INJECTABLE HYDROGEL FOR THE LONG-TERM SUPPLEMENTATION OF GLYCEROL IN THE SKIN

Abstract

An injectable hydrogel, includes, in weight, in a physiologically acceptable carrier fluid: 0.01 to 5% of glycerol and 0.1 to 5% of cross-linked hyaluronic acid, or one of the salts thereof; characterized in that the hyaluronic acid or one of the salts thereof is cross-linked by the formation of covalent bonds using bifunctional or polyfunctional molecules, the injectable hydrogel being sterilized in moist heat and having viscoelastic properties such that Tanδ at a frequency of 1 Hz is less than or equal to 1.10. A method for producing the hydrogel, to a kit containing the hydrogel, as well as to the use thereof in dermatology are also described.

Description

The present invention relates to an injectable hydrogel for the long-term supplementation of glycerol in the skin.

The present invention also relates to the method and to the use of the aforementioned hydrogel in the area of dermatology.

Glycerol, an endogenous molecule, is a trihydroxy alcohol that has a key role in the skin. Endogenous glycerol notably plays a major role in hydration of the skin, in skin elasticity and in repair of the epidermal barrier (British Journal of Dermatology, 159(1):23-34, July 2008, Fluhr, J. W.; Darlenski, R. *; Surber).

The various beneficial effects of glycerol on the epidermis notably include hydration of the stratum corneum (the outermost layer of the skin), the barrier function of the skin, the mechanical properties of the skin, protection against irritant stimuli and acceleration of the process of wound healing (British Journal of Dermatology, 159(1):23-34, July 2008, Fluhr, J. W.; Darlenski, R. *; Surber).

It is also known from the prior art that topical application of products containing glycerol improves the properties of the skin in diseases characterized by xerosis and by an epidermal barrier that has deteriorated, as is the case in atopic dermatitis.

Moreover, with age, we observe a decrease in the amount of glycerol in the skin.

It can be deduced from all of the foregoing that supplementation of glycerol is beneficial for the skin.

That is why many cosmetics have glycerol in their composition. Thus, with application once or twice a day, the skin benefits from the positive effects of glycerol. However, this solution requires topical treatment of the skin every day.

Just like the use of a cosmetic, injection of an aqueous solution of glycerol in the skin makes it possible to benefit from the positive effects of glycerol in the very short term. In fact, almost all of the glycerol injected migrates rapidly from the zone of injection to the stratum corneum, and then is removed from the surface of the skin by daily washing. Thus, the beneficial action of glycerol is “one-off” (PNAS, 100(12):7360-7365, June 2003, Hara, M. W.; Verkman, A.S./Journal d'Investigation Dermatologique, 125: 288-293, 2005, Choi, H. C).

Injectable solutions of glycerol containing hyaluronic acid (HA) are described in the prior art. Owing to their viscoelastic characteristics, these solutions appear to allow delayed release of glycerol. However, when injected into the skin, these solutions do not provide long-term supplementation of glycerol (supplementation for a period of at most one week). In fact, hyaluronic acid is metabolized within the skin in less than a week (Wenner-Gren International series; The chemistry, biology and medical applications of hyaluronan and its derivatives, Laurent, T. C.).

Consequently, an injectable hydrogel providing gradual, long-term release of glycerol in the skin does not exist in the prior art.

Thus, the aim of the invention is to propose a novel injectable hydrogel that has numerous qualities and which avoids some of the drawbacks mentioned above.

Accordingly, the invention relates to an injectable hydrogel comprising, by weight, in a physiologically acceptable carrier fluid: 0.01% to 5% of glycerol and 0.1% to 5% of a crosslinked biopolymer of hyaluronic acid or of one of the salts thereof, relative to the total weight of the hydrogel, characterized in that hyaluronic acid or one of the salts thereof is crosslinked by formation of covalent bonds between the chains of said biopolymer by means of bifunctional or polyfunctional molecules, said injectable hydrogel being sterilized in moist heat and having a Tanδ at a frequency of 1 Hz less than or equal to 1.10.

The parameter Tanδ is a usual rheological parameter, which is defined as the tangent of the phase angle, said phase angle being the phase difference between stress and strain during an oscillatory rheological test. The tangent of the phase angle makes it possible to characterize the viscoelastic properties of a gel, notably based on crosslinked hyaluronic acid as was demonstrated in the work by Falcone (Journal of Biomedical Material Research, part A, January 2008, Falcone, S. J.; Berg, R. A.). For a gel based on crosslinked hyaluronic acid, the parameter Tanδ is probably correlated with the persistence of the gel in the skin, i.e. its presence at the injection site.

Completely surprisingly, a hydrogel based on 0.01% to 5% of glycerol and 0.1% to 5% of hyaluronic acid crosslinked by formation of covalent bonds, followed by sterilization in moist heat, said hydrogel possessing viscoelastic properties such that Tanδ at a frequency of 1 Hz is less than or equal to 1.10, makes it possible:

• • to increase considerably the duration of release of glycerol in the skin relative to a gel based on glycerol and noncrosslinked hyaluronic acid sterilized in moist heat (type of gel with glycerol described in the prior art) (see comparative example 2);
  • to increase significantly the duration of release of glycerol in the skin relative to a gel based on glycerol and crosslinked hyaluronic acid not sterilized in moist heat (see comparative example 1);
  • to increase significantly the persistence, i.e. the presence of the gel at the injection site, relative to a gel based on glycerol and crosslinked hyaluronic acid not sterilized in moist heat (see comparative example 1).

This quadruple selection: covalent crosslinking of hyaluronic acid at a suitable concentration, presence of glycerol at a suitable concentration, sterilization in moist heat at a sufficiently high temperature and obtaining a gel possessing particular viscoelastic properties, makes it possible to obtain an injectable hydrogel with glycerol having a persistence of several months and a capacity for releasing glycerol in the skin over a long period. Thus, through the combination of the particular characteristics of the injectable hydrogel according to the invention, the glycerol is gradually eluted from the gel over a long period, thus allowing the skin to benefit from long-term supplementation of glycerol over time.

According to the invention, the concentration of glycerol is from 0.01% to 5 wt. %, preferably from 0.5% to 2.5% relative to the total weight of the hydrogel. Beyond 5 wt. %, the osmolarity of the hydrogel is too high, making it unsuitable for injection into the skin. According to the invention, the concentration of crosslinked hyaluronic acid or of one of the salts thereof is from 0.1% to 5 wt. %, preferably from 0.5% to 3% relative to the total weight of the hydrogel.

According to the invention, the hydrogel possesses a Tanδ at a frequency of 1 Hz less than or equal to 1.10. Preferably, the hydrogel possesses a Tanδ at a frequency of 1 Hz less than or equal to 0.80.

Preferably, the molecular weight of the hyaluronic acid or of one of the salts thereof (before crosslinking) is between 1000 Da and 10×10⁶ Da, preferably between 500,000 and 4×10⁶ Da.

According to the invention, crosslinking is effected by means of bifunctional or polyfunctional molecules selected for example from epoxides, epihalohydrins and divinylsulfone, on noncrosslinked or already crosslinked hyaluronic acid with or without one or more other polysaccharides of natural origin. For example, the crosslinking agent used is butanediol diglycidyl ether (BDDE) or divinylsulfone (DVS).

According to a particular embodiment of the invention, the gel can also comprise other biocompatible polymers (such as polysaccharides of natural origin) and/or other pharmacologically active substances (such as lidocaine, a local anesthetic) or nonpharmacologically active substances (such as vitamins or mineral salts) having positive effects on the organism or on the hydrogel.

According to the invention, said injectable hydrogel is sterilized in moist heat.

Advantageously, sterilization is carried out at a temperature above 100° C. Preferably, sterilization is carried out at a temperature above or equal to 121° C.

For example, one of the following sterilization cycles can be used: 131° C. for 1 min/130° C. for 3 min/125° C. for 7 min/121° C. for 20 min or 121° C. for 10 min.

The present invention also relates to a process for manufacturing an injectable hydrogel as described above, comprising the steps consisting of:

• • a) preparing a first mixture comprising at least 0.1% to 5 wt. % of a crosslinked biopolymer of hyaluronic acid or of one of the salts thereof by formation of covalent bonds between the chains of said biopolymer by means of bifunctional or polyfunctional molecules,
  • b) adding 0.01% to 5 wt. % of glycerol before, during or after crosslinking of the biopolymer of hyaluronic acid or of one of the salts thereof during step a), so as to form a homogeneous mixture,
  • c) transforming the gel thus obtained into a form that is ready to use,
  • d) sterilizing the product in moist heat.

The glycerol can in fact be added to the gel based on crosslinked hyaluronic acid during manufacture of the gel based on crosslinked hyaluronic acid, i.e. at step a) before or during crosslinking of the gel based on hyaluronic acid or quite simply at the end of step a): after the crosslinking of the biopolymer.

During this process for manufacturing an injectable hydrogel, the sterilization temperature is above 100° C.

Preferably, sterilization is carried out at a temperature above or equal to 121° C.

In particular, during the process for manufacture of the hydrogel, sterilization is carried out according to one of the following cycles: 131° C. for 1 min/130° C. for 3 min/125° C. for 7 min/121° C. for 20 min or 121° C. for 10 min.

The gel thus obtained possesses rheological characteristics such that Tanδ at a frequency of 1 Hz is less than or equal to 1.10 and is preferably less than or equal to 0.80.

One aim of the present invention also relates to a kit that is in the form of a syringe and contains the injectable hydrogel as described above.

According to one embodiment of the kit, this can be in the form of a vial or bottle containing the injectable hydrogel according to the invention and suitable for being taken up in an injecting syringe.

The present invention also relates to the use of an injectable hydrogel according to the invention or of the kit as described above, for improving the chemical, physical and mechanical characteristics of the skin of mammals.

In particular, the present invention also relates to the use of an aforementioned injectable hydrogel or of the kit as described above, for filling wrinkles and lines and/or for creating volume and/or for skin moisturization and/or for reviving epidermal cellular activity and/or for maintaining the mechanical properties of firmness and elasticity of the skin and/or maintaining epidermal and dermal stimulation and/or for stimulating the antioxidant activity of the dermis and/or preventing skin aging and/or accelerating the process of wound healing.

The invention will be better understood and other aims, details, characteristics and advantages thereof will become clearer on reading the following description of examples of carrying out the invention, referring to the appended figures in which:

FIG. 1 presents a curve showing the percentage change in the concentration of glycerol in the surface layers of the epidermis from two gels: gel A (gel that has not undergone sterilization in moist heat) and gel B (according to the invention) over time in weeks;

similarly, FIG. 2 presents a curve showing the percentage change in the concentration of glycerol in the surface layers of the epidermis from two gels: gel B (according to the invention) and gel C (gel based on noncrosslinked hyaluronic acid) over time in weeks.

EXAMPLE OF CARRYING OUT THE INVENTION

An example of preparation of a hydrogel is presented for illustrating the invention, but it does not in any way limit the scope of the invention.

3.5 g of sodium hyaluronate (MW=2.2×10⁶ Da) is added to 25 ml of a solution of NaOH at 1% (w/w). The mixture is left at rest for 1 h and then mixed with a spatula for 10 minutes. The crosslinking reaction is then started by adding 263 μl of butanediol diglycidyl ether (BDDE) and it is mixed with a spatula for 10 minutes. The reaction mixture is placed on a water bath at 50° C. for 2 h. The mixture is adjusted to physiological pH with 1M HCl. The volume is adjusted to 116 ml with a solution buffered at pH=7.

The gel thus obtained is then dialyzed for 24 h (regenerated cellulose, limit of separation: MW=60 kDa) against a solution buffered at pH=7 in order to remove residual crosslinking agent.

1.7% (w/w) of glycerol is added to the gel based on crosslinked hyaluronic acid, then the mixture is homogenized for 15 minutes using a spatula.

The gel is then put in 1 ml glass syringes. The total concentration of sodium hyaluronate is measured at 2.1% (w/w).

The total concentration of glycerol is measured at 1.68% (w/w).

The pH of the gel is measured at 7.02 and its osmolarity at 308 mOsm/kg.

The measurement of initial biocontamination is less than 10 CFU/g.

Half of the syringes obtained constitute hydrogel A.

The other half of the syringes obtained are sterilized in moist heat following a cycle [131° C., 1 minute]. These syringes constitute hydrogel B, according to the invention.

The rheological properties of the hydrogels are investigated by means of a type AR1000 rheometer (TA instruments) with a flat geometry of 40 mm, an air gap of 1000 microns and an analysis temperature of 25° C.

For hydrogel A, the measured value of the viscoelastic parameter Tanδ (at 1 Hz) is equal to 0.51.

For hydrogel B, the measured value of the viscoelastic parameter Tanδ (at 1 Hz) is equal to 0.67.

Comparative Test 1 Between Hydrogel A And Hydrogel B (According to the Invention) from the Above Example:

Tests In Vivo on Rabbit:

Four calibrated intradermal injections of 0.2 ml of hydrogel A and four calibrated intradermal injections of 0.2 ml of hydrogel B (hydrogel according to the invention) were performed on one and the same rabbit.

At t=0, the presence of a “papule” is found at each injection site, proof of the presence of the gel at the injection site. The diameter of each papule is measured with a caliper gauge and then the initial average area of one papule is calculated for hydrogel A and for hydrogel B.

At t=3 months, the presence of all of these papules is still found for the 2 types of hydrogels injected (the papules have an average area greater than ½ the initial average area of the 4 papules of hydrogel A or of the 4 papules of hydrogel B).

At t=6 months, it is found that the papules formed with hydrogel B according to the invention are still present (the papules have an average area greater than ½ the initial average area of the 4 papules of hydrogel B) whereas the papules obtained with hydrogel A are now barely visible (the papules have an average area less than ½ the initial average area of the 4 papules of hydrogel A).

Hydrogel B according to the invention therefore possesses a persistence that is significantly greater than that of hydrogel A.

In addition, the concentration of glycerol in the surface layers of the epidermis of the rabbit, at each papule obtained, was measured once a week for a maximum of 10 weeks. The mean value of the glycerol concentrations determined is calculated for each gel investigated and for each time investigated. The variations of the glycerol concentration determined over time for hydrogel A and for hydrogel B are compared (see FIG. 1).

Faster kinetics of release of glycerol in the skin is found for hydrogel A than for hydrogel B according to the invention.

Comparative Test 2 between Hydrogel B (According to the Invention) from the Above Example and a Hydrogel Based on Noncrosslinked Hyaluronic Acid and Glycerol, Sterilized in Moist Heat (Hydrogel C Described Below):

A gel is constituted of 1.7% (w/w) of glycerol and 2.1% (w/w) of noncrosslinked hyaluronic acid (MW=2.2×10⁶ Da) in a solution buffered at pH=7. After filling in 1 ml glass syringes, the gel is sterilized in moist heat following a cycle [131° C., 1 minute]. These syringes constitute hydrogel C.

The rheological properties of hydrogel C are investigated using a type AR1000 rheometer (TA instruments) with a flat geometry of 40 mm, an air gap of 1000 microns and an analysis temperature of 25° C.

For hydrogel C, the measured value of the viscoelastic parameter Tanδ (at 1 Hz) is equal to 0.64.

Tests In Vivo on Rabbit:

Four calibrated intradermal injections of 0.2 ml of hydrogel C were performed on the same rabbit as for the previous comparative test.

At t=0, the presence of a “papule” is found at each injection site, proof of the presence of the gel at the injection site. The diameter of each papule is measured with a caliper gauge and then the initial average area of one papule is calculated for hydrogel C.

At t=1 week, it is found that the papules obtained with hydrogel C are now barely visible (the papules have an average area of less than ½ the initial average area of the 4 papules of hydrogel C).

At t=2 weeks, it is found that all of the papules obtained with hydrogel C are no longer visible.

The hydrogel B according to the invention therefore possesses considerably greater persistence than hydrogel C.

In addition, the glycerol concentration in the surface layers of the epidermis of the rabbit, at each papule obtained, was measured after 1, 2, 3 and 4 weeks. The mean value of the glycerol concentrations determined is calculated for each time investigated. The variations of the glycerol concentration determined over time for hydrogel C and for hydrogel B are compared (see FIG. 2).

The kinetics of release of glycerol in the skin is found to be much faster for hydrogel C than for hydrogel B according to the invention.

Thus, real synergy is found between crosslinked hyaluronic acid and glycerol, after sterilization in moist heat in the formulation according to the invention. The presence of glycerol in the formulation according to the invention allows its persistence, i.e. the residence time of the gel at the injection site, to be increased significantly, and consequently it also makes it possible to increase the release of glycerol in the skin over time.

Thus, the gel based on glycerol and hyaluronic acid crosslinked by formation of covalent bonds, having undergone sterilization in moist heat and possessing viscoelastic properties such that Tanδ at a frequency of 1 Hz is less than or equal to 1.10, permits gradual, long-term release of glycerol in the skin. The glycerol and crosslinked hyaluronic acid act in synergy when they are combined according to the present invention. This can be explained by the fact that sterilization in moist heat, in the conditions of the invention, would permit thermal activation of the glycerol and/or of the crosslinked hyaluronic acid, which would permit better crosslinked HA-glycerol affinity, and consequently longer-term release of glycerol in the skin (relative to a gel not sterilized in moist heat).

It is important to point out, to clarify the relevance of the invention:

• • that a gel based on (non-crosslinked) hyaluronic acid with glycerol, sterilized in moist heat (type of gel described in the prior art), cannot ensure long-term release of glycerol in the skin
  • its duration of release is in fact less than about 1 week;
  • that a gel based on hyaluronic acid crosslinked covalently with glycerol, not sterilized in moist heat, cannot give results equivalent to the formulation according to the invention (significantly shorter duration of release of glycerol in the skin);
  • that a gel based on hyaluronic acid crosslinked covalently with glycerol, possessing rheological properties such that Tanδ at a frequency of 1 Hz is greater than 1.10 does not possess suitable viscoelastic properties and/or sufficient persistence to obtain results equivalent to the formulation according to the invention. The duration of release of glycerol in the skin is in fact significantly shorter.

It is also important to point out that these elements could not be deduced by a person skilled in the art.

In fact, a person skilled in the art knows that crosslinking a gel based on hyaluronic acid makes it possible to increase the persistence of said gel in the skin. However, bearing in mind the low molecular weight of glycerol (MW=92 g/mol) and the low concentration of hyaluronic acid in the gel (concentration less than 5 wt. %), a person skilled in the art may easily assume that the glycerol molecule will easily migrate within the gel (steric hindrance of the gel induced by hyaluronic acid insufficient to trap the glycerol in the gel) and consequently that the glycerol will quickly be released in the skin. A person skilled in the art may also easily assume that crosslinking of hyaluronic acid will cause little change in the kinetics of release of glycerol in the skin relative to a gel based on noncrosslinked hyaluronic acid as bridging of the chains of hyaluronic acid does not produce a large increase of steric hindrance within the gel.

In other words, a person skilled in the art could not predict that the combination [glycerol+hyaluronic acid crosslinked by formation of covalent bonds+sterilization in moist heat+particular viscoelastic properties] would permit long-term, gradual release of glycerol in the skin.

Although the invention has been described in relation to particular embodiment, it is quite clear that it is by no means limited to this and that it comprises all the equivalent techniques of the means described as well as their combinations if the latter fall within the scope of the invention.

Claims

1. An injectable hydrogel comprising, by weight, in a physiologically acceptable carrier fluid: 0.01% to 5% of glycerol and 0.1% to 5% of a crosslinked biopolymer of hyaluronic acid or one of the salts thereof relative to the total weight of the hydrogel, characterized in that the hyaluronic acid or one of the salts thereof is crosslinked by formation of covalent bonds between the chains of said biopolymer by means of bifunctional or polyfunctional molecules, said injectable hydrogel being sterilized in moist heat and having a Tanδ at a frequency of 1 Hz less than or equal to 1.10.

2. The injectable hydrogel as claimed in claim 1, in which glycerol is present at a concentration by weight in the range from 0.5% to 2.5% relative to the total weight of the hydrogel.

3. The injectable hydrogel as claimed in claim 1, in which hyaluronic acid or one of the salts thereof is present at a concentration by weight in the range from 0.5% to 3% relative to the total weight of the hydrogel.

4. The injectable hydrogel as claimed in claim 1, for which the parameter Tanδ at a frequency of 1 Hz is less than or equal to 0.80.

5. The injectable hydrogel as claimed in claim 1, in which the molecular weight of the hyaluronic acid or of one of the salts thereof is between 1000 Da and 10×106 Da, preferably between 500,000 and 4×106 Da.

6. The injectable hydrogel as claimed in claim 1, in which crosslinking is effected by bifunctional or polyfunctional molecules selected from epoxides, epihalohydrins and divinylsulfone, on noncrosslinked or already crosslinked hyaluronic acid with or without one or more other polysaccharides of natural origin. For example, the crosslinking agent used can be butanediol diglycidyl ether (BDDE) or divinylsulfone (DVS).

7. The injectable hydrogel as claimed in claim 1, characterized in that it comprises at least one other biocompatible polymer and/or at least one pharmacologically active substance and/or at least one nonpharmacologically active substance having positive effects on the organism or on the hydrogel.

8. A process for manufacturing an injectable hydrogel, comprising the steps consisting of: a) preparing a first mixture comprising at least 0.1% to 5 wt. % of a crosslinked biopolymer of hyaluronic acid or of one of the salts thereof by formation of covalent bonds between the chains of said biopolymer by means of bifunctional or polyfunctional molecules,b) adding 0.01% to 5 wt. % of glycerol before, during or after the crosslinking of the biopolymer of hyaluronic acid or of one of the salts thereof during step a), so as to form a homogeneous mixture,c) transforming the gel thus obtained into a form that is ready to use,d) sterilizing the product in moist heat.

9. The process for manufacturing an injectable hydrogel as claimed in claim 8, in which the sterilization temperature is above 100° C.

10. The process for manufacturing an injectable hydrogel as claimed in claim 8, in which sterilization is carried out at a temperature above or equal to 121° C.

11. The process for manufacturing an injectable hydrogel as claimed in claim 8, in which sterilization is carried out according to one of the following cycles: 131° C. for 1 min/130° C. for 3 min/125° C. for 7 min/121° C. for 20 min or 121° C. for 10 min.

12. The process for manufacturing an injectable hydrogel as claimed in claim 8, for which the gel obtained possesses a Tanδ at a frequency of 1 Hz less than or equal to 1.10, preferably less than or equal to 0.80.

13. A kit in the form of a syringe and containing the injectable hydrogel as claimed in claim 1.

14. A kit in the form of a vial or bottle and containing the injectable hydrogel as claimed in claim 1 and suitable to be taken up in an injecting syringe.

15. The injectable hydrogel as claimed in claim 1 applied for improving the chemical, physical and mechanical characteristics of the skin of mammals.

16. The injectable hydrogel as claimed in claim 1 applied for filling wrinkles and lines and/or creating volume and/or for skin moisturization and/or for reviving epidermal cellular activity and/or maintaining the mechanical properties of firmness and elasticity of the skin and/or maintaining epidermal and dermal stimulation and/or for stimulating the antioxidant activity of the dermis and/or for preventing skin aging and/or accelerating the process of wound healing.