Inert dental glass

Description

[0001] The invention relates to the use of unreactive glasses in dental materials, in particular dental cements, preferably polyelectrolyte cements, which can be used without pretreatment of the glass powder surface.

[0002] In the dental sector, glasses are used in particular for filling materials and for the fixing cements and composites for crowns, bridges and inlays.

[0003] Reactive glasses, i.e. glasses which participate in a chemical reaction, are used in what are known as polyelectrolyte cements, in particular glass-ionomer cements.

[0004] Polyelectrolyte cements of this type generally comprise three constituents, namely a polyacid, in particular a substance which contains carbonic acid, preferably in liquid form, a glass powder and water. If the three components are combined and mixed with one another, a reaction occurs, so as to form a solid body which hardens over the course of time (cement reaction).

[0005] Various raw materials are used for the production of glasses which are used in particular in glass-ionomer cements. These raw materials are firstly oxides, such as SiO2, Al2O3, CaO, fluorides, such as CaF2, SrF2, cryolite, hydroxides, such as Al(OH)3, phosphates, such as AlPO4, P2O5 or calcium phosphates. However, it is also possible to use silicates, such as mullite, or carbonates, such as Na2CO3, CaCO3 or other natural mineral raw materials. In principle, it is also possible for all the raw materials to be used in a form which contains water of crystallization.

[0006] In dental glasses, a considerable proportion of the oxygen is often replaced by fluorine. This is indicated by adding the element symbol F for fluorine to the description of the glass system.

[0007] Accordingly, glasses for glass-ionomer cements can usually be assigned to one of the following systems, in which P2O5 and Na2O in some cases are only present in small amounts or are not present at all:

[0008] SiO2—Al2O3—CaO—(P2O5)—(Na2O)—F

[0009] SiO2—Al2O3—SrO—(P2O5)—(Na2O)—F

[0010] SiO2—Al2O3—SrO—La2O3—(P2O5)—(Na2O)—F

[0011] SiO2—Al2O3—CaO—La2O3—(P2O5)—(Na2O)—F

[0012] The glasses which are used in dental cements are generally fluoroaluminosilicate glasses. The solubility of the glass in acid is a precondition for it to be used as a constituent of a polyelectrolyte cement. An acid-soluble glass structure is formed if silicon is partially replaced by aluminum. However, silicon can only be replaced by aluminum if basic oxides are present, in order to create charge equalization for the trivalent aluminum ion at positions of the tetravalent silicon ion.

[0013] When the polyacids and water are added, the glass structure is broken up, and in particular the ions with network-modifying properties are at least partially released as what are known as crosslinker ions.

[0014] The crosslinking manifests itself in hardening of the cement which increases over the course of time. All at least divalent basic ions, but also Al3+, are able to form polymeric structures of this type.

[0015] A distinction is usually drawn between the working time—the time during which the dentist is still able to work the still pasty cement material—and the hardening time—the time beyond which reworking is possible using rotating dental instruments.

[0016] It has been found that conventional glasses, which contain, for example, Ca2+ and Al3+ +s crosslinker ions, in untreated form are too reactive and, on account of an excessive solubility, set too quickly with the polyacid, and consequently the dental cement which forms cannot reasonably be worked.

[0017] Although it is possible to slow the dissolution process by reducing the calcium content in the glass, it has been found that if the level of basic oxides, such as CaO or SrO, which can dissolve, is too low, the strength properties of the cement deteriorate as a result of insufficient availability of the ions. This means that the dentist has only a very short working time available to mix the filling material and apply it. At the same time, he has to accept the drawback of having to wait a very long time before he can start reworking the cement. This runs contrary to the demands which a dentist will impose on a dental cement.

[0018] The dentist usually requires a working time of from 1 to 4 min and a hardening time of from 5 to 8 min. The hardening time is usually determined according to ISO 9917 (First Edition) Part 7.3. The working time and the hardening time can be determined using a viscometer, as described in EP 0 023 013 A.

[0019] To achieve the desired working properties of the cement, i.e. to have sufficient working time and the shortest possible time to complete hardening, it is customary for the glass powders, after the milling process, to be subjected to surface treatment, as described, for example, in Clinical Materials 12, 113-115 (1993) or DE 29 29 121 A (EP 0 230 113 A). In this case, the glasses which react too quickly, on account of their composition, are adjusted to the desired level of reaction rate by reducing the levels of reactive ions at their surface.

[0020] EP 0 023 013 A describes the use of a calcium aluminum fluorosilicate glass powder for glass-ionomer cements to which further oxides may be added if they do not adversely affect the properties of the glass. According to the description, the surface of the glass has to be deactivated in order to obtain a glass which can be used for a dental cement. The deactivation represents a procedure whereby the reaction rate of a glass powder with an acid is delayed by a surface treatment, and in this way the desired working times of the cement are produced.

[0021] The deactivation of the surface can also be effected by means of other, relatively complex surface treatments, such as coating the surface, for example with a polymer.

[0022] In EP 0 023 013 A, this is achieved by means of a chemical treatment of the powder surface. The result is a cement with favorable working times combined, at the same time, with unchanged favorable mechanical characteristic data of the material.

[0023] However, this surface treatment of the glasses represents a complex process step.

[0024] Moreover, during the washing or conditioning processes, powder agglomeration may occur, having an adverse effect on the cement properties.

[0025] DE 38 06 448 A has disclosed a glass for a bone cement which comprises the elements Si, Al, Ca, Sr, F, Na and P and can be made visible to X-rays by the addition of La2O3. It is emphasized that the quantity of additives must not adversely affect the properties.

[0026] The glass powder described in DE 38 04 469 A is substantially free of alkali metal ions and alkaline-earth metal ions, with the exception of strontium which should be used in an amount from 15 to 40% by weight.

[0027] DE 20 65 824 B2 has described a fluoroaluminosilicate glass powder for self-hardening medical cements.

[0028] One object of the present invention is to provide a glass for a dental cement, in particular a reactive glass for a polyelectrolyte cement, which is simple to produce.

[0029] A further object can be considered to lie in that of directly using the glass immediately after the milling process without having to apply complex processes such as surface treatment, acid washing, coating and/or conditioning. The reactivity and therefore the working time and hardening time are then dependent only on the glass composition and the grain size distribution and are easy to produce reproducibly.

[0030] This object is achieved by a dental material containing a glass as described in the claims, and by the use of certain ions as crosslinker ions in a glass.

[0031] The invention also relates to hardenable materials, in particular cements, in particular polyelectrolyte cements, which contain these glasses.

[0032] In the context of the present invention, the term crosslinking is to be understood as meaning a reaction in which polyacids and at least divalent ions interact with one another in a chelate-forming reaction, preferably an acid-base-type reaction, leading to the formation of a polymeric network.

[0033] In the context of the present invention, the filling and fixing materials mentioned are to be understood as meaning substantially cements, and in particular polyelectrolyte cements. Accordingly, the glass described is preferably a reactive constituent rather than a conventional filler, unlike the glasses used in the composite sector, which are pure fillers and do not take part in a reaction.

[0034] Glasses for cements generally contain strongly basic ions, such as Li+, Na+, K+, Ca2+, Sr2+, Ba2+, Zn2+. It has now been found that by completely or partially replacing the strongly basic ions with weakly basic ions, such as Sc3+, Y3+, La3+, such as Ce3+/4+, or other divalent, trivalent or tetravalent ions from the lanthanide series, and/or Ga2+ or In2+, glasses which set significantly more slowly with polyacids are obtained.

[0035] Surprisingly, such glasses can be used to produce dental cements which, substantially without a conventional surface treatment of the glass powders, have setting characteristics which are desired by the dentist. Furthermore, it has been found that the setting times can be adjusted within a wide range by means of the glass composition.

[0036] In this context, the invention has the following advantages:

[0037] As a result of the strongly basic ions, such as Ca+, Sr2+, being replaced by the weakly basic ions Sc3+, Y3+, La3+, Ce4+/3+ and other divalent, trivalent and tetravalent ions from the lanthanide series in glasses which are used in dental cements, it is possible to achieve a controlled setting reaction of the dental cement, in particular of a glass-ionomer cement, without the glass having to be surface-treated, for example by acid washing and/or conditioning, before being used in the cement. In addition to simplified production, the advantage also resides in the improved reproducibility of the working and hardening times. Although these times are not adjusted by a surface treatment, the desired setting profile, namely a relatively rapid transition from a state in which the cement can still be worked to a state in which the hardening begins and useful working is no longer possible, is surprisingly achieved.

[0038] Amazingly, it has been discovered that dental materials or cement in which the abovementioned glasses are used have mechanical properties which are identical or even slightly improved compared to cements in which glasses whose reactivity has been reduced by acid washing are used.

[0039] Furthermore, it has been found that cements according to the invention are hydrolytically stable with respect to water.

[0040] These properties were found in particular in glasses which, in addition to Al and Si, contain only Y and/or La or contain only relatively small amounts of relatively strongly basic-reacting ions, such as Ca2+ or Sr2+, Ba+, Li+, Na+, K+.

[0041] Furthermore, some of the oxygen can be replaced by fluorine, which on the one hand improves the meltability of the glass and on the other hand improves the setting properties of the cement and makes it possible to release fluoride ions for secondary caries prophylaxis.

[0042] Therefore, the previously known cement systems are expanded by the addition of the following systems.

[0043] SiO2—Al2O3—(SrO)—LnxOy—P2O5—(Na2O)—F

[0044] SiO2—Al2O3—(CaO)—LnxOy—P2O5—(Na2O)—F

[0045] LnxOy stands for an oxide of the elements Sc, Y, La to Lu. x and y may adopt values of 1, 2 or 3 in this formula. The oxides which are inside parenthesis are used in only small amounts or are not used at all, since they would greatly accelerate the reaction. For example, DE 20 65 824 A describes a glass belonging to the system

[0046] SiO2—Al2O3—La2O3—P2O5—Na2O—F

[0047] having an Na2O content of approx. 12% by weight.

[0048] Tests have shown that with this glass powder the setting rate with polyacids can only be brought into a manageable range after conditioning for several hours at 400° C. (cf. Comparative Example 4). This is presumably attributable to the high level of a strongly basic oxide, in this case Na2O. A further drawback of a high Na2O content is the increased water solubility of the resulting cement.

[0049] Moreover, it has been found that the glasses described substantially do not have any phase-separation or crystallization effect within a wide range of compositions.

[0050] It is to be expected that the reproducibility of the setting rate of the cement containing the glasses will improve with clear glasses compared to segregated, i.e. opaque glasses, since their phase composition is not dependent on the cooling rate.

[0051] In addition to the standard components SiO2, Al2O3, P2O5, and Na2O, the glasses preferably mainly contain weakly basic and/or amphoteric-reacting ions, which act as crosslinker ions during the cement reaction.

[0052] Weakly basic trivalent and tetravalent ions are preferred, and the ions Sc3+, Y3+, La3+, Ce4+/3+ and all the following trivalent and tetravalent ions from the lanthanide series are particularly preferred.

[0053] Current teaching is that Al3+ also belongs to the weakly basic or amphoteric-reacting ions. However, this ion adopts a special position among the glasses. Aluminum is primarily responsible for the solubility of the glass structure in acid and has only a secondary function as a crosslinker ion. In the glasses which are suitable for dental cements, aluminum, unlike the abovementioned trivalent and tetravalent ions, which function as network modifiers, acts as a network former.

[0054] The glasses used generally have a BET surface area of from 1 to 15 m2/g, preferably 2 to 8 m2/g.

[0055] Furthermore, the glasses have a mean grain size (d50) of from 0.01 to 20 μm, preferably 1 to 5 μm.

[0056] It is preferable for 0 to 25% by weight of the oxygen in the glass used to be replaced by fluorine, particularly preferably from 8 to 18% by weight.

[0057] The pKB value is usually used to define the term basicity. A pKB of one can be taken as the limit between weakly and strongly basic. For example, the pKB of Mg(OH)2 is given as one in R. C. Weast: CRC Handbook of Chemistry and Physics, while Ca(OH)2 is classified as strongly basic, without being assigned a numerical value.

[0058] In the context of the present invention, oxides or hydroxides which only dissociate to a relatively minor extent in aqueous solutions are considered to be weakly basic.

[0059] The following statements can be made in connection with the basicity:

[0060] The basicity increases from Sc through Y to La. La is to be classified as weakly basic compared to Sr, Ba or Na and K. At the same time, the basicity decreases again from La to Lu, and consequently the basicity of lutetium is approximately comparable to that of yttrium (lanthanide contraction).

[0061] Therefore, all oxides and hydroxides of the Sc series can be considered weakly basic in the context of present invention.

[0062] The elements from the 1st main group from Li through Cs and the elements from the second main group from Mg through Ba cannot be classified as weakly basic-reacting in the context of the present invention.

[0063] As has already been stated, it is assumed that, in addition to the base strength, the higher field strength of these ions also plays a certain role. This means that the ions described are anchored more strongly in the glass structure and are therefore dissolved out of it more slowly.

[0064] In the context of the present invention, the term polyacid is understood to mean a polyelectrolyte which includes a polymer with ionically dissociable groups, which may be substituents in the polymer chain and the number of which is so great that the polymers, at least in their (partially) dissociated form, are at least partially water-soluble. Substituents such as for example —COOH, —OH, —PO(OH)2, —OPO(OH)2, —SO2(OH) are particularly suitable for this purpose. Organic polyacids (DE 20 61 513 A), such as polymers and copolymers of acrylic acid, methacrylic acid (EP 0 024 056 A), itaconic acid, maleic acid, citraconic acid, vinylphosphonic acid (EP 0 340 016 A; GB 22 91 060 A) are particularly preferred. In addition, if a plurality of polyelectrolytes are present, water-insoluble polyelectrolytes may also be present in the polyelectrolyte cement. The only condition is that at least one of the polyelectroytes be at least partially water-soluble.

[0065] The polyelectrolytes should be able to react with the glass component as part of a chelate-forming reaction and/or an acid-base reaction/neutralization reaction.

[0066] The polyelectrolyte cement contains the at least partially water-soluble polyelectrolyte, which can be converted into the solid state, preferably in an amount from 0.5 to 30% by weight, particularly preferably 2 to 25% by weight and very particularly preferably 5 to 20% by weight.

[0067] In the case of polyelectrolyte cements, the addition of chelating agents in order to establish a suitable setting characteristic is particularly important (DE 23 19 715 A). There are numerous compounds which are suitable for this purpose, in particular those which contain hydroxyl or carboxyl groups, or both, which form the chelating agents. Particularly good results have been achieved with tartaric acid or citric acid, in particular in an amount of 5% by weight. Adding the substance in the form of a metal chelate also has the desired effect.

[0068] The polyelectrolyte cements contain from 0 to 10, preferably 0 to 5% by weight of a compound of this type, preferably tartaric acid.

[0069] Furthermore, the polyelectrolyte cement may include auxiliaries, such as dyes, pigments, X-ray contrasting agents, flow improvers, thixotropic agents, polymer thickeners or stabilizers.

[0070] Examples of standard fillers for dental materials are glass and quartz powder, plastic powder, pyrogenic highly dispersed silicas and mixtures of these components.

[0071] These other additives are usually present in the polyelectroyte cements according to the invention in amounts of from 0 to 60% by weight.

[0072] The abovementioned fillers may also be rendered hydrophobic by means of a surface treatment with organosilanes or organosiloxanes or by etherification of hydroxyl groups to form alkoxy groups.

[0073] In principle, the glass composition which has been described is also suitable for use in monomer-modified cements.

[0074] It has proven favorable for the glass to contain from 20 to 70% by weight, preferably from 30 to 60% by weight, of weakly basic oxides.

[0075] The cement according to the invention may if appropriate contain strongly basic oxides in an amount in the range from 0 to 25% by weight, preferably in the range from 0 to 10% by weight.

[0076] The cement according to the invention preferably has a flexural strength in the region of at least 25 MPa to 35 Mpa, particularly preferably of greater than 45 MPa, measured in accordance with ISO 4049.

[0077] The working time of the cement, which is determined using a viscometer, is 1 to 4 min, particularly preferably 2 to 3 min. The hardening time is 3 to 10 min, particularly preferably 4 to 8 min.

[0078] Preferred compositions of the glasses are given below.

[0079] In addition to the abovementioned weakly basic oxides from the scandium series, the glasses may also contain oxides from transition groups 4 and 5. Also, the aluminum oxide may be partially or completely replaced by boron oxide or gallium oxide. The melting conditions can be positively influenced by the addition of oxides from the first main group, phosphate, and/or basic oxides from the second main group or ZnO.

[0080] The oxides which are separated from one another by “+” in the table, may, according to the invention, also be present just individually. The crucial factor is the corresponding proportion by weight which the group forms in the glass

1OxideProportionY2O3 + La2O3 + other30 to 80% by weight, preferablylanthanide oxides35 to 60% by weightB2O3 + Al2O3 + Ga2O3 5 to 50% by weight, preferably10 to 40% by weight,particularly preferably 15 to 35SiO2 + GeO2 + SnO10 to 50% by weight, preferably15 to 50% by weightP2O5 0 to 15% by weight, preferably 0 to 10% by weight, particularlypreferably 0 to 2% by weightMgO + CaO + SrO + ZnO + BaO 0 to 10% by weight, preferably 0 to 8% by weight, particularlypreferably 0 to 5% by weightLi2O + Na2O + K2O + Rb2O + Cs2O 0 to 5% by weight, preferably 0 to 3% by weight, particularlypreferably 0 to 2% by weightTiO2 + ZrO2 + HfO2 0 to 10% by weight, preferably 0 to 4% by weight,V2O5 + Nb2O5 + Ta2O5 0 to 10% by weight, preferably 0 to 4% by weight,

[0081] Instead of the “Y2O3+La2O3+other lanthanide oxides”, it is also possible for Sc2O3 to be present in an amount of from 20 to 50% by weight, preferably from 20 to 30% by weight. Glass compositions in which Sc2O3 is present in addition to the above constituent in a relatively small amount are also included.

[0082] The invention is explained in more detail below with reference to a number of examples.

[0083] None of the glasses described in the examples was treated with an inorganic acid leading to a reduction in the number of reactive ions at the surface of the glasses (acid wash) before being reacted with a polyacid.

[0084] Production of the Glass:

[0085] Glasses of the following oxidic compositions (in % by weight) were melted at temperatures in the range from 1300 to 1600° C. over a period of 30 min to 5 h. With the exception of Comparative Example 4, the fluorine content in the starting batch was 12 to 14% by weight.

[0086] In Comparative Example 4, a glass was melted in accordance with DE 20 65 824 A1 using the following composition:

[0087] 9.5 g of SiO2, 10.0 g of Al2O3, 7.6 g of Na3AlF6, 9.4 g of LaF3, 7.3 g of AlPO4. The table gives the oxidic composition used in these examples.

2123456789C1C2C3C4C5C6C7SiO220192017322713211920184623172629Sc2O3Y2O3365820415046494830La2O34863203422.523CaO71647316SrO17Al2O344262220283237282629343536263027P2O56105ZrO25Na2O11128.561Li2O13

[0088] Milling

[0089] 60 to 80 g of the glass granules obtained were dry-milled for 40 to 50 min a vibratory agate mill (produced by Siebtechnik, milling vessel 100 ml, 910 rpm). The glass powders obtained had a mean grain size in the range from 3 to 6 μm with a specific surface area of from 1.8 to 2.5 m2/g.

EXAMPLE 6

[0090] Glass Example 6 was additionally wet-milled using a stirred ball mill. An aluminum oxide vessel (500 ml) was filled with 50 g of glass powder, 200 ml H2O and 100 g of zirconia balls (D=0.8 mm) and milling was carried out for 6 h using a perforated zirconia disk. The result was a mean grain size of 1.5 μm and a specific surface area of 10.5 m2.

[0091] Cements

[0092] The cements were produced as a result of the glass powders obtained being mixed with polyacids. In this step, an approximately 45% strength polyacrylic acid (molecular weight 20,000 to 30,000), an approximately 45% strength polyacrylomaleic acid (molecular weight approx. 40,000 to 60,000) and an approximately 55% strength polyvinylphosphonic acid (molecular weight approximately 20,000) were used.

[0093] The setting was determined firstly in accordance with ISO 9917 and secondly using the viscometer described in EP 0 023 013 A1. In all cases, the test assembly ensured that the temperature of the specimens was controlled at 28° C. Flexural strengths were determined using the three-point bending test on 2×2×25 mm cement specimens in accordance with ISO 4049.

[0094] Results:

[0095] Cement 1:

[0096] Glass 1 was mixed both with a polyacrylic acid and a polyacrylomaleic acid with a P:F of 3:1.

3PolyacrylomaleicPolyacrylic acidacidViscometer 3:30 3:50(working time)Viscometer 9:10 9:00(hardening time)ISO 9117 8:30 7:30Flexural strength39.431.8[Mpa]

[0097] Cement 6:

[0098] Glass 6 was reacted with polyacrylic acid (45% strength) with a P:F of 2.0:1.

4Stirred-ballDry millingmillingViscometer 5:00 2:10(working time)Viscometer12:00 7:45(hardening time)ISO 911710:30 4:00Flexural strength27.9 MPa41.5 MPa

[0099] Glass C6:

[0100] The glass, in one case untreated and in one case after conditioning for 6 hours at 400° C. in a circulating air oven (produced by Heraeus), was reacted with polyacrylic acid.

5untreatedconditionedViscometernot determinable 1:50(working time)Viscometer 5:20(hardening time)ISO 9117not determinable 5:00Flexural strengthnot determinable37.4 MPa

[0101] Further Cement Examples:

6Glass2345789C1C2C3C4C5C7P:F3:1 3:1 3:1 3:1 3.5:1 4:1 4:1 3:1 3:1 3:1 3:1 4:1 4:1Viscometer1:302:502:403:20 4:003:502:500:45<1:0<1:0<1:0<1:0<1:0(workingtime)Viscometer3:508:205:207:40 9:108:506:451:30<1:0<1:0<1:0<1:0<1:0(hardeningtime)ISO 99174:007:155:00 8:307:406:001:00<1:0<1:0<1:0<1:0<1:0Three-37.441.634.835.632.943.9——————pointflexuralstrength

[0102] The setting times determined for the cements obtained in Examples 1 to 9 are all within the preferred range, with the exception of Glass 6, which was only dry-milled.

[0103] The cement in accordance with Comparative Example 1 sets too quickly, presumably on account of the high Ca content. With the cements according to Comparative Examples 2 and 3, measurement was no longer possible, on account of setting taking place too quickly.

[0104] With the measurements using the viscometer, the first time corresponds to the working time and the second time corresponds to the hardening time. The times given are in minutes. The P:F ratio is given as a weight ratio.

[0105] The cements according to the invention are usually marketed packaged in vessels. In this context, it should be ensured that the individual components of the cement are in a form which is such that there is no undesirable reaction before they arrive at their intended use. The vessels usually have at least two chambers which are separated from one another. Examples of suitable vessels are described in WO 00/30953 A or EP 0 783 872 A.

[0106] Suitable vessels are mixing capsules and closeable box-like hollow bodies, such as screw-capped jars. Depending on the particular application, the cements may also be packaged in capsules.

Claims

1. A dental material comprising a dental glass characterized by the following composition:
2. The dental material as claimed in claim 1, comprising a dental glass characterized by the following composition:
3. The dental material as claimed in one of the preceding claims, in which the glass is essentially a three-component system.
4. The dental material as claimed in one of the preceding claims, in which from 0 to 25% by weight of the oxygen in the dental glass is replaced by fluorine.
5. The dental material as claimed in one of the preceding claims, in which the dental glass is present in powder form with a specific BET surface area of 1 to 15 m2/g.
6. The dental material as claimed in one of the preceding claims, in which the dental glass has a mean grain size in the range from 0.01 to 10 μm.
7. The dental material as claimed in one of the preceding claims, in which the surface of the dental glass has not been surface-treated, for example by washing with acid, surface coating and/or conditioning, in order to adjust the setting time.
8. A process for producing a dental glass as described in one of the preceding claims, comprising the steps a) providing the oxidic substances, b) mixing the oxidic substances, c) melting the mixture from step b), d) quenching the molten material to form a solid, e) milling the solid from step d) to form a glass powder, the glass powder from step d) not being treated with acid before it is used in a dental cement.
9. The use of a dental glass as described in one of the preceding claims for production of a cement, without the surface of the glass having being surface-treated.
10. The use as claimed in claim 9, in which the cement is a polyelectrolyte cement.
11. A dental cement, comprising A) mineral solid in an amount of from 50 to 90% by weight, B) water in an amount of from 5 to 50% by weight, and C) polyacid in an amount of from 5 to 50% by weight, the mineral solid comprising a dental glass as described in one of claims 1 to 8.
12. The dental cement as claimed in claim 11, in which in component A) the filler is present in an amount of from 0 to 90% by weight.
13. The dental cement as claimed in claim 12, in which the filler is selected from quartz, glasses, aluminum oxide, mineral powders, such as feldspars or kaolin, and/or plastic powder.
14. The dental cement as claimed in one of claims 11 to 13 with a flexural strength of at least 25 Mpa, measured according to ISO 4049.
15. A vessel having at least two chambers, containing a dental cement as claimed in one of claims 12 to 14, in which the free-flowing constituents are separated from the solid constituents.
16. The vessel as claimed in claim 15 in the form of a mixing capsule.
17. The use of ions of weakly basic-reacting oxides in glasses, which can enter into a cement reaction with a polyacid, to crosslink the polyacid.
18. The use as claimed in claim 17, in which the oxides are used in an amount of at least 20% by weight.
19. The use as claimed in one of claims 17 or 18, in which the oxides have a pKB value of >1.
20. The use as claimed in one of claims 17 to 19, in which the ions of the oxides are selected from Sc3+, Y3+, La3+, Ce4+ and all the following trivalent and tetravalent lanthanides and Ga2+ and/or In2+.

Priority Claims (1)

Number	Date	Country	Kind
10063939.9	Dec 2000	DE

PCT Information

Filing Document	Filing Date	Country	Kind
PCT/EP01/14721	12/23/2001	WO

Inert dental glass

Information

Publication Number

Date Filed

Date Published

Inventors

CPC

US Classifications

International Classifications

Abstract

Description

Claims

Priority Claims (1)

PCT Information