Infra-red reflecting layered structure

Abstract

The invention relates to an infra-red reflecting layered structure comprising a transparent substrate layer; a first metal oxide layer; a first silver containing layer, a second metal oxide layer; a second silver containing layer and a third metal oxide layer. The first, second and third metal oxide layer have a refractive index of at least 2.40 at a wavelength of 500 nm. The layered structure according to the present invention laminated on glass has a visual light transmittance (VLT) higher than 70% and a solar heat gain coefficient (SHGC) lower than 0.44. The invention further relates to the use of a layered structure as a transparent heat-mirror.

Description

FIELD OF THE INVENTION

The invention relates to an infra-red reflecting layered structure and to the use of such a layered structure as heat-mirror.

BACKGROUND OF THE INVENTION

Heat-mirrors that reflect radiation in the infrared spectrum while transmitting radiation in the visible spectrum have important applications for example as windows in buildings or vehicles.

For transparent heat-mirrors, visual light transmittance must be high, and hence the reflectivity and absorptivity must be low.

In the United States of America for example, automotive windshields must have a transmittance of visible light of at least 70%.

In the infrared, however, the heat-mirror must have high reflectivity and so transmittance and absorptivity in the infra-red must be low.

Heat-mirrors comprising a stack of alternating dielectric and metal layers are known in the art.

To obtain a heat-mirror characterised by a low heat transmittance, generally at least three metal layers are necessary. However, the number and the thickness of the metal layers have a negative influence on the visual light transmittance and on the cost and complexity of the manufacturing process.

It is well known to use silver as metal layer. However, a silver layer has a low stability, low durability and poor moisture and weather resistance.

SUMMARY OF THE INVENTION

It is an object of the present invention to avoid the drawbacks of the prior art.

It is another object of the invention to provide an improved infra-red reflecting layered structure.

It is also an object to provide an infra-red reflecting layered structure characterised by a good visual light transmittance and a low solar heat gain coefficient with a minimum number of metal layers.

It is a further object of the invention to provide an infra-red reflecting layered structure having silver containing layers with a high stability and a high weather resistance.

According to a first aspect of the present invention an infra-red reflecting layered structure is provided. The layered structure comprises:

• • a transparent substrate layer;
  • a first metal oxide layer;
  • a first silver containing layer;
  • a second metal oxide layer;
  • a second silver containing layer and
  • a third metal oxide layer.

The first, second and third metal oxide layer have a refractive Index of at least 2.40 at a wavelength of 500 nm.

In the layered structure according to the present invention, the number of pairs silver containing layer—metal oxide layer is limited to two. The thickness of the various metal oxide layers and the thickness of the first and second silver containing layers are adapted to each other so that the layered structure, laminated on glass, has a visual light transmittance (VLT) higher than 70% and a solar heat gain coefficient (SHGC) lower than 0.44.

The light to solar gain ratio (LSG ratio) of the layered structure laminated on glass is preferably higher than 1.60. More preferably, the LSG ratio is higher than 1.65, for example 1.69.

The visual light transmittance (VLT) refers to the percentage of the visible spectrum (380-780 nm) that is transmitted through a window.

The solar heat gain coefficient (SHGC) is the fraction of incident solar radiation (350-2500 nm) admitted through a window, both directly transmitted and absorbed and subsequently released inward by means of convection and radiation. SHGC is expressed as a number between 0 and 1. The lower a window's solar heat gain coefficient, the less solar heat it transmits.

The light to solar gain ratio (LSG ratio) is defined as $\frac{\mathrm{VLT}}{\mathrm{SHGC}\star 100}.$ The LSG ratio provides a gauge of the relative efficiency of different glass types in transmitting daylight while blocking heat gains. The higher the ratio, the brighter the room is without adding excessive amounts of heat.

The metal oxide may comprise any transparent material. However, metal oxide having a high refractive index and an almost zero extinction coefficient are preferred.

Therefore, in optical coatings where the optical thickness of the layers is of importance, the physical thickness of metal oxide having a high refractive index can be kept lower than the physical thickness of metal oxides having a lower refractive index.

The metal oxide layers of the layered structure can be deposited by any technique known in the art. Preferred techniques comprise physical vapor deposition techniques such as sputter deposition or chemical vapor deposition techniques.

A preferred metal oxide layer comprises TiO₂ and more particularly TiO₂ that is mainly composed of rutile phase and that is very dense. This type of TiO₂ has a refractive index of 2.41 at 510 nm.

A TiO₂ layer can be deposited by a reactive sputter deposition process from a Ti-target, a TiO₂-target or a substoichiometric TiO_x-target (with x between 1.75 and 2).

TiO₂ mainly composed of rutile phase is preferably deposited by DC magnetron sputtering using a TiO_x targets (preferably a rotatable TiO_x target) with x between 1.5 and 2, for example between 1.5 and 1.7.

These rotatable targets are produced by plasma spraying of rutile powder in a reducing atmosphere (e.g. Ar/H₂) on a stainless steel backing tube. The targets have enough electrical conductivity to be used as cathodes In a DC magnetron sputtering process and can withstand extremely high power levels. As a result, it is possible to achieve very high sputter deposition rates, at lower investment cost (both the deposition source itself and the power supply are considerably cheaper).

Other metal oxides having a high refractive index are for example BiO₂ (refractive index 2.45 at 550 nm) or PbO (refractive index 2.55 at 550 nm).

The different metal oxide layers of the layered structure may comprise the same material or may comprise a different material.

The first and second silver containing layers may comprise pure silver (i.e. silver with unavoidable impurities) or silver in combination with another element as for example gold, platinum, palladium, copper, aluminium, indium or zinc and/or mixtures thereof.

The silver containing layers comprise for example silver and up to 30 wt % of another element such as gold, platinum, palladium, copper, aluminium, indium or zinc and/or mixtures thereof.

A preferred silver containing layer comprises 10 wt % gold.

The silver containing layers are preferably deposited by a vacuum deposition technique, for example by sputtering or evaporation.

The deposition of the silver containing layers needs special precautions, because

• • (i) silver is, although often referred to as a precious metal, very prone to corrosion, and
  • (ii) the intermixing of the metal oxide and the silver layers has to be avoided: absorptance is essentially proportional to η.k; hence the presence of a rather thick mixed TiO2 (high η)—Ag (high k) layer will seriously increase the total absorptance of the layered structure and can eat away a big part of the theoretically achievable visual light transmittance.

This means that it can be preferred that the silver containing layer and/or the interface between the silver containing layer and the metal oxide layer is specially protected. This can for example be achieved by means of an intermediate layer between the metal oxide layer and the silver containing layer; between the silver containing layer and the metal oxide layer or by means of an intermediate layer on both sides of the silver containing layer.

Such an intermediate layer preferably comprises gold, for example pure gold (i.e. gold with unavoidable impurities) or gold in combination with up to 30 wt % of another element such as silver.

The intermediate layer has preferably a thickness between 0.5 and 10 nm, for example 1 nm.

Preferably, the intermediate layer is deposited by sputter deposition.

The layered structure according to the present invention comprises at least one transparent substrate layer.

The transparent substrate layer or layers may comprise a glass layer or a plastic layer for example a plastic layer made of polycarbonate, polyacrylate, polyester such as polyethylene terephtalate (PET), cellulose tri acetated (TCA or TAC) or polyurethane.

Possibly, an additional layer is deposited on top of the layered structure. Such an additional layer comprises for example a protective layer or an abrasion resistant layer.

According to a second aspect of the invention, the use of an infra-red reflecting layered structure as a transparent heat-mirror is provided.

According to further aspects a method of reducing the number of silver containing layers in an infra-red reflecting layered structure and a method of improving the visual light transmittance of an infra-red reflecting layered structure are provided.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will now be described into more detail with reference to the accompanying drawings wherein

FIGS. 1, 2 and 3 show different embodiments of an infra-red reflecting layered structure according to the present invention.

FIG. 4 shows the optical properties of a TiO₂ coating.

FIG. 5 shows the cross-section of a spectrally selective solar control window film.

FIG. 6 shows the cross-section of an automotive glazing comprising a layered structure according to the present invention.

FIG. 7 shows the transmittance of a layered structure according to the present invention.

FIG. 8 shows the reflectance of a layered structure according to the present invention.

FIGS. 9 and 10 compares the transmittance and the reflectance of a layered structure according to the present invention with two other types of layered structures.

DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION

An embodiment of an infra-red reflecting layered structure 10 is shown in FIG. 1. The layered structure comprises three metal oxide layers 12, 14, 16 and two silver containing layers 13,15.

The metal oxide layers comprise TiO₂.

The TiO₂ is obtained by DC magnetron sputtering using rotatable ceramic TiO_x targets with x between 1.5 and 1.7. These targets have enough electrical conductivity to be used as cathodes in a DC magnetron sputtering process.

In FIG. 4, the refractive index (η) and the extinction coefficient (ε) of a TiO₂ coatings can be seen. The refractive index (η) in function of the wavelength is given by line 44; the extinction coefficient (ε) of In function of the wavelength is given by line 42.

For wavelengths higher than 395 nm, the coating is absorption free. The refractive index at 510 nm is 2.41, which corresponds to the rutile phase of TiO₂.

The silver containing layers 12, 14 comprise pure silver (i.e. silver with unavoidable impurities).

In an alternative embodiment the silver containing layers 12, 14 comprise a silver layer comprising 10 wt % gold.

The first metal oxide layer 12 and the third metal oxide layer 16 have a thickness ranging between 25 and 35 nm.

The second metal oxide layer 14 has a thickness between 50 and 70 nm.

The first and second silver containing layer 13, 15 have a thickness between 10 and 25 nm.

FIG. 2 shows another embodiment of an infra-red reflecting layered structure 20. The layered structure is the same as the layered structure shown in FIG. 1 but additionally comprises intermediate layers 27, 27′, respectively between the first silver containing layer 22 and the second metal oxide layer 24 and between the second silver containing layer 25 and the third metal oxide layer 26.

The intermediate layers comprise gold and have a thickness of 1 nm.

The intermediate layers increase the stability and durability of the silver containing layers and avoid the intermixing at the interface of the silver containing layer and the metal oxide layer.

FIG. 3 shows a further embodiment of an infra-red reflecting layered structure 30. Intermediate layers 37, 37′ and 39, 39′ are deposited on both sides of the silver containing metal layers 33, 35.

The intermediate layers comprise gold or gold comprising 10 wt % silver.

The intermediate layers have a thickness of 1 nm.

FIG. 5 shows the cross-section of a spectrally selective solar control window film 50 comprising:

• • a hard coat top layer 52 for example comprising a cross-linked acrylate;
  • a first PET film 53 having a thickness of for example 23 μm;
  • a layered structure 54 according to the present invention;
  • a first adhesive layer 55;
  • a second PET film 56 having a thickness of for example 23 μm;
  • a second adhesive layer 57;
  • a glass layer 58.

FIG. 5 shows the sequence of the different layers. The thickness of the different layers is not in proportion to the real thickness.

FIG. 6 shows the cross-section of an automotive glazing comprising:

• • a first glass layer 62;
  • a first adhesive layer 63 for example comprising a PVB layer having a thickness of 375 μm;
  • a PET film 64 having a thickness of for example 50 μm;
  • a layered structure 65 according to the present invention;
  • a second adhesive layer 66 for example comprising a PVB layer having a thickness of 375 μm;
  • a glass layer 67.

The optical properties of the spectrally selective solar control window shown in FIG. 5 are given in Table 1.

TABLE 1
Visual properties
	VLT	Visual Light Transmittance (%)	71
	VLR	Visual Light Reflectance (%)	9
Solar Properties
	SHGC	Solar Heat Gain Coefficient	0.42
	TSER	Total Solar Energy Reflected (%)	58
	LSG ratio	light-to-solar-gain ratio	1.69
UV properties
	TUV	UV Transmittance (%)	<0.2

The transmittance T (expressed in %) of the spectrally selective solar control window film as shown in FIG. 5 is given in FIG. 7 for the UV, visible and near infra-red.

The reflectance R (expressed in %) of the spectrally selective solar control window film as shown in FIG. 5 is given in FIG. 8. The reflectance is measured on the glass side (line 82) and measured on the film side (line 84).

This infra-red reflecting structure according to the present invention combines a high visual light transmittance (VLT), with a low visual light reflectance and with a low solar heat gain coefficient (SHGC). The structure is furthermore characterized by a neutral color.

Infra-red reflecting layered structures known in the art need three silver containing layers to obtain the desired low solar heat gain coefficient. The layered structures according to the present invention have a low solar heat gain coefficient with only two silver containing layers. This reduced number of silver containing layers has a positive influence on the visual light transmittance.

In FIGS. 9 and 10, the transmittance and reflectance of the spectrally selective solar control window film as shown in FIG. 5 is compared with two other films: film A and film B.

In FIG. 9, the transmittance of the spectrally selective solar control window film according to the present prevention is given by line 92; the transmittance of film A is given by line 94 and the transmittance of film B is given by line 96.

In FIG. 10, the reflectance of the spectrally selective solar control window film according to the present prevention is given by line 102; the reflectance of film A is given by line 104 and the reflectance of film B is given by line 106.

Film A comprises alternating layers of In₂O₃ and of AgAu:

In₂O₃ layer/AgAu alloy layer/In₂O₃ layer/AgAu alloy layer/In₂O₃ layer/AgAu alloy layer/In₂O₃ layer.

Film B comprises alternating layers of SnO₂ and Ag:

SnO₂ layer/Ag layer/SnO₂ layer/Ag layer/SnO₂ layer.

From FIG. 9, it can be concluded that the visual light transmittance (VLT) of the structure according to the present invention is almost equal to the VLT of film A.

This means that for the structure according to the present invention the desired VLT can be obtained with only two silver containing layers, whereas the structure of film A needs three silver containing layers.

From FIG. 10, it can be concluded that the reflectance of the infra-red of the structure according to the present invention is higher than the reflectance of the infra-red of the structure of film B.

Claims

1. An infra-red reflecting layered structure, said layered structure comprising: a transparent substrate layer; a first metal oxide layer; a first silver containing layer; a second metal oxide layer; a second silver containing layer; a third metal oxide layer; said first, second and third metal oxide layer having a refractive index of at least 2.40 at a wavelength of 500 nm and said layered structure laminated on glass having a visual light transmittance (VLT) higher than 70% and a solar heat gain coefficient (SHGC) lower than 0.44.

2. A layered structure according to claim 1, whereby said layered structure has a light to solar gain ratio (LSG ratio) higher than 1.60.

3. A layered structure according to claim 1, whereby said metal oxide layer comprises TiO2.

4. A layered structure according to claim 3, whereby said TiO2 is mainly composed of rutile phase.

5. A layered structure according to claim 1, whereby said layered structure comprises at least one intermediate layer, said intermediate layer being located between a silver containing layer and a metal oxide layer and/or between a metal oxide layer and a silver containing layer.

6. A layered structure according to claim 5, whereby said intermediate layer comprises gold.

7. A layered structure according to claim 1, whereby said first and second silver containing layer have a thickness between 10 and 25 nm.

8. A layered structure according to claim 1, whereby said first, second and third metal oxide layer have a thickness between 25 and 70 nm.

9. Use of a layered structure according to claim 1, as a transparent heat-mirror.

10. A method of reducing the number of silver containing layers in an infra-red reflecting layered structure, said method comprising the following steps: providing a transparent substrate layer; depositing upon said substrate layer a first metal oxide layer having a refractive index of at least 2.40 at a wavelength of 500 nm; depositing upon said first metal oxide layer a first silver containing layer; depositing upon said first silver containing layer a second metal oxide layer having a refractive index of at least 2.40 at a wavelength of 500 nm; depositing upon said second metal oxide layer a second silver containing layer; depositing upon said second silver containing layer a third metal oxide layer having a refractive index of at least 2.40 at a wavelength of 500 nm.

11. A method of improving the visual light transmittance of an infra-red reflecting layered structure, said method comprising the following steps: providing a transparent substrate layer; depositing upon said substrate layer a first metal oxide layer having a refractive index of at least 2.40 at a wavelength of 500 nm; depositing upon said first metal oxide layer a first silver containing layer; depositing upon said first silver containing layer a second metal oxide layer having a refractive index of at least 2.40 at a wavelength of 500 nm; depositing upon said second metal oxide layer a second silver containing layer; depositing upon said second silver containing layer a third metal oxide layer having a refractive index of at least 2.40 at a wavelength of 500 nm.