This invention relates to an ink jet printing process for improving the durability and image quality of an ink jet image.
Ink jet printing is a non-impact method for producing images by the deposition of ink droplets in a pixel-by-pixel manner to an image-recording element in response to digital signals. There are various methods that may be utilized to control the deposition of ink droplets on the image-recording element to yield the desired image. In one process, known as continuous ink jet, a continuous stream of droplets is charged and deflected in an imagewise manner onto the surface of the image-recording element, while unimaged droplets are caught and returned to an ink sump. In another process, known as drop-on-demand ink jet, individual ink droplets are projected as needed onto the image-recording element to form the desired image. Common methods of controlling the projection of ink droplets in drop-on-demand printing include piezoelectric transducers and thermal bubble formation. Ink jet printers have found broad applications across markets ranging from industrial labeling to short run printing to desktop document and pictorial imaging.
The inks used in the various ink jet printers can be classified as either dye-based or pigment-based. A dye is a colorant that is molecularly dispersed or solvated by a carrier medium. The carrier medium can be a liquid or a solid at room temperature. A commonly used carrier medium is water or a mixture of water and organic co-solvents. Each individual dye molecule is surrounded by molecules of the carrier medium. In dye-based inks, no particles are observable under the microscope. Although there have been many recent advances in the art of dye-based ink jet inks, such inks still suffer from deficiencies such as low optical densities on plain paper, poor light-fastness and poor ozone-fastness in some porous image-receiving layers. When water is used as the carrier medium, such inks also generally suffer from poor water-fastness.
U.S. Pat. No. 6,087,051 relates to an ink jet recording element containing a protective overcoat layer of an aqueous polyurethane resin or an aqueous polyacryl resin. However, such an overcoat layer does not improve the image quality.
It is an object of this invention to provide an ink jet printing process for improving the durability of an ink jet image. It is another object of this invention to provide an ink jet printing process wherein the image quality is improved.
These and other objects are achieved in accordance with the present invention which comprises an ink jet printing process for improving the durability and image quality of an ink jet image comprising:
It was found that the durability and image quality of an ink jet image is improved using an overcoat layer of the smectite clay particles.
In a preferred embodiment of the invention, the smectite clay is montmorillonite, hectorite or saponite. In another preferred embodiment, the smectite clay comprises synthetic smectite or layered hydrous magnesium silicate. The smectite clay overcoat layer can be applied at any thickness for the intended purpose. In general, good results have been obtained when the overcoat layer has a thickness of between about 0.1 and about 100 μm, preferably between about 0.25 and about 25 μm.
Ink jet inks used to prepare the images to be protected using the invention are well-known in the art. The ink compositions used in ink jet printing typically are liquid compositions comprising a solvent or carrier liquid, dyes or pigments, humectants, penetrants, buffers, organic solvents, detergents, thickeners, preservatives, and the like. The solvent or carrier liquid can be solely water or can be water mixed with other water-miscible solvents such as polyhydric alcohols. Inks in which organic materials such as polyhydric alcohols are the predominant carrier or solvent liquid may also be used. Particularly useful are mixed solvents of water and polyhydric alcohols. The dyes used in such compositions are typically water-soluble direct or acid type dyes. Such liquid compositions have been described extensively in the prior art including, for example, U.S. Pat. Nos. 4,381,946; 4,239,543 and 4,781,758, the disclosures of which are hereby incorporated by reference.
Any known ink jet image-receiving layer or ink solvent receiving layer can be used in the present invention. For example, these layers may consist primarily of inorganic oxide particles such as silicas, modified silicas, clays, aluminas, fusible beads such as beads comprised of thermoplastic or thermosetting polymers, non-fusible organic beads, or hydrophilic polymers such as naturally-occurring hydrophilic colloids and gums such as gelatin, albumin, guar, xantham, acacia, chitosan, starches and their derivatives, and the like; derivatives of natural polymers such as functionalized proteins, functionalized gums and starches, and cellulose ethers and their derivatives; and synthetic polymers such as polyvinyloxazoline, polyvinylmethyloxazoline, polyoxides, polyethers, poly(ethylene imine), poly(acrylic acid), poly(methacrylic acid), n-vinyl amides including polyacrylamide and polyvinylpyrrolidone, and poly(vinyl alcohol), its derivatives and copolymers; and combinations of these materials. Hydrophilic polymers, inorganic oxide particles, and organic beads may be present in one or more layers on the substrate and in various combinations within a layer.
Examples of ink jet recording elements having glossy, non-porous image-receiving layers or ink solvent receiving layers which can be used in the present invention include HP Premium Inkjet Glossy Paper® and HP Premium Plus Photo paper, Glossy Media®.
A porous structure may be introduced into image-receiving layers or ink solvent receiving layers comprised of hydrophilic polymers by the addition of ceramic or hard polymeric particulates, by foaming or blowing during coating, or by inducing phase separation in the layer through introduction of nonsolvent. Commercial examples of ink jet recording elements containing small pore size glossy porous image-receiving layers or ink solvent receiving layers are Kodak Professional Instant—Dry Photographic Glossy Paper®, Konica QP Photo Quality Ink Jet Paper® and Epson Premium Glossy Photo Paper®. Papers with larger pore size, lower surface gloss or matte image-receiving layers are usually referred to as coated papers. Bond papers are examples where the porous substrate also acts as the image-receiving layer and ink solvent receiving layer.
In practice, various additives may be employed in the image-receiving layer, ink solvent receiving layer and overcoat. These additives include surface active agents, surfactant(s), to improve coatability and to adjust the surface tension of the dried coating, acid or base to control the pH, antistatic agents, suspending agents, hardening agents to cross-link the coating, antioxidants, UV stabilizers, light stabilizers, and the like. In addition, a mordant may be added in small quantities (2%-10% by weight of the base layer) to improve waterfastness. Useful mordants are disclosed in U.S. Pat. No. 5,474,843.
The layers described above, including the image-receiving layer, ink solvent receiving layer and the overcoat layer, may be coated by conventional coating means onto a transparent or opaque support material commonly used in this art. Coating methods may include, but are not limited to, spray coating, wound wire rod coating, slot coating, slide hopper coating, gravure, curtain coating, and the like. Some of these methods allow for simultaneous coatings of both layers, which is preferred from a manufacturing economic perspective.
The image-receiving layer may be present in any amount that is effective for the intended purpose. In general, good results are obtained when it is present in an amount of from about 5 to about 30 g/m2, preferably from about 8 to about 15 g/m2, which corresponds to a dry thickness of about 5 to about 30 μm, preferably about 8 to about 15 μm. In another embodiment, the image-receiving layer has a thickness of between about 1 and about 100 μm.
One type of natural occurring smectite clay that may be used in the invention is montmorillonite and another type is bentonite. Synthetic clay can be made, which closely resembles the natural clay mineral hectorite in both structure and composition, as disclosed in British Patents 1054111, 1213122 and U.S. Pat. No. 4,049,780. Synthetic smectite clay is free from natural impurities and is prepared under controlled conditions. One such synthetic smectite clay is commercially marketed under the tradename Laponite® by Laporte Industries, Ltd of UK through its US subsidiary, Southern Clay Products, Inc. It is a layered hydrous magnesium silicate, in which magnesium ions, partially replaced by suitable monovalent ions such as lithium, sodium or potassium, are octahedrally coordinated to oxygen and/or hydroxyl ions, some of which may be replaced by fluorine ions, forming the central octahedral sheet. Such an octahedral sheet is sandwiched between two tetrahedral sheets of silicon ions, tetrahedrally coordinated to oxygen.
There are many grades of Laponites® such as RD, RDS, J, S, etc. each with unique characteristics and can be used in the present invention. A typical chemical analysis of Laponite® and its physical properties, as per Laponite Product Bulletin, are provided below.
Laponite® separates into tiny platelets of lateral dimension of 25-50 nm and a thickness of 1-5 nm in deionized aqueous dispersions. Typical concentration of Laponite® can be 0.1% through 10% when used to overcoat a printed image.
The clay overcoat layer may be applied to the ink jet image in accordance with the invention either through a separate thermal or piezoelectric printhead, or by any other method that would apply the material evenly to the image, such as a spray bar. Methods of applying a overcoat layer are disclosed in U.S. Pat. Nos. 6,176,574 and 6,254,230, the disclosures of which are incorporated herein by reference. Other methods for applying the overcoat layer include submerging the element into a tank containing a liquid dispersion of the clay or by extrusion of the clay dispersion on top of the recording element.
In general, the overcoat layer may be present at a dry thickness of from about 0.1 to about 100 μm, preferably from about 0.25 to about 25 μm.
The support for the ink jet recording element used in the invention can be any of those usually used for ink jet receivers, such as paper, including resin-coated paper and laminated paper based supports, and plastic film supports, including transparent, opaque and semi-transparent (day/night) supports based on polymers such as poly(ethylene terephthalate), poly(ethylene naphthalate), cellulose acetate, and microporous materials such as polymer-containing materials sold by PPG Industries, Inc., Pittsburgh, Pa. under the trade name of Teslin®, Tyvek® synthetic paper (DuPont Corp.), and OPPalyte® films (Mobil Chemical Co.) and other composite films listed in U.S. Pat. No. 5,244,861.
The support used in the invention may have a thickness of from about 50 to about 500 μm, preferably from about 75 to 300 μm. Antioxidants, antistatic agents, plasticizers and other known additives may be incorporated into the support, if desired. In a preferred embodiment, either paper or poly(ethylene terephthalate) is employed.
In order to improve the adhesion of the image-receiving layer to the support, the surface of the support may be subjected to a corona-discharge-treatment prior to applying the image-receiving layer.
In addition, a subbing layer, such as a layer formed from a halogenated phenol or a partially hydrolyzed vinyl chloride-vinyl acetate copolymer can be applied to the surface of the support to increase adhesion of the image-receiving layer. If a subbing layer is used, it should have a thickness (i.e., a dry coat thickness) of less than about 2 μm.
The following example is provided to illustrate the invention.
Printing of Ink Jet Print
Various color patches were printed onto different receivers at various densities using a specified printer and cartridges containing colored and black dye or pigment based inks as described below.
Printer and Ink Combinations:
These elements were printed using the ink-printer combination described in Table 1 below.
Elements 1-24 of the Invention
These elements were the same as the control elements except that they were overcoated with Laponite RD®, supplied by Southern Clay Product Co. (Gonzales, Tex.), mixed with deionized water to make a 3% gel, to form a layer of 2 μm using a hopper coating knife.
Testing
Optical Density
The reflection densities of the color patches were measured with a GretagMacbeth Spectrolino® Densitometer are shown in Table 2 below. The transmission densities of the color patches were measured with a X-Rite 310 ® Densitometer and are shown in Table 3 below.
Gloss
The 20° and 60° gloss of the elements were measured with a micro-TRI-glossmeter® manufactured by BYK Gardner and are shown in Table 2 below.
The above results show that the optical density or the gloss of the images are enhanced greatly after applying the overcoat. This enhancement is generally observed on images printed on different media using different printers with different inks.
The above results show that the transmission densities of the images printed on a transparency are also enhanced greatly after applying the overcoat.
Ozone Resistance
The elements in the form of strips measuring approximately 2.54 cm×20 cm or smaller were introduced into a chamber set to deliver 5 ppm of ozone at approximately 50 l/min total flow and a dew point of about 11° C. The color densities on each of the samples were measured before and after a 65 hour ozone exposure. The optical densities after ozone exposure are shown in Table 4 below and should be compared to the optical densities in Table 2 for the same elements.
Blocking
The elements in the form of squares measuring approximately 7.6 cm×7.6 cm were placed into the 70° C./50% RH oven and allowed to equilibrate for a half hour. The two density patches were placed face to face imagewise. The patches were inserted into a metal box and a kilogram cover was applied. The samples were left in the oven for six hours. After removal from the oven and from the box, the samples were allowed to cool for at least thirty minutes. Finally, the samples were separated slowly and the performance was rated as stated below:
The results are shown in Table 4 below.
The above results, comparing the same elements in Tables 2 and 4, show that the images with overcoat did not lose their optical density after accelerated ozone testing in contrast to the images without overcoat. The overcoat provides good protection of the images from heat and pressure. The prints with overcoat do not exhibit any image degradation after the blocking test in contrast to the prints without the overcoat.
Although the invention has been described in detail with reference to certain preferred embodiments for the purpose of illustration, it is to be understood that variations and modifications can be made by those skilled in the are without departing from the spirit and scope of the invention.
Reference is made to commonly-assigned copending U.S. patent application Ser. No. 09/617,152, filed Jul. 17, 2000 entitled “Image Layer Comprising Intercalated Clay Particles”, of Majumdar, et al; and U.S. patent application Ser. No. 09/742,982, filed Dec. 20, 2000, entitled “Ink Jet Printing Process”, of Romano, Jr., et al.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5644350 | Ando et al. | Jul 1997 | A |
| 6087051 | Shoji et al. | Jul 2000 | A |
| 20030112311 | Naik et al. | Jun 2003 | A1 |
| 20030134212 | Castle et al. | Jul 2003 | A1 |
| 20030151654 | Lawrence et al. | Aug 2003 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20040041891 A1 | Mar 2004 | US |