In-situ interlocking of metals using additive friction stir processing

Abstract
A method for joining materials using additive friction stir techniques is provided. The method joins a material to a substrate, especially where the material to be joined and the substrate are dissimilar metals. One such method comprises (a) providing a substrate with one or more grooves; (b) rotating and translating an additive friction-stir tool relative to the substrate; (c) feeding a filler material through the additive friction-stir tool; and (d) depositing the filler material into the one or more grooves of the substrate. Translation and rotation of the tool causes heating and plastic deformation of the filler material, which flows into the grooves of the substrate resulting in an interlocking bond between the substrate and filler material. In embodiments, the depositing of the filler material causes deformation of the grooves in the substrate and an interlocking configuration between the grooves of the substrate and the filler material results.
Description
BACKGROUND OF THE INVENTION

Field of the Invention


The present invention is in the field of solid state materials joining. In particular the invention is in the field of joining, coating, or cladding of metals, such as two dissimilar or incompatible materials that are not typically recommended for conventional coating or cladding or joining.


Description of Related Art


Friction-stir processing provides for the solid state joining of pieces of metal at a joint region through the generation of frictional heat at the joint and opposed portions of the metal pieces by cyclical movements of a tool piece that is harder than the metal pieces. An example of this is provided by International Application Publication No. PCT/GB1992/002203. Frictional heat produced between the substrate and the tool during the process causes the opposed portions of the substrate to soften, and mechanical intermixing and pressure cause the two materials to join. Typically, two materials are placed side-by-side and are joined together at the seam between the two.


Additive friction-stir fabrication, invented by the present inventors (see U.S. Pat. Nos. 8,636,194; 8,632,850; 8,875,976; and 8,397,974, the contents of which are hereby incorporated by reference in their entireties), is an additive process for joining materials. Additive friction-stir fabrication (FSF) processes use shear-induced interfacial heating and plastic deformation to deposit metallic coatings onto metal substrates. FSF coatings have bond strengths superior to those of thermally sprayed coatings, and have the potential to enhance corrosion resistance, enhance wear resistance, repair damaged or worn surfaces, and act as an interfacial layer for bonding metal matrix composites. In this process, the coating material, such as a metal alloy, is fed through a rotating spindle or tool to the substrate surface. As shown in FIG. 1, frictional heating occurs at the filler/substrate interface due to the rotational motion of the filler material, such as a rod 23, at an angular velocity ω and the downward pressure P applied. The mechanical shearing that occurs at the interface acts to disperse any oxides or boundary layers, resulting in a metallurgical bond between the substrate 10 and filler material/coating 25. As the substrate 10 moves relative to the tool 15, the coating is extruded under the rotating shoulder of the stirring tool 15.


Conventional techniques are incapable of bonding dissimilar materials such as steel and aluminum. Currently, explosive bonding is used to achieve solid state cladding of dissimilar materials. Explosive bonding uses controlled detonations to accelerate one metal plate into another creating an atomic bond. This method has numerous limitations related to material pairing, thickness and the environment in which it is conducted. Additional techniques include those described by Geiger M. et al, Friction Stir Knead Welding of steel aluminum butt joints, International Journal of Machine Tools & Manufacture 48 (2008) 515-521), and those described in U.S. Patent Application Publication No. 20120273113, U.S. Pat. No. 4,023,613, and Chinese Patent No. CN 102120287 B. Despite these efforts, however, there remains a need in the art for new techniques for joining dissimilar materials.


SUMMARY OF THE INVENTION

The present invention is a method for joining materials using additive friction stir techniques. The method can be used to join a material to a substrate, especially where the material to be joined and the substrate comprise dissimilar metals.


One such method comprises (a) providing a substrate with one or more grooves; (b) rotating and translating an additive friction-stir tool relative to the substrate; (c) feeding a filler material through the additive friction-stir tool; and (d) depositing the filler material into the one or more grooves of the substrate. In preferred embodiments, substrate(s) with multiple grooves are provided. Translation and rotation of the tool causes heating and plastic deformation of the filler material, which flows into the grooves of the substrate resulting in an interlocking bond between the substrate and filler material. In embodiments, the depositing of the filler material causes deformation of the grooves in the substrate and an interlocking configuration between the grooves of the substrate and the filler material results.


The grooves of the substrate can have an opening, a base, and parallel sidewalls extending from the opening to the base. In embodiments, the grooves have an opening, a base, and perpendicular sidewalls extending from the opening to the base thereby providing the groove with a square or rectangular shaped cross section. In other embodiments, the grooves have an opening, a base, and parallel sidewalls sloping from the opening to the base. Additionally or alternatively, the grooves can have an opening, a base, and sidewalls sloping in opposite directions from the opening to the base. The opening of the groove can have a width larger than a width of the base. The opening can alternatively have a width smaller than a width of the base, thereby providing the groove with a dovetail shaped cross section.


According to embodiments, the methods can comprise deforming the opening to the groove thereby providing a mechanical lock between the filler material and the groove. The deforming can be performed during the depositing of the filler material into the grooves of the first substrate.


In preferred embodiments, the first substrate and the filler material can each be metal. For example, the first substrate and the filler material can each be metal independently chosen from steel, Al, Ni, Cr, Cu, Co, Au, Ag, Mg, Cd, Pb, Pt, Ti, Zn, Fe, Nb, Ta, Mo, W, or an alloy comprising one or more of these metals. In particular embodiments, the first substrate comprises steel and the filler material is metal chosen from steel, Al, Ni, Cr, Cu, Co, Au, Ag, Mg, Cd, Pb, Pt, Ti, Zn, Fe, Nb, Ta, Mo, W, or an alloy comprising one or more of these metals. The filler material can be a powder, pellet, rod, or powdered-filled cylinder.


Another method includes providing a sheet of metal or a metal plate as a second substrate and deforming and depositing the sheet of metal or the metal plate into the one or more grooves of the substrate.


Articles of manufacture are also included within the scope of the invention. For example, included is an article of manufacture comprising: two different metals disposed in an interlocking configuration; and a joint between the two metals along an area of interlocking; wherein a cross section of the joint reveals each of the two metals having a portion providing two-dimensional projections into the area of interlocking; and wherein the two-dimensional projections are of concave polygon shaped.


Methods for coating, cladding, or joining two dissimilar materials are particular features of the invention. In one embodiment, the method comprises providing a first substrate and a second substrate, wherein the first substrate has grooves disposed on a surface of the first substrate. The method further comprises overlaying the first substrate with the second substrate and moving a rotating additive friction-stir tool along the second substrate over the grooves so that it heats the second substrate. A consumable portion of the additive friction stir tool combines with the second substrate and they are plasticized together so that the plasticized material flows into the grooves, allowing the first material to be bonded to the second material through an interlocking connection. In yet another embodiment, the method comprises provided a substrate with grooves disposed on the surface of the substrate. The method further comprises moving a rotating additive friction stir tool along the grooves. A consumable material from the rotating additive friction stir tool flows into the grooves, while friction from the rotating additive friction stir tool deforms the grooves and locks the deposited material into the grooves.


The methods of the invention are useful for creating a variety of composite materials with layers of dissimilar composition and properties. Practical applications of these composite materials include use as components for manufacturing automobiles, ships, tanks, planes, and aerospace vehicles.





BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings illustrate certain aspects of embodiments of the present invention, and should not be used to limit the invention. Together with the written description the drawings serve to explain certain principles of the invention.



FIG. 1 is a schematic diagram showing an additive friction stir process.



FIG. 2 is a schematic diagram showing mechanical interlocking method embodiments using additive friction stir.



FIG. 3 is a schematic diagram showing a continuous feeding system for use in the invention.



FIG. 4 is a macrograph image showing a cross section of an article of manufacture comprising two different metals (molybdenum and copper) in an interlocking configuration prepared according to an embodiment of the invention.





DETAILED DESCRIPTION OF VARIOUS EMBODIMENTS OF THE INVENTION

Reference will now be made in detail to various exemplary embodiments of the invention. It is to be understood that the following discussion of exemplary embodiments is not intended as a limitation on the invention. Rather, the following discussion is provided to give the reader a more detailed understanding of certain aspects and features of the invention.



FIG. 2 shows a general process 5 of material coating, cladding, or joining through mechanical interlocking. The process preferably comprises the coating, cladding, or joining of materials, such as dissimilar materials for example two different metals. The general process involves coating, cladding, or joining a material to a first substrate 10 having a grooved surface 30. Any number of grooves or type of groove pattern can be used. In preferred embodiments, multiple grooves are present in the substrate, such as from 1-100 grooves, or from 5-50 grooves, or from 10-40 grooves, or 22 from 20-30 grooves, such as 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, or 19 grooves are present in the substrate. The number of grooves may be dependent on the particular application and/or size of substrate being used. Methods of creating the grooves in the substrates can include laser machining, friction based machining, conventional machining, and/or metal forming on the surface or the edges of the substrate to name a few.


One embodiment of the method is designed to join a coating of dissimilar material to a substrate. As shown in FIG. 2, the friction stir tool 15 is passed directly over the first substrate 10 over the grooved surface 30. In this embodiment, the grooves may include dove-tail shaped grooves 31, but preferably square-shaped grooves 33. The rotating friction-stir tool 15, typically non-consumable (or harder than the substrate and filler materials), is fed with a consumable filler material 23 (such as a powder or rod) such that the consumable filler material 23 is deposited into the grooves 33 while friction produced by the friction-stir tool 15 generates plastic deformation of the grooves to interlock the deposited material into the grooves 33. Thus, additive friction stir tool 15 will touch the grooved surface 33 to deform the grooves 33 and lock the deposited metal into the grooves 33.


Another embodiment of the invention comprises an additive friction stir method comprising providing a substrate having a grooved surface, translating a rotating additive friction-stir tool along the surface of the substrate along a vector that overlies one or more of the grooves of the grooved surface, and feeding the rotating friction-stir tool with a filler material (e.g., consumable filler material) such that the filler material is deposited into the grooves while friction produced by the friction-stir tool generates plastic deformation of the grooves to overlap a portion of the deposited filler material disposed within the grooves, thereby interlocking the substrate and filler.


Articles of manufacture can be prepared by such processes and can include articles of manufacture comprising metals (preferably two different metals) disposed in an interlocking configuration with a joint between the two metals along an area of interlocking; wherein a cross section of the joint reveals each of the two metals having a portion providing two-dimensional projections into the area of interlocking; and wherein the two-dimensional projections are of concave polygon shape. For example, shown in FIG. 2 are cross-sectional views of the joints (with grooves 31, 33) of each of two embodiments of articles of manufacture that can be prepared according to the invention. As illustrated, the metals on both sides of the joint with grooves 31 each have two-dimensional projections into the area of interlocking that are of a convex polygon shape, and are the same shape. In contrast, the metals of the joint with grooves 33 on either side of the joint have two-dimensional projections into the area of interlocking that are a concave polygon shape. Additionally, the two-dimensional projection on one side of the joint with grooves 33 is the same shape as the two-dimensional projection on the other side of the joint. The two-dimensional projections on either side of the joint can be the same or different shapes and all on one side can be the same or different shapes.


In another embodiment, a pre-fabricated layer (such as a sheet or plate) of material can be joined to a substrate. The substrate comprises a grooved surface and can include grooves that are interlocking in shape such as dovetail grooves 31. The grooves can have an opening, a base, and sidewalls sloping in opposite directions from the opening to the base. The opening of the grooves can have a width smaller than a width of the base of the grooves, or the opening of the grooves can have a width larger than a width of the base. In one embodiment, the grooves are provided with a dovetail shaped cross section when the grooves have a width smaller than a width of the base and when the sidewalls are also sloping in opposite directions from the opening to the base. In other embodiments, the grooves of the substrate can have an opening, a base, and parallel sidewalls extending from the opening to the base. In such embodiments, the grooves can have a square or rectangular shaped cross section.


In methods where a sheet of metal or a metal plate is used, a second substrate 20 is disposed on the first substrate 10 over the grooves 30 of the grooved surface of the first substrate. Further, in embodiments, there is no depression or groove(s) on the surface of the second substrate. An additive friction-stir tool 15 is passed over the second substrate 20 along a vector overlying one or more of the grooves 30. The friction-stir tool 15 rotates and during rotation a filler material 23 (such as a powder or rod) is fed through the friction-stir tool 15. Interaction of the rotating non-consumable friction-stir tool 15 with the second substrate 20 generates plastic deformation at an interface between the rotating non-consumable friction-stir tool 15 and the second substrate 20 such that the consumable filler 23 and the second substrate 20 are extruded into one or more of the grooves 30 of the first substrate 10 to interlock the second substrate 20 with the first substrate 10. Thus, deposition can be performed with or without touching the additive friction stir tool 15 to the grooves 30 on the surface of the first substrate 10. In this case, a dovetail type groove 31 pattern will be most beneficial for achieving improved joint properties.


Thus, one embodiment of the invention provides an additive friction stir method comprising providing a first substrate having a grooved surface, providing a second substrate having a composition that is different than the first substrate, overlaying the second substrate over the first substrate such that a surface of the second substrate is in communication with the grooved surface, translating a rotating non-consumable friction-stir tool along an opposing surface of the second substrate along a vector that overlies one or more grooves of the grooved surface and feeding the rotating non-consumable friction-stir tool with a consumable filler material such that interaction of the rotating non-consumable friction-stir tool with the second substrate generates plastic deformation at an interface between the rotating non-consumable friction-stir tool and the second substrate such that the consumable filler and second substrate are extruded through the one or more of the grooves of the first substrate to interlock the second substrate with the first substrate in situ.


In this embodiment, during translating the rotating non-consumable friction stir tool does not penetrate the second substrate, so that no depression is formed on the surface of the second substrate. Thus, the non-consumable portion of the tool may generate friction at the surface of the second substrate without substantial penetration into the second substrate. Not wishing to be bound by theory, this may be due to the addition of consumable filler material being added during the process where a volume of filler material is provided underneath the non-consumable portion of the tool.


The steps of the methods may be repeated to add successive layers of materials. For example, upon joining of a first substrate with a second substrate, the surface of the second substrate may be machined to form a grooved surface. Then a third layer may be added using the first or second embodiment of the method, and so on. Possibilities include the manufacture of bimetallic composites with alternating layers or multi-metallic composites with completely different layers. Composites with three, four, five, six, seven, eight, nine, ten or more layers are even possible.


Methods of the invention may include combinations of the features of the embodiments described above. Some embodiments may need machining of dovetail grooves 31, and other embodiments may only need simple square-shaped grooves 33, which are economical in terms of machining. However, other embodiments may include some combination of dovetail grooves 31 and square-shaped grooves 33. Additionally, a method of the invention may include (1) providing a first substrate with a grooved surface (2) overlaying a portion of the first substrate with a second substrate, leaving some portions of the first substrate exposed (3) translating an additive friction stir tool over the second substrate in a vector overlying the grooves (4) translating an additive friction stir tool directly over the first substrate at the exposed portions (5) optionally, repeating steps 1-4. Alternatively, the second substrate may include multiple panels of different thicknesses or material types. In this way, it is possible to introduce features into the surface geometries of the joined materials.


The joint strength of the samples produced in these methods will depend on the geometry of the groove pattern and the surface characteristics of the grooved surfaces. Finite element analysis can be conducted to predict the optimal grove geometry and surface characteristics. Desired groove pattern and surface characteristics can be achieved using different manufacturing processes such as various machining techniques, etching, milling, and/or plating. In one embodiment, grooves are machined on a surface of the first substrate through a Computer Numerical Control (CNC) machine. The grove patterns may be programmed in Computer-Aided Design (CAD) programs. The grooves may be of any uniform geometric shape, including polygonal shapes (e.g. square, rectangular, triangular, trapezoidal), complex polygon shapes (e.g. combinations of two or more polygonal shapes, or convex or concave polygon shapes), or nonpolygonal shape (e.g. semi-circular, semi-oval). Further, the groove pattern may include multiple grooves representing different shapes. The density of the groove pattern will depend on the size of the grooves, with smaller grooves being provided at a higher density on the surface than larger grooves. The size of the grooves depends on the particular application and the size of the additive friction stir tool used. For example, for certain substrates, the depth of the grooves from the opening to the base of the groove (measured perpendicularly from the opening to the base) may range anywhere from 10 micrometers to 10 mm in depth or width, or any range in between, including 10 micrometers to 1 mm, and 1 mm to 10 mm. Thicker materials are capable of even deeper grooves for bonding, including those exceeding 10 mm, such as 1 cm, 10 cm, or between 10-100 cm or more. The grooves may be provided at uniform or varying depth. General dimensions may range from shallow and wide to deep and narrow or anywhere in between. The optimal size and shape of the grooves may be achievable through routine experimentation. The grooves may be present on the first substrate in any pattern, including linear and non-linear. After obtaining the desired groove pattern and surface characteristics, additive friction stir can be used to interlock the filler material and/or second substrate to the first substrate using any of the methods described in this specification.


Various combinations of materials may serve as the filler material, or the first and second substrate. Suitable materials include a difference in melting temperature, density, and/or hardness of up to about 50%, such as from 2-20%, including at least about 10%. In one embodiment, materials that have a higher melting temperature or that are denser or harder serve as the first substrate, and materials that have a lower melting temperature or are less dense or lighter serve as the filler material and/or second substrate.


Materials that may serve as the filler material or as the first and second substrate may include metals and metallic materials, polymers and polymeric materials, ceramics and ceramic materials, as well as combinations of these materials. Metal matrix and polymer matrix composites, as well as metal to polymer joints are also included within the scope of the invention. The filler material, and the first and second substrate may include without limitation metal-metal combinations, polymer-polymer combinations, metal-polymer combinations, metal-ceramic combinations, and polymer-ceramic combinations. The material of the first substrate should have a machinable surface for forming the described grooves. In one particular embodiment, the first and second substrates and/or the filler material are metal or metallic. The filer material, or the first substrate and second substrate may be independently selected from any metal, including for example steel, Al, Ni, Cr, Cu, Co, Au, Ag, Mg, Cd, Pb, Pt, Ti, Zn, Fe, Nb, Ta, Mo, W, or an alloy comprising one or more of these metals. In embodiments, the first substrate and second substrate may be provided as sheet metal or metallic plates in a variety of dimensions for joining, including with a width and/or length of from about 1 inch to about 20 feet, such as for example 2′×2′, 2′×3′, 2′×4′, 3′×4′, 4′×4, 5′×5, 6′×4′, and the like. The size of the sheets is highly dependent on and can fit any desired application. Depths of the substrates as described above may be on the order of micrometers to centimeters.


In one embodiment, the first substrate has a density in the range of 7.75-8.10 g/cm3, a thermal expansion of 9.0-20.7 10−6/k, a melting point in the range of 1371-1454° C., a tensile strength of 515-827 MPa, and a hardness of 137-595 Brinell, and the filler material and/or second substrate has a density in the range of 2.50-3.00 g/cm3, a thermal expansion in the range of 20.4-25.0 10−6/k, a melting point in the range of 600-700° C., a tensile strength of 310-350 MPa, and a hardness of about 85-95 Brinell. However, these values are merely illustrative and exemplary. A skilled artisan can identify materials with desired properties for particular applications.


In these additive friction stir process embodiments, the filler material (for example, solid bar or powder) can be fed through the rotating additive friction stir tool where frictional and adiabatic heating occurs at the filler/substrate interface due to the rotational motion of the filler and the downward force applied. The frictional and adiabatic heating that occurs at the interface results in a severe plastic deformation at the tool-metal interface. In embodiments, as the friction stir tool moves along the along a vector overlying the grooves (or with any relative motion between the substrate and tool), the plasticized metal from the filler material and/or second substrate can be extruded under the rotating shoulder of the tool into the grooves of the first substrate. In embodiments, the rotating additive friction stir tool can contact the grooved surface of the first substrate directly to deposit the filler/substrate into the groove directly and deform the groove, thereby locking the deposited material into the grooves.


The filler material may be of a similar or dissimilar material as that of the first substrate and/or second substrate materials. In a particular embodiment, the filler material is a metallic material. Non-limiting examples of metallic materials useful as a filler material include steel, Al, Ni, Cr, Cu, Co, Au, Ag, Mg, Cd, Pb, Pt, Ti, Zn, Fe, Nb, Ta, Mo, W, as well as alloys of two or more of these metals and the like. In another embodiment, the filler material is a polymeric material. Non-limiting examples of polymeric materials useful as a filler material include polyolefins, polyesters, nylons, vinyls, polyvinyls, acrylics, polyacrylics, polycarbonates, polystyrenes, polyurethanes, and the like. In still yet another embodiment, the filler material is a composite material comprising at least one metallic material and at least one polymeric material. In other embodiments, multiple material combinations may be used for producing a composite at the interface.


In one embodiment, the filler material is the same as the second substrate. The filler material may be deposited on top of a sheet material comprising the second substrate as in the first embodiment or may be deposited directly from the tool on top of the first substrate as in the second embodiment.


The filler materials can be in several forms, including but not limited to: 1) metal powder or rod of a single composition; 2) matrix metal and reinforcement powders can be mixed and used as feed material; or 3) a solid rod of matrix can be bored (e.g., to create a tube or other hollow cylinder type structure) and filled with reinforcement powder, or mixtures of metal matric composite and reinforcement material. In the latter, mixing of the matrix and reinforcement can occur further during the fabrication process. In embodiments, the filler material may be a solid metal rod. In one embodiment, the filler material is aluminum.


In embodiments, the filler material is joined with a substrate using frictional heating and compressive loading of the filler material against the substrate and a translation of the rotating friction tool. The filler material may be a consumable material, meaning as frictional heating and compressive loading are applied during the process, the filler material is consumed from its original form and is applied to the substrate. Such consumable materials can be in any form including powders, pellets, rods, and powdered-filled cylinders, to name a few. As the applied load is increased, the filler material and substrate at the tool-substrate interface become malleable as a result of frictional and adiabatic heating and are caused to bond together under the compressive load. In a first embodiment, the deformed metal is then extruded into the grooves of the first substrate below the second substrate. In a second embodiment, the tool touches the groove pattern directly and deposits the filler material into the grooves.


The rotating additive friction stir tool may take a variety of forms. For example, the tool can be configured as described in any of U.S. Published Application Nos. 2008/0041921, 2010/0285207, 2012/0009339, and 2012/0279441, 2012/0279442, as well as International Patent Application Publication No. WO2013/002869. Friction-based fabrication tooling for performing methods of the invention are preferably designed or configured to allow for a filler material to be fed through or otherwise disposed through an internal portion of a non-consumable member, which may be referred to as a throat, neck, center, interior, or through hole disposed through opposing ends of the tool. This region of the tool can be configured with a non-circular through-hole shape. Various interior geometries for the tooling are possible. With a non-circular geometry, the filler material is compelled or caused to rotate at the same angular velocity as the non-consumable portion of the tool due to normal forces being exerted by the tool at the surface of the tool throat against the feedstock. Such geometries may include a square through-hole and an elliptical through-hole as examples. In configurations where only tangential forces can be expected to be exerted on the surface of the filler material by the internal surface of the throat of the tool, the feed stock will not be caused to rotate at the same angular velocity as the tool. Such an embodiment may include a circular geometry for the cross-section of the tool in combination with detached or loosely attached feedstock, which would be expected to result in the filler material and tool rotating at different velocities. As used in this disclosure, the terms “additive friction-stir tool”, “friction-stir tool”, “non-consumable friction-stir tool”, and “rotating non-consumable friction-stir tool” may be used interchangeably.


In embodiments the throat of the tool may be shaped with a non-circular cross-sectional shape. Further desired are tooling wherein the throat of the tool is shaped to exert normal forces on a solid, powder, or powder-filled tube type filler material disposed therein. Embodiments may also include features to ensure the frictional heating and compressive loading are of a degree sufficient to enable mixing of dispensed filler material with material of the substrate at a filler-substrate interface.


More specifically, the magnitude of force transferred from the rotating tool to the filler material is dependent on the coefficient of friction between the two. Thus, if the coefficient of friction is significantly low and the inertial force required to induce rotation of the filler material is significantly high, then the tool can rotate without inducing rotation (or with inducing rotation at a lower speed than the tool) in the cylindrical filler material. Under some circumstances during operation, differences in rotational velocity between the tool and the filler within the tool can lead to some filler material being deposited inside the tool, an accumulation of which can be problematic. Having the specific interior tool geometries described in this disclosure can reduce this issue, such as appropriately sized square-square or elliptical-elliptical shaped filler-dispenser geometries. Another way of reducing the difference in rotational velocity between the tool and the filler material is to manufacture filler material rods to fit tightly within the throat of the tool, or to otherwise tightly pack the filler material into the throat of the tool.


Any shape of the cross section of the interior of the tool that is capable of exerting normal forces on a filler material within the tool can be used. The throat surface geometry and the filler material geometry can be configured to provide for engagement and disengagement of the tool and filler material, interlocking of the tool and feed material, attachment of the tool and feed material, whether temporary or permanent, or any configuration that allows for the filler material to dependently rotate with the tool.


The interior surface shape of the tool (the throat) and the corresponding shape of the filler material may not be critical and can be constructed in a manner suitable for a particular application. Shapes of these surfaces can include, but are by no means limited to, square, rectangular, elliptical, oval, triangular, or typically any non-circular polygon. Additional shapes may include more distinctive shapes such as a star, daisy, key and key-hole, diamond, to name a few. Indeed, the shape of the outside surface of the filler material need not be the same type of shape as the surface of the throat of the tool. For example, there may be advantages from having a filler material rod with a square cross-section for insertion into a tool throat having a rectangular cross-section, or vice-versa where a filler material rod having a rectangular cross-section could be placed within a tool throat having a square cross-section in which the corners of the filler material rod could contact the sides of the square throat instead of sides contacting sides. Particular applications may call for more or less forces to be exerted on the filler material within the throat during operation of the tool. With concentric shapes and very close tolerance between the filler material and the tool certain advantages may be realized. Additionally, different shapes may be more suitable for different applications or may be highly desired due to their ease of manufacturing both the interior of the tool and corresponding filler material rods. One of ordinary skill in the art, with the benefit of this disclosure, would know the appropriate shapes to use for a particular application.


Additional embodiments of additive friction stir tools according to the invention include a tool with one or more pins or projections. The one or more pins may be used to penetrate into the substrate during the metal joining process. However, in other embodiments, the additive friction stir tool has no pin capable of penetrating into the substrate.


Additional embodiments of additive friction stir tools according to the invention can include a tool with a throat, where the filler material and throat are operably configured to provide for continuous feeding of the filler material through the throat of the stirring tool. In embodiments, the filler material is a powder, the throat of the tool is a hollow cylinder, and an auger shaped member disposed within the throat of the tool is used to force powder material through the throat of the tool onto the substrate. The filler material can be delivered by pulling or pushing the filler material through the throat of the stirring tool.


Additional embodiments can comprise an additive friction stir tool comprising: a non-consumable body formed from material capable of resisting deformation when subject to frictional heating and compressive loading; a throat with an internal shape defining a passageway lengthwise through the non-consumable body; an auger disposed within the tool throat with means for rotating the auger at a different velocity than the tool and for pushing powdered filler material through the tool throat; whereby the non-consumable body is operably configured for imposing frictional and adiabatic heating and compressive loading of the filler material against a substrate resulting in plasticizing of the filler material and substrate.


In embodiments, the tool and auger preferably rotate relative to the substrate. In further embodiments, the tool and auger rotate relative to one another, i.e., there is a difference in rotational velocity between the auger and the tool body. There may be some relative rotation between the filler material and the substrate, tool, or auger. The filler material and tool are preferably not attached to one another to allow for continuous or semi-continuous feeding or deposition of the filler material through the throat of the tool.


For example, the filler material to be joined with the substrate may be applied to the substrate surface using a “push” method, where a rotating-plunging tool, e.g., auger, pushes the filler material through the rotating tool, such as a spindle. Feed material can be introduced to the tool in various ways, including by providing an infinite amount of filler material into the tool body from a refillable container in operable communication with the tool.


In embodiments, the filler material is a powdered solid and is fed through the tool body using an auger shaped plunging tool (e.g., a threaded member). In such an embodiment, the plunging tool may or may not be designed to move or “plunge” in a direction toward the substrate. For example, the threaded configuration of the auger itself is capable of providing sufficient force on the powdered feed material to direct the filler material toward the substrate for deposition, without needing vertical movement of the auger relative to the tool.


As the spindle and plunging tool rotate, compressive loading and frictional heating of the filler material can be performed by pressing the filler material into the substrate surface with the downward force (force toward substrate) and rotating speed of the additive friction stir tool.


During the metal joining process, it is preferred that the spindle rotate at a slightly slower rate than the auger. Alternatively, in embodiments, the spindle can also be caused to rotate faster than the auger. What is important in embodiments is that there is relative rotation between the spindle and the auger during application of the filler material. Due to the difference in rotational velocities, the threaded portion of the auger provides means for pushing the filler material through the tool body to force the material out of the tool toward the substrate. The threads impart a force on the feedstock that pushes the feed material toward the substrate much like a linear actuator or pneumatic cylinder or other mechanical force pushing on a surface of the feedstock. Even further, it may be desired in some applications to alter the rotational velocity of the tool body and/or auger during deposition of the filler material.


Deposition rate of the filler material on the substrate can be adjusted by varying parameters such as the difference in rotational velocity between the auger screw and the spindle, or modifying the pitch of the threads on the auger. If desired, for particular applications it may be warranted to control filler material temperature inside or outside of the tool body. Such thermally induced softening of the filler material provides means to increase the rate of application of the material.


In the context of this specification, the terms “filler material,” “consumable material,” “feed material,” “feedstock” and the like may be used interchangeably to refer to the material that is applied to the substrate from the additive friction fabrication tooling. In an embodiment, a powder filler material is used in combination with an auger disposed in the tool throat for applying a constant displacement to the filler material within the throat.


The filler material (for example, powder or solid feedstock) can be fed through the rotating spindle where frictional heating occurs at the filler/substrate interface due to the rotational motion of the filler and the downward force applied. The frictional and adiabatic heating that occurs at the interface acts to plasticize the substrate and filler material at the interface resulting in a metallurgical bond between the substrate and filler.


A mechanism as shown in FIG. 3 was conceived to feed powder into the spindle and force it out of the spindle while ensuring the filler is keyed into the spindle. This system utilizes an auger screw 17 to force powder through the spindle at a defined rate, which is one means capable of accomplishing this purpose. Additional methods of feeding solid stock keyed into the orientation of the spindle and rotating at the exact rate of the spindle are conceivable. For example, force can be applied to the filler material using a metal rolling mill type mechanism which is rotating with the spindle.


In such an embodiment, the spindle is spinning at a desired rotational velocity and the auger screw is driven at a different rotational speed in the same rotational direction which acts to force material out of the spindle. As shown in FIG. 3, the angular rotational speed or velocity of the friction stir tool is identified as ω1 and the angular rotational velocity of the auger is identified as ω2. In the context of this specification, the terms “rotational speed,” “rotational velocity,” “angular speed,” and “angular velocity” can be used interchangeably and refer to the angular velocity of a component of the tool during use. The auger screw can rotate at a slower speed than the spindle, or in preferred embodiments the auger screw can rotate faster than the spindle. What is important is that there is relative rotation between the spindle and auger to cause filler material to be forced through the throat of the tool.


The pitch of the threaded auger screw and the volumetric pitch rate of the screw will affect the deposition rate under certain circumstances, and can be modified to accomplish particular goals. It is within the skill of the art to modify the pitch of the threads on the auger to obtain a certain desired result. The terms “tool,” “friction stir tool,” “spindle,” “tool body,” and the like as used in this specification may be used to refer to the outer portion of the tool body, which comprises a passageway lengthwise through the tool for holding and dispensing feed material through the tool. This passageway, or throat, is generally the shape of a hollow cylinder. The hollow cylinder can be configured to have a wider opening at the top of the tool for accommodating the auger and powder material and a smaller opening at the base of the tool where the feed material is dispensed from the tool. Thus, the shape of the throat of the tool need not be consistent throughout the length of the tool throat and can be configured to converge from one lengthwise end of the tool to the other. As shown in FIG. 3, the throat of the tool can comprise a first region which is the shape of a hollow cylinder of a first diameter. This region can transition into a second region which is the shape of a hollow cylinder of a second smaller diameter. The transition region can be a converging hollow cylinder or funnel shaped region to allow the first and second region to be connected seamlessly.


Disposed within the tool body is an auger 17. In the context of this specification, the terms “auger,” “screw,” and “plunger” may be used to refer to a component of the tool that is disposed within the tool throat for pushing or pulling material through the throat. Also within this specification, the auger can be considered a component of the friction stir tool body. The auger can have the general shape of a screw with threads, as shown in FIG. 3, or can be shaped in a spiral configuration similar to a spring. When disposed within the tool throat, there may be clearance between the auger 17 and the inside surface of the tool throat to allow for the passage of feed material between the auger and the throat. The inside of the surface of the tool throat includes sleeve 19 and bore 21. In other embodiments, there is only enough space to allow for rotation of the auger without interference from the surface of the throat. Preferably, the auger and tool body or spindle are not attached to one another. Each is operably connected with means for rotating and translating the components relative to a substrate surface, such that the auger and tool can rotate at different speeds but translate relative to the substrate at the same speed. It is preferred to keep the auger disposed within the tool throat in a manner such that there is no relative translational movement between the auger and tool body.


Powdered materials can be fed into the top of the spindle using a fluidized powder delivery system. Any type of powder delivery system can be used in connection with the tools and systems of the present invention. For example, a gravity-fed powder feeder system can be used, such as a hopper. One such feed system is the Palmer P-Series Volumetric Powder Feeder from Palmer Manufacturing of Springfield Ohio, which is capable of delivering feed material from 0.1-140 cu. ft. per hour, and which comprises a flexible polyurethane hopper, stainless steel massaging paddles, 304 stainless steel feed tube and auger, 90-volt DC gearhead drive motor, flexible roller chain drive system, sealed drive train and cabinet, and solid state control and pushbutton controls. The feed system preferably comprises a reservoir for holding powder filler material, a mixer for mixing powder(s) added to the reservoir, and a passageway for delivering feed material from the hopper to the throat of the tool body. As feed material is dispensed into and from the tool, more feed material is delivered into the tool from the hopper. In this manner, the feed material is continuously or semi-continuously delivered. The gravity-fed dispensing systems allow for feed material to automatically be dispensed from the hopper to the friction stir tool during use as soon as material within the tool is dispensed.


In embodiments, a mix of powder types can be added to the hopper which is operably connected with the stir tool. Alternatively, several different types of powder can be added individually to the hopper, then mixed within the hopper and dispensed as a mixture to the friction stir tool during use. For example a metal powder and ceramic powder could be fed into the spindle at the same time, from the same or separate hoppers, and upon consolidation/deposition the filler would be a metal matrix composite (MMC). As used herein, the term “metal matrix composite” means a material having a continuous metallic phase having another discontinuous phase dispersed therein. The metal matrix may comprise a pure metal, metal alloy or intermetallic. The discontinuous phase may comprise a ceramic such as a carbide, boride, nitride and/or oxide. Some examples of discontinuous ceramic phases include SiC, TiB2 and Al2O3. The discontinuous phase may also comprise an intermetallic such as various types of aluminides and the like. Titanium aluminides such as TiAl and nickel aluminides such as Ni3Al may be provided as the discontinuous phase. The metal matrix may typically comprise Al, Cu, Ni, Mg, Ti, Fe and the like.


Example


FIG. 4 is a macrograph image showing a cross section of an article of manufacture comprising two different metals (molybdenum and copper) in an interlocking configuration prepared according to an embodiment of the invention. The substrate comprises molybdenum and multiple grooves in the surface of the substrate. The cross-sectional shape of the grooves in the substrate is rectangular. Copper was added to the surface of the substrate using an additive friction stir tool. At least one side of the grooves was deformed during the additive friction stir process to provide for a mechanical interlocking configuration between the molybdenum substrate and the copper coating. In the area of the joint between the molybdenum and copper, each of the copper and molybdenum have two-dimensional projections into this area as shown. Some of the two-dimensional projections are of convex polygon shape and some are of concave polygon shape. Other combinations of materials can also be used, including the same material as both the substrate and the coating. Additionally, the following combinations, W—Cu, Ta—Cu, Ti—Al, Fe (steel-Al), Al—Cu, Fe—Mg, Ti—Mg, and Al—Mg, are also possible for example for different substrate and coating material.


The present invention has been described with reference to particular embodiments having various features. In light of the disclosure provided above, it will be apparent to those skilled in the art that various modifications and variations can be made in the practice of the present invention without departing from the scope or spirit of the invention. One skilled in the art will recognize that the disclosed features may be used singularly, in any combination, or omitted based on the requirements and specifications of a given application or design. When an embodiment refers to “comprising” certain features, it is to be understood that the embodiments can alternatively “consist of” or “consist essentially of” any one or more of the features. Other embodiments of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the invention.


It is noted in particular that where a range of values is provided in this specification, each value between the upper and lower limits of that range is also specifically disclosed. The upper and lower limits of these smaller ranges may independently be included or excluded in the range as well. The singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. It is intended that the specification and examples be considered as exemplary in nature and that variations that do not depart from the essence of the invention fall within the scope of the invention. Further, all of the references cited in this disclosure are each individually incorporated by reference herein in their entireties and as such are intended to provide an efficient way of supplementing the enabling disclosure of this invention as well as provide background detailing the level of ordinary skill in the art.

Claims
  • 1. An additive friction stir method comprising: providing a first substrate with a plurality of grooves;rotating an additive friction-stir tool relative to the first substrate;translating the additive friction-stir tool relative to the first substrate along a vector that overlies the plurality of grooves;feeding a filler material through an opening of the additive friction-stir tool; anddepositing the filler material into one or more of the plurality of grooves of the first substrate, without the opening of the friction-stir tool penetrating any substrate.
  • 2. The method of claim 1, wherein one or more of the plurality of grooves has a groove opening, a base, and parallel sidewalls extending or sloping from the groove opening to the base; or wherein one or more of the plurality of grooves has a groove opening, a base, and perpendicular sidewalls extending from the groove opening to the base; orwherein one or more of the plurality of grooves has a groove opening, a base, and sidewalls sloping from the groove opening to the base; orwherein one or more of the plurality of grooves has a groove opening, a base, and sidewalls sloping in opposite directions from the groove opening to the base.
  • 3. The method of claim 2, wherein one or more of the plurality of grooves has a groove opening, a base, and sidewalls sloping in opposite directions from the groove opening to the base and the groove opening has a width larger than a width of the base.
  • 4. The method of claim 2, wherein one or more of the plurality of grooves has a groove opening, a base, and sidewalls sloping in opposite directions from the groove opening to the base and the groove opening has a width smaller than a width of the base to provide one or more of the plurality of grooves with a dovetail shaped cross section.
  • 5. The method of claim 2, further comprising deforming the groove opening to provide for a mechanical lock between the filler material and one or more of the plurality of grooves of the first substrate wherein one or more of the plurality of grooves has a groove opening, a base, and perpendicular sidewalls extending from the groove opening to the base.
  • 6. The method of claim 5, wherein the deforming is performed during the depositing of the filler material into one of more of the plurality of grooves of the first substrate.
  • 7. The method of claim 4, further comprising deforming the groove opening to provide for a mechanical lock between the filler material and one or more of the plurality of grooves of the first substrate.
  • 8. The method of claim 7, wherein the deforming of the groove opening is performed during the depositing of the filler material into one or more of the plurality of grooves of the first substrate.
  • 9. The method of claim 1, wherein the first substrate and the filler material are each metal.
  • 10. The method of claim 1, wherein the first substrate and/or the filler material are independently chosen from metals, metallic materials, metal matrix composites (MMCs), polymers, polymeric materials, ceramics, ceramic materials, steel, Al, Ni, Cr, Cu, Co, Au, Ag, Mg, Cd, Pb, Pt, Ti, Zn, Fe, Nb, Ta, Mo, W, or an alloy comprising one or more of these metals, as well as combinations of any of these materials.
  • 11. The method of claim 10, wherein the first substrate and/or the filler material are a metal matrix composite comprising a metal matrix and a ceramic phase, wherein the metal matrix comprises one or more of a metal, a metal alloy, or an intermetallic and the ceramic phase comprises a ceramic.
  • 12. The method of claim 1, wherein the filler material is a powder, pellet, rod, or powdered-filled cylinder.
  • 13. The method of claim 1, further comprising providing a second substrate and deforming and depositing at least a portion of the second substrate into one or more of the plurality of grooves.
  • 14. An additive friction stir method comprising: providing a substrate with one or more grooves having a groove opening, a base, and a first and second sidewall extending from the groove opening to the base;rotating an additive friction-stir tool relative to the substrate;feeding a filler material through an opening of the additive friction-stir tool;translating the additive friction-stir tool relative to the substrate and across the one or more grooves from the first sidewall to the second sidewall of the one or more grooves; anddepositing the filler material into the one or more grooves without the opening of the friction-stir tool penetrating any substrate.
  • 15. The method of claim 14, further comprising deforming one or more of the groove openings of the substrate during the depositing of the filler material.
  • 16. An additive friction stir method comprising: providing a substrate with one or more grooves;rotating and translating an additive friction-stir tool relative to the substrate;feeding a filler material through an opening of the additive friction-stir tool; anddepositing the filler material into one or more of the one or more grooves to form a joint, without the opening of the friction-stir tool penetrating any substrate, and wherein a cross section of the joint reveals one side of the joint having at least one two-dimensional concave polygon shaped projection into the joint.
  • 17. The method of claim 1, wherein the first substrate comprises a first material and the filler material comprises a second material that is different from the first material.
  • 18. The method of claim 14, wherein the substrate comprises a first material and the filler material comprises a second material that is different from the first material.
  • 19. The method of claim 16, wherein the substrate comprises a first material and the filler material comprises a second material that is different from the first material.
  • 20. The method of claim 13, wherein the second substrate is provided as a sheet of metal or as a metal plate.
  • 21. The method of claim 1, wherein, as a result of the depositing of the filler material, one or more of the plurality of grooves of the first substrate is deformed or undeformed.
CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a Continuation-in-Part (CIP) of U.S. patent application Ser. No. 14/573,430 filed Dec. 17, 2014, the disclosure of which is incorporated herein by reference in its entirety.

US Referenced Citations (263)
Number Name Date Kind
3217957 Jarvie et al. Nov 1965 A
3279971 Gardener Oct 1966 A
3292838 Farley Dec 1966 A
3418196 Luc Dec 1968 A
3444611 Bogart May 1969 A
3455015 Daniels Henricus et al. Jul 1969 A
3466737 Hanink Sep 1969 A
3495321 Shaff Feb 1970 A
3537172 Voznesensky Valentin et al. Nov 1970 A
3831262 Luc Aug 1974 A
3899377 Luc Aug 1975 A
3949896 Luc Apr 1976 A
4023613 Uebayasi et al. May 1977 A
4106167 Luc Aug 1978 A
4144110 Luc Mar 1979 A
4491001 Yoshida et al. Jan 1985 A
4625095 Das Nov 1986 A
4824295 Sharpless Apr 1989 A
4930675 Bedford et al. Jun 1990 A
4959241 Thomas et al. Sep 1990 A
5056971 Sartori Oct 1991 A
5249778 Steichert et al. Oct 1993 A
5262123 Thomas et al. Nov 1993 A
5330160 Eisermann et al. Jul 1994 A
5460317 Thomas et al. Oct 1995 A
5469617 Thomas et al. Nov 1995 A
5611479 Rosen Mar 1997 A
5637836 Nakagawa et al. Jun 1997 A
5697511 Bampton Dec 1997 A
5697544 Wykes Dec 1997 A
5713507 Holt et al. Feb 1998 A
5718366 Colligan Feb 1998 A
5769306 Colligan Jun 1998 A
5794835 Colligan et al. Aug 1998 A
5813592 Midling Ole et al. Sep 1998 A
5826664 Richardson Oct 1998 A
5893507 Ding et al. Apr 1999 A
5971247 Gentry Oct 1999 A
5971252 Rosen et al. Oct 1999 A
5975406 Mahoney et al. Nov 1999 A
6021821 Wegman Feb 2000 A
6024141 Wegman Feb 2000 A
6029879 Cocks Feb 2000 A
6045027 Rosen et al. Apr 2000 A
6045028 Martin et al. Apr 2000 A
6050474 Aota et al. Apr 2000 A
6050475 Kinton et al. Apr 2000 A
6051325 Talwar et al. Apr 2000 A
6053391 Heideman et al. Apr 2000 A
6070784 Holt et al. Jun 2000 A
6119624 Morikawa et al. Sep 2000 A
6138895 Oelgoetz et al. Oct 2000 A
6168066 Arbegast Jan 2001 B1
6168067 Waldron et al. Jan 2001 B1
6173880 Ding et al. Jan 2001 B1
6193137 Ezumi et al. Feb 2001 B1
6199745 Campbell et al. Mar 2001 B1
6206268 Mahoney Mar 2001 B1
6213379 Takeshita et al. Apr 2001 B1
6227430 Rosen et al. May 2001 B1
6230957 Arbegast et al. May 2001 B1
6237829 Aota et al. May 2001 B1
6237835 Litwinski et al. May 2001 B1
6247633 White et al. Jun 2001 B1
6247634 Whitehouse Jun 2001 B1
6250037 Ezumi et al. Jun 2001 B1
6257479 Litwinski et al. Jul 2001 B1
6259052 Ding et al. Jul 2001 B1
6264088 Larsson Jul 2001 B1
6273323 Ezumi et al. Aug 2001 B1
6276591 Kawasaki et al. Aug 2001 B1
6290117 Kawasaki et al. Sep 2001 B1
6299048 Larsson Oct 2001 B1
6299050 Okamura et al. Oct 2001 B1
6302315 Thompson Oct 2001 B1
6305866 Aota et al. Oct 2001 B1
6311889 Ezumi et al. Nov 2001 B1
6315187 Satou et al. Nov 2001 B1
6321975 Kawasaki et al. Nov 2001 B1
6325273 Boon et al. Dec 2001 B1
6325274 Ezumi et al. Dec 2001 B2
6328261 Wollaston et al. Dec 2001 B1
6352193 Bellino et al. Mar 2002 B1
6354483 Ezumi et al. Mar 2002 B1
6360937 De Koning Mar 2002 B1
6364197 Oelgoetz et al. Apr 2002 B1
6367681 Waldron et al. Apr 2002 B1
6378264 Kawasaki et al. Apr 2002 B1
6378754 Aota et al. Apr 2002 B2
6382498 Aota et al. May 2002 B2
6386425 Kawasaki et al. May 2002 B2
6398883 Forrest et al. Jun 2002 B1
6413610 Nakamura et al. Jul 2002 B1
6419142 Larsson Jul 2002 B1
6419144 Aota et al. Jul 2002 B2
6421578 Adams et al. Jul 2002 B1
6422449 Ezumi et al. Jul 2002 B1
6450394 Wollaston et al. Sep 2002 B1
6450395 Weeks et al. Sep 2002 B1
6457629 White Oct 2002 B1
6460752 Waldron et al. Oct 2002 B1
6461072 Kawasaki et al. Oct 2002 B2
6464127 Litwinski et al. Oct 2002 B2
6468067 Ikegami Oct 2002 B1
6471112 Satou et al. Oct 2002 B2
6474533 Ezumi et al. Nov 2002 B1
6484924 Forrest Nov 2002 B1
6494011 Ezumi et al. Dec 2002 B2
6497355 Ding et al. Dec 2002 B1
6499649 Sayama et al. Dec 2002 B2
6502739 Ezumi et al. Jan 2003 B2
6513698 Ezumi et al. Feb 2003 B2
6516992 Colligan Feb 2003 B1
6527470 Ezumi et al. Mar 2003 B2
6536651 Ezumi Mar 2003 B2
6543671 Hatten Apr 2003 B2
6572007 Stevenson et al. Jun 2003 B1
6582832 Kawasaki et al. Jun 2003 B2
6599641 Nakamura et al. Jul 2003 B1
6648206 Nelson et al. Nov 2003 B2
6669075 Colligan Dec 2003 B2
6676004 Trapp et al. Jan 2004 B1
6722556 Schilling et al. Apr 2004 B2
6732901 Nelson et al. May 2004 B2
6745929 Ezumi et al. Jun 2004 B1
6758382 Carter Jul 2004 B1
6779704 Nelson et al. Aug 2004 B2
6811632 Nelson et al. Nov 2004 B2
6866181 Aota et al. Mar 2005 B2
6908690 Waldron et al. Jun 2005 B2
6953140 Park et al. Oct 2005 B2
7036708 Park et al. May 2006 B2
7066375 Bolser Jun 2006 B2
7115324 Stol et al. Oct 2006 B1
7124929 Nelson et al. Oct 2006 B2
7152776 Nelson et al. Dec 2006 B2
7156276 Slattery Jan 2007 B2
7163136 Hempstead et al. Jan 2007 B2
7240821 Talwar Jul 2007 B2
7597236 Tolle et al. Oct 2009 B2
7608296 Packer et al. Oct 2009 B2
7624910 Barnes et al. Dec 2009 B2
7661572 Nelson et al. Feb 2010 B2
7732033 Van Aken et al. Jun 2010 B2
7918379 Fujii Apr 2011 B2
7971770 Nakagawa et al. Jul 2011 B2
7992759 Steel et al. Aug 2011 B2
8052034 Fleming et al. Nov 2011 B2
8061579 Feng et al. Nov 2011 B2
8100316 Goehlich et al. Jan 2012 B2
8220693 Krajewski Jul 2012 B2
8397974 Schultz et al. Mar 2013 B2
8464926 Kou et al. Jun 2013 B2
8479970 Ishibashi et al. Jul 2013 B2
8632850 Schultz et al. Jan 2014 B2
8636194 Schultz et al. Jan 2014 B2
8678268 Obadtich Mar 2014 B1
8714431 Roos et al. May 2014 B2
8875976 Schultz et al. Nov 2014 B2
8893954 Schultz et al. Nov 2014 B2
9205578 Schultz et al. Dec 2015 B2
9266191 Kandasamy et al. Feb 2016 B2
20010011674 Ezumi Aug 2001 A1
20020011509 Nelson et al. Jan 2002 A1
20020014516 Nelson et al. Feb 2002 A1
20020168466 Tapphorn et al. Nov 2002 A1
20020179682 Schilling et al. Dec 2002 A1
20030010805 Nelson et al. Jan 2003 A1
20030042292 Hatten et al. Mar 2003 A1
20030075584 Sarik et al. Apr 2003 A1
20030098336 Yamashita May 2003 A1
20030111147 Keener et al. Jun 2003 A1
20030111514 Miyanagi et al. Jun 2003 A1
20030192941 Ishida et al. Oct 2003 A1
20030218052 Litwinski Nov 2003 A2
20040003911 Vining et al. Jan 2004 A1
20040055349 El-Soudani Mar 2004 A1
20040057782 Okamoto et al. Mar 2004 A1
20040118899 Aota et al. Jun 2004 A1
20040134972 Nelson et al. Jul 2004 A1
20040149807 Schilling Aug 2004 A1
20040155093 Nelson et al. Aug 2004 A1
20040159696 Mahoney Aug 2004 A1
20040195291 Andersson et al. Oct 2004 A1
20040265503 Clayton et al. Dec 2004 A1
20050006439 Packer et al. Jan 2005 A1
20050045694 Subramanian et al. Mar 2005 A1
20050045695 Subramanian et al. Mar 2005 A1
20050051599 Park et al. Mar 2005 A1
20050060888 Park et al. Mar 2005 A1
20050121497 Fuller et al. Jun 2005 A1
20050127139 Slattery et al. Jun 2005 A1
20050210820 Tanaka et al. Sep 2005 A1
20050242158 Bolser Nov 2005 A1
20050247756 Frazer Nov 2005 A1
20050254955 Helder et al. Nov 2005 A1
20060016854 Slattery Jan 2006 A1
20060032891 Flak et al. Feb 2006 A1
20060043151 Stol et al. Mar 2006 A1
20060060635 Slattery et al. Mar 2006 A1
20060096740 Zheng May 2006 A1
20060208034 Packer et al. Sep 2006 A1
20060289603 Zettler et al. Dec 2006 A1
20070040006 Charles et al. Feb 2007 A1
20070044406 Van Aken et al. Mar 2007 A1
20070075121 Slattery Apr 2007 A1
20070102492 Nelson et al. May 2007 A1
20070138236 Agarwal et al. Jun 2007 A1
20070187465 Eyre et al. Aug 2007 A1
20070215675 Barnes Sep 2007 A1
20070241164 Barnes et al. Oct 2007 A1
20070295781 Hunt et al. Dec 2007 A1
20070297935 Langan et al. Dec 2007 A1
20080006678 Packer et al. Jan 2008 A1
20080023524 Ohashi et al. Jan 2008 A1
20080041921 Creehan et al. Feb 2008 A1
20080047222 Barnes Feb 2008 A1
20080135405 Hori et al. Jun 2008 A1
20090090700 Sato et al. Apr 2009 A1
20090152328 Okamoto et al. Jun 2009 A1
20090188101 Durandet et al. Jul 2009 A1
20090236028 Fukuda Sep 2009 A1
20090236403 Feng et al. Sep 2009 A1
20090258232 Brice Oct 2009 A1
20090266870 Yousefiani Oct 2009 A1
20100037998 Bray et al. Feb 2010 A1
20100065611 Fukuda Mar 2010 A1
20100068550 Watson et al. Mar 2010 A1
20100089976 Szymanski et al. Apr 2010 A1
20100089977 Chen et al. Apr 2010 A1
20100101768 Seo et al. Apr 2010 A1
20100146866 Nelson et al. Jun 2010 A1
20100176182 Hanlon Jul 2010 A1
20100252614 Fujii et al. Oct 2010 A1
20100258612 Kolbeck et al. Oct 2010 A1
20100282717 Ananthanarayanan Nov 2010 A1
20100284850 Hawk Nov 2010 A1
20100285207 Creehan et al. Nov 2010 A1
20100297469 Aota et al. Nov 2010 A1
20110062219 Bezaire et al. Mar 2011 A1
20110132968 Nakagawa Jun 2011 A1
20110132970 Nakagawa et al. Jun 2011 A1
20110227590 Killian et al. Sep 2011 A1
20110266330 Bruck Nov 2011 A1
20120009339 Creehan et al. Jan 2012 A1
20120114897 Thiagarajan et al. May 2012 A1
20120132342 Kato et al. May 2012 A1
20120202089 Hangai Aug 2012 A1
20120237788 Fujii et al. Sep 2012 A1
20120273113 Hovanski et al. Nov 2012 A1
20120279043 Carter Nov 2012 A1
20120279271 Carter Nov 2012 A1
20120279441 Creehan et al. Nov 2012 A1
20120279442 Creehan et al. Nov 2012 A1
20120325894 Chun et al. Dec 2012 A1
20140061185 Schindele Mar 2014 A1
20140130736 Schultz et al. May 2014 A1
20140134325 Schultz et al. May 2014 A1
20140166731 Seo et al. Jun 2014 A1
20140174344 Schultz et al. Jun 2014 A1
20150165546 Kandasamy et al. Jun 2015 A1
20160074958 Kandasamy et al. Mar 2016 A1
20160107262 Schultz et al. Apr 2016 A1
Foreign Referenced Citations (44)
Number Date Country
102120287 Jul 2013 CN
102120287 Jul 2013 CN
203738226 Jul 2014 CN
0453182 Oct 1991 EP
0458774 Nov 1991 EP
0458774 Nov 1991 EP
0410104 Jul 1993 EP
0597335 May 1994 EP
0597335 May 1994 EP
1206995 May 2002 EP
1543913 Aug 2007 EP
1790425 Oct 2011 EP
2783976 Oct 2014 EP
572789 Oct 1945 GB
1224891 Mar 1971 GB
2270864 Mar 1994 GB
2306366 May 1997 GB
10286682 Oct 1998 JP
11156561 Jun 1999 JP
11267857 Oct 1999 JP
2002153976 May 2002 JP
2002192358 Jul 2002 JP
2002256453 Sep 2002 JP
2002283069 Oct 2002 JP
2004025296 Jan 2004 JP
2004261859 Sep 2004 JP
2004298955 Oct 2004 JP
2007222925 Sep 2007 JP
2007283317 Nov 2007 JP
2008254047 Oct 2008 JP
2010149134 Jul 2010 JP
2010279958 Dec 2010 JP
2011056582 Mar 2011 JP
2013049091 Mar 2013 JP
101256970 Apr 2013 KR
101278097 Jun 2013 KR
1393566 May 1988 RU
1393566ABSTRACT May 1988 RU
266539 Nov 1976 SU
9310935 Jun 1993 WO
WO 0174525 Oct 2001 WO
WO 2011137300 Nov 2011 WO
2013002869 Jan 2013 WO
2013095031 Jun 2013 WO
Non-Patent Literature Citations (14)
Entry
Co-Pending U.S. Appl. No. 14/926,447, filed Oct. 29, 2015.
Berbon et al., Friction stir processing: a tool to homogenize nanocomposite aluminum alloys, Scripta Materialia, vol. 44, No. 1, pp. 61-66, Jan. 5, 2001.
Co-pending Application No. PCT/US12/32793 filed Apr. 9, 2012 (published as WO2013/002869 on Jan. 3, 2013).
Co-Pending U.S. Appl. No. 14,573,430, filed Dec. 17, 2014.
Co-Pending U.S. Appl. No. 14/640,077, filed Mar. 6, 2015.
Davis, JR, editor, Handbook of Thermal Spray Technology, ASM International (2004), pp. 138-139.
Friction Stir Tooling: Tool Materials and Designs, Chapter 2 in Friction Stir Welding and Processing, pp. 7-35, ASM International, Editors Rajiv S. Mishra & Murray W. Mahoney, 2007.
Geiger et al., “Friction stir knead welding of steel aluminum butt joints.” International Journal of Machine Tools & Manufacture, vol. 48, pp. 515-521, 2008.
International Preliminary Report on Patentability of International Application No. PCT/US2012/032793, Oct. 8, 2013, 7 pages.
International Search Report and Written Opinion of International Application No. PCT/US2012/032793, Dec. 18, 2012.
Kallee et al., “Friction stir welding—invention, innovations and applications.” INALCO 2001, 8th International Conference on Joints in Aluminium, Munich, Germany, 19 pages.
Metal-Matrix Composites (ASM Metals Handbook Online, ASM International, 2002), Introduction, Aluminum-Matrix Composites.
The American Welding Society. The Everyday Pocket Handbook on Welded Joint Details for Structural Applications. 2004.
Co-Pending U.S. Appl. No. 14/954,104, filed Nov. 30, 2015.
Related Publications (1)
Number Date Country
20160175982 A1 Jun 2016 US
Continuation in Parts (1)
Number Date Country
Parent 14573430 Dec 2014 US
Child 14643396 US