Hydrofining process for hydrocarbon containing feed streams

Abstract

At least one decomposable compound selected from the group consisting of compounds of the metals of Group IIB and Group IIIB of the Periodic Table is mixed with a hydrocarbon-containing feed stream. The hydrocarbon-containing feed stream containing such decomposable compound is then contacted in a hydrofining process with a catalyst composition comprising a support selected from the group consisting of alumina, silica and silica-alumina and a promoter comprising at least one metal selected from Group VIB, Group VIIB and Group VIII of the Periodic Table. The introduction of the decomposable compound may be commenced when the catalyst is new, partially deactivated or spent with a beneficial result occurring in each case.

Description

This invention relates to a hydrofining process for hydrocarbon-containing feed streams. In one aspect, this invention relates to a process for removing metals from a hydrocarbon-containing feed stream. In another aspect, this invention relates to a process for removing sulfur or nitrogen from a hydrocarbon-containing feed stream. In still another aspect, this invention relates to a process for removing potentially cokeable components from a hydrocarbon-containing feed stream. In still another aspect, this invention relates to a process for reducing the amount of heavies in a hydrocarbon-containing feed stream.

It is well known that crude oil as well as products from extraction and/or liquefaction of coal and lignite, products from tar sands, products from shale oil and similar products may contain components which make processing difficult. As an example, when these hydrocarbon-containing feed streams contain metals such as vanadium, nickel and iron, such metals tend to concentrate in the heavier fractions such as the topped crude and residuum when these hydrocarbon-containing feed streams are fractionated. The presence of the metals make further processing of these heavier fractions difficult since the metals generally act as poisons for catalysts employed in processes such as catalytic cracking, hydrogenation or hydrodesulfurization.

The presence of other components such as sulfur and nitrogen is also considered detrimental to the processability of a hydrocarbon-containing feed stream. Also, hydrocarbon-containing feed streams may contain components (referred to as Ramsbottom carbon residue) which are easily converted to coke in processes such as catalytic cracking, hydrogenation or hydrodesulfurization. It is thus desirable to remove components such as sulfur and nitrogen and components which have a tendency to produce coke.

It is also desirable to reduce the amount of heavies in the heavier fractions such as the topped crude and residuum. As used herein the term heavies refers to the fraction having a boiling range higher than about 1000.degree. F. This reduction results in the production of lighter components which are of higher value and which are more easily processed.

It is thus an object of this invention to provide a process to remove components such as metals, sulfur, nitrogen and Ramsbottom carbon residue from a hydrocarbon-containing feed stream and to reduce the amount of heavies in the hydrocarbon-containing feed stream (one or all of the described removals and reduction may be accomplished in such process, which is generally refered to as a hydrofining process, depending on the components contained in the hydrocarbon-containing feed stream). Such removal or reduction provides substantial benefits in the subsequent processing of the hydrocarbon-containing feed streams.

In accordance with the present invention, a hydrocarbon-containing feed stream, which also contains metals (such as vanadium, nickel, iron), sulfur, nitrogen and/or Ramsbottom carbon residue, is contacted with a solid catalyst composition comprising alumina, silica or silica-alumina. The catalyst composition also contains at least one metal selected from Group VIB, Group VIIB, and Group VIII of the Periodic Table, in the oxide or sulfide form. At least one decomposable compound selected from the group consisting of the compounds of metals of Group IIB or Group IIIB of the Periodic Table is mixed with the hydrocarbon-containing feed stream prior to contacting the hydrocarbon-containing feed stream with the catalyst composition. The hydrocarbon-containing feed stream, which also contains a decomposable compound of the Group IIB or Group III B metal, is contacted with the catalyst composition in the presence of hydrogen under suitable hydrofining conditions. After being contacted with the catalyst composition, the hydrocarbon-containing feed stream will contain a significantly reduced concentration of metals, sulfur, nitrogen and Ramsbottom carbon residue as well as a reduced amount of heavy hydrocarbon components. Removal of these components from the hydrocarbon-containing feed stream in this manner provides an improved processability of the hydrocarbon-containing feed stream in processes such as catalytic cracking, hydrogenation or further hydrodesulfurization. Use of the decomposable compound results in improved removal of metals, primarily vanadium and nickel.

As used herein, Group IIB includes zinc, cadmium and mercury. Also, Group IIIB includes scandium, yttrium, lanthanum, the lanthanides and actinium.

The decomposable compound may be added when the catalyst composition is fresh or at any suitable time thereafter. As used herein, the term "fresh catalyst" refers to a catalyst which is new or which has been reactivated by known techniques. The activity of fresh catalyst will generally decline as a function of time if all conditions are maintained constant. It is believed that the introduction of the decomposable compound will slow the rate of decline from the time of introduction and in some cases will dramatically improve the activity of an at least partially spent or deactivated catalyst from the time of introduction.

For economic reasons it is sometimes desirable to practice the hydrofining process without the addition of the decomposable compound until the catalyst activity declines below an acceptable level. In some cases, the activity of the catalyst is maintained constant by increasing the process temperature. The decomposable compound is added after the activity of the catalyst has dropped to an unacceptable level and the temperature cannot be raised further without adverse consequences. It is believed that the addition of the decomposable compound at this point will result in a dramatic increase in catalyst activity based on the results set forth in Example IV.

Other objects and advantages of the invention will be apparent from the foregoing brief description of the invention and the appended claims as well as the detailed description of the invention which follows.

The catalyst composition used in the hydrofining process to remove metals, sulfur, nitrogen and Ramsbottom carbon residue and to reduce the concentration of heavies comprises a support and a promoter. The support comprises alumina, silica or silica-alumina. Suitable supports are believed to be Al.sub.2 O.sub.3, SiO.sub.2, Al.sub.2 O.sub.3 --SiO.sub.2, Al.sub.2 O.sub.3 --TiO.sub.2, Al.sub.2 O.sub.3 --BPO.sub.4, Al.sub.2 O.sub.3 --AlPO.sub.4, Al.sub.2 O.sub.3 --Zr.sub.3 (PO.sub.4).sub.4, Al.sub.2 O.sub.3 --SnO.sub.2 and Al.sub.2 O.sub.3 --ZnO. Of these supports, Al.sub.2 O.sub.3 is particularly preferred.

The promoter comprises at least one metal selected from the group consisting of the metals of Group VIB, Group VIIB, and Group VIII of the Periodic Table. The promoter will generally be present in the catalyst composition in the form of an oxide or sulfide. Particularly suitable promoters are iron, cobalt, nickel, tungsten, molybdenum, chromium, manganese, vanadium and platinum. Of these promoters, cobalt, nickel, molybdenum and tungsten are the most preferred. A particularly preferred catalyst composition is Al.sub.2 O.sub.3 promoted by CoO and MoO.sub.3 or promoted by CoO, NiO and MoO.sub.3.

Generally, such catalysts are commercially available. The concentration of cobalt oxide in such catalysts is typically in the range of about 0.5 weight percent to about 10 weight percent based on the weight of the total catalyst composition. The concentration of molybdenum oxide is generally in the range of about 2 weight percent to about 25 weight percent based on the weight of the total catalyst composition. The concentration of nickel oxide in such catalysts is typically in the range of about 0.3 weight percent to about 10 weight percent based on the weight of the total catalyst composition. Pertinent properties of four commercial catalysts which are believed to be suitable are set forth in Table I.

TABLE I______________________________________ Bulk Surface CoO MoO NiO Density* AreaCatalyst (Wt. %) (Wt. %) (Wt. %) (g/cc) (M.sup.2 /g)______________________________________Shell 344 2.99 14.42 -- 0.79 186Katalco 477 3.3 14.0 -- .64 236KF - 165 4.6 13.9 -- .76 274Commercial 0.92 7.3 0.53 -- 178Catalyst DHarshawChemicalCompany______________________________________ *Measured on 20/40 mesh particles, compacted.

The catalyst composition can have any suitable surface area and pore volume. In general, the surface area will be in the range of about 2 to about 400 m.sup.2 /g, preferably about 100 to about 300 m.sup.2 /g, while the pore volume will be in the range of about 0.1 to about 4.0 cc/g, preferably about 0.3 to about 1.5 cc/g.

Presulfiding of the catalyst is preferred before the catalyst is initially used. Many presulfiding procedures are known and any conventional presulfiding procedure can be used. A preferred presulfiding procedure is the following two step procedure.

The catalyst is first treated with a mixture of hydrogen sulfide in hydrogen at a temperature in the range about 175.degree. C. to about 225.degree. C., preferably about 205.degree. C. The temperature in the catalyst composition will rise during this first presulfiding step and the first presulfiding step is continued until the temperature rise in the catalyst has substantially stopped or until hydrogen sulfide is detected in the effluent flowing from the reactor. The mixture of hydrogen sulfide and hydrogen preferably contains in the range of about 5 to about 20 percent hydrogen sulfide, preferably about 10 percent hydrogen sulfide.

The second step in the preferred presulfiding process consists of repeating the first step at a temperature in the range of about 350.degree. C. to about 400.degree. C., preferably about 370.degree. C., for about 2-3 hours. It is noted that other mixtures containing hydrogen sulfide may be utilized to presulfide the catalyst. Also the use of hydrogen sulfide is not required. In a commercial operation, it is common to utilize a light naphtha containing sulfur to presulfide the catalyst.

As has been previously stated, the present invention may be practiced when the catalyst is fresh or the addition of the decomposable compound of a Group IIB or Group IIIB metal may be commenced when the catalyst has been partially deactivated. The addition of the decomposable compound of a Group IIB or Group IIIB metal may be delayed until the catalyst is considered spent.

In general, a "spent catalyst" refers to a catalyst which does not have sufficient activity to produce a product which will meet specifications, such as maximum permissible metals content, under available refinery conditions. For metals removal, a catalyst which removes less than about 50% of the metals contained in the feed is generally considered spent.

A spent catalyst is also sometimes defined in terms of metals loading (nickel+vanadium). The metals loading which can be tolerated by different catalyst varies but a catalyst whose weight has increased at least about 15% due to metals (nickel+vanadium) is generally considered a spent catalyst.

Any suitable hydrocarbon-containing feed stream may be hydrofined using the above described catalyst composition in accordance with the present invention. Suitable hydrocarbon-containing feed streams include petroleum products, coal, pyrolyzates, products from extraction and/or liquefaction of coal and lignite, products from tar sands, products from shale oil and similar products. Suitable hydrocarbon feed streams include gas oil having a boiling range from about 205.degree. C. to about 538.degree. C., topped crude having a boiling range in excess of about 343.degree. C. and residuum. However, the present invention is particularly directed to heavy feed streams such as heavy topped crudes and residuum and other materials which are generally regarded as too heavy to be distilled. These materials will generally contain the highest concentrations of metals, sulfur, nitrogen and Ramsbottom carbon residues.

It is believed that the concentration of any metal in the hydrocarbon-containing feed stream can be reduced using the above described catalyst composition in accordance with the present invention. However, the present invention is particularly applicable to the removal of vanadium, nickel and iron.

The sulfur which can be removed using the above described catalyst composition in accordance with the present invention will generally be contained in organic sulfur compounds. Examples of such organic sulfur compounds include sulfides, disulfides, mercaptans, thiophenes, benzylthiophenes, dibenzylthiophenes, and the like.

The nitrogen which can be removed using the above described catalyst composition in accordance with the present invention will also generally be contained in organic nitrogen compounds. Examples of such organic nitrogen compounds include amines, diamines, pyridines, quinolines, porphyrins, benzoquinolines and the like.

While the above described catalyst composition is effective for removing some metals, sulfur, nitrogen and Ramsbottom carbon residue, the removal of metals can be significantly improved in accordance with the present invention by introducing a suitable decomposable compound selected from the group consisting of compounds of the metals of Group IIB and Group IIIB of the Periodic Table into the hydrocarbon-containing feed stream prior to contacting the hydrocarbon containing feed stream with the catalyst composition. As has been previously stated, the introduction of the decomposable compound may be commenced when the catalyst is new, partially deactivated or spent with a beneficial result occurring in each case.

Any suitable Group IIB or Group IIIB metal may be used. Of the Group IIB metals, zinc is preferred because of difficulty in handling cadmium and mercury. Of the Group IIIB metals, cerium and lanthanum are preferred.

Any suitable decomposable compound of a Group IIB or Group IIIB metal can be introduced into the hydrocarbon-containing feed stream. Examples of suitable compounds of zinc are aliphatic, cycloaliphatic and aromatic carboxylates having 1-20 carbon atoms, (e.g., acetates, octoates, neodecanoates, tallates, naphthenates, benzoates), alkoxides, diketones (e.g., acetylacetonates), carbonyls, dialkyl and diaryl compounds (e.g. di-t-butylzinc and diphenylzinc), cyclopentadienyl complexes, mercaptides, xanthates, carbamates, dithiocarbamates, thiophosphates, dithiophosphates and mixtures thereof. Zinc naphthenate and zinc dithiophosphate are preferred zinc decomposable compounds.

Examples of suitable compounds of cerium and lanthanum are aliphatic, cycloaliphatic and aromatic carboxylates (e.g. acetates, oxalates, octoates, naphthenates, benzoates), diketones (e.g. acetylacetonates), alkoxides, cyclopentadiene, complexes, cyclooctatetraene complexes, carbonyl complexes, mercaptides, xanthates, carbamates, thio- and dithiocarbamates, thio- and dithiophosphates and mixtures thereof. Cerium octoate and lanthanum octoate are presently preferred cerium and lanthanum compounds.

Any suitable concentration of the decomposable compound may be added to the hydrocarbon-containing feed stream. In general, a sufficient quantity of the decomposable compound will be added to the hydrocarbon-containing feed stream to result in a concentration of Group IIB or Group IIIB metal in the range of about 1 to about 500 ppm and more preferably in the range of about 5 to about 50 ppm.

High concentrations such as about 500 ppm and above should be avoided to prevent plugging of the reactor. It is noted that one of the particular advantages of the present invention is the very small concentrations of Group IIB or Group IIIB metal which result in a significant improvement. This substantially improves the economic viability of the process.

After the decomposable compound has been added to the hydrocarbon-containing feed stream for a period of time, it is believed that only periodic introduction of the additive is required to maintain the efficiency of the process.

The decomposable compound may be combined with the hydrocarbon-containing feed stream in any suitable manner. The decomposable compound may be mixed with the hydrocarbon-containing feed stream as a solid or liquid or may be dissolved in a suitable solvent (preferably an oil) prior to introduction into the hydrocarbon-containing feed stream. Any suitable mixing time may be used. However, it is believed that simply injecting the decomposable compound into the hydrocarbon-containing feed stream is sufficient. No special mixing equipment or mixing period are required.

The pressure and temperature at which the decomposable compound is introduced into the hydrocarbon-containing feed stream is not thought to be critical. However, a temperature below 450.degree. C. is recommended.

The hydrofining process can be carried out by means of any apparatus whereby there is achieved a contact of the catalyst composition with the hydrocarbon containing feed stream and hydrogen under suitable hydrofining conditions. The hydrofining process is in no way limited to the use of a particular apparatus. The hydrofining process can be carried out using a fixed catalyst bed, fluidized catalyst bed or a moving catalyst bed. Presently preferred is a fixed catalyst bed.

Any suitable reaction time between the catalyst composition and the hydrocarbon-containing feed stream may be utilized. In general, the reaction time will range from about 0.1 hours to about 10 hours. Preferably, the reaction time will range from about 0.3 to about 5 hours. Thus, the flow rate of the hydrocarbon containing feed stream should be such that the time required for the passage of the mixture through the reactor (residence time) will preferably be in the range of about 0.3 to about 5 hours. This generally requires a liquid hourly space velocity (LHSV) in the range of about 0.10 to about 10 cc of oil per cc of catalyst per hour, preferably from about 0.2 to about 3.0 cc/cc/hr.

The hydrofining process can be carried out at any suitable temperature. The temperature will generally be in the range of about 250.degree. C. to about 550.degree. C. and will preferably be in the range of about 340.degree. to about 440.degree. C. Higher temperatures do improve the removal of metals but temperatures should not be utilized which will have adverse effects on the hydrocarbon-containing feed stream, such as coking, and also economic considerations must be taken into account. Lower temperatures can generally be used for lighter feeds.

Any suitable hydrogen pressure may be utilized in the hydrofining process. The reaction pressure will generally be in the range of about atmospheric to about 10,000 psig. Preferably, the pressure will be in the range of about 500 to about 3,000 psig. Higher pressures tend to reduce coke formation but operation at high pressure may have adverse economic consequences.

Any suitable quantity of hydrogen can be added to the hydrofining process. The quantity of hydrogen used to contact the hydrocarbon-containing feedstock will generally be in the range of about 100 to about 20,000 standard cubic feet per barrel of the hydrocarbon-containing feed stream and will more preferably be in the range of about 1,000 to about 6,000 standard cubic feet per barrel of the hydrocarbon-containing feed stream.

In general, the catalyst composition is utilized until a satisfactory level of metals removal fails to be achieved which is believed to result from the coating of the catalyst composition with the metals being removed. It is possible to remove the metals from the catalyst composition by certain leaching procedures but these procedures are expensive and it is generally contemplated that once the removal of metals falls below a desired level, the used catalyst will simply be replaced by a fresh catalyst.

The time in which the catalyst composition will maintain its activity for removal of metals will depend upon the metals concentration in the hydrocarbon-containing feed streams being treated. It is believed that the catalyst composition may be used for a period of time long enough to accumulate 10-200 weight percent of metals, mostly Ni, V, and Fe, based on the weight of the catalyst composition, from oils.

The following examples are presented in further illustration of the invention.

EXAMPLE I

In this example, the automated experimental setup for investigating the hydrofining of heavy oils in accordance with the present invention is described. Oil, with or without a dissolved decomposable molybdenum, lanthanum, zinc or cerium compound, was pumped downward through an induction tube into a trickle bed reactor, 28.5 inches long and 0.75 inches in diameter. The oil pump used was a Whitey Model LP 10 (a reciprocating pump with a diaphragm-sealed head; marketed by Whitey Corp., Highland Heights, Ohio). The oil induction tube extended into a catalyst bed (located about 3.5 inches below the reactor top) comprising a top layer of about 40 cc of low surface area .alpha.-alumina (14 grit Alundum; surface area less than 1 m.sup.2 /gram; marketed by Norton Chemical Process Products, Akron, Ohio), a middle layer of 33.3 cc of a hydrofining catalyst, mixed with 85 cc of 36 grit Alundum, and a bottom layer of about 30 cc of .alpha.-alumina.

The hydrofining catalyst used was a commercial, promoted desulfurization catalyst (referred to as catalyst D in Table I) marketed by Harshaw Chemical Company, Beachwood, Ohio. The catalyst had an Al.sub.2 O.sub.3 support having a surface area of 178 m.sup.2 /g (determined by BET method using N.sub.2 gas), a medium pore diameter of 140 .ANG. and at total pore volume of 0.682 cc/g (both determined by mercury porosimetry in accordance with the procedure described by American Instrument Company, Silver Springs, Md., catalog number 5-7125-13. The catalyst contained 0.92 weight-% Co (as cobalt oxide), 0.53 weight-% Ni (as nickel oxide); 7.3 weight-% Mo (as molybdenum oxide).

The catalyst was presulfided as follows. A heated tube reactor was filled with a 4 inch high bottom layer of Alundum, an 18 inch high middle layer of 33 cc of catalyst D mixed with 85 cc of 36 grit Alundum, and a 6 inch top layer of Alundum. The reactor was purged with nitrogen (10 l/hr) and the catalyst was heated for one hour in a hydrogen stream (10 l/hr) to about 400.degree. F. While the reactor temperature was maintained at about 400.degree. F., the catalyst was exposed to a mixture of hydrogen (10 l/hr) and hydrogen sulfide (1.4 l/hr) for about 14 hours. The catalyst was then heated for about one hour in this mixture of hydrogen and hydrogen sulfide to a temperature of about 700.degree. F. The reactor temperature was maintained at 700.degree. F. for about 14 hours while the catalyst continued to be exposed to the mixture of hydrogen and hydrogen sulfide. The catalyst was then allowed to cool to ambient temperature conditions in the mixture of hydrogen and hydrogen sulfide and was finally purged with nitrogen.

Hydrogen gas was introduced into the reactor through a tube that concentrically surrounded the oil induction tube but extended only as far as the reactor top. The reactor was heated with a Thermcraft (Winston-Salem, N.C.) Model 211 3-zone furnace. The reactor temperature was measured in the catalyst bed at three different locations by three separate thermocouples embedded in an axial thermocouple well (0.25 inch outer diameter). The liquid product oil was generally collected every day for analysis. The hydrogen gas was vented. Vanadium and nickel contents were determined by plasma emission analysis; sulfur content was measured by X-ray fluorescence spectrometry; Ramsbottom carbon residue was determined in accordance with ASTM D524; pentane insolubles were measured in accordance with ASTM D893; and N content was measured in accordance with ASTM D3228.

The following metal compounds were employed: lanthanum octoate and cerium (III) octoate (both marketed by Rhone-Poulenc, Inc., Monmouth Junction, N.J.); zinc naphthenate (Zn(C.sub.10 H.sub.12 CO.sub.2).sub.2 ; marketed by Shepherd Chemical Company, Cincinnati, Ohio); Mo(CO).sub.6 (marketed by Aldrich Chemical Company, Milwaukee, Wis.).

EXAMPLE II

A desalted, topped (400.degree. F.+) Hondo Californian heavy crude (density at 38.5.degree. C.: about 0.96 g/cc) was hydrotreated in accordance with the procedure described in Example I. The liquid hourly space velocity (LHSV) of the oil was about 1.5 cc/cc catalyst/hr; the hydrogen feed rate was about 4,800 standard cubic feet (SCF) of hydrogen per barrel of oil; the temperature was about 750.degree. F.; and the pressure was about 2250 psig. Pertinent process conditions and demetallization results of two control runs and four invention runs are summarized in Table II.

TABLE II__________________________________________________________________________ PPM in Feed Days on Temp Added PPM in Product % RemovalRun Stream LHSV (.degree.F.) Metal Ni V Ni + V Ni V Ni + V of (Ni + V)__________________________________________________________________________1 1 1.58 750 0 103 248 351 30 54 84 76(Control) 2 1.51 750 0 103 248 351 34 59 93 74No Additive 3 1.51 750 0 103 248 351 35 62 97 72 4 1.51 750 0 103 248 351 36 63 99 72 5 1.49 750 0 103 248 351 35 64 99 72 6 1.55 750 0 103 248 351 28 60 88 75 7 1.53 750 0 103 248 351 38 71 109 69 9 1.68 750 0 103 248 351 40 64 104 70 10 1.53 750 0 103 248 351 20 26 .sup. 46.sup.1 .sup. 87.sup.1 17 1.61 750 0 103 248 351 49 98 147.sup.1 .sup. 58.sup.1 18 1.53 750 0 103 248 351 40 75 115 67 19 1.53 750 0 103 248 351 40 73 113 68 20 1.57 750 0 103 248 351 44 75 119 66 21 1.45 750 0 103 248 351 41 68 109 69 22 1.49 750 0 103 248 351 41 60 101 71 24 1.47 750 0 103 248 351 42 69 111 682 1 1.56 750 .sup. 20.sup.2 103 248 351 22 38 60 83(Control) 1.5 1.56 750 20 103 248 351 25 42 67 81Mo(CO).sub.6 2.5 1.46 750 20 103 248 351 28 42 70 80Added 3.5 1.47 750 20 103 248 351 19 35 54 85 6 1.56 750 20 103 248 351 29 38 67 81 7 1.55 750 20 103 248 351 25 25 50 86 8 1.50 750 20 103 248 351 27 35 62 82 9 1.53 750 20 103 248 351 27 35 62 82 10 1.47 750 20 103 248 351 32 35 67 81 11 1.47 751 20 103 248 351 25 35 60 83 12 1.42 750 20 103 248 351 27 34 61 83 13 1.47 750 20 103 248 351 31 35 66 81 14 1.56 750 20 103 248 351 36 52 88 75 15 1.56 750 20 103 248 351 47 68 115.sup.1 .sup. 67.sup.13 2 1.42 750 .sup. 25.sup.3 104 248 352 28 48 76 78(Invention) 4 1.43 750 25 104 248 352 23 41 64 82La--Octoate 5 1.37 750 25 104 248 352 25 47 72 80Added 6 -- 750 25 104 248 352 27 54 81 77 7 1.65 750 25 104 248 352 27 55 82 77 9 1.6 750 25 104 248 352 21 49 70 80 11 1.59 750 25 104 948 352 30 59 89 754 1 1.63 750 .sup. 32.sup.4 103 257 360 23 39 62 83(Invention) 2 1.59 751 32 103 257 360 25 44 69 81Ce--Octoate 3 1.47 750 32 103 257 360 27 47 74 79Added 4 1.47 750 32 103 257 360 28 48 76 79 5 1.47 750 32 103 257 360 26 46 72 80 7 1.53 750 32 103 257 360 25 47 72 80 9 1.44 750 32 103 257 360 29 54 83 77 10 1.40 750 32 102 257 360 32 54 86 76 11 1.40 750 32 103 257 360 33 53 86 76 12 1.40 750 32 103 257 360 33 56 89 755 1 -- 750 .sup. 24.sup.5 113 248 361 24 40 64 82(Invention) 2 -- 750 24 113 248 361 26 44 70 81 4 1.68 750 24 113 248 361 29 55 84 77Zn--Naphthe- Run terminated because of mechanical problemsnate Added6 3 1.56 750 .sup. 25.sup.5 .sup. 94.sup.6 .sup. 225.sup.6 319 26 51 77 76(Invention) 4 1.46 750 25 94 225 319 26 47 73 77 5 1.46 750 25 94 225 319 27 50 77 76Zn--Dithio- 6 1.46 750 25 94 225 319 26 49 75 76phosphate 8 1.48 750 25 94 225 319 28 56 84 74Added 10 1.49 750 25 94 225 319 28 59 87 73 11 1.44 750 25 94 225 319 28 59 87 73 12 1.44 750 25 94 225 319 29 62 91 71 13 1.44 750 25 94 225 319 26 60 86 73 15 1.44 750 25 94 225 319 31 65 96 70__________________________________________________________________________ .sup.1 Results believed to be erroneous .sup.2 ppm Mo .sup.3 ppm La .sup.4 ppm Ce .sup.5 ppm Zn .sup.6 average of two feed analyses before Zn compound was added.

Data in Table II show that the tested La, Ce and Zn compounds were effective demetallizing agents (compare runs 3-6 with run 1). Their effectiveness generally was comparable of that of as Mo(CO).sub.6 (run 2).

The removal of other undesirable impurities in the heavy oil in the three runs is summarized in Tables IIIA and IIIB.

TABLE IIIA______________________________________ Run 1 Run 2 Run 3 (Control) (Control) (Invention)______________________________________Wt % in Feed:Sulfur 5.6 5.6 5.3Carbon Residue 9.9 9.9 10.0Pentane Insolubles 13.4 13.4 13.1Nitrogen 0.70 0.70 0.71Wt % in Product:Sulfur 1.5-3.0 1.3-2.0 1.1-1.8Carbon Residue 6.6-7.6 5.0-5.9 5.1-5.8Pentane Insolubles 4.9-6.3 4.3-6.7 3.3-6.3Nitrogen 0.60-0.68 0.55-0.63 0.58-0.63% Removal of:Sulfur 46-73 64-77 66-79Carbon Residue 23-33 40-49 42-49Pentane lnsolubles 53-63 50-68 52-75Nitrogen 3-14 10-21 11-18______________________________________ TABLE IIIB______________________________________ Run 4 Run 5 Run 6 (Invention) (Invention) (Invention)______________________________________Wt % in Feed:Sulfur 5.3 5.1 5.4Carbon Residue 9.6 9.6 9.6Pentane Insolubles -- -- --Nitrogen 0.71 0.64 0.64Wt % in Product:Sulfur 1.5-1.8 1.0-1.4 1.0-1.4Carbon Residue 5.1-5.9 5.4 5.2-5.3Pentane Insolubles 3.3 3.6 3.3-4.1Nitrogen 0.52-0.58 0.52-0.54 0.47-0.56% Removal of:Sulfur 66-72 73-80 73-80Carbon Residue 39-47 44 45-46Pentane Insolubles -- -- --Nitrogen 18-27 16-19 12-27______________________________________

Data in Table IIIA and IIIB show that the removal of sulfur, Ramsbottom carbon residue, pentane insolubles and nitrogen was consistently higher in invention runs 3-6 (with La, Ce and Zn compounds) than in run 1 (with no added Metal). Zn compounds (runs 5, 6) were also more effective than Mo(CO).sub.6 (run 2) in removing sulfur. The density (at 38.5.degree. C.) of the products ranged from 0.894 to 0.902 g/cc for invention run 3, and from 0.899 to 0.900 g/cc for invention run 5.

Based on these results, it is believed that other metals of Group IIB and Group IIIB would also be effective.

EXAMPLE III

An Arabian heavy crude (containing about 30 ppm nickel, 102 ppm vanadium, 4.17 wt % sulfur, 12.04 wt %, carbon residue, and 10.2 wt % pentane insolubles) was hydrotreated in accordance with the procedure described in Example I. The LHSV of the oil was 1.0, the pressure was 2250 psig, the hydrogen feed rate was 4,800 standard cubic feet hydrogen per barrel of oil, and the temperature was 765.degree. F. (407.degree. C.). The hydrofining catalyst was presulfided catalyst D.

In run 4, no molybdenum was added to the hydrocarbon feed. In run 5, molybdenum (IV) octoate was added for 19 days. Then molybdenum (IV) octoate, which had been heated at 635.degree. F. for 4 hours in Monagas pipe line oil at a constant hydrogen pressure of 980 psig in a stirred autoclave, was added for 8 days. The results of run 4 are presented in Table IV and the results of run 5 in Table V.

TABLE IV______________________________________(Run 4)Days on PPM Mo PPM in Product Oil % RemovalStream in Feed Ni V Ni + V of Ni + V______________________________________ 1 0 13 25 38 71 2 0 14 30 44 67 3 0 14 30 44 67 6 0 15 30 45 66 7 0 15 30 45 66 9 0 14 28 42 6810 0 14 27 41 6911 0 14 27 41 6913 0 14 28 42 6814 0 13 26 39 7015 0 14 28 42 6816 0 15 28 43 6719 0 13 28 41 6920 0 17 33 50 6221 0 14 28 42 6822 0 14 29 43 6723 0 14 28 42 6825 0 13 26 39 7026 0 9 19 28 7927 0 14 27 41 6929 0 13 26 39 7030 0 15 28 43 6731 0 15 28 43 6732 0 15 27 42 68______________________________________ TABLE V______________________________________(Run 5)Days on PPM Mo PPM in Product Oil % RemovalStream in Feed Ni V Ni + V of Ni + V______________________________________Mo (IV) octoate as Mo Source 3 23 16 29 45 66 4 23 16 28 44 67 7 23 13 25 38 71 8 23 14 27 41 6910 23 15 29 44 6712 23 15 26 41 6914 23 15 27 42 6816 23 15 29 44 6717 23 16 28 44 6720 Changed to hydro-treated Mo (IV) octoate22 23 16 28 44 6724 23 17 30 47 6426 23 16 26 42 6828 23 16 28 44 67______________________________________

Referring now to Tables IV and V, it can be seen that the percent removal of nickel plus vanadium remained fairly constant. No improvements in metals, sulfur, carbon residue, and pentane insolubles removal was seen when untreated or hydro-treated molybdenum octoate was introduced in run 5. This demonstrates that not all decomposable metal carboxylates provide a beneficial effect.

EXAMPLE IV

This example illustrates the rejuvenation of a substantially deactivated sulfided, promoted desulfurization catalyst (referred to as catalyst D in Table I) by the addition of a decomposable Mo compound to the feed, essentially in accordance with Example I except that the amount of Catalyst D was 10 cc. The feed was a supercritical Monagas oil extract containing about 29-35 ppm Ni, about 103-113 ppm V, about 3.0-3.2 weight-% S and about 5.0 weight-% Ramsbottom C. LHSV of the feed was about 5.0 cc/cc catalyst/hr; the pressure was about 2250 psig; the hydrogen feed rate was about 1000 SCF H.sub.2 per barrel of oil; and the reactor temperature was about 775.degree. F. (413.degree. C.). During the first 600 hours on stream, no Mo was added to the feed; thereafter Mo(CO).sub.6 was added. Results are summarized in Table VI.

TABLE VI__________________________________________________________________________Feed ProductHours on Added Ni V (Ni + V) Ni V (Ni + V) % RemovalStream Mo (ppm) (ppm) (ppm) (ppm) (ppm) (ppm) (ppm) of (Ni + V)__________________________________________________________________________ 46 0 35 110 145 7 22 29 8094 0 35 110 145 8 27 35 76118 0 35 110 145 10 32 42 71166 0 35 110 145 12 39 51 65190 0 32 113 145 14 46 60 59238 0 32 113 145 17 60 77 47299 0 32 113 145 22 79 101 30377 0 32 113 145 20 72 92 37430 0 32 113 145 21 74 95 34556 0 29 108 137 23 82 105 23586 0 29 108 137 24 84 108 21646 25 29 103 132 22 72 94 29676 25 29 103 132 20 70 90 32682 25 28 101 129 18 62 80 38706 25 28 101 129 16 56 72 44712 25 28 101 129 16 50 66 49736 25 28 101 129 9 27 36 72742 25 28 101 129 7 22 29 78766 25 28 101 129 5 12 17 87__________________________________________________________________________

Data in Table VI show that the demetallization activity of a substantially deactivated catalyst (removal of Ni+V after 586 hours: 21%) was dramatically increased (to about 87% removal of Ni+V) by the addition of Mo(CO).sub.6 for about 120 hours. At the time when the Mo addition commenced, the deactivated catalyst had a metal (Ni+V) loading of about 34 weight-% (i.e., the weight of the fresh catalyst had increased by 34% due to the accumulation of metals). At the conclusion of the test run, the metal (Ni+V) loading was about 44 weight-%. Sulfur removal was not significantly affected by the addition of Mo. Based on these results, it is believed that the addition of decomposable Group IIB or Group IIIB compounds to the feed would also be beneficial in enhancing the demetallization activity of substantially deactivated catalysts.

Claims

1. A process for hydrofining a hydrocarbon-containing feed stream comprising the steps of:

introducing a suitable decomposable compound selected from the group consisting of compounds of the metals of Group IIB and Group IIIB of the Periodic Table into said hydrocarbon-containing feed stream; and

contacting said hydrocarbon-containing feed stream containing said decomposable compound under suitable hydrofining conditions with hydrogen and a catalyst composition comprising a support selected from the group consisting of alumina, silica and silica-alumina and a promoter comprising at least one metal selected from Group VIB, Group VIIB and Group VIII of the Periodic Table.

2. A process in accordance with claim 1 wherein said suitable decomposable compound is a zinc compound.

3. A process in accordance with claim 2 wherein said suitable decomposable compound is selected from the group consisting of zinc naphthenate and zinc dithiophosphate.

4. A process in accordance with claim 1 wherein said suitable decomposable compound is a cerium compound.

5. A process in accordance with claim 4 wherein said suitable decomposable compound is cerium octoate.

6. A process in accordance with claim 1 wherein said suitable decomposable compound is a lanthanum compound.

7. A process in accordance with claim 6 wherein said suitable decomposable compound is lanthanum octoate.

8. A process in accordance with claim 1 wherein ssaid catalyst composition comprises alumina, cobalt and molybdenum.

9. A process in accordance with claim 8 wherein said catalyst composition additionally comprises nickel.

10. A process in accordance with claim 1 wherein a sufficient quantity of said decomposable compound is added to said hydrocarbon-containing feed stream to result in a concentration of Group IIB metal or Group IIIB metal in said hydrocarbon-containing feed stream in the range of about 1 to about 500 ppm.

11. A process in accordance with claim 10 wherein a sufficient quantity of said decomposable compound is added to said hydrocarbon-containing feed stream to result in a concentration of Group IIB metal or Group IIIB metal in said hydrocarbon-containing feed stream in the range of about 5 to about 50 ppm.

12. A process in accordance with claim 1 wherein said suitable hydrofining conditions comprise a reaction time between said catalyst composition and said hydrocarbon-containing feed stream in the range of about 0.1 hour to about 10 hours, a temperature in the range of 250.degree. C. to about 550.degree. C., a pressure in the range of about atmospheric to about 10,000 psig and a hydrogen flow rate in the range of about 100 to about 20,000 standard cubic feet per barrel of said hydrocarbon-containing feed stream.

13. A process in accordance with claim 1 wherein said suitable hydrofining conditions comprise a reaction time between said catalyst composition and said hydrocarbon-containing feed stream in the range of about 0.3 hours to about 5 hours, a temperature in the range of 340.degree. C. to about 440.degree. C., a pressure in the range of about 500 to about 3,000 psig and a hydrogen flow rate in the range of about 1,000 to about 6,000 standard cubic feet per barrel of said hydrocarbon-containing feed stream.

14. A process in accordance with claim 1 wherein the adding of said decomposable compound to said hydrocarbon-containing feed stream is interrupted periodically.

15. A process in accordance with claim 1 wherein said hydrofining process is a demetallization process and wherein said hydrocarbon-containing feed stream contains metals.

16. A process in accordance with claim 15 wherein said metals are nickel and vanadium.

17. In a hydrofining process in which a hydrocarbon-containing feed stream is contacted under suitable hydrofining conditions with hydrogen and a catalyst composition comprising a support selected from the group comprising alumina, silica and silica-alumina and a promoter comprising at least one metal selected from Group VIB, Group VIIB and Group VIII of the periodic table and in which said catalyst composition has been at least partially deactivated by use in said hydrofining process, the improvement comprising the step of adding a suitable decomposable compound selected from the group consisting of compounds of the metals of Group IIB and Group IIIB of the Periodic Table to said hydrocarbon-containing feed stream under suitable mixing conditions prior to contacting said hydrocarbon-containing feed stream with said catalyst composition, wherein said decomposable compound is not added to said hydrocarbon-containing feed stream until said catalyst composition is at least partially deactivated by said use in said hydrofining process.

18. A process in accordance with claim 17 wherein said suitable decomposable compound is a zinc compound.

19. A process in accordance with claim 18 wherein said suitable decomposable compound is selected from the group consisting of zinc naphthenate and zinc dithiophosphate.

20. A process in accordance with claim 17 wherein said suitable decomposable compound is a cerium compound.

21. A process in accordance with claim 20 wherein said suitable decomposable compound is cerium octoate.

22. A process in accordance with claim 17 wherein said suitable decomposable compound is a lanthanum compound.

23. A process in accordance with claim 22 wherein said suitable decomposable compound is lanthanum octoate.

24. A process in accordance with claim 17 wherein said catalyst composition is a spent catalyst composition due to use in said hydrofining process.

25. A process in accordance with claim 17 wherein said catalyst composition comprises alumina, cobalt and molybdenum.

26. A process in accordance with claim 25 wherein said catalyst composition additionally comprises nickel.

27. A process in accordance with claim 17 wherein a sufficient quantity of said decomposable compound is added to said hydrocarbon-containing feed stream to result in a concentration of Group IIB metal or Group IIIB metal in said hydrocarbon-containing feed stream in the range of about 1 to about 500 ppm.

28. A process in accordance with claim 27 wherein a sufficient quantity of said decomposable compound is added to said hydrocarbon-containing feed stream to result in a concentration of Group IIB metal or Group IIIB metal in said hydrocarbon-containing feed stream in the range of about 5 to about 50 ppm.

29. A process in accordance wwith claim 17 wherein said suitable hydrofining conditions comprise a reaction time between said catalyst composition and said hydrocarbon-containing feed stream in the range of about 0.1 hour to about 10 hours, a temperature in the range of 250.degree. C. to about 550.degree. C., a pressure in the range of about atmospheric to about 10,000 psig and a hydrogen flow rate in the range of about 100 to about 20,000 standard cubic feet per barrel of said hydrocarbon-containing feed stream.

30. A process in accordance with claim 17 wherein said suitable hydrofining conditions comprise a reaction time between said catalyst composition and said hydrocarbon-containing feed stream in the range of about 0.3 hours to about 5 hours, a temperature in the range of 340.degree. C. to about 440.degree. C., a pressure in the range of about 500 to about 3,000 psig and a hydrogen flow rate in the range of about 1,000 to about 6,000 standard cubic feet per barrel of said hydrocarbon-containing feed stream.

31. A process in accordance with claim 17 wherein the adding of said decomposable compound to said hydrocarbon-containing feed stream is interrupted periodically.

32. A process in accordance with claim 17 wherein said hydrofining process is a demetallization process and wherein said hydrocarbon-containing feed stream contains metals.

33. A process in accordance with claim 32 wherein said metals are nickel and vanadium.