The present invention relates to a III-nitride light emitting diode (LED) and a manufacturing method thereof. More particularly, the present invention relates to the structure and manufacturing method of III-nitride LED for activating the p-type III-nitride semiconductor material by using the heating method induced by electromagnetic wave.
Nowadays, because LED has advantages of low manufacturing cost, low manufacturing difficulty level, easy and convenient installation and promising development future, LED is used widely in daily life, such as electronic bulletin boards, indicator lights and car taillights, etc.
In the epitaxial process, the p-type nitride semiconductor material of the III-nitride LED is first sufficiently doped, but most of the dopants are passivated by hydrogen. Hence, an additional activation-annealing step has to be performed in the process of manufacturing the III-nitride LED after the LED structure is formed, thereby increasing the doping concentration of the nitride semiconductor material. Generally, the activation-annealing step is performed by a heating method using a furnace or microwave oven, wherein the LED is put in a proper high temperature condition, and then the atoms in the material will be processed the rearrangement of crystal lattice after a certain period of time, so that the contact resistance between the semiconductor and the metal electrode is reduced.
With the conventional method performing the activation-annealing step by using a furnace or a microwave oven, the equipment cost is increased tremendously. Therefore, the present invention provides an activation-annealing step with an equipment of simple structure so as to reduce the cost of manufacturing III-nitride LED, and also to decrease the contact resistance between the semiconductor material and metal electrode.
According to the present invention, the structure of III-nitride LED comprises: a substrate; an epitaxial structure having a plurality of III-nitride compound semiconductor layers used for generating light when current enters, wherein one side of the epitaxial structure is connected to one side of the substrate, and a first ohmic contact metal electrode is located on another side of the epitaxial structure; and a magnetic metal layer for performing a heating step induced by electromagnetic wave to activate the III-nitride compound semiconductor layers.
The aforementioned magnetic metal layer is composed of the material selected from the group consisting of Fe, Co and alloy thereof. In the preferred embodiment, the aforementioned epitaxial structure includes, sequentially from the bottom to the top: a buffer layer; a semiconductor layer having a first electrical property; a first confining layer having the first electrical property; an active layer; a second confining layer having a second electrical property; and a contact layer having a second electrical property. In addition, the epitaxial structure further comprises a trench exposing a portion of a surface of the semiconductor layer, and a second ohmic contact metal electrode located on the portion of the surface of the semiconductor layer.
The present invention, the III-nitride LED and the method for making the same, has advantages of providing the equipments of simple structure and low cost, and simultaneously achieving the objects of both activating the III-nitride compound semiconductor material and reducing the contact resistance between the semiconductors and electrodes.
The above features of the present invention will be more clearly understood from consideration of the following descriptions in connection with accompanying drawings in which:
a illustrates a top view of a structure of III-nitride LED, according to the present invention;
b illustrates a cross-sectional view of a structure of III-nitride LED along the A-A′ line in the
The conventional method activates the semiconductor material layers by heating with a furnace or a microwave oven, and the equipment cost is increased therefore. The present invention provides a simple method to activate the p-type semiconductor material and reduce the contact resistance between the semiconductor and the metal electrode meanwhile. The present invention activates the p-type semiconductor material in the III-nitride LED by the electromagnetic wave inducing method, the method generating heat by eddy current.
In the following description, the present invention is stated with preferred embodiments.
Then, the epitaxial structure is etched or polished by using the method of dry etching, wet etching or mechanical cutting and polishing, in order to form a trench 66 exposing a portion of a surface of the semiconductor layer 56 having the first electrical property. Further, by using the method of the thermal evaporation, e-beam evaporation, or ion sputtering, a transparent electrode 68 having a second electrical property and a metal electrode pad 72 having the second electrical property are formed in the epitaxial structure 52, and a metal electrode pad 70 having the first electrical property is formed on the portion of the exposed surface of the semiconductor layer 56 having the first electrical property, wherein the first electrical property can be p-type or n-type, and the second electrical property is opposite to the first electrical property.
Then, a magnetic metal layer 74 composed of Fe, Co or alloy thereof, such as FeCoV or FeNi, is formed on another side of the substrate 50 by using the method of thermal evaporation, e-beam evaporation, ion sputtering, or electroplate, wherein the magnetic metal layer composed of Fe, Co, and FeCo alloy is preferred. The LED having the aforementioned structure is put onto electromagnetic oven which generates heat by the electromagnetic inducing way, so that, as a result of eddy current of magnetic metal layer 74, the p-type nitride semiconductor material is activated. Meanwhile, the metal electrode and the nitride semiconductor are annealed to reduce the contact resistance.
The principle of producing eddy current by electromagnetic inducement is described as follows: if a magnet is placed in opposite to a coin and is moved in parallel with the coin, the current of eddy pattern will be induced on the coin, and the current of eddy pattern is induced from the electromagnetic inducement. The magnetic flux of a surface from which the coin faces the magnet is changed due to the movement of magnet, and the current having concentric circles pattern is induced. The current, which has the shape of eddy, is named eddy current. Especially when the alternating current (AC) is used, the current alternates quickly. Thus, when a conductor is put on the alternating magnetic field, the magnetic flux passing on the conductor is also alternated quickly, so that it the eddy current is induced more apparently. The electromagnetic oven may use the internal electromagnetic coil to produce an alternating magnetic field, and the alternating magnetic field can make magnetic material generate the eddy current, and as a result, joule heat is generated to heat the magnetic material.
The characteristic of the present invention is to form a magnetic metal layer 74 on the structure of the III-nitride LED, wherein the magnetic metal layer 74 can be formed on the bottom, the flank or any position of the LED, and the present invention is not limited thereto. Hence, the principle of electromagnetic inducement is used to generate heat in order to activate the p-type semiconductor material, and to reduce the resistance between the semiconductor and the metal electrode. In a preferred embodiment of the present invention, if the substrate 50 is thinned before the magnetic metal layer 74 is formed, then the better heating effect of electromagnetic inducement can be attained.
The structure of the present invention, the III-nitride LED having the magnetic metal layer, is not limited in the structure of
It is noted that, the aforementioned varieties and forming sequences of the plurality of III-nitride compound semiconductor layers in the epitaxial structure, and the aforementioned number of the metal electrodes are merely stated as examples, and can be changed due to the difference of products, functions or processes, so that the present invention is not limited thereto. In addition, the material forming the substrate 50, the buffer layer 54, the first electrical semiconductor layer 56, the first electrical confining layer 58, the active layer 60, the second electrical confining layer 62, the second electrical contact layer 64 and the magnetic metal layer 74 is also stated as examples, and the present invention is not limited thereto.
The structure of III-nitride LED having the magnetic metal layer and the heating method of electromagnetic inducement provided by the present invention utilize the equipments of simple structure and low cost. Moreover, the present invention also reduces the contact resistance between the semiconductors and electrodes while activates the III-nitride compound semiconductor material.
As is understood by a person skilled in the art, the foregoing preferred embodiments of the present invention are illustrated of the present invention rather than limiting of the present invention. It is intended to cover various modifications and similar arrangements included within the spirit and scope of the appended claims, the scope of which should be accorded the broadest interpretation so as to encompass all such modifications and similar structure.
Number | Date | Country | Kind |
---|---|---|---|
91100270 A | Jan 2002 | TW | national |
Number | Name | Date | Kind |
---|---|---|---|
6023076 | Shibata | Feb 2000 | A |
6376866 | Shakuda | Apr 2002 | B1 |
6459100 | Doverspike et al. | Oct 2002 | B1 |
6492191 | Shibata et al. | Dec 2002 | B2 |
6657237 | Kwak et al. | Dec 2003 | B2 |
20020074561 | Sawaki et al. | Jun 2002 | A1 |
Number | Date | Country | |
---|---|---|---|
20030127644 A1 | Jul 2003 | US |