Patent Application
20110140311
The present invention relates generally to thermoplastic molding methods and apparatus, and more particularly pertains to methods and apparatus for injection molding thermoplastic.
Injection molding machines are expensive to purchase, require expensive factory space and substantial quantities of electrical power. Additionally, set-up and operation of injection molding machines is a highly subjective trade, wherein there are significant set-up charges each time a tool is set. Starts and stops of such machines can be very expensive and there are always technicians and/or operators directly involved in such activities. The general practice on start up of an injection molding machine is provide an initial machine configuration (e.g., screw rotation rate, operable screw barrel temperature, injection pressure, etc.), then a “purging” process is performed where an operator first confirms that the injection molding machine is not connected to a mold, and then commences to process plastic but discarding the resulting plastic melt until the operator judges that the output plastic looks hot enough and appears to be of a low enough viscosity to commence molding test parts. Subsequently, a plurality of test parts are produced for inspection and/or analysis to thereby determine whether the machine is configured appropriately to successfully produce parts having the intended characteristics (e.g., fully conforming to the intended part shape, density, elasticity, etc.). Accordingly, the machine settings are generally fixed for mass producing the part.
The above described injection molding practice has substantial problems in that various part affecting parameters can change during the part mass production. For example, the operator settings may not be adequate for keeping the injection machine in a state for maintaining part consistency. In particular, it may not be possible to adequately determine whether the plastic is sufficiently uniformly heated so that acceptable parts can be produced therefrom. Additionally, since patches of plastic raw material inherently vary in their composition, variation in part production may be necessary dependent upon variation in the plastic raw material. Furthermore, the various injection molding parameters (whether settable by an operator or not) are generally interrelated with respect to producing acceptable parts. For instance, (a) nozzle injection pressure and plastic flow rate are inversely related, (b) plastic flow rate and plastic temperature are generally directly related, and (c) changes in screw rotation may generally be directly related to plastic temperature, although such may depend on the degree to which plastic heating is performed by shearing of the plastic in the screw barrel. Accordingly, it is very difficult to effectively and consistently configure a conventional injection molding machine to produce acceptable quality parts, and for very small quantities of parts the overhead for configuring such a machine can unacceptably expensive.
Accordingly, it would be advantageous to have an injection molding system and method of operation that is substantially more cost effective to manufacture and operate. Additionally, it is desirable for such a system and method to be less dependent upon operator trial and error to configure such systems for consistently producing acceptable quality parts.
A thermoplastic injection molding system and method of use is disclosed for molding parts from heated plastics and other organic resins, wherein the system includes an injection molding machine and a controller for controlling the machine such that when the controller is supplied with input from various machine sensors providing real time measurements related to the characteristics of the plastic or resin (collectively referred to a “plastic” hereinbelow) in the injection molding machine, the controller dynamically adjusts the injection molding process to achieve more consistent and reliable molded parts.
The injection molding machine disclosed herein includes a screw for transporting the solid unmolded plastic material (e.g., pellets) from a storage container or hopper to an injection zone or chamber for collecting melted plastic in preparation for injecting the melted plastic therein into mold. The screw is configured within a barrel or cylinder in a manner that substantially prevents the plastic being conveyed therein from being sheared, and in particular, prevents such shearing between the barrel and the screw. Accordingly, the rotation of the screw when conveying plastic requires substantially less torque than prior art injection molding machines having a screw that shears the plastic. In particular, the tolerances and configuration of the screw within the barrel are such that the gaps between the inside diameter of the barrel and the outside diameter of the screw are small enough so that the plastic pellets cannot be sheared therebetween. Moreover, the barrel (and plastic therein) is heated, insufficient heat is applied to allow the plastic to deform into such gaps and be sheared, and insufficient heat is applied to induce the plastic to adhere to the screw flutes or the inside of the barrel for substantially an entire length of the screw. Thus the present injection molding machine uses substantially less energy to rotate the screw. Furthermore, the screw can be easily removed from the barrel since both the screw and barrel are substantially free of adhered to plastic.
Due to the screw being primarily a conveyance mechanism for the plastic pellets, the screw can be designed for efficient and effective conveyance rather than for shearing. Moreover, a result of such a screw design in the present injection molding machine is that the pellets compact within the barrel as they travel toward and ultimately enter plastic melting zones of the present injection machine. Such compaction has a particular advantage of effectively providing a barrier for preventing melted plastic from leaking or flow backward in the injection molding machine. Accordingly, a valve for preventing such flow back is unnecessary. However, in the event that such compaction is diminished enough so that there is plastic melt flow back, there may be one or more thermocouples or other heat sensors for detecting an inappropriate increase in heat, and providing such information to the controller (e.g., a computer system specifically configured for controlling the production of parts by the present injection molding machine, and/or programmable logic controller), wherein one or more of the following may be initiated by the controller: an operator may be alerted, the screw rotation rate at least temporarily increased, shutting down the mold injection machine (e.g., in the event that there are insufficient plastic pellets in the hopper), activating a pellet jam breaking mechanism for jams in the hopper, and/or activating a mechanism for automatically feeding additional pellets to the hopper.
The hereinabove described screw and a corresponding extent of the barrel may be considered as a first zone of the injection molding machine, wherein there is a series linearly aligned injection molding machine zones for transforming the plastic into a melt acceptable to mold parts. At the end of this first zone (e.g., substantially where the plastic pellets compact), a second zone commences wherein one or more heat sources (controlled by the controller) are active for heating the plastic within this zone so that the plastic becomes flowable. In general, the increase in heat over that of the first zone may be only a few degrees above the heat applied in the first zone (e.g., an increase in temperature in a range of 25-250° F.). The heat sources may be one or more of a resistance, inductance or ultrasonic heat source. These heat sources are positioned and arranged so that the heat generated affects the plastic, within a relatively short portion of the screw, and substantially at the termination of the screw flutes, so that the plastic becomes flowable. More specifically, the plastic becomes sufficiently flowable (due to pressure of additional upstream plastic moving into this second zone) to flow downstream through heating channels of a third zone described hereinbelow. Since most plastics do not conduct heat well, the second zone (also known as the “transition zone” herein) may be configured so that there is an increase in heated surface area for contacting the plastic within this second zone. In one embodiment, such an increase in heated surface area may be at least partially due to a heated annular interior barrel wall that serves as an intermediary barrel portion for connecting the barrel interior of the first zone to the downstream third zone having a barrel interior of reduced cross sectional dimension. In particular, the portion of the barrel extent for the first zone may have a first diameter in a range of, e.g., 2 inches to 10 inches, and the interior dimension of the third zone may have a diameter in a range of, e.g., 40% to 60% less. Such a heated wall provides a substantial increase in surface area for transmitting heat to the adjacent plastic. Moreover, such a wall can be configured to be substantially perpendicular to the general helical path of the plastic to thereby induce a buildup of plastic (and corresponding pressure which may be in a range of 100-5000 psi (pounds per square inch)) adjacent to and in contact with this wall for facilitating heat transfer to the plastic. Additionally, the terminal end of the screw within the second zone may terminate in a substantially convex shape (e.g., a truncated conical surface which forces the plastic closer the heated wall). In one embodiment, this terminal end of the screw may also radiate heat via, e.g., one of the heat sources identified hereinabove.
It is worthwhile to note that since sufficient heat to induce adherence of the plastic to internal machine surfaces only commences in the second zone, and since this zone is of short length (relative to the screw length and the length of the machine) any plastic that adheres to the internal machine surfaces in this second zone (e.g., due to a machine shutdown or heat interruption) will not be so substantial that the screw cannot be readily extracted from the barrel. In particular, the linear extent of the total barrel residing in the second zone may be only 2% to 10% of the length of the screw, and there may be few (if any) screw portions (e.g., attenuated screw flutes) in this second zone where there could be a sufficient buildup of resolidified plastic that would substantially inhibit the screw from being extracted without damaging some portion of the machine or without disassembling the barrel screw combination from the remainder of the machine.
In the third zone following the second or transitional zone, the flowable plastic is forced by pressure buildup in the second zone, to flow through one or more (preferably a plurality of) channels of this zone, wherein such channels conduct the plastic through the length of this third zone, and into a fourth or injection zone described hereinbelow. The channels may be distributed circumferentially about an extension of the screw shaft, wherein in at least one embodiment this extension includes an injection plunger that reciprocates along the rotational axis of the screw for repeatedly injecting melted plastic into a mold. Each channel may extend parallelly to the shaft axis between a receiving opening for receiving plastic, and an exit opening from which the plastic exits. The third zone is also heated by one or more of the heat sources for continuing to elevate the temperature of the plastic provided therein. Moreover, since the channel(s) may substantially increase the heated barrel surface area in contact with the plastic, the plastic in the channel(s) liquefies, or substantially reduces its viscosity so that it may flow into the injection zone (when not prevented) at a rate in direct proportion to the number of screw rotations realized within the system. The temperature increase in the plastic due the heat imparted via the channel(s) may be in a range of 25-250° F. Note that the heat sources for this third zone may be external to the portion of the barrel for the third zone, embedded within the barrel, and/or provided by the extension to the screw shaft (such extension may have a length of, e.g., 1.5 inches to 12 inches depending on the size and plastic processing capacity of the present injection mold machine).
In at least some embodiments, the shaft extension extends (along the axial length of the barrel) substantially the entire length of the third zone. However, when the plunger is fully retracted into the screw shaft, the exit opening(s) of the channel(s) opens into the injection zone so that melted plastic can exit the channel(s) and into this injection zone. Thus, since the melted plastic is typically under pressure (e.g., a range of 100-1000 psi) in the channel(s), and there is a reduced pressure in the injection zone (e.g., ambient atmospheric pressure), plastic will flow out of the channels and into the injection zone whenever such a pressure differential exists. However, when the plunger extends into the injection zone for forcing plastic into a mold, such extension closes the channel exit opening(s) so that there is substantially no backwards flow of plastic from the injection zone into the channel(s) due to the plunger induced pressure increase in the injection zone. Accordingly, the plunger serves a dual purpose of both forcing melted plastic into the mold, and also iteratively opening and closing the channels to the injection zone. So, in particular, the present injection mold machine requires no separate valve for metering the plastic melt into the injection zone.
The fourth or injection zone (also identified as a “plastication zone”) includes an injection chamber for receiving plastic from the channels, and an injection tube through which plastic flows from the injection chamber to an injection nozzle which is attached to the mold for providing plastic therein. As with other plastic conveying portions of the present injection molding machine, the injection chamber and the injection tube are connected so that the melted plastic flows generally in a straight path along the axis of the barrel. Thus, this linear arrangement prevents plastic pressure drops which can occur where the pressurized liquid plastic is constrained to abruptly flow in substantially different directions (e.g., around a 90 degree corner).
The injection zone also includes one or more of the heat sources for providing additional heat to the plastic provided therein. As with the heat sources in the other zones, the heat sources for the injection zone are controlled by the controller (e.g., a computer system specifically configured for controlling the production of parts by the present injection molding machine, and/or programmable logic controller),
It is worthwhile to note that in one embodiment of the present injection mold machine, a vacuum controlled break valve is provided for control of gas (e.g., air) entering the injection zone. In particular, the vacuum break valve allows air to enter the injection chamber when the injection plunger lowers the pressure within the fourth zone (in particular, the injection chamber) due to the plunger retracting from the injection chamber and into the screw shaft extension. In at least one embodiment, the vacuum break valve is provided along a shaft of the plunger, wherein this plunger shaft reciprocates into and out of the screw shaft. Accordingly, when a lower pressure (e.g., lower than ambient atmospheric pressure) occurs in the injection chamber, the vacuum break valve opens to introduce air into the injection chamber as will be described further hereinbelow. During plunger retraction (toward and/or into the screw shaft), the vacuum break valve remains open until (or just before) the plunger retracts sufficiently so that the channels are open to the injection chamber, and then the valve closes hereby preventing the melted plastic entering the chamber from exiting via the valve.
It is additionally worthwhile to note that when plastic is urged under pressure into the injection chamber, the heated gas (e.g., air) therein readily escapes as a backflow product through, e.g., the channel(s). Such gas backflow is facilitated in the present injection molding machine since the screw does not tightly fit within the barrel, and thus, gas can escape into the barrel (via the channel(s)) as plastic enters the injection chamber. Empirical evidence indicates that when the present injection molding machine is operating for molding acceptable parts, the pressure in the channels is effective for rapidly filling of the injection chamber with melted plastic. Accordingly, it is believed that the melted plastic enters the injection chamber at sufficient velocity to fill this chamber with melted plastic beginning with the opposite end of the chamber from the chamber end that repeatedly provides the plastic via the channel(s). Accordingly, since the exit opening for providing plastic from the injection chamber to the injection tube is located in this opposite end of the injection chamber, when the high velocity plastic commences to fill the chamber, it does so from the chamber opposite end. Consequently, the gas within the injection chamber is displaced from this opposite chamber end thereby substantially preventing gas pockets from being trapped within the plastic proximate exit opening. Moreover, since it is believed that the melted plastic collects within the chamber from this opposite end first, the gas within the chamber is forced to travel backward toward the channel opening(s) as the melted plastic under pressure injects into the injection chamber. In some embodiments, such channel opening(s) may be shaped to facilitate the melted plastic filling the injection chamber from the opposite end to the chamber end having the channel opening(s). In particular, such channel opening(s) may be shaped to direct the melted plastic into particular portions of the injection chamber. For example, the channel opening(s) may be shaped so that when the channel(s) initially opens, melted plastic is directed generally toward the interior of the opposite end of the chamber, and as the channel opening(s) widens, the melted plastic may be generally directed to a portion of the axial centerline of the plunger reciprocation wherein this portion is progressively closer to the channel opening(s). Accordingly, the gas backflow may be generally along or adjacent to the chamber sides providing relatively direct backflow paths to the channel open(s).
Moreover, it is aspect of the present injection molding machine, that since such escaping gas is heated to substantially the temperature of the injection chamber, this gas may be reused to facilitate the heating of the plastic in the second and/or the third zones. Alternatively/additionally, such heated gas may also be recirculated back into the injection chamber via the vacuum break valve described above. Accordingly, the recycling/reuse of the heat within the escaping gas increases the efficiency of the present injection molding machine.
Further note that in one embodiment, there may be backflow vents separate from the above described channels, wherein such backflow vents do not conduct melted plastic into the injection chamber.
The injection tube of the fourth zone may be of reduced cross sectional area in comparison to the injection chamber, and additionally may be of sufficient length to contain at least one volume of plastic from the injection chamber, but generally less than two such volumes. Accordingly, since the injection tube has an increased surface area (relative to volume) in comparison to the injection chamber, and is also heated, the plastic therein is acceptably liquefied for mold injection. However, due to the relatively small volume of plastic therein, the energy consumption of the injection molding machine is reduced over similar prior art injection molding machines.
The fourth zone may also include a programmable nozzle valve at or proximate to the injection nozzle, wherein this valve opens to release melted plastic in a mold cavity when there is sufficient pressure within the injection nozzle.
It is an aspect of the present injection molding machine that the controller mentioned hereinabove receives various sensor readings indicative of plastic temperatures, plastic pressures, and plastic viscosity. In particular, the controller receives the following measurements from the injection molding machine:
It is a further aspect of the present injection molding system that it may achieve plastic and resin plastication through the conduction of electrically generated heat as opposed to pressure induced shear heat generation methods currently used by most injection molding machines. The conduction of electrically generated heat provides a process of plastication that is more accurate than shear generated heat. Additionally, since there is also a reduced pressure applied to the plastic (due to the lack or substantially reduced shearing), the injection molding machine may be used to mold parts from non-traditional materials (e.g., bio-based resins of any type, metal injection molding feedstock, and liquid silicone) that would degrade under shearing, and may be used to produce part with enhanced performance characteristics.
It is a further aspect of the present injection molding system and method of use that there may be continuous material plastication that preserves the plastic/resin quality with exact application of prescribed levels of heat to known volumes of plastic/resin. This method dramatically reduces the force and strength requirements for the subsequent injection process (via the plunger), thereby allowing a more accurate and responsive delivery of melted plastic/resin into an injection mold cavity.
It is a further aspect of the present injection molding system and method of use that integrated pressure and temperature sensors may be used by the controller to accurately quantify the output of the present injection molding machine, and in particular during the injection molding cycle for perfecting changes to the injection molding process in order to affect parts being produced. This is accomplished even when variations in the raw material are present. Moreover, such real time mold injection process changes are provided by an injection mold controller that is data-driven from measurements obtained from sensors provided in the injection molding machine. In particular, such a data-driven machine and method results in various components of the present injection molding machine having activations that are more asynchronous to one another than the lock step or a predetermined non-deviating sequence of steps prevalent in the prior art.
It is a further aspect of the present injection molding system and method that this system can initiated without an operator present (assuming the proper mold is connected to the injection molding machine, and this machine is appropriately clean). Moreover, the presently disclosed injection molding system and method can also operate unattended for molding parts. Thus, activation and operation of the present injection molding system may be performed automatically and remotely such as via a communications network (Internet) activation, wherein the present injection molding system and method remain unattended while producing the desired parts.
The above described aspects of the present injection mold system and method were combined at least in part due to the recognition of the longstanding unmet drawbacks in various prior art injection molding machines and methods. Moreover, even relatively recent supposedly improvements in plastic injection mold technology have substantial drawbacks. For example, the following recent references have been considered, and are incorporated herein by reference:
Other features and benefits of the presently disclosed injection molding machine and method of use are disclosed in the accompanying figures, and the description hereinbelow. In particular, various novel aspects of the presently disclosed injection molding machine and method not described above may be described hereinbelow. Accordingly, this Summary section is intended to present a general overview of the present injection molding machine and method of use, but may not identify every patentable aspect thereof.
In order to more fully appreciate the present invention, the following references are fully incorporated herein:
The above-identified references each have their own corresponding drawbacks that make them at most partially useful in addressing injection molding machine related problems.
An embodiment of the presently disclosed injection molding system 12 is shown in
In reference to
The barrel 40 also includes an opening 84 for receiving plastic pellets from the escapement 28. Such pellets enter the barrel 40 and are retained between the flights 88 of an auger screw 92 (also “screw” herein) provided within the barrel. The screw 92 is preferably concentric or coaxial with the barrel 40. The screw 92 includes a shaft 96 from which one or more helical flights 88 project outwardly therefrom, and such flights 88 extend from generally below the escapement 28 through the first stage 44 of the barrel 40. The shaft 96 also extends horizontally in the opposite direction from the escapement 28, wherein a thickened shaft portion 100 adjacent to the throat block 32 is secured thereabout with a bearing 104, which is provided within a mounting plate 108, which is fixedly attached to the adjacent side of the throat block 32. Accordingly, the bearing 104 supports and maintains alignment of the screw 92 within the barrel 40 so that the screw can rotate about a center axis 112 of the barrel, this center axis including the center axes for each of the first, second, third, and fourth stages of the barrel as described hereinabove. In particular, the screw 92 diameter within the barrel 40 is smaller than the interior diameter of the first stage by a tolerance of approximately 0.01 to 0.08 inches so that the screw can rotate freely within barrel when there is no plastic in the barrel to impede such free rotation. Note that the tolerance between the interior of the first stage 44 and the screw 92 may be dependent upon the intended size of the plastic pellets to be provided in the material hopper 24 since such tolerance is intended to be small enough so that such pellets cannot be caught and sheared between the interior surface of the first stage 44 and the portions (apexes) of the auger screw flights 88 that rotate closest to the first stage interior surface. Accordingly, the tolerance range above is believed appropriate for pellets that are approximately 0.125 inches in width, height and depth, pellets being a standard size for use in injection molding machines.
The shaft 96 also extends beyond the mounting plate 108, wherein a pulley 116 is also secured thereabout. For rotating the screw 92, a belt (not shown) is provided in the annular recess 120 of the pulley 116 and also provided about a pulley of a drive motor (also not shown) for rotating the pulley 116 and consequently the screw 92.
The screw 92 has a central bore 124 therethrough, the center axis of the bore is coincident with the center axis 112. Within the bore 124 there is an injection plunger 160 (having a plunger head 132 and a plunger shaft 136), and a plunger shank 140. The plunger shank 140 extends from the screw 92 rearward beyond the pulley 116. Prior to exiting the screw 92, the plunger shank 140 and the interior surface of the bore 124 are intermeshed via mating gear teeth 142 or another mechanism for both supporting the shank 140 within the bore 124, and for allowing the shank to shift along the center axis 112 under the urging of the motor (or pneumatic cylinder, hydraulic cylinder) 144 to which the shank end attaches via a bearing 148. In another embodiment, instead of mating gear teeth 142, a bearing that allows the shank 140 to move in the axial direction relative to the bore 124 and provide support for the shank 140 within the bore 124 may replace the mating gear teeth 142. Accordingly, the bearing 148 allows the shank 140 to rotate with the rotation of the screw 92 by the pulley 116. However, when activated (by the controller 16, also shown in
The sleeve 156 also projects beyond the fluted end of the screw 92. The portion of the sleeve 156 that extends beyond the end of the screw 92 is within a fine tolerance of the interior surface of the second stage 52 of the barrel 40. More precisely, the smallest interior diameter of the second stage interior side wall 58 may be within a tolerance of approximately 0.01 inches of the outer diameter of the sleeve 156. Thus, the sleeve 156 forms a rotatable inner most side of each channel 56 in the second stage 52. In the present embodiment, the exterior surface of the sleeve 156 forming the inner most channel sides may be highly polished or otherwise provided with a coating that substantially prevents melted or softened plastic from adhering thereto.
The sleeve 156 and the plunger head 132 are sealed together (such combination also referred to as plunger 160), and may be considered as an embodiment of the “shaft extension” referred in the Summary section hereinabove. An outside diameter of the sleeve 156 may be within a fine tolerance of the inside diameter of the injection chamber 64, e.g., within a range of 0.005 to 0.001, so that this sleeve 156 and plunger head 132 combination can enter the injection chamber (via an urging by the motor 144) for injecting melted plastic from the injection chamber into the injection tube 78, and also via an opposite urging by the motor 144, the plunger 160 can retract out of the injection chamber 64 once the plunger 160 reaches its full extension into the injection chamber 64.
The plunger head 132 includes a one way vacuum break valve 164 (e.g., a poppet style valve) for opening and providing a gas (e.g., air) or other fluid substance therethrough when a reduced atmospheric pressure occurs in the injection chamber 64 relative to a pressure on an opposite side of this valve, and remaining closed otherwise. When the valve 164 opens, the gas provided to the injection chamber 64 comes, in one embodiment, from within the bore 124, and more particularly, from within a plunger vent 168 within the plunger shaft 136 (
The injection molding machine 20 also includes a plurality of heat sources (e.g., such heat sources may generate heat via electrical resistance, electrical inductance, microwave or ultrasonic energy) distributed about and in contact with (or proximate to) various portions of the barrel 40. In particular, one or more such heat sources 172 may surround the barrel 40 in a later or terminal portion of the barrel first stage 44 near the commencement of the barrel second stage 52, and continue to surround barrel 44 in substantially the second stage 52. The heat sources 172 (under the control of the controller 16) preheat the plastic pellets to a point just below the softening point of the plastic.
The heat sources 172 (under the control of the controller 16) heat the plastic pellets therein to a temperature where they become at least soft and deformable for flowing into the channels 56 due to the pressure exerted on such deformable pellets from additional pellets moving into the second stage 52.
The steps performed by the controller 16 for appropriately activating and deactivating the heat sources 172 are described hereinbelow in the section entitled “Controller Operation”. Note that in one embodiment, an additional heat source 176 (not shown in figures) may be placed on a different location of the barrel 44 and controlled by controller 16. Note that in such an embodiment of the controller 16 the heat sources 172 and 176 are activated and deactivated in unison by the same processing in the controller 16. That is, the controller may not distinguish between the heat sources 172 and 176. In another embodiment, heat sources 172 and 176 may be activated, for example, in a serial or sequential manner.
An additional one or more heat sources 180 may surround the barrel 40 in substantially its third stage 60 and fourth stage 76. The heat sources 180 (under the control of the controller 16) further heat the plastic in the injection chamber 64 and the injection tube 78 so that the temperature of the plastic is above a minimum threshold to be injected into the mold cavity 83. The steps performed by the controller 16 for appropriately activating and deactivating the heat sources 180 are also described hereinbelow in the section entitled “Controller Operation”.
The injection molding machine 20 also includes a plurality of sensors for communicating measurements related to plastic processing to the controller 16. In one embodiment of the injection molding machine 20, there is a screw 92 pressure sensor (denoted “PT1” herein) attached, e.g., to the screw end between the pulley 116 and the motor 144, wherein this sensor measures the forces on the screw, wherein such forces are substantially along the center axis 112, and induced by the compaction of the plastic in first and second barrel stages 44 and 52. Accordingly, such for forces are in the direction for pushing the screw 92 out of the end of the barrel 40 provided in the throat block 32.
The injection molding machine 20 also includes a plurality of sensors for communicating measurements related to plastic processing to the controller 16. In one embodiment of the injection molding machine 20, there is a screw 92 pressure sensor or pressure transducer (denoted “PT1” herein) attached, e.g., to the screw 92 end between the pulley 116 and the motor 144, wherein this sensor measures the pressure on the screw, wherein such pressure is substantially along the center axis 112, and induced by the compaction of the plastic in first and second barrel stages 44 and 52. Accordingly, such for pressure may be considered a force in a direction for pushing the screw 92 out of the end of the barrel 40 provided in the throat block 32. A temperature sensor (denoted “TC1” herein) is attached to the barrel 40 (more particularly, the third stage thereof) for detecting temperatures in the injection chamber 64. The sensor TC1 may be a thermocouple as one skilled in the art will understand. Also attached to the barrel third stage is a pressure sensor or pressure transducer (denoted “PT2” herein) for measuring the pressure within the injection chamber 64. Downstream from the sensor PT2 is another pressure sensor or pressure transducer (denoted “PT3” herein), wherein this sensor measures the pressure within the injection tube 78. Additionally, there is a temperature sensor (denoted “TC2” herein) is attached to the barrel 40 (more particularly, the fourth stage thereof) for detecting temperatures in the injection chamber 64. The sensor TC2 may be a thermocouple as one skilled in the art will understand. Finally, there is a temperature sensor (e.g., a thermocouple) provided in the mold 46 for detecting temperatures therein. This last sensor identified as “TC3”. Each of the above identified sensors provides their corresponding readings to the controller 16 as will be described in further detail hereinbelow.
Referring to
Note that such input may include a type of material to be supplied to the injection molding machine 20, an identification(s) of the part(s) to be molded, the quantity of parts to be produced.
In step 408 of
In step 416, the subcontroller 304 is activated for controlling the heat source(s) 172 for heating the second and third zones 44 and 52. The input to the subcontroller 304 may include a desired start temperature range for readings from the temperature sensor TC1 as determined for plastic to be processed; the range of temperatures may be, e.g., +/−10 degrees F., and the range may be a set point range identified as the range [set_pt_low, set_pt_hi] wherein set_pt_low is a low set point for the readings from TC1, and set_pt_hi is a high set point for these readings. Psuedo-code representative of the processing performed by the subcontroller 304 is as follows:
Referring to the subcontroller 304 psuedo-code hereinabove, process 1 and process 2 may be activated for being performed simultaneously. However, note that process 2 can override process 1 to force the heat source(s) 172 to heat zones 44 and 52. It is believed that an important aspect of the controller 16 is the use of the pressure measurements from the sensors PT1 and PT2 to modulate the heat delivered to the first and second zones 44 and 52. In particular, the computation of “Delta12” provides a quantitative index as to whether plastic viscosity in screw 92 is high, and/or the plastic is not flowing through channels 56 into the injection chamber 64. For example, if the value Pt1 is high relative to the value of Pt2, then there is substantial pressure in the first and second zone 44 and 52 for pushing the screw 92 out the rear end of the injection molding machine 20, and little (if any) plastic in the injection chamber 64. Accordingly, this is indicative of the plastic in the second and third zones 52 and 60 not being hot enough to proper flow through the channel 56 and into the injection chamber 64. Thus, in this case, any deactivation of the heat source(s) 172 is overridden by process 2. Note that it may be important for the reading of PT1 and PT2 to be taken substantially simultaneously, and that the readings of PT2 be taken when the pressure in the injection chamber 68 is not being impacted by the movement of the plunger 160 into or out of the injection chamber. Accordingly, such reading are only taken when the controller 16 detects that the plunger is fully retracted from the injection chamber 64. The use of the Boolean variable “Delta12_Not_Measured” assists in making sure the readings are taken at a proper time.
In step 420, the subcontroller 308 is activated for controlling the heat source(s) 180 for heating the fourth zone 76. As described in the pseudo-code following. Note that the input for this subcontroller is: a desired start temperature range for readings from the temperature sensor TC2 (for heat sources 180) for plastic to be processed, the range of temperatures (e.g., +/−10 degrees F.) creating a set point range, i.e., a range: [set_pt_low2, set_pt_hi2] for the readings from TC2.
Subsequently, step 424 is performed, wherein the subcontroller 312 is activated for controlling the screw 92 rotation. Pseudo-code describing the actions performed by this subcontroller follow.
Subsequently, in step 428, the expression: (the most recent value of pt2 by subcontroller 304 is within its corresponding predetermined set point range) AND (the most recent value of Delta12 computed by subcontroller 304 is within a predetermined set point range) is repeatedly evaluated. When this expression evaluates to “TRUE”, the subcontroller 312 is deactivated and the subcontroller 316, whose pseudo-code is hereinbelow, is activated.
Subsequently, step 440 is performed.
When an appropriate profile is achieved by measurements of the heat source(s) 172 and heat source(s) 180 sequences via their corresponding sensors, we then have a volume of material where the viscosity as measured as resistance to flow, is optimized and known. When this condition is achieved we will have realized a low delta between PT1 and PT2 and furthermore a low delta between PT1 and PT3. This allows the use of the screw 92 to extrude plastic directly into the mold 46 when desired.
In any of the following modes of injection molding, operation of the last key component is PT4 pressure transducer in the injection mold.
The above disclosure lays the foundation for four different injection molding processes: Plastic Injection Molding Method (PIMM) 1 through 4 described hereinbelow.
The foregoing discussion of the injection molding system 12 has been presented for purposes of illustration and description. Further, the description is not intended to limit the invention(s) disclosed herein any to the form disclosed. Consequently, variation and modification commiserate with the above teachings, within the skill and knowledge of the relevant art, are within the scope of the present invention. The embodiment described hereinabove is further intended to explain the best mode presently known of practicing the invention, and to enable others skilled in the art to utilize each invention herein, or in other embodiments thereof, and as may be provided with the various modifications required by their particular application or uses of the invention(s) herein.
The present application is a continuation application of application Ser. No. 12/429,177, filed Apr. 23, 2009 and claims the benefit of U.S. Provisional Patent Application No. 61/125,214 filed on Apr. 23, 2008; the entire disclosures of which are hereby fully incorporated by reference as part of the present application.
| Number | Date | Country | |
|---|---|---|---|
| 61125214 | Apr 2008 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12429177 | Apr 2009 | US |
| Child | 13031367 | US |