Inhibition of silica and silicate deposition using ethylene oxide-propylene oxide block copolymers

Abstract

A method of controlling the deposition of silica-containing scales and their adhesion to surfaces in contact with an aqueous system is disclosed which comprises adding to the aqueous system an ethylene oxide-propylene oxide copolymer.

Description

FIELD OF THE INVENTION

The present invention relates to controlling silica deposits in aqueous systems. More particularly, the present invention relates to inhibiting silica/silicate deposition in cooling and boiler water systems using ethylene oxide-propylene oxide block copolymer.

BACKGROUND OF THE INVENTION

The problem of scale formation and its attendant affects have troubled water systems for many years. For instance, scale tends to accumulation the internal walls of various water systems, such as boiler and cooling water systems, thereby reducing heat transfer properties and fluid flow through heat exchanger tubes.

One particular type of deposit, silica, is especially troublesome in some systems. Where the water used in cooling the systems and water cooled industrial heat exchangers is taken directly from lakes, rivers, ponds, or municipal water sources, various amounts of dissolved and suspended solids, including silica, are present. Problems are compounded in operations where water is concentrated, or cycled up, during the process, e.g., cooling systems. As the water evaporates, the silica concentrations increase increasing both the occurrence and the degree of deposition. Increasing silica concentrations can also result in monomeric silica undergoing polymerization to form gelular and/or colloidal silica which can form tenacious deposits.

In cooling water systems, silica and silicate compounds form deposits on the internal metal surfaces in contact with the water flowing through the system. In this manner, heat transfer efficiency becomes severely impeded, which in turn has a deleterious effect on the overall operating efficiency of the cooling water system. Silica and silicate deposition also causes problems on other conduit and piping surfaces, as well as on equipment such as valves, nozzles and pumps.

Although current industrial cooling systems make use of sophisticated external treatments of the feed water, e.g., coagulation, filtration, softening of water prior to it being fed into the water system, these operations are only moderately effective. In all cases, external treatment does not in itself provide adequate treatment since muds, sludge, silts, and dissolved solids such as silicate can escape the treatment and eventually are introduced into the system.

Silica (silicon dioxide) appears naturally in a number of crystalline and amorphous forms, all of which are sparingly soluble in water; thus leading to the formation of undesirable deposits. Silicates are salts derived from silica or the silicic acids, especially orthosilicates and metosilicates, which may combine to form polysilicates. All of these, except the alkali silicates are sparingly soluble in water. A number of different forms of silica and silicate salt deposits are possible, and formation depends, among other factors, on the temperature and pH of the water.

Various methods have been utilized for resolving the problem of sludge and silt, including silica, deposition. U.S. Pat. No. 5,378,368 discloses the use of polyether polyamino methylene phosphonates to control silica/silicate deposition in industrial water systems. The polyether polyamino methylene phosphonates may be used alone or in combination with a polymer additive.

U.S. Pat. No. 5,078,879 discloses the use of 2-phosphono-butane tricarboxylicate acid-1,2,4 alone or preferably in combination with an anionic polymer such as a carboxylic/sulfonic polymer, to control the formation of silica/silicate deposits in aqueous systems.

U.S. Pat. No. 4,933,090 discloses the use of a select phosphonate and optionally a carboxylic/sulphonic/polyalkylene oxide polymer to control silica/silicate deposition.

U.S. Pat. No. 4,874,527 discloses the use of an imine polymer, a phosphanate and optionally a source of molybdate or borate ions to control the formation of silica/silicate deposits in aqueous systems.

U.S. Pat. No. 5,158,685 discloses the use of a combination of a hydroxyphosphonoacetic acid and an acrylic acid/alyl hydroxy propyl sulphonate ether polymer to control silica/silicate deposition in cooling water systems.

U.S. Pat. No. 5,300,231 discloses the use of polyether polyamino methylene phosphonates in combination with hydroxy-phosphono acetic acid or amino tris methylene phosphonate to control silica/silicate deposition in various industrial water systems.

U.S. Pat. No. 4,405,461 discloses the use of a treatment comprising an amine to which is attached at least a pair of terminal groups selected from furfuryl and saturated or unsaturated hydrocarbon radicals substituted with one or more hydroxy and carboxy, or a hydrohalide thereof to control the deposition of silica-containing scales.

DETAILED DESCRIPTION OF THE INVENTION

In accordance with the present invention, it has been discovered that ethylene oxide-propylene oxide block copolymers thereof are effective treatment agents for reducing the deposition of silica/silicate in aqueous systems. The method of the present invention comprises adding an effective amount of an ethylene oxide-propylene oxide block copolymer or mixtures thereof to an aqueous system being treated.

The treatment for aqueous systems of the present invention is a copolymer of ethylene oxide and propylene oxide (EO-PO). The preferred copolymer has an average molecular weight ranging from about 1000-5000. The molecular weight of the hydrophobe (polyoxypropylene) preferably ranges from about 950-3000, and the percent of hydrophile (polyoxyethylene) ranges from about 20-70% of the copolymer. EO-PO copolymers are available commercially from BASF under the Pluronic.TM. label.

An effective amount of EO-PO copolymer can be added to an aqueous system being treated. As used herein, the term effective amount is that amount necessary to control silica/silicate deposition in the system being treated. Generally, the effective amount will range from about 1 to 100 ppm, on an active basis based upon the total weight of the aqueous system being treated.

As used herein, the term controlling the silica/silicate deposition is to include inhibition of silica polymerization, threshold precipitation inhibition, stabilization, dispersion, solubilization, and/or particle size reduction of silica, silicates, calcium and magnesium silicates, and silicon ions. The treatments of the present invention are threshold silicate precipitation inhibitors which also stabilize, disperse and solubilize silica and silicates, and generally reduce the particle size of any precipitated material.

Aqueous system as used herein, is meant to include any type of system containing water, including, but not limited to, cooling water systems, boiler water systems, desalination system, gas scrubber water systems, evaporator systems, paper manufacturing systems, mining systems, and the like.

The EO-PO copolymers of the present invention are well known to those skilled in water treatment art, and are commercially available. The treatment materials of the present invention may be added to the aqueous system being treated by any convenient means. A preferred method of addition is to the makeup water streams. Additionally, other conventional water treatment agents such as corrosion inhibitors can be used in combination with treatments of the present invention.

The present invention will now be further described with reference to a number of specific examples which are to be regarded as illustrative, and not as restricting the scope of the present invention.

EXAMPLES

The efficiency of EO-PO copolymer chemistry to inhibit silica/silicate deposition in an aqueous system was evaluated in a stirred batch reverse osmosis apparatus. The apparatus was a pressurized water filter where the filter media was a reverse osmosis membrane and the pressure was provided by compressed nitrogen. An overhead stirrer paddle was positioned near the surface of the membrane filter to provide turbulence to minimize concentration effects.

A synthetic feed water containing 100 ppm silica as SiO.sub.2 was added to the apparatus with and without treatment. The feed water was concentrated approximately ten times over a 30-40 minute period, such that the water at the end of the experiment contained about 1000 ppm SiO.sub.2. At the conclusion of a run, the reverse osmosis membrane was removed and analyzed for silica to quantify the amount of silica deposited on the membrane. Tests with a chemical treatment were compared to control tests (no chemical treatment) to calculate a percent silica inhibition. The results are summarized in Table I.

TABLE I______________________________________ Average Percent Molecular Percent Silica Treatment Weight Polyoxyethylene Inhibition______________________________________10 ppm Pluronic L35 1900 50 27 10 ppm Pluronic L42 1630 20 33 10 ppm Pluronic L43 1850 30 41 10 ppm Pluronic L44 2200 40 45 10 ppm Pluronic L61 2000 10 29 10 ppm Pluronic L62 2500 20 34 10 ppm Pluronic L63 2650 30 37 10 ppm Pluronic L64 2900 40 28 10 ppm Pluronic P65 3400 50 27 10 ppm Pluronic P68 8400 80 0 10 ppm Pluronic P84 4200 40 29 10 ppm Pluronic L92 3650 20 24 10 ppm Pluronic F108 14600 80 0 10 ppm Pluronic L121 4400 10 0______________________________________

The data in Table I shows that EO-PO copolymers comprising from about 20-70% hydrophile (polyoxyethylene) and an average molecular weight from about 1000-5000 provide significant silica inhibition in aqueous systems. The EO-PO copolymer treatment of the present invention is effective at inhibiting silica deposition in systems having relatively low (<180 ppm) concentrations of reactive silica.

While this invention has been described with respect to particular embodiments thereof, it is apparent that numerous other forms and modifications of this invention will be obvious to those skilled in the art. The appended claims and this invention generally should be construed to cover all such obvious forms and modifications which are within the true spirit and scope of the present invention.

Claims

1. A method of inhibiting the deposition of silica and silicate compounds on surfaces in contact with an aqueous system consisting essentially of adding to the aqueous system an effective amount to inhibit deposition of silica and silicate compounds of ethylene oxide-propylene oxide copolymer of average molecular weight from 1000-5000 having a percent hydrophile ranging from about 20-70%.

2. The method of claim 1 wherein said ethylene oxide-propylene oxide copolymer is added at a dosage of about 1 to 100 ppm.

3. A method of solubilizing silica and silicate compounds in aqueous systems consisting essentially of adding to the aqueous system an effective amount to solubilize silica and silicate compounds of ethylene oxide-propylene oxide copolymer of average molecular weight from 1000-5000 having a percent hydrophile ranging from about 20-70%.

4. The method of claim 3 wherein said ethylene oxide-propylene oxide copolymer is added at a dosage of from about 1 ppm to about 100 ppm.

5. A method of dispersing silica and silicate compounds in aqueous systems consisting essentially of adding an effective amount to disperse silica and silicate compounds of ethylene oxide-propylene oxide copolymer of average molecular weight from 1000-5000 having a percent hydrophile ranging from about 20-70%.

6. The method of claim 5 wherein said ethylene oxide-propylene oxide copolymer is added at a dosage of from about 1 ppm to about 100 ppm.