1. Field of the Invention
The invention relates generally to the field of biomaterials and particularly to biocompatible nanostructured hydroxyapatite coatings on nanotubular titanium substrates.
2. Description of Background Art
Titanium and its alloys have been widely used to create dental and orthopedic implants because of their excellent biocompatibility and mechanical properties. Titanium (Ti) spontaneously forms an oxide layer up to a thickness of about 2 to 5 nm both in air and in the body, providing corrosion resistance. However, the normal oxide layer of titanium (TiO2) is not sufficiently bioactive to form a direct bond with juxtaposed bone, and much effort has been directed to developing coatings on Ti to enhance adhesion to bone as well as to promote adhesion of bone-forming cells. A lack of osseointegration is one factor leading to long-term failure of titanium implants.
In the past, many attempts have been made to improve the surface properties of Ti-based implants; e.g., by modifying Ti topography, chemistry, and surface energy, in order to better integrate into bone. Surface modification techniques have in general been aimed toward increasing surface roughness with the notion that such surfaces provide a more compatible scaffolding for attachment of bone-forming cells. A disadvantage of these approaches is that neither the mechanical nor the chemical methods produce highly controllable surface properties. Moreover, some of these methods have the potential to form surface residuals which can be harmful to osteoblast (bone forming cell) functions.
One method of titanium surface modification at the nanoscale level is use of controlled anodization. Self-assembled layers of vertically oriented TiO2 nanotubes with defined diameters are readily synthesized (Park, et al, 2007). TiO2 nanotube arrays can be fabricated by potentiostatic anodization of Ti foil (Paulose, et al., 2006). Lengths up to 134 μm have been achieved using fluoride ion solutions in combination with nonaqueous organic polar electrolytes, including dimethyl sulfoxide, formamide, ethylene glycol and N-methylformamide.
Cell adhesion, spreading and growth on Ti nanotube surfaces is enhanced compared to conventionally available smooth Ti surfaces. Oh, et al. (2006) and others have shown that adhesion/propagation of osteoblasts is substantially improved by the topographical features of the TiO2 nanotubes.
Several surface modifications and use of different coatings have been investigated as ways to improve osseointegration and biocompatibility. In a study to improve biocompatibility of dental implants, Vrespa, et al. (2002) coated titanium implants with vapor plasma spray applied nitrite titanium. While this process reduced erosion resistance, there was no effect on osseointegration as compared with uncoated Ti. On the other hand, chitosan coated titanium implanted in rabbits indicated some osseointegration similar calcium phosphate coated implants used as controls. The chitosan was solution cast and bonded to rough ground titanium (Bumgardner, et al., 2007). In a study in dogs using Ti coated with type 1 collagen, Welander, et al., (2007) found no significant difference soft tissue healing for non-coated compared to coated Ti implants.
Spire Corporation offers a calcium phosphate thin surface coating on implants such as those used for dental and joint replacement. The product, IONTITE, is advertised as a controlled adherent composition deposited at low temperature onto biomaterials such as stainless steel, titanium, cobalt-chromium and most polymers (Spire Corporation, Bedford, Mass. 01730).
Hydroxyapatite has received considerable attention as a coating on bone implant devices because of its chemical similarity to the mineral component of bone. In cell adhesion studies, Sato, et al. (2005) showed enhanced osteoblast adhesion on hydrothermally treated hydroxyapatite/titania/poly(lactide-co-glycolide) sol-gel titanium coatings. Other workers have suggested that nanophase metals, certain polymers and HA, may stimulate osteoblast interactions, although only nanophase metal surfaces were studied and found to increase osteoblast adhesion (Webster, et al., 2004).
Surface roughness is recognized as an important factor in strengthening adhesion of surface coatings, not only for protective coatings on implant surfaces, but also for more adherent cell attracting interfaces. Hayashi, et al. (2006) reported that hydroxyapatite coated on TiV surfaces of different roughness showed no difference in bone-implant interface shear strength, whereas bead coated porous TiV exhibited significantly greater resistance to shear. The failure site on the tested HA coated implants was at the coating-substrate interface.
Balasundaram, et al. (2006) suggest that osteoblast adhesion is promoted by decreasing particle size and crystallinity on hydroxyapatite surfaces as well as on hydroxyapatite surfaces functionalized with the tripeptide sequence arginine-glycine-aspartic acid (RGD). According to the authors, grain size on hydroxyapatite and other calcium phosphate materials appears to strongly influence osteoblast adhesion.
While some studies on HA coated Ti suggested that HA should be coated on rough surfaces to avoid failure at the substrate interface, HA spray coated on Ti exhibited many failed regions in vivo either at the HA-bone interface or within the bone tissue, despite some improvement in adhesion compared with uncoated Ti (Nakashima, et al., 1997)
Clearly, there is recognition that improvements need to be made in developing coatings on medically important surfaces such as Ti. Of particular importance are coatings which do not slough in the body and which have superior osseointegration properties. Despite progress in modifying metal surfaces to improve tissue and cell adhesion on hydroxyapatite surfaces, adequate adhesion of HA coatings on titanium substrates remains a challenge. Unfortunately, flat and continuous HA or calcium phosphate coatings tend to fail by fracture or delamination at the interface between the implant and the bone.
The present invention pertains to nanoparticulate hydroxyapatite (HA) coatings on nanostructured surfaces, and particularly to nanoparticulate HA coated nanotubular titanium surfaces. The HA coating is strongly adhered to the Ti surface. Anchorage-dependent cells, including osteoblasts, exhibit enhanced adhesion to the nanoparticulate HA compared to microparticulate HA surfaces, thus effectively promoting accumulation of calcium-containing minerals required for new bone formation from the extracellular matrix.
The described nanoparticulate HA surface coatings exhibit at least two notable features that distinguish them from HA coatings that have been described as “nano-sized”. Importantly, the disclosed method provides HA coatings that strongly adhere to a nanotubular Ti surface. The HA does not slough in media at a pH near that found in vivo; in contrast, HA coatings deposited on conventional smooth Ti surfaces quickly slough from the substrate surface during in vitro incubation tests and in in vivo tests.
Additionally, as demonstrated in the examples reported herein, the nanoparticulate HA coating is deposited by a molecular plasma deposition process and cured, not sintered, thereby preserving the nanoparticulate features of the HA coating. This provides a surface to which cells such as osteoblasts readily attach. These features promote strong coating adherence and attraction for bone-forming cells.
Once a nanoparticulate HA surface is deposited on the nanotubular Ti surface, a curing step is used which bonds the HA without loss of its nanostructural features. Others have described HA coatings on substrates as “nano-sized” after a sintering step. However, sintering is typically a high heat process and will convert any originally present nanoparticulate HA to micron-sized particles as a result of the bonding and atomic diffusion processes induced by the heat. The curing process used in the process described herein is not a sintering process. The molecular plasma deposited HA is heated well below its melting temperature in the range of only a few hundred degrees, generally no higher than 500° C. and preferably at 200° C. Nanoparticle size is maintained and bonding of the HA to the nanotubular Ti surface is significantly enhanced, resulting in strong adhesion of the coating to the Ti.
The nanotubes on the anodized Ti surface have open ends, which can be filled with deposited nanoparticulate HA. The deposited HA adheres to the inner surface and/or outer surface of the nanotubes to a greater or lesser extent depending on the deposition conditions. Thus the coating is deposited not only on the nanotube surface, but also inside the tubes, thereby filling the tubes, which is believed to contribute to strong adhesion.
Titanium nanotube surface characteristics can be modified by adjusting anodization parameters during the surface treatment of titanium substrates. Nanotube diameter can be controlled by changing the electrolytic solution composition, time of anodization, and temperature at which the anodization is conducted. Larger diameter nanotubes will accommodate larger deposited particulate coatings. Pore diameters ranging from 20 to 500 nm with varying wall thicknesses are readily synthesized, making it possible to load larger particles into the nanotubes. In a preferred embodiment, a pore diameter of about 70 nm results in more deposition of nanoparticulate HA than in the 120 nm pore diameter nanotubes.
Nanotube length (height) can also be controlled so that the titanium nanotube surface is relatively uniform. Uniformity provides a more level surface on which depth of deposited biomolecule layers can be better controlled.
While the invention has been illustrated with a surface-modified (nanotubular) Ti substrate, it is believed that a nanotubular surface can be created on titanium-based substrates; e.g. nickel/titanium, and various titanium compositions with molybdenum, zirconium, niobium, aluminum, iron, vanadium, and tantalum. Several of these alloys are currently used in the fabrication of medical implant devices.
Nanoparticulate HA is deposited by a molecular plasma deposition (MPD) process onto a nanostructured nanotubular titanium surface. The MPD process results in clumps of HA, which are not evenly distributed over the surface. Using a low temperature curing in the range of 200° C., the HA surface becomes relatively even, while still retaining nanoparticulate features and hydroxyapatite crystalline phase. Higher temperatures, e.g, sintering, convert the deposited nanoparticles to micron-sized particles, which have less surface area and changes in the hydroxyapatite crystalline phase. Importantly, the cured nanoparticulate HA is highly adherent to the nanotubular Ti surface so that even after several hours incubation in an aqueous buffer at physiological pH, the HA coating remains intact.
The described nano HA coated nanotubular titanium surfaces promote cell adhesion to a greater extent than to nanotubular titanium surfaces without the HA coating. The greater density and adherence of osteoblast cells to the nanoparticulate HA surfaces provides a significant advantage over currently used coatings in orthopaedic implants.
Sintering is understood to be the process of heating at a temperature below the melting point of the main constituent for the purpose of increasing strength through bonding together of the particles. Sintering strengthens a powder mass and normally produces densification and, in powdered metals, recrystallization. Atomic diffusion occurs so that welded areas formed during compaction grow until they may be lost completely. Sintering of HA is generally conducted at temperatures near 1000° C., which is close to the melting point.
Curing is the heating of a material, particularly as used herein with respect to hydroxyapatite, to a temperature that does not induce recrystallization and does not change particulate size. The temperature employed to cure hydroxyapatite is in the range of 100-500° C., which is well below the melting and sintering temperatures.
The present invention provides stable nanoparticulate hydroxyapatite coatings on nanostructured titanium surfaces, which are particularly suitable as coatings on implants where bone growth is required. The deposited nanoparticulate HA closely mimics normal bone structure so that osteoblast growth and proliferation on the coating scaffold is enhanced compared to osteoblast adhesion on metal or polymer surfaces.
While titanium and its alloys are widely used in orthopedic and dental applications, the titanium oxide surface that forms when the metal is exposed to air is not sufficiently bioactive to bond with bone. It has been found that increased osteoblast adhesion occurs on nanoparticulate HA deposited on electrochemically anodized titanium surfaces. Unanodized titanium surfaces, in contrast, are poor substrates for coating materials and exhibit little, if any, tendency to attract cells.
By using selected anodization conditions, nanotubes can be created on a titanium metal surface, thereby mimicking features of natural bone. Type I collagen is the main organic component of bone, exhibiting a triple helix 300 nm in length, 0.5 nm in width and a periodicity of 67 nm. All type I collagen dimensions and inorganic bone components are compatible with the dimensional aspects of the nanostructured titanium surface. Hydroxyapatite (HA) and other calcium phosphates have particle sizes approximately 20-40 nm in length. HA crystals are patterned anisotropically within the collagen network in the long bones of the body. It is considered desirable to develop HA coatings on metals used for orthopedic implants because such natural coatings are expected to enhance bone formation.
The nanotube titanium surface produced under the described anodization conditions is more compatible with natural bone than the micropatterned surfaces commonly found on orthopedic implants. Both length and nanotube diameter can be changed to accommodate desired deposited materials, such as the different types of collagen, hydroxyapatite and other calcium phosphate based compounds, whether natural or synthetic, that may be suitable for enhancing osteoblast adhesion and bone growth. Modifications in the diameter and length of the nanotubes formed on Ti surfaces by etching processes can be made so that pore diameter can range from about 30 to over 500 nm (Grimes, 2006). Pore size and other characteristics of an anodized titanium surface are controlled by electrolyte composition, pH and length of time the anodization process is carried out.
Osteoblast cells adhering to the appropriate matrix will promote bone formation by attracting bone forming cells in vivo; i.e., osteoblasts, osteoclasts and osteocytes. As shown herein, nanoHA coated nanotubular Ti surfaces exhibit excellent cell-attracting characteristics. Cell densities of osteoblasts deposited in vitro from DMEM media were higher on nanoparticulate HA coated nanotubular Ti than on microparticulate HA coated Ti, nanotubular Ti or on conventional smooth Ti surfaces.
The following examples are provided as illustrations of the invention and are in no way to be considered limiting.
XRD was obtained with a Siemens D500 Kristalloflex (Bruker AXD, Inc.) using Cu-Ka radiation. TEM was obtained with a JEOL 1200 EXII.
SEM measurements were made on substrates sputter-coated with a thin layer of gold using an Ernest Fullam Sputter Coater, Model AMS-76M, in a 100 mTorr vacuum in argon for 3 min at 10 mA. Images were taken using a TESCAN MIRA/LSM SEM at a 20 kV accelerating voltage. Digital images were recorded using the TESCAN-MIRA software.
When fluorescence measurements are desired, substrates can be stained using a CBQCA amine-labeling kit (Molecular Probes, Eugene, Oreg.) following manufacturer instructions and then visualized by fluorescence microscopy. CBQCA is a non-fluorescence molecule but upon reaction with amine groups in the presence of cyanide molecules, exhibits fluorescence. Images can be obtained using software interfaced with fluorescence microscopy. Osteoblasts (CRL-11372) were purchased from American Type Culture Collection; and Endothelial Cells were obtained from VEC Technologies, (Rensselaer, N.Y.).
Ti foils with a thickness of 250 μm (99.7%; Alfa Aesar) were ultrasonically cleaned with water, 2-propanol, and water for 30 minutes. The cleaned substrates were then etched with 5M nitric acid for 3 minutes and cleaned ultrasonically 3 times with deionized water for 10 minutes. The foils were subjected to potentiostatic anodization in a two-electrode electrochemical cell connected to a DC power supply. In all cases, a platinum foil (Alfa Aesar) was used as the counter electrode. All of the experiments were performed at or near room temperature. A 20 V anodizing voltage was applied for 10 minutes. Substrates were then rinsed with deionized water followed by 3 washes with 2-propanol and stored at 60° C. for 8 hours. Anodized samples were kept under desiccation until further use.
The deposition apparatus shown in
The apparatus and modifications that allow generation of a molecular plasma are such that the needle, tube, and reservoir can be disposed in a separate enclosure (not shown) that excludes air, but allows introduction of other gases or use of a partial vacuum somewhat below atmospheric pressure. Optionally selected gases include argon, oxygen, nitrogen, xenon, hydrogen, krypton, radon, chlorine, helium, ammonia, fluorine and combinations of these gases. While atmospheric pressure is generally preferred for generation of the plasma at the needle tip, reduced pressure in the separate chamber housing the needle, tube and reservoir can be up to about 100 mTorr may in some instances provide satisfactory depositions.
For use as illustrated in
To prepare nano-HA coated anodized Ti substrates, 10 ml of a colloidal solution of nanoparticulate HA was loaded into the reservoir (see
Hydroxyapatite is formed in accordance with the reaction:
10Ca(NO3)2+6(NH4)2HPO4+8NH4OH→Ca10(PO4)6(OH)2+6H2O+20NH4NO3
Nanoparticulate HA was synthesized suing a wet chemical process followed by hydrothermal treatment. Concentrated ammonium hydroxide was used to maintain the reaction mixture at pH 10 throughout the reaction. 0.6M ammonium phosphate and 1.0M calcium nitrate were also added slowly at 3.6 ml/min. Calcium phosphate precipitation occurred while stirring for 10 min at room temperature. After 10 min, suspension volume was reduced by 75% using centrifugation. The concentrated HA precipitated aqueous solution was added to a 125 ml TEFLON liner (Parr Instruments). The liner was sealed tightly in an autoclave (Parr Acid Digestion Bomb 4748) and processed hydrothermally at 120° C. for 20 hr. After hydrothermal treatment, the HA particles were rinsed 3 times with deionized water.
Nanoparticulate hydroxyapatite was characterized by X-ray diffraction (XRD), inductively coupled plasma atomic emission spectroscopy (ICP-AES) to measure Ca/P ratio, a particle size analyzer to measure the agglomerated mean particle size, BET to measure individual particle size, and Scanning Electron Microscope (SEM) to characterize particle morphology.
X-ray diffraction (XRD) showed that nanoHA powders retain nanostructural features (HA crystalline phase) after heating at 200° C. (
Micron-sized hydroxyapatite was obtained as described above except that the concentrated HA was hydrothermally digested at 200° C. in a Parr Digestion Bomb, and the precipitated paste washed with water to strip of side products and contaminants before drying in a glass Petri dish in an oven at 70° C. for 24 hr. The pellets so produced were crushed using mortar and pestle to obtain a fine powder. Micron-sized HA was obtained by drying the powder, then sintering at 1100° C. in air for 2 hr with a kiln ramp rate of 22° C./min.
In order to examine the surface characteristics of anodized Ti and HA deposited coatings on anodized Ti substrates, one or more of fluorescence, SEM, TEM and X-ray photoelectron spectroscopy (XPS) methods were used.
SEM spectra were recorded for unanodized Ti and anodized Ti surfaces. While actual measurements were not made, the diameter of the nanotubes on the anodized titanium used in the methods described was approximated at 70 nm and length at about 200 nm, based on measurements made in the past by others who have reported such measurements on anodized surfaces.
Surface roughness of anodized titanium was about 25 nm, compared with unanodized titanium, which has a roughness on the order of 5 nm. Roughness was determined by Ra values measured by SEM analysis of gold sputtered anodized substrates. A selected kV was used to obtain images of substrate topography at low and high magnification in order to observe pore geometry and surface feature size.
Surface roughness was quantified using an atomic force microscope (AFM) interfaced with imaging software. A scan rate, typically 2 Hz, was used at a selected scanning point; e.g., 512, to obtain root mean square roughness values. Scans were performed in ambient air at 15-20% humidity. 1×1 μM AFM scans were employed for plain substrates and 2×2 μM for coated substrates. Anodized Ti (
Ti samples (10×10×1 mm), 99.7% pure (Alfa Aesar), 250 um thick, were cleaned ultrasonically with ethanol and water before being etched in a mixture of HF/HNO3. The pretreated samples were anodized in 1.5% hydrofluoric acid. A DC power supply with a current density of 7 A/m2 was used. A 10V anodizing voltage was applied for 10 min. Samples were rinsed with deionized water and dried with nitrogen immediately after anodization. Prior to exposure to cell cultures, the titanium samples were ultrasonically cleaned and sterilized in 70% ethanol for 15 min, rinsed in deionized water and air dried under a laminar flow hood.
Alternatively, etching time may be carried out for minutes to hours and/or the electrolyte can be hydrofluoric acid (HF) or mixtures of HF with dimethylsulfoxide (DMSO) in various ratios. Such modifications, which are known in the art, result in nanotube structures having different tube diameters and heights.
The anodized titanium substrate surfaces were characterized by scanning electron microscopy (SEM). Prior to scanning, substrates were sputter-coated with a thin layer of gold-palladium using a Hummer I Sputter Coater (Technics) in a 100 mTorr vacuum argon environment for 3 min at 10 mA current. Images were taken using a JEOL JSM-840 Scanning Electron Microscope at 5 kV accelerating voltage. Digital images were recorded using a Digital Scan Generator Plus (JEOL) software. Substrate surfaces were characterized by scanning electron microscopy (SEM). For SEM, substrates were first sputter-coated with a thin layer of gold using an Ernest Fullam Sputter Coater (Model; AMS-76M) in a 100 mTorr vacuum argon environment for a 3 min period and 10 mA of current. Images were taken using a TESCAN-MIRA/LSM SEM at a 20 kV accelerating voltage. Digital images were recorded using the TESCAN-MIRA software.
XRD on nano-HA coated nanotubular Ti indicated that the HA single phase was maintained after deposition and heating of the coated substrates up to 500° C. SEM images of the nanoHA coating at 200° C. (
However, after curing at 900° C., the nanostructure features were lost (
Stability of the nanoHA coating on nanotubular Ti surfaces was tested by soaking in DMEM media at 37° C. for 4 hr and 24 hr. The substrates were rinsed 1× with phosphate buffer followed by 3× with deionized water and 3× with anhydrous ethanol. Coated substrates were dried under vacuum for 4 hr.
Tests showed that the HA coatings were stable for up to at least 24 hr, thereafter slowly disengaging from the surface. SEM images shown in
Transmission electron microscopy (TEM) data confirmed the nanoparticulate nature of the deposited HA coating on Ti substrates. Nanocrystalline HA particles processed hydrothermally were rod-like in appearance, exhibiting a length of 50-100 nm and diameters of 15-20 nm (
Nano-sized hydroxyapatite prepared as described was deposited on an anodized (nanotubular) titanium substrate using the molecular plasma discharge procedure described. The nano-HA was prepared as a colloidal suspension in water and ejected from a high voltage tip to form a corona discharge. The ionized material was directed through an aperture into an evacuated chamber onto a nanotubular titanium substrate that was either grounded or oppositely biased (
Anodized titanium substrates were sterilized under UV light for 4 hours prior to cell incubation. Human osteoblasts (bone-forming cells; CRL-11372 American Type Culture Collection, population numbers 5-7) in Dulbecco's Modified Eagle Medium (Gibco) supplemented with 10% fetal bovine serum (Hyclone) and 1% Penicillin/Streptomycin (Hyclone) were seeded at a density of 3500 cells/cm2 onto the substrate and were then incubated under standard cell culture conditions (humidified, 5% CO2/95% air environment, 34° C.). After 4 hr incubation, the substrates were rinsed in phosphate buffered saline to remove any non-adherent cells. The remaining cells were fixed with formaldehyde (Aldrich Chemical Inc, USA), stained with Hoescht 33258 dye (Sigma), and counted under a fluorescence microscope (Leica, DM IRB). Five random fields were counted per substrate sample. Standard t-tests were used to check statistical significance between cell adhesion numbers.
Osteoblast adhesion on anodized Ti and anodized Ti coated with nano-HA showed a wide-spread morphology compared to a smooth uncoated Ti substrate and micron-HA coated substrates. The SEM images of the cells adhering to nano-HA coated Ti showed that the cells had a wide-spread morphology with extended filapodia (
This application claims benefit of U.S. Provisional Patent Application Ser. No. 60/953,241, filed Aug. 1, 2007, which is hereby incorporated by reference herein in its entirety, including any figures, tables, nucleic acid sequences, amino acid sequences, or drawings.