Claims
- 1. A thermoplastic composition comprising:
- A. 100 parts by weight of a base resin comprising a compatibilized polyphenylene ether resin and polyamide resin,
- B. 1 to 30 parts by weight per 100 parts of base resin A. of a selectively hydrogenated diblock copolymer of the A-B type wherein block A is an alkenyl aromatic polymer and block B is an ethylene-propylene polymer, and
- C. 5 to 45 weight percent of glass fibers based upon the weight of components A., B., and C. taken together.
- 2. A composition as in claim 1 wherein said compatible base resin A. is comprised of (a.) 5 to 95 weight percent polyphenylene ether resin and (b.) 95 to 5 weight percent polyamide resin, based upon the weight of a. and b. together.
- 3. A composition as in claim 2 wherein said polyamide resin constitutes a continuous phase in an amount greater than, approximately, 35 weight percent of the resinous components.
- 4. A composition as in claim 1 further comprising a compatibilizing agent selected from the group consisting of: maleic anhydride, fumaric acid, citric acid, malic acid, and reaction products of a polyphenylene ether and trimellitic anhydride acid chloride.
- 5. A composition as in claim 1 wherein said polyphenylene ether resin is a polymer or copolymer comprised primarily of one or more units derived from units selected from the group consisting of 2,6-dimethyl phenol units and 2,3,6-trimethyl phenol units, and wherein said resin has an intrinsic viscosity of 0.25 to 0.6 dl/g as measured in chloroform at 25.degree. C.
- 6. A composition as in claim 5 wherein said polyphenylene ether is poly(2,6-dimethyl-1,4-phenylene ether).
- 7. A composition as in claim 1 wherein said polyamide resin is selected from the group consisting of polyamide 6, and polyamide 6,6.
- 8. A composition as in claim 1 wherein said diblock copolymer is comprised of, approximately, 20 to 40 weight percent styrene and 80 to 60 weight percent ethylene-propylene polymer based upon the weight of both blocks taken together.
- 9. A composition as in claim 1 wherein said diblock copolymer is present in an amount of, approximately, 5 to 25 parts by weight based upon the total weight of polyphenylene ether and polyamide.
- 10. A composition as in claim 1 wherein the glass fibers are present in an amount of, approximately, 10 to 30 weight percent based upon the weight of components A., B., and C. taken together
- 11. A composition as in claim 1 wherein the selectively hydrogenated diblock copolymer is a selectively hydrogenated diblock copolymer of styrene and isoprene.
- 12. A thermoplastic composition comprising:
- (a) a base resin comprising a compatiblized polyphenylene ether resin and polyamide resin,
- (b) a selectively hydrogenated diblock copolymer of the A-B type wherein block A is an alkenyl aromatic polymer and block B is an ethylene-propylene polymer, and
- (c) glass fibers, wherein the total weight of components (a), (b) and (c) is 100 parts by weight.
- 13. A composition according to claim 12 wherein the polyphenylene ether resin is present in an amount of at least about 27 parts by weight.
- 14. A composition according to claim 12 wherein the polyamide resin is present in an amount of at least about 37 parts by weight.
- 15. A composition according to claim 12 wherein the selectively hydrogenated diblock copolymer is present in an amount of at least about 6 parts by weight.
- 16. A composition according to claim 12 wherein the glass fibers are present in an amount of at least about 10% by weight.
- 17. A composition according to claim 12 wherein the polyphenylene ether resin is present in an amount of 27 to about 42 parts by weight.
- 18. A composition according to claim 12 wherein the polyamide resin is present in an amount of from about 37 to about 42 parts by weight.
- 19. A composition according to claim 12 wherein the glass fibers are present in an amount of from about 10 to about 30 parts by weight.
- 20. A composition according to claim 12 wherein the polyphenylene ether resin is present in an amount of from about 27 to about 42 parts by weight, the polyamide is present in an amount of from about 37 to about 42 parts by weight, and the glass fibers are present in an amount of from about 10 to about 30 parts by weight.
CROSS-REFERENCE TO RELATED APPLICATION
This a continuation-in-part of copending application Serial No. 837,474; filed Mar. 7, 1986, now abandoned, and incorporated herein by reference.
US Referenced Citations (4)
Number |
Name |
Date |
Kind |
3379792 |
Finholt |
Apr 1968 |
|
4315086 |
Uens et al. |
Feb 1982 |
|
4339376 |
Kasahara et al. |
Jul 1982 |
|
4421892 |
Kasahara et al. |
Dec 1983 |
|
Foreign Referenced Citations (2)
Number |
Date |
Country |
117250 |
Jul 1983 |
JPX |
8505375 |
Dec 1985 |
WOX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
837474 |
Mar 1986 |
|