C., respectively, (so as to make A3 particles), was a shift toward a substantially greater portion of pores in the 40-200 A pore diameter range. About 80% of the total pore volume of A3 was in pores of the 40-200 Angstrom range, whereas the percentage of the total pore volume of A1 and A2 in the 40-200 Angstrom pore diameter range was only about 40%.

Based on the above-described test results, it is concluded that heating at 600.degree.-800.degree. C. in step (A) for preparing the impregnated, substantially spherical alumina-containing particles of this invention will have a very similar effect in the pore volume distribution of the Mg-impregnated particles of this invention as the above-described effect on the pore volume distribution of Particles A3.

The total pore volume of the Mo-impregnated alumina spheres A3 ranged from about 0.5 to about 0.6 cc/g when the calcination was carried out for 16 hours at a temperature in the range of from about 400.degree. C. to about 800.degree. C. Thus, the effect of the calcination temperature on the total pore volume of calcined spheres A3 was rather insignificant. Based on these results, it is concluded that the total pore volume of the Mg-impregnated, substantially spherical alumina-containing particles of this invention (such as Particles A7, A8 and A11 through A15) will also vary only insignificantly with the calcination temperature.

EXAMPLE VI

This example illustrates the improved performance of Particles A8 (with 0.3 weight-% Mo) in prolonged hydrotreating tests versus commercial Particles A1 and A2. Crush strength results, obtained substantially in accordance with the hydrotreating procedure described in Example I, are summarized in Table IV. Hydrotreating conditions were: 2200 psig total pressure; 760.degree. F.; 110 psi steam pressure, LHSV of 0.1 cc/cc catalyst/hour. The resid feed contained about 2.0 weight-% sulfur and about 60 ppmw (Ni+V).

TABLE IV______________________________________ Hours on Stream: 0 16 30 140 270 360Particles.sup.1 Crush Strength (lb/Particle)______________________________________1/6" A1 35 11 N/A N/A N/A N/A 1/4" A2 58 11 N/A N/A N/A N/A 1/4" A4 55 39 37 34 38 38 1/4" A4 100+ 80+ 80+ 80+ 80+ 80+ 1/8" B 49 N/A 42 N/A N/A N/A______________________________________ .sup.1 Fractions indicate particle diameter expressed in inches.

Test data in Table IV clearly show a significant improvement in crush strength retention of Particles A8 over commercial Particles A1 and A2, after use in the several hydrotreating runs in the presence of steam, as described in Example I. Based on these results and based on the fact that the Mg-impregnated, substantially spherical alumina-containing Particles of this invention have a higher crush strength retention that Particles A8 (See Example III, it is concluded that the Mg-impregnated, substantially spherical alumina-containing particles of this invention will also be superior to commercial Particles A1 and A2, in terms of crush strength retention.

Reasonable variations and modifications are possible within the scope of the disclosure and appended claims.

Claims

1. A hydrotreating process comprising the step of contacting a substantially liquid hydrocarbon-containing feed stream, which also contains compounds of sulfur and metals, with a free hydrogen containing gas in the presence of a fixed catalyst bed comprising

(a) at least one layer of impregnated, substantially spherical alumina-containing particles and

(b) at least one layer of hydrotreating catalyst particles comprising a refractory inorganic carrier material and at least one hydrogenation promoter selected from the group consisting of transition metals belonging to Groups IIIB, IVB, VB, VIB, VIIB, IB and IIB of the Periodic Table and compounds of said transition metals;

under such hydrotreating conditions as to obtain at least one liquid hydrocarbon-containing product stream having lower concentrations of sulfur and metals than said hydrocarbon-containing feed stream;

wherein said impregnated, substantially spherical alumina-containing particles in catalyst layer (a) have been prepared by a process comprising the steps of

(A) impregnating (i) a starting material of substantially spherical alumina-containing particles, which have an initial average particle size of at least about 0.05 inch, an initial surface area, determined in accordance with ASTM method D3037, of at least about 20 cm.sup.2 /g, an initial pore volume, determined by mercury intrusion porosimetry, of at least about 0.1 cc/g, and an initial content of Al.sub.2 O.sub.3 of at least about 80 weight-%, with (ii) a solution comprising at least one dissolved magnesium compound; and

(B) heating the material obtained in step (A) at a temperature in the range of from about 500.degree. to about 900.degree. C. for a period of time of at least 10 minutes, under such heating conditions as to convert at least a portion of said at least one magnesium compound absorbed in step (A) to magnesium oxide and to obtain a material having a higher retention of crush strength, measured after exposure for about 100 hours to a liquid hydrocarbon-containing stream which contains at least about 0.5 weight-% sulfur, under hydrotreating conditions at about 2250 psig total pressure, about 350 psig partial pressure of steam and about 700.degree. F., than said starting material;

wherein a layer (a) of said impregnated, substantially spherical alumina-containing particles is placed as support layer below at least one layer (b) of said hydrotreating catalyst particles;

wherein said impregnated, substantially spherical alumina-containing particles in said support layer are promoted with at least one compound of at least one element selected from the group consisting of Y, La, Ce, Ti, Zr, Hf, Cr, Mo, W, Mn, Re, Ni, Co, Cu, Zn and P, at a level of from about 0.1 to about 2.0 weight percent of said at least one element;

and wherein said hydrotreating catalyst particles contain said at least one hydrogenation promoter at a level which is effective for lowering the concentration of sulfur and metals present in said hydrocarbon-containing feed stream under said hydrotreating conditions.

2. A process in accordance with claim 1, wherein said compounds of metals in said hydrocarbon-containing feed steam comprise compounds of at least one metal selected from the group consisting of nickel and vanadium.

3. A process in accordance with claim 1, wherein said hydrocarbon-containing feed stream comprises about 3-500 ppmw Ni and about 5-1000 ppmw V.

4. A process in accordance with claim 1, wherein said hydrocarbon-containing feed comprises about 0.5-5.0 weight-% sulfur.

5. A process in accordance with claim 1, wherein said hydrocarbon-containing feed stream contains from about 0.3 to about 20 weight-% water.

6. A process in accordance with claim 1, wherein said hydrocarbon-containing feed stream contains from about 0.5 to about 10 weight-% water.

7. A process in accordance with claim 1, wherein said starting material used in step (A) has an initial average particle diameter in the range of from about 0.1 to about 1.0 inch, an initial surface area in the range of from about 40 to about 600 m.sup.2 /g, an initial pore volume in the range of from about 0.2 to about 1.0 cc/g, and an initial normalized crush strength in the range of from about 100 to about 400 lb. per inch diameter per particle.

8. A process in accordance with claim 7, wherein the initial content of Na in said starting material is less than about 1.0 weight-%, and said initial content of Al.sub.2 O.sub.3 is in the range of from about 90 to about 99 weight-%.

9. A process in accordance with claim 1, wherein the concentration of said at least one dissolved magnesium compound in the impregnating solution used in step (A) is in the range of from about 0.0001 to about 2.0 mol/l, and the weight ratio of said starting material to said impregnating solution is in the range of from about 0.1:1 to about 2.0:1.

10. A process in accordance with claim 9, wherein said magnesium compound is magnesium nitrate and the concentration of dissolved magnesium nitrate in said impregnated solution is in the range of from about 0.01 to about 1.0 mol/l.

11. A process in accordance with claim 1, wherein said heating in step (B) is carried out at a temperature in the range of from about 550.degree. to about 800.degree. C. for a period of time in the range of from about 10 minutes to about 20 hours.

12. A process in accordance with claim 1, wherein said substantially spherical alumina-containing particles in layer (a) have a pore volume of pores having a diameter of about 40-200 Angstroms in the range of from 50% to about 90% of the total pore volume, and a crush strength in the range of from about 150 to about 350 lb. per inch diameter per particle.

13. A process in accordance with claim 1, wherein said impregnated, substantially spherical alumina-containing particles in layer (a) have a surface area in the range of from about 50 to about 300 m.sup.2 /g and a pore volume in the range of from about 0.3 to about 0.8 cc/g, and contain from about 0.06 to about 6.0 weight-% Mg.

14. A process in accordance with claim 1, wherein said at least one element is selected from the group consisting of Mo, Ni and Co.

15. A process in accordance with claim 1, wherein said refractory inorganic carrier comprises alumina, and said at least one hydrogenation promoter is selected from the group consisting of comppounds of Y, La, Ce, Ti, Zr, Cr, Mo, W, Mn, Re, Ni, Co and Cu.

16. A process in accordance with claim 1, wherein said hydrotreacting catalyst particles in layer (b) comprise alumina as carrier material and at least one hydrogenation promoter selected from the group consisting of oxides and sulfides of Mo, oxides and sulfides of Ni, oxides and sulfides of Co, and mixtures thereof, have a surface area in the range of from about 50 to about 500 m.sup.2 /g, and have a pore volume in the range of from about 0.2 to about 2.0 cc/g.

17. A process in accordance with claim 1, wherein another layer (a) of impregnated, substantially spherical alumina-containing particles is placed on top of at least one layer (b) of hydrotreating catalyst particles.

18. A process in accordance with claim 1, wherein the weight ratio of each layer (a) of impregnated, substantially spherical alumina-containing particles to each layer (b) of hydrotreating catalyst particles is in the range of from about 1:100 to about 1:1.

19. A process in accordance with claim 1, wherein

said hydrotreating conditions comprise a reaction time in the range of from about 0.05 to about 10 hours, a reaction temperature in the range of from about 250.degree. to 550.degree. C., a reaction pressure in the range of from about 0 to about 5,000 psig, and a quantity of added hydrogen gas in the range of from about 100 to about 10,000 cubic feet of H.sub.2 per barrel of hydrocarbon-containing feed stream.

20. A process in accordance with claim 19, wherein said hydrotreating conditions comprise a reaction time in the range of from about 0.4 to about 5 hours, a reaction temperature in the range of from about 300.degree. to about 450.degree. C., a reaction pressure in the range of from about 100 to about 2,500 psig, and a quantity of added hydrogen in the range of from about 1,000 to about 5,000 cubic feet of H.sub.2 per barrel of hydrocarbon-containing feed stream.

21. A process in accordance with claim 1, wherein said hydrocarbon-containing feed stream contains at least one added thermally decomposable compound selected from the group consisting of compounds of metals belonging to Groups IIIB, IVB, VB, VIB, VIIB, VIII, IB and IIB of the Periodic Table.

22. A process in accordance with claim 21, wherein said at least one added thermally decomposable compound is selected from the group consisting of molybdenum compounds, tungsten compounds, manganese compounds, chromium compounds, zirconium compounds and zinc compounds.

23. A process in accordance with claim 22, wherein said at least one thermally decomposable compounds is at least one compound of molybdenum.

24. A process in accordance with claim 5, wherein said water is introduced as steam.

25. A process in accordance with claim 1, wherein said feed stream has an API gravity, measured at 60.degree. F., in the range of from about 5 to about 30.

26. A process in accordance with claim 25, wherein said API gravity, is in the range of from about 8 to about 25.

27. A process in accordance with claim 1, wherein said at least one element is molybdenum.

28. A process in accordance with claim 27, wherein molybdenum is present at a level of about 0.2 to about 1.0 weight-% Mo.

29. A process in accordance with claim 1, wherein said temperature in step (B) is in the range of from about 550.degree. to about 800.degree. C.