The present invention generally relates to a transparent hard coating and more particularly to a method and material for coating a lens or housing of portable electronic devices.
The market for personal portable electronic devices, for example, cell phones, laptop computers, personal digital assistants (PDAs), digital cameras, and music playback devices (MP3), is very competitive. Manufacturers, distributors, service providers, and third party providers have all attempted to find features that appeal to the consumer. Manufacturers are constantly improving their product with each model in the hopes it will appeal to the consumer more than a competitor's product. Many times these manufacturer's improvements do not relate directly to the functionality of the product.
The look and feel of personal portable electronics devices is now a key product differentiator and one of the most significant reasons that consumers choose specific models. From a business standpoint, outstanding designs (form and appearance) may increase market share and margin.
The widespread use of portable electronic devices such as cell phones, personal data assistants, and digital media players has resulted in two trends. The first trend is the use of larger displays and the increase in the use of glass or a thermoplastic as a transparent display cover. While these layers have excellent transparency and are physically strong, they suffer both aesthetic and functional degradation due to scratches, scuffing, abrasions and the like. The other trend is the use of very high gloss materials for the housing with a focus on the aesthetic appeal of the device, which suffers a similar aesthetic and functional degradation due to scratches, scuffing, abrasions and the like. This is particularly true for products which receive significant handling, such as persona data assistants (PDAs) and cell phones. This has led to the result that any type of scratches, scuffing, or abrasions is especially undesirable as it tends to be very noticeable and can degrade both the functional and aesthetic performance of the device. This degradation may also lead to breakage of the display cover.
An amorphous material is generally too soft to serve as a coating as it is susceptible to scratching. A crystalline material is harder (scratch resistant), but typically requires an undesirable high temperature during formation.
Many materials have been mentioned for use as hard coatings. A single layer ceramic coating including Al2O3, ZrO2, and DLC (amorphous diamond like carbon) is most common. Al2O3, commercially available as coatings of, for example, cutting tools, is hard and chemically inert, and is excellent as an anti-oxidation coating for high temperatures. It has a smooth surface with minimum friction and very low optical absorption in the visible range extending to ultraviolet. Corundum, the most stable phase of Al2O3, has a high hardness but requires a deposition temperature as high as 1000 degrees C., which is too high for coatings of electronic devices and leads to significant thermal stress. ZrO2 requires stabilization. DLC has issues with the ability to control bonding, adhesion to substrates, and absorption in the visible range. Composite layers include TiN+SiN which is not transparent, SiO2/resin which is a DVD coating, and Al2O3/SiO2/poly which is used on wood floors. Multilayer/Superlattice materials include SiON/polymer/SiON (an OLED encapsulation) as a permeation barrier and Ti/Zr/N (on cutting tools) which is non-transparent.
Typical films deposited at low temperatures are amorphous even though their crystalline phases have lower energy. High temperature is normally required to overcome this energy barrier to form crystalline phases.
Accordingly, it is desirable to provide a coating material that forms a crystalline phase at a low temperature, and is transparent. Furthermore, other desirable features and characteristics of the present invention will become apparent from the subsequent detailed description and the appended claims, taken in conjunction with the accompanying drawings and this background.
Embodiments of the present invention will hereinafter be described in conjunction with the following drawing figures, wherein like numerals denote like elements, and
The following detailed description is merely exemplary in nature and is not intended to limit the invention or the application and uses of the invention. Furthermore, there is no intention to be bound by any theory presented in the preceding background or the following detailed description.
An induced phase composite provides the required hardness for coating another material to protect against scratching while requiring a low processing temperature. The atomic bonding (length, direction, and type) dictates the hardness of the coating. In a first exemplary embodiment, a magnesium oxide (MgO) material may be disposed simultaneously with another transparent oxide at room temperatures to form a poly crystalline film or crystallites in an amorphous matrix on the substrate material. In a second exemplary embodiment, a thin layer of the MgO may be deposited on the substrate as a seed layer and a subsequent layer of the transparent oxide may be deposited on the MgO layer. The MgO layer crystallizes when formed and causes the transparent oxide to crystallize as it is formed.
Amorphous materials typically have higher energy than crystalline material. A high temperature is needed to overcome the energy barrier existing between the amorphous state and the crystalline state in order to convert the amorphous material to a crystalline material.
There are two methods disclosed herein to overcome this energy barrier. One method is to increase the energy of the film forming particles by, for example, plasma, ion assist, pulsed laser, and a substrate bias cathodic arc. A second method is to decrease the nucleation energy by providing a crystalline template by providing a seeding layer. A combination of these two methods may be used.
Referring to
The application of the transparent oxide 106 and the MgO material 108 is made at a temperature generally in the range of 20 to 300 degrees Centigrade and more preferably at room temperature (between 25 to 27 degrees Centigrade) to a thickness of between 100 nanometers to 5000 nanometers, and preferably to a thickness of about 500 nanometers. The transparent oxide 106 and MgO material 108 are applied wherein the MgO occupies approximately 5% to 95% by volume.
Though the transparent oxide 106 is amorphous when applied, it may crystallize in contact with the MgO material 108, or remain amorphous, resulting in a transparent composite material 112.
Referring to
The application of the transparent oxide 206 and the MgO material 208 is made at a temperature generally in the range of 20 to 50 degrees Centigrade and more preferably at room temperature (between 25 to 27 degrees Centigrade). The MgO material 208 generally has a thickness of between 1 nanometers and 1000 nanometers, and preferably has a thickness of about 50 nanometers. The transparent oxide 206 generally has a thickness of between 100 nanometers and 5000 nanometers, and preferably has a thickness of about 500 nanometers and a hardness above 10 GPa.
The MgO material 208 crystallizes when deposited. Though the transparent oxide 106 is amorphous when applied, it may crystallize in contact with the MgO material 108, resulting in transparent crystalline oxide/MgO layers 212, or form a crystallites-amorphous matrix.
The driving force for crystallization of an amorphous material comes from the lowering of the potential energy of the atoms or molecules when they form bonds to each other (the length, direction, and type of bonding determines hardness). Crystalline growth, by physical vapor transport for example, occurs when several atoms or molecules start forming clusters when the bulk free energy of the cluster is less than that of the host material. When the cluster has a radius greater than a critical radius, the cluster will increase in size by the addition of more atoms. The critical radius defines a critical energy barrier between the amorphous and crystalline states that must be overcome. The amorphous material may be converted to a crystalline material by overcoming the energy barrier by increasing the energy of the film forming particles, for example, by application of plasma, ion assist, a pulsed laser, or substrate bias cathodic arc. However, these methods are difficult to control and may not always overcome the energy barrier. Alternatively, the nucleation energy may be decreased by providing a crystalline template in accordance with the exemplary embodiments described herein.
This combination of materials, a first transparent oxide that crystallizes upon deposition at temperatures below 300 degrees Centigrade and a second transparent oxide having a hardness above 10 GPa, provides a high hardness for abrasion resistance, a low visible light absorption for optical transparency, and a low temperature (less than 300 degrees Centigrade) deposition.
While at least one exemplary embodiment has been presented in the foregoing detailed description, it should be appreciated that a vast number of variations exist. It should also be appreciated that the exemplary embodiment or exemplary embodiments are only examples, and are not intended to limit the scope, applicability, or configuration of the invention in any way. Rather, the foregoing detailed description will provide those skilled in the art with a convenient road map for implementing an exemplary embodiment of the invention, it being understood that various changes may be made in the function and arrangement of elements described in an exemplary embodiment without departing from the scope of the invention as set forth in the appended claims.