Wet grinding operations, defined by grinding processes using water-based coolant systems, have been found to be hampered with shorter life of the abrasive product as compared with dry grinding applications. This phenomenon typically has been addressed by addition of sealant in the formulation of make resin employed in the abrasive. Chemicals added to the make resin to counteract the effect of water generally include hydrophobic molecules that increase hydrophobicity of the make resin to thereby reduce the intake of water, to retard swelling of the resin system consequent to deterioration of mechanical properties, and to retard abrasive loss. Examples of hydrophobic molecules typically are siloxanes and organo-functional silanes (hereinafter referred to as “silanes”) or other organic molecules that have hydrophobic moieties, such as vinyl bonds, and sulfur or fluorine atoms in the organic molecule. However, inclusion of hydrophobic components in the make resin often does not protect abrasive particles upon contact with water, thereby permitting water over extended use periods to migrate along abrasive particles until the abrasive tool fails. In the case of coated abrasive products, contact of the backing material with water employed as a coolant can cause separation of the abrasive and make coat from the backing material.
In one alternative, abrasive particles are first treated by applying a coating of a silane. Hydrolysis of the silane at a surface of an abrasive particle can cause formation of covalent bonds, particularly where the abrasive particle is a metal. However, formation of a hydrophilic coating on grains can reduce the strength with which particles are held in place by the make coat, particularly where the make coat includes a hydrophobic component, such as a hydrophobic silane component.
Therefore, a need exists for abrasive particles, coated abrasive products and other grinding tools, such as bonded abrasive tools, that overcome or minimize the above-referenced problems.
The invention generally is directed to surface-modified abrasive grains, coated abrasive products, bonded abrasive products, and methods of manufacturing and using the grains and abrasive products. In one embodiment, the invention is a surface-modified abrasive grain that includes an abrasive grain substrate and a film on the abrasive grain that includes a relatively hydrophilic silane component and a relatively hydrophobic silane component. The relatively hydrophilic silane component, in one embodiment, can be one member selected from the group consisting of amines, diamines, triamines, azine, azol, ureido, isocyanate, alkoxy, acetoxy, oximino, chloro, morpholinyl and piperazinyl silanes, and the relatively hydrophobic silane can be one member selected from the group consisting of vinyl silanes, methacrylate silanes, sulfur silanes, mercapto silanes, epoxy silanes and phenyl silanes. The film can be either a single layer that includes a combination of relatively hydrophilic and relatively hydrophobic silane components. In this embodiment, polymers of the relatively hydrophilic and hydrophobic components can be distinct polymers, or co-polymers of the relatively hydrophilic and relatively hydrophobic silane components. Typically, the abrasive grain substrate includes at least one member selected from the group consisting of aluminum oxide, silicon carbide, fused ceramics, alloy abrasives, sol-gels, ceramic grains and super abrasives.
In another specific embodiment, the coating of the abrasive particles includes two layers, the first of which is most proximate to the abrasive particle and includes at least one relatively hydrophilic silane component. The second layer is distal, and generally applied over the first layer. The second layer includes at least one silane component that is hydrophobic relative to the silane component of the first layer.
In another embodiment, the invention is a coated abrasive product that includes surface-modified abrasive grains of the invention. In still another embodiment, the invention is bonded abrasive product employing the surface-modified abrasive particles of the invention.
A surface-modified abrasive grain of the invention can be formed, in one embodiment, by combining a relatively hydrophilic and relatively hydrophobic silane components to form a mixture. The mixture is then combined with a carrier that includes water to form a silane solution. At least a portion of the silane component is hydrolyzed to form a hydrolyzed solution, which is then blended with an abrasive grain component to thereby form the surface-modified abrasive grain.
A method of forming a coated abrasive product of the invention includes combining the surface-modified abrasive grains of the invention with a resin and then applying the combined surface-modified abrasive grains and resin to a backing. The resin is then cured, thereby forming the coated abrasive product.
A method of making a bonded abrasive product of the invention includes combining surface-modified abrasive grains of the invention with a resin or a vitreous glass bond along with a binder. The resulting green compound is molded or formed into the desired shape and subsequently thermally cured or fired to result in the final product.
Other embodiments of the invention include grinding or cutting a workpiece employing a coated or bonded abrasive product of the invention.
The invention has many advantages. For example, the relatively hydrophilic silane component of the film is believed to effectively seep into most types of abrasive particles, thereby facilitating wetting of the component with a sealant that includes the relatively hydrophilic silane component. In addition, it is believed that the same film forms covalent bonds that bind the sealant tightly to the particle. In addition, the relative hydrophobic silane component of the film can either be blended with the relatively hydrophilic silane component or applied as a separate film that binds tightly to most make coat resins, particularly those that include a hydrophobic silane component apart from that of the film of the abrasive grain. As a result, the film of the abrasive grain does not separate easily from either the particle or from the make coat upon exposure to water, thereby significantly reducing penetration of the abrasive product by water coolants employed during grinding or cutting. Material Removal Rate (MRR) and Cumulative Material Retention (CMR) are significantly increased as a result. “Surface finish,” or “Ra,” of a work piece also is significantly improved relative to that produced by use of abrasive products which do not employ a silane treatment or film of the invention. Further, the usable life of abrasive products of the invention can be significantly extended beyond that which would be expected of abrasive products that do not employ the surface-modified abrasive grains of the invention.
The foregoing will be apparent from the following more particular description of exampled embodiments of the invention, as illustrated by the accompanied drawings in which like reference characters refer to the same parts throughout the different views. The drawings are not necessarily to scale, with emphasis instead being placed on illustrated embodiments of the present invention.
The invention generally is directed to surface-modified abrasive grains, and to coated abrasive products and bonded abrasive products employing the surface-modified abrasive grains. The surface-modified abrasive grains of the invention include an abrasive grain substrate and a film on the abrasive grain that includes a relatively hydrophilic silane component and a relatively hydrophobic silane component. The invention is also directed to methods of making the surface-modified abrasive grains of the invention, as well as to coated and bonded abrasive products employing the surface-modified abrasive grains, and to methods of making and using coated and bonded abrasive products of the invention.
The term “relatively hydrophilic silane component,” as that term is defined herein, means a silane monomer, oligomer or polymer, or to a monomeric repeating unit of an oligomer or polymer that exhibits more affinity for water than does another monomer, oligomer or polymer, or repeating monomeric silane component with which the relatively hydrophilic silane component has been combined. Examples of relatively hydrophilic silane components include amino silanes, amino silanes, ureido silanes, isocyanate silanes, oximino silanes and chloro silanes. Specific examples of particularly suitable relatively hydrophilic silane components include 3-aminopropyltriethoxy silane, 3-Aminopropyltriethoxysilane, Bis[(3-Triethoxysilyl)Propyl]Amine, 3-Aminopropyltrimethoxysilane, 3-Aminopropylmethyldiethoxysilane, 3-Aminopropylmethyldimethoxysilane, Aminoethylaminopropyltrimethoxysilane, Aminoethylaminopropyltriethoxysilane, Aminoethylaminopropylmethyldimethoxysilane, Aminoethylaminopropylmethyldiethoxysilane, Aminoethylaminomethyltriethoxysilane, Aminoethylaminomethylmethyldiethoxysilane, Diethylenetriaminopropyltrimethoxysilane, Diethylenetriaminopropyltriethoxysialne, Diethylenetriaminopropylmethyldimethoxysilane, Diethylenetriaminopropylmethyldiethoxysilane, Diethylenetriaminomethylmethyldiethoxysilane, Diethylaminomethyltriethoxysilane, Diethylaminomethylmethyldiethoxysilane, Diethylaminomethyltrimethoxysilane, Diethylaminopropyltrimethoxysilane, Diethylaminopropylmethyldimethoxysilane, Diethylaminopropylmethyldiethoxysilane, N—(N-Butyl)-3-Aminopropyltrimethoxysilane, (N-Phenylamino)Methyltrimethoxysilane, (N-Phenylamino)Methyltriethoxysilane, (N-Phenylamino)Methylmethyldimethoxysilane, (N-Phenylamino)Methylmethyldiethoxysilane, 3-(N-Phenylamino)Propyltrimethoxysilane, 3-(N-Phenylamino)Propyltriethoxysilane, 3-(N-Phenylamino)Propylmethyldimethoxysilane, 3-(N-Phenylamino)Propylmethyldiethoxysilane, piperazinylpropylmethyldimethoxysilane, piperazinylpropylmethyldiethoxysilane, piperazinylmethylmethyldiethoxysilane, Morpholinylpropyltrimethoxysilane, Morpholinylpropyltriethoxysilane, Morpholinylpropylmethyldimethoxysilane, Morpholinylpropylmethyldiethoxysilane, Morpholinylmethyltrimethoxysilane, Morpholinylmethylmethyldiethoxysilane, Aminohexylaminomethyltrimethoxysilane, Hexanediaminomethyltriethoxysilane, Aminohexylaminomethyltrimethoxysilane, Octanoylaminopropyltriethoxysilane, Cyclohexylaminopropyltrimethoxysilane, Cyclohexylaminopropyltriethoxysilane, Cyclohexylaminopropylmethyldimethoxysilane, Cyclohexylaminopropylmethyldiethoxysilane, 3-ureidopropyltrimethoxysilane, 3-ureidopropyltriethoxysilane, 3-isocyanatepropyltrimethoxysilane, 3-isocyanatepropyltriethoxysilane, Trimethoxysilane, Triethoxysilane, Methyldimethoxysilane, Methyldiethoxysilane, Methyltrimethoxysilane, Methyltriethoxysilane, Methyltripropoxysilane, Methyltributoxysilane, Methyltris(Tert-Butylperoxy)Silane, Dimethylethoxysilane, Dimethyldimethoxysilane, Dimethyldiethoxysilane, Propyltrimethoxysilane, N-Butyltrimethoxysilane, N-Butyltriethoxysilane, 1-Butyltrimethoxysilane, 1-Butyltriethoxysilane, Allyltriethoxysilane, Dodecyltrimethoxysilane, Dodecylmethyldimethoxysilane, Octodecyltrimethoxysilane, Octodecyltriethoxysilane, Octodecylmethyldimethoxysilane, N-Octyltrimethoxysilane, N-Octyltriethoxysilane, Octylmethyldiethoxysilane, Cyclohexyltriethoxysilane, Tetraacetoxysilane, Ethyltriacetoxysilane, Methyltriacetoxysilane, Dimethyldiacetoxysilane, Di-Tertbutoxy-Diacetoxysilane, Phenyltris(Methylethylketoxime)Silane, Tetra(Methylisobutylketoxime)Silane, Trimethyl(Methylethylketoxime)Silane, Dimethyldi(Methylethylketoxime)Silane, Methyltris(Methylisobutylketoxime)Silane, Methyltris(Acetoxime)Silane, Methyltris(Methylethylketoxime)Silane, Vinyltris(Methylisobutylketoxime)Silane, Methylvinyldi(Cyclohexanoneoxime)Silane, Methylvinyldi(Methylethylketoxime)Silane, Vinyltris(Methylethylketoxime)Silane.
As defined herein, the term “relatively hydrophobic silane component,” means monomer, oligomeric and polymeric compounds that include moieties that cause the monomer, oligomer or polymer to have an affinity for water that is less than that of another silane component with which it is combined. Examples of classes of relatively hydrophobic silane components include vinyl silanes, methacrylate silanes, sulfur silanes, mercapto silanes, epoxy silanes, phenyl silanes. Examples of particular relatively hydrophobic silane components include γ-methacryloxypropyltrimethoxy silane, Vinyltrimethoxysilane, Vinyltriethoxysilane, Vinyltris(2-Methoxyethoxy)Silane, Vinyltrisisopropoxysilane, Vinyltris(Tert-Butylperoxy)Silane, Vinyldimethylethoxysilane, Vinylmethyldimethoxysilane, Vinylmethyldiethoxysilane, Allyltriethoxysilane, Vinyltriacetoxysilane, Vinyltrichlorosilane, Vinyldimethylchlorosilane, Vinylmethyldichlorosilane, Vinyltris(Methylisobutylketoxime)Silane, Methylvinyldi(Cyclohexanoneoxime)Silane, Methylvinyldi(Methylethylketoxime)Silane, Vinyltris(Methylethylketoxime)Silane, 3-Methacryloxypropyltrimethoxysilane, Methacryloxypropyltris(Trimethylsiloxy)Silane, 3-Methacryloxypropyltriethoxysilane, 3-Methacryloxypropylmethyldimethoxysilane, 3-Methacryloxypropylmethyldiethoxysilane, Methacryloxymethyltriethoxysilane, 3-Mercaptopropyltrimethoxysilane, 3-Mercaptopropyltriethoxysilane, 3-Mercaptopropylmethyldimethoxysilane, Bis(Triethoxysilylpropyl)Tetrasulfide, Bis(Triethoxysilylpropyl)Disulfide, Bis(Triethoxysilylpropyl)Polysulfide, Thiocyanto silane: 3-Thiocyanatopropyltriethoxysilane, 3-Glycidoxypropyltrimethoxysilane, 3-Glycidoxypropyltriethoxysilane, 3-Glycidoxypropylmethyldiethoxysilane, 3-Glycidoxypropylmethyldimethoxysilane, Vinyltriacetoxysilane.
The definitions of “relatively hydrophilic silane component” and “relatively hydrophobic silane component” mean that inclusion in a single layer, or within distinct layers of an abrasive particle, of two silane components that differ in affinity for water, will constitute the presence of a “relatively hydrophilic silane component” and a “relatively hydrophobic silane component.” Further, preferably, at least one of the silanes can chemically react with a component of a binder resin employed to form a coated abrasive product or bonded abrasive tool of the invention. In a more preferred embodiment, at least one of the silanes forms a covalent bond with a component of the binder resin. Suitable resins are such as are known in the art.
Typically, the weight ratio of film that includes relatively hydrophilic and relatively hydrophobic silane components over an abrasive grain is in the range of between about 1:99 and about 99:1 of relatively hydrophilic silane component to relatively hydrophobic silane component. In a preferred embodiment, the ratio is in a range of between about 1:49 and about 49:1. In a particularly preferred embodiment, the ratio is in a range of between about 1:9 and about 9:1.
The weight ratio of film to abrasive particle in a coated abrasive particle of the invention typically is in a range between about 1:8000 and about 1:400. In a preferred embodiment the weight ratio is between about 1:6000 and about 1:300. In an even more preferred embodiment, the weight ratio is in a range of between about 1:4000 and about 1:200.
The thickness of a coating that includes relatively hydrophilic an relatively hydrophobic silane components over an abrasive particle can be, for example, in a range of between about 1 angstrum (Å) and 5 microns. In a preferred embodiment the thickness of the coating is between about 10 Å and about 2 microns. In another embodiment, the thickness of the coating is a range of between about 15 Å and about 1 micron.
Generally, any abrasive particle that is suitable as an abrasive in industrial or commercial applications is suitable for use in the invention. A suitable material for abrasive particles useful in the invention can be of any conventional abrasive particle material utilized in the formation of coated abrasive tools. Examples of suitable abrasive particle materials for use in the invention include diamond, corundum, emery, garnet, chert, quartz, sandstone, chalcedony, flint, quartzite, silica, feldspar, pumice and talc, boron carbide, cubic boron nitride, fused alumina, ceramic aluminum oxide, heat treated aluminum oxide, alumina zirconia, glass, silicon carbide, iron oxides, tantalum carbide, cerium oxide, tin oxide, titanium carbide, synthetic diamond, manganese dioxide, zirconium oxide, and silicon nitride.
Other suitable grains include agglomerates such as are described in U.S. Pat. No. 6,797,023, the teachings of which are incorporated herein by reference in their entirety. A coated abrasive product of the invention can include particulate material containing green, unfired abrasive comprising abrasive grit particles and nanoparticle binder, as described in U.S. application Ser. No. 12/018,589, filed Jan. 23, 2008, the teachings of which are incorporated herewith in their entirety.
The abrasive materials can be oriented or can be applied to the substrate without orientation (i.e., randomly), depending upon the particular desired properties of the coated abrasive tools. In choosing an appropriate abrasive material, characteristics, such as size, hardness, compatibility with workpieces and heat conductivity, are generally considered. Abrasive particle materials useful in the invention typically have a particle size ranging from about 10 nanometers (nm) to about 6 millimeters (mm), such as from about 100 nm to about 3 mm, or from about 1 micron (μ) to about 600μ.
The film of surface-modified abrasive particles of the invention can include a single or a plurality of layers. In one embodiment, the film is a single layer that includes a relatively hydrophilic silane component and a relatively hydrophobic silane component. Each of the relatively hydrophilic and relatively hydrophobic silane components can independently be included in the coating as an independent monomer unit, an oligomer or a polymer. Further, the relatively hydrophilic and relatively hydrophobic silane components can be components of oligomers or polymers. The polymers can be co-polymers or block co-polymers, such as random block co-polymers, of at least one of the hydrophilic and relatively hydrophobic silane components. Similarly, oligomers can include at least one of the relatively hydrophilic and relatively hydrophobic silane components.
In another embodiment, the film of the surface-modified abrasive grain of the invention includes a first film layer proximate to the abrasive particle that includes only, or predominately, a relatively hydrophilic silane component, as opposed to relatively hydrophobic silane component. A second, or distal film layer of the film predominately includes a relatively hydrophobic silane component as opposed to the relatively hydrophilic silane component. It is believed that surface-modification of an abrasive particle with a relatively hydrophilic silane component significantly increases wettability of the particle and provides a better seal against water when an abrasive product that employs the surface-modified abrasive grain is in use. It is further believed that, typically, the relatively hydrophilic silane component will form a relatively high proportion of covalent bonds with the abrasive grain substrate. It is also believed that the relatively hydrophobic silane component will bind tightly both with the relatively hydrophilic silane component and with materials generally employed as make coats of coated abrasive products and with bond materials of bonded abrasive products.
In one embodiment, a method of forming a surface-modified abrasive grain of the invention includes combining relatively hydrophobic and relatively hydrophilic silane components to form a mixture. The mixture is combined with a solvent to form a silane solution. Examples of suitable solvents include isopropyl alcohol, ethanol, methanol, toluene, acetone, water and mixtures thereof. The amount of solvent employed is at least sufficient to dissolve the silane components. In one embodiment, the pH of the solution can be adjusted to a suitable pH, such as a pH in a range of between about 3 and about 7, or, more preferably, between about 4 and about 6. An example of a suitable method by which the pH can be adjusted is addition of acetic acid. Other methods of adjusting the pH include, for example, use of maelic acid, stearic acid, maelic anhydride, weak solutions of HCl, HNO3, H2SO4, ammonium chloride, ammonium hydroxide, sodium hydroxide solution, potassium hydroxide solution. The solution is reacted to form an at least partially oligomerized silane solution. Further, depending upon the silane component employed, the solution can be at least partially hydrolyzed to form a hydrolyzed solution. The at least partially oligomerized silane solution, is then blended with an abrasive grain component to form the surface-modified abrasive grain. In one embodiment, the surface-modified abrasive grain is exposed to ambient, or, alternatively, some elevated temperature, or other suitable conditions, to thereby cure the film. Preferably, the surface-modified grain is cured at a temperature in a range of between about 10° C. and about 300° C. Also, preferably, the period of time of the curing is in a range of between about 15 minutes and about 24 hours. In one embodiment the surface-modified grain is cured at a temperate of about 10° C. for about 24 hours. In another embodiment, the surface-modified grain is cured at a temperature of about 80° C. for about 3 hours, and in still another embodiment, the surface-modified grain is cured at a temperature of about 100° C. for about 1.5 hours. In another embodiment, the surface-modified grain is cured at a temperature of about 200° C. for about 30 minutes, or at about 300° C. for about 15 minutes.
In a preferred embodiment, the relatively hydrophilic silane component is 3-aminopropyltriethoxy silane, the relatively hydrophobic silane component is γ-methacryloxypropyltrimethoxy silane and a weight ratio of the two is about 1:1. In this preferred embodiment, the abrasive grain is a seeded-gel ceramic grain or powder, having a mean particle diameter of about 100 microns. The weight ratio of silane component to weight of abrasive particles is about 1:1000. The solvent is isopropyl alcohol and the pH is adjusted to a range of about 3-7 with glacial acetic acid. The surface-modified abrasive particles of this embodiment are cured at a temperature of a about 80° C. for a period of time of about 3 hours.
In another embodiment, the invention is a coated abrasive product. An example of a coated abrasive product of the invention is shown in
Coated and bonded abrasive products of the invention can optionally further include one or more additives, such as fillers, coupling agents, fibers, lubricants, surfactants, pigments, dyes, wetting agents, grinding aids, anti-loading agents, anti-static agents and suspending agents. In one embodiment, a filler component that can be employed in the invention includes a cryolite and at least one member selected from the group consisting of a hexafluorophosphate, a hexafluoroferrate, a hexafluorozirconate and ammonium tetrafluoroborate ((NH4)BF4). Examples of hexafluorophosphates (salts of PF6−) include ammonium salt ((NH4)PF6), alkali metal salts (e.g., LiPF6, NaPF6, KPF6, CsPF6, etc.) and alkaline earth metal salts (e.g., Mg(PF6)2, Ca(PF6)2, Sr(PF6)2, Ba(PF6)2, etc.), and mixed salts thereof (e.g., ammonium and sodium salts, such as (NH4)Na(PF6)2, ammonium and potassium salts, such as (NH4)K(PF6)2, sodium and potassium salts, such as NaK(PF6)2, etc.). Specific examples of hexafluorophosphates include sodium hexafluorophosphate (NaPF6) and potassium hexafluorophosphate (KPF6), and combinations thereof. Examples of hexafluoroferrates (salts of FeF63-) include ammonium salt ((NH4)3FeF6), alkali metal salts (e.g., Li3FeF6, Na3FeF6, K3FeF6, Cs3FeF6, etc.) and alkaline earth metal salts (e.g., Mg3(FeF6)2, Ca3(FeF6)2, Sr3(FeF6)2, Ba3(FeF6)2, etc.), and mixed salts thereof (e.g., ammonium and sodium salts, such as (NH4)Na2FeF6 and (NH4)2NaFeF6, ammonium and potassium salts, such as (NH4)K2FeF6 and (NH4)2KFeF6, sodium and potassium salts, such as K2NaFeF6 and KNa2FeF6, calcium and sodium salts, such as CaNaFeF6, calcium and potassium salts, such as CaKFeF6, etc.). Specific examples of hexafluoroferrates include ammonium hexafluoroferrate ((NH4)3FeF6) and alkali metal hexafluoroferrates, such as sodium hexafluoroferrate (Na3FeF6) and potassium hexafluoroferrate (K3FeF6), and combinations thereof. Examples of hexafluorozirconates (salts of ZrF62-) include ammonium salt ((NH4)2ZrF6), alkali metal salts (e.g., Li2ZrF6, Na2ZrF6, K2ZrF6, Cs2ZrF6, etc.) and alkaline earth metal salts (e.g., MgZrF6, CaZrF6, SrZrF6, BaZrF6, etc.), and mixed salts thereof (e.g., ammonium and sodium salts, such as (NH4)NaZrF6, ammonium and potassium salts, such as (NH4)KZrF6, sodium and potassium salts, such as NaKZrF6, etc.). Specific examples of hexafluorozirconates include ammonium hexafluorozirconate ((NH4)2ZrF6) and alkali metal hexafluorozirconates, such as sodium hexafluorozirconate (Na2ZrF6) and potassium hexafluorozirconate (K2ZrF6), and combinations thereof. In a specific embodiment, at least one of the hexafluorophosphate, the hexafluoroferrate and the hexafluorozirconate is an ammonium salt or a sodium salt. In yet another specific embodiment, the hexafluorophosphate is ammonium hexafluorophosphate, the hexafluoroferrate is sodium hexafluoroferrate, and the hexafluorozirconate is sodium hexafluorozirconate. In yet another specific embodiment, the filler component includes at least one member selected from the group consisting of ammonium hexafluorophosphate, sodium hexafluoroferrate, sodium hexafluorozirconate and ammonium tetrafluoroborate. In yet another specific embodiment, the filler component includes at least one member selected from the group consisting of ammonium hexafluorophosphate, sodium hexafluoroferrate and sodium hexafluorozirconate. In yet another specific embodiment, the filler component includes at least one member selected from the group consisting of sodium hexafluorozirconate and sodium hexafluoroferrate.
As used herein, a “cryolite” means a salt of aluminum hexafluoride (AlF63-), such as an alkali metal salt, an alkaline earth metal salt, or an ammonium salt, or a combination thereof. Examples of cryolites include lithium aluminum hexafluoride (Li3AlF6), sodium aluminum hexafluoride (Na3AlF6), potassium aluminum hexafluoride (K3AlF6), ammonium aluminum hexafluoride ((NH4)3AlF6), sodium ammonium hexafluoride (e.g., K(NH4)2AlF6 or K2(NH4)AlF6), potassium ammonium aluminum hexafluoride (e.g., Na(NH4)2AlF6 or Na2(NH4)AlF6), sodium potassium ammonium hexafluoride (i.e., NaK(NH4)AlF6), lithium ammonium aluminum hexafluoride (e.g. Li(NH4)2AlF6 or Li2(NH4)AlF6), etc. In one specific embodiment, sodium aluminum hexafluoride (Na3AlF6) is employed as a cryolite. The cryolite generally is present in an amount in a range of between about 2 wt % and about 98 wt %, such as between about 2 wt % and about 65 wt %, between about 2 wt % and about 50 wt %, of the filler component. In a specific embodiment, the amount of the cryolite is in a range between about 2 wt % and about 30 wt %, or between about 2 wt % and about 20 wt % of the filler component.
In another embodiment, the filler component that can be employed in the invention includes at least one member selected from the group consisting of a hexafluoroferrate, a hexafluorophosphate and a hexafluorozirconate. Suitable examples, including particular examples, of the hexafluoroferrate, the hexafluorophosphate and the hexafluorozirconate are as described above. In one specific embodiment, at least one of the hexafluoroferrate and the hexafluorozirconate is an ammonium salt or a sodium salt. In another specific embodiment, the filler component includes at least one member selected from the group consisting of a hexafluoroferrate and a hexafluorozirconate. In another specific embodiment, the filler component includes at least one member selected from the group consisting of sodium hexafluoroferrate and sodium hexafluorozirconate. Any suitable amount of the hexafluoroferrate, the hexafluorophosphate and the hexafluorozirconate can be employed in the invention.
In a specific embodiment, the hexafluoroferrate, the hexafluorophosphate and the hexafluorozirconate, disclosed herein, is each independently present in a range of between about 2 wt % and about 100 wt % of the filler component, such as between about 2 wt % and about 98 wt %, between about 35 wt % and about 98 wt % or between about 50 wt % and about 98 wt %, of the filler component. Alternatively, in an embodiment further employing a cryolite, the hexafluoroferrate, the hexafluorophosphate and the hexafluorozirconate is each independently present in a range of between about 2 wt % and about 98 wt % of the filler component, such as between about 35 wt % and about 98 wt % or between about 50 wt % and about 98 wt %, of the filler component.
In another specific embodiment, the filler component of the invention is present in an amount in a range between about 0.5 wt % and about 50 wt %, between about 10 wt % and about 50 wt %, between about 0.5 wt % and about 20 wt %, or between about 10 wt % and about 20 wt %, of the weight of the abrasive component.
In some embodiments, the filler component is incorporated into a bond component for abrasive products, such as coated abrasive products and bonded abrasive products. The bond component also includes a binder. Any suitable bond material known in the art can be used for the binder. The binder can be an inorganic binder or an organic binder. Suitable examples of organic binders include hide glue, urethane resins, acrylate resins, polyvinyl alcohols, epoxy resins, phenolic resins, urea-formaldehyde phenolic resins, aminoplast resins and melamine-formaldehyde resins, and combinations thereof. Suitable examples of inorganic binders include cement, calcium oxide, clay, silica, magnesium oxide, and combinations thereof. Specific examples of suitable inorganic binders can be found in U.S. Pat. Nos. 4,543,107; 4,898,597; 5,203,886; 5,025,723; 5,401,284; 5,095,665; 5,536,283; 5,711,774; 5,863,308; and 5,094,672, the entire teachings of all of which are incorporated herein by reference. Specific binder(s) included in the bond component can be chosen depending upon particular application(s) of the bond component, for example, types of abrasive products and/or coats employing the bond component.
A suitable method of fabricating a coated abrasive product of the invention includes combining surface-modified abrasive grains of the invention with a resin that will become the make coat. The combined surface-modified abrasive grains and resin are applied to the backing, and the resin is then cured by a suitable method, such as by radiation, thermal, microwave, RF polymerization, individually or in any combination, as is known in the art.
In another embodiment, the invention is bonded abrasive product, such as bonded wheel 22, shown in
In still another embodiment, the invention includes a method of grinding or cutting the work piece. The method includes the step of applying to the work piece an abrasive product of the invention that includes a polymerized combination of relatively hydrophilic and hydrophobic silane components. The abrasive product employed in the method can, for example, be either a coated abrasive product or a bonded abrasive product.
The following examples are representative only, and not intended to be limiting.
The following components were used for the preparation of the silane treated grain:
Procedure for Silane Treatment of Grain:
The silane treatment of the abrasive grain included three steps, namely (1) the preparation of the silane solution, (2) mixing of the prepared silane solution with the abrasive grain and blending the mix, and (3) curing the subsequent silane treated grain at elevated temperature.
Step 1. The recipe for preparing the silane solution was as follows:
The silane solution was prepared by starting out with measuring 5.68 grams of the γ-methacryloxypropyltrimethoxy silane and 5.68 grams of the 3-aminopropyltriethoxy silane. The two silanes were mixed using a magnetic stirrer. To this mixture 101.25 grams of isopropyl alcohol was added with continued agitation of the mix. Once the silane mixtures was dispersed in the isopropyl alcohol, 11.35 gram of DI water was added to the mix. Glacial acetic acid was added to the mix to attain a pH of 5-6 and the solution was left under agitation for 3-4 hours for hydrolysis of the silane.
Step 2. Treatment of the abrasive grain with the silane solution prepared in step 1:
For treating the abrasive grain with the silane solution prepared in Step 1, a V-blender with an intensifier bar was used. The V-blender was loaded with 9090.91 grams of seeded gel SG P150 grain to correspond with the amount of silane solution prepared in Step 1. The silane was pumped into the V-blender at around 5-7 milliliters per minute while the V-blender was on and turning. Once all the silane solution prepared in Step 1 had been pumped into the V-blender, the mixture was allowed to blend in the V-blender for another 15-20 minutes. The contents of the V-blender were then taken out of the V-blender and processed through Step 3.
Step 3. Curing the silane treated grain The V-blended seeded gel grain was subsequently cured in an oven at 80° C. for 3 hours to produce the final silane treated grain used for preparing the make resin slurry and in the electrostatic grain projection.
Example of Using Silane Treated Grain:
Formulation #1 Recipe:
The mixing instructions were as follows:
Engineered abrasive belts were prepared by employing the following steps:
Test machine: Loeser RSP374 centerless
Contact Wheel: 65 Shore A 1:3 serrated
Regulating wheel: 55 Shore A
Belt speed: 7400 SFPM
Contact Wheel speed: 1766 RPM
Regulating Wheel speed: 112 RPM
Belt Tension: 40 lbs
Regulating wheel tilt degree: 5
Reg. Wheel Swing Deg.: 2
Contact wheel pressure: 85 PSI
Regulating wheel pressure: 65 PSI
Applied forces: 30 or 50 lbs
Coolant: 2% Trimclear in DI water
Work piece material: 1045 CS; hardness 13.49 Rc
Work piece dimension: Φ1.5″×20″ long
Work pieces were passed through the centerless machine at setting force. The weight and surface finish of the parts and the thickness of the belt at three designated location were taken at part 1, 2, 5, 10, 15, 20, and then every 20 parts.
Two batches of belts were prepared using the formulation shown above. The control used grains without any treatment. Another batch used aforementioned surface-modified grains. The belts were tested on a Loesser centerless grinder with 30 lbs (
1.1. Materials used:
1.2. Steps of Silane Treatment of Abrasive Grain:
To prepare the silane solution for the pretreatment the requisite amount of silane was added to the beaker. If two silanes were to be used, as in the combination of A-174 and A-1100 silane both the silanes were added in the requisite amount and mixed in a beaker using a shear mixer. To this mixture the specified amount of isopropyl alcohol was added while continuing the agitation. At this point the pH was adjusted to 5 using glacial acetic acid. Further, the specified amount of water was added with continued stirring and the solution was left to stand for 3.5 hours for hydrolysis.
For the testing 6, 30 seconds grind cycles were used under dry grinding conditions. The substrate being ground was chosen as an acrylic panel using 6 panels such that each cycle would start afresh on a newly prepared sample. After each 30 seconds grind cycle the ground panel was weighed to measure the loss in weight and the material removal was recorded.
Coated abrasive disks were made as described with variation in grain and grain treatment. Treated FRPL and BFRPL Grains, which included single silane A174, bis-sulfur silane, and combination of A 174 and A 1100, were all evaluated against the control made by raw FRPL and BFRPL. For both grain types, disks with combination silane (combination of relatively hydrophilic silane component and relatively hydrophobic silane component) treatment grains showed the highest cumulative material removed compared to control and single (single silane component) treated grain versions. Although CMR of one of the single-silane-treatment versions performed close to that of the combination treatment (of relatively hydrophilic and relatively hydrophobic silane components) of the invention, the material removal rate after an initial break-in period of 30 seconds showed great advantage of combination-treated grain of the invention relative to grain treated with only a single silane component.
While this invention has been particularly shown and described with reference to exampled embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the scope of the invention encompassed by the appended claims.
This application claims the benefit of U.S. Provisional Application No. 61/124,618, filed on Apr. 18, 2008. The entire teachings of the above application are incorporated herein by reference.
Number | Date | Country | |
---|---|---|---|
61124618 | Apr 2008 | US |