Patent Application
20090122412
The present invention relates to an image presentation system that in an exemplary embodiment is formed of microstructured icon elements in a polymer film. The present invention also relates to a synthetic magnification micro-optic system that in an exemplary embodiment is formed as a polymer film. The unusual effects provided by the various embodiments of the disclosure can be used as a security device for overt and covert authentication of currency, documents, and products as well as visual enhancement of products, packaging, printed material, and consumer goods.
Various image presentation systems have previously been attempted. Typical image presentation systems involve conventional printing techniques. Some image presentation systems involve holographic image displays and/or embossed image features. These systems all have drawbacks in relation to the nature or quality of the image displayed. More particularly they all have the disadvantage that they can be readily copied, and thus cannot serve as an authentication or security device.
Various optical materials have been employed to provide image systems for authentication of currency and documents, to identify and distinguish authentic products from counterfeit products, and to provide visual enhancement of manufactured articles and packaging. Examples include holographic displays, and other image systems involving lenticular structures and arrays of spherical micro-lenses. Holographic displays have become prevalent for use with credit cards, drivers' licenses, and clothing tags.
An example of a lenticular structure for document security is disclosed in U.S. Pat. No. 4,892,336 to Kaule, et al. directed to a security thread for embedding within a document to provide anti-falsification measures. The security thread is transparent having a printed pattern on one side, on the opposite side, a lenticular lens structure coordinated with the printed pattern. The lenticular lens structure is described as comprised of a plurality of parallel cylinder lenses, or alternatively spherical or honeycomb lenses.
U.S. Pat. No. 5,712,731 to Drinkwater, et al. discloses a security device that includes an array of micro-images coupled with an array of substantially spherical micro-lenses. The lenses may also be astigmatic lenses. The lenses are each typically 50-250 μm and with a focal length of typically 200 μm.
These approaches all suffer from similar drawbacks. They result in a relatively thick structure that is not particularly suitable for use with document authentication. Their use of cylindrical or spherical lenses provides a narrow field of view resulting in fuzzy images and requiring exact and difficult alignment of the focal point of the lenses with the associated images. Additionally, they have not proven particularly effective as security or anti-counterfeiting measures.
In view of these and other deficiencies, a need exists in the industry for secure and visually unique optical materials that can facilitate overt authentication of currency, documents, manufactured articles, and products and for optical materials that provide visual enhancement of manufactured articles, products, and packaging.
The present disclosure relates to an image presentation system, such as a micro-image presentation system. For example, in one form a synthetic optical image system can be provided that includes an array of focusing elements, and an image system that includes or is formed from an array or pattern of microstructured icon elements, such as those described below, wherein the microstructured icon elements are designed to collectively form an image or certain desired information, and wherein the array of focusing elements and the image system cooperate, for example through optical coupling, to form a synthetic optical image which image may optionally be magnified. In another form an image presentation system is provided that includes or is formed from an array or pattern of microstructured icon elements, such as those described below, wherein the microstructured icon elements are designed to collectively form an image or certain selected information, and wherein the image system is designed to stand alone and be the image viewed or the information read by use of a magnifying device, such as a magnifying glass or microscope, that is provided separately from the image system.
The present disclosure also relates to a film material that utilizes a regular two-dimensional array of non-cylindrical lenses to enlarge micro-images, called icons herein, and to form a synthetically magnified image through the united performance of a multiplicity of individual lens/icon image systems. The synthetically magnified images and the background surrounding them can be either colorless or colored, and either or both the images and the background surrounding them can be transparent, translucent, pigmented, fluorescent, phosphorescent, display optically variable color, metallized, or substantially retroreflective. The material displaying colored images on a transparent or tinted background is particularly well suited for use in combination with underlying printed information. When a piece of such material is applied over printed information both the printed information and the images are seen at the same time in spatial or dynamic motion relationship to each other. Material of this kind can also be overprinted, i.e. have print applied to the uppermost (lens) surface of the material. Alternatively, the material displaying colored images (of any color, including white and black) on a translucent or substantially opaque background of different color is particularly well suited for stand-alone use or with overprinted information, not in combination with underlying printed information.
The magnitude of the synthetic magnification achieved can be controlled by the selection of a number of factors, including the degree of ‘skew’ between the axes of symmetry of the lens array and the axes of symmetry of the icon array. Regular periodic arrays possess axes of symmetry that define lines that the pattern could be reflected around without changing the basic geometry of the pattern, that in the ideal of arrays are infinite in extent. A square array, for example, can be reflected around any diagonal of any square without changing the relative orientation of the array: if the sides of the squares are aligned with the x and y axes of the plane, then the sides of the squares will still be aligned with those axes after reflection, with the assumption that all sides are identical and indistinguishable. We refer to such arrays as having rotational symmetry or being rotationally symmetric.
Instead of mirroring the square array the array can be rotated through an angle equal to the angle between the axes of symmetry of the same type. In the case of a square array the array can be rotated through an angle of 90 degrees, the angle between diagonals, to arrive at an array orientation which is indistinguishable from the original array. Similarly, an array of regular hexagons can be mirrored or rotated about a number of axes of symmetry, including the “diagonals” of the hexagon (the lines connecting opposite vertices) or “midpoint divisors” (lines that connect between the center points of faces on opposite sides of the hexagon). The angle between the axes of symmetry of either type is sixty degrees (60°) results in an array orientation that is indistinguishable from the original orientation.
If a lens array and an icon array are initially arranged with their planar dimensions defining their respective x-y plane, one of the axes of symmetry being chosen to represent the x axis of the first array, the corresponding type of axis of symmetry (for example, diagonal axis of symmetry) being chosen to represent the x axis of the second array, with the two arrays separated by a substantially uniform distance in the z axis direction, then the arrays are said to have zero skew if the x axes of the arrays appear to be parallel to each other when the arrays are viewed along the z axis direction. In the case of hexagonal arrays, rotation of one array through an angle of 60 degrees, or multiples thereof, puts the arrays in alignment again, so there is no skew, just as there is no skew for a rotation of 90 degrees, or multiples thereof, in the case of square arrays. Any angular misalignment between the x axes that is different from these “zero skew rotations” is called the skew. A small skew, such as 0.06 degree, can create a large magnification, in excess of 1,000×, and a large skew, such as 20 degrees produces a small magnification, potentially as small as 1×. Other factors, such as the relative scales of the two arrays and the F# of the lens, can affect both the magnification of the synthetic image as well as its rotation, orthoparallactic movement, and apparent visual depth.
There are a number of distinct visual effects that can be provided by the present material (subsequently referred to as “Unison” for the material in general, or by the names “Unison Motion”, “Unison Deep”, “Unison SuperDeep”, “Unison Float”, “Unison SuperFloat”, “Unison Levitate”, “Unison Morph”, and “Unison 3-D” for Unison material presenting those respective effects), and their various embodiments producing each of these effects, generally described as follows:
Unison Motion presents images that show orthoparallactic movement (OPM)—when the material is tilted the images move in a direction of tilt that appears to be perpendicular to the direction anticipated by normal parallax. Unison Deep and SuperDeep present images that appear to rest on a spatial plane that is visually deeper than the thickness of the material. Unison Float and SuperFloat present images that appear to rest on a spatial plane that is a distance above the surface of the material; and Unison Levitate presents images that oscillate from Unison Deep (or SuperDeep) to Unison Float (or SuperFloat) as the material is rotated through a given angle (e.g. 90 degrees), then returning to Unison Deep (or SuperDeep) again as the material is further rotated by the same amount. Unison Morph presents synthetic images that change form, shape, or size as the material is rotated or viewed from different viewpoints. Unison 3-D presents images that show large scale three-dimensional structure, such as an image of a face.
Multiple Unison effects can be combined in one film, such as a film that incorporates multiple Unison Motion image planes that can be different in form, color, movement direction, and magnification. Another film can combine a Unison Deep image plane and a Unison Float image plane, while yet another film can be designed to combine Unison Deep, Unison Motion, and Unison Float layers, in the same color or in different colors, those images having the same or different graphical elements. The color, graphical design, optical effect, magnification, and other visual elements of multiple image planes are largely independent; with few exceptions, planes of these visual elements can be combined in arbitrary ways.
For many currency, document and product security applications it is desirable that the total thickness of the film be less than 50 microns, (also referred to herein as “μ”, or “um”), for example less than about 45 microns, and as a further example in the range of about 10 microns to about 40 microns. This can be accomplished, for example, through the use of focusing elements having an effective base diameter of less than 50 microns, as a further example less than 30 microns, and as yet a further example, from about 10 microns to about 30 microns. As another example, a focusing element having a focal length of less than about 40 microns, and as a further example having a focal length of about 10 to less than about 30 microns, can be used. In a particular example focusing elements having a base diameter of 35 microns and a focal length of 30 microns can be used. An alternate, hybrid refractive/diffractive embodiment, can be made as thin as 8 microns.
The films herein are highly counterfeit resistant because of their complex multi-layer structure and their high aspect-ratio elements that are not amenable to reproduction by commonly available manufacturing systems.
Thus, the present system provides a micro-optic system preferably in the form of a polymer film having a thickness that when viewed by unaided eye(s) in reflective or transmitted light projects one or more images that:
i. show orthoparallactic movement (Unison Motion);
ii. appear to lie on a spatial plane deeper than the thickness of the polymer film (Unison Deep and Unison SuperDeep);
iii. appear to lie on a spatial plane above a surface of the polymer film (Unison Float and Unison SuperFloat);
iv. oscillate between a spatial plane deeper than the thickness of the polymer film and a spatial plane above a surface of the film as the film is azimuthally rotated (Unison Levitate);
v. transform from one form, shape, size, color (or some combination of these properties) into a different form, shape, size, or color (or some combination of these properties) (Unison Morph); and/or
vi. appear to have realistic three-dimensionality (Unison 3-D).
A synthetic magnification micro-optic system is disclosed that can for example service as a security or authentication device, comprising:
(a) a micro image comprised of a periodic, rotationally symmetric planar array of a plurality of image icons having an axis of symmetry within its plane; and
(b) a periodic planar array of a plurality of image icon focusing elements having a rotational symmetry and a periodicity substantially corresponding to the rotational symmetry and periodicity of the micro image array and having an axis of symmetry within its plane, the axis of symmetry of the array of image icon focusing elements having a selected angle with respect to the corresponding axis of symmetry of the micro image planar array, the image icon focusing elements including focusing elements either having an effective diameter of less than 50 microns or being polygonal base multi-zonal focusing elements, wherein the plane of the image icon focusing elements is disposed substantially parallel to the plane of the image icons at a distance sufficient for the image focusing elements to form a synthetic image of the image icons. The synthetic magnification micro-optic system of claim 1, wherein the focusing elements are selected from the group consisting of non-cylindrical lenses and non-cylindrical focusing reflectors and combinations thereof.
In another embodiment a method of producing a synthetic magnification micro-optic system and a method for producing a document security device, each comprising the steps of:
(a) providing a micro image comprised of a periodic, rotationally symmetric planar array of a plurality of image icons having an axis of symmetry within its plane; and
(b) providing a periodic planar array of a plurality of image icon focusing elements having a rotational symmetry and a periodicity substantially corresponding to the rotational symmetry and periodicity of the micro image array and having an axis of symmetry within its plane, the axis of symmetry of the array of image icon focusing elements having a selected angle with respect to the corresponding axis of symmetry of the micro image planar array, the image icon focusing elements including focusing elements having an effective diameter of less than 50 microns; and
(c) disposing the plane of the image icon focusing elements substantially parallel to the plane of the image icons at a distance sufficient for the image focusing elements to form a synthetic image of the image icons.
In yet another embodiment a method of controlling optical effects in a synthetic magnification micro-optic system or in a security or authentication device is disclosed, the optical effects including motion effects, magnification, visual depth effects or combinations of said effects, the method comprising the steps of:
(a) providing a micro image comprised of a rotationally symmetric planar array of a plurality of image icons having an axis of symmetry within its plane and having a selected repeat period for the image icons;
(b) providing a planar array of a plurality of image icon focusing elements having a rotational symmetry substantially corresponding to the rotational symmetry of the micro image array and having an axis of symmetry within its plane, the axis of symmetry of the array of image icon focusing elements having a selected angle with respect to the corresponding axis of symmetry of the micro image planar array, and having a selected repeat period for the focusing elements, the image icon focusing elements including focusing elements having an effective diameter of less than 50 microns or being polygonal base multi-zonal focusing elements; and
(c) disposing the plane of the image icon focusing elements substantially parallel to the plane of the image icons at a distance sufficient for the image focusing elements to form a synthetic image of the image icons;
(d) wherein the ratio of the repeat period of the image icons to the repeat period of the focusing elements is selected from the group consisting of less than 1, substantially equal to 1, and greater than 1, and selecting whether the axis of symmetry of the periodic planar array of the micro image and the corresponding axis of symmetry of the periodic planar array of image icon focusing elements are aligned or misaligned.
In a further exemplary embodiment an image icon for use in a synthetic micro-optic system is disclosed, the synthetic magnification micro-optic system including:
(a) a micro image comprised of a substrate having a planar array of a plurality of image icons; and
(b) a planar array of image icon focusing elements, wherein the planar array of image icon focusing elements is disposed in relation to the planar array of image icons at a distance and in a manner sufficient for the image focusing elements to form a synthetic image of the image icons;
the image icons including image icons formed as recesses in the substrate, the recesses forming voids that are optionally filled with a material providing a contrast with the substrate.
A synthetic magnification micro-optic system or document security device and methods of making same are also disclosed, comprising:
(a) a micro image comprised of a planar array of a plurality of image icons; and
(b) a planar array of image icon focusing elements, the focusing elements including focusing elements that are polygonal base multi-zonal focusing elements.
Further, a security or authentication thread is disclosed, comprising:
(a) a material having a periodic array of micro-images or icons comprising filled recesses formed in the material;
(b) a periodic array of non-cylindrical, flat field, aspheric or polygonal base multi-zonal micro-focusing elements disposed at a distance sufficient for the focusing elements to form a synthetic image of the micro-images or icons, wherein the micro-focusing elements including focusing elements having a base diameter ranging from about 20 to about 30 microns; and
(c) a pigmented or metallic sealing or obscuring layer covering the array of micro-images or icons.
A document security device or security thread, particularly for use in currency, are disclosed comprising:
(a) a micro image comprised of a periodic, rotationally symmetric planar array of a plurality of image icons having an axis of symmetry within its plane; and
(b) a periodic planar array of a plurality of image icon focusing elements having a rotational symmetry and a periodicity substantially corresponding to the rotational symmetry and periodicity of the micro image array and having an axis of symmetry within its plane, the axis of symmetry of the array of image icon focusing elements having a selected angle with respect to the corresponding axis of symmetry of the micro image planar array, the image icon focusing elements including focusing elements either having an effective diameter of less than 50 microns or being polygonal base multi-zonal focusing elements, wherein the plane of the image icon focusing elements is disposed substantially parallel to the plane of the image icons at a distance sufficient for the image focusing elements to form a synthetic image of the image icons.
And a synthetic magnification optical and security system are disclosed comprising an image and a plurality of image focusing elements, the focusing elements and the image arranged in a plane in relation to each other wherein when the system is tilted about an axis substantially parallel to the plane of the system the synthetic image appears to move in a direction parallel to the tilt axis.
The present disclosure further provides a synthetic magnification micro-optic system and method of making the same comprising:
(a) one or more optical spacers;
(b) a micro image comprised of a periodic planar array of a plurality of image icons having an axis of symmetry about at least one of its planar axes, and positioned on or next to the optical spacer; and
(c) a periodic planar array of image icon focusing elements having an axis of symmetry about at least one of its planar axes, the axis of symmetry being the same planar axis as that of the micro image planar array, each focusing element being either a polygonal base multi-zonal focusing element, a lens providing an enlarged field of view over the width of the associated image icon so that the peripheral edges of the associated image icon do not drop out of view, or an aspheric focusing element having an effective diameter of less than 50 microns.
The system can include one or more of the aforementioned effects. A method is provided by which said effects can be selectively included within the system.
The present disclosure further provides a security device suitable for at least partial incorporation in or on, and for use on or in association with, a security document, label, tear tape, tamper indicating device, sealing device, or other authentication or security device, which comprises at least one micro-optic system, as defined above. More particularly the present disclosure provides a document security device and method of making the same comprising:
(a) one or more optical spacers;
(b) a micro image comprised of a periodic planar array of a plurality of image icons having an axis of symmetry about at least one of its planar axes, and positioned on or next to the optical spacer; and
(c) a periodic planar array of image icon focusing elements having an axis of symmetry about at least one of its planar axes, the axis of symmetry being the same planar axis as that of the micro image planar array, each focusing element being either a polygonal base multi-zonal focusing element, a lens providing an enlarged field of view over the width of the associated image icon so that the peripheral edges of the associated image icon do not drop out of view, or an aspheric focusing element having an effective diameter of less than 50 microns.
Additionally, the present disclosure provides a visual enhancement device which comprises at least one micro-optic system, as defined above and having the above described effects, for visual enhancement of clothing, skin products, documents, printed matter, manufactured goods, packaging, point of purchase displays, publications, advertising devices, sporting goods, financial documents and transaction cards, and all other goods.
Also provided is a security document or label having at least one security device, as defined above, at least partially embedded therein and/or mounted thereon.
Other features and advantages of the present disclosure will be apparent to one of ordinary skill from the following detailed description and accompanying drawings.
Other systems, devices, methods, features, and advantage will be or become apparent to one with skill in the art upon examination of the following drawings and detailed description. It is intended that all such additional systems, methods, features, and advantages be included within this description, be within the scope of the present disclosure, and be protected by the accompanying claims.
Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. All publications, patent applications, patents and other references mentioned herein are incorporated by reference in their entirety. In case of conflict, the present specification, including definitions, will control. In addition, the materials, methods, and examples are illustrative only and not intended to be limiting.
Many aspects of the disclosure can be better understood with reference to the drawings. The components in the drawings are not necessarily to scale, emphasis instead being placed upon clearly illustrating the principles of the present disclosure. Moreover, in the drawings, like reference numerals designate corresponding parts throughout the several views.
a is a cross-section of a micro-optic system exemplifying one embodiment of the present disclosure providing orthoparallactic movement of the images of the system.
b is an isometric cutaway view of the embodiment of
a illustrates an orthoparallactic synthetic image motion effect of the embodiment of
b-c illustrate the visual effects of the Deep and Float embodiments of the present system.
d-f illustrate the visual effects obtained by rotation of a Levitate embodiment of the present system.
a-i are plan views showing various embodiments and fill-factors of different patterns of symmetric two dimensional arrays of lenses of the present system.
a-c are plan views illustrating how the synthetic magnification of the icon images can be controlled by the relative angle between the lens array and icon array axes of the present system.
a-c are plan views illustrating an embodiment accomplishing a morphing effect of synthetically magnified images of the present system.
a-c are cross-sections showing various embodiments of the icon layer of the present system.
a-b are plan views illustrating both ‘positive’ and ‘negative’ icon element embodiments.
a-b are cross-section views showing reflective optics and pinhole optics embodiments of the present system.
a-b are cross-section views comparing the structures of an all-refractive material embodiment with a hybrid refractive/reflective material embodiment.
a-d are cross-section views showing various embodiments of two-sided systems.
a-f are cross-section views and corresponding plan views illustrating three different methods for creating grayscale or tonal icon element patterns and subsequent synthetically magnified images by the present system.
a-d are cross-section views showing the use of the present system in conjunction with printed information.
a-f are cross-section views illustrating the application of the present system to, or incorporation into, various substrates and in combination with printed information.
a-b are cross-section views comparing the in-focus field of view of a spherical lens with that of a flat field aspheric lens when each are incorporated into the present system.
a-c are cross-section views illustrating two benefits of utility which result from the use of a thick icon layer in the present system.
a illustrates use of the present system to create combined synthetic images that are smaller in dimension than the smallest feature of the individual synthetic images.
b illustrates use of the present system to create narrow patterns of gaps between icon image elements.
a,b illustrate alternate embodiments of microstructured icon elements.
a,b illustrate the microstructured icon elements of
a,b illustrate the microstructured icon elements of
a-c illustrate positive and negative icon elements.
a-c illustrate the combination of filled and coated microstructured icon elements.
a-c illustrate the application and combination of patterned coating materials to the microstructured icon elements of
a-c illustrate the use of a patterned coating material to create icon image elements.
a,b illustrate a “lock and key” embodiment of the micro-optic system disclosed herein.
a,b illustrate an immersible embodiment of the micro-optic system disclosed herein.
a,b illustrate alternate embodiment of the immersible embodiment of
a-f illustrate a method of creating filled microstructured icon elements for use in an embodiment of the present micro-optic system.
Reference is now made in detail to the description of the embodiments as illustrated in the figures. While several embodiments are described in connection with these figures, there is no intent to limit the invention to the embodiment or embodiments disclosed herein. On the contrary, the intent is to cover all alternatives, modifications, and equivalents.
In the interest of brevity and to avoid repetitive explanations, all subsequent references to the following terms are to be understood as defined, explained, and detailed herein. For convenience, the defined terms are subsequently printed in bold upon their first instance of use within the description of a particular embodiment.
Icon fill material—any material used to fill micro-structured icon elements. Icon fill material may be a gas, liquid, gel, powder, solid, an emulsion, suspension, a composite material, and combinations thereof. Icon fill material typically provides some properties that are measurably or detectably different than the surrounding icon layer material. These different properties may provide optical effects or they may provide properties that enable non-contact detection or authentication of the material, or both. Combinations of materials can be used for icon fill materials to provide a multiplicity of desirable icon element properties.
Material properties of icon fill materials that may produce desirable optical effects include, but are not limited to: transparency, opacity, refractive index, chromatic dispersion, scattering properties, pearlescence, opalescence, iridescence, color reflection and color absorption, reflectivity, linear, circular, and elliptical polarizing properties, Raman or Rayleigh properties, optical rotation, fluorescence, luminescence, phosphorescence, two-photon effects, thermochromicity, piezochromicity, photochromicity, triboluminescence, electroluminescence, electrochromicity, and magnetochromicity. Icon fill materials may obtain these properties as pure materials or as mixtures, compounds, suspensions, or other combinations of a multiplicity of materials.
Material properties of icon fill materials that may produce desirable non-contact detection or authentication properties include, but are not limited to: magnetic reactivity, magnetization, electric charge separation, electrical reactivity, electrical conductivity, thermal conductivity, dielectric strength, fluorescence, luminescence, phosphorescence, two-photon effects, nuclear magnetic resonance, transparency, opacity, refractive index, chromatic dispersion, scattering properties, pearlescence, opalescence, iridescence, color reflection and color absorption, reflectivity, linear, circular, and elliptical polarizing properties, Raman or Rayleigh properties, radioactivity, radioactivation, optical rotation, fluorescence, luminescence, phosphorescence, two-photon effects, thermochromicity, piezochromicity, photochromicity, triboluminescence, electroluminescence, electrochromicity, and magnetochromicity.
Icon fill material can preferably include carrier material, such as monomer, oligomer, or polymer materials, and combinations thereof, that is solvent cured, thermally cured, oxidation cured, reaction cured, or radiation cured. An exemplary radiation cured photopolymer is Lord Industries U107 photopolymer.
The optical, non-contact detection, and non-contact authentication properties of the icon fill carrier material can be modified by mixing or combining it with any of the following (for example, but not limited to these materials): dyes, coloring agents, pigments, powdered materials, inks, powdered minerals, magnetic materials and particles, magnetized materials and particles, magnetically reactive materials and particles, phosphors, liquid crystals, liquid crystal polymers, carbon black or other light absorbing materials, titanium dioxide or other light scattering materials, photonic crystals, non-linear crystals, nanoparticles, nanotubes, buckeyballs, buckeytubes, organic materials, pearlescent materials, powdered pearls, multilayer interference materials, opalescent materials, iridescent materials, low refractive index materials or powders, high refractive index materials or powders, diamond powder, structural color materials, polarizing materials, polarization rotating materials, fluorescent materials, phosphorescent materials, thermochromic materials, piezochromic materials, photochromic materials, tribolumenscent materials, electroluminescent materials, electrochromic materials, magnetochromic materials and particles, radioactive materials, radioactivatable materials, electret charge separation materials, combinations thereof. An exemplary icon fill material includes a photopolymer carrier, such as Lord Industries U107, that is ground with a submicron pigment powder to form a thick “ink”.
Other properties, materials, methods, means, and combinations thereof not explicitly taught here are understood to be included in the scope of this invention as they would be obvious to a worker skilled in the art.
Coating material—any material used to coat an icon layer or icon fill material, or to coat any layer of a moiré magnification system, including but not limited to the lenses, the icon plane, the icon layer, microstructured icon elements, icon fill material, or to any layer(s) of materials deposited, laminated, or applied to the lenses, the icon layer, or any layer internal or external to the lenses, icon layer, substrate, or transparent substrate.
Coating materials typically provide some properties that are detectably different from the properties of the other materials in the icon layer, icon fill material, substrate, transparent substrate, or lens layer. These different properties may provide optical effects or they may provide properties that enable non-contact detection or authentication of the material, or both. Combinations of materials can be used for coating materials to provide a multiplicity of desirable coating material properties.
Material properties of coating materials that may produce desirable optical effects include, but are not limited to: transparency, opacity, refractive index, chromatic dispersion, scattering properties, pearlescence, opalescence, iridescence, color reflection and color absorption, reflectivity, linear, circular, and elliptical polarizing properties, Raman or Rayleigh properties, optical rotation, fluorescence, luminescence, phosphorescence, two-photon effects, thermochromicity, piezochromicity, photochromicity, triboluminescence, electroluminescence, electrochromicity, and magnetochromicity. Coating materials may obtain these properties as pure materials or as mixtures, compounds, suspensions, or other combinations of a multiplicity of materials.
Suitable methods for applying coating materials depend on many factors, including the material properties and the desired function or effect of the material. Metals, metal oxides, semiconductor coatings, and combinations thereof may be applied by wet reduction reactions (as in wet silvering), electro-less plating, electroplating, vapor deposition, sputtering, plasma spraying, molecular beam epitaxy, hot stamping, foil transfer, laminating and other suitable and well known means and combinations thereof. Coating materials incorporating a liquid carrier material may be applied by wet coating, spraying, printing, laminating, chemical reaction at the icon surface, inkjet, electro printing, dipping, meniscus coating, wave coating, reactive coating and other suitable and well known means and combinations thereof. Film or foil based coating materials can be applied by hot stamping, foil transfer, lamination and other suitable and well known means and combinations thereof.
Coating materials may preferably be an evaporated or sputtered metal, such as aluminum, gold, or silver, or metal oxides, such as indium-tin-oxide or iron oxide. Coating materials incorporating a fill material may preferably include carrier material, such as monomer, oligomer, or polymer materials, and combinations thereof, that is solvent cured, thermally cured, oxidation cured, reaction cured, or radiation cured. An exemplary radiation cured photopolymer is Lord Industries U107 photopolymer.
The optical, non-contact detection, and non-contact authentication properties of a coating carrier material can be modified by mixing or combining it with any of the following (for example, but not limited to these materials): dyes, coloring agents, pigments, powdered materials, inks, powdered minerals, magnetic materials and particles, magnetized materials and particles, magnetically reactive materials and particles, phosphors, liquid crystals, liquid crystal polymers, carbon black or other light absorbing materials, titanium dioxide or other light scattering materials, photonic crystals, non-linear crystals, nanoparticles, nanotubes, buckeyballs, buckeytubes, organic materials, pearlescent materials, powdered pearls, multilayer interference materials, opalescent materials, iridescent materials, low refractive index materials or powders, high refractive index materials or powders, diamond powder, structural color materials, polarizing materials, polarization rotating materials, fluorescent materials, phosphorescent materials, thermochromic materials, piezochromic materials, photochromic materials, tribolumenscent materials, electroluminescent materials, electrochromic materials, magnetochromic materials and particles, radioactive materials, radioactivatable materials, electret charge separation materials, combinations thereof. An exemplary coating material includes a photopolymer carrier, such as Lord Industries U107, that is ground with a submicron pigment powder to form a thick “ink”.
Coating materials may also be selected to provide physical, chemical, mechanical, priming, or adhesion promoting properties.
Other properties, materials, methods, means, and combinations thereof not explicitly taught here are understood to be included in the scope of this invention as they would be obvious to a worker skilled in the art.
Positive icon element—A graphical element of an icon design or pattern wherein object patterns of the icon element, such as characters or logos, are pigmented, colored, metallized, or otherwise distinguished from the background of the icon element. In general, in the process of manufacturing, the object patterns of a positive icon element will obtain its distinguishing properties prior to any distinguishing properties obtained or applied to the background of a positive icon element.
Positive image—The image or synthetic image formed by positive icon elements.
Negative icon element—A graphical element of an icon design or pattern wherein the background of the icon element is pigmented, colored, metallized, or otherwise distinguished from the object patterns of the icon element, such as characters or logos. In general, in the process of manufacturing, the background of a negative icon element will obtain its distinguishing properties prior to any distinguishing properties obtained or applied to the object patterns of a negative icon element
Negative image—The image or synthetic image formed by negative icon elements.
Object patterns of (the/an) icon element—The discrete and bounded graphical elements of an icon design or pattern, such as characters or logos. In general, object patterns of an icon element are preferably bounded within one, two, or three icon elements or patterns, but may be bounded with more.
Background of (the/an) icon element—The unbounded regions of an icon design or pattern that surround the object patterns. In general, the background of an icon element or patterns is continuous across multiple icon elements or patterns.
Icon layer—A substantially planar layer of micro-printing that may be applied to a face of a substrate or transparent substrate or may be a free-standing layer. A wide variety of materials can be used for the icon layer, including but not limited to thermoset polymers, thermoformable polymers, cast polymers, reactive cast polymers, radiation cured polymers, biopolymers, gelatines, starches, sugars, silicone polymers, multilayer dielectric polymer films, solvent cast polymers, compression molded polymers, injection molded polymers, embossed polymers, glasses, metal oxides, diamond, aluminum oxide, photopolymers, photoresists, printed ink or patterned coatings, ink-jet printed coatings, electro-printed coatings, and combinations thereof.
An exemplary icon layer material is a photopolymer, such as Lord Industries U107 photopolymer. An icon layer can be a single material or it can incorporate dyes, coloring agents, pigments, powdered materials, inks, powdered minerals, magnetic materials and particles, magnetized materials and particles, magnetically reactive materials and particles, phosphors, liquid crystals, liquid crystal polymers, carbon black or other light absorbing materials, titanium dioxide or other light scattering materials, photonic crystals, non-linear crystals, nanoparticles, nanotubes, buckeyballs, buckeytubes, organic materials, pearlescent materials, powdered pearls, multilayer interference materials, opalescent materials, iridescent materials, low refractive index materials or powders, high refractive index materials or powders, diamond powder, structural color materials, polarizing materials, polarization rotating materials, fluorescent materials, phosphorescent materials, thermochromic materials, piezochromic materials, photochromic materials, tribolumenscent materials, electroluminescent materials, electrochromic materials, magnetochromic materials and particles, radioactive materials, radioactivatable materials, electret charge separation materials, combinations thereof, and other suitable materials that can enhance or alter its optical, electrical, magnetic, nuclear magnetic resonance, or other physical properties.
An exemplary icon layer material is Lord Industries U107 photopolymer. Other properties, materials, methods, means, and combinations thereof not explicitly taught here are understood to be included in the scope of this invention as they would be obvious to a worker skilled in the art.
Microstructured icon image elements—Icon elements having a physical relief or microstructure that can be formed in an icon layer by many suitable means, including thermoforming, casting, compression molding, injection molding, embossing, patterned radiation exposure and development, laser exposure and development, ink-jet printing, electro printing, printing, engraving, electroforming, ruling, photographic, holographic, and laser exposure of a photosensitive emulsion combined with well-known hardening and etching or swelling processes, masking and deposition processes, masking and chemical etching, masking and reactive ion etching, masking and ion beam milling, micromachining, laser machining and laser ablation, photopolymer exposure and development, and other suitable means and combinations thereof.
Microstructured image elements are preferably formed by casting a liquid photopolymer between a polymer substrate (usually PET) and a nickel microstructured icon image elements tool, radiation curing said photopolymer, and peeling said polymer substrate with the attached cured photopolymer from said nickel microstructured icon image elements tool.
Other properties, materials, methods, means, and combinations thereof not explicitly taught here are understood to be included in the scope of this invention as they would be obvious to a worker skilled in the art.
Microstructured icon image elements tooling and methods—Tooling and methods used to form microstructured icon image elements into an icon layer by thermoforming, casting, compression molding, injection molding, embossing, patterned radiation exposure and development, electroforming, and photopolymer exposure and development. Said tooling can be created by many similar and suitable means, including thermoforming, casting, compression molding, injection molding, embossing, patterned radiation exposure and development, laser exposure and development, ink-jet printing, electro printing, printing, engraving, electroforming, ruling, photographic, holographic, and laser exposure of a photosensitive emulsion combined with well-known hardening and etching or swelling processes, masking and deposition processes, masking and chemical etching, masking and reactive ion etching, masking and ion beam milling, micromachining, laser machining and laser ablation, photopolymer exposure and development, and other suitable means and combinations thereof.
Microstructured icon image elements tooling is preferably produced by the well known methods of generation of an original microstructure by optical exposure and development of a photoresist material on a rigid substrate or a rigid transparent substrate, conductive metallization of the microstructured photoresist surface, and nickel electroforming onto the conductive surface.
Other properties, materials, methods, means, and combinations thereof not explicitly taught here are understood to be included in the scope of this invention as they would be obvious to a worker skilled in the art.
Transparent substrate—Any substantially planar and substantially optically transparent material, including, but not limited to glass, metal oxides, polymers, composite material, biopolymers, sugars, celluloses, starches, gelatines and combinations thereof that is used to support the optical elements of a Unison moiré magnification system, said optical elements optionally including a microlens array and one or more icon image arrays. PET polymer film is an exemplary substrate for the icon layers and moiré magnification systems of this invention.
Other properties, materials, methods, means, and combinations thereof not explicitly taught here are understood to be included in the scope of this invention as they would be obvious to a worker skilled in the art.
Substrate—Any substantially planar material, including, but not limited to glass, metals, composite materials, metal oxides, polymers, biopolymers, sugars, cellulose, starches, gelatins, paper, fibrous materials, non-fibrous materials, foils, non-woven paper substitutes and combinations thereof. PET polymer film is an exemplary substrate for this invention.
Other properties, materials, methods, means, and combinations thereof not explicitly taught here are understood to be included in the scope of this invention as they would be obvious to a worker skilled in the art.
Conformal coating material—A coating material that conforms to the shape of the surface it is applied to. A sputtered metal coating is typically conformal—it coats vertical surfaces, micro-structure sidewalls, and undercut areas as well as horizontal surfaces.
Non-conformal coating material—A coating material that does not conform to the shape of the surface it is applied to. An evaporated metal coating is typically non-conformal—it preferentially coats horizontal surfaces but poorly coats vertical surfaces and micro-structure sidewalls and does not coat undercut areas.
Directional coating material—A coating material that preferentially coats horizontal surfaces and surfaces with a surface normal that points in the general direction of the coating source but does not coat surfaces with a surface normal that points in a general direction away from the coating source. An offset or baffled evaporated metal coating is one example of a directional coating material: the stream of metal vapor is directed at the surface at an angle substantially off-normal, causing the “near” surfaces of microstructures to be coated, but the “far” surfaces of microstructures to be shadowed and uncoated.
Referring now to the drawings,
The system 12 micro-lenses 1 that have at least two substantially equal axes of symmetry and that are arranged in a two-dimensional periodic array. Lens diameter 2 is preferably less than 50μ and the interstitial space between lenses 3 is preferably 5μ or less. (We use the terms “μ” and “μm” interchangeably to mean the same measurement). Micro-lens 1 focuses an image of icon element 4 and projects this image 10 toward a viewer. The system is commonly used in situations having normal levels of ambient lighting, so the illumination of the icon images arises from reflected or transmitted ambient light. Icon element 4 is one element of a periodic array of icon elements having periods and dimensions substantially similar to those of the lens array including lens 1. Between the lens 1 and the icon element 4 is an optical spacer 5, which may be contiguous with the lens 1 material or may optionally be a separate substrate 8—in this embodiment the lenses 9 are separate from the substrate. The icon elements 4 may be optionally protected by a sealing layer 6, preferably of a polymer material. Sealing layer 6 may be transparent, translucent, tinted, pigmented, opaque, metallic, magnetic, optically variable, or any combination of these that provide desirable optical effects and/or additional functionality for security and authentication purposes, including support of automated currency authentication, verification, tracking, counting and detection systems, that rely on optical effects, electrical conductivity or electrical capacitance, magnetic field detection.
The total thickness 7 of the system is typically less than 50μ; the actual thickness depends on the F# of the lenses 1 and the diameter of the lenses 2, and the thickness of additional security feature or visual effect layers. The repeat period 11 of the icon elements 4 is substantially identical to the repeat period of the lenses 1; the “scale ratio”, the ratio of the repeat period of the icons to the repeat period of the lenses, is used to create many different visual effects. Axially symmetric values of the scale ratio substantially equal to 1.0000 result in Unison Motion orthoparallactic effects when the symmetry axes of the lenses and the icons are misaligned, axially symmetric values of the scale ratio less than 1.0000 result in Unison Deep and Unison SuperDeep effects when the symmetry axes of the lenses and the icons are substantially aligned, and axially symmetric values of the scale ratio greater than 1.0000 result in Unison Float and Unison SuperFloat effects when the symmetry axes of the lenses and the icons are substantially aligned. Axially asymmetric values of the scale ratio, such as 0.995 in the X direction and 1.005 in the Y direction, result in Unison Levitate effects.
Unison Morph effects can be obtained by scale distortions of either or both the lens repeat period and the icon repeat period, or by incorporating spatially varying information into the icon pattern. Unison 3-D effects are also created by incorporating spatially varying information into the icon pattern, but in this embodiment the information represents different viewpoints of a three dimensional object as seen from specific locations substantially corresponding to the locations of the icons.
b presents an isometric view of the present system, as depicted in cross-section in
In the case of the Unison (orthoparallactic motion) material embodiment of
The Motion synthetic images produced by a particular combination of lenses, optical spacer(s), and icons move a consistent amount for a given change in viewing angle, and this consistent amount is a percentage of the synthetic image repeat distance. For example, if a Unison Motion material is produced that presents synthetic images having a 0.25 inch repeat distance and these synthetic images appear to have 0.1 inch of orthoparallactic movement when the angle of view changes by 10 degrees, then the same lenses, icons, and spacer(s) used to create Unison that has a synthetic image repeat distance of 1.0 inch will exhibit a proportionally larger orthoparallactic movement—0.4 inch—when the angle of view changes by 10 degrees. The amount of orthoparallactic image movement is scaled to match the repeat distance of the synthetic image produced. The relationship between the change in the angle of view and the scaled orthoparallactic movement depends on the F# of the lenses used. Low F# lenses produce a smaller amount of orthoparallactic movement for a selected change in viewing angle than larger F# lenses.
An exemplary lens used for a Unison Motion material may have an F# of 0.8. One reason that this is a desirable F# is that it minimizes vertical disparity between the images seen with by left eye and those seen by the right eye of the observer. Vertical disparity is a vertical misalignment between the left eye and right eye images—one image appears to be vertically displaced with respect to the other image. Horizontal image disparity is a familiar and natural phenomenon: it is one of the factors used by the eye-brain system to perceive three dimensional depth. Vertical image disparity is not normally encountered by people—it may sometimes be seen in binoculars or binocular microscopes if their optics are out of alignment. While horizontal image disparity is a continuous occurrence for people with sight in both eyes, vertical image disparity is never encountered in the natural world, so humans have very limited capacity to adapt to vertical image disparity. Such adaptation requires that one eye point slightly upward or downward with respect to the other eye. This is an unnatural experience and, while it will not harm a person, it causes an immediate physical sensation in the viewer's eyes as a result of the unaccustomed eye muscle action. This physical sensation has been described in various ways, from “it makes my eyes feel weird” to “it's hard for me to look at”. The effect is present regardless of the azimuthal direction of view (ie: the Unison Motion material can be rotated to any angle within its plane without any loss of the effect). No conventional printing of any kind causes this physical sensation in the viewer's eyes.
Unison Motion materials can be designed to elicit this sensation in the viewer by enhancing the vertical disparity of the images. Vertical image disparity is present in Unison Motion materials because the viewer's eyes are disposed in a horizontal plane. The view from the left eye is from a different horizontal angle than the view from the right eye, so the synthetic image seen by the left eye is orthoparallactically displaced in a vertical direction with respect to the synthetic image seen by the right eye, thus creating vertical image disparity. The amount of vertical image disparity is small for low F# lenses and is usually unnoticed by viewers. The vertical image disparity can be enhanced, however, by using larger F# lenses, such as F# 2.0 or larger, so as to purposefully create the vertical disparity sensation in the viewer's eyes.
One benefit that can be obtained by creating enhanced vertical image disparity in Unison Motion materials is that the physical sensation thus elicited in the viewer is unique, immediate, and automatic, and can therefore function as a novel authentication method. No other known material can provide a similar sensation from all azimuthal directions of view.
The synthetic magnification factor of Unison Deep, Unison Float, and Unison Levitate embodiments depends on the angular alignment of the lens 1 axes and the icon elements 4 axes as well as the scale ratio of the system. When the scale ratio is not equal to 1.0000 the maximum magnification obtained from substantial alignment of these axes is equal to the absolute value of 1/(1.0000−(scale ratio)). Thus a Unison Deep material having a scale ratio of 0.995 would exhibit a maximum magnification of |1/(1.000−0.995)=200×. Similarly, a Unison Float material having a scale ratio of 1.005 would also exhibit a maximum magnification of |1/(1.000−1.005)|=200×. In a manner similar to the Unison Motion material embodiment, slight angular misalignment of the lens 1 axes and icon elements 4 axes of the Unison Deep, Unison Float, and Unison Levitate embodiments reduces the magnification factor of the synthetic images of the icon elements and causes the magnified synthetic images to rotate.
The synthetic image produced by a Unison Deep or SuperDeep icon pattern is upright with respect to the orientation of the Unison Deep or SuperDeep icon pattern, while the synthetic image produced by a Unison Float or SuperFloat icon pattern is upside down, rotated one hundred and eighty degrees (180°) with respect to the orientation of the Unison Float or Super Float icon pattern.
a schematically depicts the counter-intuitive orthoparallactic image motion effects seen in the Unison Motion embodiment. The left side of
The visual effects of the Unison Deep and Unison Float embodiments are isometrically depicted in
The Unison Levitate embodiment effect is illustrated in
The visual effect of a Unison Levitate image 38 moving from beneath the Unison Levitate material 36 (
When a Unison material is illuminated by a strongly directional light source such as a ‘point’ light source (ex: a spotlight or an LED flashlight) or a collimated source (ex: sunlight), “shadow images” of the icons may be seen. These shadow images are unusual in many ways. While the synthetic image presented by Unison does not move as the direction of illumination is moved, the shadow images produced do move. Furthermore, while the Unison synthetic images may lie in different visual planes than the plane of the material, the shadow images always lie in the plane of the material. The color of the shadow image is the color of the icon. So black icons create black shadow images, green icons create green shadow images, and white icons create white shadow images.
The movement of the shadow image as the angle of illumination moves is tied to the specific depth or motion Unison effect in a way that parallels the visual effect present in the synthetic image. Thus the movement of a shadow image as the angle of the light is altered parallels the movement that the synthetic image shows when the angle of view is altered. In particular:
Unison Morph shadow images show morphing effects as the light source is moved.
Additional unusual shadow image effects are seen when a diverging point light source, such as an LED light, is moved toward and away from a Unison film. When the light source is further away its diverging rays more closely approximate collimated light, and the shadow images produced by Deep, SuperDeep, Float, or SuperFloat Unison synthetic images appear approximately the same size as the synthetic images. When the light is brought closer to the surface the shadow images of Deep and SuperDeep materials shrink because the illumination is strongly divergent, while the shadow images of Float and SuperFloat materials expand. Illuminating these materials with converging illumination causes Deep and SuperDeep shadow images to enlarge to a size greater than the synthetic images, while Float and SuperFloat shadow images shrink.
The shadow images of Unison motion material do not change scale significantly as the convergence or divergence of illumination is changed, rather, the shadow images rotate about the center of illumination. Unison Levitate shadow images shrink in one direction and enlarge in the perpendicular direction when the convergence or divergence of the illumination is changed. Unison Morph shadow images change in ways specific to the particular Morph pattern as the convergence or divergence of the illumination is changed.
All of these shadow image effects can be used as additional authentication methods for Unison materials utilized for security, anti-counterfeiting, brand protection applications, and other similar applications.
a-i are plan views showing various embodiments and fill-factors of different patterns of symmetric two-dimensional arrays of micro-lenses.
The lens patterns of
Lenses having a low F# are particularly suitable for use in the present system. By low F# we mean an F# equivalent to 4 or less, and in particular for Unison Motion approximately 2 or lower. Low F# lenses have high curvature and a correspondingly large sag, or center thickness, as a proportion of their diameter. A typical Unison lens, with an F# of 0.8, has a hexagonal base 28 microns wide and a center thickness of 10.9 microns. A typical Drinkwater lens, with a diameter of 50 microns and a focal length of 200 microns, has an F# of 4 and a center thickness of 3.1 microns. If scaled to the same base size, the Unison lens has a sag almost six times larger than the Drinkwater lens.
We have discovered that polygonal base multi-zonal lenses, for example hexagonal base multi-zonal lenses, have important and unexpected advantages over circular base spherical lenses. As explained above, hexagonal base multi-zonal lenses significantly improve manufacturability by virtue of their stress-relieving geometry, but there are additional unexpected optical benefits obtained through the use of hexagonal base multi-zonal lenses.
We refer to these lenses as multi-zonal because they possess three optical zones that each provide a different and unique benefit to the subject invention. The three zones are the central zone (constituting approximately half of the area of the lens), the side zones, and the corner zones. These polygonal lenses have an effective diameter that is the diameter of a circle drawn inside the corner zones around the central zone and including the side zones.
The central zone of the hexagonal base multi-zonal lens of the subject invention has an aspheric form (for example, having the form defined by [y=(5.1316E)×4−(0.01679)×3+(0.124931)×+11.24824] for a 28 micron diameter lens with a nominal 28 micron focal length) that brings light to a focus at least as well as a spherical surface having the same diameter and focal length.
Each of the six side zones 796 of the hexagonal base multi-zonal lens 784 of the subject invention have focal lengths that depend on the location with the zone in a complex way, but the effect is to cause the focus of the side zones 796 to be spread over a range of values 798 spanning approximately +/−10 percent of the central zone focus, as illustrated in
This is particularly important for off-normal viewing: the increased depth of field, and effectively flatter field, mitigates the abrupt image defocus that can occur with a spherical lens when its curved focal surface separates from the icon plane. Consequently, a Unison material using hexagonal base multi-zonal lenses displays synthetic images that fade from focus more softly at higher viewing angles than the equivalent Unison material using spherical lenses. This is desirable because it increases the effective viewing angle of the material and therefore increases its usefulness as a security device or an image presentation device.
The corner zones 806 of the hexagonal base multi-zonal lens 784 of
The benefit obtained from the exemplary hexagonal base multi-zonal lenses is further magnified because hexagonal base multi-zonal lenses have a higher fill factor (ability to cover the plane) than spherical lenses. The interstitial space between spherical lenses provides virtually no scattering of ambient light, while this non-scattering area is much smaller in the case of hexagonal base multi-zonal lenses.
Thus it is seen that even though the focal properties of a hexagonal base multi-zonal lens are inferior to those of a spherical lens as evaluated by conventional optical standards, in the context of the subject invention hexagonal base multi-zonal lenses provide unexpected benefits and advantages over spherical lenses.
Either type of lens can benefit from the addition of scattering microstructures or scattering materials introduced into, or incorporated into, the lens interstitial spaces to enhance the scattering of ambient illumination onto the icon plane. Furthermore, the lens interstitial spaces can be filled with a material that will form a small radius meniscus, with either converging or diverging focal properties, to direct ambient illumination onto the icon plane. These methods may be combined, for example, by incorporating light scattering particles into a lens interstitial meniscus fill material. Alternatively, the lens interstitial zones can be originally manufactured with suitably scattering lens interstitial zones.
A spherical lens having these proportions is very difficult to manufacture because the high contact angle between the surface of the film and the edge of the lens acts as a stress concentrator for the forces applied to separate the lens from the tool during manufacture. These high stresses tend to cause the adhesion of the lens to the film to fail and to failure of removal of the lens from the tool. Furthermore, the optical performance of a low F# spherical lens is progressively compromised for radial zones away from the center of the lens: low F# spherical lenses do not focus well except near their central zone.
Hexagonal base lenses have an unexpected and significant benefit over lenses that have a more substantially circular base: hexagonal lenses release from their tools with lower peeling force than the optically equivalent lenses with substantially circular bases. Hexagonal lenses have a shape that blends from substantially axially symmetric near their center to hexagonally symmetric, with corners that act as stress concentrators, at their bases. The stress concentrations caused by the sharp base corners reduce the overall peeling force required to separate the lenses from their molds during manufacturing. The magnitude of this effect is substantial—the peeling forces can be reduced during manufacturing by a factor of two or more for hexagonal base lenses as compared to substantially circular base lenses.
The image contrast of the material can be enhanced by filling the lens interstitial spaces with a light absorbing (dark colored) opaque pigmented material, effectively forming a mask for the lenses. This eliminates the contrast reduction that arises from light scattered from the icon layer through the lens interstitial spaces. An additional effect of this interstitial fill is that the overall image becomes darker because incoming ambient illumination is blocked from passing through the interstitial spaces to the icon plane. The image clarity produced by lenses having aberrant focusing at their periphery can also be improved by an opaque pigmented interstitial fill, providing that this fill occludes the aberrant peripheral lens zone.
A different effect can be obtained by filling the lens interstitial spaces with a white or light colored material, or a material color matched to a substrate to be used with the Unison material. If the light colored lens interstitial fill is dense enough and the icon plane incorporates a strong contrast between the icon elements and the background, the Unison synthetic image will be substantially invisible when viewed with reflected light, yet will be distinctly visible when viewed in transmitted light from the lens side, but not visible when viewed from the icon side. This provides the novel security effect of having a one-way transmission image that is visible only in transmitted light and visible only from one side.
Fluorescing materials can be utilized in a lens interstitial coating instead of, or in addition to, visible light pigments to provide additional means of authentication.
Adjacent to this is zone 70 in which the SSR is ramped from 0.995 up to 1.005, producing a spatial transition from a Unison Deep to a Unison Float effect. The SSR in the next zone 72 is 1.005 creating a Unison Float effect. The next zone 74 creates a smooth transition down from a Unison Float effect to a Unison Deep effect. Zone 76 proceeds stepwise up from a Unison Deep effect, to OPM, to a Unison Float effect, and zone 78 steps it back down to OPM. The variations in repeat period needed to accomplish these effects are generally most easily implemented in the icon element layer. In addition to varying the SSR in each zone, it may be desirable to vary the rotational angle of each zone of the arrays, preferably within the icon element array, to keep the synthetically magnified images substantially similar in size.
The easiest way to interpret this graph is to see it as a cross-section of the stereoscopic depth that will be perceived across this axis of a piece of system material. It is therefore possible to create a stereoscopically sculpted field of images, a contoured visual surface, by local control of the SSR and optionally by corresponding local control of the array rotational angle. This stereoscopically sculpted surface can be used to represent an unlimited range of shapes, including human faces. A pattern of icon elements that create the effect of a stereoscopically sculpted grid, or periodic dots, can be a particularly effective way to visually display a complex surface.
a-c are plan views depicting the effect of rotating one array pattern with respect to the other in the production of material of the present system.
a-c illustrate a method for causing one synthetically magnified OPM image 98 to morph into another synthetically magnified image 102 as the first image moves across a boundary 104 in the icon element patterns 92 and 94. Icon element pattern 92 bears circle-shaped icon elements 98, shown in the magnified inset 96. Icon element pattern 94 bears star-shaped icon elements 102, shown in the magnified inset 100. Icon element patterns 92 and 94 are not separate objects, but are joined at their boundary 104. When the material is assembled using this combined pattern of icon elements the resulting OPM images will show the morphing effects depicted in
a-c are cross-sections of materials of the present system that illustrate alternative embodiments of the icon elements.
b depicts a similar material system with a different embodiment of icon elements 112. In this embodiment the icon elements are formed from pigments, dyes, or particles embedded in a supporting material 110. Examples of this embodiment of icon elements 112 in supporting material 110 include: silver particles in gelatin, as a photographic emulsion, pigmented or dyed ink absorbed into an ink receptor coating, dye sublimation transfer into a dye receptor coating, and photochromic or thermochromic images in an imaging film.
c depicts a microstructure approach to forming icon elements 114. This method has the benefit of almost unlimited spatial resolution. The icon elements 114 can be formed from the voids in the microstructure 113 or the solid regions 115, singly or in combination. The voids 113 can optionally be filled or coated with another material such as evaporated metal, material having a different refractive index, or dyed or pigmented material.
a,b depict positive and negative embodiments of icon elements.
a,b are cross-sections illustrating non-refractive embodiments of the present system.
a,b are cross-sections comparing the structures of an all-refractive material 188 with a hybrid refractive/reflective material 199.
This embodiment of a tamper indicating material is well suited to application as a tape or label applied to an article. Tampering releases the top layer 232, leaving the second system 230 attached to the article. Prior to tampering, this embodiment presents a first image 248. After tampering 254 the second system 230, still attached to the article, presents a second image 258 while the peeled layer 256 presents no image at all. Effects of each of the above described embodiments, OPM, Deep, Float, and Levitate, can be included in either the first system 232 or the second system 230.
Note that an alternative embodiment accomplishing a similar effect to that of
a-d are cross-sections showing various two-sided embodiments of the present system.
b illustrates another two-sided embodiment 272 having two icon planes 276 and 278 that are imaged, 282 and 286 respectively, by two sets of lenses, 274 and 280 respectively. This embodiment is essentially two separate systems, 287 and 289, such as illustrated in
c shows yet another two-sided material 290 having a pigmented icon layer spacer 298 that blocks the lenses on one side of the material from seeing the ‘wrong’ set of icons. Lenses 292 image 294 icon layer 296 but cannot image icon layer 300 because of the presence of pigmented icon layer 298. Similarly, lenses 302 image 304 icon layer 300, but cannot image icon layer 296 because of the presence of pigmented icon layer 298. Effects of each of the above described embodiments, OPM, Deep, Float, and Levitate, can be displayed from either side of a two-sided material according to this embodiment, and the projected images 294 and 304 can be of the same or different colors.
d discloses a further two-sided material 306 embodiment having lenses 308 that image 318 icon layer 314 and lenses 316 on the opposite side that image 322 icon layer 310. Icon layer 310 is close to, or substantially in contact with, the bases of lenses 308 and icon layer 314 is close to, or substantially in contact with, the bases of lenses 316. Icons 310 are too close to lenses 308 to form an image, so their light scatters 320 instead of focusing. Icons 314 are too close to lenses 316 to form an image, so their light scatters 324 instead of focusing. Effects of each of the above described embodiments, OPM, Deep, Float, and Levitate, can be displayed from either side of a two-sided material according to this embodiment, and the projected images 318 and 322 can be of the same or different colors.
a-f are cross-sections and corresponding plan views illustrating three different methods for creating grayscale or tonal icon element patterns and subsequent synthetically magnified images with the present system.
a includes icon element 313, dyed or pigmented icon element fill 323, and corresponding plan view 337. The cross section view of the icon plane at the top of this figure can only show one cutting plane through the icon elements. The location of the cutting plane is indicated by the dashed line 319 through the plane views 337, 339, and 341. Accordingly, the cross-section of icon element 313 is one plane through a substantially hemispherical-shaped icon element. By suitably limiting the overall dye or pigment density of the fill 323, thickness variations of the dyed or pigmented fill 323 create a tonal, or grayscale, optical density variations represented in the plan view 337. An array of icon elements of this type can be synthetically magnified within the present material system to produce images that show equivalent grayscale variations.
b includes icon element 315, dyed or pigmented icon element fill 325, and corresponding plan view 339. Plan view 339 shows that the icon element 315 is a bas-relief representation of a face. The tonal variations in an image of a face are complex, as shown by the complex thickness variations 325 in the cross-section view. As disclosed with regard to icon element 313, an array of icon elements of this type, as shown by 315, 325, and 339, can be synthetically magnified within the present material system to produce images that show equivalent grayscale variations representing, in this example, the image of a face.
c includes icon element 317, dyed or pigmented fill 327, and corresponding plan view 341. In a manner similar to the discussion of
d,e disclose another embodiment 326 of transparent bas-relief micro structured icon layer 311 including icon elements 329 and 331 that are coated with a high refractive index material 328. The icon layer 311 can be sealed with an optional sealing layer 321 that fills the icon elements 329 and 331, 330 and 332, respectively. The high refractive index layer 328 enhances the visibility of sloping surfaces by creating reflections from them by total internal reflection. Plan views 342 and 344 present representative images of the appearance of icon elements 329 and 331 and their synthetically magnified images. This high refractive index coating embodiment provides a kind of edge-enhancement effect without adding pigment or dye to make the icons and their images visible.
f discloses yet another embodiment 333 of transparent bas-relief micro structured icon 335 utilizing an air, gas, or liquid volume 336 to provide visual definition for this phase interface 334 microstructure. Optional sealing layer 340 may be added with or without optional adhesive 338 to entrap the air, gas, or liquid volume 336. The visual effect of a phase interface icon element is similar to that of a high refractive index coated icon element 329 and 331.
a-d are cross-sections showing the use of the present system as a laminating film in conjunction with printed information, such as may be utilized in the manufacture of I.D. cards and driver's licenses, wherein the material 348 (consisting of the coordinated micro-array of lenses and images described above) covers a substantial proportion of the surface.
b shows an embodiment of the system material used as a laminate over a print element 352 applied to a nonfibrous substrate 358, such as a polymer film. As in
c depicts the use of a print element directly on the lens side of material 360. In this embodiment material 348 has print element 352 directly applied to the upper lens surface. This embodiment does not require that the material be at least partly transparent: the print element 352 lies on top of the material and the dynamic image effects can be seen around the print element. In this embodiment the material 348 is used as the substrate for the final product, such as currency, ID cards, and other articles requiring authentication or providing authentication to another article.
d depicts the use of a print element directly on the icon side of an at-least partially transparent material 362. Print element 352 is applied directly to the icon layer or sealing layer of an at-least partially transparent system material 348. Because the system material 348 is at least partially transparent, the print element 352 can be seen through it and the effect of this combination is to provide the dynamic image effect in combination with the static print. In this embodiment the system material 348 is used as the substrate for the final product, such as currency, ID cards, and other articles requiring authentication or providing authentication to another article.
Each of the embodiments of
a-f are cross-sections illustrating the application of the present system to, or incorporation into, various substrates and in combination with printed information. The embodiments of
b illustrates an embodiment of single-sided system material 364 incorporated into an non-optical substrate 378 as a window, wherein at least some of the edges of the system material 364 are captured, covered, or enclosed by the non-optical substrate 378. Print elements 380 may be optionally applied on top of the system material lens surface and these print elements may be aligned with, or correspond to, print elements 382 applied to the non-optical substrate 378 in the area adjacent to print element 380. Similarly, print elements 384 can applied to the opposite side of the non-optical substrate aligned with, or corresponding to, print elements 386 applied to the icon or sealing layer 388 of the system material 364. The effect of a window of this kind will be to present distinct images when the material is viewed from the lens side and no images when viewed from the icon side, providing a one-way image effect.
c shows a similar embodiment to that of
d illustrates a transparent substrate 373 acting as the optical spacer for a material formed by a zone of lenses 374 of limited extent and an icon layer 376 extending substantially beyond the periphery of the zone of lenses 374. In this embodiment the present effects will only be visible in that zone that includes both lenses and icons (corresponding to lens zone 374 in this figure). Both the lenses 374 and the adjacent substrate may optionally be printed 375, and print elements may also be applied to the icon layer 376 or to an optional sealing layer covering the icons (not indicated in this figure—see
e shows an embodiment that is similar to that of
f depicts an embodiment that is similar to
a,b illustrate cross-sectional views comparing the in-focus field of view of a spherical lens with that of a flat field aspheric lens when each are incorporated into a structure of the type described above.
b illustrates an aspheric lens as applied to the present system. As an aspheric lens, its curvature is not approximated by a sphere. Aspheric lens 438 is separated from icon layer 442 by optical spacer 440. Aspheric lens 438 projects image 444 of icon plane 442 normal to the plane of the material. The image originates at focal point 446. The focal length of aspheric lens 438 lies within the icon plane 442 for a wide range of viewing angles, from normal 444 to oblique 448, because it has a flat-field 452. The focal length of the lens varies according to the angle of view through it. The focal length is shortest for normal viewing 444 and increases as the viewing angle becomes more oblique. At the oblique viewing angle 448 the focal point 450 is still within the thickness of the icon plane, and the oblique image is therefore still in focus for this oblique viewing angle 448. The in-focus zone 454 is much larger for the aspheric lens 438 than the in-focus zone 434 of the substantially spherical lens 418. The aspheric lens 438 thus provides an enlarged field of view over the width of the associated image icon so that the peripheral edges of the associated image icon do not drop out of view compared to that of the spherical lens 418. Aspheric lenses are preferred for the present system because of the larger field of view they provide and the resulting increase in visibility of the associated images.
a-c are cross-sections illustrating two benefits of utility which result from the use of a thick icon layer. These benefits apply whether the lens 456 used to view them is substantially spherical 418 or aspheric 438, but the benefits are greatest in combination with aspheric lenses 438.
b illustrates the benefits obtained from the incorporation of an icon plane 471 that is thick 472 in comparison to the field curvature of lens 456. Lenses 456 are separated from thick icon elements 474 by optical spacer 458. Thick icon elements 474 remain in focus 475 over a larger field of view, 55 degrees, than the thin icon elements 462 of
c illustrates yet another advantage of a thick icon plane 492; reducing the sensitivity of the present system material to variations in thickness S that may result from manufacturing variations. Lens 484 is spaced a distance S from the bottom surface of icon layer of thickness i. Lens 484 projects image 496 from focal point 498 disposed at the bottom of icon layer 492. This figure is drawn to demonstrate that variations in the optical space S between the lenses and the icon layer can vary over a range equal to the thickness of the icon layer i without loss of image 496, 500, 504 focus. At lens 486 the optical spacer thickness is about (S+i/2) and the focal point 502 of image 500 is still within the thickness i of icon layer 492. At lens 488 the thickness of the optical spacer has increased to (S+i) 490 and the focal point 506 of image 504 lies at the top of thick icon element 494. The optical spacer thickness can therefore vary over a range corresponding to the thickness of the icon layer i: a thin icon layer therefore provides a small tolerance for optical spacer thickness variations and a thick icon layer provides a larger tolerance for optical spacer thickness variations.
An additional benefit is provided by a thick icon layer 492. Imperfect lenses, such as substantially spherical lenses, may have a shorter focal length 493 towards their edges than at their center 496. This is one aspect of the common spherical aberration defect of substantially spherical lenses. A thick icon layer provides an icon element that can be clearly focused over a range of focal lengths, 498 to 495, thereby improving the overall clarity and contrast of an image produced by a lens 484 having focal length variations.
The thread 508 may be at least partially incorporated in security papers during manufacture by techniques commonly employed in the paper-making industry. For example, thread 508 may be pressed within wet papers while the fibers are unconsolidated and pliable, as taught by U.S. Pat. No. 4,534,398 which is incorporated herein by reference.
The windowed thread of the present system is particularly well suited for application to currency. A typical total thickness for the thread material is in the range of 22μ to 34μ, while the total thickness of currency paper may range as high as 88μ. It is possible to incorporate a windowed security thread of the present system into currency paper without substantially altering the total thickness of the paper by locally reducing the thickness of the paper by an amount equivalent to the thickness of the thread.
In an exemplary embodiment, thread 508 comprises:
(a) one or more optical spacers;
(b) one or more optionally periodic planar arrays of micro-images or icons positioned within, on, or next to an optical spacer; and
(c) one or more optionally periodic planar arrays of non-cylindrical micro lenses positioned on or next to either an optical spacer or a planar icon array, with each micro-lens having a base diameter of less than 50 microns.
In another embodiment, the micro-images or icons constitute filled voids or recesses that are formed on a surface of the one or more optical spacers, while the non-cylindrical micro-lenses are aspheric micro-lenses, with each aspheric micro-lens having a base diameter ranging from about 15 to about 35 microns. At least one pigmented sealing or obscuring layer 516 may be positioned on the planar array(s) of micro-images or icons for increasing contrast and thus visual acuity of the icons and also for masking the presence of thread 508 when the thread is at least partially embedded in a security document.
In yet another embodiment of the present invention, thread 508 comprises:
(a) an optical spacer having opposing upper and lower planar surfaces;
(b) a periodic array of micro-images or icons comprising filled recesses formed on the lower planar surface of the optical spacer;
(c) a periodic array of non-cylindrical, flat field, aspheric or polygonal base multi-zonal micro-lenses positioned on the upper planar surface of the optical spacer, wherein each micro-lens have a base diameter ranging from about 20 to about 30 microns; and
(d) a pigmented sealing or obscuring layer 516 positioned on the icon array.
The optical spacer(s) may be formed using one or more essentially colorless polymers including, but not limited to, polyester, polypropylene, polyethylene, polyethylene terephthalate, polyvinylidene chloride, and the like. In an exemplary embodiment, the optical spacer(s) is formed using polyester or polyethylene terephthalate and has a thickness ranging from about 8 to about 25 microns.
The icon and micro-lens arrays can be formed using substantially transparent or clear radiation curable material including, but not limited to acrylics, polyesters, epoxies, urethanes and the like. Preferably, the arrays are formed using acrylated urethane which is available from Lord Chemicals under the product designation U107.
The icon recesses formed on the lower planar surface of the optical spacer each measures from about 0.5 to about 8 microns in depth and typically 30 microns in micro-image or icon width. The recesses can be filled with any suitable material such as pigmented resins, inks, dyes, metals, or magnetic materials. In an exemplary embodiment, the recesses are filled with a pigmented resin comprising a sub-micron pigment which is available from Sun Chemical Corporation under the product designation Spectra Pac.
The pigmented sealing or obscuring layer 516 can be formed using one or more of a variety of opacifying coatings or inks including, but not limited to, pigmented coatings comprising a pigment, such as titanium dioxide, dispersed within a binder or carrier of curable polymeric material. Preferably, the sealing or obscuring layer 516 is formed using radiation curable polymers and has a thickness ranging from about 0.5 to about 3 microns.
Thread 508, which is described above, may be prepared in accordance with the following method:
In many cases, it is desirable that security threads used in currency and in other high value financial and identification documents be detected and authenticated by high-speed non-contact sensors, such as capacitance sensors, magnetic field sensors, optical transmission and opacity sensors, fluorescence, and/or nuclear magnetic resonance.
Incorporation of fluorescent materials into the lens, substrate, icon matrix, or icon fill elements of a Unison film can enable covert or forensic authentication of the Unison material by observation of the presence and spectral characteristics of the fluorescence. A fluorescing Unison film can be designed to have its fluorescent properties visible from both sides of the material or from only one side of the material. Without an optical isolation layer in the material beneath the icon layer, the fluorescence of any part of a Unison material will be visible from either of its sides. Incorporation of an optical isolation layer makes it possible to separate the visibility of the fluorescence from its two sides. Thus a Unison material incorporating an optical isolation layer beneath the icon plane may be designed to exhibit fluorescence in a number of different ways: fluorescent color A visible from the lens side, no fluorescence visible from the optical isolation layer side, fluorescent color A or B visible from the optical isolation layer side but not from the lens side, and fluorescent color A visible from the lens side and fluorescent color A or B visible from the optical isolation layer side. The uniqueness provided by the variety of fluorescent signatures possible can be used to further enhance the security of the Unison material. The optical isolation layer can be a layer of pigmented or dyed material, a layer of metal, or a combination of pigmented layers and metal layers, that absorbs or reflects the fluorescent emission from one side of the material and prevents it from being seen from the other side.
Icons formed from shaped voids and their inverse, icons formed from shaped posts, are particularly enabling for adding machine-readable authentication features to a Unison material security thread for currency and other high value documents. The icon matrix, the icon fill, and any number of back coats (sealing coats) can all, separately and/or in all combinations, incorporate non-fluorescing pigments, non-fluorescing dyes, fluorescing pigments, fluorescing dyes, metal particles, magnetic particles, nuclear magnetic resonance signature materials, lasing particles, organic LED materials, optically variable materials, evaporated metal, thin film interference materials, liquid crystal polymers, optical upconversion and downconversion materials, dichroic materials, optically active materials (possessing optical rotary power), optically polarizing materials, and other allied materials.
In some circumstances, such as when a dark or colored coating (such as a magnetic material or conductive layer) has been added to a Unison material or when the color of the icon plane is objectionable when seen through the back side of a substrate, it may be desirable to mask or hide the appearance of an embedded, partially embedded, or windowed Unison material security thread from one side of a paper substrate as seen in reflected light, while the thread is visible from the opposite side of the substrate. Other types of currency security threads commonly incorporate a metal layer, typically aluminum, to reflect light that filters through the surface substrate, thereby providing similar brightness to the surrounding substrate. Aluminum or other color neutral reflecting metal can be used in similar manner to mask the appearance of a Unison thread from the back side of a paper substrate by applying the metal layer on the back surface of the Unison material and then optionally sealing it in place. A pigmented layer can be utilized for the same purpose, that of hiding or obscuring the visibility of the security thread from the “back” side of the document, in place of a metallized layer, or in conjunction with it. The pigmented layer can be of any color, including white, but the most effective color is one that matches the color and intensity of the light internally scattered within, and outside of, the fibrous substrate.
The addition of a metallized layer to a Unison material can be accomplished in a number of ways, including direct metallization of the icon or sealing layer of the Unison material by evaporation, sputtering, chemical deposition, or other suitable means, or lamination of the icon or sealing layer of the Unison material to the metallized surface of a second polymer film. It is common practice to create currency security threads by metallizing a film, pattern demetallizing this film to leave narrow ‘ribbons’ of metallized area, laminating the metallized surface to a second polymer film, then slitting the laminated material such that the metal ribbons are isolated from the edges of the slit threads by the laminating adhesive, thereby protecting the metal from chemical attack at the edges of the thread. This method can also be applied in the case of the subject invention: the Unison material can simply replace the second laminating film. Thus a Unison material can be augmented by the addition of patterned or unpatterned metallized layers.
Synthetic images can be designed as binary patterns, having one color (or absence of color) defining the icons and a different color (or absence of color) defining the background; in this case each icon zone includes a complete single-tone image that utilizes image ‘pixels’ that are either full on or full off. More sophisticated synthetic images can be produced by providing tonal variations of the selected icon color. The synthetic image tonal variation can be created by controlling the density of the color in each icon image or by effectively ‘half-toning’ the synthetic image by including or excluding design elements in selected groups of icons.
The first method, controlling the density of the color in each icon image, may be accomplished by controlling the optical density of the material creating the microprinted icon image. One convenient method to do this utilizes the filled void icon embodiment, already described previously.
The second method, ‘half-toning’ the synthetic image by including or excluding design elements in selected groups of icons, illustrated in
A related icon image design method, illustrated in
This method can also be used to create narrow patterns of gaps between icon image elements, as shown in
Covert, hidden information can be incorporated into the icon images that cannot be seen in the resulting synthetic images. Having such covert information hidden in the icon images can be used, for example, for covert authentication of an object. Two methods for accomplishing this are illustrated by
A second method for incorporating covert information into icon images is illustrated by triangles 632 in
At a different location on the Unison 3-D material we find icon zone 650 that includes a different icon image 652. As with icon image 642, icon image 652 represents a scale-distorted view of the synthetic image 672 as seen from the different vantage point of this icon zone 650. The relative scaling of foreground frame 654 and background frame 658 are similar to the corresponding elements of icon image 642 (although this will not be true, in general), but the position of the background frame 658 has shifted, along with the size and orientation of the corner patterns 656. Icon zone 660 is located a further distance away on the Unison 3-D material and it presents yet another scale-distorted icon image 662, including icon image 662 with foreground frame 664, tapered gap patterns 667, and background frame 668.
In general, the icon image in each icon zone in a Unison 3-D material will be slightly different from its nearby neighbors and may be significantly different from its distant neighbors. It can be seen that icon image 652 represents a transitional stage between icon images 642 and 662. In general, each icon image in a Unison 3-D material may be unique, but each will represent a transitional stage between the icon images to either side of it.
Synthetic image 670 is formed from a multiplicity of icon images like icon images 640, 650, and 660 as synthetically imaged through an associated lens array. The synthetic image of the hollow cube 674 shows the effects of the different synthetic magnification factors that result from the effective repeat periods of the different elements of each of the icon images. Let us assume that the hollow cube image 674 is intended to be viewed as a SuperDeep image. In this case if icon zone 640 was disposed some distance to the lower left of icon zone 650, and icon zone 660 was disposed some distance to the upper right of icon zone 650, it can be seen that the effective period of the foreground frames 644, 654, and 664 will be less than that of the background frames 648, 658, and 668, thereby causing the closest face 676 of the cube (corresponding to the foreground frames 644, 654, and 664) to lie closer to the plane of the Unison material and the farthest face 678 of the cube to lie deeper and further from the plane of the Unison material, and to be magnified by a greater factor. The corner elements 646, 656, and 667 coordinate with both the foreground and background elements to create the effect of smoothly changing depth between them.
The method of designing icon images for Unison 3-D is more fully described in
In this example we wish to create a Unison 3-D synthetic image that incorporates three copies of the word “UNISON”, 686, 690 and 694, at the same visual size at three different SuperDeep image planes 684, 690, and 692. The diameter of the image planes 684, 688, and 692 expands with the field of view cone: in other words, as the depth of image increases, area covered by the field of view cone increases. Thus the field of view at the shallowest depth plane 684 only encompasses portions of “NIS” of the word UNISON, while the middle depth plane 688 encompasses all of “NIS” and portions of “U” and “O” and the deepest depth plane 692 encompasses almost all of “UNISON”, lacking only part of the final “N”.
The information they presented (UNISONs 686, 690, and 694) by each of these synthetic image planes 684, 688, and 692, must ultimately be incorporated into a single icon image in image projector 680. This is accomplished by capturing the information in the field of view cone 686 at each depth plane 684, 688, and 692, then scaling the resulting icon image patterns to the same dimensions. Icon image 696 represents the field of view of UNISON image 686 as seen at depth plane 684, icon image 704 represents the field of view of UNISON image 690 as seen at depth plane 688, and icon image 716 represents the field of view of UNISON image 694 as seen at depth plane 692.
Within icon image 696 icon image elements 698 originate from a portion of the first “N” of UNISON image 686, icon image element 700 originates from a portion of the “I” of UNISON image 686, and icon image elements 702 originate from portions of the “S” of UNISON image 686. Within icon image 704 icon image element 706 originates from a portion of the “U” of UNISON image 690, icon image element 708 originates from the first “N” of UNISON image 690, icon image element 710 originates from the “S” of UNISON image 690, and icon image element 714 originates from a portion of the “O” of UNISON image 690. Note that although the synthetic images 686, 690, and 694 are presented at similar scale, icon image 704 for the middle depth plane 688 presents its UNISON letters at a smaller scale than those of icon image 696. This accounts for the higher synthetic magnification that icon image 704 will experience (when synthetically combined with a multiplicity of surrounding icon images for the same depth plane). In similar manner, icon image 716 incorporates icon image elements 718 that originate from the UNISON image 694 and the UNISON letters incorporated in its icon image are at a further reduced scale.
The final icon image for this image projector is created by combining these three icon images 696, 704, and 716 into a single icon image 730, shown in
Each of the icon images required to present a chosen 3-D image can be computed from knowledge of the three-dimensional digital model of the synthetic image, desired depth position and depth span to be presented in the synthetic image, the lens repeat period, the lens field of view, and the ultimate graphical resolution of the icon images. This latter factor puts an upper limit on the level of detail that can be presented at each depth plane. Since depth planes that lie further from the plane of the Unison material carry a larger amount of information (because of the increased field of view) the graphical resolution limit of the icons has the greatest impact on the resolution of these synthetic image depth planes.
The method of
The resolution of the synthetic image depends on the resolution of the optical projectors and the graphical resolution of the icon images. We have obtained icon image graphical resolutions, less than 0.1 micron, that exceed the theoretical optical resolution limit of magnifying optics (0.2 micron). A typical icon image is created with a resolution of 0.25 micron.
Unison materials can be manufactured by sheet or web processing utilizing tools that separately incorporate the lens and icon microstructures. Both the lens tools and the icon tools are originated using photomasks and photoresist methods.
Lens tools are initially designed as semiconductor-type masks, typically black chrome on glass. Masks having sufficient resolution can be created by photoreduction, electron beam writing, or laser writing. A typical mask for a lens tool will incorporate a repeating pattern of opaque hexagons at a chosen period such as 30 microns, with clear lines separating the hexagons that are less than 2 microns wide. This mask is then used to expose photoresist on a glass plate using a conventional semiconductor UV exposure system. The thickness of the resist is selected to obtain the desired sag of the lens. For example, a thickness of 5 microns of AZ 4620 positive photoresist is coated onto a glass plate by suitable means, such as by spin coating, dip coating, meniscus coating, or spraying, to form lenses having a nominal 30 micron repeat and a nominal 35 micron focal length. The photoresist is exposed with the mask pattern, and developed down to the glass in a conventional manner, then dried and degassed at 100° C. for 30 minutes. The lenses are formed by thermal reflow according to standard methods that are known in the art. The resulting photoresist micro-lenses are coated with a conductive metal, such as gold or silver, and a negative nickel tool is created by electroforming.
Icon tools are created in a similar manner. An icon pattern is typically designed with the aid of CAD software and this design is transmitted to a semiconductor mask manufacturer. This mask is used in similar manner to the lens mask, except the thickness of the resist to be exposed is typically in the range of 0.5 micron to 8 microns, depending on the optical density of the desired synthetic image. The photoresist is exposed with the mask pattern, developed down to glass in a conventional manner, coated with a conductive metal, and a negative nickel tool is created by electroforming. According the choice of original mask design and in the choice of resist type used (positive or negative), the icons can be created in the form of voids in the resist pattern or they can be created in the form of “mesas” or posts in the resist pattern, or both.
Unison materials can be manufactured from a variety of materials and a multiplicity of methods that are known in the art of micro-optic and microstructure replication, including extrusion embossing, radiation cured casting, soft embossing, and injection molding, reaction injection molding, and reaction casting. An exemplary method of manufacture is to form the icons as voids in a radiation cured liquid polymer that is cast against a base film, such as 75 gage adhesion-promoted PET film, then to form the lenses from radiation cured polymer on the opposite face of the base film in correct alignment or skew with respect to the icons, then to fill the icon voids with a submicron particle pigmented coloring material by gravure-like doctor blading against the film surface, solidify the fill by suitable means (ex: solvent removal, radiation curing, or chemical reaction), and finally apply an optional sealing layer that may be either clear, dyed, pigmented, or incorporate covert security materials.
The manufacture of Unison Motion material requires that the icon tool and the lens tool incorporate a chosen degree of misalignment of the axes of symmetry of the two arrays. This misalignment of the icon and lens patterns axes of symmetry controls the synthetic image size and synthetic image rotation in the produced material. It is often desirable to provide the synthetic images substantially aligned with either the web direction or the cross-web direction, and in these cases the total angular misalignment of the icons and the lenses is divided equally between the lens pattern and the icon pattern. The degree of angular misalignment required is usually quite small. For example, a total angular misalignment on the order of 0.3 degree is suitable to magnify 30 micron icon images to a size of 5.7 mm in a Unison Motion material. In this example, the total angular misalignment is divided equally between the two tools, so each tool is skewed through an angle of 0.15 degree in the same direction for both tools. The skew is in the same direction because the tools form microstructures on opposite faces of a base film, so the skews of the tools add to each other, instead of canceling each other.
Skew can be incorporated into the tools at the time of the original design of the masks by rotating the whole pattern through the desired angle before writing it. Skew can also be mechanically incorporated into a flat nickel tool by cutting it at the appropriate angle with a numerically controlled mill. The skewed tool is then formed into a cylindrical tool using the skew-cut edge to align the tool to the rotational axis of an impression cylinder.
The synthetic magnification micro-optic system herein can be combined with additional features including but not limited to these embodiments as single elements or in various combinations, such as icon fill materials, back coatings, top coatings, both patterned and non-patterned, fill or inclusions in the lens, optical spacer or icon materials, as a laminate or coating. inks and or adhesives including aqueous, solvent or radiation curable, optically transparent, translucent or opaque, pigmented or dyed Indicia in the form of positive or negative material, coatings, or print including but not limited to inks, metals, fluorescent, or magnetic materials, X-ray, infrared, or ultra-violet absorbent or emitting materials, metals both magnetic and non-magnetic including aluminum, nickel, chrome, silver, and gold; magnetic coatings and particles for detection or information storage; fluorescent dye and pigments as coatings and particles; IR fluorescent coatings, fill, dyes or particles; UV fluorescent coatings, fill, dyes or particles; phosphorescent dye and pigments as coatings and particles, planchettes, DNA, RNA or other macro-molecule taggants, dichroic fibers, radioisotopes, print receptive coatings, sizing, or primers, chemically reactive materials, micro-encapsulated ingredients, field affected materials, conductive particles and coatings both metallic and non-metallic, micro-perforated holes, colored threads or fibers, patches of Unison embedded in the surface of a document, label, or materials surface, bonded to paper or polymer as a carrier to adhere to paper during manufacture, fluorescent Dichroic threads or particles, raman scattering coatings or particles, color shifting coatings or particles, Unison laminated to paper, paper board, card board, plastic, ceramic, fabric, or metal substrate, Unison as a thread, patch, label, over wrap, hot stamp foil, or tear tape, holographic, diffractive, diffractive kinegram, isograms, photographic or refractive optical elements, liquid crystal materials, Up Conversion and Down Conversion materials.
While the image icon component has been detailed in conjunction with the aforementioned array of focusing elements, the image icon component can be used to provide image “printing” in other applications. For example,
The icon layer 821 may be freestanding or it may optionally be provided on a substrate 820 or a transparent substrate 820 (the latter being required if the icon layer constitutes an element in a moiré magnification system wherein the icon layer 821 is optically coupled to a microlens array through the transparent substrate 820). Optional substrate or transparent substrate 820 supports or is in contact with icon layer 821 that incorporates a variety of microstructures that can act as elements of icon images. The microstructured icon elements can be formed as either recesses or raised areas in a layer of material, such as icon layer 821, or in a substrate. Microstructured icon image elements can take a wide variety of forms and geometries, including but not limited to asymmetric void patterns 822, symmetric void patterns 823, light trap patterns 824, holographic surface relief patterns 825, generalized diffractive surface relief patterns 826, binary structured patterns 827, “binary optic”, “structural color” and general stepped relief patterns 828, random rough and pseudo-random rough patterns 829, nominally flat-surfaced patterns 830, and concave 831 and convex 832 patterns (as viewed from the lower side, as drawn, of the icon layer).
The icon layer 821 can incorporate an array or pattern of homogeneous microstructures, for example, solely asymmetric void patterns 822. Alternatively, icon layer 821 can incorporate an array or pattern of two or more of microstructure embodiments 822-832. The microstructures serve as icon elements that can be formed into an array of microstructured icon elements that collectively form an image, similar to a group or array of pixels forming a conventional printed image. For example, a system can be created having an array of microstructured icon elements that can be combined with the aforementioned array of focusing elements, wherein the two arrays cooperate to form a synthetic optical image that may or may not be magnified. A system can also be created having an array of microstructured icon elements that collectively form a “micro-printed” image intended to be viewed upon magnification, such as viewing through a magnifying glass or with the aid of a microscope.
The micro-structured icon elements 822-832 of
Microstructured Icon Elements
The microstructured icon image elements are formed in the icon layer using any of the aforementioned microstructured icon image elements tooling and methods.
Any icon element microstructure can be coated with a conformal, non-conformal, and/or directional coating material 793.
Patterned Coatings
Coating material 793 can be conformal, non-conformal, continuous, discontinuous, patterned, unpatterned, directional, or it can have different properties or materials than the icon layer 777, or combinations thereof. Patterning of coating material 793 can provide icon image elements that are coordinated with microstructured image element patterns or independent of the microstructured image element patterns, or both. Coating material 793 can be patterned to provide icon image elements on the surface of icon layer 777 whether or not icon layer 777 incorporates any microstructured patterns. The coating material 793, whether patterned or unpatterned need not cover the entire surface of icon layer 777. The coating material can be applied to only selected portions of icon layer 777.
For example, icon image elements can be formed by creating a pattern demetallized aluminum layer as a coating material (as one example of coating material 793) on a polyester icon layer (as one example of icon layer 777) in an area of the polyester icon layer that does not have any microstructure formed into it (such as illustrated in
Positive and Negative Images, Including Patterned Coatings
Both microstructured icon image elements and patterned icon layer coatings can be used to form either positive images or negative images (see also
As an example, any of these icon image element methods can be used to provide images (such as a currency denomination—“50”) that are opaque or in a first color against a transparent background or a background of a second color, while in a different region of the icon layer 777 the coloring pattern can be reversed, such that the images are transparent or of the second color, while the background is opaque or of the first color.
Icon Image Element Embodiments Used for Micro-Printing
While any and all of the icon image element embodiments of the present disclosure can be used as elements of a moiré magnification system, they can also be used alone as ultra-high resolution micro-printing for a broad range of applications. The icon image element methods of the subject invention can be used to create micro-printing for compact information storage, for covert identification of currency, documents, packaging, and manufactured articles, for bar code and digital tagging of currency, documents, packaging, and manufactured articles, and for all applications that could benefit from ultra-high resolution printing or information tagging. In this embodiment, a pattern or array of microstructured icon elements is provided that collectively form an image or provide certain information that requires magnification to be viewed.
The icon layer 836 may be freestanding or it may optionally be provided on a substrate 834 or a transparent substrate 834. Optional substrate or transparent substrate 834 supports or is in contact with icon layer 836 that incorporates a variety of microstructures that can act, either alone or in combination, as elements of icon images. Microstructured icon image elements can take a wide variety of forms and geometries, including but not limited to the embodiments 844-864 corresponding to those of
As illustrated in
In this embodiment the coating material layer 840 is in close proximity to, or in contact with, the micro-structured icon image elements 844-856. The coating layer is similar to coating layer 793 of
In
In this embodiment the coating material layer 841 is separated from the icon layer 837 by the laminating substrate 843. The coating layer 841 can be any of the materials previously listed for coating layers 840 and 793.
While the micro-structured icon image elements 844-864 are shown in
Micro-structured icon image elements can be presented as either positive or negative images, or both. In
In
Object patterns of the positive icon image elements 872 are provided as depressions or voids 871 in the icon layer 868 while the background areas of positive icon image elements 872 are provided as raised areas in the positive icon area 872. The background areas of negative icon image elements 874 are provided as depressions 875 in the icon layer 868 and the object patterns of negative icon image elements 874 are provided as raised areas in the icon layer.
b) illustrates how the effect of positive and negative icon elements and patterns is particularly dramatic when the icons are filled with an icon fill material having different properties from the icon layer 868 material. A different area of icon layer 868 and optional substrate 866 is shown with filled positive icons 876 and filled negative icons 880. Icon fill material 878 forms the object patterns 886 of the positive icon elements 876 but the background of the filled negative icon elements 880.
A detailed plan view 882, see
By these means, and in combination with other teachings herein, it can be seen that both positive and negative image icon elements can be made. When used as elements of a moiré magnification system, these positive and negative image icon elements can be employed to produce positive and negative synthetic images. Positive and negative image elements can be used singly or in combination.
A representative sampling of embodiments combining filled icons and coatings is presented in
a) shows coating material 900 that has been applied by suitable means (as described for
The embodiment shown in
The embodiment shown in
The visual effect of the embodiment of
Provided that the icon elements are substantially completely filled with icon fill material 902, at all places that the coating material 900 is visible, whether seen through the icon fill material 902 or seen directly, the coating material 900 is substantially parallel to the surface of the icon layer 898. Thus the presence of the coating material 900 may modify the overall appearance of the icon fill material 902 but it does not provide an outlining or edge enhancing function as in
If the icon elements are underfilled with icon fill material 902, then coating material 900 may not be substantially parallel to the surface of the icon layer 898. In this case (not illustrated) there may be additional optical effects provided by coating material 900 in the areas that it contacts icon fill material 902 and is substantially non-planar.
The embodiment of
The first icon fill material 916 can be optionally stabilized, cured, or dried by drying, by chemical reaction (such as a two-part epoxy or a resin and hardener polymerization reaction), by radiation curing, by oxidation, or by other suitable means. The first icon fill material 916 can also be optionally not stabilized so that it can chemically react in some manner with the second icon fill material 918.
The icon microstructures 926 and 928 are then optionally filled with the second icon fill material 918. Depending on the method used to provide the underfilling of the first icon fill material 916, the relative thicknesses of the first icon fill material 916 and the second icon fill material 918 may differ in different regions or differ for icon element microstructures that have different depth, width, or aspect ratio. Positive icon elements 926 show approximately equal volumes of first icon fill material 916 and second icon fill material 918, with the thickness of the two fill materials being approximately equal in the center of the filled areas 920. The negative icon elements in this drawing show a large difference in aspect ratio, so that the central zones 922 of the two larger filled icon elements show a fill material thickness ratio of about, for example, 1:3 for the first 916 and second 918 icon fill materials, respectively. The center of the smaller negative icon element 924 shows a very different fill material thickness ratio of about, for example, 4:1 for the first 916 and second 918 icon fill materials, respectively. The filled icons can optionally be coated with coating material 900.
Coating material 900 may also be optionally applied to the icon layer 898 prior to filling the icons with the first icon fill material 916 or it may be applied to the icon layer 989 and first icon fill material 916 prior to filling with the second icon fill material 918. These variations are not illustrated in the figure.
Positive icon elements 920 have their object pattern microstructures filled with icon fill materials 916 and 918 and their background elements unfilled. Negative icon elements 928 have their background microstructures filled with icon fill materials 916 and 918 while their object pattern microstructures are unfilled.
Note that any icon layer material in any embodiment of this invention, not limited to those of
If the icon elements of
Patterned Coatings on Icons and as Icons
In
A patterned metallized coating that is not coordinated with the scale and geometry of the icon elements in a moiré magnification film can be used to produce an effect of partial transparent metal in the synthetic images because the locations of the demetallized areas will vary from icon element to icon element—a synthetic image formed from these icon elements with present an opacity that is proportionate to the percentage of coating present, in a manner similar to half toning methods used in printing.
Alternatively, a patterned demetallized metal coating can be used to create a different set of icon elements from the microstructured icon elements that could be used to generate a second set of synthetic images. One application of such additional synthetic images is for covert authentication of materials for currency, document, and brand protection.
In
In contrast, coating layer 934 in the area indicated by bracket 938 is coordinated with the icon elements, coating the depressed shapes 931 but not coating the “flats” 939 between them. This kind of patterning can be accomplished by coating the whole surface of the icon layer 932 with coating material 934, including both the depressed areas 931 and the “flats” 939, then removing the coating material 932 from the “flats” 939 by scraping, rubbing, brushing, skiving, abrading, chemical etching, adhesive pull-off, or by other suitable means.
A patterned coating material 934 coordinated with the icon elements in this manner can provide strong visual, optical, electromagnetic, magnetic, or other enhancement of the icon elements. For example: an icon layer 932 incorporating microstructured icon elements can be sputtered with gold, then the gold can be removed from the flats 939 by rubbing the coated surface against a fibrous material, such as paper. The gold remaining in the icon elements then provides them with a gold metallic appearance, while the flats are free of gold, so the icon elements appear to be separate gold objects against the background.
In the area indicated by bracket 958 two directional coatings are employed. Arrow 954 indicates the direction of application of the first directional coating 954 that coats the “flats” and right sides of the microstructured icon elements in this area. The second directional coating 962 is applied from the direction indicated by arrow 960, and coats the left sides of the microstructured icon elements. The first and second directional coatings (952 and 962, respectively) may be either the same material or be different materials, and they may be applied from opposing directions (954 and 960), as shown, or they may be applied from similar directions. For example: if the first directional coating 952 is silver and it is applied from the direction shown by arrow 954, and if the second directional coating 962 is gold and it is applied from the direction shown by arrow 960, then the right sides of the microstructured icon elements will appear silver and their left sides will appear gold, while their centers remain uncoated and may appear transparent. As another example: the conditions of the previous example, except the silver is applied at the angle shown by arrow 954 and the gold is applied from the same general direction, at an angle that is ten degrees closer to the overall icon layer 932 surface normal. The gold will then coat the same sides of the icon elements as the silver, but the gold will coat higher up the right side or onto the center of the icon. The resulting icon element appear to have a silvered right side that blends into a gold color towards the top of the icon element (as drawn). Many other such combinations and variations will be obvious to one skilled in the art.
Yet another variation is shown in the area of
a) illustrates the use of a patterned coating material 967 as a means to create icon image elements. Patterned coating material 967 is provided on a substrate 966 or a transparent substrate 966, said patterning incorporating regions of coating material 968 of a selected thickness and either regions of coating material 969 having a smaller thickness or regions without coating material 970, or both. The different thicknesses of coating material—full thickness (968), partial thickness (969), and zero thickness (970) (or the absence of coating material)—can be patterned to represent icon image information as an element in a moiré magnification system. Either the full thickness coating material or the zero thickness coating material can be used to form object patterns of the icon elements.
The patterning of coating material 967 can be performed by any of the methods previously described with respect to
Additional coating material layers can be optionally added to the patterned coating material 967. Examples include, but are not limited to, metallization by vacuum deposition, pigmented or dyed coatings, or any of those list previously in the Definitions section of this document. Example: such layers may be directly applied, laminated, hot stamped, coated, or otherwise provided. Application of such additional layers may provide a benefit of altering the appearance of the regions of partial thickness coating material 969 and the regions of zero thickness (absent) coating material 970.
Lens sheet 1000 is not permanently attached to icon sheet 1002, but is a free and separate piece that can be used as an authentication device for icon sheet 1002.
When used as an authentication device lens sheet 1000 is brought into contact or close proximity to the surface of icon sheet 1002. The gap 992 between the two sheets will, in general, contain a thin film of air, or gap 992 can optionally be filled with water, glycerin, or other fluid to provide optical or mechanical coupling between the lens sheet 1000 and the icon sheet 1002.
Icon sheet 1002, incorporating optional transparent substrate 990, icon layer 994 and icon elements 996 (shown here optionally filled with an icon fill material 997), is disposed with the icon layer on the surface furthest from the lens sheet 1000. The total thickness of icon sheet 1002 plus lens sheet 1000 is designed to be substantially equal to the focal length 1004 of the micro-lenses 986. When the lens sheet 1000 is placed substantially in proximity, for example in contact with the icon sheet 1002, with or without coupling fluid, the focal point 998 of the micro-lenses 986 should lie somewhere within or near the icon layer 994. The optimal position of the focal point 998 is at, or slightly below, the bottom surface of the icon layer 994.
A system formed according to the embodiments of
An example of such additional imaging could be a person's photograph for identification, such that the icon sheet performs as a background to the photograph. The icon sheet 1002, and by association, the object to which it is securely attached, can be authenticated by placing an appropriately scaled lens sheet 1000 substantially into contact with the icon sheet 1002 and rotating the lens sheet 1000 within its plane until the lenses and icon elements 996 align sufficiently to form a synthetic image of the icon elements 996. (An “appropriately scaled” lens sheet is a lens sheet in which the array of focusing elements has a rotational symmetry and repeat period substantially matching that of the array of icon elements 996 on the icon sheet 1002, with an icon/lens repeat ratio designed to achieve the selected optical effect [SuperDeep, Deep, Motion, Float, SuperFloat, Levitate, 3-D, combinations thereof, etc.])
b) illustrates an alternate embodiment of this aspect of the invention. In this figure lens sheet 1010 includes is monolithic, consisting of a single material including micro-lenses 1008 on its upper surface and an optional additional thickness of material 1006 to provide optical spacing. The lens sheet 1000 of
The function of the lens sheet 1010 in the embodiment of
The functional differences between icon sheet 1014 and icon sheet 1002 are that the former has its icon elements on the surface closest to the lens sheet 1010 while the latter has its icon elements on the surface most distant from the lens sheet 1000. In addition, since the icon elements 1020 of icon sheet 1014 are on its upper surface, the material 1018 that lies beneath the icon elements 1020 does not need to be transparent, whether the icon sheet 1014 is monolithic or whether it has the structure of icon sheet 1002, with an icon layer and a substrate. The substrate 990 of icon sheet 1002 does need to be substantially transparent, since light must pass through the substrate 990 in order for the lenses 986 to form an image of the icon elements 996.
An optional coating material 1016 can be provided on the icon elements 1020 of the icon sheet 1014. A coating material 1016 may be desirable to provide optical or non-contact authentication of the icon sheet by means different from the use of lens sheet 1010. The coating layer 1016 may include other optical features, such as a holographic or diffractive structure. The icon elements of both icon sheet 1002 and icon sheet 1014 can take any form, including any of the icon element embodiments taught herein.
As was the case for the embodiment of
When used as an authentication device lens sheet 1010 is brought into contact or close proximity to the surface of icon sheet 1014. The gap 1012 between the two sheets will, in general, contain a thin film of air, or gap 1012 can optionally be filled with water, glycerin, or other fluid to provide optical or mechanical coupling between the lens sheet 1010 and the icon sheet 1014.
The total thickness of icon sheet 1014 plus lens sheet 1010 is designed to be substantially equal to the focal length 1024 of the micro-lenses 1008. When the lens sheet 1010 is placed substantially in contact with the icon sheet 1014, with or without coupling fluid, the focal point 1022 the micro-lenses 1008 should lie somewhere within or near the icon elements 1020. The optimal position of the focal point 1022 is at, or slightly below, the lower extent of the icon elements 1020.
A system formed according to the embodiment of
Either structure or form of icon sheet (1002 or 1014) can incorporate multiple patterns of icon elements (996 or 1020, respectively) that form different synthetic images that can be read or authenticated at different lens sheet rotation angles (such as one icon pattern that produces a maximum magnification synthetic image at a lens sheet rotation angle of 0 degrees and a second icon pattern that produces a maximum magnification synthetic image at a lens sheet rotation angle of 30 degrees), different lens repeat period, different lens and icon array geometry (such as one array set having a hexagonal geometry and a second array set having a square geometry), and combinations thereof.
An example of the different lens period authentication method is an icon sheet incorporating an icon element pattern that produces a Deep image when synthetically magnified by a lens sheet having a repeat period of 30 microns and also incorporating a second icon element pattern that produces a Float image when synthetically magnified by a lens sheet having a repeat period of 45 microns. The second icon element pattern can optionally be authenticated at a different rotational angle than the first icon element pattern.
Materials having multiple icon patterns can incorporate one set of information that can be revealed by a first key (lens sheet having a first selected repeat period) and additional sets of information that can each be revealed by additional keys (lens sheets each matched to the scale of their respective icon element repeats). The multiple icon patterns can also be provided in different icon layers requiring focusing elements having differing focal lengths for forming visible synthetic optical images from the different icon layers.
The embodiment of
For example, the repeat period of the covert icon patterns 1034 can be designed to be substantially different from the repeat period of the micro-lenses 1028; the covert icon pattern 1034 period may be designed to be 37 microns while the micro-lens 1028 period may be designed to be 32 microns. This icon to lens scale ratio (about 1.156) will create a Float synthetic image of the covert icon pattern 1034 having a period of about 205 microns. The features of a covert synthetic image of this size are essentially invisible to the naked eye. (The covert icon period can alternatively be chosen to produce a Deep synthetic image of equivalent period with an icon to lens scale ratio of about 0.865. For a given micro-lens repeat period, the repeat period of the covert icons can be designed to produce synthetic images having any Unison moiré magnification effect, including but not limited to SuperDeep, Deep, Motion, Float, SuperFloat, Morph.) The specific dimensions presented here represent only a single example of the continuum of dimensions that may be chosen.
As another example, the rotational symmetry of the covert icon patterns 1034 can be designed to be substantially different from that of the micro-lenses 1028. In this example we will assume that both the micro-lenses 1028 and the covert icon patterns 1034 are arranged in a hexagonal array, but the orientation of the array of covert icon patterns 1034 is rotated 30 degrees from that of the array of micro-lenses 1028. This misalignment of the two arrays will also prevent the formation of an overtly viewable synthetic image of the covert icon patterns 1034. Yet another method to prevent the formation of covert icon pattern 1034 synthetic images is to arrange the micro-lenses 1028 into one array geometry, such as hexagonal, while the covert icon patterns 1034 are arranged into a different array geometry, such as square.
The covert icon patterns 1034 can be revealed by forming a synthetic image with an additional, separate element, a covert authentication lens sheet 1040 that is brought near to, or substantially in contact with, the micro-lenses 1028 of the magnification system 1026 with an optically coupling material 1044 filling the gaps between them. The optically coupling material is preferably a liquid, such as glycerin or corn syrup, that has a refractive index that is similar to the refractive indices of the material 1052 forming the covert authentication lens sheet and the material 1050 forming the magnification system lenses 1028. The coupling material has the function of partially or fully negating the focusing power of lenses 1028 by immersing them in a medium having a similar refractive index. Other materials that can be used to perform this function include gels (including gelatins), elastomers, and pressure sensitive adhesives.
The properties of the covert authentication lens sheet 1040, including its array geometry, repeat period, and micro-lens focal length, are designed to coordinate with the array geometry and repeat period of the covert icon patterns 1034 and the total distance from the covert authentication lens sheet lenses 1042 and the icon plane 1030.
In practice, a small amount of a fluid such as glycerin is placed on the surface of the magnification system lenses 1028 and the flat surface of the covert authentication lens sheet 1040 is placed in contact with the fluid and pressed substantially into contact with the lenses 1028. The covert authentication lens sheet 1040 is then rotated in its plane to substantially align the orientation of the array of micro-lenses 1042 with the orientation of the array of covert icon patterns 1034. As alignment is approached the covert icon pattern 1034 synthetic image 1048 becomes magnified sufficiently to be distinguished with the naked eye, reaching maximum magnification at the position wherein the two arrays have substantially identical orientations.
An alternative embodiment is to form the covert authentication lens sheet 1040 as a pressure-sensitive label or tape that can be applied to the surface of lenses 1028. In this embodiment the function of the optically coupling material 1044 is performed by a substantially transparent pressure sensitive adhesive applied to the flat surface of the covert authentication lens sheet 1040. A method of aligning the covert authentication lens sheet 1040 to the orientation of the covert icon pattern 1034 is desirable, such as by printed alignment patterns or oriented edges of the magnification system 1026 that the edge of the covert authentication lens sheet 1040 can be matched to at the time of application.
Yet another alternative structure for a ‘wet decoder’ method and system is to incorporate the covert icon patterns 1034 into a second icon layer. This second icon layer may be either closer to the lenses 1028 or further from the lenses 1028 than the first icon layer 1030. The focal length and thickness of the covert authentication lens sheet 1040 is then designed to cause its focal point to fall in the second icon layer when the covert authentication lens sheet 1040 is applied to lenses 1028 with optically coupling material 1044. In this embodiment, the array properties of the covert icon patterns 1034 can be the same as those of the overt icon patterns, so long as the position of the second icon plane does not enable the lenses 1028 to form a distinguishable overt image of the covert icon patterns 1034.
The embodiment of
the covert icon pattern 1060 period may be designed to be 28.071 microns while the micro-lens 1056 period may be designed to be 28.000 microns. This icon to lens scale ratio (about 1.00255) will create a floating synthetic image 1063 (of the covert icon patterns 1060) having a period of about 392 microns. The features of a covert synthetic image of this size are essentially invisible to the naked eye. (The covert icon period can alternatively be chosen to produce a Deep synthetic image of equivalent period with an icon to lens scale ratio of about 0.99746 For a given micro-lens repeat period, the repeat period of the covert icons can be designed to produce synthetic images having any Unison moiré magnification effect, including but not limited to SuperDeep, Deep, Motion, Float, SuperFloat, Morph.) The specific dimensions presented here represent only a single example of the continuum of dimensions that may be chosen.
As another example, the rotational symmetry of the covert icon patterns 1060 can be designed to be substantially different from that of the micro-lenses 1056. In this example we will assume that both the micro-lenses 1056 and the covert icon patterns 1060 are arranged in a hexagonal array, but the orientation of the array of covert icon patterns 1060 is rotated 30 degrees from that of the array of micro-lenses 1056. This misalignment of the two arrays will also prevent the formation of an overtly viewable synthetic image of the covert icon patterns 1060. Yet another method to prevent the formation of covert icon pattern 1060 synthetic images is to arrange the micro-lenses 1056 into one array geometry, such as hexagonal, while the covert icon patterns 1060 are arranged into a different array geometry, such as square.
The covert synthetic images 1063 can be made visible by forming a second synthetic image by means of an additional, separate element, a covert authentication lens sheet 1064 that is brought near to, or substantially in contact with, the micro-lenses 1056 of the magnification system without the use of an optically coupling material filling the gap 1065 between them. Gap 1065 is filled with air, vacuum, or any other gas that permeates the ambient environment of the magnification system 1054.
The properties of the covert authentication lens sheet 1064, including its array geometry, repeat period, and micro-lens focal length, are designed to coordinate with the array geometry and repeat period of the covert synthetic images 1063 and the total distance from the covert authentication lens sheet lenses 1066 and the position of the covert synthetic images 1063 as they are projected into the material 1070 forming the covert authentication lens sheet 1064.
In practice, the flat surface of the covert authentication lens sheet 1064 is placed in contact with the magnification lenses 1056. The covert authentication lens sheet 1064 is then rotated in its plane to substantially align the orientation of the array of micro-lenses 1066 with the orientation of the array of covert synthetic images 1063. As alignment is approached the covert synthetic images 1063 form a second synthetic image 1068 that becomes magnified sufficiently to be distinguished with the naked eye, reaching maximum magnification at the position wherein the two arrays have substantially identical orientations.
An alternative embodiment is to form the covert authentication lens sheet 1064 as a pressure-sensitive label or tape that can be applied to the surface of lenses 1056. In this embodiment either a very thin (substantially less than the height of micro-lenses 1056) substantially transparent pressure-sensitive adhesive (not shown in the figure) may be applied to the entire flat surface of the covert authentication lens sheet 1064 or a patterned pressure-sensitive adhesive (not shown in the figure) may be applied to this surface. In the first case, application of the very thin substantially transparent pressure-sensitive adhesive-coated covert authentication lens sheet to the magnification system 1056 will cause the adhesive to contact the tops of the lenses 1056 without filling the gap 1065 and obscuring the sides of the lenses, thus preserving the air gap that enables lenses 1056 to form the first covert synthetic images 1063. In the second case the covert authentication lens sheet 1064 will maintain an unfilled gap 1065 in those areas where there is no adhesive. A method of aligning the covert authentication lens sheet 1064 to the orientation of the covert icon pattern 1060 is desirable, such as by printed alignment patterns or oriented edges of the magnification system 1056 that the edge of the covert authentication lens sheet 1064 can be matched to at the time of application.
Yet another alternative structure for a ‘dry decoder’ method and system is to incorporate the covert icon patterns 1060 into a second icon layer. This second icon layer may be either closer to the lenses 1056 or further from the lenses 1056 than the first icon layer 1058, in any location that enables lenses 1056 to form a real or virtual image of covert icons 1060. The focal length and thickness of the covert authentication lens sheet 1064 is then designed to cause its focal point to fall in the location of the covert synthetic image formed by lenses 1056 when covert authentication lens sheet 1064 is placed substantially in contact with lenses 1056.
Yet another method of revealing hidden information in a magnification system of the present disclosure is illustrated in
b) illustrates the effect of immersing the micro-lenses 1080 in a suitable fluid 1092 such as water. (Immersion is a relative situation—so long as the fluid 1092 lies over micro-lenses 1080 in a layer that is greater than the center height 1091 of the lenses 1080, the lenses are “immersed” from the standpoint of optics.) Changing the refractive index of the medium outside of the HydroUnison moiré magnification system 1078 can change the focal length of the micro-lenses 1080. In this example, increasing the refractive index of the medium outside of the system increases the focal length of micro-lenses 1080. The thickness of optical spacer 1081 is chosen to bring the focal points 1088 of the fluid 1092 immersed micro-lenses 1080 into or near the icon layer 1082. Under these conditions the micro-lenses 1080 can project well-focused synthetic images 1095 of the icon patterns 1084.
HydroUnison system according to this embodiment appears to have no distinct image when it is viewed in a dry state, with the lenses 1080 in air. When the lenses are wetted (immersed) with a liquid having a refractive index substantially equal to the selected immersion fluid 1092 index, a synthetic image suddenly appears. This effect is particularly dramatic if the synthetic image is a combination Float/Deep image or a SuperDeep image. As the HydroUnison system dries the synthetic image fades away and disappears.
Designing a HydroUnison system to produce this effect when immersed in a fluid 1092 having a selected refractive index is accomplished by making the thickness of the optical spacer 1081 to be approximately equal to the fluid 1092 immersed micro-lens 1080 focal length 1094 for a given choice of fluid 1092. A convenient fluid 1092 is water, with a typical refractive index of about 1.33. Although the HydroUnison moiré magnification system 1078 may not be a “thin lens” optical system, the thin-lens system design Lens-maker's Formula can be used to find a suitably accurate design thickness of the optical spacer 1081 for a chosen immersion fluid 1092.
The Lens-maker's formula is:
1/f=(nlens−no) (1/R1−1/R2)
wherein:
f=the lens focal length when immersed in a medium of refractive index no
nlens=the refractive index of the lens material
n0=the refractive index of the immersion medium
R1=the radius of curvature of the first lens surface
R2=the radius of curvature of the second lens surface
Since the focal point of the lenses 1080 is internal to the HydroUnison moiré magnification system 1078, the only curvature affecting the focal length is the first curvature, R1—the second curvature, R2, can be treated as a flat surface with a radius of infinity, reducing the ratio 1/R2 equal to zero. The Lens-maker's formula then simplifies to:
1/f=(nlens−no)/R1 or f=R1/(nlens−no)
For the case of a lens in air, nlens=1.487, and no=nair=1.000:
f
air
=R
1/(1.487−1.000)=R1/0.487=2.053R1
For the case of a lens immersed in water, nlens=1.487, and no=nH2O=1.333:
f
H2O
=R
1/(1.487−1.333)=R1/0.154=6.494R1
So the water-immersed focal length of the lenses 1080 is found to be approximately greater than the in-air focal length of the lenses 1080 by a factor of:
f
H2O
/f
air=(6.494R1)/(2.053R1)=3.163
For example, if a given micro-lens 1080 formed from a material having a refractive index of 1.487 has an in-air focal length 1086 of 23 microns, then that micro-lens 1080 will have an approximate focal length of 23×3.163=72.7 microns when immersed in water.
Other fluids having a similar refractive index to the selected immersion fluid 1092 refractive index can be used to reveal the hidden image, with the effectiveness of a particular fluid depending, in part, on how closely its refractive index matches that of the selected immersion fluid refractive index 1092. For example, ethyl alcohol has a refractive index of about 1.36. The focal length of the lenses in the example above would be 88.2 microns when immersed in ethyl alcohol, so the synthetic image 1095 would be slightly out of focus if the optical spacer 1081 was designed with a thickness of about 73 microns, corresponding to a selected immersion fluid 1092 having the refractive index of water.
The embodiment of
Other embodiments of Unison moiré magnification systems as taught previously herein are also wetness indicating—immersing the lenses of these Unison systems in a fluid will generally prevent the materials from forming a synthetic image.
The synthetic image returns when the liquid is dried or removed.
The embodiment of
The example presented in
Each of these three synthetic images can be the same color, pattern, and type of Unison effect as the others, or they can be different from the others in color, pattern, and Unison effect. While the type, color, and pattern of a Unison synthetic image can be the same for some or all synthetic images produced by a HydroUnison system, it is important to note that the magnitude of Unison depth effects (SuperDeep, Deep, Float, SuperFloat, Levitate), i.e., the apparent height of float images and the depth of Deep images, is proportional to the f-number of the micro-lenses 1112. Immersing the micro-lenses 1098 in media having different refractive indices changes the f-number of the micro-lenses 1098 and proportionately amplifies the magnitude of the Unison depth effects in the synthetic images respectively produced.
HydroUnison moiré magnification system 1096 incorporates micro-lenses 1098, first optical spacer 1100 separating micro-lenses 1098 from first icon layer 1102, first icon layer 1102 bearing first icon patterns 1117, second optical spacer 1104 separating first icon layer 1102 from second icon layer 1106, second icon layer 1106 bearing second icon patterns 1119, third optical spacer 1108 separating second icon layer 1106 from third icon layer 1110, and third icon layer 1110 bearing third icon patterns 1111.
a) illustrates the function of an exemplary multiple image HydroUnison system 1096. When the micro-lenses 1098 are immersed in a medium having an index substantially equal to 1.000 (such as vacuum, air, and most gases) the micro-lenses 1098 have a focal length 1116 that places their focal points 1118 in or near first icon layer 1102. Icon layer 1102 may be omitted, but if it is present and if it bears suitable icon patterns 1117 in the correct geometric relationship to the micro-lenses 1098 (as has been taught in connection with the various embodiments of the subject invention) then micro-lenses 1098 will project a synthetic image 1114 of the first icon pattern 1117.
In
The function of the example multiple image HydroUnison moiré magnification system 1096 when micro-lenses 1098 are immersed in a fluid 1128 have a refractive index of 1.418 is illustrated in
Infinitely many variations of the embodiment of
Applications of the embodiment of
Another effect that can be obtained through the use of the magnification system of the present disclosure is illustrated in
The method of accomplishing the effect is also illustrated in
This embodiment has a multiplicity of uses. Examples include: a synthetic image that does not appear to change from different azimuthal angles, such that it always faces, or “tracks” the viewer; a series of connected images that form a motion picture or animation can be presented; multiple pages of text or graphical information can be provided such that the viewer “turns the pages” by rotating the material and viewing it from different azimuthal positions; street signs or traffic control signs that present different information to drivers approaching them from different directions; and many other applications.
If the icon fill material 1512 is solvent-based, the final process step may include heating to drive off the excess solvent.
The systems and devices herein have many fields of use and applications. Examples include:
Government and defense applications—whether Federal, State or Foreign (such as Passports, ID Cards, Driver's Licenses, Visas, Birth Certificates, Vital Records, Voter Registration Cards, Voting Ballots, Social Security Cards, Bonds, Food Stamps, Postage Stamps, and Tax Stamps);
currency—whether Federal, State or Foreign (such as security threads in paper currency, features in polymer currency, and features on paper currency);
documents (such as Titles, Deeds, Licenses, Diplomas, and Certificates);
financial and negotiable instruments (such as Certified Bank Checks, Corporate Checks, Personal Checks, Bank Vouchers, Stock Certificates, Travelers' Checks, Money Orders, Credit cards, Debit cards, ATM cards, Affinity cards, Prepaid Phone cards, and Gift Cards);
confidential information (such as Movie Scripts, Legal Documents, Intellectual Property, Medical Records/Hospital Records, Prescription Forms/Pads, and “Secret Recipes”);
product and brand protection, including Fabric & Home Care (such as Laundry Detergents, fabric conditioners, dish care, household cleaners, surface coatings, fabric refreshers, bleach, and care for special fabrics);
beauty care (such as Hair care, hair color, skin care & cleansing, cosmetics, fragrances, antiperspirants & deodorants, feminine protection pads, tampons and pantiliners);
baby and family care (such as Baby diapers, baby and toddler wipes, baby bibs, baby change & bed mats, paper towels, toilet tissue, and facial tissue);
health care (such as Oral care, pet health and nutrition, prescription pharmaceuticals, over-the counter pharmaceuticals, drug delivery and personal health care, prescription vitamins and sports and nutritional supplements; prescription and non-prescription eyewear; Medical devices and equipment sold to Hospitals, Medical Professionals, and Wholesale Medical Distributors (ie: bandages, equipment, implantable devices, surgical supplies);
food and beverage packaging;
dry goods packaging;
electronic equipment, parts & components;
apparel and footwear, including sportswear clothing, footwear, licensed and non-licensed upscale, sports and luxury apparel items, fabric;
biotech pharmaceuticals;
aerospace components and parts;
automotive components and parts;
sporting goods;
tobacco Products;
software;
compact disks and DVD's;
explosives;
novelty items (such as gift wrap and ribbon)
books and magazines;
school products and office supplies;
business cards;
shipping documentation and packaging;
notebook covers;
book covers;
book marks;
event and transportation tickets;
gambling and gaming applications (such as Lottery tickets, game cards, casino chips and items for use at or with casinos, raffle and sweepstakes);
home furnishing (such as towels, linens, and furniture);
flooring and wallcoverings;
jewelry & watches;
handbags;
art, collectibles and memorabilia;
toys;
displays (such as product Point of Purchase and Merchandising displays);
product marking, labeling and packaging (such as labels, hangtags, tags, threads, tear strips, over-wraps, securing a tamperproof image applied to a branded product or document for authentication or enhancement, as camouflage, and as asset tracking).
Suitable materials for the embodiments described above include a wide range of polymers. Acrylics, acrylated polyesters, acrylated urethanes, polypropylenes, urethanes, and polyesters have suitable optical and mechanical properties for both the microlenses and the microstructured icon elements. Suitable materials for the optional substrate film include most of the commercially available polymer films, including acrylic, cellophane, Saran, nylon, polycarbonate, polyester, polypropylene, polyethylene, and polyvinyl. Microstructured icon fill materials can include any of the materials listed above as suitable for making microstructured icon elements, as well as solvent based inks and other commonly available pigment or dye vehicles. Dyes or pigments incorporated into these materials should be compatible with the chemical makeup of the vehicle. Pigments must have a particle size that is substantially smaller than the smallest dimensions of any component of an icon element. Optional sealing layer materials can include any of the materials listed above as suitable for making microstructured icon elements, plus many different commercially available paints, inks, overcoats, varnishes, laquers, and clear coats used in the printing and paper and film converting industries. There is no preferred combination of materials—the choice of materials depends on the details of the material geometry, on the optical properties of the system, and on the optical effect that is desired.
Although exemplary embodiments have been shown and described, it will be clear to those of ordinary skill in the art that a number of changes, modifications, or alterations to the invention as described can be made. All such changes, modifications, and alterations should therefore be seen as within the scope of the disclosure.
This application is a continuation of U.S. patent application Ser. No. 11/438,081, filed May 18, 2006, now U.S. Pat. No. 7,468,842, and claims the benefit of and priority to U.S. Provisional Patent Application No. 60/682,231 filed May 18, 2005 and U.S. Provisional Patent Application No. 60/683,037 filed May 20, 2005, each of which is incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 60682231 | May 2005 | US | |
| 60683037 | May 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11438081 | May 2006 | US |
| Child | 12341702 | US |