The present invention concerns improvements in and relating to melting metals using electromagnetic movers and/or electromagnetic moving, such as stirring, of molten metals, particularly apparatus for stirring and methods of stirring.
It is known to use electromagnets to generate moving magnetic fields within molten metal and as a consequence generate motion within the molten metal. The movement causes stirring of the molten metal within its container, with beneficial effects on heat transfer, material dispersion and the like.
There is often a need, for instance when recycling aluminium, to be able to draw non-melted metal down into a body of molten metal to provide melting. Various approaches have been taken to trying to achieve this melting and stirring aim. Electromagnetic movers have been used to try and create suitable flow patterns in the molten metal for such purposes, but the resulting flow patterns are less than optimal.
The present invention has amongst its potential aims to provide apparatus for stirring and methods of stirring which generate better flow patterns for drawing non-melted metal into molten metal and/or for mixing non-molten metal with molten metal. The present invention has amongst its potential aims to provide apparatus for stirring and methods of stirring which provide optimised molten metal flow out of and into a side chamber to a furnace or other container for molten metal. The present invention has amongst its potential aims to provide apparatus for stirring and methods of stirring which avoid conflicts in the flow of molten metal to a location relative to the flow of molten metal from the location.
According to a first aspect of the invention there is provided apparatus for moving molten metal, the apparatus comprising:
According to a second aspect of the invention there is provided apparatus for moving molten metal, the apparatus comprising:
According to a third aspect of the invention there is provided a method of moving molten material within a container, the method comprising:
According to a fourth aspect of the invention there is provided a method of moving molten material within a container, the method comprising:
The third and fourth aspects of the invention may further provide that the apparatus further comprises a mounting location for the electromagnetic mover and a support for the mounting location.
The first, second, third and fourth aspects of the invention may include any of the following features, options and possibilities.
The electromagnetic mover may be a linear motor. The electromagnetic mover may include a core and one or more teeth. The electromagnetic mover may include one or more teeth with an electrical conductor wrapped around. The electromagnetic mover may be provided within a casing. The casing may be a rectangular box.
The mounting location may be provided with fasteners for mounting the electromagnetic mover. The mounting location may provide a fixed position mounting for the electromagnetic mover. The mounting location may allow for rotational movement of the electromagnetic mover, for instance to vary the inclination of the electromagnetic mover in the second plane relative to the vertical. The mounting location may allow for movement of the electromagnetic mover to vary the extent to which the electromagnetic mover is reclined, for instance in the first plane relative to the vertical. The mounting location may be rotationally mounted on the support. The mounting location may be pivotally mounted on the support. The mounting location may comprise a framework, for instance a rectangular framework.
The support for the mounting location may be moveable, for instance using wheels. The support may provide a framework upon which the mounting location is provided. The support may allow the mounting location to have a variable inclination, for instance through being able to rotate. The support may allow the mounting location to have a variable extent of recline, for instance through being pivotally moveable. The support may comprise a framework, for instance a base frame and one or more uprights extending therefrom upon which the mounting location is provided.
The container may be a feed route for non-molten metal to the container or a larger container connected to the container. The container may be a well. The container may be an exit route for molten metal from the container or a larger container to a third container. The container may be provided on the side of the larger container. The container may be fluidly connected to the larger container.
The container may be defined by a first side wall, a second side wall, a base wall, a back wall and a front wall. The back wall may be part of the larger container. The aperture may be provided in the back wall. The back wall may be vertical+/−10°. The side walls may be vertical+/−20°. The first side wall and second side wall may taper towards one another away from the back wall. The first side wall and/or second side wall may be planar. The base wall may be horizontal+/−10°. The base wall may be planar. The front wall may be angled at 30°, −10°, +20° to the vertical. The front wall may be planar. The front wall may lean outward away from the back wall further at the top of the front wall than at the bottom.
The larger container may be a furnace or molten metal holding chamber. The larger container may have at least 10× the volume of the container, more preferably at least 20× and ideally at least 50×.
The third container may be a discrete container, such as a ladle, or may be a transfer route to another location, such as a launder.
The container may be mounted on a side wall of the larger container. The larger container may be rectilinear in plan and the container may be mounted on a long wall of the larger container and most preferably in a mid-section. The mid-section may be the section which includes the mid-point of the side and 20% of the length either side thereof.
The container may be fluidly connected to the larger container by only a single aperture. The single aperture may provide an entrance area for molten metal entering the container from the larger container. The single aperture may provide an exit area for molten metal exiting the container to the larger container. The entrance area and the exit area may be separated from one another in use by a zone of low velocity molten metal. The velocity may be low compared with the velocity into the container via the entrance area and/or compared with the velocity out of the container via the exit area, for instance a velocity less than 20% thereof, more preferably less than 10% thereof.
The operative location for the electromagnetic mover may be adjacent the front wall of the container. Adjacent may refer to an average, more preferably maximum, airgap between the electromagnetic mover and the front wall of less than 10 cm, more preferably less than 5 cm and ideally less than 3 cm.
The angle of overhang for the front wall of the container may match the recline of the electromagnetic mover+/−5°, more preferably +/−1° and ideally+/−0.3°. The top part of the front face of the container may overhang a part of the electromagnetic mover, particularly the middle and/or bottom thereof. The front wall of the container and the electromagnetic mover, particularly the face thereof opposing the front wall of the container, may be parallel to one another.
The electromagnetic mover may have a primary motion axis, the primary motion axis being aligned along the direction of the maximum linear force generated by the electromagnetic stirrer. The primary motion axis corresponds to the primary axis along which molten metal moves. The primary motion axis is preferably parallel to the longitudinal axis of the electromagnetic mover.
The electromagnetic mover may have a longitudinal axis. The longitudinal axis may comprise the centreline for the body electromagnetic mover. The longitudinal axis may comprise the centreline of the face of the electromagnetic mover opposing the front wall of the container.
The primary motion axis may be inclined relative to the vertical in a first plane due to the electromagnetic mover being reclined away from the container and/or larger container. The electromagnetic mover may be reclined such that the upper part of the electromagnetic mover is further from the larger container than the lower part of the electromagnetic mover. The primary motion axis may be inclined relative to the vertical in a first plane by between 20° and 65°, preferably between 25° and 45°, for instance 30°+/−5°.
The primary motion axis may be inclined relative to the vertical in a second plane due to the electromagnetic mover being rotated from the vertical. The electromagnetic mover may be inclined such that the upper part of the electromagnetic mover is to the left side or right side of the front wall of the container and the lower part of the electromagnetic mover is to the other of the right side or the left side of the front wall of the container. The primary motion axis may be inclined relative to the vertical in a second plane by between 3° and 50°, preferably between 5° and 35°, more preferably between 5° and 15° and ideally between 6° and 12°, for instance 8°+/−1°.
The longitudinal axis may be inclined relative to the vertical in a first plane due to the electromagnetic mover being reclined away from the container and/or larger container. The electromagnetic mover may be reclined such that the upper part of the electromagnetic mover is further from the larger container than the lower part of the electromagnetic mover. The longitudinal axis may be inclined relative to the vertical in a first plane by between 20° and 65°, preferably between 25° and 45°, for instance 30°+/−5°.
The longitudinal axis may be inclined relative to the vertical in a second plane due to the electromagnetic mover being rotated from the vertical. The electromagnetic mover may be inclined such that the upper part of the electromagnetic mover is to the left side or right side of the front wall of the container and the lower part of the electromagnetic mover is to the other of the right side or the left side of the front wall of the container. The longitudinal axis may be inclined relative to the vertical in a second plane by between 3° and 50°, preferably between 5° and 35°, more preferably between 5° and 15° and ideally between 6° and 12°, for instance 8°+/−1°.
Preferably the linear force is directed upward along the primary motion axis. Preferably the linear force is directed upward along the longitudinal axis. The direction of the linear force is preferably determined by the control system for the electromagnetic mover.
The linear force may be applied in a single direction. The linear force may be applied in a single direction for one or more first time periods. The linear force may be absent for one or more second time periods. The linear force may be applied in a second direction, such as downward, for one or more third time periods. The first, second and third time periods may be combined in various sequences. The reverse direction for the linear force may be applied periodically.
The method may include generating a plurality of different flow zones within the container and/or larger container. The different flow zones may differ from one another in terms of their position in the container and/or larger container. The different flow zones may differ from one another in terms of the relative flow velocities. The different flow zones may differ from one another in terms of the relative directions of flow.
A first flow zone may be generated in a middle and/or upper part of the container. The first flow zone may feed molten metal to a second flow zone. The first flow zone may include intermediate and/or low flow velocities. The first flow zone may include flows away from the larger container and/or across the container, particularly diagonally across the container. The first flow zone may include horizontal and/or moderate rising flows. The first flow zone may include flow towards the junction of the angled front wall of the container and a side wall of the container. The first flow zone may be fed non-molten metal to be melted. The first zone may be Zone A of the illustrations.
A second flow zone may be generated in the middle and/or upper part of the container. The second flow zone may receive molten metal from the first flow zone and/or a sixth zone. The second flow zone may feed molten metal to a third flow zone. The second flow zone may include high and/or very high flow velocities. The second flow zone may include flow away from the larger container which then turns to flow towards the larger container. The second flow zone may include flow across the container, potentially in a moderate rising flow. The second flow zone may then provide flow down and along the side wall of the container, preferably with a strong downward flow. The second flow zone may include a moderate rising flow flowed by a strong downward flow. The second flow zone may include flow down the junction of the angled front wall of the container and side wall of the container and/or down the angled front wall of the container and/or along the side wall of the container. The second flow zone may be to one side only of the container. The second flow zone is preferably absent from the other side of the container and/or from the middle of the container. The second flow zone may submerge the non-molten metal. The second flow zone may be Zone B of the illustrations.
A third flow zone may be provided in the middle and/or lower part of the container and/or lower part of the larger container. The third flow zone may receive molten metal from the second flow zone. The third flow zone may feed molten metal to the fourth flow zone. The third flow zone may include high and/or very high flow velocities. The third flow zone may include flow toward the larger container and/or into the larger container. The third flow zone may provide flow down and along the side wall of the container and/or along the base of the container and/or along the base of the furnace. The third flow zone may be to one side only of the container. The third flow zone is preferably absent from the other side of the container and/or from the middle of the container. The third flow zone may further submerge and/or melt the non-molten metal feed to the container. The third flow zone may be Zone C of the illustrations.
A fourth flow zone may be provided in the lower part of the larger container. The fourth flow zone may receive molten metal from the third flow zone. The fourth flow zone may feed molten metal to a fifth flow zone and/or a sixth flow zone. The fourth flow zone may include high flow velocities. The fourth flow zone may include flow away from the container across the larger container. The fourth flow zone may provide flow across the base of the larger container and/or across the middle level part of the larger container. The fourth zone may be provided only to one side of the middle of the larger container. The fourth flow zone may be absent from either ends of the larger container. The fourth flow zone may provide further melting of the non-melted metal feed to the container. The fourth flow zone may be Zone D of the illustrations.
A fifth flow zone may be provided in the lower part and/or middle part of the larger container. The fifth flow zone may receive molten metal from the fourth flow zone. The fifth flow zone may feed molten metal to a sixth flow zone. The fifth flow zone may include low and/or very low flow velocities. The fifth flow zone may include flow from the larger container towards and/or into the container. The fifth flow zone may provide flow across the base of the larger container and/or across the middle level of the container. The fifth zone may be provided in the part of the larger container facing one side of the container and/or facing the middle of the container. The fifth flow zone may be absent for the part of the larger container facing the other side of the container, particularly the part of the container with the third flow zone. The fifth flow zone may provide molten metal to the container. The fifth flow zone may be Zone E in the illustrations.
A sixth flow zone may be provided in the lower and/or middle part of the container. The sixth flow zone may receive molten metal from the fifth flow zone. The sixth flow zone may feed molten metal to the first flow zone and/or second flow zone. The sixth flow zone may include low and/or moderate flow velocities. The sixth flow zone may include from close to the larger container further into the container. The sixth flow zone may include flow across the base of the container and/or through the middle depth of the container. The sixth zone may be provided in one side of the container and/or in the middle of the container. The sixth flow zone may be absent from the other side of the container, particularly the part of the container with the third flow zone. The sixth flow zone may provide molten metal to the angled end wall of the container. The sixth flow zone may be Zone F in the illustrations.
The inclination of the electromagnetic mover, relative to the vertical in the first plane, may be varied with time. The inclination of the electromagnetic mover, relative to the vertical in the second plane, may be varied with time. Preferably no variation with respect to the vertical in the first plane occurs with time, but variation to the vertical in the second plane does occur. The variation in the inclination with time may arise as a result of feedback from one or more sensors. The variation in the inclination with time may arise as a result of the volume and/or level of molten metal within the container and/or larger container. The inclination may be greater when the volume and/or level of molten material is lower. The inclination may be less when the volume and/or level of molten metal is higher. The variation in the inclination with time may arise as a result of whether or not non-molten material is being fed to the container. The inclination may be greater when non-molten metal is not being added to the container. The inclination may be less when non-molten metal is being added to the container.
The electromagnetic mover may be moveable to a further location. The electromagnetic mover may be moveable by movement of the mounting location and/or the support for the mounting location. The further location may be proximate to the same larger container. The further location may be a location for the removal of molten metal from the larger container and/or from a further container connected to the larger container.
The further location may include an inclined wall. The inclined wall may be a part of the larger container or may be connected to the larger container. The inclined wall may be part of a further container for molten metal, with the molten metal being in fluid communication with the molten metal of the larger container.
The electromagnetic mover may be provided adjacent to the inclined wall. The electromagnetic mover may force molten metal up the inclined wall. The molten metal may be forced up and over the end of the inclined wall. The molten metal may be forced out of the further container and into a receptacle such as a ladle, yet further container or launder. The molten metal may flow away from the location.
The inclined wall may be inclined at more than 40° to the vertical, preferably more than 45°, still more preferably more than 50° and potentially more than 60°. The electromagnetic mover may have a matching inclination. The electromagnetic mover may be inclined only in one plane relative to the vertical. The longitudinal axis of the electromagnetic mover may be aligned with the longitudinal axis of the inclined wall. The primary motion axis of the electromagnetic mover may be aligned with the longitudinal axis of the inclined wall.
The inclined wall may include a metal plate. The metal plate may extend above the resting level of molten metal in the larger container or further container. The metal plate may extend at least 50 mm, preferably 80 mm and ideally at least 100 mm above the resting level.
The first, second and third aspects of the invention may include any of the following features, options and possibilities, together with those set out in the specific description and elsewhere within the application.
The method of stirring may be a method of stirring molten metal. The method of stirring may be a method of stirring aluminium.
The non-molten metal may be aluminium, for instance chips of aluminium.
The method of stirring may be a method of stirring a furnace. The method of stirring may be a method of stirring a ladle, storage vessel, transport vessel, holding furnace.
The method of stirring may be a method of stirring using a side mounted stirrer.
A apparatus may further include one or more of: a casing for the apparatus; a support frame; one or more cooling spaces; a control system. The support frame may support the core and/or one or more or all of the coils of electrical conductor and/or the control system.
The support frame may support the core and/or teeth and/or electrically conducting coils and/or casing for the apparatus and/or cooling system and/or control system. The support frame preferably maintains a consistent position for the support the core and/or teeth and/or electrically conducting coils and/or casing for the apparatus during the application of and removal of current to one or more or all of the electrically conducting coils.
The one or more cooling spaces may be provided within the apparatus and be in fluid communication with a source of coolant.
The control system may control the current and/or voltage and/or timing thereof and/or duration thereof for one or more and preferably all of the electrically conductive coils. The control system may control the phases and/or phasing of activation and/or deactivation of the magnetic field and/or current to the electrically conductive coils. The control system may apply a current to at least one of the electrically conducting coils at a first time to generate a first magnetic field configuration and/or applying a current to at least one of the other electrically conducting coils at a second time to generate a second magnetic field configuration, such that the changes in magnetic field configuration cause movement of the molten metal within the container. A three phase electromagnetic mover may be provided.
The core is preferably formed of a ferromagnetic material, such as iron or steel. The core preferably integrally provides the connection base and the teeth extending therefrom.
The connections preferably provide for the separate application of current to the separate electrically conducting coils. The connections preferably allow a single power supply to provide the current to the separate electrically conducting coils.
The support may be moved from one location to another using rails.
The wall of the container facing the electromagnetic mover may be formed of a metal plate, for instance a stainless steel plate. The plate may be the full depth through to the molten metal, but it is preferred that the plate abuts a refractory material and the refractory material contacts the molten metal.
Various embodiments of the invention will not be described, with reference to the accompanying drawings by way of example only, in which:
aa illustrates more schematically the flow paths and flow velocities for a first orientation of the electromagnetic mover;
aa illustrates more schematically the flow paths and flow velocities for a second orientation of the electromagnetic mover unit;
aa illustrates more schematically the flow paths and flow velocities for the same instance as
bb illustrates more schematically the flow paths and flow velocities for the same instance as
cc illustrates more schematically the flow paths and flow velocities for the same instance as
dd illustrates more schematically the flow paths and flow velocities for the same instance as
In a variety of instances, it is desirable to be able to introduce materials to a furnace or other container of molten metal and effectively disperse the introduced material in the molten metal. The introduced material could be one or more treatment additives for the molten metal. A commonly encountered situation, however, is one in which recycled aluminium in the form of aluminium chips needs to be melted for processing and reuse. The aluminium chips are relatively buoyant and so present difficulties in fully introducing them to the molten metal at a high rate. It is desirable to be able to quickly contact the non-melted metal with the existing molten metal and so promote fast melting of the newly introduced metal.
One option for achieving the above is to create a downward flow of molten metal at a location, such that non-melted metal introduced to the location is drawn with the flow down into the melt. The flow then preferably passes out into the furnace where the bulk of the molten metal is being held and where the heat input is provided. To maintain the flow, there needs to be a matching inward flow to the location of hot molten metal.
The well 1 is a separate unit to the rest of the furnace 5 and so it is possible to provide different configurations of well 1 in terms of the internal profile and shape of the well 1 to a limited extent. However, it is rarely acceptable to materially change the interface between the well 1 and the furnace 5, for instance by forming new openings into the furnace 5, removing parts of the furnace 5 internal profile or adding to that profile. Hence, there is a strong need to identify solutions which work with the exiting profile and can readily be retrofitted to a pre-existing furnace.
Returning to
Achieving the optimum flow within the well 1 and the furnace 5 is a significant problem.
Referring to
Whilst establishing the primary motion axis C-C in
Whilst establishing the primary motion axis C″-C″ in
The above examples demonstrate the problems in generalising from the primary motion axis C-C up to the observed flow path, particularly where a single inlet and outlet to the furnace 5 from the well 1 is used.
The applicant has established that there are material advantages in the flow paths and flow velocities to be obtained by careful selection of the orientation of the electromagnetic mover unit. An example is provided in the third orientation shown in
Whilst the change between the first orientation, 0° inclined, and the third orientation, 8° inclined, is small, the impact is significant as can be seen in the details provided in
As a consequence of the above, in Zone A there is a flow across, slightly upward and towards the junction of the angled front wall 17 and side wall 30a. This provides strong transportation of the non-molten metal introduced to Zone A.
In Zone B, which in this orientation is focused towards the junction of the angled front wall 17 and the side wall 30a, there is increasing velocity, an initial upward and across movement and then a change to a higher velocity downward movement. The downward movement is focussed along the side wall 30a. A large part of the metal entering Zone B is drawn from Zone F in the lower and middle part of the well 1. The combination of movements in Zones A, F and B provides a strong motion to submerge the non-molten metal added. This brings the non-molten metal into contact with hot molten metal and moves the non-molten metal quickly away from Zone A as it is processed.
By Zone C, the downward motion and high flow velocities are maintained alongside the side wall 30a and then out of the well 1 into the furnace. In Zone D, within the first part 25 of the furnace 5 the flow direction is steered into a more horizontal direction by the bottom surface 32 of the furnace 5. The flow velocity starts to decline as the side wall 30a of the well is no longer present to constrain the flow and so the flow can spread out further.
The return flow to the well 1 and the upper part thereof, Zone A can be seen in Zone E and Zone F. In Zone E within the furnace 5 and close to the well, there is a general low velocity flow across a large part of the width of the well 1 into the well. In Zone F the velocity increases under the effect of the electromagnetic mover unit 21 and starts to develop an upward motion as a result and due to the constraining effect of the angled front wall 17. The flow then returns to Zone A and Zone B.
The third orientation ensures good circulation within the furnace 5 and the avoidance of problem zones, such as Zone H in the first orientation above.
In general effect, the twisting of the primary motion axis C-C in the third orientation serves to allow a separate entrance zone from the furnace 5 to the well 1 (middle and lower parts in
The majority of the flow through Zone E is behind the jet of Zone C in
The flow paths and flow velocities of the third orientation are beneficial in the context of the well 1 and the first part 25 of the furnace 5 as shown above. However, the benefits also extend out into the wider parts of the furnace. These benefits are shown in
Whilst in the third orientation described in detail above, an angle of 8° relative to the vertical is provided together with a lifting motion, other angles relative to the vertical can be employed. Decreases in the angle relative to the vertical are possible, 5° to 8°, whilst still generating lift to the molten metal and still forming a preferential flow out of one side of the well and a return flow on the other side. Lower angles 3° to 5° may still offer some separation of the flows in some well/furnace configurations, but are less optimal. Higher angles are certainly possible, with 8° to 15° expected to offer similar separation of flows and good flow velocities out into the furnace 5 from the well 1. Still higher angles, 15° to 35°, are expected to still offer good lifting and hence downward and outward flow paths and velocities to one side of the well in preference to the other to still give good submergence rates for the non-molten metal. Higher angles 35° to 50° are expected to give reasonable submergence for the scrap and preferential flow to the side of the well out into the furnace, but are likely to be able to handle decreasing volumes feed rates of non-molten metal feed.
To maximise the amount of low reluctance material between the ends of the teeth in the inductor of the electromagnetic mover unit 21 and the molten metal in the container, it is desirable to use a metal plate on the opposing face of the angled front wall 17 of the well 1. This allows a thinner wall to be used than if a purely refractory wall is used. The metal plate also has a lower reluctance per unit thickness than a refractory wall. A 10 mm metal plate and 270 mm refractory thickness represent a useful configuration. No cooling of the plate is provided, but air cooling of the inductors.
As described above in the third orientation, the electromagnetic mover unit 21 is operating with the primary motion axis set to the upward direction. This lifts the molten metal up and across the angled front face before it falls again in Zone B and C. The embodiment includes the possibility of occasionally and/or periodically reversing the current to the electromagnetic mover unit 21 and hence reversing the primary motion axis C-C. This reversal might be applied for a shorter period of time compared with the usual direction. The reversal might be used to clean or purge the well 1 and surround parts of the furnace 5 of any build-up of metal as the reversal will produce higher velocities in many of the areas having a lower velocity when in the usual direction.
A variety of inductor designs are possible for the electromagnetic mover unit 21, but a three phase design is preferred.
In the third orientation described in detail above, an angle of 8° relative to the vertical is provided and used throughout the processing. The option to reverse the current and hence the primary motion axis C-C still retains the electromagnetic mover unit 21 at that same inclination.
In addition to the operation of the electromagnetic mover unit 21 in the third orientation described above, it is possible to vary the angle of the orientation at different stages or times. For instance, during start up and/or after tapping when the volume of molten metal in the furnace 5 and hence in the well 1 is low, no non-molten metal may be being fed to the well 1 and the focus might be on merely stirring the existing molten metal. In that instance, the inclination of the electromagnetic mover unit 21 may be much greater, for instance up to the 90° angle used in the second orientation. This could give the strongest stirring effect with the limited molten metal present and the absence of the ability to submerge non-molten metal is not important in this stage as there is no such non-molten metal to handle. A single step, multiple step or continuous movement to the next orientation, such as the third orientation, could then be provided. This would provide the orientation best suited to submergence of non-molten metal. The movement may be controlled according to a pre-determined sequence and/or based upon feedback from sensors associated with the well 1 and/or furnace 5 and/or their contents.
As can be seen in
The cradle 13 includes an adjustable mounting frame 15 and that has been adjusted so as to present the electromagnetic mover unit 21 at a much more reclined angle, for instance >50°. Once again, the mounting frame 15 presents the electromagnetic mover unit to the angled front wall 104 of the transfer well 102. The angled front wall 104 of the transfer well 102 may always be at this angle or may be at this angle because the container 106 (potentially the same furnace 5 as above) has been tipped to assist in emptying the container 106.
Once in position, the electromagnetic mover unit 21 has a primary motion axis C-C aligned with the centre axis Z-Z of the angled front wall 104 of the transfer well 102. Application of current such that the primary motion is upward then causes the molten metal 108 in the transfer well 102 to be lifted up the angled front wall 104 to a level above the resting level 110 in the container 106. This causes the molten metal 108 to fall into a transfer launder 112 or transfer container and hence be removed from the container 106. Once again, to maximise the amount of low reluctance material between the ends of the teeth in the inductor of the electromagnetic mover unit 21 and the molten metal in the container 106, a metal plate on the opposing face of the angled front wall 104 of the transfer well 102 is provided. A 10 mm metal plate and 100 mm refractory thickness represent a useful configuration. The metal plate preferably extends around 100 mm above the resting level 110 of the molten metal 108 in the container 106. The arrangement allows high volumes of molten metal to be discharged in short timeframes, using the same electromagnetic mover unit 21 as already used for another purpose. The electromagnetic mover unit 21 can be completely removed to allow tipping or further tipping of the container 106.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1620025.5 | Nov 2016 | GB | national |
| 1620026.3 | Nov 2016 | GB | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/GB2017/053561 | 11/27/2017 | WO | 00 |