Patent Grant
10815404
Adhesives have been used for a variety of marking, holding, protecting, sealing and masking purposes. Adhesive tapes generally comprise a backing, or substrate, and an adhesive. One type of adhesive, a pressure-sensitive adhesive, is particularly useful for many applications.
Pressure-sensitive adhesives are well known to one of ordinary skill in the art to possess certain properties at room temperature including the following: (1) aggressive and permanent tack, (2) adherence with no more than finger pressure, (3) sufficient ability to hold onto an adherend, and (4) sufficient cohesive strength to be removed cleanly from the adherend. Materials that have been found to function well as pressure-sensitive adhesives are polymers designed and formulated to exhibit the requisite viscoelastic properties resulting in a desired balance of tack, peel adhesion, and shear strength. The most commonly used polymers for preparation of pressure-sensitive adhesives are natural rubber, synthetic rubbers (e.g., styrene/butadiene copolymers (SBR) and styrene/isoprene/styrene (SIS) block copolymers), various (meth)acrylate (e.g., acrylate and methacrylate) copolymers and silicones. Each of these classes of materials has advantages and disadvantages.
In some aspects of the present description, a polyester including at least two different diacid residues, and at least two different diol residues is provided. The polyester includes at least one pendant group containing an alkenyl group. A ratio of a total number of the at least one pendant group to the total number of ester groups in the polyester is in a range of 0.001 to 0.1. The polyester has a glass transition temperature in a range of −50° C. to −10° C. The polyester is a pressure-sensitive adhesive.
In some aspects of the present description, a crosslinked polyester including at least two different diacid residues and at least two different diol residues is provided. The crosslinked polyester has a glass transition temperature in a range of −50° C. to −10° C. and has a crosslinking density, as determined by gel-percent test, of less than 35 percent. The crosslinked polyester is a pressure-sensitive adhesive.
In some aspects of the present description, a pressure-sensitive adhesive composition comprising the polyester is provided, and in some embodiments, a tape comprising the polyester or the pressure-sensitive adhesive composition is provided.
In the following description, reference is made to the accompanying drawings that forms a part hereof and in which various embodiments are shown by way of illustration. The drawings are not necessarily to scale. It is to be understood that other embodiments are contemplated and may be made without departing from the scope or spirit of the present disclosure. The following detailed description, therefore, is not to be taken in a limiting sense.
The use of adhesives, especially pressure-sensitive adhesives, in areas such as the medical, electronic and optical industries is increasing. The requirements of these industries place additional demands upon the pressure-sensitive adhesive beyond the traditional properties of tack, peel adhesion and shear strength. New classes of materials are desirable to meet the increasingly demanding performance requirements for pressure-sensitive adhesives.
Polyesters may be formed as the reaction product of diacids and diols. For example, terephthalic acid (a diacid) and ethylene glycol (a diol) can be reacted to form polyethylene terephthalate (PET). More generally, one or more diacids and one or more diols can be reacted, in equal molar portions of total diacids and total diols, to form a polyester comprising residues of the diacids and residues of the diols. The term residue when used in reference to the components of a polyester, refers to the moiety in the polyester resulting from the reaction of a corresponding monomer. In some cases, different monomers can produce the same moiety in the polyester and the moiety may be referred to as a residue of any of the monomers that result in the moiety in the polyester. For example, PET can be formed by the esterification reaction between terephthalic acid and ethylene glycol with water as a byproduct or by the transesterification reaction between dimethyl terephthalate and ethylene glycol with methanol as a byproduct. Since the residue of the terephthalic acid and the residue of the dimethyl terephthalate is the same moiety, the moiety may be referred to either as a residue of terephthalic acid or as a residue of dimethyl terephthalate regardless of how the polyester is formed.
Polyesters can be chain-extended or cross-linked in a solution phase reaction by utilizing a di-functional or a multifunctional isocyanate as a chain extending or crosslinking agent. In some cases, the resulting chain-extended or cross-linked polyester compositions can be used as adhesives but such adhesives typically exhibit poor shear strength.
The term “adhesive” refers to polymers or polymeric compositions useful to adhere together two adherends. An example of an adhesive is a pressure-sensitive adhesive. Pressure-sensitive adhesive compositions are well known to those of ordinary skill in the art to possess properties including the following: (1) aggressive and permanent tack, (2) adherence with no more than finger pressure, (3) sufficient ability to hold onto an adherend, and (4) sufficient cohesive strength to be cleanly removable from the adherend. Materials that have been found to function well as pressure-sensitive adhesives are polymers designed and formulated to exhibit the requisite viscoelastic properties resulting in a desired balance of tack, peel adhesion, and shear holding power. Obtaining the proper balance of properties is not a simple process.
According to the present description, polyesters, and compositions that include the polyesters, which offer improved performance as adhesives are described. In some embodiments, the polyester is a pressure-sensitive adhesive. In some embodiments, a pressure-sensitive adhesive composition including the polyester and tackifier at 1 to 60 weight percent, or 1 to 30 weight percent, or 1 to 15 weight percent is provided. In some embodiments, the polyester has sufficient adhesive properties without the need for including a tackifier. Polyesters, or compositions comprising the polyesters, having good pressure-sensitive adhesion properties typically have a low glass transition temperature (e.g., less than −10° C.) and a low shear or storage modulus (e.g., less than 0.3 MPa). Such properties of the polyesters of the present description are described further elsewhere herein.
In some embodiments, the polyesters include at least two different diacid residues and at least two different diol residues. In some embodiments, the at least two at least two different diacid residues include, based on the total moles of the at least two diacid residues, 20 to 80 mole percent of a residue of at least one aromatic dicarboxylic acid, and 20 to 80 mole percent of at least one of a residue of adipic acid or sebacic acid. In some embodiments, the residue of the at least one aromatic dicarboxylic acid comprises a residue of at least one of isophthalic acid, phthalic acid, terephthalic acid, bibenzoic acid, and naphthalic acid. In some embodiments, the at least two different diol residues include, based on the total moles of the at least two diol residues, at least 5 mole percent of a first diol residue and at least 5 mole percent of a different second diol residue. In some embodiments, the at least two different diol residues comprise at least three different diol residues which include at least 5 mole percent of a first diol residue, at least 5 mole percent of a different second diol residue, and 0.1 to 10 mole percent of a residue of trimethylolpropane monoallyl ether. In some embodiments, each of the first and second diol residues is a residue of ethylene glycol, 1,6-hexanediol, 1,4-butanediol, neopentyl glycol, or 1,4-cyclohexanedimethanol.
In some embodiments, the polyesters include one or more diacid residues or one or more diol residues which are crosslinkable by virtue of having crosslinkable pendant groups. The crosslinkable pendant groups may include one or more reactive unsaturated carbon-carbon bonds, e.g., alkene or alkyne, which could undergo efficient radical-based addition or propagation reactions. In some embodiments, the crosslinkable pendant group includes terminal alkene, substituted alkene, alkenyl, allyl, allyloxy, alkyne, cyclic alkene, (meth)acrylate or other reactive groups. The term (meth)acrylate group refers to acrylate groups, methacrylate groups, or a combination of acrylate and methacrylate groups. In some embodiments, the crosslinkable pendant groups include a carbon-carbon double bond (C═C). The polyesters may be crosslinkable by the application of actinic radiation (e.g., ultraviolet radiation or electron beam radiation) and/or may be crosslinkable by the application of heat (thermal-induced crosslinking). The polyesters of the present description offer advantages over other polyester containing adhesives. For example, the polyesters can be crosslinked with high efficiency and without low molecular weight monomer additives, the polyesters have improved chemical resistance, and/or the polyesters have improved impact resistance.
In some embodiments, a ratio of a total number of the at least one crosslinkable pendant groups in the polyester to a total number of ester groups in the polyester is in a range of 0.0001 to 0.5, or in a range of 0.001 to 0.2, or in a range of 0.001 to 0.1. In some embodiments, a ratio of a total number of the at least one crosslinkable moiety to a total number of ester groups in the polyester is in a range of 0.0001 to 0.5, or in a range of 0.001 to 0.2, or in a range of 0.001 to 0.1.
In some embodiments, the polyester is made by reacting precursors that include at least one diacid, at least one diol not containing a crosslinkable pendant group, and at least one monomer containing a crosslinkable pendant group. In some embodiments, the at least one diacid includes at least two diacids and in some embodiments, the at least one diol not containing a crosslinkable pendant group includes at least two diols. A pendant group may refer to a side group attached to a backbone chain of a polymer. A monomer may be said to contain a pendant group if it contains a group which becomes a side group upon polymerization. A ratio of the number of molecules of the at least one monomer to a sum of the number of molecules of the at least one diacid and the number of molecules at least one diol may be in a range of 0.0001 to 0.5, or in a range of 0.001 to 0.2, or in a range of 0.001 to 0.1. In some embodiments, a ratio of the number of molecules of the at least one diacid to the number of molecules of the at least one diol is in a range of 0.85 to 1.15, or 0.9 to 1.1. In some embodiments, the at least one monomer containing a crosslinkable pendant group may be an alkene- or alkyne-containing diacid or diol or diester. It will be understood that the polyesters of the present description can be alternatively made by substituting diesters for diacids in the reactive precursors.
Each moiety containing a crosslinkable pendant group may include a carbon-carbon double bond and in some embodiments may be represented by the general Formula 1 below:
wherein:
R1 is —O—, —(CH2)n-, —C(═O)O—, —OCH2O—, —OC(═O)—, —S—, —(C═O)—, or a combination thereof;
R2 is —OH, —CO2H or —R2′—, wherein —R2′— is —O—, —C(═O)O—, —(CH2)n—, —(C═O)—, —S—, or a combination thereof,
R3 is —H, —CH3, —OH, —CH2OH, —(CH2)mCH3, —SO3Na, —CO2Na, or a combination thereof, and
R4 is —O—, —C(═O)O—, —(CH2)p-, —(C═O)—, —S— or a combination thereof.
Here, n, m and p are integers greater than 0. For example, n, m and p may each be independently in the range of 1 to 100, or independently in a range of 1 to 20, or independently in a range of 1 to 18. In some embodiments, an end group of the polyester may comprise the moiety (e.g., R2 may be —CO2H, or —OH). In some embodiments, the moiety is a diol residue that may be represented by the Formula 2 below:
In some embodiments, the polyester may be made by reacting precursors that include at least one diacid, at least one diol not containing a crosslinkable pendant group, and a monomer which forms the moiety having the crosslinkable pendant group. In some embodiments, the monomer may be selected to give a moiety represented by the general Formula 1 above. In some embodiments, the monomer is trimethylolpropane monoallyl ether (TMPME) which can form the moiety represented by Formula 2. In other exemplary embodiments, monomers represented by any of Formulas 3 to 5 may be chosen.
The monomers represented by Formulas 3 to 5 are diols. In other embodiments, monomers represented by any of the Formulas 3 to 5 with the —OH groups replaced by —CO2H groups (or alternatively by ester groups) may be used. In some embodiments, the pendant groups of the moiety generating monomer have at least 3 functionalities, among which 2 of them are either —OH or —CO2H terminated while the third one is neither —OH nor —CO2H. The third pendant functional group may be terminated by a C═C bond. Other suitable possibilities are provided in Formula 1. Further possibilities for the crosslinkable pendant groups are provided in Formulas 6 to 9 where R represents a constituent of the backbone of the polyester; R5 is independently —CH2— or —O—; R6 is independently —CH3 or —H; and R7 is —(CH2)m—, where m in an integer from 1 to 4.
In some embodiments, the polyesters are formed by reacting precursors (e.g., in an esterification reaction) that include at least one acid (e.g., a diacid such as a dicarboxylic acid or a polyacid such as a polycarboxylic acid), at least one alcohol (e.g., a diol or a polyol), and at least one monomer containing at least one crosslinkable pendant group. Examples of suitable acids include terephthalic acid (e.g., 1,4-terephthalic acid), 1,4-naphthalenedicarboxylic acid, isophthalic acid, phthalic acid, 2,6-naphthalenedicarboxylic acid, diphenyldicarboxylic acid, succinic acid, adipic acid, azelaic acid, sebacic acid, dodecanedioic acid, 1,4-cyclohexanedicarboxylic acid, bibenzoic acid, naphthalic acid, and combinations thereof. Examples of suitable alcohols include ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, polypropylene glycol, 1,3-butanediol, 1,4-butanediol, 1,6-hexanediol, neopentyl glycol, 1,4-cyclohexanedimethanol, and combinations thereof. Suitable monomers containing at least one crosslinkable pendant group include those selected to give a moiety represented by the general Formula 1 above. In some embodiments, the at least one monomer containing at least one crosslinkable pendant group may be one or more diol monomers, one or more diacid monomers, or a combination of diol and diacid monomers.
A polyester which does not dissolve and which does not detached from a substrate to which it is adhered when exposed to a chemical for a specified time at a specified temperature may be described as chemical resistant. For example, a polyester may maintain adhesion and not dissolve when submerged in either oleic acid or a mixture of isopropyl alcohol (IPA) and water at a weight ratio of 70:30 (IPA/H2O) at 70° C. for 8 hrs.
Utilizing at least one aromatic dicarboxylic acid has been found to provide enhanced chemical resistance over utilizing only non-aromatic diacids. In some embodiments, the polyester includes, based on the total moles of diacid residues, 20 to 80 mole percent, or 30 to 70 mole percent, or 40 to 60 mole percent, or about 50 mole percent, of a residue of at least one aromatic dicarboxylic acid. In some embodiments, the polyester also includes residues of at least two different diols, or at least three different diols. Is some embodiments, the at least two different diols, or the at least three different diols, include at least one diol containing a crosslinkable pendant group as described further elsewhere herein. In some embodiments, the polyester further includes residues of polyols or polyacids.
In some embodiments, the polyesters are formed by reacting precursors that include at least one diacid, at least one diol, and, optionally, at least one monomer containing a crosslinkable pendant group. Monomers in the at least one monomer containing a crosslinkable pendant group may be diols or diacids, for example, or may be other suitable monomers. The reaction between the diols, the diacids and the monomers containing the pendant group may be catalyzed by tetrabutyl titanate, cobalt acetate, zinc acetate, antimony triacetate, and/or other metal acetates. Stabilizers such as triethyl phosphonoacetate may be included to stabilize the catalyst after the reaction. Branching agents such as trimethylol propane may also be used in the reaction.
The polyester or polyester composition may be an adhesive, and may be a pressure-sensitive adhesive, without crosslinking the polyester. However, in some embodiments, the properties of the adhesive (e.g., modulus, bond strength, etc.) can be improved by crosslinking (curing) the polyester, which can be done by applying actinic radiation, for example. The adhesive may have adequate adhesion properties without the addition of a plasticizer, but a plasticizer may optionally be included. For example, in some embodiments, an adhesive composition comprises the polyester at 99 to 40 weight percent and comprises tackifier at 1 to 60 weight percent. In some embodiments, the adhesive composition includes other additives or ingredients in addition to the polyester and the tackifier. In some embodiments, the tackifier is included at 10 to 60 weight percent, or at 20 to 50 weight percent. In some embodiments, the tackifier is included at 1 to 30 weight percent, or at 1 to 15 weight percent. The tackifier may be any suitable compound or compounds for increasing the tack or stickiness of the adhesive. Suitable tackifiers include C5 hydrocarbons, C9 hydrocarbons, aliphatic resins, aromatic resins, terpenes, terpenoids, terpene phenolic resins, rosins, rosin esters, and combinations thereof. Suitable tackifiers include ARKON P140 which has a softening point of 140° C. and which is available from Arakawa Europe GnbH, Germany, CLEARON P150 which has a softening point of 150° C. and which is available from Yasuhara Chemical Co., Japan, and ENDEX 160 which has a softening point of 160° C. and which is available from Eastman Chemical Company, Kingsport, Tenn. In some embodiments, the tackifier is a terpene phenol resin such as SP-560 which has a softening point of 155° C. and which is available from SI Group Inc., Schenectady, N.Y. In some embodiments, the tackifier has a softening point no less than 140° C. In some embodiments, the tackifier has a softening point of at least 140° C. and less than 190° C., or less than 180° C.
In some embodiments, the polyesters have a glass transition temperature (Tg) determined by differential scanning calorimetry (DSC) less than 0° C., or less than −10° C., or less than −20° C. or less than −30° C. In some embodiments, the glass transition temperature is in a range of −60° C. to −10° C., or in a range of −50° C. to −10° C.
In some embodiments, the polyesters prior to curing (crosslinking) have a shear modulus at 1 Hz and 23° C. that is less than 1 MPa, or less than 0.5 MPa, or less than 0.3, or less than 0.2 MPa. In some embodiments, the shear modulus is in a range of 0.001 MPa to 1 MPa. The shear modulus refers to the real part of the complex shear modulus, which may be denoted G′ (G prime) based on Dynamic Mechanical Analysis (DMA), unless specified differently. A tan δ value may also be determined by DMA. Unless specified differently, tan δ values specified herein refer to the tan δ value determined by DMA.
In some embodiments, the polyesters have a weight-average molecular weight (Mw) in a range of 40 to 4000 kg/mole, or in a range of 100 to 1000 kg/mole, or in a range of 200 kg/mole to 500 kg/mole. In some embodiments, the weight-average molecular weight is at least 60 kg/mole, or at least 100 kg/mole, or at least 200 kg/mole. The weight-average molecular weight (Mw) refers the Mw value determined using gel permeation chromatography (GPC) unless specified differently. The number-average molecular weight (Mn) can also be determined using gel permeation chromatography (GPC). In some embodiments, the polyesters have a polydispersity index (Mw/Mn) is in a range of 3 to 60, or in a range of 3 to 30, or in a range of 3 to 20.
In some embodiments, the polyesters of the present description have an intrinsic viscosity in the range of 0.8 to 2 dL/g or in a range of 1.0 to 1.6 dL/g. Intrinsic viscosity of a polymer refers to the difference in viscosity of a solution of the polymer in solvent and the solvent without the polymer divided by the product of the concentration of the polymer and the viscosity of the solvent without the polymer in the limit of small concentration. Unless specified differently, the solvent used to determine the intrinsic viscosity of the polyester is a 60/40 weight percent mixture of phenol/o-dichlorobenzene and the intrinsic viscosity is determined at 23° C. using an Ubbelohde capillary viscometer.
The crystallinity of the polyesters can be determined from the heat of melting (ΔHm) determined using differential scanning calorimetry (DSC). In some embodiments, the polyesters have a crystallinity corresponding to a melting endotherm of less than 20 J/g, or less than 10 J/g, or less than 5 J/g, or less than 1 J/g, or substantially zero. The crystallinity may be said to be substantially zero if a statistically meaningful non-zero value of the melting endotherm cannot be measured using standard DSC techniques. In some embodiments, the polyester will not crystalize and so the polyester does not have a melting point.
In some embodiments, the polyesters after curing (e.g., crosslinking via applying actinic radiation) have a shear modulus at 1 Hz and 23° C. that is less than 300,000 Pa, or less than 200,000 Pa. In some embodiments, the polyesters after curing have a shear modulus at 1 Hz and 23° C. in a range of 0.001 MPa to 1 MPa. In some embodiments, the polyesters after curing have a shear modulus at 1 Hz and 70° C. that is at least 20,000 Pa. In some embodiments, the polyesters after curing have a shear modulus at 1 Hz and 100° C. that is at least 10,000 Pa In some embodiments, the polyesters after curing have a shear modulus at 1 Hz and 130° C. that is at least 10,000 Pa.
In some embodiments, the polyesters have a tan δ as determined by DMA that is less than 0.7 at 23° C. after curing. In some embodiments, the polyesters have a tan δ less than 0.8 at 70° C. after curing, based on DMA. In some embodiments, the polyesters have a tan δ less than 0.8 at 100° C. after curing, based on DMA. In some embodiments, the polyesters have a tan δ less than 0.8 at 130° C. after curing, based on DMA.
In some embodiments, the polyester is a pressure-sensitive adhesive having good impact or drop resistance. Impact resistance or drop resistance refers to the ability of the polyester to maintain adhesion between two adherents when subjected to repeated impacts. For example, a polyester pressure-sensitive adhesive can be used to laminate an aluminum plate and a polycarbonate plate together and the laminate repeatedly dropped up to 30 times each from 1 meter, then 1.2 meters, and then 2.0 meters, for example. The drop resistance can be characterized by the number of drops without the plates delaminating.
Crosslinking density can be characterized by using gel content as an indication of the degree of crosslinking. It has been found that drop resistance is improved when the polyester has a glass transition temperature in a range of −50° C. to −10° C. and/or has a crosslinking density of less than 35 percent as determined by gel-percent test. For example, in the drop test described above, the laminate can, in some embodiments, survive at least 40, at least 60, at least 85, or at least 90 such drops. Gel-percent testing can be used to determined crosslinking density as specified in the ASTM D 3616-95 test standard. In brief summary, the gel percent is determined by subjecting a sample to extraction in tetrahydrofuran, determining the weight lost during extraction, and calculating the extract percent and the gel percent from:
Except where specified differently, the crosslinking density of the polyesters of the present description refers to the gel percent determined according to the ASTM D 3616-95 test standard.
In some embodiments, it may be desired that a polyester pressure-sensitive adhesive be both drop resistant and chemical resistant. In such embodiments, the polyester may have a glass transition temperature in a range of −50° C. to −10° C., a crosslinking density of less than 35 percent as determined by gel-percent test, and may include, based on the total moles of the at least two diacid residues, 20 to 80 mole percent of a residue of at least one aromatic dicarboxylic acid. In some applications, chemical resistance may be more important than drop resistance. In such applications, the crosslinking density may be higher than 35 percent. For example, in some embodiments, the polyester has a crosslinking density of 20 to 60 percent as determined by gel-percent test.
In some embodiments, a tape that includes the polyester, or an adhesive composition including the polyester, disposed on a substrate is provided.
Either of the tapes 100 or 200 can be made by coextrusion of the layers of the tapes. Either of the tapes 100 or 200 may be provided with a release layer adjacent the adhesive layer(s).
The peel strength of the tapes of the present description can be tested using standard peel test specifications such as that of D3330/D3330M-04(2010). In some embodiments, the peel strength of tape 100 or tape 200 is at least 300 g/cm, or at least 1000 g/cm, or at least 2000 g/cm, or in a range of 300 g/cm to 10000 g/cm when tested at a 180 degree peel from a stainless steel substrate at a peel rate of 300 mm/minute.
Chemical-resistance polyester pressure-sensitive adhesives related to the polyesters of the present description are described in U.S. Provisional Application 62/355,989 entitled “CHEMICAL-RESISTANT POLYESTER PRESSURE-SENSITIVE ADHESIVE”, filed on an even date herewith, and hereby incorporated herein by reference to the extent that it does not contradict the present description. Related polyesters are described in U.S. Prov. Pat. App. No. 62/206,618 (Liu et al.), filed on Aug. 18, 2015, which is hereby incorporated herein by reference to the extent that it does not contradict the present description.
Test Methods
Differential Scanning Calorimetry (DSC)
The glass transition temperature (Tg) and crystal melting enthalpy (ΔHm) were measured using a Differential Scanning Calorimeter (DSC) Model Q-1000 (commercially available from TA Instruments, New Castle, Del.). The heating rate was 20° C./min.
Dynamic Mechanical Analysis (DMA)
The storage modulus refers to the real part of the complex shear modulus, denoted G′ (G prime), and was measured using Dynamic Mechanical Analysis (DMA) tester Model G2 ARES (commercially available from TA Instruments, New Castle, Del.). Tests were performed at 1 Hz and 23° C.
Peel Adhesion Strength
Specimens were prepared by slitting test strips 12.7 mm×127 mm in dimension from each of the adhesive tapes prepared. Two replicate specimens were prepared for each Example. The exposed adhesive surface of a test strip was adhered along the length of a Type 304 stainless steel (SS) plate with a bright annealed finish (ChemInstruments, Incorporated, Fairfield, Ohio), measuring 5.1 cm wide by 12.7 cm long by 0.12 cm thick. The test strip was rolled down 5 times using a 2.0 kg rubber roller. The plate was cleaned prior to applying the tape by wiping with acetone once and then with heptane three times using a tissue paper (trade designation KIMWIPE, available from Kimberly-Clark Corporation, Irving, Tex.). After being conditioned for 72 hours at 50% relative humidity (RH) at room temperature (RT), the peel adhesion strength was evaluated using an MTS INSIGHT tensile tester (MTS Systems Corporation, Eden Prairie, Minn.) equipped with a 1000 N load cell, using a crosshead speed of 300 mm/min, at an angle of 180° with the test specimen held in the bottom clamp and the tail in the top clamp. The average peel adhesion strength of two test specimens was reported in g/cm.
Drop Test
A DROP TESTER (Shinyei Technology Co., Ltd., Kobe, Japan) was used. One substrate was an aluminum plate (1.6×102×152 mm) and one substrate was a polycarbonate panel (3.2×74×96 mm). These were bonded to each other using a rectangle frame made of strips of 2 mm width of the adhesive composition to be tested. The adhesive frame dimension was 50×70 mm. Procedure: 1) The aluminum plate was cleaned with 3 wipes of isopropyl alcohol (IPA) 2) The polycarbonate panel was cleaned with 3 wipes of IPA. 3) The aluminum/adhesive/polycarbonate assembly was pressed together at 70 lbs (gauge pressure) for 10 sec, and then allowed to dwell at room temperature for 24 hour before testing. The prepared panel was then dropped at 3 different heights until the assembly fell apart (failure). Results were reported as the number of drops from the 3 different heights: 1.0 meter (30 drops max), then 1.2 meters (30 drops max), and then 2.0 meters (30 drops max). The sum of total drops from all three heights were used for characterizing the impact resistance of the adhesive. More than total 40 drops is considered good impact resistance. Less than 20 total drops is considered poor in impact resistance. It is considered fair impact resistance when the total number of drops is between 20 and 40 drops.
Intrinsic Viscosity (IV) Test
Intrinsic viscosity (IV) of polyesters was measured in 60/40 wt. % phenol/o-dichlorobenzene at 23° C.
Molecular Weight Test
Weight average molecular weight (Mw) was determined using a standard GPC unit with Polystyrene as standards and tetrahydrofuran (THF) as solvent.
Gel Fraction Test (Tested According to ASTM D 3616-95):
A test specimen containing approximately 0.08 g of adhesive tape was cut from the tape and placed within a 120-mesh stainless steel basket measuring approximately 5 cm×10 cm. The contents were weighed to within 0.1 mg and immersed in a metal pan containing sufficient amount of tetrahydrofuran to cover the specimen. After extraction for 24 to 48 hours, the pouch (containing the remaining specimen) was removed and placed under vacuum to remove residual solvent. The pouch was weighed and the gel content was determined by:
At least two specimens were measured for gel content and the reported values represent the average of the at least two specimens.
Raw Materials
The materials used in the polyester syntheses are shown in Table 1. All are available from Sigma Aldrich Corp., St. Louis, Mo.
This polyester composition was synthesized in a 8000 cc reactor with the following raw material charge: ethylene glycol (6 parts by mole of total diols), 1,6-hexanediol (90 parts by mole of total diols), trimethylolpropane (3 parts by mole of total diols), trimethylolpropane monoallyl ether (1 parts by mole of total diols), sebacic acid (30 parts by mole of total acids), isophthalic acid (70 parts by mole of total acids), tetrabutyl titanate (450 ppm by total theoretical polymer weight based on the monomers charged), and triethylphosphonoacetate (450 ppm by total theoretical polymer weight based on the monomers charged). The mixture was heated to a temperature of 248° C. at a pressure of two atmospheres (270 kPa) and the mixture allowed to react while removing the water by-product. After completing the reaction and removing water, the pressure was reduced to the 0.5 to 5 mmHg range while heating to 271° C. The condensation by-product was continuously removed until a polymer of viscous nature was produced. The Mw of the resulting polyester determined by GPC was 309 kg/mol. The IV of the resulting polymer was 1.4. The Tg determined by DSC was −21° C.
This polyester composition was synthesized in a 8000 cc reactor with the following raw material charge: ethylene glycol (7 parts by mole of total diols), 1,6-hexane diol (60 parts by mole of total diols), 1,4-cyclohexane dimethanol (30 parts by mole of total diols), trimethylolpropane (1 parts by mole of total diols), trimethylolpropane monoallyl ether (2 parts by mole of total diols), sebacic acid (50 parts by mole of total acids), isophthalic acid (50 parts by mole of total acids), tetrabutyl titanate (450 ppm by total theoretical polymer weight based on the monomers charged), and triethylphosphonoacetate (450 ppm by total theoretical polymer weight based on the monomers charged). The mixture was heated to a temperature of 248° C. at a pressure of two atmospheres (270 kPa) and the mixture allowed to react while removing the water by-product. After completing the reaction and removing water, the pressure was reduced to the 0.5 to 5 mmHg range while heating to 271° C. The condensation by-product was continuously removed until a polymer of viscous nature was produced.
The Mw of the resulting polyester determined by GPC was 167 kg/mol. The IV of the resulting polymer was 1.2. The Tg determined by DSC was −26° C. The storage modulus (G′) determined by DMA was 0.26 MPa at 23° C.
This polyester composition was synthesized in a 8000 cc reactor with the following raw material charge: ethylene glycol (22 parts by mole of total diols), 1,6-hexane diol (25 parts by mole of total diols), neopentyl glycol (25 parts by mole of total diols), 1,4-cyclohexane dimethanol (25 parts by mole of total diols), trimethylolpropane (1 parts by mole of total diols), trimethylolpropane monoallyl ether (2 parts by mole of total diols), sebacic acid (70 parts by mole of total acids), isophthalic acid (30 parts by mole of total acids), tetrabutyl titanate (450 ppm by total theoretical polymer weight based on the monomers charged), and triethylphosphonoacetate (450 ppm by total theoretical polymer weight based on the monomers charged). The mixture was heated to a temperature of 248° C. at a pressure of two atmospheres (270 kPa) and the mixture allowed to react while removing the water by-product. After completing the reaction and removing water, the pressure was reduced to the 0.5 to 5 mmHg range while heating to 271° C. The condensation by-product was continuously removed until a polymer of viscous nature was produced.
The Mw of the resulting polyester determined by GPC was 224 kg/mol. The IV of the resulting polymer was 1.2. The Tg determined by DSC was −39° C.
This polyester composition was synthesized in a 8000 cc reactor with the following raw material charge: ethylene glycol (1 parts by mole of total diols), 1,6-hexane diol (28 parts by mole of total diols), neopentyl glycol (34 parts by mole of total diols), 1,4-cyclohexane dimethanol (34 parts by mole of total diols), trimethylolpropane (1 parts by mole of total diols), trimethylolpropane monoallyl ether (2 parts by mole of total diols), sebacic acid (50 parts by mole of total acids), isophthalic acid (50 parts by mole of total acids), tetrabutyl titanate (450 ppm by total theoretical polymer weight based on the monomers charged), and triethylphosphonoacetate (450 ppm by total theoretical polymer weight based on the monomers charged). The mixture was heated to a temperature of 248° C. at a pressure of two atmospheres (270 kPa) and the mixture allowed to react while removing the water by-product. After completing the reaction and removing water, the pressure was reduced to the 0.5 to 5 mmHg range while heating to 271° C. The condensation by-product was continuously removed until a polymer of viscous nature was produced.
The Mw of the resulting polyester determined by GPC was 216 kg/mol. The IV of the resulting polymer was 1.2. The Tg determined by DSC was −16° C. The storage modulus (G′) determined by DMA was 0.47 MPa at 23° C.
The compositions of the polyesters of Examples 1-4 are summarized in Table 2, and the adhesive properties of the polyesters of Examples 1-4 are summarized in Table 3.
Polyester of Example 1 was extruded in a twin screw extruder along with a tackifier, VINSOL ESTER GUM (“VEG”) (Pinova, Inc., Brunswick, Ga.), at the composition ratio of 70 wt/30 wt % (Polyester/VEG). The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape at 200 micrometer thickness. The resulting pressure sensitive tape had a glass transition temperature of 8° C. The tape was then tested for drop performance and obtained a total number of 1 drop before failure. The drop performance is considered poor for impact resistance.
Polyester of Example 2 was extruded in a twin screw extruder along with a tackifier, VINSOL ESTER GUM (“VEG”), at the composition ratio of 80 wt/20 wt % (Polyester/VEG). The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape at 200 micrometer thickness. The resulting pressure sensitive tape had a glass transition temperature of −8° C. The tape was then tested for drop performance and obtained a total number of 12 drops before failure. The drop performance is considered poor for impact resistance.
Polyester of Example 2 was extruded in a twin screw extruder along with a tackifier, FORAL 3085 (Pinova, Inc., Brunswick, Ga.), at the composition ratio of 80 wt/20 wt % (Polyester/Foral 3085). The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape at 200 micrometer thickness. The resulting pressure sensitive tape had a glass transition temperature of −14° C. The tape was then tested for drop performance and obtained a total number of 90 drops before failure. The drop performance is considered good for impact resistance.
Polyester of Example 3 was extruded in a twin screw extruder along with a tackifier, VINSOL ESTER GUM (“VEG”), at the composition ratio of 80 wt/20 wt % (Polyester/VEG). The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape at 200 micrometer thickness. The resulting pressure sensitive tape had a glass transition temperature of −16° C. The tape was then tested for drop performance and obtained a total number of 90 drops before failure. The drop performance is considered good for impact resistance.
Polyester of Example 2 was extruded in a twin screw extruder. The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape at 200 micrometer thickness. The resulting pressure sensitive tape had a glass transition temperature of −26° C. The tape was then tested for drop performance and obtained a total number of 90 drops before failure. The drop performance is considered good for impact resistance.
Polyester of Example 3 was extruded in a twin screw extruder. The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape at 200 micrometer thickness. The resulting pressure sensitive tape had a glass transition temperature of −39° C. The tape was then tested for drop performance and obtained a total number of 90 drops before failure. The drop performance is considered good for impact resistance.
Drop Test performance of Comparative Examples 1 and 2 and Examples 5-8 are compared in Table 4.
Polyester of Example 4 was extruded in a twin screw extruder. The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape at 100 micrometer thickness. The resulting pressure sensitive tape had a glass transition temperature of −16° C. The resulting tape was tested for gel % and was determined to have 0% gel residual. The tape was then tested for drop performance and obtained a total number of 70 drops before failure. The drop performance is considered good for impact resistance.
Polyester of Example 4 was extruded in a twin screw extruder along with a photoinitiator, IRGACURE 651 (BASF North America, Charlotte, N.C.), at composition of 99.5 wt %/0.5 wt % (Polyester/Irgacure 651). The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape at 100 micrometer thickness. The resulting pressure sensitive tape was cured using a FUSION UV D Bulb lamp (Heraeus Noblelight Fusion UV, Inc., Gaithersburg, Md.) at 2000 mJ/cm2. The resulting tape was tested for gel % and was determined to have 8% gel residual. The tape was then tested for drop performance and obtained a total number of 66 drops before failure. The drop performance is considered good for impact resistance.
Polyester of Example 4 was extruded in a twin screw extruder along with a photoinitiator, IRGACURE 651, at composition of 99.2 wt %/0.8 wt % (Polyester/Irgacure 651). The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape at 100 micrometer thickness. The resulting pressure sensitive tape was cured using a FUSION UV D Bulb lamp at 2000 mJ/cm2. The resulting tape was tested for gel % and was determined to have 15% gel residual. The tape was then tested for drop performance and obtained a total number of 70 drops before failure. The drop performance is considered good for impact resistance.
Polyester adhesive tape of Example 9 was subjected to electron beam radiation at 200 KV and a total dosage of 3 Mrads. The resulting tape was tested for gel % and was determined to have 23% gel residual. The tape was then tested for drop performance and obtained a total number of 52 drops before failure. The drop performance is considered good for impact resistance.
Polyester adhesive tape of Example 9 was subjected to electron beam radiation at 200 KV and at a total dosage of 6 Mrads. The resulting tape was tested for gel % and was determined to have 30% gel residual. The tape was then tested for drop performance and obtained a total number of 44 drops before failure. The drop performance is considered good for impact resistance.
Polyester adhesive tape of Example 9 was subjected to electron beam radiation at 200 KV and at a total dosage of 9 Mrads. The resulting tape was tested for gel % and was determined to have 39% gel residual. The tape was then tested for drop performance and obtained a total number of 3 drops before failure. The drop performance is considered poor for impact resistance.
Polyester adhesive tape of Example 9 was subjected to electron beam radiation at 200 KV and at a total dosage of 12 Mrads. The resulting tape was tested for gel % and was determined to have 45% gel residual. The tape was then tested for drop performance and obtained a total number of 2 drops before failure. The drop performance is considered poor for impact resistance.
Drop Test performance of Examples 9-13 and Comparative Examples CE 3 and CE 4 are compared in Table 5.
An article was made via processing on a coextrusion line. Two hot melt twin-screw extruders were set up side by side. The combination of a 3 layer ABA feedblock and a cast film die were used. The skin extruder, Extruder A, was fed with the polyester of Example 2. The melt temperature on the skin extruder was controlled at 350° F. The screw was run at 100 rpm. A gear pump was used to control the feed rate into the feedblock. The feedblock split the skin PSA melt stream into two and fed them to the outer surface “A” layers. The other extruder, Extruder B, was fed with the following foam composition: KRATON D1161 (Kraton Performance Polymers, Houston Tex.)/CUMAR 130 (Neville Chemical Co., Pittsburgh, Pa.)/ARKON P125 (Arakawa Chemical USA Inc., Chicago, Ill.)/ECOCELL-P (Polyfil corp., Rockaway, N.J.) (53/20/25/2, wt %). The melt temperature on the core extruder was controlled at 350° F. The rheological characteristics of the adhesive layers and core layer were closely matched by adjusting their melt temperatures such that their viscosities are within 30% of each other. The die/feedblock temperature was 350° F. The resulting coextruded ABA articles had good flow and rheological match, resulting in uniform foam/adhesive formation and uniform micro-foam structure. The skin to core ratio was controlled by the feeding ratios from the two extruders such that the split was 1:2:1. The multilayer melt stream was then spread out in the cast film die and then quenched on a chill roll with a double-coated release liner. The sample was then wound up in a roll format. Sample rolls of 2 mil, 4 mil, and 8 mil overall thicknesses were made by adjusting the casting wheel speed.
The polyester polymer used in this Example was synthesized as follows: The polyester polymer was synthesized in a 7.6 liter batch reactor with the following raw material charge:
isophthalic acid (1221 grams),
sebacic acid (1553 grams),
ethylene glycol (1003 grams),
1,6-hexanediol (1288 grams),
cyclohexanedimethanol (766 grams),
trimethylolpropane (24.2 grams),
trimethylolpropane monoallyl ether (63.7 grams),
triethyl phosphonoacetate (2.0 g), and
tetrabutyl titanate (2.0 grams).
All reagents are commonly commercially available. Under a pressure of 20 psig, this mixture was heated to 254° C. while removing water (a reaction by-product). After approximately 541 grams of water was removed, the pressure was gradually reduced to about 1 mmHg while heating to 275° C. The condensation reaction by-product, ethylene glycol, was continuously removed until a polymer with an intrinsic viscosity of 1.2 dL/g (as measured in 60/40 wt. % phenol/o-dichlorobenzene at 23° C.) was produced.
The resulting polyester polymer exhibited a glass transition of −28 C by DSC and a Mw of 200 kg/mol by GPC.
The film was made on a coextrusion line. Two hot melt twin-screw extruders were set up side by side. The combination of a 3 layer ABA feedblock and a cast film die was used. The skin extruder, Extruder A, was fed with the following composition:
The melt temperature of the skin extruder was controlled at 320° F. (160° C.). The screw was run at 200 rpm. A gear pump was used to control the feed rate into the feedblock. The feedblock split the skin adhesive melt stream into two and fed them onto the outer surfaces of the core layer. The other extruder, Extruder B, was fed with the following composition:
39% by weight KRATON D1161 P linear triblock copolymer based on styrene and isoprene, with a polystyrene content of 15% (Kraton Performance Polymers, Houston, Tex.)
5% by weight IonPhasE IPE PE 0107M, a static dissipative polymer (IonPhasE Oy, Tempere, Finland)
5% by weight NUCREL 960 Ethylene-Methacrylic Acid Copolymer (DuPont Co., Wilmington, Del.) 17% by weight CUMAR 130 aromatic hydrocarbon resin (Neville Chem. Co., Pittsburgh, Pa.)
25% by weight ARKON P-125 alicyclic saturated hydrogenated hydrocarbon resin (Arakawa Chem. Ind., Ltd., Osaka, Japan)
6% by weight REMAFIN BLACK 40% black pigment EVA masterbatch (Clariant, Charlotte, N.C.)
1% by weight IRGANOX 1726 multifunctional phenolic antioxidant (BASF Corp., Florham Pk., N.J.).
2% by weight ECOCELL-P. foaming agent (Polyfil Corp., Rockaway, N.J.).
The melt temperature of the core extruder was controlled at 350° F. (177° C.). The rheological characteristics of the adhesive layers and core layer were closely matched by adjusting their melt temperatures such that their viscosities were close to each other. The die/feedblock temperature was 330° F. (166° C.). The resulting coextruded multilayer article had good flow properties, resulting in uniform foam/adhesive formation and uniform micro-foam structure. The feeding ratio from the two extruders was controlled at 1.0:2.5 (Skin extruder to Core extruder). The multilayer melt stream was then spread out in the cast film die and then quenched on a chill roll with a double-coated release liner. The sample was then wound up in a roll format. Sample rolls of 11 mil (0.28 mm) overall thicknesses were collected.
This polyester composition was synthesized in a 8000 cc reactor with the following raw material charge: ethylene glycol (7 parts by mole of total diols), 1,6-hexanediol (60 parts by mole of total diols), 1,4-cyclohexane dimethanol (30 parts by mole of total diols), trimethylolpropane (1 parts by mole of total diols), trimethylolpropane monoallyl ether (2 parts by mole of total diols), sebacic acid (50 parts by mole of total acids), isophthalic acid (50 parts by mole of total acids), tetrabutyl titanate (450 ppm by total theoretical polymer weight based on monomers charged), and triethylphosphonoacetate (450 ppm by total theoretical polymer weight based on monomers charged). The mixture was heated to a temperature of 248° C. at a pressure of two atmospheres (270 kPa) and the mixture allowed to react while removing the water by-product. After completing the reaction and removing water, the pressure was reduced to the 0.5 to 5 mmHg range while heating to 271° C. The condensation by-product was continuously removed until a polymer of viscous nature was produced.
The Mw of the resulting polyester determined by GPC was 155 kg/mol and the polydispersity index was 6.1. The Tg determined by DSC was −26° C. This polyester was free of crystallinity with ΔHm of 0 J/g by DSC. The storage modulus at room temperature (G′) was 1×105 Pa as determined by Dynamic Mechanical Analysis (DMA).
To examine the peel adhesion, the polyester of Example 16 was hot melt extruded in a twin screw extruder. The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The melt was cast onto a release liner to form an adhesive transfer tape of 50 micrometer thickness. The resulting tape was then tested on a stainless steel substrate by the 180 degree peel test. The peel adhesion was measured to be 2200 g/cm.
The polyester of Example 16 was hot melt extruded in a twin screw extruder along with a tackifier, FORAL 85 (Eastman Chemical Co., Kingsport, Tenn.), at the composition ratio of 70 wt/30 wt % (Polyester/Foral 85). The extruder melt temperature was controlled at 176° C. and screw speed was 100 rpm. The mixed melt was then cast onto a release liner to form a transfer tape of 50 micrometer thickness. The resulting tape was then tested on a stainless steel substrate by the 180 degree peel test.
The peel adhesion was measured to be 2400 g/cm.
The following is a list of exemplary embodiments of the present description.
Embodiment 1 is a polyester comprising:
at least two different diacid residues;
at least two different diol residues;
wherein the polyester comprises at least one pendant group containing an alkenyl group, a ratio of a total number of the at least one pendant group to the total number of ester groups in the polyester being in a range of 0.001 to 0.1,
wherein the polyester has a glass transition temperature in a range of −50° C. to −10° C., and
wherein the polyester is a pressure-sensitive adhesive.
Embodiment 2 is the polyester of Embodiment 1, wherein the at least two different diacid residues comprises the at least one pendant group.
Embodiment 3 is the polyester of Embodiment 1, wherein the at least two different diol residues comprises the at least one pendant group.
Embodiment 4 is the polyester of Embodiment 1, wherein the at least two different diol residues comprises, based on the total moles of the at least two different diol residues, 0.1 to 10 percent of a residue of trimethylolpropane monoallyl ether.
Embodiment 5 is the polyester of Embodiment 1, wherein the at least two different diol residues comprises, based on the total moles of the at least two different diol residues, 0.5 to 5 percent of a residue of trimethylolpropane monoallyl ether.
Embodiment 6 is the polyester of Embodiment 1, wherein the alkenyl group is an allyl group.
Embodiment 7 is the polyester of Embodiment 1, wherein the alkenyl group is an allyloxy group.
Embodiment 8 is the polyester of Embodiment 1, wherein the at least two different diacid residues comprises a residue of at least one aromatic dicarboxylic acid.
Embodiment 9 is the polyester of Embodiment 8, wherein the residue of the at least one aromatic dicarboxylic acid comprises a residue of at least one of isophthalic acid, phthalic acid, terephthalic acid, bibenzoic acid, and naphthalic acid.
Embodiment 10 is the polyester of Embodiment 1, wherein the at least two different diacid residues comprises a residue of at least two of isophthalic acid, phthalic acid, terephthalic acid, bibenzoic acid, and naphthalic acid, adipic acid, and sebacic acid.
Embodiment 11 is the polyester of Embodiment 1, wherein the at least two different diol residues comprises a residue of at least two of ethylene glycol, 1,6-hexanediol, 1,4-butanediol, neopentyl glycol, and 1,4-cyclohexanedimethanol.
Embodiment 12 is the polyester of Embodiment 1 having a weight-average molecular weight in a range of 100 kg/mole to 1000 kg/mole.
Embodiment 13 is the polyester of Embodiment 12, wherein the weight-average molecular weight is in a range of 200 kg/mole to 500 kg/mole.
Embodiment 14 is the polyester of Embodiment 1 having an intrinsic viscosity in a range of 0.8 to 2 dL/g.
Embodiment 15 is the polyester of Embodiment 14, wherein the intrinsic viscosity is in a range of 1.0 to 1.6 dL/g.
Embodiment 16 is a crosslinked polyester preparable by at least partially curing the polyester of any one of Embodiments 1 to 15.
Embodiment 17 is the crosslinked polyester of Embodiment 16 having a crosslinking density, as determined by gel-percent test, of less than 35 percent.
Embodiment 18 is a crosslinked polyester comprising:
at least two different diacid residues;
at least two different diol residues;
wherein the crosslinked polyester has a glass transition temperature in a range of −50° C. to −10° C.,
wherein the crosslinked polyester has a crosslinking density, as determined by gel-percent test, of less than 35 percent, and
wherein the crosslinked polyester is a pressure-sensitive adhesive.
Embodiment 19 is the polyester any one of Embodiments 1 to 15 or the crosslinked polyester of any one of Embodiments 16 to 18 having a shear modulus, G′, at 1 Hz and 23° C., as determined by dynamical mechanical analysis, in a range of 0.001 MPa to 1 MPa.
Embodiment 20 is the polyester of Embodiment 19, wherein the shear modulus is less than 0.5 MPa.
Embodiment 21 is the polyester of Embodiment 19, wherein the shear modulus is less than 0.3 MPa.
Embodiment 22 is the polyester any one of Embodiments 1 to 15 or the crosslinked polyester of any one of Embodiments 16 to 18 having a crystallinity, as determined by the heat of melting determined by differential scanning calorimetry (DSC), of less than 5 J/g.
Embodiment 23 is the polyester of Embodiment 22, wherein the crystallinity is less than 1 J/g.
Embodiment 24 is a pressure-sensitive adhesive composition comprising the polyester of any one of Embodiments 1 to 15 or the crosslinked polyester of any one of Embodiments 16 to 18, and further comprising 1 to 60 weight percent tackifier.
Embodiment 25 is the pressure-sensitive adhesive composition of Embodiment 24 comprising 1 to 30 weight percent of the tackifier.
Embodiment 26 is the pressure-sensitive adhesive composition of Embodiment 24 comprising 1 to 15 weight percent of the tackifier.
Embodiment 27 is a tape comprising a substrate and the polyester of any one of Embodiments 1 to 15 or the crosslinked polyester of any one of Embodiments 16 to 18 or the pressure-sensitive adhesive composition of any one of Embodiments 24 to 26 disposed on the substrate.
Embodiment 28 is the tape of Embodiment 27, having a peel strength of at least 300 g/cm when tested at a 180 degree peel from a stainless steel substrate at a peel rate of 300 mm/minute.
Embodiment 29 is the tape of Embodiment 28, wherein the peel strength is at least 1000 g/cm.
Embodiment 30 is the tape of Embodiment 28, wherein the peel strength is at least 2000 g/cm.
Embodiment 31 is a tape comprising a first layer, a second layer and a third layer, the first layer disposed directly on a first major surface of the second layer, the third layer disposed directly on a second major surface of the second layer opposite the first major surface of the second layer, the first and third layers comprising the polyester of any one of Embodiments 1 to 15 or the crosslinked polyester of any one of Embodiments 16 to 18 or the pressure-sensitive adhesive composition of any one of Embodiments 24 to 26.
Embodiment 32 is the tape of Embodiment 31, wherein the second layer comprises a polyester comprising a residue of at least one aromatic dicarboxylic acid.
Embodiment 33 is the tape of Embodiment 31, wherein the second layer is a foamed layer.
Descriptions for elements in figures should be understood to apply equally to corresponding elements in other figures, unless indicated otherwise. Although specific embodiments have been illustrated and described herein, it will be appreciated by those of ordinary skill in the art that a variety of alternate and/or equivalent implementations can be substituted for the specific embodiments shown and described without departing from the scope of the present disclosure. This application is intended to cover any adaptations or variations of the specific embodiments discussed herein. Therefore, it is intended that this disclosure be limited only by the claims and the equivalents thereof.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2016/046463 | 8/11/2016 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2017/030881 | 2/23/2017 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3658670 | Holicky | Apr 1972 | A |
| 3804921 | Jamison | Apr 1974 | A |
| 3932326 | Hoh | Jan 1976 | A |
| 4028305 | Li et al. | Jun 1977 | A |
| 4091141 | Harris | May 1978 | A |
| 4122073 | Georgoudis | Oct 1978 | A |
| 4124571 | Georgoudis | Nov 1978 | A |
| 4477636 | Muroi | Oct 1984 | A |
| 4745141 | Akiyama | May 1988 | A |
| 4820745 | Muller | Apr 1989 | A |
| 4822829 | Muller | Apr 1989 | A |
| 4873023 | Schulz | Oct 1989 | A |
| 5278199 | Ohkawa | Jan 1994 | A |
| 5371112 | Sayre | Dec 1994 | A |
| 5380775 | Cowley | Jan 1995 | A |
| 5656681 | Shimizu | Aug 1997 | A |
| 5674623 | Haddon | Oct 1997 | A |
| 5879759 | Zang | Mar 1999 | A |
| 5900473 | Acevedo | May 1999 | A |
| 6342122 | Riley | Jan 2002 | B1 |
| 6429235 | Varlemann | Aug 2002 | B1 |
| 6645617 | Okazaki | Nov 2003 | B1 |
| 8962136 | Takahira | Feb 2015 | B2 |
| 8999503 | Takahira | Apr 2015 | B2 |
| 20020016407 | Buter | Feb 2002 | A1 |
| 20030069323 | Varlemann | Apr 2003 | A1 |
| 20030232222 | Anderson | Dec 2003 | A1 |
| 20040039136 | Godi | Feb 2004 | A1 |
| 20040072964 | Udding et al. | Apr 2004 | A1 |
| 20040087714 | Baumgart | May 2004 | A1 |
| 20050025903 | Fink | Feb 2005 | A1 |
| 20060047140 | Hayakawa | Mar 2006 | A1 |
| 20070010651 | Finch et al. | Jan 2007 | A1 |
| 20070027269 | Stumbe | Feb 2007 | A1 |
| 20100184880 | Fukui | Jul 2010 | A1 |
| 20100255239 | Hammond | Oct 2010 | A1 |
| 20110244156 | Lock | Oct 2011 | A1 |
| 20110257273 | Yabuuchi | Oct 2011 | A1 |
| 20120208016 | Takahira | Aug 2012 | A1 |
| 20120208017 | Yoshie | Aug 2012 | A1 |
| 20140107246 | Bigwood | Apr 2014 | A1 |
| 20150184040 | Tian | Jul 2015 | A1 |
| 20160312073 | Yoshida | Oct 2016 | A1 |
| 20180215959 | Liu | Aug 2018 | A1 |
| 20180237585 | Liu | Aug 2018 | A1 |
| Number | Date | Country |
|---|---|---|
| 1430657 | Jul 2003 | CN |
| 0558905 | Sep 1993 | EP |
| 2325228 | May 2011 | EP |
| 2003-268052 | Sep 2003 | JP |
| 2003-268052 | Sep 2003 | JP |
| 2007-099879 | Apr 2007 | JP |
| 201202361 | Jan 2012 | TW |
| WO 2015-093526 | Jun 2015 | WO |
| WO 2017-030877 | Feb 2017 | WO |
| WO 2017-031042 | Feb 2017 | WO |
| Entry |
|---|
| JP 2003-268052 A (Nakajima et al) (published Sep. 25, 2003) full English translation (Year: 2003). |
| International Search Report for PCT International Application No. PCT/US2016/046463, dated Nov. 1, 2016, 3 pages. |
| Cheng, “Popularization book on Modern Petroleum and Petrochemical Industry Technology: Synthetic Rubber”, China Petrochemical Press, Oct. 2000, pp. 85. |
| Handbook of Polyurethane Elastomers, Chemical Industry Press of China, Jan. 2001, pp. 359. |
| Number | Date | Country | |
|---|---|---|---|
| 20180215970 A1 | Aug 2018 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62206618 | Aug 2015 | US | |
| 62356010 | Jun 2016 | US |