Patent Application
20150030802
The technical field relates to an infrared absorption material, a method for fabricating the same, and a thermal isolation structure employing the same.
In order to achieve energy savings and carbon reduction, a thermal isolation film is generally formed on the window glass of buildings or vehicles. Due to their thermal isolation characteristics, metal oxides have been widely used in the thermal isolation film.
Accordingly, there is a need to develop a thermal isolation material having a high visible light transmittance and a high infrared radiation absorption efficiency.
An embodiment of the disclosure provides an infrared absorption material, wherein the infrared absorption material includes a tungsten bronze complex having a formula of M1xM2yWOz, wherein 0.6≦x≦0.8, 0.2≦y≦0.33, 0.8≦x+y<1, and 2<z≦3, and M1 is Li, or Na; M2 is K, Rb, or Cs. In particular, the tungsten bronze complex consists of a cubic tungsten bronze and a hexagonal tungsten bronze. The infrared absorption material can be applied in a thermal isolation structure to meet the requirements of high transmittance and high thermal isolation.
An embodiment of the disclosure provides a method for fabricating an infrared absorption material, wherein the method includes: providing a tungsten-containing precursor; providing a first alkali metal compound and a second alkali metal compound; mixing the first alkali metal compound, the second alkali metal compound, and the tungsten-containing precursor to form a mixture; and, subjecting the mixture to a thermal treatment, obtaining the aforementioned infrared absorption material. The thermal treatment includes a first heating step and a second heating step.
Embodiments of the disclosure provide a thermal isolation structure, including: a first substrate and a first functional layer formed on the substrate. In particular, the first functional layer includes the aforementioned infrared absorption material.
A detailed description is given in the following embodiments with reference to the accompanying drawings.
The disclosure can be more fully understood by reading the subsequent detailed description and examples with references made to the accompanying drawings, wherein:
An embodiment of the disclosure provides an infrared absorption material including a tungsten bronze complex. In particular, the tungsten bronze complex consists of a cubic tungsten bronze, and a hexagonal tungsten bronze.
According to an embodiment of the disclosure, the disclosure provides an infrared absorption material. The infrared absorption material includes a tungsten bronze complex having a formula of M1xM2yWOz, wherein 0.6≦x≦0.8, 0.2≦y≦0.33, 0.8≦x+y<1, and 2<z≦3, and M1 is lithium (Li), or sodium (Na); M2 is potassium (K), rubidium (Rb), or cesium (Cs). In particular, the tungsten bronze complex consists of a cubic tungsten bronze and a hexagonal tungsten bronze.
According to an embodiment of the disclosure, when the infrared absorption material includes a tungsten bronze complex having a formula of M1xM2yWOz and the molar ratio between the cubic tungsten bronze and the hexagonal tungsten bronze is between 0.995:99.005 and 5.005:94.995, of more than 60% of infrared radiation (with a wavelength between 750-2500 nm), which is emitted into the infrared absorption material, can be absorbed thereby. Further, the infrared absorption material can have an average visible light (with a wavelength between 400-750 nm) transmittance more than 65%.
According to an embodiment of the disclosure, the tungsten bronze complex has a formula of NaxKyWOz, wherein 0.6≦x≦0.8, 0.2≦y≦0.33, 0.8≦x+y<1, and 2<z≦3. In addition, according to an embodiment of the disclosure, the tungsten bronze complex has a formula of NaxCsyWOz, wherein 0.6≦x≦0.8, 0.2≦y≦0.33, 0.8≦x+y<1, and 2<z≦3. The tungsten bronze complex can have an average particle size between 20 nm and 200 nm (such as between 20 nm and 150 nm).
According to an embodiment of the disclosure, the disclosure also provides a method for fabricating the aforementioned infrared absorption material. As show in
It should be noted that, in order to obtain the infrared absorption material with the specific ratio between the cubic tungsten bronze and the hexagonal tungsten bronze, the ratio between the weight of the tungsten-containing precursor and the total weight of the first and the second alkali metal compounds is between 2 and 6, and the weight ratio between the first alkali metal compound and the second alkali metal compound is between 0.5 and 2. In addition, the thermal treatment includes a first heating step and a second heating step, and the process temperature of the second heating step is greater than that of the first heating step by at least 20° C. (for example greater than or equal to 30° C.). For example, the first heating step has a process temperature between 90° C. and 150° C. and a processing time between 10 hr and 24 hr; and the second heating step has a process temperature between 151° C. and 200° C. and a process time between 10 hr and 24 hr. It should be noted that, when the process time of the first heating step or the second heating step is less than 10 hr or more than 24 hr, the content of the metal element M1 (such as sodium) and the metal element M2 (such as potassium) of tungsten bronze complex (having a formula of M1xM2yWOz) would not be within the specific range (i.e. x would be less than 0.6 or more than 0.8, and y would be less than 0.2 or more than 0.33), resulting in that the molar ratio between the cubic tungsten bronze and the hexagonal tungsten bronze not being between 0.995:99.005 and 5.005:94.995. For example, when the metal element M1 is sodium and the process time of the first heating step or the second heating step is less than 10 hr, a result, having sodium, is apt to be tetragonal tungsten bronze, rather than cubic tungsten bronze. On the other hand, when the metal element M2 is potassium and the process time of the first heating step or the second heating step is less than 10 hr, a result, having potassium, is apt to be tetragonal tungsten bronze, rather than hexagonal tungsten bronze. In addition, the heating step can be, for example, a hydrothermal process.
According to an embodiment of the disclosure, the first heating step and second heating step can be hydrothermal treatments. For example, the mixture of the first alkali metal compound, the second alkali metal compound, and the tungsten-containing precursor are dissolved in water to obtain an aqueous solution. Next, the aqueous solution is introduced into the autoclave, and then the autoclave is sealed. Next, the aqueous solution is subjected to the first heating step and the second heating step sequentially, resulting in tungsten bronze crystals being formed via a supersaturated solution derived from the aqueous solution.
According to an embodiment of the disclosure, the disclosure also provides a thermal isolation structure. As shown in
Next, the dispersion is coated on the first substrate 14 to form a coating. The method for coating the dispersion on the first substrate 14 can be spin coating, bar coating, blade coating, roller coating, wire bar coating, or dip coating. The first substrate 14 can include a glass substrate, a transparent plastic substrate, or a combination thereof. Next, the first substrate 14 is dried in an oven with a process temperature between about 25 and 200° C. and a process time between about 0.5 and 60 min, obtaining the first functional layer 12. The first functional layer 12 can have a thickness between about 1 μm and 50 μm, such as between about 4 μm and 6 μm.
According to an embodiment, the thermal isolation structure 10 of the disclosure can further include a second substrate 16 disposed on the first functional layer 12, as show in
According to an embodiment, the thermal isolation structure 10 of the disclosure can further include a third substrate 22 disposed on the second substrate 16, As show in
According to an embodiment of the disclosure, the thermal isolation structure 10 of the disclosure can further include a second functional layer 24 disposed on the third substrate 22. Further, the thermal isolation structure 10 of the disclosure can further include a fourth substrate 26 disposed on the second functional layer 24, as show in
Below, exemplary embodiments will be described in detail with reference to accompanying drawings so as to be easily realized by a person having ordinary knowledge in the art. The disclosure concept may be embodied in various forms without being limited to the exemplary embodiments set forth herein. Descriptions of well-known parts are omitted for clarity, and like reference numerals refer to like elements throughout.
Preparation of Infrared Absorption Material
30 g of ammonium metatungstate (sold and manufactured by SHOWA), 4.388 g of sodium carbonate (sold and manufactured by Alfa Aesar), and 2.488 g of potassium carbonate (sold and manufactured by Alfa Aesar) were dissolved into 95 ml DI water. Next, the obtained solution was introduced into a stainless steel autoclave, and then the autoclave was sealed. The autoclave was heated at 120° C. for 12 hr, and then heated at 180° C. for 12 hr. After reacting, the result was filtered, and the filtrate was washed and then dried at 50° C. via a vacuum oven for 4 hr, obtaining a tungsten bronze complex powder with an average particle size of about 80 nm.
The tungsten bronze complex was characterized using an X-ray photoelectron spectrometer (XPS), and the results show that the molar ratio between Na, K, and W is 0.69:0.3:1 (i.e. the product may have a chemical formula of Na0.69K0.3WO3). Next, the diffraction pattern (
Next, the transmission spectrum (within the wavelength range between 400 nm and 2500 nm) of the tungsten bronze complex was measured, as show in
30 g of ammonium metatungstate (sold and manufactured by SHOWA), and 4.388 g of sodium carbonate (sold and manufactured by Alfa Aesar) were dissolved into 71 ml DI water. Next, the obtained solution was introduced into a stainless steel autoclave, and then the autoclave was sealed. The autoclave was heated at 120° C. for 12 hr, and then heated at 180° C. for 12 hr. After reacting, the result was filtered, and the filtrate was washed and then dried at 50° C. via a vacuum oven for 4 hr, obtaining a powder with an average particle size about 80 nm.
The powder was characterized using an X-ray photoelectron spectrometer (XPS), and the results show that the molar ratio between Na, and W is 0.69:1. Next, the powder was characterized using an X-Ray Diffractometer (XRD), the result shows that the product of Comparative Example 1 consists of a cubic tungsten bronze (CTB).
Next, the transmission spectrum (within the wavelength range between 400 nm and 2500 nm) of the powder was measured, as show in
30 g of ammonium metatungstate (sold and manufactured by SHOWA), and 2.488 g of potassium carbonate (sold and manufactured by Alfa Aesar) were dissolved into 66.3 ml DI water. Next, the obtained solution was introduced into a stainless steel autoclave, and then the autoclave was sealed. The autoclave was heated at 120° C. for 12 hr, and then heated at 180° C. for 12 hr. After reacting, the result was filtered, and the filtrate was washed and then dried at 50° C. via a vacuum oven for 4 hr, obtaining a powder with an average particle size about 80 nm.
The powder was characterized using an X-ray photoelectron spectrometer (XPS), and the results show that the molar ratio between K, and W is 0.3:1. Next, the powder was characterized using an X-Ray Diffractometer (XRD), the result shows that the product of Comparative Example 2 consists of a hexagonal tungsten bronze (HTB).
Next, the transmission spectrum (within the wavelength range between 400 nm and 2500 nm) of the powder was measured, as show in
As shown in
In addition, in comparison with the product of Comparative Examples 1 and 2, the infrared absorption material of the disclosure (Example 1) has a higher infrared radiation (with a wavelength between 750-2500 nm) absorption efficiency.
30 g of ammonium metatungstate (sold and manufactured by Sigma-Aldrich), 4.388 g of sodium carbonate (sold and manufactured by Alfa Aesar), and 2.488 g of potassium carbonate (sold and manufactured by Alfa Aesar) were dissolved into 95 ml DI water. Next, the obtained solution was introduced into a stainless steel autoclave, and then the autoclave was sealed. The autoclave was heated at 120° C. for 15 hr, and then heated at 180° C. for 12 hr. After reacting, the result was filtered, and the filtrate was washed and then dried at 50° C. via a vacuum oven for 4 hr, obtaining a tungsten bronze complex powder with an average particle size about 80 nm.
The tungsten bronze complex was characterized using an X-ray photoelectron spectrometer (XPS), and the results show that the molar ratio between Na, K, and W is 0.69:0.3:1 (i.e. the product may have a chemical formula of Na0.69K0.3WO3). Next, the diffraction pattern of the tungsten bronze complex was generated using an X-Ray Diffractometer (XRD), and the result shows that the tungsten bronze complex of Example 2 consists of a hexagonal tungsten bronze (HTB) and a cubic tungsten bronze (CTB). The molar ratio between the cubic tungsten bronze and the hexagonal tungsten bronze was determined using an inductively coupled plasma - atomic emission spectrometer (ICP-AES), and the result shows that the molar ratio between the cubic tungsten bronze and the hexagonal tungsten bronze is (1±0.005)%:(99±0.005)%.
Next, the transmission spectrum (within the wavelength range between 400 nm and 2500 nm) of the tungsten bronze complex was measured, as show in
30 g of ammonium metatungstate (sold and manufactured by Sigma-Aldrich), 4.388 g of sodium carbonate (sold and manufactured by Alfa Aesar), and 5.865 g of caesium carbonate (sold and manufactured by Alfa Aesar) were dissolved into 95 ml DI water. Next, the obtained solution was introduced into a stainless steel autoclave, and then the autoclave was sealed. The autoclave was heated at 120° C. for 12 hr, and then heated at 180° C. for 12 hr. After reacting, the result was filtered, and the filtrate was washed and then dried at 50° C. via a vacuum oven for 4 hr, obtaining a tungsten bronze complex powder with an average particle size about 80 nm.
The tungsten bronze complex was characterized using an X-ray photoelectron spectrometer (XPS), and the results show that the molar ratio between Na, Cs, and W is 0.69:0.3:1 (i.e. the product may have a chemical formula of Na0.69Cs0.3WO3). Next, the diffraction pattern of the tungsten bronze complex was generated using an X-Ray Diffractometer (XRD), and the result shows that the tungsten bronze complex of Example 2 consists of a hexagonal tungsten bronze (HTB) and a cubic tungsten bronze (CTB). The molar ratio between the cubic tungsten bronze and the hexagonal tungsten bronze was determined using an inductively coupled plasma-atomic emission spectrometer (ICP-AES), and the result shows that the molar ratio between the cubic tungsten bronze and the hexagonal tungsten bronze is (1±0.005)%:(99±0.005)%.
Next, the transmission spectrum (within the wavelength range between 400 nm and 2500 nm) of the tungsten bronze complex was measured, as show in
30 g of ammonium metatungstate (sold and manufactured by SHOWA), 4.388 g of sodium carbonate (sold and manufactured by Alfa Aesar), and 2.488 g of potassium carbonate (sold and manufactured by Alfa Aesar) were dissolved into 95 ml DI water. Next, the obtained solution was introduced into a stainless steel autoclave, and then the autoclave was sealed. The autoclave was heated at 120° C. for 12 hr, and then heated at 180° C. for 6 hr. After reacting, the result was filtered, and the filtrate was washed and then dried at 50° C. via a vacuum oven for 4 hr, obtaining a powder with an average particle size about 80 nm.
The powder was characterized using an X-ray photoelectron spectrometer (XPS), and the results show that the molar ratio between Na, K, and W is 0.46:0.3:1 (i.e. the product may have a chemical formula of Na0.46K0.3WO3). Next, the diffraction pattern of the tungsten bronze complex of Comparative Example 3 was generated using an X-Ray Diffractometer (XRD), and the result shows that the tungsten bronze complex of Comparative Example 3 consists of a hexagonal tungsten bronze (HTB) and a tetragonal tungsten bronze (TTB).
Next, the transmission spectrum (within the wavelength range between 400 nm and 2500 nm) of the tungsten bronze complex of Comparative Example 3 was measured, as show in
30 g of ammonium metatungstate (sold and manufactured by Sigma-Aldrich), 4.388 g of sodium carbonate (sold and manufactured by Alfa Aesar), and 2.488 g of potassium carbonate (sold and manufactured by Alfa Aesar) were dissolved into 95 ml DI water. Next, the obtained solution was introduced into a stainless steel autoclave, and then the autoclave was sealed. The autoclave was heated at 150° C. for 6 hr, and then heated at 180° C. for 12 hr. After reacting, the result was filtered, and the filtrate was washed and then dried at 50° C. via a vacuum oven for 4 hr, obtaining a powder with an average particle size about 80 nm.
The powder was characterized using an X-ray photoelectron spectrometer (XPS), and the results show that the molar ratio between Na, K, and W is 0.46:0.3:1 (i.e. the product may have a chemical formula of Na0.46K0.3WO3). Next, the diffraction pattern of the tungsten bronze complex of Comparative Example 4 was generated using an X-Ray Diffractometer (XRD), and the result shows that the tungsten bronze complex of Comparative Example 4 consists of a hexagonal tungsten bronze (HTB) and a tetragonal tungsten bronze (TTB).
30 g of ammonium metatungstate (sold and manufactured by Sigma-Aldrich), 4.388 g of sodium carbonate (sold and manufactured by Alfa Aesar), and 4.147 g of potassium carbonate (sold and manufactured by Alfa Aesar) were dissolved into 99.2 ml DI water. Next, the obtained solution was introduced into a stainless steel autoclave, and then the autoclave was sealed. The autoclave was heated at 120° C. for 6 hr, and then heated at 150° C. for 24 hr. After reacting, the result was filtered, and the filtrate was washed and then dried at 50° C. via a vacuum oven for 4 hr, obtaining a powder with an average particle size about 80 nm.
The powder was characterized using an X-ray photoelectron spectrometer (XPS), and the results show that the molar ratio between Na, K, and W is 0.46:0.5:1 (i.e. the product may have a chemical formula of Na0.46K0.5WO3). Next, the diffraction pattern of the tungsten bronze complex of Comparative Example 5 was generated using an X-Ray Diffractometer (XRD), and the result shows that the tungsten bronze complex of Comparative Example 5 consists of a tetragonal tungsten bronze (TTB).
Next, the transmission spectrum (within the wavelength range between 400 nm and 2500 nm) of the tungsten bronze complex of Comparative Example 5 was measured, as show in
According to Examples 1-3, and Comparative Examples 3-5, since the process time of the first heating step or the second heating step of Comparative Examples 3-5 is less than 10 hr, the content of the sodium (the metal element M1) or potassium (the metal element M2) of tungsten bronze complex (having a formula of M1xM2yWOz) would not be within the specific range (i.e. x would be less than 0.6 or more than 0.8, and y would be less than 0.2 or more than 0.33), resulting in the tungsten bronze not consisting of a cubic tungsten bronze and a hexagonal tungsten bronze. For example, when the process time of the first heating step or the second heating step is less than 10 hr, the sodium-containing tungsten bronze is apt to be a tetragonal tungsten bronze, rather than a cubic tungsten bronze. On the other hand, when the process time of the first heating step or the second heating step is less than 10 hr, the potassium-containing tungsten bronze is apt to be a tetragonal tungsten bronze, rather than a hexagonal tungsten bronze. In addition, as shown in
Thermal Isolation Structure
The tungsten bronze complex of Example 1 (Na0.69K0.3WO3, serving as infrared absorption material), a polymeric dispersant (DISPERBYK-2000), and a solvent (propylene glycol mono-methyl ether acetate) were ground and mixed, forming a dispersion. Next, the dispersion and an acrylic resin were mixed and then coated on a blue glass (sold by Taiwanglass with a trade name of TGI Tinted Glass Ocean Blue, having a thickness of 5 mm) to form an infrared absorption film after curing, obtaining a thermal isolation structure (1) (having a structure as shown in
The tungsten bronze complex of Example 3 (Na0.69Cs0.3WO3, serving as infrared absorption material), a polymeric dispersant (DISPERBYK-116), and a solvent (propylene glycol mono-methyl ether acetate) were ground and mixed, forming a dispersion. Next, the dispersion and an polyvinyl butyral resin (sold by Chang Chun Plastics Co., Ltd) were mixed and then coated on a first clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) to form an infrared absorption film after curing. Next, a second clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) was disposed on the infrared absorption film, obtaining a thermal isolation structure (2) (having a structure as shown in
The tungsten bronze complex of Example 3 (Na0.69Cs0.3WO3, serving as infrared absorption material), a polymeric dispersant (DISPERBYK-116), and a solvent (ethyl acetate) were ground and mixed, forming a dispersion. Next, the dispersion and an epoxy resin (sold by Nan Ya Plastics Co., Ltd) were mixed and then coated on a green glass (sold by Taiwanglass with a trade name of TGI Tinted Glass French Green, having a thickness of 5 mm) to form an infrared absorption film after curing. Next, a clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) was disposed on the infrared absorption film, obtaining a thermal isolation structure (3) (having a structure as shown in
The tungsten bronze complex of Example 1 (Na0.69K0.3WO3, serving as infrared absorption material), a polymeric dispersant (Efka PX4300), and a solvent (methyl ethyl ketone) were ground and mixed, forming a dispersion. Next, the dispersion and an acrylic pressure-sensitive adhesive were mixed and then coated on a green glass (sold by Taiwanglass with a trade name of TGI Tinted Glass French Green, having a thickness of 5 mm) to form an infrared absorption film after curing. Next, a first clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) was disposed on the infrared absorption film. Next, a support spacer (foam warm-edge spacer) was disposed on the first clear glass, and then a second clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) was disposed on the support spacer, such that the first clear glass and the second clear glass were separated by the support spacer and a chamber. The chamber was filled with air. Therefore, a thermal isolation structure (4) (having a structure as shown in
The tungsten bronze complex of Example 1 (Na0.69K0.3WO3, serving as infrared absorption material), a polymeric dispersant (DISPERBYK-116), and a solvent (ethyl acetate) were ground and mixed, forming a dispersion. Next, the dispersion and an epoxy resin were mixed and then coated on a fluorine-doped tin oxide (FTO) glass (sold by Pilkington with a trade name of Low-E Glass) to form an infrared absorption film after curing. Next, a clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) was disposed on the infrared absorption film. Next, a support spacer (foam warm-edge spacer) was disposed on the first clear glass, and then a green glass (sold by Taiwanglass with a trade name of TGI Tinted Glass French Green, having a thickness of 5 mm) was disposed on the support spacer, such that the clear glass and the green glass were separated by the support spacer and a chamber. The chamber was filled with air. Therefore, a thermal isolation structure (5) (having a structure as shown in
The tungsten bronze complex of Example 3 (Na0.69Cs0.3WO3, serving as infrared absorption material), a polymeric dispersant (DISPERBYK-2000), and a solvent (propylene glycol mono-methyl ether acetate) were ground and mixed, forming a dispersion. Next, the dispersion and an acrylic resin were mixed and then coated on a green glass (sold by TAIWANGLASS with a trade name of TGI Tinted Glass French Green, having a thickness of 5 mm) to form an infrared absorption film after curing. Next, a clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) was disposed on the infrared absorption film, obtaining a first element.
Next, the above-mentioned steps were repeated, obtaining a second element.
Finally, the second element was disposed on the first element, wherein the first element and the second element were separated by a support spacer (foam warm-edge spacer), forming a chamber between the first element and the second element. Namely, the clear glass of the first element was separated from the green glass of the second element by the support spacer and the chamber. The chamber was filled with air. Therefore, a thermal isolation structure (6) (having a structure as shown in
The tungsten bronze complex of Example 3 (Na0.69Cs0.3WO3, serving as infrared absorption material), a polymeric dispersant (DISPERBYK-116), and a solvent (methyl ethyl ketone) were ground and mixed, forming a dispersion. Next, the dispersion and an acrylic resin were mixed and then coated on a green glass (sold by TAIWANGLASS with a trade name of TGI Tinted Glass French Green, having a thickness of 5 mm) to form an infrared absorption film after curing. Next, a first clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) was disposed on the infrared absorption film, obtaining a first element.
Next, the tungsten bronze complex of Example 3 (Na0.69Cs0.3WO3, serving as infrared absorption material), a polymeric dispersant (Efka PX4300), and a solvent (ethyl acetate) were ground and mixed, forming a dispersion. Next, the dispersion and an acrylic resin were mixed and then coated on a second clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) to form an infrared absorption film after curing. Next, a third clear glass (sold by Taiwanglass with a trade name of TGI Clear Float Glass, having a thickness of 5 mm) was disposed on the infrared absorption film, obtaining a second element.
Finally, the second element was disposed on the first element, wherein the first element and the second element were separated by a support spacer (aluminum spacer), forming a chamber between the first element and the second element. Namely, the first clear glass of the first element was separated from the second clear glass of the second element by the support spacer and the chamber. The chamber was filled with air. Therefore, a thermal isolation structure (7) (having a structure as shown in
Next, the visible light transmittance and the solar radiation transmittance of the thermal isolation structures (1)-(7) of Examples 4-10 were measured, and the results are shown in Table 3.
As shown in Table 3, the tungsten bronze complex of the disclosure can serve as an infrared absorption material and can be further employed by a thermal isolation structure. Therefore, the thermal isolation structure employing the tungsten bronze complex of the disclosure provides daylighting and thermal isolation functions.
It will be apparent to those skilled in the art that various modifications and variations can be made to the disclosed methods and materials. It is intended that the specification and examples be considered as exemplary only, with a true scope of the disclosure being indicated by the following claims and their equivalents.
| Number | Date | Country | Kind |
|---|---|---|---|
| 102145805 | Dec 2013 | TW | national |
| 103116353 | May 2014 | TW | national |
This application claims the benefit of U.S. Provisional Application No. 61/857,421, filed on Jul. 23, 2013, which provisional application is hereby incorporated herein by reference. The application is based on, and claims priorities from Taiwan Application Serial Number 102145805, filed on Dec. 12, 2013, and Taiwan Application Serial Number 103116353, filed on May. 8, 2014, the disclosure of which is hereby incorporated by reference herein in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61857421 | Jul 2013 | US |