The present invention relates to techniques for attaching antenna structures, including but not limited to dielectric resonators or pellets, to electrical feed structures so as to form antennas, for example dielectric resonator antennas (DRAs), high dielectric antennas (HDAs) and dielectrically-loaded antennas (DLAs).
Dielectric resonator antennas are resonant antenna devices that radiate or receive radio waves at a chosen frequency of transmission and reception, as used in for example in mobile telecommunications. In general, a DRA consists of a volume of a dielectric material (the dielectric resonator or pellet) disposed on or close to a grounded substrate, with energy being transferred to and from the dielectric material by way of monopole probes inserted into the dielectric material or by way of monopole aperture feeds provided in the grounded substrate (an aperture feed is a discontinuity, generally rectangular in shape, although oval, oblong, trapezoidal or butterfly/bow tie shapes and combinations of these shapes may also be appropriate, provided in the grounded substrate where this is covered by the dielectric material. The aperture feed may be excited by a strip feed in the form of a microstrip transmission line, coplanar waveguide, slotline or the like which is located on a side of the grounded substrate remote from the dielectric material). Direct connection to and excitation by a microstrip transmission line is also possible. Alternatively, dipole probes may be inserted into the dielectric material, in which case a grounded substrate is not required. By providing multiple feeds and exciting these sequentially or in various combinations, a continuously or incrementally steerable beam or beams may be formed, as discussed for example in the present applicant's co-pending U.S. patent application Ser. No. 09/431,548 and the publication by KINGSLEY, S. P. and O'KEEFE, S. G., “Beam steering and monopulse processing of probe-fed dielectric resonator antennas”, IEE Proceedings—Radar Sonar and Navigation, 146, 3, 121-125, 1999, the full contents of which are hereby incorporated into the present application by reference.
The resonant characteristics of a DRA depend, inter alia, upon the shape and size of the volume of dielectric material and also on the shape, size and position of the feeds thereto. It is to be appreciated that in a DRA, it is the dielectric material that resonates when excited by the feed. This is to be contrasted with a dielectrically loaded antenna, in which a traditional conductive radiating element is encased in a dielectric material that modifies the resonance characteristics of the radiating element.
DRAs may take various forms, a common form having a cylindrical shape dielectric pellet which may be fed by a metallic probe within the cylinder. Such a cylindrical resonating medium can be made from several candidate materials including ceramic dielectrics.
Since the first systematic study of dielectric resonator antennas (DRAs) in 1983 [LONG, S. A., McALLISTER, M. W., and SHEN, L. C.: “The Resonant Cylindrical Dielectric Cavity Antenna”, IEEE Transactions on Antennas and Propagation, AP-31, 1983, pp 406-412], interest has grown in their radiation patterns because of their high radiation efficiency, good match to most commonly used transmission lines and small physical size [MONGIA, R. K. and BHARTIA, P.: “Dielectric Resonator Antennas—A Review and General Design Relations for Resonant Frequency and Bandwidth”, International Journal of Microwave and Millimetre-Wave Computer-Aided Engineering, 1994, 4, (3), pp 230-247]. A summary of some more recent developments can be found in PETOSA, A., ITTIPIBOON, A., ANTAR, Y. M. M., ROSCOE, D., and CUHACI, M.: “Recent advances in Dielectric-Resonator Antenna Technology”, IEEE Antennas and Propagation Magazine, 1998, 40, (3), pp 35-48.
A variety of basic shapes have been found to act as good DRA resonator structures when mounted on or close to a ground plane (grounded substrate) and excited by an appropriate method. Perhaps the best known of these geometries are:
Rectangle [McALLISTER, M. W., LONG, S. A. and CONWAY G. L.: “Rectangular Dielectric Resonator Antenna”, Electronics Letters, 1983, 19, (6), pp 218-219].
Triangle [ITTIPIBOON, A., MONGIA, R. K., ANTAR, Y. M. M., BHARTIA, P. and CUHACI, M.: “Aperture Fed Rectangular and Triangular Dielectric Resonators for use as Magnetic Dipole Antennas”, Electronics Letters, 1993, 29, (23), pp 2001-2002].
Hemisphere [LEUNG, K. W.: “Simple results for conformal-strip excited hemispherical dielectric resonator antenna”, Electronics Letters, 2000, 36, (11)].
Cylinder [LONG, S. A., McALLISTER, M. W., and SHEN, L. C.: “The Resonant Cylindrical Dielectric Cavity Antenna”, IEEE Transactions on Antennas and Propagation, AP-31, 1983, pp 406-412].
Half-split cylinder (half a cylinder mounted vertically on a ground plane) [MONGIA, R. K., ITTIPIBOON, A., ANTAR, Y. M. M., BHARTIA, P. and CUHACI, M: “A Half-Split Cylindrical Dielectric Resonator Antenna Using Slot-Coupling”, IEEE Microwave and guided Wave Letters, 1993, Vol. 3, No. 2, pp 38-39].
Some of these antenna designs have also been divided into sectors. For example, a cylindrical DRA can be halved [TAM, M. T. K. and MURCH, R. D.: “Half volume dielectric resonator antenna designs”, Electronics Letters, 1997, 33, (23), pp 1914-1916]. However, dividing an antenna in half, or sectorising it further, does not change the basic geometry from cylindrical, rectangular, etc.
High dielectric antennas (HDAs) are similar to DRAs, but instead of having a full ground plane located under the dielectric pellet, HDAs have a smaller ground plane or no ground plane at all. Removal of the ground plane underneath gives a less well-defined resonance and consequently a very much broader bandwidth. HDAs generally radiate as much power in a backward direction as they do in a forward direction.
In both DRAs and HDAs, the primary radiator is the dielectric pellet. In DLAs, the primary radiator is a conductive component (e.g. a metal wire or printed strip or the like), and a dielectric component then just modifies the medium in which the DLA operates and generally allows the antenna as a whole to be made smaller or more compact.
A DLA may also be excited or formed by a direct microstrip feedline. In particular, the present applicant has found that a pellet of dielectric material may be placed on or otherwise associated with a microstrip feedline or the like so as to modify radiation properties of the feedline when operating as an antenna.
The present application is particularly but not exclusively directed towards techniques for constructing DRAs, HDAs and DLAs by way of assembly-line processes in a large-scale industrial context. Furthermore, the present application is particularly but not exclusively concerned with DRAs or HDAs comprised as a piece of high dielectric constant ceramic material excited by some form of feed structure on a printed circuit board (PCB), and also with DLAs comprising a conductive radiator provided with a pellet of dielectric material.
For the purposes of the present application, the expression “dielectric antenna” is hereby defined as encompassing DRAs, HDAs and DLAs.
According to a first aspect of the present invention, there is provided a dielectric antenna comprising a dielectric pellet mounted in direct contact with a microstrip transmission line formed on one side of a dielectric substrate.
According to a second aspect of the present invention, there is provided a method of manufacturing a dielectric antenna, wherein a dielectric pellet is mounted in direct contact with a microstrip transmission line formed on one side of a dielectric substrate.
The dielectric substrate may be in the form of a printed circuit board (PCB) and may have optional metallisation on at least part of one or other of its major surfaces.
In preferred embodiments, the dielectric pellet is made of a ceramic material, preferably with a high dielectric constant.
The dielectric antenna may be a DRA, an HDA or a DLA.
This has the advantage of making an antenna with good gain and bandwidth and a very simple method of assembly because everything is on one side of the dielectric substrate or PCB (with slot feeding, for example, the microstrip is on one side of the board and the ceramic pellet is on the other). On a production line, a pick-and-place machine can take ceramic pellets supplied on a reel and place these directly onto the dielectric substrates or PCBs.
Several methods of attachment can be used such as gluing or gluing with conducting epoxy. The present applicant has discovered that it is possible to solder the ceramic pellets into place, and that this can give a very strong joint with good electrical and radio-frequency properties. In production, the microstrip will have been already screen-printed with solder paste before the pick-and-place machine positions the ceramic pellet onto the dielectric substrate or PCB. The substrate or PCB with ceramic pellet attached is then passed into a reflow oven that melts the solder, thereby soldering the ceramic resonator in place. This is a procedure ideally suited to modern automated electronic assembly production lines.
Solder will not generally adhere directly to ceramic materials, so the ceramic pellets are advantageously first metallised. Several metals can be used for this and can be deposited in different ways, but the present applicant has found that conductive silver paint is a particularly efficient and cost effective solution for preferred dielectric antenna products. A screen-printing process can easily apply the paint. In some cases (i.e. for some types of paint and for some ceramics) the paint can be allowed to dry, but usually it is preferable for the painted ceramic to be fired in an oven or on a hot plate to ensure good adhesion and a surface that has a low loss at radio frequencies.
With direct microstrip feeding it is often advantageous to have the ceramic pellet substantially offset from the microstrip, as this gives unproved gain, bandwidth and match to 50 ohms (an industry standard impedance in antenna design). However, with such an offset the joint is not strong mechanically because the ceramic pellet is balanced on the microstrip line (see
In general, metallisation of parts of the lower surface of a dielectric pellet (e.g. a ceramic pellet) and/or the substrate or PCB surface beneath the resonator will cause a concentrating effect on the electric field inside the dielectric, thereby changing the electrical performance of the antenna. The effect of metallisation can even cause the antenna to resonate in a different mode with a consequently larger change in the electrical performance. The shape and extent of the microstrip line feeding the dielectric antenna also affects the overall performance. With careful design, these changes can be used to improve the antenna performance. Whilst it is usual for the metallisation on the two surfaces (underside of dielectric/pellet and substrate/PCB) to be matched with each other, the present applicant has found a few cases where improved antenna performance can be obtained with the metallisations being non-matching.
The present applicant has successfully created DRAs and HDAs with rectangular ceramic pellets acting as dielectric resonators and also with half-split cylindrical ceramic pellets in this way. By extension, all or most other shapes of dielectric pellet (such as those mentioned in the introductory part of the present application) may therefore be attached to a dielectric substrate/microstrip transmission line assembly in this manner.
To form a DLA in accordance with embodiments of the present invention, a conductive microstrip feedline is printed or otherwise provided on a first surface of a dielectric substrate such as a PCB and a second surface of the dielectric substrate or PCB, opposed to the first surface, is metallised over a predetermined portion thereof, leaving at least one area of the second surface free of metallisation. A dielectric pellet is then mounted on top of the microstrip feedline on the first surface or otherwise mounted on the first surface so as to be directly contacted by the microstrip feedline. The dielectric pellet serves to lower an operating frequency of the DLA by making the feedline behave as is it were longer in length and may also improve match of impedance or other properties, but it will be appreciated that in a DLA of the present invention, it is the feedline that serves as the primary radiator (as opposed to the dielectric pellet in a DRA or HDA).
The dielectric pellet is advantageously mounted on an area of the first surface corresponding to the at least one area of the second surface that is not metallised. The microstrip feedline may pass underneath the dielectric pellet, or may be fed up a side surface or wall of the pellet, or may be fed onto a top surface of the pellet. It is generally preferred, when constructing a DLA of embodiments of the present invention, that the microstrip feedline terminates at the dielectric pellet. It is also preferred that the microstrip feedline extends along the first surface of the dielectric substrate from a feed or connection point to the dielectric pellet, and that the second surface of the dielectric substrate is metallised over the full longitudinal extent of the microstrip feedline on the first side except where the feedline contacts the dielectric pellet. A full width of the second surface of the dielectric substrate may be metallised, or only a partial width of the second surface, provided that the partial width is wider than a width of the feedline. In some embodiments, at least one surface of the dielectric pellet, for example an exposed end surface facing away from the feed or connection point, is also metallised, with the feedline being connected to the metallised surface so as to form a “fat” monopole.
The dielectric pellet in DLA applications may also be metallised or soldered as previously described in relation to DRAs and HDAs, and may also be provided with pads as hereinbefore described.
When using a direct connection (e.g. a direct microstrip connection) to feed a DRA or HDA; the present applicant has found that the position of the dielectric material (the dielectric pellet) relative to the direct connection (e.g. a microstrip) influences the direction of a resultant radiation beam. Where a dielectric material of appropriate shape is placed centrally on top of a microstrip transmission line, the dielectric material will tend to generate a beam in a vertical direction. When the dielectric material is placed on top of the microstrip line with a greater volume of the material to the right or left of the microstrip line, a beam having respectively a rightward or leftward component is generated. This technique may be used to help aim a radiation beam in a desired direction and/or to broaden a radiation beam by using a plurality of dielectric resonators positioned in different ways on the microstrip transmission line.
Accordingly, there may be provided one or more dielectric resonators mounted on a microstrip transmission line, wherein at least one of the dielectric resonators is positioned off-centre on the microstrip transmission line.
There may also be provided a method of feeding a DRA or HDA or an array thereof, wherein at least one dielectric resonator is positioned off-centre on the microstrip transmission line in a predetermined direction so as to generate a beam having a directional component in the predetermined direction.
According to a third aspect of the present invention, there is provided an array of dielectric antennas each comprising a dielectric resonator mounted on a microstrip transmission line, wherein at least one of the dielectric resonators is positioned off-centre on the microstrip transmission line.
According to a fourth aspect of the present invention, there is provided a method of feeding a dielectric resonator of a dielectric antenna, wherein the dielectric resonator is positioned off-centre on the microstrip transmission line in a predetermined direction so as to generate a beam having a directional component in the predetermined direction.
For a better understanding of the present invention and to show how it may be carried into effect, reference shall now be made by way of example to the accompanying drawings, in which:
Ceramic materials with relative permittivities ranging from 37 to 134 have been successfully used as resonator pellets 1 fed directly by microstrip transmission lines 2. Specific paints suitable for metallisation of the pellets 1 vary according to the type of ceramic material. Examples of suitable metallic paints include DuPont® 8032 and 5434I, which may be used with Solderplus® 42NCLR-A solder paste.
Generally the benefits that can be obtained by metallising parts of the undersurface of the pellets are improved bandwidth and lower resonant frequency (resulting in a smaller antenna for a given operating frequency).
The return loss bandwidth of an antenna is dependent upon:
In effect, metallisation used to improve the soldered joint can affect the first three items on the list above. Examples where metallisation of a rectangular pellet for solder purposes have resulted in an increase in bandwidth and reduced frequency without adversely affecting the other properties of the antenna are shown in
Specifically,
The preferred features of the invention are applicable to all aspects of the invention and maybe used in any possible combination.
Throughout the description and claims of this specification, the words “comprise” and “contain” and variations of the words, for example “comprising” and “comprises”, mean “including but not limited to”, and are not intended to (and do not) exclude other components, integers, moieties, additives or steps.
Number | Date | Country | Kind |
---|---|---|---|
0211109.4 | May 2002 | GB | national |
0211114.4 | May 2002 | GB | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/GB03/02114 | 5/15/2003 | WO |