The present invention relates generally to the data processing field, and more particularly, relates to pre-treated water cooling hoses and a method for implementing pretreatment of water cooling hoses for increased reliability.
Current high performance computer systems have rapidly migrated to water cooling solutions to effectively remove the massive heat load from the central electronic complex (CEC). The system design typically includes a flexible tubing option incorporating a large number of connections to a cold plate/heat sink.
The cooling liquid chosen is typically a deionized water solution containing a corrosion inhibitor to protect the copper within the system from corroding. Challenges arise though due to depletion of the corrosion inhibitors to other materials such as the hose, which ultimately may lead to the corroding of the copper components and present a challenge to ensure adequate product reliability over the life of the system.
A need exists for an efficient and effective pretreatment of the water cooling hoses to maintain acceptable levels of corrosion inhibitors within the water cooling loop over the life of the system. It is desirable to provide such pretreatment for water cooling hoses including ethylene propylene diene monomer (EPDM) water cooling hoses.
EPDM rubber (ethylene propylene diene monomer rubber) is a type of synthetic rubber, which is an elastomer or a polymer with viscoelasticity, often used in water cooling applications.
Principal aspects of the present invention are to provide pre-treated water cooling hoses and a method for implementing pretreatment of water cooling hoses for increased reliability. Other important aspects of the present invention are to provide such pre-treated water cooling hoses and method substantially without negative effects and that overcome many of the disadvantages of prior art arrangements.
In brief, pre-treated water cooling hoses and a method for implementing pretreatment of water cooling hoses for increased reliability are provided. Pretreatment of the water cooling hoses includes attaching the water cooling hose to a water cooling system, filling the water cooling system with a high concentration corrosion inhibitor solution, and running the system for an extended time to saturate the attached hose with the high concentration corrosion inhibitor.
In accordance with features of the invention, the water cooling hoses include an ethylene propylene diene monomer (EPDM) water cooling hoses. The water cooling hoses include zinc oxide cured hoses. The high concentration corrosion inhibitor solution used for pretreatment of the water cooling hoses includes a high concentration solution of benzotriazole (BTA), such as 10,000 ppm BTA.
In accordance with features of the invention, the pretreatment method enables the use of zinc oxide hoses, eliminating the need for processing by peroxide curing.
In accordance with features of the invention, the pre-treated water cooling hoses provide increased reliability.
In accordance with features of the invention, the pre-treated water cooling hoses maintain acceptable levels of corrosion inhibitors within the water cooling loop over the life of the system.
The present invention together with the above and other objects and advantages may best be understood from the following detailed description of the preferred embodiments of the invention illustrated in the drawings, wherein:
In the following detailed description of embodiments of the invention, reference is made to the accompanying drawings, which illustrate example embodiments by which the invention may be practiced. It is to be understood that other embodiments may be utilized and structural changes may be made without departing from the scope of the invention.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.
In accordance with features of the invention, pre-treated water cooling hoses and a method for implementing pretreatment of water cooling hoses for increased reliability are provided.
EPDM rubber (ethylene propylene diene monomer rubber) is a type of synthetic rubber, which is an elastomer or a polymer with viscoelasticity, often used in water cooling applications. Benzotriazole (BTA) is a common copper corrosion inhibitor that adsorbs to metal oxides including MgO, PbO, ZnO, and the like. These metal oxides are typically found in EPDM hoses.
In order to prevent the adsorption of BTA onto metal oxides, hoses are usually processed by peroxide curing without zinc oxide. This process of peroxide curing further drives up the cost of a typically inexpensive hose and complicates manufacturing due to the requirement of inert atmospheres.
To overcome cost and depletion challenges, the present invention provides a method to prevent significant depletion of BTA in metal oxide containing EPDM hoses. Typically, systems run 1000 ppm BTA solutions with the intent that the BTA will be maintained over the life of the system. This is possible with peroxide cured hoses but not with zinc oxide. The method of the present invention allows the use of zinc oxide hoses by utilizing a pre-treatment process in manufacturing settings.
Having reference now to the drawings, in
As indicated at a block 102, the assembled water cooling hoses including EPDM water cooling hoses are attached to a water cooling system. For example, a zinc-oxide hose is first assembled with quick-connects, barbs, and clamps at block 100, and then assembled to a water cooling system at block 102.
The water cooling system is filled with a high concentration corrosion inhibitor solution as indicated in a block 104. Benzotriazole (BTA) is a heterocyclic compound containing three nitrogen atoms, with the chemical formula C6H5N3 and is a common copper corrosion inhibitor that adsorbs to metal oxides including MgO, PbO, ZnO, and the like. These metal oxides are typically found in water cooling hoses, such as EPDM water cooling hoses.
The water cooling system is run for an extended time to saturate the water cooling hoses with the high concentration corrosion inhibitor solution as indicated in a block 106. During system test and pretreatment of the water cooling system at block 104, a high concentration of BTA, such as a 10,000 ppm BTA, is passed through the system in order to saturate the zinc oxide cured hoses and maintained for an extended time, such as 24 hours. Conventionally, a 1000 ppm BTA solution is used, while this low concentration is not sufficient to maintain acceptable levels of corrosion inhibitors over the life of a system.
Prior to shipping, the water cooling system is drained and then is shipped to the field for use as indicated in a block 108. The water cooling system is filled with a low concentration corrosion inhibitor solution, such as a 1,000 ppm BTA solution, as indicated in a block 110. By using pretreatment with the high concentration of BTA, the hose becomes saturated and the zinc oxide will no longer significantly deplete BTA.
In accordance with features of the invention, the use of the high concentration corrosion inhibitor solution for pre-treatment of the water cooling hoses is provided in order to maintain acceptable levels of corrosion inhibitors within the water cooling loop over the life of the system. Challenges are avoided that otherwise arise due to depletion of the corrosion inhibitors to other materials such as the hose, which ultimately may lead to the corroding of the copper components. The process of the invention to pre-treat water cooling hoses decreases the amount of depletion of the corrosion inhibitor within the water cooling loop improving the reliability of the cooling system. By pre-treating water cooling hoses, other hoses may be used that are most cost effective.
Referring also to the data of
Typically, systems run 1000 ppm BTA solutions with the intent that the BTA will be maintained over the life of the system. For example, this is possible with peroxide cured hoses but not with zinc oxide cured hoses, as illustrated in
It should be understood that the present invention is not limited to the example pretreatment time and high concentration of BTA provided in
While the present invention has been described with reference to the details of the embodiments of the invention shown in the drawing, these details are not intended to limit the scope of the invention as claimed in the appended claims.