The invention relates to a ceramic tile according to the preamble of claim 1 and a method for producing same.
According to the invention, the term “ceramic tile” is understood to refer to ceramic slabs that are used to line walls and as floor coverings in the indoor and outdoor areas.
The term “tile” is also used for natural stone, glass, floor coverings, etc., to classify parts having a similar shape. The bisque (body) of such a ceramic tile is preferably made of clay minerals, consisting primarily of extremely fine-grained weathering products of feldspar formed with a wide variety of admixtures. The composition of the clay, the preparation and the firing determine the color of the unglazed piece.
Clay is thus the main ingredient used as the basic material for the ceramic tiles. Depending on the application, mixtures of various clay samples are used for this purpose. In addition to clay, other mineral raw materials are also used in a recipe for a ceramic. The most important additives are quartz, kaolin and feldspar. Depending on the intended purpose, calcite, dolomites, fluorspar or refractory clay are also added.
The extrusion process and powder pressing (also known as dry pressing) are used in modern ceramic production. In the extrusion process, a continuous strip is produced as a single tile or double tile from a plastic ceramic composition and then divided into tile size. In the dry pressing method, specially prepared ceramic powder is pressed into molds under a high pressure and then fired.
A third method uses roller presses for large-format fine tiles. A basic ceramic material is pressed between two rollers moving axially.
The present invention therefore relates to an illuminated ceramic tile produced according to one or more of the aforementioned methods.
There have been various attempts in the prior art to provide illumination for ceramic tile. For example, DE 20 2009 016 078 U1 proposes that one or more light sources may be arranged in a transparent cover layer above the body of a ceramic tile, such that this cover layer is made of a transparent plastic slab in which the lighting elements are embedded. However, the disadvantage of this arrangement is that the character of the ceramic tile, namely its highly load-bearing surface, its abrasion resistance, its impact hardness and other preferred properties are lost as a result of the arrangement of an illumination layer on the visible face.
DE 20 2004 000 810 U1 proposes an illuminated tile made of glass, in which the tile slab is formed as a sheet of glass and, with a spacer, has a light source carrier on which numerous light-emitting diodes are arranged. Therefore, a sheet of glass, which alters the original physical properties of the ceramic tile in an unwanted manner, is also arranged above the ceramic tile.
DE 295 11 741 U1 describes a ceramic tile, into which several cutouts or passages for insertion elements are incorporated. The disadvantage of such a ceramic tile is that the cutouts or passages must be created after the ceramic tile has been completed, which is a disadvantage associated with a high mechanical investment and leading to a high reject rate. Providing a completely fired ceramic slab with cutouts is associated with a high complexity in terms of tools and processing effort, and there is also the risk of breakage during processing.
Therefore, against the background of DE 295 11 741 U1, the object of the present invention is to improve upon an illuminated ceramic tile in such a way that it can be produced with little effort and retains the physical properties of a ceramic surface at least on the visible face.
To achieve the object as formulated, the invention is characterized by the technical teaching of claim 1.
The ceramic tile according to the present invention proposes that at least one glaze covering the visible face is provided, and a light generated by one or more light sources is visible on the visible face.
Accordingly, a densely fired ceramic tile is provided in both the prior art and in the present invention.
The glaze serves as a surface finish for ceramic products, such as stoneware, earthenware and porcelain and, in contrast with the porous crystalline body, creates a closed surface layer with a vitreous finish.
Stoneware and clay pieces are densely fired at a firing temperature of 1250° C. or more. Porcelain is densely fired at temperatures up to 1400° C. This results in intercrystalline vitreous phases, which supply a closed porosity and possibly also a self-glaze. The glaze is formed by additional substances, with which a hard closed surface layer can be produced in various colors. The components of the glaze form a vitreous layer from a mixture of various oxides with one another and with the base material.
Accordingly, the invention is directed at a fired ceramic tile, and it has been recognized according to the invention that, at the time of its production, the body of the ceramic tile may already be permeated by a plurality of bores or recesses, which form the future light-emitting openings on the visible face.
Thus, if the unfired clay piece is obtained in production of ceramic tiles, while still in the raw state, i.e., after production by the extrusion process or by the powder pressing method or the roll pressing method, it is provided according to the present invention that a number of bores and/or recesses are introduced into the body of the ceramic tile of this unfired material, which is still soft, passing through the body, i.e., extending from the visible face all the way through to the back face of the body of the tile.
Such holes or slots in the unfired tile, which is still soft, can be created, for example, by a nail plate, by a knife plate or by punching tools, which create the desired punched-out areas, bores or recesses in the unfired body of the ceramic tile while it is still soft.
After creating the bores, recesses or slots passing through the body of the ceramic tile, the ceramic tile is processed further by essentially known methods. It is thus coated with a liquid glaze and fired to form a dense piece.
It is assumed here that the glaze covering at least the visible face will flow into the bores, recesses or slots created previously in the body of the ceramic tile during the firing operation—or even prior to that—and will fill up these bores, recesses or slots.
Furthermore, it is provided that the glaze used is at least partially light conducting, transparent or opaque and enables the passage of visible light.
After the final firing of the ceramic tile thus provided with holes, slots or other recesses, the recesses created previously are thus filled with the light-conducting glaze.
According to the invention, it is then provided that one or more light sources are arranged on the back face of the ceramic tile and are arranged in light-conducting connection to the bores, slots or recesses.
It is thus sufficient to arrange one or more light sources on the back face of the ceramic tile to illuminate the back face of the ceramic tile, because the bores, slots or other recesses, which were previously filled with the light-conducting glaze, will now transport the light generated on the back face to the visible face of the ceramic tile and make it visible there.
The ceramic tile thus provides light on the visible face because the light emerges from the bores, slots or recesses and is readily discernible.
It is possible to provide that the glaze is transparent like glass and uncolored so as to achieve a high luminous density on the visible face of the ceramic tile.
In other embodiments, it is also possible to provide that the glaze is pigmented, and there are various possibilities for this pigmentation:
Various layers of glaze can be created in this way, one above the other.
In another embodiment of the invention, it is possible to provide that the ceramic tiles are perforated, slotted or provided with other recesses in the green state, and these holes, slots or recesses are then filled with suitable placeholders while the glaze is applied, and thereby kept free for the subsequent firing operation.
After the final firing of the piece, the bores, slots or recesses that had been created are thus free of the glaze on the surface and can then subsequently be filled with another composition, preferably made of a plastic that hardens by curing.
The bores, slots or recesses are then filled with a different light-conducting plastic material in comparison with the hardened glaze covering the other surfaces of the ceramic tile.
In one preferred embodiment of the invention, it is provided that the light source is embodied as a lighting tile, which is fitted into a respective bottom recess on the back face of the ceramic tile as a surface lighting element. Such a lighting tile may be furnished with light sources, for example, on the edge side or at least on the edges, that create a uniform luminous impression over the entire surface of the lighting tile.
The lighting tile may also be designed as an electrically activatable fluorescent or luminescent sheet.
Instead of a lighting tile covering the surface, individual lighting elements such as LEDs distributed discretely may also be used, in which case it is preferable if such discrete lighting elements are attached to the back face of the ceramic tile, so that they are flush and are attached to the back face of the ceramic tile, opposite the respective bore or recess, to thereby shine their light directly into the bore.
In another embodiment, it may also be provided that the individual discrete, point-type lighting elements are connected electrically to one another to form a chain as a lighting strip, and such lighting strips are then attached to the back face of the ceramic tile in the respective recesses.
A method directed at production of an illuminated tile is based on the fact that, in a first method step, the unfired ceramic tile comprising a blank in a moist and moldable raw state containing an earth-moist clay mixture and some other mineral additives is subjected to an extrusion or roll-forming process, and then numerous bores and/or recesses are created in the body of the ceramic tile while in the form of unfired earth-moist extruded material, which is molded in the form of a slab, these bores and/or recesses passing completely through the body, i.e., extending from the visible face to the back face of the body of the tile, and next the bores and/or recesses are filled and closed with a glaze that is at least partially light conducting, and only then does the firing operation take place, converting the tile to a dense ceramic piece.
In a preferred embodiment of the method, the holes or slots in the unfired tile, which is still soft, are created by a nail plate or a knife plate or punching tools, which create the bores or recesses or punched-out areas in the body of the ceramic tile, while it is still soft and unfired.
The subject matter of the present invention is derived not only from the subject matter of the individual claims but also from the combination of the individual claims with one another.
All the information and features disclosed in these documents, including the abstract, in particular the three-dimensional design, as illustrated in the drawings, are claimed as essential to the invention inasmuch as they are novel individually or in combination in comparison with the prior art.
The invention is explained in greater detail below on the basis of several drawings illustrating methods of implementation. Additional features that are essential to the invention and advantages of the invention are derived from the drawings and the description thereof, in which:
According to
In preferred embodiments, the ceramic tile 1 has a total thickness in the range of approx. 15 to 20 mm, and the peripheral bottom edge 5 has a width in the range of approx. 10 to 20 mm.
The height of the bottom edge 5 over the bottom recess 4, which is recessed deeper, may be in the range of approx. 4 mm.
In
However, it is also possible to provide that the bottom recess 4 and the bottom edge 5 are covered with the vitreous glaze 11 and fired.
To produce an illuminated ceramic tile, it is therefore provided that, according to
The area of the lighting tile 6 should be selected so that it does not protrude beyond the width 8 of the peripheral bottom edge 5 but instead can be fitted so that it is flush in the bottom recess 4.
This ensures that, when the ceramic tile is used, its properties are maintained, i.e., a highly abrasion resistant surface with a high resistance to breaking and a high hardness, as would be expected of unlighted ceramic tiles 1.
Light generated in this way is emitted in the direction of arrow 15 into the bore 2 and is also distributed in the direction of arrow 16 on the bottom side of the ceramic tile 1 and may propagate in these directions of arrows 15, 16 in the lighting tile 6.
They may also be arranged crosswise, so that the recesses 9 arranged opposite one another may also have an additional lighting strip 17 passing through them.
It is likewise possible to have a power cable 18 passing through the recesses 9 in order to electrically connect the ceramic tiles 1 situated side by side to one another by means of suitable cables.
In modification of the embodiments shown previously,
In the embodiment shown here, these recesses 22 are designed in the form of slots.
The rays of light 13 generated by the lighting sources in this way (see
| Number | Date | Country | Kind |
|---|---|---|---|
| 20 2015 006 801.4 | Sep 2015 | DE | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2016/001601 | 9/26/2016 | WO | 00 |