Patent Application
20220158305
The instant disclosure is directed to new, improved or optimized battery separators, Z wrap separators, Z wrap serrated rib separators, Z wrap serrated rib separators for tubular batteries, components, cells, modules, systems, batteries, tubular batteries, industrial batteries, inverter batteries, batteries for heavy or light industrial applications, forklift batteries, float charged batteries, inverters, accumulators, methods, profiles, additives, compositions, composites, mixes, coatings, and/or related methods of Z wrapping separators, Z wrapping separators on electrodes of tubular batteries, water retention, water loss prevention, improved charge acceptance, production, use, and/or related Z wrapping equipment, and/or combinations thereof. More particularly, the present invention is directed to one or more improved battery separators having various improvements that may result in automated separator Z wrapping, automated Z wrapped cell module production, automated tubular battery production, decreased water loss for a battery in which such a separator is incorporated, enhanced charge acceptance, or combinations thereof. Additionally, the present invention relates to one or more improved battery separators having various improvements with regard to shape, and/or physical profile, and/or chemical(s), additives, mixes, coatings, and/or the like used to make such battery separators (such as oil(s), and/or chemical additive(s) or agents used to coat, finish or improve such battery separators (such as surfactant(s))). Furthermore, the present invention relates to one or more improved separator configurations, Z wrap cell modules, Z wrap tubular electrodes, and/or battery electrode and separator assembly configurations providing for automation, better acid mixing and/or reduced acid stratification over prior sleeves, pockets, or envelope separator configurations. One or more improved battery electrode and separator assembly configurations and/or manufacturing methods and/or manufacturing equipment. The improved Z wrap battery separators of the instant invention are particularly useful in or with tubular batteries, industrial batteries, such as inverter batteries, batteries for heavy or light industry, and so forth.
Various batteries are used in industrial settings and/or settings in which deep discharge is desirable. Such batteries may include, but are not limited to, for example, lead acid batteries, inverter batteries, solar batteries, golf cart batteries, batteries for equipment (such as a floor scrubber or the like), batteries for a forklift or other equipment, submarine batteries, tubular inverter batteries, flat plate inverter batteries, and/or flooded inverter batteries. As is known, discharging deeply means that the battery must provide a lot of energy over a long period of time; therefore, such batteries may begin with a relatively high capacity for energy storage and loose some of its capacity in service over a period of time. Such deep discharge may mean that it may take a relatively long amount of time to fully re-charge such a battery to its full capacity. Thus, improving re-chargeability of such a battery may be important, and obtaining a battery with an improved state of charge or higher partial state of charge may also be important in the battery industry.
For at least certain applications, and charge/discharge cycling applications in particular, it is desirable to provide battery separators far industrial batteries that differentiate from previously known battery separators. A battery separator is a component that divides, or “separates”, the positive electrode from the negative electrode within a battery cell. A battery separator may have two primary functions. First, a battery separator should keep the positive electrode physically apart from the negative electrode in order to prevent any electronic current passing between the two electrodes. Second, a battery separator should permit an ionic current between the positive and negative electrodes with the least possible resistance. A battery separator may be made out of many different materials, but these two opposing functions have been met well by a battery separator being made of a porous nonconductor.
Improving the re-chargeability of industrial batteries (such as, for example, inverter batteries) is desired. As is known, an inverter turns DC into AC and may be helpful in a wide variety of settings, such as areas where a power grid is unstable or has been deteriorated. Batteries such as inverter batteries operate primarily under a partial state of charge. Constantly operating in a partial state of charge may mean that corrosion occurs, and/or battery life is compromised, and/or negative plate sulfation may become a limiting factor in the performance and life of such batteries. Enhancing the re-chargeability of the battery as well as lowering the amount of water loss encountered by the battery are desirable.
Some previously known battery separators, despite having improved features, have not been able to facilitate automation, to increase acid mixing, to reduce acid stratification, and/or to improve the charge acceptance, and therefore, re-chargeability, of the industrial batteries in which they are placed. Thus, a need exists for an improved battery separator for an industrial battery that provides various improvements over known separators. An improved battery separator that meets such needs may result in improvements in battery characteristics, such as improved charge acceptance of the battery, improved re-chargeability of the battery, reduced water loss of the battery, improved charge/discharge cycling efficiency of the battery, and/or extended life of the battery.
In accordance with at least selected embodiments, the instant invention or disclosure may address one or more of the above mentioned desires, needs, issues, and/or problems and may provide new, improved or optimized battery separators, Z wrap separators, Z wrap serrated rib separators, Z wrap serrated rib separators for tubular batteries, components, cells, modules, systems, batteries, tubular batteries, industrial batteries, inverter batteries, batteries for heavy or light industrial applications, forklift batteries, float charged batteries, inverters, accumulators, methods, profiles, additives, compositions, composites, mixes, coatings, and/or related methods of Z wrapping separators, Z wrapping separators on electrodes of tubular batteries, water retention, water loss prevention, improved charge acceptance, production, use, and/or related Z wrapping equipment, and/or combinations thereof. More particularly, the present invention is directed to one or more improved battery separators having various improvements that may result in automated separator Z wrapping, automated Z wrapped cell module production, automated tubular battery production, decreased water loss for a battery in which such a separator is incorporated, enhanced charge acceptance, or combinations thereof. Additionally, the present invention relates to one or more improved battery separators having various improvements with regard to shape, and/or physical profile, and/or chemical(s), additives, mixes, coatings, and/or the like used to make such battery separators (such as oil(s), and/or chemical additive(s) or agents used to coat, finish or improve such battery separators (such as surfactant(s))). Furthermore, the present invention relates to one or more improved separator configurations, Z wrap cell modules, Z wrap tubular electrodes, z wrap gauntlet covered tubular electrodes, and/or battery electrode and separator assembly configurations providing for automation, better acid mixing and/or reduced acid stratification over prior sleeves, pockets, or envelope separator configurations. One or more improved battery electrode and separator assembly configurations and/or manufacturing methods and/or manufacturing equipment. The improved Z wrap battery separators of the instant invention are particularly useful in or with tubular batteries, industrial batteries, such as inverter batteries, batteries for heavy or light industry, and so forth.
In accordance with at least certain embodiments, aspects or objects, the instant invention or disclosure may address one or more of the above mentioned desires, needs, issues, and/or problems and may provide new, improved or optimized battery separators, Z wrap separators, Z wrap serrated rib separators, Z wrap serrated rib separators for tubular batteries, components, cells, modules, systems, batteries, tubular batteries, industrial batteries, inverter batteries, batteries for heavy or light industrial applications, forklift batteries, float charged batteries, inverters, accumulators, methods, profiles, additives, compositions, composites, mixes, coatings, and/or related methods of Z wrapping separators, Z wrapping separators on electrodes of tubular batteries, water retention, water loss prevention, improved charge acceptance, production, use, and/or related Z wrapping equipment, and/or battery separators and methods relating to batteries, including, but not limited to, industrial batteries. In at least select embodiments, the battery separator may have an improved physical shape and/or profile and may include an optimized amount of one or more chemical additives, such as one or more surfactants, to provide the improved battery separator with improved properties. Additionally, the present invention relates to one or more improved battery separators having various improvements with regard to shape, and/or physical profile, and/or chemical(s) used to make such battery separators (such as oil), and/or chemical additive(s) used to coat, finish or improve such battery separators (such as surfactants).
The improved battery separators and methods of the present invention may result in improved battery properties for batteries into which such separators are incorporated. Such improved properties include, but are not limited to, increased charge acceptance for the battery in which the separator is used and increased re-chargeability for such battery as well as decreased water loss for such a battery. The improved battery separators of the instant invention are particularly useful with industrial batteries, such as inverter batteries, batteries for heavy or light duty industrial applications, and so forth. In accordance with at least selected embodiments, aspects, or objects, the present invention may address the limitations of the prior art and is directed to new, improved or optimized battery separators, components, batteries, industrial batteries, inverter batteries, batteries for heavy or light industrial applications, forklift batteries, float charged batteries, inverters, accumulators, systems, methods, profiles, additives, compositions, composites, mixes, coatings, and/or related methods of water retention, water loss prevention, improved charge acceptance, production, use, and/or combinations thereof. More particularly, the present invention is directed to one or more improved battery separators having various improvements that may result in decreased water loss for a battery in which such a separator is incorporated, enhanced charge acceptance, or combinations thereof. Additionally, the present invention relates to one or more improved battery separators having various improvements with regard to shape, and/or physical profile, and/or chemical(s), additives, mixes, coatings, and/or the like used to make such battery separators (such as oil(s), and/or chemical additive(s) or agents used to coat, finish or improve such battery separators (such as surfactant(s))). The improved battery separators of the instant invention are particularly useful in or with industrial batteries, such as inverter batteries, batteries for heavy or light duty industrial applications, and so forth.
The details of one or more embodiments are set forth in the description herinafter. Other features, objects, and advantages will be apparent from the description and from the claims. In accordance with at least select embodiments, the present disclosure or invention may address the above issues or needs. In accordance with at least certain embodiments, aspects, or objects, the present disclosure or invention may provide an improved separator and/or battery utilizing said separator which overcomes the aforementioned problems. For instance, by providing batteries having reduced acid starvation; reduced acid stratification; improved separator resiliency; mitigating the formation of dendrites; increased oxidation resistance; reduced water loss; reduced internal resistance; increased separator wettability; improved acid diffusion through the separator; improved cold cranking amps, improved uniformity; and/or having improved cycling performance; and any combination thereof.
In certain preferred embodiments, the present disclosure or invention provides a battery separator whose components and physical attributes and features synergistically combine to address, in unexpected ways, previously unmet needs in the deep cycle battery industry, with an improved battery separator (a separator having a porous, membrane of polymer, such as polyethylene, plus a certain amount of a performance enhancing additive and ribs) that meets or, in certain embodiments, exceeds the performance of the previously known flexible, which are currently used in many deep cycle battery applications. In particular, the inventive separators described herein are more robust, less fragile, less brittle, more stable over time (less susceptible to degradation) than separators traditionally used with deep cycle batteries. The flexible, performance enhancing additive-containing and rib possessing separators of the present invention combine the desired robust physical and mechanical properties of a polyethylene-based separator with the capabilities of a conventional separator, while also enhancing the performance of the battery system employing the same.
In accordance with at least selected embodiments, the present disclosure or invention may address the above issues or needs. In accordance with at least certain objects, the present disclosure or invention may provide an improved separator and/or battery which overcomes the aforementioned problems, for instance by providing for increased automation and/or production of Z wrap separators, cells, cell modules, tubular batteries, inverter batteries, and/or enhanced flooded batteries having reduced acid starvation, reduced acid stratification, reduced dendrite growth, reduced internal electrical resistance and/or increased cold cranking amps.
In accordance with at least select embodiments, the present disclosure or invention may address the above issues or needs. In accordance with at least certain objects, aspects, or embodiments, the present disclosure or invention may provide an improved separator and/or battery which overcomes the aforementioned problems, for instance by providing batteries with separators that reduce acid starvation and/or mitigate the effects of acid starvation.
In accordance with at least select embodiments, the present disclosure or invention is directed to novel or improved separators, cells, batteries, systems, and/or methods of manufacture and/or use of such novel separators, cells, and/or batteries. In accordance with at least certain embodiments, the present disclosure or invention is directed to novel or improved battery separators for flat-plate batteries, tubular batteries, flooded lead acid batteries, enhanced flooded lead acid batteries (“EFBs”), deep-cycle batteries, gel batteries, absorptive glass mat (“AGM”) batteries, inverter batteries, solar or wind power storage batteries, vehicle batteries, starting-lighting-ignition (“SLI”) vehicle batteries, idling-start-stop (“ISS”) vehicle batteries, automobile batteries, truck batteries, motorcycle batteries, all-terrain vehicle batteries, forklift batteries, golf cart batteries, hybrid-electric vehicle batteries, electric vehicle batteries, e-rickshaw batteries, e-bike batteries, and/or improved methods of making and/or using such improved separators, cells, batteries, systems, and/or the like. In addition, disclosed herein are methods, systems and battery separators for enhancing battery performance and life, reducing battery failure, reducing acid stratification, mitigating dendrite formation, improving oxidation stability, improving, maintaining, and/or lowering float current, improving end of charge current, decreasing the current and/or voltage needed to charge and/or fully charge a deep cycle battery, reducing internal electrical resistance, reducing antimony poisoning, increasing wettability, improving acid diffusion, improving uniformity in a lead acid battery, and/or improving cycle performance. In accordance with at least particular embodiments, the present disclosure or invention is directed to an improved separator wherein the novel separator includes decreased electrical resistance, performance enhancing additives or coatings, improved fillers, increased wettability, increased acid diffusion, negative cross ribs, and/or the like.
Referring now to
Physical Description
An exemplary separator may be provided with a web of a porous membrane, such as a microporous membrane having pores less than about 5 μm, preferably less than about 1 μm, a mesoporous membrane, or a macroporous membrane having pores greater than about 1 μm. The porous membrane may preferably have a pore size that is sub-micron up to 100 μm, and in certain embodiments between about 0.1 μm to about 10 μm. Porosity of the separator membrane described herein may be greater than 50% to 60% in certain embodiments. In certain select embodiments, the porous membrane may be flat or possess ribs that extend from a surface thereof.
Ribs
With reference now to
While it is preferred that the positive ribs 304 face a positive electrode and the negative cross ribs 306 face a negative electrode, they may nonetheless be disposed on opposite sides and face the opposite electrode, may have serrated ribs on both sides, and/or the negative cross ribs may be instead disposed in a machine or longitudinal direction.
The positive ribs 304 or negative ribs 306 may additionally be any form or combination of solid ribs, discrete broken ribs, continuous ribs, discontinuous ribs, discontinuous peaks, discontinuous protrusions, angled ribs, linear ribs, longitudinal ribs extending substantially in a machine direction of said porous membrane, lateral ribs extending substantially in a cross-machine direction of said porous membrane, transverse ribs extending substantially in said cross-machine direction of the separator, discrete teeth, toothed ribs, serrations, serrated ribs, battlements, battlemented ribs, curved ribs, sinusoidal ribs, disposed in a continuous zig-zag-sawtooth-like fashion, disposed in a broken discontinuous zig-zag-sawtooth-like fashion, grooves, channels, textured areas, embossments, dimples, columns, mini columns, porous, non-porous, mini ribs, cross-mini ribs, and combinations thereof.
With reference now to
In some select embodiments, at least a portion of the porous membrane may have negative ribs that are longitudinal or transverse or cross-ribs. The negative ribs may be parallel to the top edge of the separator, or may be disposed at an angle thereto. For instance, the negative ribs may be oriented approximately 0°, 5°, 15°, 25°, 30°, 45°, 60°, 70°, 80°, or 90° relative to the top edge. The cross-ribs may be oriented approximately 0° to approximately 30°, approximately 30° to approximately 45°, approximately 45° to approximately 60°, approximately 30° to approximately 60°, approximately 30° to approximately 90°, or approximately 60° to approximately 90° relative to the top edge.
Backweb Thickness In some embodiments, the porous separator membrane can have a backweb thickness from approximately 50 μm to approximately 1.0 mm. for example, the backweb thickness may be may be approximately 50 μm, 100 μm, 150 μm, 200 μm, 300 μm, 400 μm, 500 μm, 600 μm, 700 μm, 800 μm, 900 μm, or 1.0 mm. In other exemplary embodiments, the backweb thickness TBACK may be no greater than approximately 1.0 mm, 900 μm, 800 μm, 700 μm, 600 μm, 500 μm, 400 μm, 300 μm, 200 μm, 100 μm, or 50 μm. In certain preferred embodiments, a backweb thickness may be between approximately 200 μm and approximately 500 μm.
The total thickness of exemplary separators (backweb thickness and the heights of positive and negative ribs) typically range from approximately 250 μm to approximately 4.0 mm. The total thickness of separators used in automotive start/stop batteries are typically approximately 250 μm to approximately 1.0 mm. The total thickness of separators used in industrial traction-type start/stop batteries are typically approximately 1.0 mm to approximately 4.0 mm.
Assembly
With reference now to
With respect to tubular batteries, the radius of curvature of the separator matches well with the radius of the tubular electrodes or gauntlet covered tubular electrodes, and the spacing of the serrations is selected such that the backweb is less likely to come into contact with the tubular electrode or gauntlet covered tubular electrodes and oxidize. Having the top, bottom, and one edge open, the Z wrap allows for better electrolyte flow around the electrodes, enhances acid mixing, reduces acid stratification, increases filling speeds, increases cycle life, and/or the like.
In some embodiments two bottom edges of a z wrapped membrane that are facing one another may be sealed or partially sealed. Preferably, the two bottom edges (edges closest to the bottom of the battery) of the z wrapped membrane are on either side of an electrode. In some embodiments, all sets of edges that face each other may be sealed or partially sealed. For example, they may be sealed by at least one of the following means: stapling, gluing, or heat sealing. Partial sealing and stapling may be preferred as the flow of electrolyte is not so hindered. Also, sealing of the minimum number of edges needed to get the desired effect may be preferred so as to allow maximum movement of electrolyte. Sealing or partially sealing the bottom edges pf the z wrapped membrane may help to prevent floating up of the separator during battery operation. The seal will bump into an electrode preventing further movement upward.
In addition, negative cross ribs add some rigidity across the bend and prevent the separator from creasing, which may lead to punctures that result in early failures due to shorts.
With reference now to
First a separator web 300 is manufactured as a roll 400 (described hereinafter), and is fed into an assembler 410. The assembler picks a negative plate 201 on a first side of the web 300 and shuttles it into the web 300 and half wraps the negative electrode 201. The assembler then picks a positive electrode 200 on an opposite side of the web 300 and shuttles it into the web 300 and half wraps it.
Composition
In certain embodiments, the improved separator may include a porous membrane may be made of: a natural or synthetic base material; a processing plasticizer; a filler; natural or synthetic rubber(s) or latex, and one or more other additives and/or coatings, and/or the like.
Base Materials
In certain embodiments, exemplary natural or synthetic base materials may include: polymers; thermoplastic polymers; phenolic resins; natural or synthetic rubbers; synthetic wood pulp; lignins; glass fibers; synthetic fibers; cellulosic fibers; and any combination thereof. In certain preferable embodiments, an exemplary separator may be a porous membrane made from thermoplastic polymers. Exemplary thermoplastic polymers may, in principle, include all acid-resistant thermoplastic materials suitable for use in lead acid batteries. In certain preferred embodiments, exemplary thermoplastic polymers may include polyvinyls and polyolefins. In certain embodiments, the polyvinyls may include, for example, polyvinyl chloride (“PVC”). In certain preferred embodiments, the polyolefins may include, for example, polyethylene, polypropylene, ethylene-butene copolymer, and any combination thereof, but preferably polyethylene. In certain embodiments, exemplary natural or synthetic rubbers may include, for example, latex, uncross-linked or cross-linked rubbers, crumb or ground rubber, and any combination thereof.
Polyolefins
In certain embodiments, the porous membrane layer preferably includes a polyolefin, specifically polyethylene. Preferably, the polyethylene is high molecular weight polyethylene (“HMWPE”), (e.g., polyethylene having a molecular weight of at least 600,000). Even more preferably, the polyethylene is ultra-high molecular weight polyethylene (“UHMWPE”). Exemplary UHMWPE may have a molecular weight of at least 1,000,000, in particular more than 4,000,000, and most preferably 5,000,000 to 8,000,000 as measured by viscosimetry and calculated by Margolie's equation. Further, exemplary UHMWPE may possess a standard load melt index of substantially zero (0) as measured as specified in ASTM D 1238 (Condition E) using a standard load of 2,160 g. Moreover, exemplary UHMWPE may have a viscosity number of not less than 600 ml/g, preferably not less than 1,000 ml/g, more preferably not less than 2,000 ml/g, and most preferably not less than 3,000 ml/g, as determined in a solution of 0.02 g of polyolefin in 100 g of decalin at 130° C.
Rubber
The novel separator disclosed herein may contain latex and/or rubber. As used herein, rubber shall describe, rubber, latex, natural rubber, synthetic rubber, cross-linked or uncross-linked rubbers, cured or uncured rubber, crumb or ground rubber, or mixtures thereof. Exemplary natural rubbers may include one or more blends of polyisoprenes, which are commercially available from a variety of suppliers. Exemplary synthetic rubbers include methyl rubber, polybutadiene, chloropene rubbers, butyl rubber, bromobutyl rubber, polyurethane rubber, epichlorhydrin rubber, polysulphide rubber, chlorosulphonyl polyethylene, polynorbornene rubber, acrylate rubber, fluorine rubber and silicone rubber and copolymer rubbers, such as styrene/butadiene rubbers, acrylonitrile/butadiene rubbers, ethylene/propylene rubbers (“EPM” and “EPDM”) and ethylene/vinyl acetate rubbers. The rubber may be a cross-linked rubber or an uncross-linked rubber; in certain preferred embodiments, the rubber is uncross-linked rubber. In certain embodiments, the rubber may be a blend of cross-linked and uncross-linked rubber.
Plasticizer
In certain embodiments, exemplary processing plasticizers may include processing oil, petroleum oil, paraffin-based mineral oil, mineral oil, and any combination thereof.
Fillers
The separator can contain a filler having a high structural morphology. Exemplary fillers can include: silica, dry finely divided silica; precipitated silica; amorphous silica; highly friable silica; alumina; talc; fish meal; fish bone meal; carbon; carbon black; and the like, and combinations thereof. In certain preferred embodiments, the filler is one or more silicas. High structural morphology refers to increased surface area. The filler can have a high surface area, for instance, greater than 100 m2/g, 110 m2/g, 120 m2/g, 130 m2/g, 140 m2/g, 150 m2/g, 160 m2/g, 170 m2/g, 180 m2/g, 190 m2/g, 200 m2/g, 210 m2/g, 220 m2/g, 230 m2/g, 240 m2/g, or 250 m2/g. In some embodiments, the filler (e.g., silica) can have a surface area from about 100 m2/g to about 300 m2/g, about 125 m2/g to about 275 m2/g, 150 m2/g to about 250 m2/g, or preferably 170 m2/g to about 220 m2/g. Surface area can be assessed using TriStar 3000™ for multipoint BET nitrogen surface area. High structural morphology permits the filler to hold more oil during the manufacturing process. For instance, a filler with high structural morphology has a high level of oil absorption, for instance, greater than about 150 ml/100 g, 175 ml/100 g, 200 ml/100 g, 225 ml/100 g, 250 ml/100 g, 275 ml/100 g, 300 ml/100 g, 325 ml/100 g, or 350 ml/100 g. In some embodiments the filler (e.g., silica) can have an oil absorption from 200-500 ml/100 g, 200-400 ml/100 g, 225-375 ml/100 g, 225-350 ml/100 g, 225-325 ml/100 g, preferably 250-300 ml/100 g. In some instances, a silica filler is used having an oil absorption of 266 ml/100 g. Such a silica filler has a moisture content of 5.1%, a BET surface area of 178 m2/g, an average particle size of 23 μm, a sieve residue 230 mesh value of 0.1%, and a bulk density of 135 g/L.
In some select embodiments, the filler (e.g., silica) has an average particle size no greater than 25 μm, in some instances, no greater than 22 μm, 20 μm, 18 μm, 15 μm, or 10 μm. In some instances, the average particle size of the filler particles is 15-25 μm.
The particle size of the silica filler and/or the surface area of the silica filler contributes to the oil absorption of the silica filler. Silica particles in the final product or separator may fall within the sizes described above. However, the initial silica used as raw material may come as one or more agglomerates and/or aggregates and may have sizes around 200 μm or more.
In some preferred embodiments, the silica used to make the inventive separators has an increased amount of or number of surface silanol groups (surface hydroxyl groups) compared with silica fillers used previously to make lead acid battery separators. For example, the silica fillers that may be used with certain preferred embodiments herein may be those silica fillers having at least 10%, at least 15%, at least 20%, at least 25%, at least 30%, or at least 35% more silanol and/or hydroxyl surface groups compared with known silica fillers used to make known polyolefin lead acid battery separators. The ratio (Si—OH)/Si of silanol groups (Si—OH) to elemental silicon (Si) can be measured, for example, as follows.
1. Freeze-crush a polyolefin porous membrane (where certain inventive membranes contain a certain variety of oil-absorbing silica according to the present invention), and prepare the powder-like sample for the solid-state nuclear magnetic resonance spectroscopy (29Si-NMR).
2. Perform the 29Si-NMR to the powder-like sample, and observe the spectrums including the Si spectrum strength which is directly bonding to a hydroxyl group (Spectrum: Q2 and Q3) and the Si spectrum strength which is only directly bonding to an oxygen atom (Spectrum: Q4), wherein the molecular structure of each NMR peak spectrum can be delineated as follows:
Where Si* is proved element by NMR observation.
3. The conditions for 29Si-NMR used for observation are as follows:
4. Numerically, separate peaks of the spectrum, and calculate the area ratio of each peak belonging to Q2, Q3, and Q4. After that, based on the ratios, calculate the molar ratio of hydroxyl groups (—OH) bonding directly to Si. The conditions for the numerical peak separation is conducted in the following manner:
5. The peak area ratios (Total is 100) of Q2, Q3, and Q4 are calculated based on each peak obtained by fitting. The NMR peak area corresponded to the molecular number of each silicate bonding structure (thus, for the Q4 NMR peak, four Si—O—Si bonds are present within that silicate structure; for the Q3 NMR peak, three Si—O—Si bonds are present within that silicate structure while one Si—OH bond is present; and for the Q2 NMR peak, two Si—O—Si bonds are present within that silicate structure while two Si—OH bonds are present). Therefore, each number of the hydroxyl group (—OH) of Q2, Q3, and Q4 is multiplied by two (2) one (1), and zero (0), respectively. These three results are summed. The summed value displays the mole ratio of hydroxyl groups (—OH) directly bonding to Si.
In certain embodiments, the silica may have a molecular ratio of OH to Si groups, measured by 29Si-NMR, that may be within a range of approximately 21:100 to 35:100, in some preferred embodiments approximately 23:100 to approximately 31:100, in certain preferred embodiments, approximately 25:100 to approximately 29:100, and in other preferred embodiments at least approximately 27:100 or greater.
In some select embodiments, use of the fillers described above permits the use of a greater proportion of processing oil during the extrusion step. As the porous structure in the separator is formed, in part, by removal of the oil after the extrusion, higher initial absorbed amounts of oil results in higher porosity or higher void volume. While processing oil is an integral component of the extrusion step, oil is a non-conducting component of the separator. Residual oil in the separator protects the separator from oxidation when in contact with the positive electrode. The precise amount of oil in the processing step may be controlled in the manufacture of conventional separators. Generally speaking, conventional separators are manufactured using 50-70% processing oil, in some embodiments, 55-65%, in some embodiments, 60-65%, and in some embodiments, about 62% by weight processing oil. Reducing oil below about 59% is known to cause burning due to increased friction against the extruder components. However, increasing oil much above the prescribed amount may cause shrinking during the drying stage, leading to dimensional instability. Although previous attempts to increase oil content resulted in pore shrinkage or condensation during the oil removal, separators prepared as disclosed herein exhibit minimal, if any, shrinkage and condensation during oil removal. Thus, porosity can be increased without compromising pore size and dimensional stability, thereby decreasing electrical resistance.
In certain select embodiments, the use of the filler described above allows for a reduced final oil concentration in the finished separator. Since oil is a non-conductor, reducing oil content can increase the ionic conductivity of the separator and assist in lowering the ER of the separator. As such, separators having reduced final oil contents can have increased efficiency. In certain select embodiments are provided separators having a final processing oil content (by weight) less than 20%, for example, between about 14% and 20%, and in some particular embodiments, less than 19%, 18%, 17%, 16%, 15%, 14%, 13%, 12%, 11%, 10%, 9%, 8%, 7%, 6%, or 5%.
The fillers may further reduce what is called the hydration sphere of the electrolyte ions, enhancing their transport across the membrane, thereby once again lowering the overall electrical resistance or ER of the battery, such as an enhanced flooded battery or system.
The filler or fillers may contain various species (e.g., polar species, such as metals) that facilitate the flow of electrolyte and ions across the separator. Such also leads to decreased overall electrical resistance as such a separator is used in a flooded battery, such as an enhanced flooded battery.
Electrical Resistance
In certain selected embodiments, the disclosed separators exhibit decreased electrical resistance, for instance, an electrical resistance no greater than about 200 mΩ·cm2, 190 mΩ·cm2, 180 mΩ·cm2, 170 mΩ·cm2, or 160 mΩ·cm2.
To test a sample separator for ER testing evaluation in accordance with the present invention, it must first be prepared. To do so, a sample separator is preferably submerged in a bath of demineralized water, the water is then brought to a boil and the separator is then removed after 10 minutes in the boiling demineralized water bath. After removal, excess water is shaken off the separator and then placed in a bath of sulfuric acid having a specific gravity of 1.280 at 27° C.±1° C. The separator is soaked in the sulfuric acid bath for 20 minutes. The separator is then ready to be tested for electrical resistance.
Oxidation Stability
In certain select embodiments, exemplary separators may be characterized with an improved and higher oxidation resistance. Oxidation resistance is measured in elongation of sample separator specimens in the cross-machine direction after prolonged exposure to the lead acid battery electrolyte. For instance, exemplary separators may have an elongation at 40 hours of approximately 150% or higher, 200% or higher, 250% or higher, 300% or higher, 350% or higher, 400% or higher, 450% or higher, or 500% or higher. In certain embodiments, exemplary separators may have a preferred oxidation resistance or elongation at 40 hours of approximately 200% or higher.
To test samples for oxidation resistance, sample specimens 2100 of exemplary separators are first cut to a shape as generally set forth in
A first sample set is tested dry, at time=zero (0) hours, for elongation % to break. The elongation is based upon the 50 mm distance as measured from points A and B in
The elongation test is designed to simulate extended exposure to electrolyte in a cycling battery in a shortened time period. The samples 2100 are first fully submersed in isopropanol, drained and then submersed in water for 1 to 2 seconds. The samples are then submersed in an electrolyte solution. The solution is prepared by adding, in order, 360 ml of 1.28 specific gravity sulfuric acid, 35 ml of 1.84 specific gravity sulfuric acid, then 105 ml of 35% hydrogen peroxide. The solution is kept at 80° C. and the samples are submerged in the solution for an extended period. Samples may be tested for elongation at regular time intervals, such as 20 hours, 40 hours, 60 hours, 80 hours, etc. To test at these intervals, the samples 400 are remove from the 80° C. electrolyte bath and placed under luke-warm running water until the acid has been removed. The elongation can then be tested.
In accordance with at least select embodiments, the present disclosure or invention is directed to improved battery separators, Low ER or high conductance separators, improved lead acid batteries, such as flooded lead acid batteries, high conductance batteries, and/or, improved vehicles including such batteries, and/or methods of manufacture or use of such separators or batteries, and/or combinations thereof. In accordance with at least certain embodiments, the present disclosure or invention is directed to improved lead acid batteries incorporating the improved separators and which exhibit increased conductance.
Additives/Surfactants
In certain embodiments, exemplary separators may contain one or more performance enhancing additives added to the separator or porous membrane. The performance enhancing additive may be surfactants, wetting agents, colorants, antistatic additives, an antimony suppressing additive, UV-protection additives, antioxidants, and/or the like, and any combination thereof. In certain embodiments, the additive surfactants may be ionic, cationic, anionic, or non-ionic surfactants.
In certain embodiments described herein, a reduced amount of anionic or non-ionic surfactant is added to the inventive porous membrane or separator. Because of the lower amount of surfactant, a desirable feature may include lowered total organic carbons (“TOCs”) and/or lowered volatile organic compounds (“VOCs”).
Certain suitable surfactants are non-ionic while other suitable surfactants are anionic. The additive may be a single surfactant or a mixture of two or more surfactants, for instance two or more anionic surfactants, two or more non-ionic surfactants, or at least one ionic surfactant and at least one non-ionic surfactant. Certain suitable surfactants may have HLB values less than 6, preferably less than 3. The use of these certain suitable surfactants in conjunction with the inventive separators described herein can lead to even further improved separators that, when used in a lead acid battery, lead to reduced water loss, reduced antimony poisoning, improved cycling, reduced float current, reduced float potential, and/or the like, or any combination thereof for that lead acid batteries. Suitable surfactants include surfactants such as salts of alkyl sulfates; alkylarylsulfonate salts; alkylphenol-alkylene oxide addition products; soaps; alkyl-naphthalene-sulfonate salts; one or more sulfo-succinates, such as an anionic sulfo-succinate; dialkyl esters of sulfo-succinate salts; amino compounds (primary, secondary, tertiary amines, or quaternary amines); block copolymers of ethylene oxide and propylene oxide; various polyethylene oxides; and salts of mono and dialkyl phosphate esters. The additive can include a non-ionic surfactant such as polyol fatty acid esters, polyethoxylated esters, polyethoxylated alcohols, alkyl polysaccharides such as alkyl polyglycosides and blends thereof, amine ethoxylates, sorbitan fatty acid ester ethoxylates, organosilicone based surfactants, ethylene vinyl acetate terpolymers, ethoxylated alkyl aryl phosphate esters and sucrose esters of fatty acids.
In certain embodiments, the additive may be represented by a compound of Formula (I)
R(OR1)n(COOM1/xx+)m (I)
in which:
The ratio of oxygen atoms to carbon atoms in the compound according to Formula (I) being in the range from 1:1.5 to 1:30 and m and n not being able to simultaneously be 0. However, preferably only one of the variables n and m is different from 0.
By non-aromatic hydrocarbon radicals is meant radicals which contain no aromatic groups or which themselves represent one. The hydrocarbon radicals may be interrupted by oxygen atoms (i.e., contain one or more ether groups).
R is preferably a straight-chain or branched aliphatic hydrocarbon radical which may be interrupted by oxygen atoms. Saturated, uncross-linked hydrocarbon radicals are quite particularly preferred. However, as noted above, R may, in certain embodiments, be aromatic ring-containing.
Through the use of the compounds of Formula (I) for the production of battery separators, they may be effectively protected against oxidative destruction. Battery separators are preferred which contain a compound according to Formula (I) in which:
Formula R2—[(OC2H4)p(OC3H6)q]— is to be understood as also including those compounds in which the sequence of the groups in square brackets differs from that shown. For example according to the invention compounds are suitable in which the radical in brackets is formed by alternating (OC2H4) and (OC3H6) groups.
Additives in which R2 is a straight-chain or branched alkyl radical with 10 to 20, preferably 14 to 18 carbon atoms have proved to be particularly advantageous. OC2H4 preferably stands for OCH2CH2, OC3H6 for OCH(CH3)2 and/or OCH2CH2CH3.
As preferred additives there may be mentioned in particular alcohols (p=q=0; m=0) primary alcohols being particularly preferred, fatty alcohol ethoxylates (p=1 to 4, q=0), fatty alcohol propoxylates (p=0; q=1 to 4) and fatty alcohol alkoxylates (p=1 to 2; q=1 to 4) ethoxylates of primary alcohols being preferred. The fatty alcohol alkoxylates are for example accessible through reaction of the corresponding alcohols with ethylene oxide or propylene oxide.
Additives of the type m=0 which are not, or only difficulty, soluble in water and sulphuric acid have proved to be particularly advantageous. However, additives that are partially soluble or fully soluble in water, an aqueous solution, or sulfuric acid may also be used. Also preferred are additives which contain a compound according to Formula (I), in which:
Salt Additives
In certain embodiments, suitable additives may include, in particular, polyacrylic acids, polymethacrylic acids and acrylic acid-methacrylic acid copolymers, whose acid groups are at least partly neutralized, such as by preferably 40%, and particularly preferably by 80%. The percentage refers to the number of acid groups. Quite particularly preferred are poly(meth)acrylic acids which are present entirely in the salt form. Suitable salts include Li, Na, K, Rb, Be, Mg, Ca, Sr, Zn, and ammonium (NR4, wherein R is either hydrogen or a carbon functional group). Poly(meth)acrylic acids may include polyacrylic acids, polymethacrylic acids, and acrylic acid-methacrylic acid copolymers. Poly(meth)acrylic acids are preferred and in particular polyacrylic acids with an average molar mass Mw of 1,000 to 100,000 g/mol, particularly preferably 1,000 to 15,000 g/mol and quite particularly preferably 1,000 to 4,000 g/mol. The molecular weight of the poly(meth)acrylic acid polymers and copolymers is ascertained by measuring the viscosity of a 1% aqueous solution, neutralized with sodium hydroxide solution, of the polymer (Fikentscher's constant).
Also suitable are copolymers of (meth)acrylic acid, in particular copolymers which, besides (meth)acrylic acid contain ethylene, maleic acid, methyl acrylate, ethyl acrylate, butyl acrylate and/or ethylhexyl acrylate as comonomer. Copolymers are preferred which contain at least 40% by weight and preferably at least 80% by weight (meth)acrylic acid monomer; the percentages being based on the acid form of the monomers or polymers.
To neutralize the polyacrylic acid polymers and copolymers, alkali metal and alkaline-earth metal hydroxides such as potassium hydroxide and in particular sodium hydroxide are particularly suitable. In addition, a coating and/or additive to enhance the separator may include, for example, a metal alkoxide, wherein the metal may be, by way of example only (not intended to be limiting), Zn, Na, or Al, by way of example only, sodium ethoxide.
In some embodiments, the porous polyolefin porous membrane may include a coating on one or both sides of such layer. Such a coating may include a surfactant or other material. In some embodiments, the coating may include one or more materials described, for example, in U.S. Pat. No. 9,876,209, which is incorporated by reference herein. Such a coating may, for example, reduce the overcharge voltage of the battery system, thereby extending battery life with less grid corrosion and preventing dry out and/or water loss.
Ratios
In certain select embodiments, the membrane may be prepared by combining, by weight, about 5-15% polymer, in some instances, about 10% polymer (e.g., polyethylene), about 10-75% filler (e.g., silica), in some instances, about 30% filler, and about 10-85% processing oil, in some instances, about 60% processing oil. In other embodiments, the filler content is reduced, and the oil content is higher, for instance, greater than about 61%, 62%, 63%, 64%, 65%, 66%, 67%, 68%, 69% or 70% by weight. The filler:polymer ratio (by weight) may be about (or may be between about these specific ranges) such as 2:1, 2.5:1, 3:1, 3.5:1, 4.0:1. 4.5:1, 5.0:1, 5.5:1 or 6:1. The filler:polymer ratio (by weight) may be from about 1.5:1 to about 6:1, in some instances, 2:1 to 6:1, from about 2:1 to 5:1, from about 2:1 to 4:1, and in some instances, from about 2:1 to about 3:1. The amounts of the filler, the oil, and polymer are all balanced for runnability and desirable separator properties, such as electrical resistance, basis weight, puncture resistance, bending stiffness, oxidation resistance, porosity, physical strength, tortuosity, and the like.
In accordance with at least one embodiment, the porous membrane can include an UHMWPE mixed with a processing oil and precipitated silica. In accordance with at least one embodiment, the porous membrane can include an UHMWPE mixed with a processing oil, additive and precipitated silica. The mixture may also include minor amounts of other additives or agents as is common in the separator arts (e.g., surfactants, wetting agents, colorants, antistatic additives, antioxidants, and/or the like, and any combination thereof). In certain instances, the porous polymer layer may be a homogeneous mixture of 8 to 100% by volume of polyolefin, 0 to 40% by volume of a plasticizer and 0 to 92% by volume of inert filler material. The preferred plasticizer is petroleum oil. Since the plasticizer is the component which is easiest to remove, by solvent extraction and drying, from the polymer-filler-plasticizer composition, it is useful in imparting porosity to the battery separator.
In certain embodiments, the porous membrane disclosed herein may contain latex and/or rubber, which may be a natural rubber, synthetic rubber, or a mixture thereof. Natural rubbers may include one or more blends of polyisoprenes, which are commercially available from a variety of suppliers. Exemplary synthetic rubbers include methyl rubber, polybutadiene, chloropene rubbers, butyl rubber, bromobutyl rubber, polyurethane rubber, epichlorhydrin rubber, polysulphide rubber, chlorosulphonyl polyethylene, polynorbornene rubber, acrylate rubber, fluorine rubber and silicone rubber and copolymer rubbers, such as styrene/butadiene rubbers, acrylonitrile/butadiene rubbers, ethylene/propylene rubbers (EPM and EPDM) and ethylene/vinyl acetate rubbers. The rubber may be a cross-linked rubber or an uncross-linked rubber; in certain preferred embodiments, the rubber is uncross-linked rubber. In certain embodiments, the rubber may be a blend of cross-linked and uncross-linked rubber. The rubber may be present in the separator in an amount that is at least about 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, or 10% by weight relative to the final separator weight (the weight of the polyolefin separator sheet or layer containing rubber and/or latex). In certain embodiments, the rubber may be present in an amount from approximately 1-6%, approximately 3-6% by weight, approximately 3% by weight, and approximately 6% by weight. The porous membrane may have a filler to polymer and rubber (filler:polymer and rubber) weight ratio of approximately 2.6:1.0. The amounts of the rubber, filler, oil, and polymer are all balanced for runnability and desirable separator properties, such as electrical resistance, basis weight, puncture resistance, bending stiffness, oxidation resistance, porosity, physical strength, tortuosity, and the like. A porous membrane made in accordance with the present invention, comprising polyethylene and filler (e.g., silica) typically has a residual oil content; in some embodiments, such residual oil content is from about 0.5% up to about 40% of the total weight of the separator membrane (in some instances, about 10-40% of the total weight of the separator membrane, and in some instances, about 20-40% of that total weight). In certain select embodiments herein, some to all of the residual oil content in the separator may be replaced by the addition of more of a performance enhancing additive, such as a surfactant, such as a surfactant with a hydrophilic-lipophilic balance (“HLB”) less than 6, or such as a nonionic surfactant. For example, a performance enhancing additive such as a surfactant, such as a nonionic surfactant, may comprise up to 0.5% all the way up to all of the amount of the residual oil content (e.g., all the way up to 20% or 30% or even 40%) of the total weight of the porous separator membrane, thereby partially or completely replacing the residual oil in the separator membrane.
Manufacture
In some embodiments, an exemplary porous membrane may be made by mixing the constituent parts in an extruder. In one non-limiting example, about 30% by weight filler is mixed with about 10% by weight UHMWPE to form a dry blend. This dry blend is then mixed with approximately 60% processing oil may be mixed in an extruder. The exemplary porous membrane may be made by passing the constituent parts through a heated extruder, passing the extrudate generated by the extruder through a die and into a nip formed by two heated presses or a calender stack or rolls to form a continuous web. A substantial amount of the processing oil from the web may be extracted by use of a solvent, thereby followed with removing the solvent by drying. The web may then be cut into lanes of predetermined width, and then wound onto rolls. Additionally, the presses or calender rolls may be engraved with various groove patterns to impart ribs, grooves, textured areas, embossments, and/or the like as substantially described herein. The amounts of the constituent parts are all balanced for runnability and desirable separator properties, such as puncture resistance, backweb thickness, electrical resistance, basis weight, bending stiffness, oxidation resistance, porosity, physical strength, tortuosity, and the like.
In addition, other exemplary embodiments may add various other additives such as natural or synthetic rubbers, performance enhancing additives or agents (e.g., surfactants, wetting agents, colorants, antistatic additives, antioxidants, and/or the like, and any combination thereof) into the constituent parts before forming the extrudate. Alternatively, these additional additives may be applied to the extrudate before or after the processing oil has been extracted, or before or after it has been slit into lanes. Such methods may include forming a slurry to add by dip coat, roller coat, spray coat, or curtain coat one or more surfaces of the separator, or any combination thereof. Furthermore, the additives may be deposited onto the membrane by impregnation and drying.
In certain embodiments, the performance enhancing additive(s) (e.g., a non-ionic surfactant, an anionic surfactant, or mixtures thereof) may be present at a density or add-on level of at least 0.5 g/m2, 1.0 g/m2, 1.5 g/m2, 2.0 g/m2, 2.5 g/m2, 3.0 g/m2, 3.5 g/m2, 4.0 g/m2, 4.5 g/m2, 5.0 g/m2, 5.5 g/m2, 6.0 g/m2, 6.5 g/m2, 7.0 g/m2, 7.5 g/m2, 8.0 g/m2, 8.5 g/m2, 9.0 g/m2, 9.5 g/m2 or 10.0 g/m2 or even up to about 25.0 g/m2. The additive may be present on the separator at a density or add-on level between 0.5-15 g/m2, 0.5-10 g/m2, 1.0-10.0 g/m2, 1.5-10.0 g/m2, 2.0-10.0 g/m2, 2.5-10.0 g/m2, 3.0-10.0 g/m2, 3.5-10.0 g/m2, 4.0-10.0 g/m2, 4.5-10.0 g/m2, 5.0-10.0 g/m2, 5.5-10.0 g/m2, 6.0-10.0 g/m2, 6.5-10.0 g/m2, 7.0-10.0 g/m2, 7.5-10.0 g/m2, 4.5-7.5 g/m2, 5.0-10.5 g/m2, 5.0-11.0 g/m2, 5.0-12.0 g/m2, 5.0-15.0 g/m2, 5.0-16.0 g/m2, 5.0-17.0 g/m2, 5.0-18.0 g/m2, 5.0-19.0 g/m2, 5.0-20.0 g/m2, 5.0-21.0 g/m2, 5.0-22.0 g/m2, 5.0-23.0 g/m2, 5.0-24.0 g/m2, or 5.0-25.0 g/m2.
Combined with a Fibrous Mat
In certain embodiments, exemplary separators according to the present disclosure may be combined with another layer (laminated or otherwise), such as a fibrous layer or fibrous mat having enhanced wicking properties and/or enhanced wetting or holding of electrolyte properties. The fibrous mat may be woven, nonwoven, fleeces, mesh, net, single layered, multi-layered (where each layer may have the same, similar or different characteristics than the other layers), composed of glass fibers, or synthetic fibers, fleeces or fabrics made from synthetic fibers or mixtures with glass and synthetic fibers or paper, or any combination thereof.
In certain embodiments, the fibrous mat (laminated or otherwise) may be used as a carrier for additional materials. The addition material may include, for example, rubber and/or latex, optionally silica, water, and/or one or more performance enhancing additive, such as various additives described herein, or any combination thereof. By way of example, the additional material may be delivered in the form of a slurry that may then be coated onto one or more surfaces of the fibrous mat to form a film, or soaked and impregnated into the fibrous mat.
When the fibrous layer is present, it is preferred that the porous membrane has a larger surface area than the fibrous layers. Thus, when combining the porous membrane and the fibrous layers, the fibrous layers do not completely cover the porous layer. It is preferred that at least two opposing edge regions of the membrane layer remain uncovered to provide edges for heat sealing which facilitates the optional formation of pockets or envelopes and/or the like. Such a fibrous mat may have a thickness that is at least 100 μm, in some embodiments, at least about 200 μm, at least about 250 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 2 mm, and so forth. The subsequent laminated separator may be cut into pieces. In certain embodiments, the fibrous mat is laminated to a ribbed surface of the porous membrane porous membrane. In certain embodiments, handling and/or assembly advantages are provided to the battery maker with the improved separator described herein, as it may be supplied in roll form and/or cut piece form. And as mentioned previously, the improved separator may be a standalone separator sheet or layer without the addition of one or more fibrous mats or the like.
If the fibrous mat is laminated to the porous membrane, they may be bonded together by adhesive, heat, ultrasonic welding, compression, and/or the like, or any combination thereof. And, the fibrous mat may be a PAM or NAM retention mat.
Various battery separators were made according to the embodiments of the present invention.
In Example 1, a separator was made having a physical profile in accordance with what is shown in
In Example 2, several batteries constructed and were tested to determine how well a sleeve type separator with a rib profile according to
For the experimental batteries, the separator used was a coated polyethylene separator having a backweb thickness of about 400 μm, an overall thickness of about 1.6 mm, and a serrated profile according to
Referring now to
Referring now to
Float current data was also obtained for the batteries and is presented in
Similar to
Additional testing of the batteries was performed to determine the discharge duration of the batteries as a function of the number of cycles (see
The batteries in these Examples were also looked at from the perspective of specific gravity of the electrolyte. As a battery is cycled, the sulfuric acid in the electrolyte of the battery system can become stratified into layers of varying concentration. It can be important to minimize such acid stratification and to keep the specific gravity of the electrolyte consistent, which may lead to extended battery life.
The batteries formed for these Examples were also tested for end charge current. The data for such testing is shown in
Finally, the batteries formed for these Examples were also tested to determine charging current versus duration at various cycles. Essentially, this testing helped to determine how quickly the various batteries could be recharged. The results depicted in
The instant disclosure or invention is directed to new, improved or optimized battery separators, Z wrap separators, Z wrap serrated rib separators, Z wrap serrated rib separators for tubular batteries, components, cells, modules, systems, batteries, tubular batteries, industrial batteries, inverter batteries, batteries for heavy or light industrial applications, forklift batteries, float charged batteries, inverters, accumulators, methods, profiles, additives, compositions, composites, mixes, coatings, and/or related methods of Z wrapping separators, Z wrapping separators on electrodes of tubular batteries, water retention, water loss prevention, improved charge acceptance, production, use, and/or related Z wrapping equipment, and/or combinations thereof. More particularly, the present invention is directed to one or more improved battery separators having various improvements that may result in automated separator Z wrapping, automated Z wrapped cell module production, automated tubular battery production, decreased water loss for a battery in which such a separator is incorporated, enhanced charge acceptance, or combinations thereof. Additionally, the present invention relates to one or more improved battery separators having various improvements with regard to shape, and/or physical profile, and/or chemical(s), additives, mixes, coatings, and/or the like used to make such battery separators (such as oil(s), and/or chemical additive(s) or agents used to coat, finish or improve such battery separators (such as surfactant(s))). Furthermore, the present invention relates to one or more improved separator configurations, Z wrap cell modules, Z wrap tubular electrodes, z wrap gauntlet covered tubular electrodes, and/or battery electrode and separator assembly configurations providing for automation, better acid mixing and/or reduced acid stratification over prior sleeves, pockets, or envelope separator configurations. One or more improved battery electrode and separator assembly configurations and/or manufacturing methods and/or manufacturing equipment. The improved Z wrap battery separators of the instant invention are particularly useful in or with tubular batteries, industrial batteries, such as inverter batteries, batteries for heavy or light industry, and so forth.
In accordance with certain embodiments, aspects or objects, new, improved or optimized battery separators, components, batteries, industrial batteries, inverter batteries, batteries for heavy or light industrial applications, forklift batteries, float charged batteries, tubular batteries, inverters, accumulators, systems, methods, profiles, additives, compositions, composites, mixes, coatings, and/or related methods of water retention, water loss prevention, improved charge acceptance, production, use, and/or combinations thereof may be or are provided or disclosed. More particularly, the present invention is directed to one or more improved battery separators having various improvements that may result in decreased water loss for a battery in which such a separator is incorporated, enhanced charge acceptance, or combinations thereof. Additionally, the present invention relates to one or more improved battery separators having various improvements with regard to shape, and/or physical profile, and/or chemical(s), additives, mixes, coatings, and/or the like used to make such battery separators (such as oil(s), and/or chemical additive(s) or agents used to coat, finish or improve such battery separators (such as surfactant(s))). Furthermore, inventive separator and electrode assemblies are provided with a z-shaped separator wrap about and between the electrodes. The improved battery separators of the instant invention are particularly useful in or with industrial batteries, such as inverter batteries, tubular batteries for heavy or light duty industrial applications, and so forth.
The compositions and methods of the appended claims are not limited in scope by the specific compositions and methods described herein, which are intended as illustrations of a few aspects of the claims and any compositions and methods that are functionally equivalent are intended to fall within the scope of the claims. Various modifications of the compositions and methods in addition to those shown and described herein are intended to fall within the scope of the appended claims. Further, while only certain representative compositions and method steps disclosed herein are specifically described, other combinations of the compositions and method steps also are intended to fall within the scope of the appended claims, even if not specifically recited. Thus, a combination of steps, elements, components, or constituents may be explicitly mentioned herein or less, however, other combinations of steps, elements, components, and constituents are included, even though not explicitly stated. The term “comprising” and variations thereof as used herein is used synonymously with the term “including” and variations thereof and are open, non-limiting terms. Although the terms “comprising” and “including” have been used herein to describe various embodiments, the terms “consisting essentially of” and “consisting of” may be used in place of “comprising” and “including” to provide for more specific embodiments of the invention and are also disclosed. Other than in the examples, or where otherwise noted, all numbers expressing quantities of ingredients, reaction conditions, and so forth used in the specification and claims are to be understood at the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, to be construed in light of the number of significant digits and ordinary rounding approaches. The present invention may be embodied in other forms without departing from the spirit and the essential attributes thereof, and, accordingly, reference should be made to the appended claims, rather than to the foregoing specification, as indicating the scope of the invention. Disclosed are components that may be used to perform the disclosed methods and systems. These and other components are disclosed herein, and it is understood that when combinations, subsets, interactions, groups, etc. of these components are disclosed that while specific reference of each various individual and collective combinations and permutation of these may not be explicitly disclosed, each is specifically contemplated and described herein, for all methods and systems. This applies to all aspects of this application including, but not limited to, steps in disclosed methods. Thus, if there are a variety of additional steps that may be performed it is understood that each of these additional steps may be performed with any specific embodiment or combination of embodiments of the disclosed methods.
The foregoing written description of structures and methods has been presented for purposes of illustration only. Examples are used to disclose exemplary embodiments, including the best mode, and also to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. These examples are not intended to be exhaustive or to limit the invention to the precise steps and/or forms disclosed, and many modifications and variations are possible in light of the above teaching. Features described herein may be combined in any combination. Steps of a method described herein may be performed in any sequence that is physically possible. The patentable scope of the invention is defined by the appended claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal language of the claims.
The compositions and methods of the appended claims are not limited in scope by the specific compositions and methods described herein, which are intended as illustrations of a few aspects of the claims. Any compositions and methods that are functionally equivalent are intended to fall within the scope of the claims. Various modifications of the compositions and methods in addition to those shown and described herein are intended to fall within the scope of the appended claims. Further, while only certain representative compositions and method steps disclosed herein are specifically described, other combinations of the compositions and method steps also are intended to fall within the scope of the appended claims, even if not specifically recited. Thus, a combination of steps, elements, components, or constituents may be explicitly mentioned herein or less, however, other combinations of steps, elements, components, and constituents are included, even though not explicitly stated.
As used in the specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. Ranges may be expressed herein as from “about” or “approximately” one particular value, and/or to “about” or “approximately” another particular value. When such a range is expressed, another embodiment includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another embodiment. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint. “Optional” or “optionally” means that the subsequently described event or circumstance may or may not occur, and that the description includes instances where said event or circumstance occurs and instances where it does not.
Throughout the description and claims of this specification, the word “comprise” and variations of the word, such as “comprising” and “comprises,” means “including but not limited to,” and is not intended to exclude, for example, other additives, components, integers, or steps. The terms “consisting essentially of” and “consisting of” may be used in place of “comprising” and “including” to provide for more specific embodiments of the invention and are also disclosed. “Exemplary” or “for example” means “an example of” and is not intended to convey an indication of a preferred or ideal embodiment. Similarly, “such as” is not used in a restrictive sense, but for explanatory or exemplary purposes.
Other than where noted, all numbers expressing geometries, dimensions, and so forth used in the specification and claims are to be understood at the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, to be construed in light of the number of significant digits and ordinary rounding approaches.
Unless defined otherwise, all technical and scientific terms used herein have the same meanings as commonly understood by one of skill in the art to which the disclosed invention belongs. Publications cited herein and the materials for which they are cited are specifically incorporated by reference.
Additionally, the invention illustratively disclosed herein suitably may be practiced in the absence of any element which is not specifically disclosed herein.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201911001882 | Jan 2019 | IN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2020/013785 | 1/16/2020 | WO | 00 |