Immobilization of cells with a polyazetidine prepolymer

The present invention is concerned with the immobilization of microbial cells and processes for preparing and using the same. The invention is particularly concerned with an improved process for manufacturing L-aspartic acid using immobilized microbial cells, notably E. coli (Escherichia coli) cells, which contain L-aspartase activity. However, the immobilization and use of other cells are also contemplated.
BACKGROUND TO THE INVENTION
There is a considerable amount of prior art regarding the immobilization of E. coli or other microbial cells for use in the preparation of L-aspartic acid. For example, U.S. Pat. No. 3,791,926 (Chibata et al) describes a process for the production of L-aspartic acid which involves polymerizing a monomer selected from acrylamide, N,N'-lower alkylene-bis(acrylamide) and bis(acrylamidomethyl)ether in an aqueous suspension containing an aspartase-producing microorganism such as E. coli ATCC No. 11303. The resultant immobilized aspartase-producing microorganism is treated with ammonium fumarate or a mixture of fumaric acid or its salt and an inorganic ammonium salt which by enzymatic reaction gives L-aspartic acid.
The immobilization of E. coli cells containing aspartase activity and use of the resulting immobilized cells for the production of L-aspartic acid are also described by Fusee et al, Applied and Environmental Microbiology, Vol. 42, No. 4, October 1981, pages 672-676. According to Fusee et al, the cells are immobilized by mixing a suspension of the cells with a liquid isocyanate-capped polyurethane prepolymer (Hypol.RTM.) so as to form a "foam" containing the immobilized cells.
Sato et al (Biochimica et Biophysica Acta, 570 (1979) pages 179-186) have disclosed the immobilization of E. coli cells containing aspartase activity with .kappa.-carrageenan, and use of the immobilized preparation for the production of L-aspartic acid.
Additional literature disclosures describing the immobilization of microbial cells in urethane prepolymers or polyurethanes or the like include the following:
(a) Immobilization of Microbial Cells in Polyurethane Matrices by Klein et al, Biotechnology Letters, Vol. 3, No. 2, 65-70 (1981);
(b) Hydrophilic Urethane Prepolymers: Convenient Materials for Enzyme Entrapment, Biotechnology & Bioengineering, Vol. XX, pages 1465-1469 (1978);
(c) Transformation of Steroids by Gel-Entrapped Cells in Organic Solvent by Omata et al, European J. Applied Microbiology and Biotechnology 8, 143-155 (1979); and
(d) Entrapment of Microbial Cells and Organelles With Hydrophilic Urethane Prepolymers, by Tanaka et al, European J. Applied Microbiology and Biotechnology, 7, 351-354 (1979).
The above-noted processes for preparing L-aspartic acid using immobilized microbial cells suffer from various disadvantages. For example, .kappa.-carrageenan gum and polyurethane "foam" as disclosed by Fusee et al and Sato et al are relatively soft and compressible. Hence when these immobilized cell compositions are used, in a column through which ammonium fumarate is passed for conversion to ammonium aspartase, they tend to be compressed and plug up, particularly where high flow rates and/or relatively tall column heights are involved.
OBJECTS OF THE INVENTION
The principal object of the present invention is to provide an improved process for preparing L-aspartic acid using L-aspartase active microbial cells, preferably E. coli cells, which have been immobilized in a special way whereby the resulting composition is highly effective for the preparation of L-aspartic acid batchwise or in continuous fashion.
A more specific object includes the provision of an improved process for preparing L-aspartic acid from ammonium fumarate using immobilized E. coli cells which maintain optimum L-aspartase activity for relatively long periods of time. Another specific object of the invention is to provide novel immobilized microbial systems suitable for use in making L-aspartic acid which obviate problems encountered in prior procedures involving the use of immobilized cells. Other objects will also be hereinafter apparent.
SUMMARY OF THE INVENTION
According to one aspect of the invention, there is provided a process for preparing L-aspartic acid by contacting ammonium fumarate or its equivalent with an immobilized microbial cell composition comprising E-coli 11303 cells or equivalent cells containing L-aspartase activity, the cells being immobilized by means of a fixed, insoluble, crosslinked polymer obtained by curing a curable prepolymer material selected from the group consisting of polyazetidine prepolymers, carboxymethyl cellulose (CMC), polyurethane hydrogel prepolymers and polymethylene isocyanates cured at a temperature below the temperature at which the L-aspartase activity of the microbial cells is significantly reduced, the cell/crosslinked polymer composition constituting a coating on a solid inert carrier. The application of the immobilized cell/crosslinked polymer coating on the carrier provides a highly advantageous form of the cell/polymer composition for use in preparing L-aspartic acid. It is a particularly advantageous feature that the cell/polymer systems of the invention can be provided as a dry coating on the carrier without significant loss of the L-aspartase activity.
An especially preferred aspect of the invention contemplates the provision of immobilized E. coli cells having L-aspartase activity, the cells being immobilized by means of a crosslinked, water-insoluble polymer obtained by curing a polyazetidine prepolymer.
Broadly speaking, the invention is dependent on binding whole cells of E. coli, notably E. coli ATCC 11303, or the equivalent, which are known to have L-aspartase activity and therefore are capable of producing L-aspartic acid (or ammonium salt thereof) by conversion of ammonium fumarate, in a novel and useful configuration using a special crosslinked polymer system as set forth above to bind the cells.
The indicated prepolymer systems can be crosslinked at temperatures below 40.degree. C. and in the presence of relatively large volumes of water containing E. coli cells without significantly deteriorating the L-aspartase activity of the cells. It is a surprising aspect of the invention that such aqueous crosslinking conditions leave the E. coli cells with their L-aspartase activity even though the cells are immobilized in insoluble, crosslinked polymer networks.
Another unique aspect of the invention is that the wet dispersion of the E. coli cells in the aqueous polymer solutions can be taken to dryness while the immobilized cells still surprisingly retain most of their original L-aspartase activity. The drying process has the advantage of providing strong, well-crosslinked, insoluble compositions in the form of coatings, membranes, particles, etc. having high concentrations of cells retaining L-aspartase activity.
The novel immobilized L-aspartase cell compositions disclosed herein have been found to outperform the immobilized L-aspartase active E. coli cell compositions previously reported by, for example, Fusee et al and Sato et al in the references noted above.
Prepolymer materials suitable for use to provide the crosslinked polymer network for immobilizing the E. coli cells according to the invention include:
(1) polyazetidine prepolymers which may be crosslinked in aqueous solution by reaction with >NH, --SH, --OH, --COOH; or other polyazetidines which may be crosslinked by H.sub.2 O removal, heat, or by changing to a more basic pH. The following is an idealized structure of a representative polyazetidine such as Polycup.RTM. 172 (Hercules, Inc.) which is useful for present purposes: ##STR1## where R is typically --CH.sub.2 --.sub.4
(2) carboxymethyl cellulose which can be crosslinked in aqueous solution by reaction with polyvalent ions such as Fe.sup.+++, Al.sup.+++, Ca.sup.++, Mg.sup.++. The following is an idealized structure of a carboxymethyl cellulose polymer such as CMC7HF (Hercules, Inc.): ##STR2##
(3) polyurethane hydrogel prepolymers which can be crosslinked in aqueous solution by reaction with --NH, --SH, --OH, --COOH or H.sub.2 O. The following is an idealized structure of a representative polyurethane hydrogel prepolymer which is made by taking a water soluble polyether polyol having greater than two hydroxyl groups per molecule and a molecular weight greater than 3,000 and capping each hydroxyl group with a low molecular weight polyisocyanate: ##STR3## where R.sub.1 typically is a low molecular weight polyol fragment (from glycerol, pentaerithritol, sorbitol, etc.);
a and b are integers, e.g. a is typically>10 and the ratio of a/b is generally from 2 to 5, the sequence of arrangement of the a and b segments being random or in blocks;
n is also an integer typically>2; and
R.sub.2 is typically a diisocyanate such as a toluene diisocyanate, methylene di(phenylisocyanate), m-xylylene diisocyanate, isophorone-diisocyanate, hexamethylene diisocyanate, hexahydro-m-xylylene diisocyanate, dodecahydro-methylene di(phenylisocyanate) and the like; and
(4) polymethylene isocyanates which can be cured by mixing with water such as the following: ##STR4## where n=0 to 4
Such polyisocyanates are commercially available and are commonly called "crude polymeric methylene di(phenylisocyanates)". Other polyisocyanates which are convertible into crosslinked insoluble polymers with water are also thought to be useful, e.g. toluene diisocyanates, methylene di(phenylisocyanate), m-xylylene diisocyanate, isophorone-diisocyanate, hexamethylene diisocyanate, hexahydro-m-xylylene diisocyanate, dodecahydro-methylene di(phenylisocyanate) and the like.
The isocyanates are usefully employed by coating an appropriate particulate substrate and then mixing with an aqueous slurry of E. coli cells.
Any of the above-noted polymer systems may be used to immobilize L-aspartase active E. coli cells to provide cell/polymer compositions having a variety of different forms and shapes. For example, the immobilized cell/polymer composition may be prepared in the form of membranes, filaments, fibers, tubes, beads or the like. A particularly important embodiment of the invention involves providing the immobilized cell/polymer composition as a coating on an appropriately shaped support which advantageously, although not necessarily, is in the form of solid or reticulated beads or particles composed of an inert solid organic or inorganic, porous or non-porous material. As noted earlier, the composition of the invention can be cured and dried without substantively affecting the L-aspartase activity of the cells and, as a consequence, the composition can be made up in the form of dried coated beads or other particulate material and stored until needed for use. Typically useful supports or carriers for the immobilized cell/crosslinked polymer compositions of the invention include the following in bead or particle form:
Molecular sieves
Ion exchange resins
Alumina
Silica and silica gel
Foraminifera skeletons
Polymer latexes
Metals
It is a useful property of the polymer systems used in the present invention that they can be contacted or mixed in water with E. coli cells containing L-aspartase and then crosslinked (or cured) to form insoluble and relatively fixed polymer matrices which hold or otherwise immobilize the E. coli cells. It is particularly useful that the crosslinking conditions which need to be used are mild enough so that the L-aspartase activity of the E. coli mutant cells is maintained.
As indicated, a particularly desirable composition according to the invention is obtained by applying the E. coli cells containing L-aspartase activity and the immobilizing polymer as a coating on hard inorganic or organic polymer beads. Using these relatively noncompressible compositions an L-aspartase active catalyst bed capable of high throughput in a fixed bed or fluidized bed is possible. As noted earlier, the L-aspartase active immobilized cell compositions previously described in the literature involving the use of relatively soft, compressible .kappa.-carrageenan gum or polyurethane foam are compressible and therefore tend to plug under high flow rates, and/or tall column (bed) heights.
Various methods may be used to immobilize the E. coli ATCC 11303 cells, while retaining their L-aspartase activity, by combination with cured or crosslinked forms of prepolymers according to the invention. The preferred method used in any specific situation will depend, at least to some extent, on the prepolymer involved. Thus:
(a) In the case of the preferred polyazetidine prepolymers, E. coli ATCC 11303 cells are advantageously mixed with an aqueous solution of the prepolymer so as to obtain a homogeneous mixture after which the polyazetidine may be cured or crosslinked to give an insoluble L-aspartase active composition by any of the following means:
Removal of part or nearly all of the water at temperatures below 60.degree. C. (usually between 40.degree. and 0.degree. C.) and pressures of 760 to 1.0 Torr; raising the pH above 7.5; exposing the E. coli/polyazetidine mixture to polyamines (using, for example, 100 parts of the composition for each 1-2 parts/wt. of polyethylene imine, polyamino ion exchange resins, diethylene triamine, ethylene diamine, etc.)
(b) For carboxymethyl cellulose (CMC) gums, homogeneous mixtures with E. coli ATCC 11303 may be crosslinked (cured) to insoluble, L-aspartase active coatings, membranes, fibers, beads, etc., by contacting an aqueous mixture of, for example, 1.0 part/wt. of cell paste/CMC mixture with an aqueous solution of 0.001 to 1.0 parts/wt. of polyvalent cation salt or, ideally 0.01 to 0.4 parts/wt. of polyvalent cation salt per 1.0 part/wt. of the cell paste/CMC mixture.
The resultant water insoluble immobilized cells/polymer network composition can be thus cured in the form of membranes, fibers or beads, but most efficiently as a coating around high surface area particles. As an illustration, 10 to 1000 parts/wt. of the high surface area particles may be coated with 1.0 part/wt. of cell paste/CMC mixture and ideally 50 to 500 parts/wt. of the particles per 1.0 part/wt. of cell paste/CMC mixture are used. Removal of 75% or more of the water contained in the cured coatings may be desirable to improve strength and bonding of the cell/polymer coating.
(c) When polyurethane hydrogels are used, homogeneous aqueous dispersions of E. coli ATCC 11303 (typically 1.0 g of cells per 1.0 to 1000 ml H.sub.2 O broadly and 10 to 100 ml H.sub.2 O preferably) are mixed with the hydrogel prepolymer and the prepolymer is cured into a water-insoluble L-aspartase active composition by allowing the polyisocyanate to react with water or in a more rapid manner by either removing 50 to 100% of the available water at 1000 to 0.1 Torr and below 50.degree. C. (preferably 760 to 5.0 Torr and 0.degree. to 30.degree. C.) or by exposing the undried compositions to aqueous solutions of molecules having more than two primary or secondary amine groups. Typically these polyamine molecules can range from hydrazine or ethylene diamine to polyethylene imine. Generally for each 1.0 g of hydrogel prepolymer used, from 0.01 to 10.0 g of the polyamine in from 1.0 to 500 ml of water could be used. Ideally 0.1 to 1.0 g of the polyamine and 10 to 100 ml of water are employed per gram of hydrogel prepolymer used.
The above E. coli/hydrogel compositions can be fabricated into membranes, fibers, beads, etc.; but a preferred configuration is to use the compositions as coatings onto high surface area particles, as discussed before. Depending on the surface area of the particle employed from 0.1 to 100.0 g of the E. coli/hydrogel composition can be coated onto 100 g of the particle.
(d) In the case where polyisocyanates are used, these are generally first applied to a surface and the cells of E. coli ATCC 11303 thereafter added thereto. Usually, from 0.1 to 20.0 g of the polyisocyanate per 10.0 g of the surface material can be employed, preferably 0.5 to 10.0 g of polyisocyanate per 10.0 g of surface material. The polyisocyanates, if liquid, can be added undiluted to the substrate with good mixing (agitator or tumbling). However, the preferable method is to use solutions of the polyisocyanates in inert, readily evaporated solvents such as toluene, acetone, chloroform, tetrahydrofuran, dimethoxyethane, ethyl acetate, and the like. These solutions are added to the substrate, preferably dry particles of high surface area, with good mixing and the solvents removed at their boiling points at 760 Torr or below while continuing good mixing to insure homogeneously coated, mobile substrate particles. The amounts of solvents used will usually range from 1.0 to 100 parts/wt. per 1.0 parts/wt. of polyisocyanate.
The immobilized cell/polymer compositions of the invention may be used to make aspartic acid by either a batch or continuous process. However, it is noted that these compositions, particularly when coated onto a bead or other particulate support, are especially effective for the continuous conversion of aqueous solutions of ammonium fumarate to ammonium L-aspartate according to the following equation: ##STR5##
As illustrative of processes which may be used to prepare L-aspartic acid or ammonium L-aspartate according to the invention are the following:
(i) A batch type process wherein the catalyst compositions are stirred in from 0.1 to 5.0 molar (preferably 0.5 to 2.0 molar) solutions of ammonium fumarate in water at 5.0 to 10.0 pH (preferably 7.5 to 9.5 pH) for periods of 1.0 to 100 hours (preferably 8 to 48 hours) at temperatures below 50.degree. C. (preferably 20.degree. to 40.degree. C). Broadly from 0.05 to 50 g of immobilized cells, preferably from 1.0 to 15 g, are used per 1.0 mole of starting ammonium fumarate. After the conversion, the catalyst compositions may be removed by filtration or the equivalent for reuse in converting fresh batches of fumarate solutions. The product solutions are obtained in a form suitable for conventional processing to isolate the L-aspartic acid (acidification, precipitation, filtration, washing, recrystallization, drying).
(ii) A continuous process wherein the catalyst compositions, e.g. coated beads, are placed in columns and the solutions of ammonium fumarate (concentrations, pH's, and temperatures are the same as described above for the batch processes) are passed through the catalyst beds either from above or from below (fluidized bed mode). The rates of passage of these fumarate solutions may range from 0.1 to 1000 space velocities/hour. For example, 5.0 liters of solution per hour may be passed through 1.0 liter of catalyst bed representing 5.0space velocities (S.V.) per hour. Preferably the fumarate solution flow rates which yield essentially 100% conversion of the fumarate to the L-aspartate fall in the range of 0.5 to 20.0 S.V./hour. The effluent from these columns of catalyst beds is suitable for conventional processing to isolate L-aspartic acid (as outlined above in the batch processes).
The invention is illustrated by the following Examples:

EXAMPLE 1
Preparation of E. coli Containing L-Aspartase Immobilized in CMC Gum.
To 10 g of a 1% aqueous solution of high molecular weight carboxymethyl cellulose (Hercules 7 HF CMC gum, approximate molecular weight of 700,000 and 0.65 to 0.85 carboxymethyl groups per anhydroglucose units) was added 0.5 g of a paste of the E. coli cells, American Type Culture Collection #11303. A thoroughly homogeneous dispersion was made by hand mixing with a wooden stick. A 2.0 g aliquot of this dispersion was placed onto 10 g of hydrated 5 A molecular sieve beads (8-12 mesh, previously hydrated by mixing 100 g of the beads with 200 g of water following by decanting the excess water and allowing the beads to dry at 25.degree. C. in air). After a thorough mixing by hand for five to ten minutes, uniformly coated, damp, but free flowing, beads were obtained. These coated beads were then poured into 40 ml of a 0.1% solution of FeSO.sub.4.nH.sub.2 O in water. After 4 hours of periodic gentle stirring at 25.degree. C. the liquid was decanted (considerable gel microparticles were noted in the liquid) and the beads washed four times with 0.1M sodium phosphate buffer solution. A total of 22.2 g of wet coated beads were obtained. The beads were stored at 5.degree. C. in damp air. For L-aspartase activity (see Table I) a 5.0 ml aliquot of these wet beads was taken. This aliquot weighed 6.3 g and was estimated to contain 0.027 g of the E. coli cells ##EQU1##
EXAMPLE 2
Preparation of E. coli cells Containing L-Aspartase Immobilized In a Polyurethane Hydrogel.
(a) A polyurethane hydrogel prepolymer was prepared by capping a 7,000 molecular weight water soluble polyether (high level of polyoxyethylene segments) triol, Pluracol.RTM. V-7 from BASF Wyandotte, with three mols of dodecahydromethylene di(phenylisocyanate), Desmodur.RTM. W from Mobay Chemical Company. A solution of 1.0 g of this hydrogel prepolymer in 9.0 g of water was thoroughly mixed with 1.0 g of E. coli ATCC 11303 cell paste at 25.degree. C. To 20 g of hydrated 5 .ANG. 8-12 mesh molecular sieve beads was added a 2.0 g aliquot of the E. coli-hydrogel prepolymer aqueous dispersion. The resultant mixture was stirred over a period of 10 minutes by hand with a wooden stick at 25.degree. C. to give 22.0 g of wet but free flowing coated beads. Preliminary experiments showed that 10% solutions of this hydrogel prepolymer in water formed water soluble gels upon drying at 25.degree. C. in air for 8 to 24 hours. Thus, the wet coated beads were allowed to dry in the open air at 25.degree. C. for 16 hours to give 20.1 g of free flowing cured coated beads. A 4.3 g aliquot of these coated beads had a volume of 5.0 ml and an estimated E. coli cell content of 0.039 g ##EQU2## This 5.0 ml sample was used for L-aspartase activity measurements (see Table 1).
(b) A 1.0 g aliquot of the aqueous E. coli-hydrogel prepolymer dispersion described above was also coated onto 10.0 g of 5 .ANG. 8-12 mesh, hydrated molecular sieve beads at 25.degree. C. After stirring for 5 to 10 minutes the resultant free flowing wet beads were poured with good mixing into 40 ml of a 0.1% solution of polyethylene imine (Aldrich Chemical Co. #18197-8) in water. Preliminary experiments showed that a fresh, less than 15 minute old, solution of 1.0 g of hydrogel prepolymer in 10 ml H.sub.2 O formed a water insoluble gel immediately upon contacting a 0.1% aqueous solution of the polyethylene imine. The slurry of coated beads in the polyethylene imine solution were gently stirred for 30 minutes at 25.degree. C. and then washed four times with 40 ml portions of 0.1M sodium phosphate buffer solution (pH 7.5) to give 11.5 g damp, free flowing beads. A 5.0 ml aliquot of those beads weighed 5.1 g and was estimated to contain 0.040 g of the E. coli cells ##EQU3## This 5.0 ml aliquot was used for L-aspartase measurements (see Table I).
(c) A polyurethane hydrogel membrane having E. coli ATCC 11303 containing L-aspartase was prepared in the following manner:
A slurry of 10.0 g of E. coli ATCC 11303 cell paste in 10.0 g of phosphate buffered saline water (pH 7.4) was mixed for 30 minutes at 25.degree. C. to insure a homogeneous dispersion. A solution of 5.0 g of the above mentioned hydrogel prepolymer (7,000 molecular weight triol capped with three moles of Desmodur.RTM. W) in 10.0 g of deionized water was formed by vigorous stirring for one minute at 25.degree. C. This solution was mixed with the homogeneous cell paste slurry. Within 20 seconds of vigorous stirring the resultant mixture became quite thick and was immediately poured onto a Teflon.RTM. sheet. Within a few seconds at 25.degree. C. the mixture became an elastomeric gel. After 45 minutes in air at 25.degree. C. the resultant elastomeric membrane composite (1/16" to 1/4" thick by 4" diameter) was stripped off the Teflon.RTM. surface.
The membrane was placed in 500 ml of 1.5M ammonium fumarate solution and shaken for 30 minutes. Considerable turbidity developed in the aqueous solution indicating cells and/or gel were washed out of the membrane. This washing process was repeated with one liter of the 1.5M ammonium fumarate solution at 25.degree. C. for 64 hours. The solution was only very slightly hazy and its optical density at 280 nm (1/1000 dilution) was 0.005 compared to 0.43 (1/1000 dilution) at the start. This indicates that essentially all the ammonium fumarate had been consumed.
The membrane was removed intact and placed in 750 ml fresh 1.5M ammonium fumarate. After 16 hours of gentle stirring at 25.degree. C. the clear product liquid over the membrane had an optical density at 280 nm (1/1000 dilution) of 0.005. This process was repeated with 750 ml more of the ammonium fumarate for 20 hours at 25.degree. C. The combined 15000 ml of product solution was clear and had an optical density at 280 nm of 0.005.
A 1000 ml aliquot of the combined product solution was acidified to a pH of 2.8 using 145 g of concentrated hydrochloric acid. The resultant slurry of white crystals was kept at 5.degree. C. for 16 hours and then filtered. The damp filter cake was then stirred in 1000 ml of deionized water at 80.degree. to 90.degree. C. for 2 hours and then allowed to cool to 30.degree. C. The white crystalline solids were collected by filtration and washed with 250 ml deionized water. The solids were dried at 25.degree. C. to 100.degree. C. and 5 to 20 Torr for 16 hours to a constant weight of 178.0 g which represents an 89.4% yield of L-aspartic acid ##EQU4## The optical rotation of a solution of 2.04 g of the white solid in 100 ml of 6.0N HCl was measured on a Perkin-Elmer polarimeter at 25.degree. C. and found to be +0.497. On the same instrument a solution of 2.04 g of an authentic sample of L-aspartic acid (Sigma Chemical Co. #A-9256) had a rotation of +0.495.
EXAMPLE 3
Preparation of E. coli Containing L-Aspartase Immobilized On Surfaces Pretreated with Polyisocyanates.
(a) A 10.0 g sample of activated anhydrous 5 .ANG., 8-12 mesh molecular sieve beads was mixed in a rotary evaporation apparatus with a solution of 2.0 g of a crude polymeric aromatic polyisocyanate (Upjohn Chemical Company PAPI.RTM. 20, 7.1 meg NCO/g) in 50.0 g of dry toluene. The toluene was removed at 85.degree. C. and 10 to 20 Torr over a period of an hour of continued tumbling. The free flowing impregnated beads were cooled to 25.degree. C. and a slurry of 1.0 g E. coli ATCC 11303 paste in 1.0 g of 0.1M sodium phosphate buffer (pH 7.5) was added. The resultant bead mixture was tumbled slowly for four hours at 25.degree. C. and one atmosphere to give 12.9 g dry free flowing beads. A 5.0 ml aliquot of the dry beads weighed 4.9 g. This volume did not change after soaking in 1.5M ammonium fumarate solution. An estimated 0.38 g of E. coli cells were on this 5.0 ml aliquot ##EQU5## which was used to measure L-aspartase activity (see Table I).
(b) In a similar manner 10.0 g of anhydrous, weakly basic, >N--H form, ion exchange beads (Rohm & Haas, Amberlite.RTM. IRA45, 0.42 mm diameter dried at 85.degree. to 90.degree. C. and 5 to 20 Torr for several hours) were treated with a solution of 2.0 g PAPI.RTM. 20 in 50 ml dry toluene. Removal of the toluene at 85.degree. to 90.degree. C. and 5 to 20 Torr over a period of an hour gave a smoewhat sticky but still mobile mass of coated beads. To this tumbled mixture was added a slurry of 1.0 g E. coli ATCC 11303 paste in 1.0 ml of 0.1M sodium phosphate (pH 7.5) buffer solution. To aid in achieving a homogeneous coating of this rather gummy mass, sixty 0.25" diameter Teflon.RTM. balls were added. The resultant mixture was tumbled at 25.degree. C. and 5 to 20 Torr for two hours to give, after removal of the Teflon.RTM. balls, 15.6 g of dry free flowing coated beads. A 5.0 ml aliquot of these coated beads weighed 2.8 g and did not change volume after soaking in 1.5M ammonium fumarate solution. This 5.0 ml aliquot was used for L-aspartase measurements (see Table I) and was estimated to contain 0.18 g of E. coli ##EQU6##
EXAMPLE 4
Preparation of E. coli Containing L-Aspartase Immobilized With Polyazetidine Gels.
(a) A mixture of 2.0 g of an aqueous polyazetidine solution (Hercules Polycup.RTM. 172, as received 12% solids in H.sub.2 O) and 2.0 g of E. coli ATCC 11303 paste was stirred rapidly with a magnetic stirring bar for five minutes at 25.degree. C., to insure a homogeneous dispersion. This mixture was then poured out onto a polystyrene surface to dry at 16 hours and 25.degree. C. The resultant 2".times.2".times.1/16" thick flexible membrane was stripped from the surface and found to weigh 0.7 g. This film was used in L-aspartase measurements (see Table I) and was estimated to contain 2.0 g of E. coli cells (hydrated state).
(b) A homogeneous mixture of 2.0 Polycup.RTM. 172 and 2.0 g E. coli ATCC 11303 was distributed onto 30 g of hydrated 5 .ANG., 8-12 mesh molecular sieve beads by means of tumbling at 25.degree. C. and 5 to 20 Torr for 45 minutes. After 16 more hours drying at 25.degree. C. in open air the resultant coated beads weighed 30.4 g. A 5.0 ml aliquot of these coated beads weighed 3.9 g. This sample was used for L-aspartase activity (see Table I) and was estimated to have 0.26 g of E. coli cells ##EQU7##
(c) A homogeneous dispersion of 2.0 g E. coli ATCC 11303 in 2.0 g of Polycup.RTM. 172 at 25.degree. C. was dispersed onto 30.0 g of Amberlite.RTM. IRA 45 ion exchange beads (as received, 42% H.sub.2 O, >N--H form) by hand mixing with a wooden stick for 30 minutes at 25.degree. C. A thin layer of the somewhat sticky mixture was allowed to stand in air at 25.degree. C. for 16 hours. The resultant free flowing beads weighed 25.8 g. A 3.0 g sample of these dry coated beads had a volume of 5.0 ml. Upon soaking in 1.5M ammonium fumarate solution the volume expanded to 5.5 ml. A 5.0 ml aliquot of these wet coated beads was taken for L-aspartase measurements (see Table I) and the estimated E. coli content was 0.21 g ##EQU8##
(d) A homogeneous dispersion of 2.0 g E. coli ATCC 11303 in 4.0 g deionized water and 2.0 g Polycup.RTM. 172 was added over a period of 3.5 hours in three equal portions to 10.0 g of Amberlite.RTM. IRA 45 (as received, 42% H.sub.2 O, free >N--H form) containing sixty 0.25 diameter Teflon.RTM. balls. This mixture was tumbled at 25.degree. C. at 5 to 20 Torr. After a total of five hours of drying at reduced pressure the resultant dry, coated beads (Teflon.RTM. balls removed) weighed 7.8 g. A 5.0 aliquot of these dry, free flowing coated beads weighed 2.9 g. After saturating with 1.5M ammonium fumarate solution the volume swelled to 6.25 ml. A 5.0 ml aliquot of these wet, coated beads was taken for L-aspartase measurements (see Table I). The estimated E. coli content of this aliquot was ##EQU9##
(e) A homogeneous dispersion of 3.0 g E. coli ATCC 11303 in 6.0 ml deionized water plus 3.0 g of Polycup.RTM. 172 was spread onto 10.0 g of Amberlite.RTM. IRA 45 (as received, 42% H.sub.2 O, free >N--H form) in the same manner of drying at reduced pressure described above. A total of 10.7 g dry, coated, free flowing beads were obtained. A 5.0 ml aliquot of dry coated beads weighed 3.0 g. After soaking in 1.5M ammonium fumarate solution this volume swelled to 5.75 ml. A 5.0 ml aliquot of the wet, coated beads was taken for L-aspartase measurement (see Table 1). The estimated E. coli content of this 5.0 ml aliquot was 0.73 g ##EQU10##
(f) A homogeneous dispersion of 4.0 g E. coli ATCC 11303 in 4.0 g of Polycup.RTM. 172 and 8.0 g deionized water was added in approximately six equal portions over a 5.5 hour period at 25.degree. C. and 5 to 20 Torr to 10.0 g of Amberlite.RTM. IRA 938 beads (Rohm and Haas, 73% H.sub.2 O, 0.38 mm diameter, tert. amine chloride salt form) containing eight 0.5" diameter Teflon.RTM. balls. After 6 hours total of tumbling at 25.degree. C. and 5 to 20 Torr the resultant dry, coated free flowing beads weighed 10.3 g and had a volume of 16.6 ml. Soaking these beads in excess 1.5M ammonium fumarate solution (pH 8.5) for 16 hours at 25.degree. C. gave 17.5 ml wet beads. A 5.0 ml aliquot of the wet beads, estimated to contain 1.14 g E. coli ATCC 11303 ##EQU11## was taken for L-aspartase activity measurements (see Table I).
EXAMPLE 5
Coating Molecular Sieve Beads and Ion Exchange Resin Beads with E. coli Cells Containing L-Aspartase Using No Polymer Binders.
To demonstrate the utility of the above described polymer systems used to immobilize the E. coli cells containing L-aspartase, the following experiments were conducted to coat materials with the cells containing L-aspartase alone, i.e. with no polymer binders.
(a) A homogeneous slurry of 1.0 g E. coli cells, ATCC 11303, containing L-aspartase in 5.0 ml of Na phosphate buffer (0.1M, pH 7.5) was added in four equal portions over a period of 3.5 hours to 10.0 g of hydrated 5 A molecular sieve beads (8-12 mesh) also containing ten 0.5" diameter Teflon.RTM. balls. This mixture was tumbled at 25.degree. C. and 5 to 10 Torr. After a total of about 4.0 hours the resultant dry, coated, free flowing beads weighed 9.9 g. A 5.0 ml aliquot of these dry beads weighed 4.2 g. The volume did not change upon soaking in 1.5M ammonium fumarate solution. The estimated E. coli cell content of this aliquot of coated beads was ##EQU12## A 5.0 ml aliquot of the coated beads was gently stirred in 50 ml 1.5M ammonium fumarate solution at 25.degree. C. for 24 hours. The solution became very turbid indicating considerable amounts of material were sloughing off the beads. The beads were isolated by decantation and again gently stirred in 50.0 ml fresh 1.5M ammonium fumarate at 25.degree. C. for L-aspartase activity measurement (see Table I). However, even after one hour the solution became very turbid again. On several more occasions the beads were isolated and gently stirred in fresh 1.5M ammonium fumarate solution. The beads continued to give off considerable amounts of material to make the solutions very turbid. This behavior was not observed in any of the preparations of L-aspartase active cell coatings of beads where the polymer binders were also added to the formulation. In all the polymer binder examples the ammonium fumarate solutions over the coated beads remained clear.
(b) In a similar way, a slurry of 10.0 g E. coli ATCC 11303 in 30 g of aqueous phosphate buffer solution (0.1M, pH 7.5), but no polymer binders, was coated onto 50.0 g of Amberlite.RTM. IRA 45 (as received from Rohm and Haas, 42% H.sub.2 O, >N--H form) over a period of 4.5 hours at 25.degree. C. and 5 to 20 Torr. The resultant 47.6 g of free flowing dry, coated beads had a volume of 83.5 ml. Upon soaking these beads in excess 1.5M aqueous ammonium fumarate the solution became thick and opaque from the massive amount of material detached from the beads. All attempts to filter (cotton wadding, fiber-glass mat, 43 mesh nylon screen, medium porosity sintered glass) off the beads from this opaque mother liquid failed because the thick gelatinous particles quickly plugged the filters. This behavior was not observed in any of the examples where the polymer binders were incorporated into the formulation. In these cases the aqueous solutions over the beads remained clear at all times, and flowed quickly through filters.
EXAMPLE 6
L-Aspartase Activity Measurements
Shown in Table I are the L-aspartase activities of the immobilized E. coli ATCC 11303 compositions described in the preceding examples. In each case the samples were preconditioned by gently shaking in 50 ml of a 1.5M ammonium fumarate solution in deionized water (pH 8.5) containing 0.002M MgSO.sub.4 for a period of 8 to 16 hours at 25.degree. C. The solution was then drained from each sample and 50 ml fresh fumarate solution added prior to gentle shaking again for 8 to 16 hours at 25.degree. C. At this point all the samples prepared with the polymer binders discussed in the previous examples showed no evidence of material sloughing off the solid supports; i.e., their supernatent solutions were all clear. Samples prepared using no polymer binders (Example 5) continued to give very turbid supernatant solutions even after several washings. This indicates the cell material was not securely bound to the solid supports.
The next step in each example was to take a 5.0 ml aliquot (or in the case of the membrane, a 2".times.2".times.0.125" section) of the washed and well drained composites and gently shake in a fresh 50.0 ml of the above mentioned ammonium fumarate solution at 25.degree. C. Samples were removed after 60 minutes and diluted 1/1000 with deionized water. The decrease in optical density at 280 nm from the starting 1.5M ammonium fumarate solution (observed to be 0.43 at 1/1000 dilution) indicated the L-aspartase activity. The optical density of a 1.5M L-aspartic acid ammonium salt (pH 8.5) at 280 nm is essentially zero (<0.005).
The observed conversion of the fumarate to the L-aspartate is shown in Table I as moles of aspartic acid/hr/liter of catalyst bed and as moles of aspartic acid/hr/kg wet E. coli. For example in experiment #4d using polyazetidines, cell paste and ion exchange beads, the optical density at 280 nm dropped from 0.43 to 0.32 after 60 minutes at 25.degree. C. The calculations are: ##EQU13## Also shown in Table I are values calculated from data in the literature showing the L-aspartase performance at 37.degree. C. of a polyurethane foam (HYPOL.RTM.) containing E. coli ATCC 11303. Here a 0.777 l bed having 126 g of cells required 32 minutes to convert 2.0 liters of 1.0M fumarate 100% to L-aspartate at 37.degree. C. These workers also report the average rate of conversion of 1.5M fumarate to be 8% lower than 1.0M fumarate solution. They also observed rates of 37.degree. C. to be 1.67 times rates at 25.degree. C. Thus a fair estimate of their L-aspartic acid production rate for comparison to our data (25.degree. C., 1.5M fumarate) is: ##EQU14## Comparing these values to the data obtained representative of the present invention shows the superiority of the present process over the polyurethane foam system.
TABLE I__________________________________________________________________________ASPARTASE ACTIVITY OF BOUND E. COLI (ATCC 11303) AT 25.degree. C. Est. g of E. coli Moles of ASP Moles of ASP used (per 5.0 mlEXAMPLE # BINDING METHOD (hr .times. 1 cat. bed) (hr .times. kg wet E. bed samp)__________________________________________________________________________1 CMC + Fe.sup.+++ 0.87M.S. beads 185 0.0272a P.U. Hydrogel via drying on 0.45 57.7 0.039 M.S. beads2b P.U. Hydrogel via poly EI on 0.27 33.8 0.040 M.S. beads3a PAPI 20 on M.S. beads 2.5 32.9 0.383b PAPI 20 on I.E. beads 1.2 33.3 0.184a Polycup 172 film 65.0 0.804b Polycup 172 on M.S. beads 0.6 11.5 0.264c Polycup 172 on I.E. beads 1.0 23.8 0.214d Polycup 172 on I.E. beads 3.8 32.5 0.594e Polycup 172 on I.E. beads 3.9 26.7 0.734f Polycup 172 on I.G. beads 12.75 55.9 1.145a E. coli alone (No binder) on 2.6* 30.9* 0.42* M.S. beads-- HYPOL foam (estimate from data 2.69 16.4 of Fusee et.al).sup.2__________________________________________________________________________ *Massive amounts of cells sloughed off the beads, thus much of the activity shown is caused by unbound cells.
EXAMPLE 7
Continuous Production of L-Aspartic Acid (as ammonium L-aspartate).
A 5.0 ml aliquot of the wet beads from Example #4d were placed in a 0.7 cm diameter.times.15 cm jacketed glass column. The column temperature was maintained at 37.degree. C. A fresh 1.5M ammonium fumarate solution in deionized water containing 0.002 m MgSO.sub.4 (all at pH 8.5) was continuously passed up through the bed of beads at a rate of 0.5 ml/min. Samples of the effluent product solution were taken periodically and analyzed for L-aspartate content as 1/1000 dilutions in deionized water as described in Example 6. The bulk of the effluent was collected but not returned to the column. The following data show that over a period of 50 days of continuous running the L-aspartase activity of the coated beads remained essentially unchanged.
______________________________________ L-aspartate contentTime, days of effluent, %______________________________________ 1 59.625 61.5 62.5 average50 66.5______________________________________
At the 62.5% conversion rate for a flow of 6.0 bed volumes/hr (0.5 ml/min through 5.0 ml of catalyst bed) the production rate of L-aspartic acid is: ##EQU15## For a period of one hour at 37.degree. C. the same column was run at the rate of 4.0 bed volumes/hr (0.33 ml/min through 5.0 ml of catalyst bed) and the average rate of fumarate (1.5M) conversion was 80.0%. This corresponds to: ##EQU16## Based on these conversion rates of 62.5% and 80.0% at 6.0 and 4.0 bed vol/hr respectively, a conservative estimate by graphical methods, of the flow rate required to achieve 100% conversion is 1.5 bed volumes/hr. At 1.5 bed volumes/hr the L-ASP production rate is: ##EQU17## These values (100% conversion at 1.5 bed vol/hr, and ##EQU18## are significantly better than the values of 1.1 bed vol/hr for 100% conversion and ##EQU19## reported for the continuous operation of a column of E. coli ATCC 11303 cells immobilized on k-carrageenan gel.
In a further variation of the invention, it is contemplated that the aqueous ammonium L-aspartate solution obtained in Example 7 may be used directly, i.e. without recovery or separation of dry, solid aspartic acid, for reaction with benzyl chloroformate to form the benzyloxy carbamate of the amine of aspartic acid, this carbamate being an important intermediate in the preparation of the commercially important sweetener, L-aspartyl-L-phenylalanine methyl ester. Presently this benzyloxy carbamate is made by starting with dry, crystalline solid L-aspartic acid. The acid is dissolved in aqueous sodium hydroxide prior to reaction with benzyl chloroformate according to the following reactions: ##STR6## The immobilized whole cell enzymatic process for converting ammonium fumarate to ammonium L-aspartate according to the invention provides directly a basic aqueous product stream of, for example, 1.5 molar 98.5% ammonium L-aspartate solution which, after removal of ammonia, is suitable for direct use in the reaction of benzyl chloroformate (or other chloroformate) to make the desired aqueous solution of benzyl (or other) oxycarbamates. This should make it possible to avoid the need to isolate dry aspartic acid crystals and the time and expense incident thereto. For example, the isolation of dry aspartic acid crystals from the ammonium L-aspartate solution of Example 7 would generally require the following:
(1) acidification of the 1.5 molar ammonium L-aspartate product (L-ASP) stream using approximately 0.7 to 0.8 moles of H.sub.2 SO.sub.4 to precipitate the L-ASP at pH of 2.8. This offers a prospective corrosion problem and the expense involved in disposing of the ammonium sulfate by-product;
(2) although the L-ASP product stream may contain 98.5% L-ASP (the rest is ammonium fumarate), the precipitate of L-ASP and washing with water gives only an 89-93% yield of solid L-ASP. The retention of 5-9% of the L-ASP in the mother liquor is an appreciable loss, considering the value of the L-ASP.
(3) subsequent drying of the precipitated L-ASP crystals is also costly (estimated at about 5-10 cents per pound).
Use of the aqueous ammonium L-ASP product directly, according to the invention, eliminates the disadvantage inherent in steps (1)-(3). Adjustment of the ammonium L-ASP product stream is appropriate to obtain optimum results. For example, the addition of sodium hydroxide (in the order of 0.5 to 2.0 moles/mole ammonium L-ASP) results in displacement of the NH.sub.4.sup.+ as NH.sub.3 which can be boiled off and used to make additional ammonium fumarate. Most of the NH.sub.4.sup.+ ion should be removed to facilitate the chloroformate reaction.
The invention is not limited to the immobilization of E. coli cells or the use of such immobilized cells for the production of L-aspartic acid. Thus, other cells may be immobilized in generally similar fashion using the indicated curable polymeric materials. Such further immobilized cell variations, and uses thereof. are exemplified in the following examples:
EXAMPLE 8
Production of L-Alanine Via Immobilization of a Pseudomonas dacunhae Immobilized with Polyazetidine Gels.
Pseudomonas dacunhae ATCC #21192 was cultured on a medium of: peptone (Bacto-Difco), 9.0 g/L.; casein hydrolysate (Casamino acids, Difco), 2.0 g/L.; KH.sub.2 PO.sub.4, 0.5 g/L.; MgSO.sub.4.7H.sub.2 O, 0.1 g/L.; and L-glutamic acid sodium salt, 15.0 g/L., pH adjusted to 7.2 with NH.sub.4 OH. The fermentation was carried out under aerobic conditions for 23 hours at 30.degree. C., 300 rotations/min. A mixture of 3.62 grams (wet weight) of cell paste and 3.6 grams of aqueous polyazetidine solution (Hercules Polycup.RTM. 172) was stirred to homogenity at 25.degree. by hand mixing with a wooden stick. This mixture was dispersed on 3.6 g of Amerlite.RTM. IRA 938 ion exchange bead (Rohm and Haas) which had been previously air dried at 25.degree.-30.degree. C. for 60 hours to remove greater than 85% of the moisture associated with the beads. The thin film of the mixture on the beads was allowed to air dry at 25.degree. for 24 hours. The resulting free flowing beads occupied a volume of 20 ml. These beads were washed with 5 volumes of normal saline and an 18 ml. aliquot was placed in a flask containing 0.5 liters of 1.5M ammonium aspartate solution, pH 5.5 (adjusted with H.sub.2 SO.sub.4) which was held at 37.degree. C. The entire mixture was stirred for a period of 48 hours while the pH was maintained by the addition of sulfuric acid as needed.
Analysis of the liquid at the end of this period on HPLC (uNH.sub.2 Bondapak column, Waters Assoc.; eluant CH.sub.3 CN, 25%, 5 mM KHPO.sub.4 pH 4.4, 75%) showed that L-aspartic acid had been decarboxylated to form L-alanine in 98% yield.
EXAMPLE 9
Preparation of Penicillin G Acylase Containing Bacillus megaterium Immobilized With Polyazetidine Gels.
Bacillus megaterium ATCC 14945 was cultured under aerobic conditions as previously described (U.S. Pat. No. 3,446,705). A mixture of 10.5 g (wet weight) of the cell material and 10.5 g of an aqueous polyazetidine solution (Hercules Polycup.RTM. 172) was stirred to homogeneity at 25.degree. C. by hand mixing with a wooden stick. This mixture was dispersed onto 9.8 g of Amberlite.RTM. IRA 938 ion exchange beads (Rohm and Haas) which had been previously air-dried at 25.degree.-30.degree. C. for 60 hours which removed >85% of the moisture from the beads. A thin layer of the mixture was allowed to air dry at 25.degree. C. for 24 hours. The resultant free-flowing beads weighed 13.1 g and occupied a volume of 53 ml. A 1247 mg aliquot of these beads corresponding to 1 gram of free cells was assayed for penicillin acylase activity. 6-Aminopenicillanic acid production was quantitated by high pressure liquid chromatography (HPLC). The activity of the immobilized preparation was 19.7.mu. moles hr.sup.-1 g cell paste.sup.-1. This value was 67% of the free cell activity.
EXAMPLE 10
Preparation of Penicillin G Acylase Containing Escherichia coli Immobilized With Polyazetidine Gels.
Escherichia coli ATCC 9637 was cultured aerobically as described by Sato et al, Eur. J. Appl. Microbiol. 2:153-160 (1976). A mixture of 20.7 g (wet weight) of cell paste and 20.7 g of aqueous polyazetidine solution (Hercules Polycup.RTM. 172) was stirred to homogeneity at 25.degree. C. by hand mixing with a wooden stick. This mixture was dispersed onto 19.3 g of Amberlite.RTM. IRA 938 ion exchange beads (Rohm and Haas) which had been previously air-dried at 25.degree.-30.degree. C. for 60 hours to remove >85% of the moisture associated with the beads. A thin film of the mixture was allowed to air dry at 25.degree. C. for 24 hours. The resultant free-flowing beads weighed 27.4 g and occupied a volume of 95 ml. A 1325 mg aliquot of these beads corresponding to 1 gram of free cells was assayed for penicillin acylase activity. 6-Amino-penicillanic acid production was quantitated by high-pressure liquid chromatography (HPLC). The activity of the immobilized preparation was 53.6.mu. moles hr.sup.-1 gram cell paste.sup.-1 which was 99% of the free cell activity.
EXAMPLE 11
Immobilization of Arthrobacter Species Containing Glucose Isomerase Activity for Production of High Fructose Corn Syrup.
Arthrobacter species ATCC 21748 was grown under submerged aerobic conditions and the cells were harvested. The cells had a glucose isomerase activity of 420.mu. moles.hr.sup.-1.gm.sup.-1 cell paste (wet weight) at 60.degree. C.
To 47 gm of Polycup.RTM. 172 was added 47 gm of Arthrobacter species ATCC 21748 (wet weight) and the mixture was stirred vigorously for 5-10 minutes. The Polycup.RTM./cell mixture was then added slowly to 46.4 gm of air dried IRA.RTM. 938 beads with mixing and the resultant beads were dried at room temperature for 24 hours.
To a flask containing 5 ml of the Arthrobacter species ATCC 21748 immobilized beads was added 50 ml of 0.2M phosphate buffer, pH 7.5, 10 mM MgSO.sub.4, 1 mM CoCl.sub.2 and the solution was heated to 60.degree. C. with stirring. 450 mg of .alpha.-D-glucose was added to the flask and the flask was placed in an incubated shaker at 60.degree. C. for 1 hour at 150 rpm. The glucose isomerase activity of the immobilized Arthrobacter species ATCC 21748 was 530.mu. moles.hr.sup.-1.gm.sup.-1 cell paste (wet weight) at 60.degree. C. as determined by the cysteine/H.sub.2 SO.sub.4 reaction. (Dische, Biochim. Biophys. Acta 39, 140, 1960).
10 Ml of the Arthrobacter species ATCC 21748 immobilized beads were added to a 0.9.times.30 cm jacketed glass column which was maintained at 60.degree. C. by a circulating waterbath. Prewarmed substrate solution containing 250 mM glucose, 5 mM MgSO.sub.4 and 0.5 mM CoCl.sub.2 in 50 mM Tris-HCl buffer, pH 7.5, was passed through the column. After 6 days of continuous operation the glucose isomerase activity of the immobilized Arthrobacter species ATCC 21748 was 280.mu. moles.hr.sup.-1.gm.sup.-1 cell paste (wet weight) at 60.degree. C. and after 37 days the glucose isomerase activity was 18.mu. moles.hr.sup.-1.gm.sup.-1 cell paste (wet weight) at 60.degree. C.
EXAMPLE 12
Immobilization of Arthrobacter simplex Having Steroid Dehydrogenase Activity for The Production of Prednisolone or Related Steroids.
Arthrobacter simplex ATCC 6946 was grown under submerged aerobic conditions and the cells were harvested. The cells has a .DELTA.-1-dehydrogenase activity of 980.mu. moles.hr.sup.-1.gm.sup.-1 cell paste (wet weight) at 34.degree. C.
To 20 gm of Polycup.RTM. 172 was added 20 gm of A. simplex ATCC 6946 and the mixture was stirred vigorously for 5-10 minutes. The Polycup.RTM./cell mixture was then added slowly to 18.6 gm of air dried IRA.RTM. 938 beads with mixing and the resultant beads were dried at room temperature for 24 hours.
To a flask containing 5 Ml of the A. simplex ATCC 6946 immobilized beads was added 36 Ml of 20 mM phosphate buffer (pH 7.0) followed by 4 Ml of ethanol containing 60 mg of hydrocortisone. The flask was placed in an incubated shaker at 34.degree. C. for 1 hr at 150 rpm. The .DELTA.-1-dehydrogenase activity of the immobilized A. simplex ATCC 6946 was 440.mu. moles.hr.sup.-1.gm.sup.-1 cell paste (wet weight) at 34.degree. C. as determined by absorbance at 285 nm.
EXAMPLE 13
Immobilization of a Streptomyces Species Having Glucose Isomerase Activity for the Production of High Fructose Corn Syrup.
Streptomyces phaeochromogenes NRRL B3559 was grown under submerged aerobic conditions and the cells were harvested. The cells had a glucose isomerase activity of 7.7.mu. moles.min.sup.-1.gm.sup.-1 cell paste (wet weight) at 60.degree. C.
To 64.5 gm of Polycup.RTM. 172 was added 64.5 gm of S. phaeochromogenes NRRL B3559 and the mixture was vigorously stirred 5-10 minutes. The Polycup.RTM./cell mixture was then slowly added to 60.0 gm of air dried IRA.RTM. 938 beads with mixing and the resultant beads were dried at room temperature for 24 hours.
10 Ml of the S. phaeochromogenes NRRL B3559 immobilized beads were added to a 0.9.times.30 cm jacketed glass column which was maintained at 60.degree. C. by a circulating waterbath. Prewarmed substrate solution containing 250 mM glucose, 100 mM Na.sub.2 SO.sub.3, 10 mM MgSO.sub.4 and 1 mM CoCl.sub.2 adjusted to pH 7.0 with HCl was passed through the column at a flowrate of 28 ml/hr. The glucose isomerase activity of the immobilized S. phaeochromogenes NRRL B3559 was 7.7.mu. moles.min.sup.-1.gm.sup.-1 cell paste (wet weight) at 60.degree. C. as determined by the cysteine/H.sub.2 SO.sub.4 reaction (Dische et al supra).
EXAMPLE 14
Immobilization of a Rhodosporidum Species High In Phenylalanine Ammonia Lyase for the Production of Phenylalanine.
Rhodosporidium toruloides ATCC 10788 was grown under submerged aerobic conditions and the cells were harvested. The cells had an L-phenylalanine ammonia-lyase activity of 112.mu. moles.hr.sup.-1.gm.sup.-1 cell paste (wet weight) at 30.degree. C.
To 14.9 gm of Polycup.RTM. 172 was added 14.9 gm of R. toruloides ATCC 10788 and the cells mixture was vigorously stirred for 5-10 minutes. The Polycup.RTM./cell mixture was then added slowly to 13.8 gm of air dried IRA.RTM. 938 beads with mixing and the resultant beads were dried at room temperature for 24 hours.
To a flask containing 1 Ml of the R. toruloides ATCC 10788 immobilized beads was added 5 Ml of 25 mM Tris-HCl buffer (pH 8.8), 25 mM L-phenylalanine, 0.005% cetyl pyridinium chloride. The flask was placed in a Dubnoff shaking incubator at 30.degree. C. for 1 hour at 100 rpm. The phenylalanine ammonia-lyase activity of the immobilized R. toruloides ATCC 10788 was 10.mu. moles.hr.sup.-1.gm.sup.-1 cell paste (wet weight) at 30.degree. C. as determined by absorbance at 278 nm.
Those in the art will appreciate from the prior literature how the immobilized cell/polymer compositions disclosed in Examples 8-14 can be used to make the products indicated. Thus, with respect to Example 8, it is known that the production of L-alanine via decarboxylation of aspartic acid is mediated by the enzyme, L-aspartic-.beta.-decarboxylase. The presence of this enzyme is well known in many genera of microorganisms, as reported by Chibata et al, Applied Microbiology, Vol. 13, No. 5, pages 638-645 (1965). It is produced by Clostridium perfringens, Desulfovibrio desulfuricans, Nocardia globerula, Pseudomonas reptilivora, Acetobacter species, Achromobacter species, and Alcaligenes faecalis.
Chibata et al determined that alanine forming strains were fairly common in the general Acetobacter, Achromobacter, Pseudomonas, Torula, Torulopsis, Absidia, Aspergillus, Mucor, and Oospora. Chibata et al increased the knowledge previously obtained by Meister and coworkers and determined that L-aspartic acid was converted stoichiometrically to alanine. Isolated yields of L-alanine over 90% from L-aspartic acid were easily obtained. This process is described with respect to the organisms, Pseudomonas dacunhae and Achromobacter pestifer in U.S. Pat. No. 3,458,400, which claims a process for production of L-alanine in an aqueous nutrient medium, by dried living cells, or by cell free extracts. A modification of this process was patented by Chibata et al, 1975 (U.S. Pat. No. 3,898,128) by immobilization of the microorganism in acrylamide polymers. A further patent on the use of th enzyme from Pseudomonas dacunhae was obtained in 1969, U.S. Pat. No. 3,463,704. Continued research by Shibatani et al, Applied & Environmental Microbiology, Vol. 38, No. 3, pages 359-364 (1979) has shown that additional species have been found by other workers to possess L-aspartic-.beta. -decarboxylase and shows that production of this enzyme can be stimulated by the addition of certain amino acids, such as glutamate. An improved continuous method of production was published by Yamamoto et al, Biotechnology & Bioengineering, Vol. XXII, pages 2045-2054 (1980), when the whole organism was immobilized in carrageenan gel. Additionally, others have worked on the production of alanine from Pseudomonas dacunhae and Alcaligenes faecalis immobilized in Hypol.RTM. foam (Fusee et al, American Society for Microbiology Abstracts, Dallas, March 1980).
The present invention contemplates using the exemplified cell/polymer composition to produce L-alanine from aspartic acid in lieu of the previously used cell compositions.
A great deal of work has also previously been done with respect to the immobilization of the enzyme penicillin acylase. See, for example, Biochimie, 1980, 62: 317-321. Marconi et al have immobilized penicillin acylase in cellulose triacetate fibers (Biotechnology and Bioengineering 22: 735-756, 1980; Biotech. and Bioeng. 21: 1057-1073, 1979) and a number of U.S. patents have issued on the enzyme immobilization: U.S. Pat. Nos. 3,278,391, 3,116,218, 3,190,586, 3,446,705, 3,622,462, 3,736,230, 3,766,009, 3,801,962, 3,883,394, 3,900,488, 3,499,909, 3,736,230, 4,001,264, 4,113,566 and 4,230,804.
It appears that relatively few papers on whole cell immobilization are available. Tanabe Seiyaku has published a report of cells entrapped in polyacrylamide gel. Chibata et al (1974), German Pat. No. 2,414,128, and Mandel et al, published on entrapment in polyacrylamide gel (Mandel et al 1975, Prikl. Blkhim. Mikrobiol. 11: 219-225). Immobilized whole cells of Bacillus metaterium or Achromobacter adsorbed on DEAE cellulose have been used by Toyo Jozo, Fujii et al, Japanese Pat. No. 739393 and Sato et al, 1976, Fur. J. Applied Microbiology 2: 153-160 have reported on the production of 6-APA from pencillin-G by using immobilized E. coli having high penicillin acylase activity.
It will be appreciated that various other modifications may also be made without deviating from the invention, the scope of which is defined in the following claims wherein:

Number	Name	Date
3791926	Chibata et al.	Feb 1974
3860490	Guttag	Jan 1975
4138292	Chibata et al.	Feb 1979
4237229	Hartdegen	Dec 1980
4436813	Wood et al.	Mar 1984

Immobilization of cells with a polyazetidine prepolymer

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

RELATED APPLICATION

US Referenced Citations (5)

Non-Patent Literature Citations (2)

Continuation in Parts (1)

Entry
Fusee, et al., Applied and Environmental Microbiology, vol. 42, No. 4, 1981 (pp. 672-676).
Hustad, et al., J. Dz. Sci., vol. 56, No. 9, 1973 (pp. 1111-1117).