Hyperplaty clays and their use in paper coating and filling, methods for making same, and paper products having improved brightness

Information

  • Patent Grant
  • 7226005
  • Patent Number
    7,226,005
  • Date Filed
    Wednesday, March 23, 2005
    19 years ago
  • Date Issued
    Tuesday, June 5, 2007
    17 years ago
Abstract
The present invention relates to a hydrous kaolin product having improved optical properties, for example, when used in the production of paper products. The present invention comprises an improved barrier coating for paper and a method of making the coated paper. The present invention also comprises an improved method from making filled and coated paper products. The present invention uses a composition comprising kaolin having a shape factor of at least about 70:1, such as at least about 80:1 or at least about 100:1.
Description
FIELD OF THE INVENTION

The present invention relates to a hydrous kaolin, which provides improved optical properties when used as a filler or coating. Also, the present invention relates to a paper coating and a coated paper product that exhibits improved properties, such as improved brightness. Further, the present invention relates to methods for preparing hydrous kaolin products.


BACKGROUND OF THE INVENTION

Particulate kaolin products find a variety of uses, including as pigments, fillers, and extenders for use in paint, plastics, polymers, papermaking and paper coating. Kaolin clay, also referred to as China Clay, or hydrous kaolin, is comprised predominantly of the mineral kaolinite, a hydrous aluminum silicate, together with small amounts of a variety of impurities.


Particulate kaolins generally exist in three forms: hydrous kaolin, calcined kaolin and chemically aggregated kaolin. Hydrous kaolin is primarily the mineral kaolinite, which has been mined and beneficiated from natural sources. Calcined kaolins are obtained by processing hydrous kaolin at high temperatures, e.g., greater than 500° C. Chemically aggregated kaolins are particle aggregates having a microstructure resembling that of calcined kaolins produced by treating hydrous kaolin with chemicals. Calcined and chemically aggregated kaolins can show benefits in certain application compositions when compared with hydrous kaolins. However, the benefits associated with calcined and chemically aggregated kaolins are not without disadvantages. The manufacturing costs of calcined and chemically aggregated kaolins are significantly higher than those of hydrous kaolins. The calcined and chemically aggregated kaolins also have the effect of improving certain paper properties while adversely effecting other properties, e.g., strength.


Kaolin has been used as an extender or pigment in paints, plastics and paper coating compositions. Kaolin pigments confer desirable physical and optical properties to such compositions. As flattening (or matting) agents, they help smooth the surfaces of the substrates to which they are applied. As opacifiers, they impart brightness, whiteness, gloss and other desirable optical properties. As extenders, they allow partial replacement of titanium dioxide and other more expensive pigments with minimal loss of whiteness or brightness.


Paper coatings are applied to sheet materials for a number of purposes including, but not limited to, increasing the gloss, smoothness, opacity and/or brightness of the material. Coatings may also be applied to hide surface irregularities or in other ways improve the surface for the acceptance of print. Paper coatings are generally prepared by forming a fluid aqueous suspension of pigment material together with a hydrophilic adhesive and other optional ingredients.


Coatings have been conventionally applied by means of a coating machine including a short dwell time coating head, which is a device in which a captive pond of coating composition under a slightly elevated pressure is held in contact with a moving paper web for a time sufficient to coat the paper before excess coating composition is removed by means of a trailing blade.


Additional advantages of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the invention. The objects and advantages of the invention will be realized and attained by means of the elements and combinations particularly pointed out in the appended claims.


It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention, as claimed.


The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate several embodiments of the invention and together with the description, serve to explain the principles of the invention.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a flowchart illustrating a process for refining a coarse fraction kaolin according to Example 1;



FIG. 2 is a flowchart illustrating a process for refining a coarse fraction kaolin according to Example 2;



FIG. 3 is a flowchart illustrating a process for refining a coarse fraction kaolin according to Example 3;



FIG. 4 is a flowchart illustrating the process for making a barrier coating pigment from a coarse fraction kaolin;



FIG. 5 is a graph illustrating brightness (y-axis) as a function of the TiO2 content (x-axis) for two paper coatings according to the present invention;



FIG. 6 is a graph illustrating sheen (y-axis) versus opacity (x-axis) of various ground U.S. clays;



FIG. 7 illustrates a plot of the d50 (y-axis) versus shape factor (x-axis) for Invention Kaolin 3 and Invention Kaolin 4 compared to two prior art kaolins;



FIG. 8 is a flowchart illustrating a process for refining a coarse fraction kaolin according to Example 10.





SUMMARY OF THE INVENTION

Generally, kaolins used in coatings and fillers are selected to have a narrow particle size distribution and high crystallinity which have been believed to provide the favored set of physical and optical properties, for example, maximum light scatter. Generally, coarse kaolin clays have been recognized as exhibiting poor light scatter. The present invention differs from the prior art in providing a coating or filling composition including a kaolin that may be rather coarse, but which nonetheless exhibits high light scatter. As a filler in, for example, unbleached kraft paper, the kaolins according to the present invention showed a light scatter similar to calcined clays without the detrimental effects on strength associated with calcined clays. The compositions according to the present invention further improve over prior compositions by making it possible to maintain sheet brightness while further reducing the amount of expensive TiO2 present in the paper coating composition.


There is disclosed a paper coating composition comprising at least one kaolin having a shape factor of at least about 70:1, a TiO2, a binder, and optionally a dispersant, and wherein the paper coating composition has a ratio of the kaolin to TiO2 of less than about 85:15 parts by weight.


There is further disclosed a method of making a coated paper comprising coating a fibrous substrate with a paper coating composition comprising a binder and at least one kaolin having a shape factor of at least about 70:1.


There is still further disclosed a method of making a filled paper comprising adding to said paper kaolin having a shape factor of at least about 70:1


There is also disclosed a coated paper comprising a fibrous substrate and a paper coating composition comprising kaolin having a shape factor of at least about 70:1.


Finally, there is disclosed a method of improving barrier properties in paper comprising coating a fibrous substrate with a coating composition comprising kaolin having a shape factor of at least about 70:1.


One aspect of the present invention provides a composition comprising kaolin having a shape factor of at least about 70:1. In other embodiments, the kaolin can have a shape factor of at least about 80:1, at least about 90:1, or at least about 100:1.


Another aspect of the present invention provides a coating composition, comprising kaolin having a shape factor of at least about 70:1, a binder; and optionally a dispersant.


Another aspect of the present invention provides a filler comprising kaolin having a shape factor of at least about 70:1.


Another aspect of the present invention provides a method of making a coated paper comprising coating a fibrous substrate with a paper coating composition comprising a carrier and kaolin having a shape factor of at least about 70:1.


Another aspect of the present invention provides a method of making a filled paper comprising providing a fibrous substrate, and adding to the substrate kaolin having a shape factor of at least about 70:1.


Another aspect of the present invention provides a coated paper comprising a fibrous substrate and a coating on the substrate comprising kaolin having a shape factor of at least about 70:1.


Another aspect of the present invention provides a method of improving barrier properties in paper comprising coating a fibrous substrate with a coating composition comprising kaolin having a shape factor of at least about 70:1.


Another aspect of the present invention provides a method of refining kaolin, comprising providing a kaolin slurry, attrition grinding the kaolin slurry, removing the coarse particle size fraction from the slurry by centrifugation, and attrition grinding the coarse-particle size fraction to provide a kaolin product having a shape factor of at least about 70:1.


Another aspect of the present invention provides an extender for paint comprising kaolin, prepared by a method comprising providing a kaolin slurry comprising whole crude kaolin or a blend of whole crude and coarse-particle size fractions from a centrifuge, attrition grinding the kaolin slurry, removing the coarse particle size fraction from the slurry by centrifugation, and attrition grinding the coarse-particle size fraction to provide a kaolin product having a shape factor of at least about 70:1.


Another aspect of the present invention provides a slurry comprising kaolin having a shape factor of greater than 70:1 and a stabilizing agent.


DETAILED DESCRIPTION

One aspect of the present invention provides a composition that is used in the production of coated or filled substrates. Another aspect of the present invention provides the coated or filled products made according to the present invention. The compositions and products according to the present invention utilize kaolin having a high shape factor to prepare a coated or filled paper exhibiting improved brightness. “Shape factor” as used herein is a measure of an average value (on a weight average basis) of the ratio of mean particle diameter to particle thickness for a population of particles of varying size and shape as measured using the electrical conductivity method and apparatus described in U.S. Pat. No. 5,128,606, which is incorporated herein by reference in its entirety. In the measurement method described in U.S. Pat. No. 5,128,606, the electrical conductivity of a fully dispersed aqueous suspension of the particles under test is caused to flow through an elongate tube. Measurements of the electrical conductivity are taken between (a) a pair of electrodes separated from one another along the longitudinal axis of the tube, and (b) a pair of electrodes separated from one another across the transverse width of the tube, and using the difference between the two conductivity measurements the shape factor of the particulate material under test is determined. “Hyperplaty” refers to hydrous kaolin clays with shape factors of greater than about 40:1. In one embodiment according to the present invention, the kaolin clays have shape factors of greater than about 70:1, for example greater than about 80:1, or greater than about 90:1. According to another aspect of the invention, the shape factor is greater than about 100:1, for example 110:1 and above. In another embodiment, the kaolin clay has a shape factor of at and above about 120:1 and at and above about 140:1. The clays according to these embodiments of the invention have been found to show surprisingly high light scatter in paper coatings and fillings.


The high shape factor may be achieved by grinding mined kaolinitic clays until the desired shape factor is achieved. Any art recognized grinding method can be used with the present invention including but not limited to, for example, wet grinding using sand or ceramic media. According to one embodiment of the present invention, the kaolin may be prepared by light comminution, e.g., grinding or milling, of a coarse kaolin to give suitable delamination thereof. The comminution may be carried out by use of beads or granules of a ceramic or plastic, e.g., nylon, grinding or milling aid. Appropriate grinding energies will be readily apparent and easily calculated by the skilled artisan. Significant grinding energies may be necessary to attain desirable high shape factors, however kaolin crude selected for its natural platyness will grind to high shape factors in an energy range typically used to manufacture standard delaminated kaolin pigments that have lesser shape factors.


Crude kaolin or a high shape factor product obtained from grinding or milling may be refined to remove impurities and improve physical properties using well known procedures generally referred to as beneficiation processes. The kaolin may be treated by a known particle size classification procedure, screening and/or centrifuging, to obtain particles having a desired particle size distribution and d50 value (as discussed below). According to one embodiment according to the present invention, mined clays are suitably first degritted before they are subjected to grinding to achieve the desired shape factor.


“Mean particle diameter” is defined as the diameter of a circle that has the same area as the largest face of the particle. The mean particle size, d50 value, and other particle size properties referred to in the present application are measured in a well known manner by sedimentation of the particulate material in a fully dispersed condition in an aqueous medium using a SEDIGRAPH 5100 machine as supplied by Micromeritics Corporation. Such a machine provides measurements and a plot of the cumulative percentage by weight of particles having a size, referred to in the art as the “equivalent spherical diameter” (esd), less than the given esd values. The mean particle size d50 is the value determined in this way of the particle esd at which there are 50% by weight of the particles, which have an esd less than that d50 value.


The value of d50 for the particulate kaolin according to the present invention may be, for example, in the range of about 0.2 μm to about 10 μm.


Previously, it was believed that coarse kaolin particles yielded pigment products having poor light scatter. The present invention's use of hyperplaty clay allows significantly coarser products to be used with comparable or better light scatter. According to one embodiment of the present invention, the particle size distribution of the kaolin may be such that about 20% or more of the particles have an esd of 2 microns or less. A suitable product according to the invention may have a particle size distribution where about 50% to about 85% of the particles have an esd of 2 microns or less.


The steepness of the particle size distribution (psd) of the particulate kaolin according to the present invention, often referred to as narrowness of the psd, refers to the slope of the psd curve. Thus, in some cases the psd of the kaolin according to the present invention may be steep and in other cases it may be broad. The steepness or broadness of the psd is one indicator of anticipated product performance and can be selected by the skilled artisan based upon desired end properties. Steepness, as used in herein, is measured as 100 times the ratio of d30 to d70, where d30 is the value of the particle esd less than which there are 30% of the particles and d70 is the value of the particle esd less than which there are 70% of the particles as obtained from the psd measure above.


Another aspect of the present invention provides a kaolin product having a shape factor value of at least about 70 formed by attrition grinding a coarse particle size kaolin fraction. Kaolin consists predominantly of kaolinite crystals, which are shaped as thin hexagonal plates or in booklets of platelets called “stacks.” Kaolinite stacks may be subjected to a grinding action to easily separate or delaminate the stacks or books comprised of more than one platelet into smaller books or individual platelets. The act of delamination parts or cleaves natural kaolinite crystals along the (001) crystallographic plane that is perpendicular to its “c-axis.” Many standard kaolin products are made by attrition grinding a dispersed slurry of blunged-degritted-brightness beneficiated blend of whole crude and coarse-particle size fraction from a centrifuge. These standard delaminated products, however, may not show sufficient delamination, as they can contain booklets that comprise several to scores of kaolinite platelets.


Accordingly, this aspect of the present invention provides a method for obtaining a kaolin having a shape factor of about 70:1 or higher. The method comprises: (a) providing a kaolin slurry, where in one embodiment, the slurry comprises a whole crude kaolin or a blend of whole crude and coarse particle kaolin from a centrifuge; (b) attrition grinding the kaolin slurry; (c) removing a coarse particle size fraction from the slurry by centrifugation; and (d) attrition grinding the coarse-particle size fraction. Optionally, a centrifugation step may be inserted prior to (b) to remove ultrafine particles in order to enhance the efficiency of attrition grinding.


In one embodiment, the kaolin product is produced by attrition grinding a crude clay slurry. The crude can comprise, in one embodiment, either a whole crude or a blend of whole crude and coarse-particle size fractions from a centrifuge. The clay slurry may be a dispersed-degritted-brightness beneficiated clay slurry.


In one embodiment, the kaolin slurry can be obtained from crude kaolin ore, which is generally a viscous, sedimentary kaolin containing micas, mixed-layered clay minerals, smectites, and vermiculites or hydrous micas. An exemplary kaolin clay crude further comprises potassium oxide in an amount ranging from 0.10% to 3.0% by weight, and magnesium oxide in an amount ranging from 0.03% to 0.5% by weight. Such crude can have a shape factor equal to or greater than 15, or equal to or greater than 25. The crude kaolin can have a particle size distribution of 75% by weight less than 2 μm.


To form the kaolin slurry, water can be added to a dry kaolin crude to form an aqueous suspension, such as a suspension containing from 30% to 70% kaolin on a dry weight basis. Chemicals can be added to disperse the clay particles. The kaolin slurry can then be degritted to remove sand-sized particles prior to further processing or transport by pipeline to a plant.


Where the crude kaolin slurry comprises a blend of whole crude and coarse-particle size fractions from a centrifuge, the coarse particle size fraction may have a shape factor of greater than 20, such as a shape factor greater than 25. In another embodiment, the coarse particle size fraction may have a shape factor of greater than 35.


The attrition grinding steps can be performed with a particulate grinding medium for a time sufficient to dissipate in the slurry or suspension enough energy to impart the kaolin particles with a shape factor value ranging from about 35 to about 60 or greater. In another embodiment, the attrition grinding the crude kaolin slurry results in kaolin having a shape factor value of at least about 60.


The amount of energy dissipated in the suspension of kaolin clay can range from about 20 kWh to about 100 kWh, such as from about 25 to about 75 kWh of energy per ton of kaolin present on a dry weight basis. The attrition grinding mill is equipped with a stirrer, which is capable of being rotated at a speed such that a vortex is formed in the suspension in the mill during grinding.


The particulate grinding medium can have a specific gravity of 2 or more. In one embodiment, the grinding medium comprises grains of quartz sand, or similar media. The grains can have a diameter of less than 2 mm. In another embodiment, the grains have a diameter of greater than 0.25 mm and less than 2 mm. In yet another embodiment, the grinding medium comprises fine (20-40#) Carbolite media.


Prior to attrition grinding the crude kaolin slurry, the slurry can be subjected to beneficiation and/or degritting processes. In one embodiment, the crude kaolin slurry comprises a dispersed-degritted-brightness beneficiated clay slurry. Degritting is the process of passing a kaolin clay slurry through drag boxes and a screen to remove coarse (grit) particles of a given size. For example, the screen can be a +325 mesh (U.S. Standard) screen suitable for removing particles larger than 45 μm.


After attrition grinding the crude slurry, the slurry can be passed through a centrifuge, such as a solid-bowl decanter centrifuge, for a classification step, where the clay is classified to a particle size distribution such that 80% to 95% by weight of the particles have an esd less than 2 μm. In one embodiment, 85% to 92% by weight of the particles have an esd less than 2 μm. In yet another embodiment, 20% to 40% of the particles have an esd less than 0.25 μm. In still another embodiment, 25% to 35% of the particles have an esd less than 0.25 μm. In still another embodiment, the weight of the particles in the finer fraction ranges from 5% to 30% of the feed to centrifuge.


After removing the coarse-particle size fraction of the attrition-ground product, i.e. the “b-fraction” via a centrifuge, the coarse-fraction can be diluted with water to form a slurry that may be subjected to an additional attrition grinding step to produce the final kaolin product having a shape factor value of at least 70. This product may alternatively subject to further beneficiation to obtain desired brightness or rheology through conventional processing techniques such as flotation, selective flocculation, and bleaching. Previously, in some instances, course fractions were discarded, as this kaolin fraction was sometimes regarded as being too coarse for coating applications. Thus, one advantage of this embodiment arises from the use of coarse fraction, which was in some cases a previously undesired manufacturing by-product, to produce a useful, kaolin product.


In one embodiment, the coarse particle size fraction comprises kaolin having a shape factor of at least about 20, such as at least about 25 or at least about 30, and in some cases as high as about 50 to about 60.


The final kaolin particles can have a mean particle size (d50 by Sedigraph) ranging from about 0.1 μm to about 2.0 μm, such as a d50 ranging from about 0.25 μm to about 1 μm.


In another embodiment the coarse particle fraction kaolin slurry is subjected to a beneficiation step and/or a degritting step, prior to the attrition grinding process. In another embodiment, the coarse particle fraction kaolin slurry is subjected to both beneficiation and degritting processes.


In one embodiment, the invention can advantageously reduce the population of kaolin crystals that exist as stacks. The kaolin product of the invention can have superior coverage relative to standard kaolin in lightweight and ultra lightweight coated paper applications, as the higher population of individual plate crystals present in hyperplaty kaolin provides a relatively thin and uniform plate thickness. In one embodiment, the invention provides a paper coated with hyperplaty kaolin, as described herein.


Another aspect of the present invention provides an extender for paints, the extender comprising a coarse particle size kaolin having a d50 ranging from about 0.25 μm to about 2.0 μm. In one embodiment, the kaolin extender has a shape factor of greater than about 90. The extender can be prepared by attrition grinding a coarse particle size kaolin fraction, as described above.


In certain applications, it may be desired to use extenders with a balance of low sheen and high opacity. Accordingly, in one embodiment, the extender is coarse, with a d50 ranging from 0.25 μm to 2.0 μm, such as a d50 ranging from 0.5 μm to 1.5 μm. For example, the d50 can be approximately 1.3 μm. In other applications, control of sheen may not be required, and therefore the kaolin can comprise finer particles with a d50 ranging from 0.25 μm to 1 μm. For example, the d50 can be approximately 0.6 μm.


Another embodiment provides a paint comprising an extender comprising a coarse particle size kaolin having a d50 ranging from 0.25 μm to 2.0 μm. In one embodiment, the kaolin extender has a shape factor of at least 70:1, or any other value described herein. In another embodiment, the kaolin extender has a shape factor of at least 100:1.


Another aspect of the present invention provides an extender for paint comprising a kaolin, prepared by a method comprising providing a kaolin slurry comprising whole crude kaolin or a blend of whole crude and coarse-particle size fractions from a centrifuge, attrition grinding the kaolin slurry, removing the coarse particle size fraction from the slurry by centrifugation, and attrition grinding the coarse-particle size fraction to provide a kaolin product having a shape factor of at least about 70:1, or any of the shape factors described herein.


Another aspect of the present invention relates to the use of the hyperplaty clay for filling, for example, paper or paperboard product, such as a supercalendered magazine paper filler product. In one embodiment, the paper or paperboard product is filled with a kaolin having a shape factor value of at least about 70.


Another aspect of the invention provides a method of making a matte paper coating, comprising: (a) attrition grinding a crude kaolin slurry comprising a blend of coarse-fractions from a centrifuge that have been degritted to 80% finer than 5 μm; (b) removing the coarse particle size fraction from the slurry by centrifugation; and (c) attrition grinding the coarse particle size fraction to provide kaolin having a shape factor of at least 70:1.


Another aspect of the invention provides a method for producing a pigment product comprising:


(a) mixing a raw or partially processed kaolin clay with water to form an aqueous suspension;


(b) attrition grinding the suspension produced by step (a) by using a particulate grinding medium by a process in which the average shape factor of the kaolin clay is increased by at least 10, preferably at least 20;


(c) separating the suspension of ground kaolin clay from the particulate grinding medium; and


(d) dewatering the suspension of ground kaolin clay separated in step (c) to recover a kaolin pigment therefrom.


In step (a) of the method according to the second aspect of the present invention, the kaolin clay may form from 20% to 70%, usually from 20% to 45% of the treated suspension. The kaolin clay can comprise a sedimentary kaolin clay, such as a sedimentary kaolin clay from Georgia, USA. The raw kaolin clay may have a psd such that not more than about 40% by weight comprises particles having an esd larger than 10 μm and not more than 50% by weight, e.g. from about 20% to about 40% by weight, comprising particles having an esd smaller than 2 μm. The shape factor of the kaolin clay treated in step (a) may be less than 15, such as in the range of from about 5 to about 10. Thus, the shape factor may be increased by a differential of at least 30, in some cases at least 40, e.g. from a shape factor value of less than 15 to a shape factor value greater than 55.


When preparing an aqueous suspension of the kaolin clay to be treated in step (a) a dispersing agent for the kaolin clay may or may not be added to the kaolin clay.


The kaolin clay employed in step (a) may be a coarse component obtained from classifying, e.g. using a centrifuge, a standard blocky sedimentary kaolin clay, such as a kaolin clay having a shape factor of from 5 to 10. The coarse component may have not more than 50% by weight of particles having an esd less than 2 μm and not more than 10% by weight having an esd less than 0.25 μm.


The psd of the kaolin clay may be adjusted by blending from 99 to 50 parts by weight of the kaolin clay with from 1 to 50 parts by weight, such as from 10 to 30 parts by weight, of a fine platy kaolin component, e.g. having a shape factor of at least 15, such as from 15 to 40 and whose percentages by weight of particles smaller than 2 μm and 0.25 μm are respectively at least 85% by weight and at least 20% by weight. The fine platy kaolin component may be a kaolin derived from either a primary or a sedimentary deposit. The fine platy kaolin component may be added to the kaolin or obtained from the coarse component prior to or after the grinding step (b). The addition may be carried out with the kaolins to be blended in either powdered, dry form or in the form of an aqueous suspension.


A resulting kaolin product prepared by blending in the manner described can improve characteristics of the kaolin, such as the rheology and dewatering characteristics of a resulting aqueous suspension, and can provide better runnability and particle alignment when the kaolin is used in a coating composition.


The kaolin clay may be subjected to one or more well known purification steps to remove undesirable impurities, e.g. between steps (a) and (b) or between steps (c) and (d). For example, the aqueous suspension of kaolin clay may be subjected to a froth flotation treatment operation to remove titanium containing impurities in the froth. Alternatively, or in addition, the suspension may be passed through a high intensity magnetic separator to remove iron containing impurities.


Step (b) may comprise a process wherein the suspension of kaolin clay is treated by medium attrition grinding wherein an energy of from about 40 kWh to about 250 kWh per tonne of clay (on a dry weight basis) is dissipated in the suspension.


The process of step (b) may comprise a process comprising at least two stages, namely a first stage (b1) wherein delamination of the kaolin clay occurs and a second stage (b2) wherein comminution of the platelets of the kaolin clay occurs.


A gentle comminution step (b1) can be performed, such as grinding via a particulate grinding medium in order to break down composite particles, which are present in the raw kaolin clay. Such composite particles generally comprise coherent stacks or blocks of individual hexagonal plate-like particles, especially where the kaolin clay is from a sedimentary deposit. When the kaolin clay is subjected to relatively gentle comminution, e.g. by grinding in step (b1), many of the composite particles can be broken down to give the individual thin, substantially hexagonal plates, i.e., delamination, the result being an increase of the average shape factor of the kaolin clay. For example, this process may increase the shape factor of the kaolin clay from a starting shape factor of about 5 to 10 to an increased shape factor of at least about 50 to 55. By “relatively gentle grinding” we mean grinding in an attrition grinding mill with a particulate grinding medium, the contents of the attrition grinding mill being agitated by means of an impeller which rotates at a speed which is insufficient to set up a vortex in the suspension, such as at a peripheral speed below about 10 m.s−1 and in which the amount of energy dissipated in the suspension during grinding is less than about 75 kWh, such as less than about 55 kWh per ton of kaolin clay on a dry weight basis. The particulate grinding medium can be of relatively high specific gravity, for example 2 or more, and may for example may comprise grains of silica sand, the grains generally having diameters not larger than about 2 mm and not smaller than about 0.25 mm.


The second stage (b2) of the two stage form of step (b) can comprise grinding in an attrition grinding mill which is equipped with a stirrer capable of being rotated at a speed such that a vortex is formed in the suspension in the mill during grinding. The particulate grinding medium can have a specific gravity of 2 or more, and can comprise, for example, grains of silica sand where the grains can have diameters not larger than about 2 mm and not smaller than about 0.25 mm. If stage (b2) is preceded by a relatively gentle comminution in stage (b1), the amount of energy dissipated in the suspension of kaolin clay in stage (b2) can be in the range of from about 40 kWh to about 120 kWh per dry ton of kaolin clay. If the relatively gentle comminution step (b1) is omitted, the amount of energy dissipated in the suspension of kaolin clay in step (b) can be in the range of from about 100 kWh to about 250 kWh per dry ton of kaolin clay.


In step (c), the suspension of ground kaolin clay can be separated from the particulate grinding medium in any manner known in the art, such by passing the suspension through a sieve of appropriate aperture size, for example a sieve having nominal aperture sizes in the range of from about 0.1 mm to about 0.25 mm.


Following step (c) or step (d) the kaolin clay may be further treated to improve one or more of its properties. For example high energy liquid working, such as by using a high speed mixer, may be applied to the product in slurry form, e.g. before step (d) or after step (d) and subsequent re-dispersion in an aqueous medium, e.g. during makedown of a coating composition.


In step (d), the suspension of ground kaolin may be dewatered in one of the ways well known in the art, e.g. filtration, centrifugation, evaporation and the like. In one embodiment, dewatering can be performed via a filter press. For example, use of a filter press may be made to form a cake having a water content in the range of from about 15% to about 35% by weight. This cake may be mixed with a dispersing agent for the kaolin clay and can be converted into a fluid slurry, which may be transported and sold in this form. Alternatively, the kaolin clay may be thermally dried, for example by introducing the fluid slurry of the kaolin clay into a spray drier and transported in a substantially dry form.


A fine platy kaolin component may be blended with the product of step (d) in the manner described earlier if such a component has not already been added prior to step (d).


In one embodiment, the pigment product may have a specific surface area as measured by the BET, N2 method of at least 12 m2.g−1, preferably from 15 m2.g−1 to 20 m2.g−1.


In one embodiment, pigment product produced in this aspect of the invention may be used in paper coating. The coating composition can be used for producing gloss coatings on paper and other substrates which composition comprises an aqueous suspension of a particulate pigment together with a hydrophilic adhesive or binder.


The solids content of the paper coating composition may be greater than 60% by weight, such as a solids content of at least 70%, or even as high as possible but still giving a suitably fluid composition which may be used in coating. The composition may include a dispersing agent, e.g. up to 2% by weight of a polyelectrolyte based on the dry weight of pigment present, or any other dispersing agent known in the art, such as those described herein. The pigment product according to the first aspect of the invention may be used as the sole pigment in a paper coating composition, or it may be used in conjunction with one or more other known pigments, such as (commercially available) kaolin, calcined kaolin, natural or precipitated calcium carbonate, titanium dioxide, calcium sulphate, satin white, talc and so called ‘plastic pigment’. In one embodiment, when a mixture of pigments is used, the pigment product according to this aspect of the invention, is present in the mixture in an amount of at least 80% of the total dry weight of the mixed pigments.


The binder of the composition may comprise an adhesive derived from natural starch obtained from a known plant source as described herein, although it is not essential to use starch as a binder ingredient. Other binders, which may be used with or without starch are also described herein.


Where starch is employed as a binder ingredient, the starch may be unmodified or raw starch, or it may be modified by one or more chemical treatments known in the art. The starch may, for example, be oxidized to convert some of its —CH2OH groups to —COOH groups. In some cases the starch may have a small proportion of acetyl, —COCH3, groups. Alternatively, the starch may be chemically treated to render it cationic or amphoteric, i.e., with both cationic and anionic charges. The starch may also be converted to a starch ether, or hydroxyalkylated starch by replacing some —OH groups with, for example, —OCH2CH2OH groups, —OCH2CH3 groups or —OCH2CH2CH2OH groups. A further class of chemically treated starches that may be used is that known as the starch phosphates. Alternatively, the raw starch may be hydrolyzed by means of a dilute acid or an enzyme to produce a gum of the dextrin type.


The starch binder used in the composition according to this aspect of the invention can be present in an amount ranging from 4% to 25% by weight, based on the dry weight of pigment. The starch binder may be used in conjunction with one or more other binders, for example synthetic binders of the latex or polyvinyl acetate or polyvinyl alcohol type. When the starch binder is used in conjunction with another binder, e.g. a synthetic binder, the amount of the starch binder can be present in an amount ranging from 2% to 20% by weight, and the amount of the synthetic binder can be present in an amount ranging from 2% to 12% by weight, both based on the weight of dry pigment. In one embodiment, at least 50% by weight of the binder mixture comprises modified or unmodified starch.


Another aspect of the present invention provides a method of forming a coated paper, comprising applying the kaolin composition to coat a sheet of paper and calendering the paper to form a gloss coating thereon. In one embodiment, the gloss coating is formed on both sides of the paper.


Another aspect of the present invention provides a method of making a coated paper comprising, coating a fibrous substrate with a paper coating composition comprising a filler comprising kaolin having a shape factor of at least about 70:1, or any of the shape factors described herein.


Another aspect of the present invention provides a coated paper comprising a fibrous substrate and a coating on the substrate comprising kaolin having a shape factor of at least about 70:1, or any of the shape factors described herein.


Another aspect of the present invention provides a method of making a filled paper comprising providing a fibrous substrate and adding to the substrate kaolin having a shape factor of at least about 70:1, or any of the shape factors described herein.


Calendering is a well known process in which paper smoothness and gloss is improved and bulk is reduced by passing a coated paper sheet between calender nips or rollers one or more times. Usually, elastomer coated rolls are employed to give pressing of high solids compositions. An elevated temperature may be applied. Five or more passes through the nips may be applied.


The paper after coating and calendering in the method according to this aspect may have a total weight per unit area ranging from 30 g.m−2 to 70 g.m−2, such as from 49 g.m−2 to 65 g.m−2, or further from 35 g.m−2 to 48 g.m−2. The final coating can have a weight per unit area ranging from 3 g.m−2 to 20 g.m−2, such as from 5 g.m−2 to 13 g.m−2. Such a coating may be applied to both sides of the paper. The coated paper may be LWC or ULWC paper. The paper gloss may be greater than 45 TAPPI units and the Parker Print Surf value at a pressure of 1 MPa of each paper coating may be less than 1 μm.


The gloss of a coated paper surface may be measured by means of a test laid down in TAPPI Standard No 480 ts-65. The intensity of light reflected at an angle from the surface of the paper is measured and compared with a standard of known gloss value. The beams of incident and reflected light are both at an angle of 75° to the normal to the paper surface. The results are expressed in TAPPI gloss units. In one embodiment, the gloss of the pigment product may be greater than 50, in some cases greater than 55, TAPPI units.


The Parker Print Surf test provides a measure of the smoothness of a paper surface, and comprises measuring the rate at which air under pressure leaks from a sample of the coated paper which is clamped, under a known standard force, between an upper plate which incorporates an outlet for the compressed air and a lower plate, the upper surface of which is covered with a sheet of either a soft or a hard reference supporting material according to the nature of the paper under test. From the rate of escape of the air, a root mean cube gap in μm between the paper surface and the reference material is calculated. A smaller value of this gap represents a higher degree of smoothness of the surface of the paper under test.


An improvement can be provided where the binder present in the coating composition comprises starch. However, an improvement is also obtained where other known starch-free binders are employed (with or without starch present). In each case the adhesive or binder may form from 4% to 30%, e.g., 8% to 20%, for example from 8% to 15% by weight of the solids content of the composition. The amount employed will depend upon the composition and the type of adhesive, which may itself incorporate one or more ingredients


The particulate kaolin according to the present invention may be mixed with other pigments, fillers and extenders to obtain a blend of properties provided by the constituents of the mixture. The added pigment, filler or extender material may comprise one or more of hydrous kaolin, calcined kaolin, aggregated kaolin, calcium carbonate (ground or precipitated) talc, gypsum or other known white particulate mineral or pigment material.


Paper coatings and paper fillers according to the present invention include, in addition to the kaolin as described above, materials generally used in the production of paper coatings and paper fillers. Specifically, the compositions will include a binder and a pigment, typically TiO2. The fillers and coatings according to the present invention may optionally include other additives, including, but not limited to, dispersants, cross linkers, water retention aids, viscosity modifiers or thickeners, lubricity or calendering aids, antifoamers/defoamers, gloss-ink hold-out additives, dry or wet rub improvement or abrasion resistance additives, dry or wet pick improvement additives, optical brightening agents or fluorescent whitening agents, dyes, biocides, leveling or evening aids, grease or oil resistance additives, water resistance additives and/or insolubilisers.


Any art recognized binder may be used in the present invention. Exemplary binders include, but are not limited to, adhesives derived from natural starch obtained from a known plant source, for example, wheat, maize, potato or tapioca; synthetic binders, including styrene butadiene, acrylic latex, vinyl acetate latex, or styrene acrylic; casein; polyvinyl alcohol; polyvinyl acetate; or mixtures thereof.


Paper coatings have very different binder levels depending upon the type of printing to be used with the coated paper product. Appropriate binder levels based upon the desired end product would be readily apparent to the skilled artisan. Binder levels are controlled to allow the surfaces to receive ink without disruption. The latex binder levels for paper coatings generally range from about 3% to about 30%. In one embodiment according to the present invention, the binder is present in the paper coating in an amount of from about 3% to about 10%. In another embodiment according to the present invention, the binder is present in the coating in an amount ranging from about 10% to about 30% by weight.


Another aspect of the present invention provides a method of making a barrier coating from a coarse fraction kaolin having the properties described herein. Barrier coatings are useful to impart to paper resistance to moisture, moisture vapor, grease, oil, air, etc.


When making barrier coatings, the amount of binder in the formulation may be very high on the order of 40% to 50%. The binder combined with the flattest possible plates result in a coating, which exhibits excellent barrier properties.


Another aspect of the present invention provides a barrier coating composition, comprising a slurry comprising kaolin having a shape factor of at least about 70:1, or any of the shape factors described herein. The solids content of the slurry can range from about 45% to about 70%.


Another aspect of the present invention provides a method of improving barrier properties in a paper comprising coating a fibrous substrate with a paper coating composition comprising a kaolin having a shape factor of at least about 70:1, or any of the shape factors described herein.


Another aspect of the present invention provides a filler comprising a kaolin having a shape factor of at least about 70:1, or any of the shape factors described herein.


Another aspect of the present invention provides a slurry comprising a kaolin having a shape factor of greater than 70:1 and a stabilizing agent. In one embodiment, the kaolin can have a shape factor of at least about 80:1, or any of the shape factors described herein.


Many stabilizing agents are known in the art for such slurries. In one embodiment, the stabilizing agent comprises carboxymethylcellulose. In another embodiment, the stabilizing agent can comprise a smectite clay. In yet another embodiment, the stabilizing agent can comprise bentonite. In still another embodiment, the stabilizing agent can comprise hectorite.


In one embodiment, the stabilizing agent is present in the slurry in an amount ranging from about 4 pounds per dry tonne kaolin to about 10 lbs per dry tonne kaolin.


In one embodiment, the slurry has a solids content of greater than about 45%, such as a solids content ranging from about 50% to about 60%.


Dispersants may be chosen from any art recognized dispersants for use in paper coating or paper filling compositions. Appropriate dispersants will be readily apparent to the skilled artisan. Dispersant may be chosen from polyelectrolytes such as polyacrylates and copolymers containing polyacrylate species, especially polyacrylate salts (such as sodium and aluminum optionally with a group II metal salt), sodium hexametaphosphates, non-ionic polyol, polyphosphoric acid, condensed sodium phosphate, non-ionic surfactants, alkanolamine and other reagents commonly used for this function.


The kaolin according to the present invention may be used as the sole pigment in the paper coatings and paper fillers of the present invention. Alternatively, the hyperplaty kaolin described above may be combined with another pigment. Additional pigments for use in the composition according to the present invention can be selected from any art recognized pigment. Pigments may be selected from other kaolin, calcined kaolin, natural or precipitated calcium carbonate, titanium dioxide, calcium sulphate, satin white, talc or other plastic pigments. According to the present invention, a pigment can be TiO2. In exemplary compositions according to the present invention, TiO2 is present in an amount ranging from 0 to 30 parts, such as from 5–20 parts or from 10–20 parts.


If cross linkers are used in the coating or filling composition for use with the present invention, crosslinkers are generally present in levels of up to 5% by weight. Any art recognized crosslinker may be used. Appropriate crosslinkers include, but are not limited to, glyoxals, melamine formaldehyde resins, ammonium zirconium carbonates and mixtures thereof.


If a water retention aid is used in the coating or filling composition for use with the present invention, water retention aids are generally present up to 2% by weight. Any art recognized water retention aid may be used. Appropriate water retention aids include, but are not limited to, sodium carboxymethyl cellulose, hydroxyethyl cellulose, PVA (polyvinyl acetate), starches, proteins, polyacrylates, gums, alginates, polyacrylamide bentonite and other commercially available products sold for such applications.


If a viscosity modifier or thickener is used in the coating or filling composition of the present invention, it is generally present in levels up to 2% by weight. Any art recognized thickener or viscosity modifier may be used. Appropriate viscosity modifiers or thickeners include, but are not limited to, polyacrylates, emulsion copolymers, dicyanamide, triols, polyoxyethylene ether, urea, sulphated castor oil, polyvinyl pyrrolidone, montmorillonite, CMC (carboxymethyl celluloses), sodium alginate, xanthan gum, sodium silicate, acrylic acid copolymers, HMC (hydroxymethyl celluoses) HEC (hydroxyethyl celluloses) and mixtures thereof.


If a lubricity/calender aid is used in the coating or filling composition of the present invention, it is generally present in levels up to 2% by weight. Any art recognized lubricity or calendering aid may be used. Appropriate lubricity or calendering aids include, but are not limited to, calcium stearate, ammonium stearate, zinc stearate, wax emulsions, waxes, alkyl ketene dimer, glycols and mixtures thereof.


If an antifoamer or defoamer is used in the coating or filling composition of the present invention, it is generally present in levels up to 1% by weight. Any art recognized antifoamer or defoamer may be used. Appropriate antifoamer and defoamers include, but are not limited to, blends of surfactants, tributyl phosphate, fatty polyoxyethylene esters plus fatty alcohols, fatty acid soaps, silicone emulsions and other silicone containing compositions, waxes and inorganic particulates in mineral oil, blends of emulsified hydrocarbons and other compounds sold commercially to carry out this function.


If dry or wet pick improvement additives are used in the coating or filling composition of the present invention, they are generally present in levels up to 2% by weight. Any art recognized dry or wet pick improvement additives may be used. Appropriate dry or wet pick improvement additives include, but are not limited to, melamine resin, polyethylene emulsions, urea formaldehyde, melamine formaldehyde, polyamide, calcium stearate, styrene maleic anhydride and mixtures thereof.


If dry or wet rub improvement and abrasion resistance additives are used in the coating or filling composition of the present invention, they are generally present in levels up to 2% by weight. Any art recognized dry or wet rub improvement and abrasion resistance additives may be used. Appropriate dry or wet rub improvement and abrasion resistance additives include, but are not limited to, glyoxal based resins, oxidized polyethylenes, melamine resins, urea formaldehyde, melamine formaldehyde, polyethylene wax, calcium stearate and mixtures thereof.


If a gloss-ink hold-out additive is used in the coating or filling composition of the present invention, it is generally present in levels up to 2% by weight. Any art recognized gloss-ink hold out additive may be used. Appropriate gloss-ink hold out additives include, but are not limited to, oxidized polyethylenes, polyethylene emulsions, waxes, casein, guar gum, CMC, HMC, calcium stearate, ammonium stearate, sodium alginate and mixtures thereof.


If optical brightening agents (OBA) and fluorescent whitening agents (FWA) are used in the coating or filling composition of the present invention, they are generally present in levels up to 1% by weight. Any art recognized optical brightening agents (OBA) and fluorescent whitening agents (FWA) may be used. Appropriate optical brightening agents (OBA) and fluorescent whitening agents (FWA) include, but are not limited to, stilbene derivatives.


If a dye is used in the coating or filling composition of the present invention, it is generally present in levels up to 0.5% by weight. Any art recognized dye may be used.


If a biocide/spoilage control agent is used in the coating or filling composition of the present invention, it is generally present in levels up to 1% by weight. Any art recognized biocide/spoilage agent may be used. Appropriate biocides/spoilage agents include, but are not limited to, metaborate, sodium dodecylbenene sulphonate, thiocyanate, organosulphur, sodium benzonate and other compounds sold commercially for this function such as the range of biocide polymers sold by Calgon Corporation.


If a leveling aid is used in the coating or filling composition of the present invention, it is generally present in levels up to 2% by weight. Any art recognized leveling aid may be used. Appropriate leveling aids include, but are not limited to, non-ionic polyol, polyethylene emulsions, fatty acid, esters and alcohol derivatives, calcium stearate and other compounds sold commercially for this function.


If a grease and oil resistance additive is used in the coating or filling composition of the present invention, it is generally present in levels up to 2% by weight. Any art recognized grease and oil resistance additive may be used. Appropriate grease and oil resistance additives include, but are not limited to, oxidized polyethylenes, latex, SMA (styrene maleic anhydride), polyamide, waxes, alginate, protein, CMC, HMC and mixtures thereof.


If a water resistance additive is used in the coating or filling composition of the present invention, it is generally present in levels up to 2% by weight. Any art recognized water resistance additive may be used. Appropriate water resistance additives include, but are not limited to, oxidized polyethylenes, ketone resin anionic latex, polyurethane, SMA, glyoxal, melamine resin, urea formaldehyde, melamine formaldehyde, polyamide, glyoxals, stearates and other materials commercially available for this function.


If an insolubilizer is used in the coating or filling composition of the present invention, it is generally present in levels up to 2% by weight. Any art recognized insolubilizer may be used.


The substrate to be filled or coated may be selected from any art recognized fibrous substrate. Substrates for use in the present invention include both wood based and woodfree substrates. Exemplary substrates according to the present invention are paper.


The present invention can be used in the production of all paper grades, from ultra lightweight coated paper to coated or filled board.


Lightweight coated, or LWC, paper is generally coated to a weight of from about 5 g.m2 to about 13 g.m2 on each side, and the total weight per unit area of the coated paper is generally in the range of from about 49 g.m2 to about 65 g.m2.


LWC paper is generally used for printing magazines, catalogues and promotional material. The coated paper is required to meet certain standards of surface gloss and smoothness. For example, the paper is generally required to have a gloss value of at least about 32, and up to about 60, TAPPI units, and a Parker Print Surf value in the range of from about 0.5 to about 1.6 μm.


Ultra lightweight coated, or ULWC, paper is sometimes otherwise known as light lightweight coated, or LLWC, paper and is used for catalogues and for advertising and promotional material sent through the mail to reduce mailing costs. The coating weight is generally in the range of from about 2 g.m−2 to about 7 g.m−2 on each side, and the total weight per unit area of the coated paper is generally in the range of from about 25 g.m−2 to about 48 g.m−2.


Methods of coating paper and other sheet materials are widely published and well known. See, for example, Pulp and Paper International, May 1994, page 18, et. seq. Sheets may be coated on the sheet forming machine, i.e., “on-machine” or they may be coated on a coating machine, i.e., “off-machine.” Any art recognized coating method may be used to produce the coated sheet according to the present invention. According to one embodiment, the coating is applied to the sheet material by an applicator, and a metering device assures that the proper level of coating composition is applied. When an excess of coating composition is applied by the applicator, the metering device is downstream of the applicator. Alternatively, the correct amount of coating composition may be applied to the applicator by the metering device, such as a film press. While coating the sheet, the sheet may be supported by backing rolls or may be subjected only to tension.


Examples of known coaters which may be used with the present invention, include, but are not limited to, air knife coaters, blade coaters, rod coaters, bar coaters, multi-head coaters, roll coaters, roll/blade coaters, case coaters, liquid application systems, reverse roll coaters, extrusion coaters, and curtain coaters.


The present invention may be used in the production of coated paper for printing. Any art recognized method of printing may be used with the coated paper according to the present invention. Appropriate printing techniques will be readily apparent to the skilled artisan. Printing techniques for use according to the present invention include, but are not limited to, rotogravure, offset printing, or flexo printing. Rotogravure involves the use of an engraved or etched cylinder as an image carrier. Image areas are etched or engraved below non-image areas in the form of tiny sunken cells. The cylinder is immersed in ink, and the excess ink is scraped off by a blade. When the substrate contacts the printing cylinder, ink transfers, forming the image. Offset printing is an indirect printing method in which the inked image on a press plate is first transferred to a rubber blanket that, in turn, “offsets” the inked impression to a press sheet.


The invention will be further clarified by the following examples, which are intended to be purely exemplary of the invention.


EXAMPLES
Example 1

This example illustrates a method of refining kaolin to produce a high shape factor kaolin, i.e., greater than or equal to 70, either as a dry kaolin or a kaolin slurry that is stabilized by adding additional water and carboxymethyl cellulose (a thickener). A “stabilized slurry” refers to a slurry where the kaolin does not appreciably settle out of solution over time. It would be expected that adding additional water would have provided a less stabilized slurry. By including a CMC (carboxymethylcellulose) thickener, a stabilized slurry is formed while decreasing the slurry solids. The stabilization process is performed as follows:


1. The product is reblunged with a small amount of dispersant, such as 35/65 Mill Chem, which is a mixture of soda ash and polyacrylate.


2. Add approximately 8 lbs/ton CMC to thicken and stabilize.


3. Add biocide to prevent bacterial interaction with the CMC.



FIG. 1 is a flowchart outlining the process of providing a high shape factor kaolin. A Georgia coarse crude kaolin is blunged, degritted, and subjected to magnetic separation. After a first attrition grinding step with sand, the product is classified to separate the coarse fraction from the fines. The coarse fraction is subjected to a second attrition grinding step, followed by leaching and filtering. A dry kaolin can be prepared by drying in a spray dryer, whereas a kaolin slurry can be prepared, such as a slurry further comprising CMC, biocide and a dispersant.
















PROCESS
COARSE FRACTION FROM
COARSE FRACTION FROM
AFTER
AFTER SPRAY


PRODUCT
1ST ATTRITION GRINDING
2ND ATTRITION GRINDING
LEACHING**
DRY



















% solids
33.6%
33.1%
51.6%
1.0%


s.g.
1.262


Tons
8.9

4.56


pH



7.3


Brightness



86


L



94.27


a



−0.2


b



2.6


TiO2



0.612


Fe2O3



0.44


Brookfield*



180


Hercules*



450


Panacea
74.7
99.8
99.9
93


PSD


  <2 m
39.3
56.9
56.5
56.0


  <1 m
23.1

36.1
36.6


 <.5 m
12.9

20.5
20.0


<.25 m
6.8

10.0
11.0


Recovery
100.0%
99.0%
98.0%
99.0%





*(60% solids)


**2 lbs/ton sodium hydrosulfite






Example 2


FIG. 2 is a flowchart outlining a process for the preparation of a high shape factor kaolin. A Georgia crude kaolin is subjected to blunging and degritting steps, followed by magnetic separation and a first attrition grinding step. The product is then classified where the coarse fraction is subjected to a second attrition grinding step, followed by another classification to obtain a product where 70% of the particles have an esd less than 2 μm. This product is then leached and filtered, followed by the formation of either a dry kaolin product or a slurry.


















COARSE FRACTION FROM




PROCESS
COARSE FRACTION FROM
2ND ATTRITION GRINDING
AFTER
AFTER SPRAY


PRODUCT
1ST ATTRITION GRINDING
& CLASSIFYING
LEACHING**
DRY



















% solids
33.6%
25.5%
52.1%
1.2%


s.g.
1.262
1.184


Tons
8.9
3.58


Brightness


87.2
87.44


L



95.17


a



−0.18


b



2.77


TiO2



0.613


Fe2O3



0.419


Brookfield*



160


Hercules*



480


Panacea
74.7

97.4
87.4


PSD


  <2 m
39.3
69.7

69.1


  <1 m
23.1


48.0


 <.5 m
12.9


28.4


<.25 m
6.8


15.0


Recovery
100.0%
57.3%
98.0%
99.0%





*(60% solids)


**2 lbs/ton sodium hydrosulfite






Example 3

This Example provides another process where a Georgia crude kaolin is reblunged and degritted, as illustrated in the flowchart of FIG. 3. After selective flocculation, the kaolin is subjected to magnetic separation. A coarse fraction from a size classification centrifuge is then added to the kaolin prior to a first attrition grinding step. After a size classification, the coarse fraction is subjected to a second attrition grinding step, followed by leaching and filtering to produce a high shape factor product.






















AFTER




PROCESS
Grinder
Grinder
Coarse
LEACH-
Spray
Bird


PRODUCT
Feed
Product
Fraction
ING**
Dry
Rejects





















% solids
32.7
32.1
29.6
43.9
96.2
54.1


Brightness
84.56
85.83
85.98
87.67
87.21
82.36


L
94.6
95.02
95.08
95.5
95.25
92.64


a
−0.2
−0.18
−0.13
−0.22
−0.19
−0.27


b
4.19
3.83
3.8
3.11
3.11
3.11


TiO2
0.613
0.635
0.652
0.639
0.63
0.666


Fe2O3
0.394
0.406
0.43
0.385
0.375
0.382


Brookfield*




1360


Hercules*




50 rpm


Panacea
51.6
87.1
87.1
85.8
87.1
57.8


PSD <2 m
48
66.3
70.9
69.3
69.7
35.8


<1 m
27.2
44.2
49.2
46.9
47.4
20.4


<.5 m
13.6
24.3
28.3
26.3
26
10.1


<.25 m
4.8
7.8
10.6
10
11.6
2.7


Recovery

99%
88.1%
98%
99%
11.9%





*(60% solids)


**5 lbs/ton sodium hydrosulfite






Example 4


FIG. 4 is a flowchart illustrating a process for making a barrier coating pigment from coarse fraction kaolin prepared according to the method of Example 1, where the barrier coating comprises kaolin having a shape factor of at least about 90:1. 5 gallons of coarse hyperplaty fraction kaolin is obtained in accordance with one of the previously described embodiments of the invention. The slurry is adjusted to have a solids content of 35%. 1 lb/ton C-211 is added, and more can be added if necessary. The batch is subjected to sand grinding to increase the percentage of particles having a size of less than 2 μm by 24% to 26%. 3600 mL sand and 1800 mL clay slip was used. In the final slurry, at least 55% of the solids had a size less than 2 μm.


The slurry was screened on a 325 mesh screen and flocculated to pH=3 with sulfuric acid. After filtering, the filter cake was 35% Sodium Polyacrylate and 65% Soda Ash) to pH=6.5. Some of the reblunged filter cake was spray dried and added back to the slip to make a slurry having a solids content of 58% to 60%, but the slurry could optionally be as low as 50% solids or even 45% solids. The table below provides size distribution and shape factor values of the final product.


















Brightness GE
85.79



PH
7.2



325 m Residue
0.0071












PSD %
<10
μm
97.2



PSD %
<5
μm
86.5



PSD %
<2
μm
56.0



PSD %
<1
μm
35.4



PSD %
<.5
μm
18



PSD %
<.25
μm
9.7



PSD %
<.1
μm
4










Visc. Brook #2 As Is
79



Visc. Herc rpm @ 18 dynes
400



Visc: Solids %
59.2



Panacea (shape factor)
92










Kaolin samples A–C were tested for grease and oil barrier properties. Samples A and B are known kaolin products whereas sample C is a kaolin product prepared in accordance with the method of Example 1. Barrier coatings were prepared as described in this Example, with these kaolin products.

















Sample A -
Sample B -
Sample C -



Comparative
Comparative
Invention





















PSD %
82.4
89.9
56.0



<2 μm



Panacea-
35
58.9
92



Shape



Factor










Barrier coatings were applied to a 60 g/m2 woodfree base sheet with a cylindrical laboratory coater. The coatings comprised the kaolin, calcium carbonate, latex, calcium stearate, and a viscosity modifier. The physical properties of the kaolins can be found in the table, above. The barrier coatings were applied twice on the same paper sample. The coated paper samples were finished on a laboratory scale calender.


The calendered paper samples were evaluated using a 3M Kit test in accordance with TAPPI procedure T559 pm-96 and for oil and grease resistance (OGR) in accordance with TAPPI procedure T509 cm-85. When using these test methods, higher values using the 3M kit are superior, while lower values when testing for oil and grease resistance are superior.


The 3M test kit was developed to determine the effectiveness of fluorochemical treated papers. The tests involve exposing the paper to a series of solution, which contain castor oil, heptane and toluene. There are 12 solutions of levels in the Kit test. As the Kit levels increase the proportion of solvent is larger.


The OGR test involves exposing the coated paper samples to a suitable oil or oil containing compound for a set period of time. The amount of oil that seeps through the coated sample and is absorbed on an underlying blotter is quantified. The test values from the OGR represent that percentage of the blotter paper covered by the oil. Thus, lower values are preferred. OGR values of 3 and less denote fully satisfactory products.
















3M Kit (Coated)
OGR













Sample No.
Flat
Creased
Flat
Creased

















Sample A
>12
<3
9
17



Sample B
>12
<3
11
21



Sample C
>12
<3
3
5










As can be seen from the table above, the sample according to the present invention provides stronger barriers when compared with prior art kaolins. Such results can be attributed to the high shape factor and large plate diameter associated with the kaolins of the present invention.


Example 5

Example 5 illustrates the utility of the inventive kaolin compositions as a component of a paper coating. Paper coating formulations were made up based upon 100 parts of pigment with 14 parts Dow 692 latex binder, 4 parts PROCOTE protein binder, 1.1 parts DISPEX polyacrylate dispersant, TiO2 and kaolin were added as indicated in the Table, below.



















Coating
A
B
C
D
E
F
G






















Pigment









Prior Art
70








Kaolin


Invention

70
85
100





Kaolin 1


Invention




70
85
100


Kaolin 2


TiO2
30
30
15

30
15



Dispex
0.1
0.1
0.1
0.1
0.1
0.1
0.1


Dow 692
14
14
14
14
14
14
14


Procote
4
4
4
4
4
4
4


pH
8.5
8.5
8.5
8.5
8.5
8.5
8.5


Brookfield


Viscosity


Spindle


#2


cps@10
156
96
128
244
60
100
384


rpm


cps@20
108
68
102
156
48
74
244


rpm


cps@50
74
60
72
102
49
63
152


rpm


cps@100
72
63
70
96
53
70
154


rpm









The kaolin properties are set forth in the Table below:

















Prior Art Kaolin
Invention Kaolin 1
Invention Kaolin 2



















Brightness
90
91
92


2 micron
91
85.6
66.7


0.5 micron
35
34.4
18.1


Shape
15
107
141


Factor


Surface
15
15.9
11.3


Area


Steepness
45
37
33









The formulations were drawn down with wire wound rods onto a basestock. The fibrous substrate was coated to a coat weight of 15 gsm. The coatings were air dried and brightness and gloss were measured using Tappi standard methods. The results are set forth in the Table below.



















Coating
A
B
C
D
E
F
G






















Pigment
15.3
15.1
15.2
15.2
15.4
15.4
15.3


Level


Brightness


ISO


Mean
65.8
69.4
64.8
54.9
68.7
66.2
57.8


St. Dev.
1.15
1.16
1.06
0.86
0.55
0.72
1.46


St. Error
0.36
0.37
0.34
0.27
0.17
0.23
0.46


N
10
10
10
10
10
10
10


Sheet


Gloss (75)


Mean
13.0
9.4
10.9
11.2
9.5
9.1
10.1


St. Dev.
1.05
0.89
0.49
0.64
1.23
0.92
1.34


St. Error
0.27
0.23
0.13
0.17
0.32
0.24
0.35


N
15
15
15
15
15
15
15









Samples according to the present invention exhibited improved brightness at accepted TiO2 levels and comparable brightness at lower TiO2 levels. See FIG. 5 which plots the brightness results noted above as a function of TiO2 content. Paper coated according to the present invention gives high brightness even with TiO2, significantly above the brightness of the uncoated sheet.


Thus, the inventive kaolin compositions are useful in applications wherein a high opacity, brightness or scattering are required, such as in brown board coating applications and may serve to reduce the amount of TiO2 required therein. Further, although the present example illustrates the utility of the inventive kaolin as a paper coating, the composition could also be used to coat other substances wherein a high brightness or opacity coating is needed.


Example 6

To test the utility of the inventive kaolins as a filler, handsheets were prepared from a unbleached natural Kraft which has undergone no refining. While the present example pertains to use as a paper filler, it is anticipated that the inventive kaolins could also be useful as a high opacity filler for plastics and like materials.


The handsheets were made with a TAPPI sheet mold at a pH of 4.5. The sheets were made on a fourdinier paper machine using unbleached hardwood kraft. The conditions are discussed in the table, below.


















pH
6.75



Freeness (CSF)
470



Freeness (CSF) after beating
380



Britt Fines



% Fiber
80.3



% Fines
18.9



% Ash
0.8



Brightness
22.7



Specific Conductivity
1750



Mutek PCD:
−340



Total Dissolved Solids
 2327 ppm



Inorganic Dissolved
 1880 ppm










The handsheets were air dried and a range of properties were measured for unfilled sheets, sheets made using the commercially available prior art pigment ASTRAPLATE (available from Imerys, Inc.) and two sets of samples using the composition identified as Invention Kaolin 2 in Example 5 above. The ASTRAPLATE and Invention 2 Samples included 2 lbs per ton of a commercially available retention aid of a sort that would be readily obtainable by one of ordinary skill in the art.

















Sample
1
2
3
4
5







Description
Unfilled
Unfilled
Prior Art
Invention
Invention





Astraplate
Kaolin 2
Kaolin 2


% Ash (450))
0.7
0.7
5.9
12.3
23.9


% Ash (900)
2.1
0.6
4.6
12.2
21.4


GSM
53.9
51.4
52.4
51.5
52.3


Sheet Brightness
19.9
20.1
22.8
29.4
38.5


Opacity
88.4
88.2
90.3
94.2
96.2


F8 Sheet Scatter
179
220
236
307
524


F8 Absorption
271.5
318.8
295.9
246.4
246.7


F10 Sheet Scatter
208
213
241
341
481


F10 Absortion
176.1
168.7
168.3
157.6
132.7


Pigment Scatter


807
1073
1557


Gurley Porosity
13.22
11.23
13.97
20.25
22.25


Burst Factor
45.4
44.6
40.2
28.6
17.2


Sheffield Smooth-
293
277
276
261
252


ness









Example 7

Filled paper was made using a bleached hardwood, softwood mixture beaten to a 400 Canadian Standard Freeness (CSF), a retention aid, and Invention Kaolin 2 of Example 5. The pH was maintained at 5.0. Handsheet were made and allowed to air dry. A range of properties were measured.
















Sample
1
2
3
4







Description
Unfilled
Invention
Invention
Invention




Kaolin 2
Kaolin 2
Kaolin 2


Retention Aid in Toms
1
1
1
1


Headbox % Ash (450))

7.62
21.12
28.13


% Retention on (450)

85
58.2
74.1


Handsheet % Ash (450)

6.48
12.29
20.84


GSM
58.6
59.2
57.5
57.4


Sheet Brightness
83.8
85.3
85.9
86.7


Opacity
73.9
79.5
83.1
87.2


Sheet Scatter
351
457
541
695


Absorption
4.9
5.8
6.3
7.1


Caliper
3.839
3.851
3.788
3.736


Bulk
1.66
1.65
1.67
1.65


Pigment Scatter

1987
1897
2002


Gurley Porosity
7.9
10.2
9.3
14.2


Sheffield Smoothness
271293
251
244
206









As can be seen from the table above, the pigment light scatter according to the present invention (1900–2000 cm2/g) compares favorably with that which can be achieved using calcined clay at 2500 and standard filler clay at 1100.


Example 8

In this example, a series of coarse fractions, i.e., “b-fraction” clays were subjected to attrition grinding to determine which clays result in high shape factor extenders while retaining particle size. The properties of the resulting materials were assessed to determine which materials provided high opacity and low sheen in a high PVC paint formulation.


Carbolite grinding experiments with fine (20–40 lbs) Carbolite grinding media were performed on four materials: (1) Invention Kaolin 3, (see column 0), having a coarse, platy character; (2) Invention Kaolin 4 from a Bird centrifuge, having a coarser, platy character (see column 0); (3) a Georgia feed clay (DBK 110 Contour 100, Imerys), a Dry Branch feed clay; and (4) a fine particle size clay (K20, Imerys), a Kaopaque 20 product that had already been processed to a fine particle size. Physical properties of the ground clay are shown in the Table, below.












Physical properties of the ground clays.









Energy
Invention Kaolin 3
Invention Kaolin 4















kwh/t
0
50
100
150
0
50
100
1560


















Colour










ISO B'ness
81.5
84.7
85.7
86.5
74.7
75.7
75.4
75.7


Yellowness
6.9
5.8
5.6
4.8
8.3
8.7
9.1
8.9


L*
94.8
95.8
96.1
96.2
92.2
92.8
92.8
92.9


a*
0.24
−0.05
0.03
−0.13
0.77
0.62
4
0.54


b*
4.54
3.88
3.64
3.22
5.57
5.89
6.12
6.01


Sedigraph


<10 μm
92.5
98.9
98.7
99.5
87.6
99.2
98.7
99


<8 μm
86.9
97.8
98.6
98.8
72.6
98.5
98.3
98.4


<5 μm
86.6
91.5
96.7
97.1
64.5
96.3
96.3
96.5


<2 μm
27.5
62.9
79.1
83.1
28.3
76.7
81
83.7


<1 μm
18
41.8
59.6
64.8
19
53.3
62.6
67


<0.75 μm
14.9
33.8
50.8
57.3
16.3
44.8
55.4
59.5


<0.50 μm
11.1
23.3
35.4
43
13.1
32.3
42.3
45.6


<0.25 μm
5.8
10.1
13.7
17.2
7
15.1
17.3
18.7


<0.10 μm
1.9
4.7
3.1
5.3
1.7
5.7
4.1
5.2


d50
2.94
1.22
0.77
0.64
3.01
0.86
0.67
0.6


Steepness*
32
30
32
31
27
30
29
31


S.F.
28.8
89
96
98.8
18.7
101
103
98.3


S.A.
7.49

13.22

9.52

13.48





*Steepness is given by d30/d70* 100. Increasing steepness indicates a narrower PSD.



S.F. = Shape factor




S.A. = Surface area



















Energy
Georgia Feed Clay
Fine Particle Size Clay















kwh/t
0
50
100
150
0
50
100
150


















Colour










ISO B'ness
81.6
84.2
84.5
85
84.4
85.8
85.8
86.3


Yellowness
7.9
6.7
6.5
6.1
6.4
5.6
5.7
5.3


L*
95.1
95.8
95.9
96
95.8
96.1
96.1
96.2


a*
0.16
0.02
0
−0.03
0.08
0.02
0.02
−0.03


b*
5.21
4.39
4.27
4
4.17
3.67
3.7
3.48


Sedigraph


<10 μm
90.4
98.5
99.6
99.2
99.6
99.9
99.8
99.3


<8 μm
86.9
98.3
99
98.8
99.2
99.9
99.9
99.4


<5 μm
78.8
97.1
98
99
95.5
99.2
99
99.3


<2 μm
55.6
84.4
87.8
93.4
79.7
91.4
92
95.2


<1 μm
42.1
65.5
69
81.2
63.9
78.5
79.5
86.1


<0.75 μm
36.1
54.9
58.7
72.8
57
72.1
72.1
80.4


<0.50 μm
27.4
39.7
43.1
56.3
45.7
59
58.4
68.2


<0.25 μm
13.4
20.54
21.3
25.7
25
32.8
31.8
39.2


<0.10 μm
5.7
9
7.4
8.8
10.4
12.6
12.8
15.9


d50
1.4
0.65
0.59
0.44
0.6
0.4
0.41
0.32


Steepness
19
31
33
38
25
31
32
35


S.F.
7.3
37.5
37.5
42
29.9
45.7
44.3
43.5





*Steepness is given by d30/d70* 100. Increasing steepness indicates a narrower PSD.



S.F. = Shape factor




S.A. = Surface area








Other Properties


Rheology


In all cases Carbolite grinding had a small but significant effect on the rheology. As the grinding energy input increased there was an increase in both the Brookfield and Rotothinner viscosities, while the high shear (cone and plate) viscosity did not change.


Scrub and Stain Resistance


As expected, scrub and stain resistances worsened as the opacity increased.


Color


The ground Invention Kaolin 3 had good color, better than the existing fine particle size clay product. Further improvements may be possible through bleaching of the ground clay.


Conclusions


The light Carbolite grinding of Invention Kaolin 3 can provide a product comprising a coarse, high shape factor clay giving a combination of low sheen with significant opacity improvements. These results reflect the performance of a small batch of material. The more highly ground Invention Kaolin 3 can have a fine high shape factor clay giving large opacity improvements, at the cost of increased sheen. Such a product may offer an alternative to calcined clays in formulations where high scrub resistance is not regarded as important.


Opacity and Sheen



FIG. 6 presents the opacity and sheen of the ground clays in the high PVC formulation. The clays were prepared by grinding with fine Carbolite media. The grinding energy is indicated by the size of each point. To allow comparison some standard clays (SUPREME and GLOMAX LL*, all of which are Imerys clay products) are plotted.


Invention Kaolin 3


The 50 kwh/t ground Invention Kaolin 3 rejects gave a noteworthy combination of high opacity and low sheen.


The 100 kwh/t ground Invention Kaolin 3 gave high opacity with high sheen.


Other Feeds


Invention Kaolin 4 had a poor color, a substantial part of their opacity originated from absorption, rather than scattering of light. They also ground to a finer particle size than Invention Kaolin 3, resulting in higher sheen.


A 1.5 unit increase in opacity was achievable by Carbolite grinding of the fine particle size clay feed material. Similar opacities were obtained with the ground Georgia Feed Clay. For these materials, any increase in opacity was always accompanied by a significant increase of the sheen, brought about by a decreasing particle size.


Chemical and mineralogical analysis of the US feed clays are provided in the Table below.












Chemical and mineralogical analysis of the clays used in Example 8.












Invention
Invention
Georgia Feed
Fine particle



Kaolin 3
Kaolin 4
Clay
size clay















XRF Analysis






SiO2
45.08
44.93
46.51
46.49


Al2O3
39.54
38.91
37.79
37.91


Fe2O3
0.29
0.61
0.33
0.44


TiO2
0.89
1.42
1.24
1.05


CaO
0.05
0.01
0.05
0.05


MgO
<.01
0.02
0.04
0.05


K2O
0.23
0.56
0.04
0.05


Na2O
0.14
0.21
0.09
0.09


L.O.I.
13.79
13.33
13.91
13.88


XRD Analysis


Kaolin
98
94
99
98


Mica
2
6
1
2


Quartz
<0.5
<0.5
0
0


Feldspar
0
0
0
0










FIG. 7 is a plot of the d50 versus shape factor. For each of the four feeds, the Carbolite grinding resulted in an increase in the clay's shape factor, and a decrease in the mean particle size. From FIG. 7, it can be seen that Invention Kaolin 3 and Invention Kaolin 4 yielded the highest shape factors. Invention Kaolin 4 suffered from poor color, with an ISO brightness of 75.7.


Example 9

The ground products of Example 8 were tested in a series of paints using a generic high PVC paint formulation, as exemplified in the Table below.












Simplified matt paint formulation.











Weight/pounds



Weight %
per US gallon















Tipure R706 TiO2
9.0
1.11



Extender
10.0
1.23



Carbital 120
30.0
3.70



Dispex N40
0.35
0.04



Calgon S
0.05
0.01



Ammonia 0.880
0.15
0.02



Natrosol 250 MBR
0.3
0.04



Nopco NXZ
0.3
0.04



Proxel GXL
0.1
0.01



Propylene Glycol
2.0
0.25



Texanol
1.4
0.17



Acronal 290D latex
13.0
1.60



Primal TT935
0.8
0.10



Water
32.55
4.02



Total =
100.00










% PVC
74.09



Specific gravity, g/cm3
 1.479



Solids wt. %
56.25



Solids vol. %
34.35










The opacity, gloss, stain resistance, BS scrub loss and mud crack resistance values are shown in the Table below.












Comparison of the Carbolite ground US clays as extenders.















159






Paint No. →
154
G.F.
160
161
162
163


Extender
Supreme
C.**
G.F.C
G.F.C
I.K.4*
I.K.4
















Work/kwh/t

50
100
150
50
100


Brookfield


viscosity,


poise


@1 r.p.m.
2960
1250
1340
1580
1160
1270


@10 r.p.m.
430
202
214
239
182
213


@100 r.p.m.
65.4
42.2
42.5
44.7
40
43.8


Rotothinner,
12.1
9.7
9.9
10
10.4
10.6


poise


Cone &
1.4
1.2
1.2
1.2
1.3
1.3


Plate, poise


Opacity @
90.3
90.1
90.2
90.8
92.7
93.0


20 m2/l


S, mm−1
78.2
76.1
76.6
80.3
90.1
92.0


K, mm−1
0.3
0.4
0.4
0.4
0.7
0.7


Gloss @ 60°
3
3.3
3.3
3.2
2.9
2.9


Gloss @ 85°
3.4
3.3
3.7
3.7
3.7
3.9


L*
96.39
96.22
96.25
96.28
95.39
95.34


a*
−0.68
−0.39
−0.38
−0.4
0.03
0.05


b*
2.21
3.38
3.37
3.24
3.78
4


Stain
83.4
80.6
79.2
80.0
72.9
73.4


resistance, %


BS scrub
5.80
6.24
6.26
6.34
8.14
8.17


loss, mg


cm−2


Mud crack
1500
1350
1350
1500
1500
1400


resistance,


μm





*I.K.4 = Invention Kaolin 4


**G.F.C = Georgia Feed Clay



BS scrub loss, 100 cycles, 7 days


























155
156
157
158


Paint No. →
164
165
F.P.
F.P.
F.P.
F.P.


Extender
I.K.3
I.K.3
S.C.*
S.C.
S.C.
S.C.





















Work/kwh/t
50
100
0
50
100
150


Brookfield


viscosity, poise


@1 r.p.m.
1220
1370
1190
1470
1520
1730


@10 r.p.m.
189
210
209
249
246
277


@100 r.p.m.
42
43.5
44.6
45.8
46
50.5


Rotothinner,
10.2
10.3
10
10.4
10.4
10.6


poise


Cone & Plate,
1.2
1.3
1.3
1.3
1.2
1.3


poise


Opacity @ 20
90.9
92.0
89.3
90.8
90.6
90.9


m2/l


S, mm−1
81.9
89.6
71.7
80.0
79.0
81.1


K, mm−1
0.3
0.3
0.4
0.4
0.4
0.4


Gloss @ 60°
3.3
3.3
3.2
3
3.3
3.1


Gloss @ 85°
2.9
3.8
2.8
3.6
3.5
3.5


L*
96.71
96.86
96.19
96.32
96.32
96.4


a*
−0.43
−0.44
−0.41
−0.42
−0.42
−0.37


b*
2.62
2.48
3.25
3.03
3.05
2.96


Stain
73.3
72.3
82.5
80.1
81.9
82.5


resistance, %


BS scrub loss†,
7.19
7.96
5.66
6.67
6.58
7.02


mg cm−2


Mud crack
1350
1500
1350
1050
1500
1150


resistance, μm






I.K.3 = Invention Kaolin 3



*F.P.S.C. = fine particle size clay






In all cases, Carbolite grinding had a small but significant effect on the rheology. As the grinding energy input increased, there was an increase in both the Brookfield and Rotothinner viscosities, while the high shear (cone and plate) viscosity did not change.


Scrub and stain resistances worsened as the opacity increased.


Invention Kaolin 3 had good color in that it is better than that of the existing fine particle size clay product.


Example 10


FIG. 8 is a flowchart outlining a process where two coarse fractions are combined, followed by leaching and filtering to produce a stabilized high-solids slurry by adding a stabilizing agent such as carboxymethlycellulose or a smecite clay (i.e. bentonite, hectorite, montmorillonite, etc.). To illustrate this, a two tote sized samples (˜250–300 gallons) of the inventive product of Example 9 were made down by blunging with a 65/35 SAPA (soda ash/sodium polyacrylate) dispersant package to a pH of 6.5. The two sample totes of the product were each treated with biocide (1 lb/dry tonne Proxel) then treated with 8 lbs/dry tonne of the carboxymethylcellulose PE-30 EX. The final solids content of Sample 1 was 52% and the final solids content of sample 2 was 49.6%. The initial Hercules viscosity of samples 1 and 2 were measured using a no. 2 spindle at 20 rpm and found to be 30 cps and 18 cps respectively. The initial Hercules viscosity of sample 1 was measured as 8.5 dynes at 4400 rpm at pH 7.2 and the initial Hercules viscosity of sample 2 was measured as 5.0 dynes at pH 7.0.


Next, the stability over time of the slurries was measured and the results are displayed in the following table. One pint samples were set aside and allowed to settle for a desired amount of time, after which the Brookfield viscosity of the top and bottom portion of each sample was measured using a ‘T’ bar at ½ rpm. If the slurry was not stable, one would expect the measured viscosity to rise over time to a maximum value of approximately 400,000.
















Sample Loc.
0 Day
14 Day
21 Day
28 Day







Sample 1 - Top
6,800
16,000
15,200
14,000


Sample 1 - Bottom
6,800
18,000
22,400
21,200


Sample 2 - Top
6,000
14,400
14,400
14,000


Sample 2 - Bottom
6,000
14,800
16,400
17,600









At the end of the 28 day test period, each one pint sample was subjected to a pour test wherein it was upended and allowed to pour for 1 minute. In this time approximately 93.4% sample 1 and 94.9% of sample 2 was seen to pour from the container, illustrating the continued fluidity of the sample. A similar test performed on each entire tote (˜250–300 gallons) of samples 1 and 2 resulted in 99.7% and 99.2% pouring respectively. As can be seen from the pour test results and the above table, the CMC stabilized slurry is basically stable, which is surprising in light of the fact that the make down process with CMC results in an effective decrease in the slurry solids. Generally this process should be useful in relation to slurries having a solids content, for example, in the range of greater than about 45%, between about 45% and about 60%, or even in the range of about 50 to about 60%.


Unless otherwise indicated, all numbers expressing quantities of ingredients, reaction conditions, and so forth used in the specification and claims are to be understood as being modified in all instances by the term “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that may vary depending upon the desired properties sought to be obtained by the present invention.


Other embodiments of the invention will be apparent to those skilled in the art from consideration of the specification. Other embodiments of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. It is intended that the specification and examples be considered as exemplary only, with a true scope and spirit of the invention being indicated by the following claims.

Claims
  • 1. A method of refining kaolin, comprising: providing a kaolin slurry;attrition grinding the kaolin slurry;removing a coarse particle size fraction from the slurry by centrifugation; andattrition grinding the coarse-particle size fraction to provide a kaolin product having a shape factor of at least about 70:1.
  • 2. The method according to claim 1, wherein the kaolin slurry comprises whole crude kaolin or a blend of whole crude and coarse-particle size fractions from a centrifuge.
  • 3. The method according to claim 1, wherein the kaolin product has a shape factor ranging from about 70:1 to about 140:1.
  • 4. The method according to claim 1, wherein the kaolin product has a shape factor ranging from about 80:1 to about 100:1.
  • 5. The method according to claim 1, wherein the kaolin slurry is beneficiated prior to the attrition grinding.
  • 6. The method according to claim 1, wherein the kaolin slurry is degritted prior to the attrition grinding.
  • 7. The method according to claim 1, wherein the kaolin slurry comprises a blunged-degritted-brightness beneficiated slurry.
  • 8. The method according to claim 1, wherein the coarse particle size fraction that is removed comprises kaolin particles comprising from 80% to 95% by weight of the particles having an esd of less than 2 μm.
  • 9. The method according to claim 1, wherein the kaolin product resulting from attrition grinding the coarse particle size fraction comprises particles having an esd ranging from 0.2 μm to 1.7 μm.
  • 10. The method according to claim 1, wherein the kaolin product resulting from attrition grinding the coarse particle size fraction comprises particles having a shape factor value ranging from 80:1 to 110:1.
  • 11. The method according to claim 1, wherein the kaolin product has a shape factor of at least about 80:1.
  • 12. The method according to claim 1, wherein the kaolin product has a shape factor of at least about 90:1.
  • 13. The method according to claim 1, wherein the kaolin product has a shape factor of at least about 100:1.
RELATED APPLICATION

This is a divisional of application Ser. No. 10/233,599, filed Sep. 4, 2002, now abandoned, which claims the benefit of priority of U.S. Provisional Application No. 60/318,207, filed Sep. 7, 2001, both of which are incorporated herein by reference.

US Referenced Citations (144)
Number Name Date Kind
2158987 Maloney May 1939 A
2414391 Peaker Jan 1947 A
2531396 Carter et al. Nov 1950 A
2883356 Gluesenkamp Apr 1959 A
3034859 Gunn et al. May 1962 A
3171718 Gunn et al. Mar 1965 A
3291769 Woodford et al. Dec 1966 A
3463350 Unger Aug 1969 A
3526768 Rai et al. Sep 1970 A
3615806 Torock et al. Oct 1971 A
3635662 Lyons Jan 1972 A
3663260 Poppe et al. May 1972 A
3790402 Eastes Feb 1974 A
3798044 Whitley et al. Mar 1974 A
4082880 Zboril Apr 1978 A
4102974 Boni Jul 1978 A
4125411 Lyons Nov 1978 A
4176148 Magder et al. Nov 1979 A
4183991 Smiley et al. Jan 1980 A
4198333 von Bonin et al. Apr 1980 A
4221697 Osborn et al. Sep 1980 A
4225496 Columbus et al. Sep 1980 A
4227920 Chapman et al. Oct 1980 A
4233199 Abolins et al. Nov 1980 A
4234469 Ohta et al. Nov 1980 A
4241142 Kaliski et al. Dec 1980 A
4243574 Manwiller Jan 1981 A
4250077 von Bonin et al. Feb 1981 A
4251576 Osborn et al. Feb 1981 A
4298711 Moulson et al. Nov 1981 A
4311635 Pearson Jan 1982 A
4359497 Madger et al. Nov 1982 A
4381948 McConnell et al. May 1983 A
4409344 Moulson et al. Oct 1983 A
4414352 Cohen et al. Nov 1983 A
4427450 Kostansek Jan 1984 A
4467057 Dieck et al. Aug 1984 A
4528235 Sacks et al. Jul 1985 A
4543287 Briggs et al. Sep 1985 A
4546126 Breitenfellner et al. Oct 1985 A
4582866 Shain Apr 1986 A
4584333 Prigent et al. Apr 1986 A
4708975 Shain Nov 1987 A
4728478 Sacks et al. Mar 1988 A
4795776 Milner Jan 1989 A
4800103 Jeffs Jan 1989 A
4820761 Saito et al. Apr 1989 A
4873116 Ancker Oct 1989 A
4888315 Bowman et al. Dec 1989 A
4918127 Adur et al. Apr 1990 A
4943324 Bundy et al. Jul 1990 A
4966638 Mudgett Oct 1990 A
4981521 Bettacchi et al. Jan 1991 A
5085707 Bundy et al. Feb 1992 A
5104925 Honda et al. Apr 1992 A
5109051 Kroenke et al. Apr 1992 A
5112782 Brown et al. May 1992 A
5128606 Gate et al. Jul 1992 A
5153039 Porter et al. Oct 1992 A
5167707 Freeman et al. Dec 1992 A
5168083 Matthews et al. Dec 1992 A
5169443 Willis et al. Dec 1992 A
5214091 Tanaka et al. May 1993 A
5234763 Rosen Aug 1993 A
5294654 Hellstern-Burnell et al. Mar 1994 A
5302404 Rissanen et al. Apr 1994 A
5332493 Ginn et al. Jul 1994 A
5364899 Watanabe et al. Nov 1994 A
5411587 Willis et al. May 1995 A
5416151 Tanaka May 1995 A
5439558 Bergmann et al. Aug 1995 A
5454865 Ginn et al. Oct 1995 A
5516829 Davis et al. May 1996 A
5522924 Smith et al. Jun 1996 A
5573946 Haxell et al. Nov 1996 A
5578659 Anada et al. Nov 1996 A
5593490 Etheridge et al. Jan 1997 A
5624488 Forbus et al. Apr 1997 A
5635279 Ma et al. Jun 1997 A
5645635 Behl et al. Jul 1997 A
5665183 Kresge et al. Sep 1997 A
5685900 Yuan et al. Nov 1997 A
5695608 Yagi et al. Dec 1997 A
5700560 Kotani et al. Dec 1997 A
5707912 Lowe et al. Jan 1998 A
5735946 Bloodworth et al. Apr 1998 A
5749958 Behl et al. May 1998 A
5810998 Arrington-Webb et al. Sep 1998 A
5846309 Freeman et al. Dec 1998 A
5879512 McGenity et al. Mar 1999 A
5883173 Elspass et al. Mar 1999 A
5897411 Stark et al. Apr 1999 A
5925454 Bekele Jul 1999 A
5948156 Coutelle et al. Sep 1999 A
5952093 Nichols et al. Sep 1999 A
6031036 Rosenquist et al. Feb 2000 A
6087016 Feeney et al. Jul 2000 A
6117541 Frisk Sep 2000 A
6149723 Pruett et al. Nov 2000 A
6186335 Arrington-Webb et al. Feb 2001 B1
6193831 Overcash et al. Feb 2001 B1
6232389 Feeney et al. May 2001 B1
6238793 Takahashi et al. May 2001 B1
6245395 Falat et al. Jun 2001 B1
6262161 Betso et al. Jul 2001 B1
RE37385 Okada et al. Sep 2001 E
6312511 Billimoria et al. Nov 2001 B1
6358576 Adur et al. Mar 2002 B1
6402826 Yuan et al. Jun 2002 B1
6416817 Rangwalla et al. Jul 2002 B1
6447845 Nanavati et al. Sep 2002 B1
6447860 Mueller et al. Sep 2002 B1
6465064 Branch Oct 2002 B1
6531196 Aho et al. Mar 2003 B1
6537363 Golley et al. Mar 2003 B1
6545079 Nurmi et al. Apr 2003 B1
6554892 Manasso et al. Apr 2003 B1
6564199 Pruett et al. May 2003 B1
6610137 Golley et al. Aug 2003 B2
6616749 Husband et al. Sep 2003 B1
6623866 Migliorini et al. Sep 2003 B2
6632868 Qian et al. Oct 2003 B2
6758895 Wesley Jul 2004 B2
6759463 Lorah et al. Jul 2004 B2
6790896 Chaiko Sep 2004 B2
6794042 Merlin et al. Sep 2004 B1
6808559 Golley et al. Oct 2004 B2
6814796 Husband et al. Nov 2004 B2
6838507 Chou et al. Jan 2005 B2
6841211 Knoll et al. Jan 2005 B1
6864110 Summers et al. Mar 2005 B2
6884450 Wu et al. Apr 2005 B2
6887302 Rajagopalan et al. May 2005 B2
6914095 Lorah et al. Jul 2005 B2
6942897 Joyce et al. Sep 2005 B2
20030187120 Chaiko et al. Oct 2003 A1
20040033379 Grunlan et al. Feb 2004 A1
20040161594 Joyce et al. Aug 2004 A1
20040241475 Morabito Dec 2004 A1
20040250973 John et al. Dec 2004 A1
20050145138 Raju et al. Jul 2005 A1
20050171243 Hemmings et al. Aug 2005 A1
20050228096 Kirsten et al. Oct 2005 A1
20050228104 Feeney et al. Oct 2005 A1
Foreign Referenced Citations (180)
Number Date Country
2 089 613 Sep 1993 CA
2 467 284 Nov 2004 CA
2 241 577 Mar 1973 DE
24 49 656 Dec 1975 DE
26 58 814 Jan 1978 DE
28 18 954 Nov 1978 DE
27 39 620 Mar 1979 DE
30 12 235 Oct 1980 DE
30 47 269 Jul 1982 DE
34 66 547 Apr 1987 DE
35 65 272 Apr 1987 DE
36 32 606 Apr 1987 DE
35 36 371 May 1987 DE
35 40 524 May 1987 DE
37 50 864 Apr 1988 DE
38 84 605 Aug 1988 DE
36 79 147 Jun 1991 DE
43 01 730 Jul 1993 DE
42 13 746 Oct 1993 DE
36 89 760 May 1994 DE
100 10 941 Sep 2001 DE
0 001 066 Apr 1980 EP
0 026 075 Apr 1981 EP
0 054 424 Jun 1982 EP
0 132 094 Jan 1985 EP
0 132 228 Jan 1985 EP
0 160 777 Nov 1985 EP
0 163 427 Dec 1985 EP
0 217 626 Apr 1987 EP
0 222 138 May 1987 EP
0 222 298 May 1987 EP
0 239 986 Oct 1987 EP
0 245 553 Nov 1987 EP
0 262 649 Apr 1988 EP
0 274 888 Jul 1988 EP
0 341 981 Nov 1989 EP
0 352 714 Jan 1990 EP
0 456 363 Nov 1991 EP
0 204 324 Feb 1992 EP
0 475 434 Mar 1992 EP
0 524 635 Jan 1993 EP
0 528 078 Feb 1993 EP
0 543 793 May 1993 EP
0 586 904 Mar 1994 EP
0 588 239 Mar 1994 EP
0 589 461 Mar 1994 EP
0 596 442 May 1994 EP
0 494 594 Oct 1995 EP
0 691 375 Jan 1996 EP
0 764 739 Mar 1997 EP
0 804 505 Nov 1997 EP
0 824 130 Feb 1998 EP
0 991 530 Apr 2000 EP
0 991 815 Apr 2000 EP
1 088 852 Apr 2001 EP
1 245 730 Oct 2002 EP
1 484 176 Dec 2004 EP
1 512 552 Mar 2005 EP
1 299 089 Jul 1962 FR
2 150 953 Apr 1973 FR
2 273 040 Dec 1975 FR
2 359 645 Feb 1978 FR
2 359 874 Feb 1978 FR
2 389 645 Dec 1978 FR
2 452 511 Oct 1980 FR
2 558 168 Jul 1985 FR
2 774 689 Aug 1999 FR
2 822 086 Sep 2002 FR
819 050 Aug 1959 GB
1032536 Jun 1966 GB
1 100 496 Jan 1968 GB
1 101 950 Feb 1968 GB
1118723 Jul 1968 GB
1 136 350 Dec 1968 GB
1 241 177 Jul 1971 GB
1 310 933 Mar 1973 GB
1375057 Nov 1974 GB
1469028 Mar 1977 GB
1493393 Nov 1977 GB
1 496 088 Dec 1977 GB
1513657 Jun 1978 GB
1597213 Sep 1981 GB
2223758 Jan 1990 GB
240398 Jul 1991 GB
2 306 392 May 1997 GB
2310215 Aug 1997 GB
51005383 Jan 1976 JP
53016063 Feb 1978 JP
54010394 Jan 1979 JP
54047751 Apr 1979 JP
55 129439 Oct 1980 JP
55131024 Oct 1980 JP
5907 4152 Apr 1984 JP
6008 4364 Jan 1985 JP
6002 3488 Feb 1985 JP
6003 8455 Feb 1985 JP
6023 1443 Aug 1985 JP
6023 5858 Nov 1985 JP
06211 6667 May 1987 JP
6223 2452 Oct 1987 JP
6313 2964 Jun 1988 JP
6317 5047 Jul 1988 JP
0201 8362 Jan 1990 JP
0203 4653 Feb 1990 JP
0204 5551 Feb 1990 JP
0412 2752 Apr 1992 JP
4 270650 Sep 1992 JP
0526 2974 Oct 1993 JP
0601 6918 Jan 1994 JP
0606 5490 Mar 1994 JP
06502684 Mar 1994 JP
0614 5442 May 1994 JP
07502068 Mar 1995 JP
07 251486 Oct 1995 JP
0801 2886 Jan 1996 JP
08022945 Jan 1996 JP
09 111696 Apr 1997 JP
10114854 May 1998 JP
10 298358 Nov 1998 JP
11 129379 May 1999 JP
11 129381 May 1999 JP
2000 265391 Sep 2000 JP
2000 303386 Oct 2000 JP
2000 345032 Dec 2000 JP
2001 020200 Jan 2001 JP
2001 098149 Apr 2001 JP
2002 363885 Dec 2002 JP
2003 192861 Jul 2003 JP
2003 292678 Oct 2003 JP
2004 003118 Jan 2004 JP
2004 034390 Feb 2004 JP
77224 Aug 1983 PT
WO 8001167 Jun 1980 WO
WO 8002430 Oct 1980 WO
WO 9011605 Oct 1980 WO
WO 9732934 Sep 1987 WO
WO 8805804 Aug 1988 WO
WO 9304119 Mar 1993 WO
WO 9407956 Apr 1994 WO
WO 9615321 May 1996 WO
WO 9622329 Jul 1996 WO
WO 9700910 Jan 1997 WO
WO 9734956 Sep 1997 WO
WO 9837152 Aug 1998 WO
WO 9823831 Dec 1998 WO
WO 9854409 Dec 1998 WO
WO 9854410 Dec 1998 WO
WO 9856598 Dec 1998 WO
WO 9856860 Dec 1998 WO
WO 9858613 Dec 1998 WO
WO 9901504 Jan 1999 WO
WO 9941309 Aug 1999 WO
WO 9943747 Sep 1999 WO
WO 9951815 Oct 1999 WO
WO 9958613 Nov 1999 WO
WO 0005311 Feb 2000 WO
WO 0059840 Oct 2000 WO
WO 0059841 Oct 2000 WO
WO 0066657 Nov 2000 WO
WO 0076862 Dec 2000 WO
WO 0078540 Dec 2000 WO
WO 0112708 Feb 2001 WO
WO 0146307 Jun 2001 WO
WO 0153159 Jul 2001 WO
WO 0159215 Aug 2001 WO
WO 0166627 Sep 2001 WO
WO 0166635 Sep 2001 WO
WO 0166655 Sep 2001 WO
WO 0187580 Nov 2001 WO
WO 0187596 Nov 2001 WO
WO 0216509 Feb 2002 WO
WO 03039228 May 2003 WO
WO 2004046463 Jun 2004 WO
WO 2004074574 Sep 2004 WO
WO 2005013704 Feb 2005 WO
WO 2005014283 Feb 2005 WO
WO 2005044938 May 2005 WO
WO 2005047372 May 2005 WO
WO 2005061608 Jul 2005 WO
WO 2005108222 Nov 2005 WO
Related Publications (2)
Number Date Country
20050178292 A1 Aug 2005 US
20060032405 A2 Feb 2006 US
Provisional Applications (1)
Number Date Country
60318207 Sep 2001 US
Divisions (1)
Number Date Country
Parent 10233599 Sep 2002 US
Child 11086563 US