ILLUMINANT AND ILLUMINANT LAMP COMPRISING SAID ILLUMINANT

Abstract
A phosphor for low-pressure discharge lamps is disclosed, wherein the phosphor is present in the form of phosphor grains coated with a protective layer, wherein the protective layer consists of a metal oxide, a metal borate, a metal phosphate or mixtures thereof.
Description
TECHNICAL FIELD

The present disclosure relates to a phosphor for a low-pressure discharge lamp, a phosphor composition, and a low-pressure discharge lamp.


BACKGROUND

Regulation EC 245/2009 (amended by regulation 347/2010) prohibits a number of fluorescent lamps having rare-earth-free phosphor coating. Lamps having the same power consumption but significantly higher luminous efficiency and higher luminous flux have been used as a replacement product, with a coating composed of rare earth phosphors being used. The proportion of rare earths is disadvantageous here since rare earths are increasingly running short and their prices on the world market have increased greatly in recent years. Therefore, there is a need for fluorescent lamps having a reduced proportion of rare earths and having the same efficiency and the same luminous flux stability as the fluorescent lamps currently in use, in order thus to reduce the material costs and to reduce environmental burdens resulting from the extraction and transport of rare earths.


In order to reduce the proportion of rare earths, fluorescent lamps have previously been produced in a double-layer design, wherein the lower layer consists of a customary halophosphate phosphor and the top layer consists of a mixture containing rare earth phosphors. Disadvantages of these fluorescent lamps include the high loss of light and the higher Hg consumption over the operating life. The loss of light is caused by radiation damage, in particular hard UV radiation e.g. in the VUV range, of the halophosphate phosphor. The higher Hg consumption can be attributed to the fact that Hg diffuses into the halophosphate phosphor grains.


Another measure for reducing the proportion of rare earths is to produce fluorescent lamps in a reflector layer design. In this case, the inner side of the discharge vessel is coated with an Al2O3 protective layer and a top layer containing rare earth phosphors is applied thereabove. Disadvantages in this case include the higher proportion of rare earth phosphors compared with the double-layer design and less covering of the ends of the lamp bulbs as a consequence of layer thickness fluctuations over the lamp bulb length.


SUMMARY

Various embodiments provide a phosphor and a phosphor composition for low-pressure discharge lamps, and a low-pressure discharge lamp including such a phosphor composition, which fulfill this requirement by having a reduced proportion of rare earths with the same efficiency and the same luminous flux stability.







The disclosure is based on the inventors' discovery that, by coating phosphor grains with a protective layer, it is possible to improve the stability of the phosphor and thereby to maintain the luminous efficiency for longer. As a result of this coating of the phosphors/phosphor grains of the phosphor composition, the use in fluorescent and compact fluorescent lamps can make a positive contribution with regard to stability toward exciting radiation, with regard to low affinity for Hg and thus low adsorption of Hg during lamp operation, and with regard to stability in water, in order that the environmentally friendly coating methods that are customary nowadays and make use of water-based suspensions can be used. This protective layer surrounding the phosphor grains is embodied as a layer that is as thin and dense as possible and differs in its composition from the composition inside the phosphor grain.


In a first aspect, however, the disclosure relates to a phosphor for low-pressure discharge lamps, wherein the phosphor is present in the form of phosphor grains coated with a protective layer. In this case, the protective layer consists of a metal oxide, a metal borate, a metal phosphate or mixtures thereof.


In various embodiments, the protective layer is applied to the surface of the phosphor grains and covers the latter completely.


The terms “protective layer” or “coating” are used interchangeably herein and relate to a layer or a film that coats the surface of the phosphor grains. Preferably, the entire surface of the phosphor grain is coated. In various embodiments, the layer thickness of the protective layer is approximately 10 nm to 1 μm.


“Phosphor grain”, as used herein, relates to a particle composed of one or more phosphors. The particle can be a substantially spherical particle. The term includes crystallites, agglomerates, amorphous particles, etc.


In various embodiments of the disclosure, the protective layer contains Al2O3, Y2O3, La2O3, a metal borate, a metal phosphate, or mixtures thereof, wherein the metal is selected from Sc, Y, La, Gd, Lu, Al, Ce, Mg, Ca, Sr, Ba and mixtures thereof. In specific embodiments, the protective layer substantially or completely consists of the abovementioned materials.


The metal borate or metal phosphate can be a binary metal borate or metal phosphate of the formula MePO4 or MeBO3, wherein Me is selected from Sc, Y, La, Gd, Lu and Al. The metal borate or metal phosphate can likewise be a ternary metal borate or metal phosphate of the formula (Me11-xMe2x) PO4 or (Me11-xMe2x)BO3, wherein Me1 and Me2 are selected independently of one another from Sc, Y, La, Gd, Lu and Al.


In various embodiments of the disclosure, the phosphor is a halophosphate phosphor. “Halophosphate phosphor” as used herein, is understood to mean phosphors that are halogen-containing phosphates, in particular of metals, such as strontium, calcium, barium and magnesium, for example. In particular fluorine (F) and chlorine (Cl) are used as “halogen”. Exemplary halophosphate phosphors include, but are not restricted to Ca10(PO4)6(F,Cl)2:Sb,Mn; Ca10(PO4)6F2:Sb,Mn; Sr5(PO4)3F:Sb; Ca5(PO4)3F:Sb; 3Ca3 (PO4)2.Ca(F,Cl)2:Mn,Sb; and 3Sr3(PO4)2.Sr(F,Cl)2:Mn,Sb. “Halophosphate phosphors” within the meaning of the invention are substantially free of rare earths, i.e. they neither contain rare earth compounds nor are they doped with rare earths. Therefore, in various embodiments, the content of rare earths relative to the coated halophosphate phosphor is <0.1% by weight, preferably <0.05% by weight, even more preferably <0.01% by weight. In various embodiments of the phosphor compositions of the invention, mixtures of two or more halophosphate phosphors can be used. The use of coated halophosphate phosphors in low-pressure discharge lamps allows the layer thickness of the rare-earth-containing tri-band phosphors to be reduced, since the non-absorbed UV radiation is converted into visible light by the halophosphate phosphor. By virtue of the stabilizing coating, furthermore, halophosphate phosphors can be used for certain spectral ranges. In this regard, by way of example, bluish halophosphate phosphors can partly replace the blue phosphor BaMgAl10O17:Eu.


In various other embodiments of the disclosure, the phosphor is a rare earth phosphor. “Rare earth phosphors” within the meaning of the invention denote phosphors which contain elements of the rare earths either as the basis or as a doping element. “Rare earth metals” or “rare earths”, as used herein, include the following elements: scandium (Sc), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), thulium (Tm), ytterbium (Yb) and lutetium (Lu). The term “rare earth phosphors”, as used herein, likewise includes halophosphates of rare earths or halophosphates of other elements doped with rare earths. Exemplary rare earth phosphors include, but are not restricted to, LaPO4:Ce,Tb; Y2O3:Eu; BaMgAl10O17:Eu; BaMg2Al16O27:Eu,Mn; Y2O2S:Eu; Y2O2S:Tb; Y2O3:Tb; Y2SiO5:Ce; Y2SiO5:Tb; Y3Al5O12:Ce; Gd(Zn,Mg)B5O10:Ce,Mn; Gd2O2S:Eu; Gd2O2S:Tb, Gd2O2S:Pr; CeMg—Al11O19:Tb; (Ce,Tb)MgAl11O19:Ce,Tb; Sr4Al14O25:Eu; Sr10(PO4)6Cl2:Eu; (Sr,Ca)10(PO4)6Cl2:Eu; (Sr,Ca,Ba)10(PO4)6Cl2:Eu Y3(Al,Ca)5O12:Ce; Y3(Al,Ca)5O12:Tb; YAlO3:Ce; and Y(P,V)O4:Eu. In phosphors doped with rare earths, the content of rare earths relative to the phosphor in various embodiments is >0.1% by weight, preferably >0.5% by weight, even more preferably >1% by weight. In various embodiments of the invention, mixtures of two or more rare earth phosphors can be used.


In specific embodiments of the disclosure, the rare earth phosphor coated with a protective layer is a phosphor which emits in the blue wavelength range, such as BaMgAl10O17:Eu, for example. The stability, in particular of rare-earth-containing blue phosphors, can be improved by this coating.


The phosphor is preferably present in the form of phosphor grains. In various embodiments, said phosphor grains have an average diameter of <25 μm, preferably <10 μm, even more preferably <8 μm. The particle size distribution can be substantially monodisperse. Methods for producing phosphor grains are known in the prior art.


The protective layer can be applied to the phosphor grains by means of a variety of methods. Suitable methods include, but are not restricted to, chemical vapor deposition (CVD) or wet-chemical methods. Corresponding coating methods are known in the prior art.


In a further aspect, the disclosure relates to phosphor compositions containing at least one phosphor according to the invention. In one embodiment, the phosphor composition contains a halophosphate phosphor according to the invention or consists thereof. In further embodiments, the phosphor composition can additionally contain a rare earth phosphor. The latter can likewise be present in the form of phosphor grains coated with a protective layer according to the invention.


“Phosphor composition”, as used herein, is understood to mean, in particular, the composition of all phosphors present in a phosphor layer in the discharge vessel of a low-pressure discharge lamp.


In one embodiment of the disclosure, the phosphor composition contains a coated halophosphate phosphor, for example selected from the list mentioned above, and a rare earth phosphor which emits in the blue wavelength range and which can likewise be coated, such as, for example, BaMgAl10O17:Eu.


In yet another aspect, the disclosure relates to a low-pressure discharge lamp including a discharge vessel filled with a filling gas composition, and including—applied on the inner side of said discharge vessel—a multilayered phosphor coating including a phosphor layer (lower layer) facing the inner side of the discharge vessel and a phosphor layer (top layer) facing the discharge space, wherein the phosphor layer facing the inner side of the discharge vessel contains or consists of a phosphor composition according to the disclosure.


In various embodiments of the disclosure, the phosphor layer facing the discharge space contains at least one rare earth phosphor. The latter can be selected from the group consisting of: LaPO4:Ce,Tb; Y2O3:Eu; BaMgAl10O17:Eu; BaMg2Al16O27:Eu,Mn; Y2O2S:Eu; Y2O2S:Tb; Y2O5:Tb; Y2SiO5:Ce; Y2SiO5:Tb; Y3Al5O12:Ce; Gd(Zn,Mg)B5O10:Ce,Mn; Gd2O2S :Eu; Gd2O2S:Tb, Gd2O2S:Pr; CeMgAl11O19:Tb; (Ce,Tb)MgAl11O19:Ce,Tb; Sr4Al14O25:Eu; Sr10(PO4)6Cl2:Eu; (Sr,Ca)10(PO4)6Cl2:Eu; (Sr,Ca,Ba)10(PO4)6Cl2:EU Y3(Al,Ca)5O12:Ce; Y3(Al,Ca)5O12:Tb; YAlO3:Ce; and Y(P,V)O4:Eu.


In one embodiment of the disclosure, the phosphor layer facing the discharge space also contains a phosphor composition according to the invention. Preferably, said phosphor layer contains at least one rare earth phosphor according to the disclosure.


In various embodiments, the phosphor composition facing the discharge space contains at least 3 rare earth phosphors, wherein the latter include a phosphor which emits in the red wavelength range, a phosphor which emits in the green wavelength range and a phosphor which emits in the blue wavelength range. Alternatively, the phosphor composition facing the discharge space may include at least 4 rare earth phosphors, wherein the latter include a phosphor which emits in the red wavelength range, a phosphor which emits in the green wavelength range, a phosphor which emits in the blue wavelength range and a phosphor which emits in the blue-green wavelength range. The phosphor which emits in the red wavelength range can be, for example, Gd(Zn,Mg)B5O10:Ce,Mn or Y2O3:Eu. The phosphor which emits in the green wavelength range can be, for example, LaPO4:Ce,Tb or CeMg—Al11O19:Tb. The phosphor which emits in the blue wavelength range can be, for example, BaMgAl10O17:Eu or Sr10(PO4)6Cl2:Eu. The phosphor which emits in the blue-green wavelength range can be, for example, Sr4Al14O25:Eu or BaMg2Al16O27:Eu,Mn. These rare earth phosphors can be coated phosphors according to the disclosure or else uncoated phosphors.


The production of low-pressure discharge lamps including corresponding phosphor layers is known in the prior art. For the production of the low-pressure discharge lamps of the present invention, the coated phosphors are used as powder for the production of an aqueous phosphor suspension, which is then applied to the inner side of the discharge vessel by means of known methods.


In various embodiments, the low-pressure discharge lamp furthermore includes a protective layer arranged between the inner side of the discharge vessel and the phosphor layer facing the inner side of the discharge vessel. Said protective layer may include of Al2O3, Y2O3, La2O3, a metal borate, a metal phosphate, or mixtures thereof, wherein the metal consists of Sc, Y, La, Gd, Lu, Al, Ce, Mg, Ca, Sr, Ba and mixtures thereof. As a result, diffusion of the mercury present in the discharge vessel, into the material of the discharge vessel usually glass, and associated blackening thereof can be effectively prevented.


In various embodiments of the disclosure, the low-pressure discharge lamps of the invention contain a filling gas, which is a noble gas or a mixture of noble gases. In one embodiment, the filling gas is a filling gas composition consisting of argon and/or krypton.


The low-pressure discharge lamp of the disclosure can be an Hg low-pressure discharge lamp. The Hg low-pressure discharge lamp can be, for example, a compact fluorescent lamp (energy-saving lamp). In various embodiments, the phosphor composition according to the invention is used in a rod-shaped low-pressure discharge lamp, for example of the design T8 L36W.


“Approximately”, as used herein in connection with numerical values, includes a variation of up to ±10%, preferably ±5%.


All chemical formulae indicated for the phosphor mixture and the phosphor compounds are indicated as ideal forms, but the intention is for the invention alternatively also to explicitly encompass all compounds going beyond these ideal formulae and having slight deviations from stoichiometry. That applies, in particular, to deviations for which the crystal structure remains unchanged and the deviations in emission and absorption spectra differ by less than 1% in the peak position and by less than 5% in the peak width.


In a further aspect, the disclosure relates to the use of the phosphors and phosphor compositions according to the invention as phosphor coating in a low-pressure discharge lamp.


The disclosure is described herein by reference to specific embodiments, but is not restricted thereto. In particular, it is readily apparent to a person skilled in the art that various amendments to the invention described can be made, without departing from the meaning and scope of the invention as determined by the appended patent claims. The scope of the invention is thus determined by the patent claims and the intention is for the invention to encompass all modifications and amendments which fall within the scope of interpretation and equivalence of the claims.

Claims
  • 1. A phosphor for low-pressure discharge lamps, whereinthe phosphor is present in the form of phosphor grains coated with a protective layer, wherein the protective layer consists of a metal oxide, a metal borate, a metal phosphate or mixtures thereof.
  • 2. The phosphor as claimed in claim 1, whereinthe protective layer consists of Al2O3, Y2O3, La2O3, a metal borate, a metal phosphate, or mixtures thereof, wherein the metal is selected from Sc, Y, La, Gd, Lu, Al, Ce, Mg, Ca, Sr, Ba and mixtures thereof.
  • 3. The phosphor as claimed in claim 2, whereinthe metal borate or metal phosphate is a binary metal borate or metal phosphate of the formula MePO4 or MeBO3, wherein Me is selected from Sc, Y, La, Gd, Lu and Al; orthe metal borate or metal phosphate is a ternary metal borate or metal phosphate of the formula (Me11-xMe2x)PO4 or (Me11-xMe2x)BO3, wherein Me1 and Me2 are selected independently of one another from Sc, Y, La, Gd, Lu and Al.
  • 4. The phosphor as claimed in claim 1, whereinthe phosphor is a halophosphate phosphor.
  • 5. The phosphor as claimed in claim 4, whereinthe phosphor is selected from the group consisting of Ca10(PO4)6(F,Cl)2:Sb,Mn; Ca10(PO4)6F2:Sb,Mn; Sr5(PO4)3F:Sb; Ca5(PO4)3F:Sb; 3Ca3(PO4)2Ca(F,Cl)2:Mn,Sb; and 3Sr3(PO4)2.Sr(F,Cl)2:Mn,Sb.
  • 6. The phosphor as claimed in claim 1, whereinthe phosphor is a rare earth phosphor.
  • 7. The phosphor as claimed in claim 6, whereinthe phosphor is selected from the group consisting of: LaPO4:Ce,Tb; Y2O3:Eu; BaMgAl10O17:Eu; BaMg2Al16O27:Eu,Mn; Y2O2S:Eu; Y2O2S:Tb; Y2O5:Tb; Y2SiO5:Ce; Y2SiO5:Tb; Y3Al5O12:Ce; Gd(Zn,Mg)B5O10:Ce,Mn; Gd2O2S:Eu; Gd2O2S:Tb, Gd2O2S:Pr; CeMg—Al11O19:Tb; (Ce,Tb)MgAl11O19:Ce,Tb; Sr4Al14O25:Eu; Sr10(PO4)6Cl2:Eu; (Sr,Ca)10(PO4)6Cl2:Eu; (Sr,Ca,Ba)10(PO4)6Cl2:Eu Y3(Al,Ca)5O12:Ce; Y3(Al,Ca)5O12:Tb; YAlO3:Ce; and Y(P,V)O4:Eu.
  • 8. The phosphor as claimed in claim 1, whereinthe protective layer is applied to the phosphor grains by means of chemical vapor deposition (CVD) or by means of wet-chemical methods.
  • 9. The phosphor as claimed in claim 1, whereinthe phosphor has an average grain size of less than 10 μm.
  • 10. A phosphor composition for low-pressure discharge lamps, whereinthe phosphor composition contains at least one phosphor, wherein at least one phosphor of the at least one phosphor is present in the form of phosphor grains coated with a protective layer, wherein the protective layer consists of a metal oxide, a metal borate, a metal phosphate or mixtures thereof.
  • 11. The phosphor composition as claimed in claim 10, whereinthe phosphor composition contains a halophosphate phosphor and furthermore at least one rare earth phosphor, wherein the phosphor is selected from the group consisting of: Ca10(PO4)6(F,Cl)2:Sb,Mn; Ca10(PO4)6F2:Sb,Mn; Sr5(PO4)3F:Sb; Ca5(PO4)3F:Sb; 3Ca3(PO4)2.Ca(F,Cl)2:Mn,Sb; and 3Sr3(PO4)2.Sr(F,Cl)2:Mn,Sb.
  • 12. The phosphor composition as claimed in claim 11, whereinthe at least one rare earth phosphor is a rare earth phosphor, wherein the from the group consisting of: LaPO4:Ce,Tb; Y2O3:Eu; BaMgAl10O17:Eu; BaMg2Al16O27:Eu,Mn; Y2O2S:Eu; Y2O2S:Tb; Y2O5:Tb; Y2SiO5:Ce; Y2SiO5:Tb; Y3Al5O12:Ce; Gd(Zn,Mg)B5O10:Ce,Mn; Gd2O2S:Eu; Gd2O2S:Tb, Gd2O2S:Pr; CeMgAl11O19:Tb; (Ce,Tb)MgAl11O19:Ce,Tb; Sr4Al14O25:Eu; Sr10(PO4)6O2:Eu; (Sr,Ca)10(PO4)6Cl2:Eu; (Sr,Ca,Ba)10(PO4)6Cl2:Eu Y3(Al,Ca)5O12:Ce; Y3(Al,Ca)5O12:Tb; YAlO3:Ce; and Y(P,V)O4:Eu.
  • 13. A low-pressure discharge lamp comprising a discharge vessel filled with a filling gas composition, and comprising a multilayered phosphor coating comprising a phosphor layer facing the inner side of the discharge vessel and a phosphor layer facing the discharge space, wherein the phosphor layer facing the inner side of the discharge vessel contains a phosphor composition, whereinthe phosphor composition contains at least one phosphor, wherein at least one phosphor of the at least one phosphor is present in the form of phosphor grains coated with a protective laver, wherein the protective layer consists of a metal oxide, a metal borate, a metal phosphate or mixtures thereof.
  • 14. The low-pressure discharge lamp as claimed in claim 13, whereinthe phosphor layer facing the discharge space contains at least one rare earth phosphor.
  • 15. The low-pressure discharge lamp as claimed in claim 14, whereinthe at least one rare earth phosphor is selected from the group consisting of LaPO4:Ce,Tb; Y2O3:Eu; BaMgAl10O17:Eu; BaMg2Al16O27:Eu,Mn; Y2O2S:Eu; Y2O2S:Tb; Y2O5:Tb; Y2SiO5:Ce; Y2SiO5:Tb; Y3Al5O12:Ce; Gd(Zn,Mg)B5O10:Ce,Mn; Gd2O2S:Eu; Gd2O2S:Tb, Gd2O2S:Pr; CeMgAl11O19:Tb; (Ce,Tb)MgAl11O19:Ce,Tb; Sr4Al14O25:Eu; Sr10(PO4)6Cl2:Eu; (Sr,Ca)10(PO4)6Cl2:En; (Sr,Ca,Ba)10O4)6Cl2:Eu Y3(Al,Ca)5O12:Ce; Y3(Al,Ca)5O12:Tb; YAlO3:Ce; and Y(P,V)O4:Eu.
  • 16. The low-pressure discharge lamp as claimed in claim 13, whereinthe phosphor layer facing the discharge space contains a phosphor composition, wherein the phosphor composition contains at least one phosphor, wherein at least one phosphor of the at least one phosphor is present in the form of phosphor grains coated with a protective layer, wherein the protective layer consists of a metal oxide, a metal borate, a metal phosphate or mixtures thereof.
  • 17. The low-pressure discharge lamp as claimed in claim 13, whereinthe phosphor composition facing the discharge space contains at least 3 rare earth phosphors, wherein the latter comprise a phosphor which emits in the red wavelength range, a phosphor which emits in the green wavelength range and a phosphor which emits in the blue wavelength range; orthe phosphor composition facing the discharge space contains at least 4 rare earth phosphors, wherein the latter comprise a phosphor which emits in the red wavelength range, a phosphor which emits in the green wavelength range, a phosphor which emits in the blue wavelength range and a phosphor which emits in the blue-green wavelength range.
  • 18. The low-pressure discharge lamp as claimed in claim 13, whereinthe low-pressure discharge lamp further comprises a protective layer arranged between the inner side of the discharge vessel and the phosphor layer facing the inner side of the discharge vessel.
  • 19. The low-pressure discharge lamp as claimed in claim 18, whereinthe protective layer consists of Al2O3, Y2O3, La2O3, a metal borate, a metal phosphate, or mixtures thereof, wherein the metal is selected from Sc, Y, La, Gd, Lu, Al, Ce, Mg, Ca, Sr, Ba and mixtures thereof.
  • 20. The low-pressure discharge lamp as claimed in claim 13, whereinthe filling gas composition comprises argon or krypton.
  • 21. (canceled)
Priority Claims (2)
Number Date Country Kind
20 2011 109 804.8 Jul 2011 DE national
102012203419.6 Mar 2012 DE national
RELATED APPLICATIONS

The present application is a national stage entry according to 35 U.S.C. §371 of PCT application No. PCT/EP2012/062248 filed on Jun. 25, 2012, which claims priority from German application No. 20 2011 109 804.8 filed on Jul. 29, 2011 and German application No. 10 2012 203 419.6 filed on Mar. 5, 2012 and is incorporated herein by reference in its entirety.

PCT Information
Filing Document Filing Date Country Kind 371c Date
PCT/EP2012/062248 6/25/2012 WO 00 1/29/2014