Ink-jet recording sheet with improved ozone resistance

TECHNICAL FIELD OF THE INVENTION

[0001] The present invention concerns a recording material for the ink-jet recording process with a carrier, at least one ink-absorbing layer and at least one dye-fixing layer.

BACKGROUND OF THE INVENTION

[0002] In the case of the ink-jet printing process, tiny ink droplets are applied by means of different techniques, which have already been repeatedly described, onto a recording material and absorbed by the latter. The recording material is subject to different requirements such as a high colour density of the printed dots, a high ink absorption capacity, a short drying time and a sufficient smudge resistance associated therewith, a dye diffusion in the transverse direction of the printed dots not exceeding the required extend (bleed) as well as a low color coalescence and a high resistance to water. Other requirements, in particular for photograph-type prints, are an even print gloss and surface gloss of the recording material.

[0003] As a result of the great progress achieved in the ink-jet technology field regarding the quality of the image and the speed of printing of the printer, the ink-jet color printer market has grown enormously. It is expected that, in the next few years, the area of digital photography, in particular of ink-jet materials of photographic quality, will continue to develop strongly. Due to the need to achieve a photographic image quality in the case of ink-jet printed products, achieving a high image durability is one of the most important development tasks. This leads to new developments both regarding the image-receiving materials and the dye-based inks.

[0004] Ink-jet recording materials can be divided into two classes: materials with recording layers swelling in water which contain binders such as gelatine or polyvinyl alcohol, and materials with microporous layers.

[0005] Materials with layers swelling in water have the advantage that they are glossy and exhibit high color densities after printing. They exhibit a satisfactory stability vis-à-vis ozone since the swellable layers—like a barrier—prevent ozone from penetrating into the material. However, the material has disadvantages regarding the image quality (bleed, color coalescence) and the drying time.

[0006] The microporous systems, which are capable of rapidly absorbing the ink during printing as a result of cavities in the applied layer, exhibit an excellent image quality as a result of the good color fixing effect. They have a short drying time and problems regarding coalescence and bleed do not occur. The images produced by means of such microporous recording materials are not resistant to light and react in a sensitive manner to the gases contained in the air, particularly ozone. The gas can easily penetrate into the micropores of the recording layers and—encouraged by the catalytic effect of the pigments contained in the layers—possibly attack the double bonds of the dyes. The reactivity vis-à-vis ozone can be further increased by moisture at elevated temperatures. Cyan blue dye has a particularly sensitive reaction to ozone.

[0007] The solutions to the problem suggested at present include laminating of the printed image with a polyester film or the use of inks containing alkali metal additives and ammonium or amine salt groups. Although these solutions have positive aspects, they are not free from disadvantages. The disadvantages include, on the one hand, an increase in the production costs caused by the laminating step; on the other hand, the metal-containing compounds tend to cause significant tint shifts which become noticeable as color turbidity.

[0008] According to JP 10-264501, the stability vis-à-vis ozone can be improved by using a plasticiser-containing thermoplastic resin as binder in the ink absorption layer. The anti-ozone-protecting effect is presumably achieved by the pigment and the absorbed ink dyes being enveloped by the resin.

[0009] A further possibility of improving the stability vis-à-vis ozone is described in JP 08-164664 where an inorganic pigment, the surface of which is modified with cycloamylose, is used in the ink absorption layer.

[0010] In EP 0 524 635 A1, a recording material is suggested which contains a combination of starch particles, an ethylene-vinyl acetate copolymer and a cationic dye-fixing agent in the ink absorption layer.

[0011] According to U.S. Pat. No. 6,344,262 B1 an Mg thiocyanate is used in a porous layer containing aluminium oxide in order to improve the stability vis-à-vis light and ozone. The porous layer is the ink-recepting layer.

[0012] In EP 1 157 847 A1, the use of benzotriazol derivatives in the ink absorption layer for improving the resistance of the recording material to gas is described.

SUMMARY OF THE INVENTION

[0013] The object underlying the present invention is to provide a further recording material for the ink-jet printing process, which exhibits an improved resistance to the effect of ozone.

[0014] This object is achieved by way of an ink-jet recording material with a carrier and at least one ink-absorbing layer, at least one dye-fixing layer, at least one water-soluble compound exhibiting ionic charge centres being arranged on the top and/or the bottom surface of the dye-fixing layer, which compound exhibits a dissociation constant in the region of 1×10−3 to 1×10−14 with a conductivity range λ of 6 to 25 ms at a temperature of 25° C.±1° C. in a 0,1 molar aqueous solution.

[0015] The invention is based on the finding that the stability of the ink dyes vis-à-vis ozone in microporous recording materials is increased in the presence of compounds exhibiting ionic centres. The absorption of ink is not negatively affected by the arrangement of the compounds.

DETAILED DESCRIPTION OF THE INVENTION

[0016] According to a particularly preferred embodiment, the compounds exhibiting ionic centres are arranged on the top and/or bottom side of the dye-fixing layer in the form of one layer. This layer is free from pigments.

[0017] Compounds exhibiting ionic charge centres should be understood to mean compounds charged according to the invention. Water-soluble compounds exhibiting ionic charge centres, which are suitable according to the invention, are, for example, those containing functional groups such as RCO2−, RO−, RS−, SCN−, S2O3− and/or RSO3−, R being a substituted or unsubstituted alkyl with 1 to 8, in particular 1 to 4 carbon atoms, or a substituted or unsubstituted, aromatic or non-aromatic ring system with 5 to 10 carbon atoms. Alkali metals of group I and an ammonium ion have proved to be particularly suitable as counter ions.

[0018] According to a preferred embodiment of the invention, the compound additionally contains an ethylene-unsaturated bond.

[0019] Compounds with a water-solubility of more than about 10% by weight at 25° C. have proved to be particularly suitable.

[0020] The arrangement of these compounds can be present in the form of a layer which also contains binders, wetting agents, surfactants, defoaming agents and light stabilizing agents. Suitable binders are, for example, water-soluble and/or water-dispersible polymers with a glass transition temperature Tg of 30 to 85° C., measured according to the so-called ‘dynamic scanning colorimetry’ method (DSC); these polymers have a viscosity of maximum 60 cPs, measured in a 4% aqueous solution. They include in particular polyurethanes, polyacrylates, polyvinyl alcohols, gelatine, gelatine derivatives, cellulose, starches, modified starches and/or polyvinyl acetates. A layer containing a polyurethane and/or a polyacrylate, apart from the compound according to the invention, as binder is particularly preferred. The quantitative ratio of polymer to water-soluble compound is preferably 1:1 to 1:10. The application weight of the pigment-free layer can be 0.05 to 5 g/m2, in particular 0.1 to 2 g/m2.

[0021] The arrangement of these compounds in a binder-containing layer has proved advantageous because the resistance to ozone and the gloss are further enhanced without negatively affecting the ink absorption.

[0022] According to a preferred embodiment I of the invention (FIG. 1), the recording material contains a sheet of paper (1)coated on both sides with polyolefin, at least one ink-absorbing layer (2) arranged thereon containing finely divided pigment and a binder, at least one dye-fixing layer (3) containing a finely divided pigment and a binder and at least one layer (4), arranged on the dye-fixing layer (3), containing a layer containing a water-soluble compound with ionic charge centres.

[0023] According to a further preferred embodiment II of the invention (FIG. 2), the recording material contains a paper (1) coated on both sides with polyolefin, at least one ink-absorbing layer (2) arranged thereon containing a finely divided pigment and a binder, at least one layer (4) containing a water-soluble compound with ionic charge centres and at least one dye-fixing layer (3), arranged on the layer (4), containing a finely divided pigment and a binder.

[0024] The grain size distribution of the pigment of the ink-absorbing layer (2) is preferably in the region of 150 to 1,000 nm with an average particle size of 240 to 350 nm.

[0025] Pigments, suitable according to the invention, of the ink-absorbing bottom layer (2) are, for example, aluminium oxide, aluminium hydroxide, aluminium oxide hydrate, silicic acid, barium sulphate and titanium dioxide. In the bottom layer, a pigment based on amorphous silica is particularly preferred. Such a pigment can be cationically modified.

[0026] The pigment used in the dye-fixing layer has an average particle size of 10 to 500 nm, in particular 50 to 100 nm.

[0027] Pigments of the dye-fixing layer which are suitable according to the invention are, for example, aluminium oxide, aluminium hydroxide, aluminium oxide hydrate, silicic acid, barium sulphate and titanium dioxide.

[0028] The ink-absorbing and the dye-fixing layer contain a water-soluble and/or water-dispersible polymeric binder. Suitable binders are, for example, polyvinyl alcohol, completely or partly saponified, cationically modified polyvinyl alcohol, polyvinyl alcohol exhibiting silyl groups, polyvinyl alcohol exhibiting acetal groups, gelatine, polyvinyl pyrrolidone, starch, carboxymethylcellulose, polyethylene glycol, styrene-butadiene latex and styrene-acrylate latex. The quantity of binder in the dye-fixing and the ink-absorbing layer is 5 to 35% by weight, preferably 10 to 30% by weight respectively, based on the weight of the dry layer.

[0029] Both layers may contain usual additives and auxiliary agents such as surfactants, wetting agents and dye-fixing agents such as polyammonium compounds.

[0030] The application thicknesses of the ink-absorbing and the dye-fixing layer can be 10 to 60 μm, preferably 20 to 50 μm.

[0031] In principle, any raw paper can be used as carrier material. Surface-sized, calendered or non-calendered or highly sized raw paper is preferred. The paper can be acid-sized or neutrally sized. The raw paper should have a high dimensional stability and be capable of absorbing the liquid contained in the ink without forming undulations. Paper with a high dimensional stability made of cellulose mixtures of soft wood cellulose and eucalyptus cellulose is particularly suitable. In this respect, reference is made to the disclosure of DE 196 02 793 B1 which describes a raw paper for an ink-jet recording material. The raw paper can contain further auxiliary agents and additives common in the paper industry such as dyes, optical brighteners or defoaming agents. Using waste cellulose and recovered waste paper is also possible.

[0032] Raw paper with a weight per surface area of 50 to 300 g/m2 is used.

[0033] Paper coated on one or both sides with polyolefin, in particular with polyethylene (LDPE and/or HDPE) is particularly suitable as carrier material. The amount of polyethylene applied is 5 to 20 g/m2.

[0034] Polymer sheets, for example of polyester or polyvinyl chloride are also suitable as carriers. The weight per surface area of the carrier can be 50 to 300 g/m2.

[0035] Any desired, generally known method of application and metering can be used to apply the layers, e.g. roller application, gravure or nipp methods as well as air brush or roller blade metering. The application by means of a cascade coating facility or a slot die is particularly preferred.

[0036] To adjust the curl behaviour, antistatics and the feeding in the printer, the reverse side can be provided with a separate operating layer. Suitable reverse layers are described in DE 43 08 274 A1 and DE 44 28 941 A1, reference to the disclosure of which is made herewith.

[0037] The following examples serve as further illustration of the invention.

EXAMPLES 1 to 10

[0038] For the following tests, a paper, neutrally sized with alkyl ketene dimer and coated on both sides with polyethylene, with a weight per surface area of 173 g/m2 was used as carrier. The front side of the raw paper was extrusion-coated with a low density polyethylene (LDPE) coating mass containing 10% by wt. of TiO2 and the reverse side was extrusion-coated with a clear LDPE. The coating on the front side amounted to 19 g/m2, the application on the reverse side amounted to 22 g/m2.

[0039] The front side of the carrier was coated, using a feed hopper, with a coating mass containing 75% by wt. of a finely divided silicic acid (300 nm) and 25% by wt. of a polyvinyl alcohol (degree of saponification 88 mole %). Onto the layer absorbing the solvent of the ink, whose application weight was 12 g/m2, a dye-fixing layer containing 89% by wt. of a finely divided aluminium oxide (100 nm) and 11% by wt. of a polyvinyl alcohol (degree of saponification 88 mole %) was applied with a feed hopper. The application weight was 30 g/m2.

[0040] The following aqueous solutions were applied onto the dye-fixing layer. The compounds used therein have the properties listed in Table 1. The application quantities of the substances used, in the dry state, are given in Table 2.

1TABLE 1Compounds used according to the inventionCompoundMWtKbpKbλ (ms)° C.N-Vinyl acetamide852.29 × 10−15(14.6)0.025.1Na acrylate941.66 × 10−1211.86.0823.9Na vinyl sulphonate1301.26 × 10−1312.98.8123.9Disodium fumarate160 1.8 × 10−1312.712.6823.9Na acetate821.05 × 10−1212.06.4223.5Na citrate dihydrate2943.80 × 10−1110.48.2923.94-Hydroxybenzoic acid1608.32 × 10−1312.15.7525.5Na saltLi thiocyanate hydrate651.58 × 10−1110.85.6726.0Trisodium405 1 × 10−33>2023.7trithiocyanuratenonahydrateTrisodium ethylene-3582.51 × 10−1211.613.7724.4diaminetetraacetatehydrateNa thiosulphate2481.05 × 10−17(17) 15.6326.5pentahydrateDiammnonium ethylene-3261.15 × 10−18(17.9)12.3323.8diaminetetraacetatehydrateEthylenediaminetetra-292 1.0 × 10−21(21) 0.5828.6acetic acid

[0041]

2

TABLE 2

Application quantity

Example
Compound
(mmole/m2)

1 A
Na acrylate
10.9

1 B
Na acrylate
18.1

2 A
Na vinyl sulphonate
6.5

2 B
Na vinyl sulphonate
13

3 A
Na acetate
10.9

3 B
Na acetate
18.1

4 A
4-OH benzoic acid Na salt
6.4

4 B
4-OH benzoic acid Na salt
10.6

5 A
Na thiosulphate pentahydrate
8.23

5 B
Na thiosulphate pentahydrate
10.7

6
Li thiocyanate
4.9

7
Na citrate dihydrate
3.5

8 A
Trisodium trithiocyanurate
2.5

nonahydrate

8 B
Trisodium trithiocyanurate
4.2

nonahydrate

9 A
Trisodium
2.85

methylenediaminetetraacetate

hydrate

9 B
Trisodium
4.7

methylenediaminetetraacetate

hydrate

10 A
Diammoniummethylenediaminetetra-
3.5

acetate hydrate

10 B
Diammoniummethylenediaminetetra-
5.8

acetate hydrate

EXAMPLES 11 to 15

[0042] The coating was applied as in examples 1 to 10 with the difference that the solution according to the invention was not applied onto the dye-fixing layer but underneath the dye-fixing layer. The application quantities of the substances used amounted to, in the dry state (Table 3):

3TABLE 3Application quantityExampleCompound(mmole/m2)11Na acrylate6.012Na vinyl sulphonate2.713 ANa acetate1.713 BNa acetate3.414 ANa thiosulphate pentahydrate3.314 BNa thiosulphate pentahydrate4.415Disodium fumarate1.75

COMPARISON EXAMPLES

Comparison Example VI

[0043] An ink-jet paper consisting of a polyethylene-coated paper, an ink-absorbing and a dye-fixing layer was used. The paper and the layers are composed in the same way as in Examples 1 to 15. This recording material does not contain the compounds used according to the invention.

Comparison Example V2

[0044] A conventional standard paper for ink-jet printers from Epson Inc. was used for reference purposes.

Comparison Example V3

[0045] A conventional standard paper for ink-jet printers from Canon Inc. was used for reference purposes.

Comparison Example V4 and V5

[0046] The tests were carried out as in examples 1 to 10 with the difference that, in the aqueous coating solution, N vinyl acetamide (V4) and ethylenediaminetetraacetic acid (V5) was used for the upper layer. The N-vinyl acetamide contains a double bond but no charge centres. Ethylenediaminetetraacetic acid has a dissociation constant of 1×10−21.

[0047] The application quantities of the substances used amounted to, in the dry state (Table 4):

4TABLE 4Application quantityExampleCompound(mmole/m2)V1FS in-house standardNo additivesV2OEM standard Epson PMNo additivesV3OEM standard Canon Pr101No additivesV4 AN-vinyl acetamide10.9V4 BN-vinyl acetamide18.1V5 AEthylenediaminetetraacetic acid3.1V5 BEthylenediaminetetraacetic acid5.2

[0048] Test

[0049] The recording materials obtained were tested for their resistance to ozone, color density, gloss, coalescence and bleed.

[0050] The basis for the tests consisted of color prints from two different printer types: Epson Stylus 870 Photo Printer and Canon S800 Photo Printer. Circular dots with a diameter of 10 mm were printed for the colors cyan, magenta, yellow and black. The test results are summarised in Tables 5 to 9.

[0051] Resistance to ozone—The printed paper samples were dried and stored for 24 hours while the effect of light, gas and moisture was excluded. Subsequently, the calorimetric L*a*b values of the colored surfaces were determined.

[0052] In the next step, the samples were stored for 24 hours in an ozone chamber at an ozone concentration of 3.5 ppm, a temperature of 20 to 22° C. and a relative atmospheric humidity of 40 to 50%. Subsequently, the L*a*b* values were measured again and the degree of fading ΔE was determined.

[0053] The L*a*b* values were measured by means of an X-Rite Color Digital Swatchbook (X-Rite Inc., Grandville, Mich., USA). The calculation of the difference in tint ΔE was effected in line with the equation: ΔE=[(ΔL*)2+[ΔAa*)2+(Δb*)2]½.

[0054] Fading of any colored surface in comparison with the standard material is calculated as % ΔE in line with the following equation (DIN 6174) and listed in Tables 5 to 9: % ΔE=(ΔE/ΔE standard)×100%. The lower the % ΔE value, the better the resistance of the material to ozone.

[0055] Color density—The color density was measured with an X-Rite Densitometer, type 428, using the colors cyan, magenta, yellow and black. The higher the value for a certain color, the better the color density.

[0056] Gloss—The gloss was measured with a gloss meter made by Dr. Lange GmbH according to DIN 67530 at an angle of 60°. The measurement was carried out on an unprinted recording sheet.

[0057] Bleed—The running into each other of the inks at the edges of colored surfaces lying together was assessed visually by awarding marks 1 (very good) to 5 (very poor).

[0058] Coalescence—The disturbance or color coalescence with a colored surface arises as a result of the merging of ink droplets not yet taken up by the recipient layer to form a larger liquid phase. After drying, the colored surface is characterized by an uneven color distribution or so-called ‘color disturbance’. It is assessed visually by awarding the marks 1 (very good) to 5 (very poor).

5TABLE 5Print and gloss properties(Epson 870 Printer) (Embodiment I).Color densityGlossCyan/Magenta/Example% 60°CoalescenceBleedYellow/BlackV1FS in-house standard40OO2.38; 1.79;1.05; 2.41V2OEM Standard Epson PM35OO2.46; 1.84;1.08; 2.55V4 AN-vinyl acetamide39OO2.31; 1.78;1.04; 2.31V4 BN-vinyl acetamide38.9O2.35; 1.75;1.04; 2.32V5 AEthylenediaminetetra-43.1OO2.38; 1.73;acetic acid1.09; 2.34V5 BEthylenediaminetetra-43.3OO2.16; 1.62;acetic acid1.08; 2.261 ANa acrylate43.1OO1.97; 1.68;1.09; 2.271 BNa acrylate38.2OO1.92; 1.68;1.11; 2.252 ANa vinyl sulphonate40.3OO2.09; 1.73; 1.09; 2.342 BNa vinyl sulphonate40.9OO2.09; 1.72;1.10; 2.313 ANa acetate41.6OO2.21; 1.81;1.08; 2.383 BNa acetate43.1OO2.12; 1.76;1.12; 2.384 A4-OH benzoic acid Na46.8OO2.22; 1.82;salt1.13; 2.544 B4-OH benzoic acid Na47.5OO2.32; 1.83;salt1.13; 2.485 ANa thiosulphate39.8OO2.01; 1.76;pentahydrate1.06; 2.305 BNa thiosulphate42.2OO2.02; 1.73;pentahydrate1.11; 2.316Li thiocyanate46.3OO2.34; 1.88;1.13; 2.447Na citrate dihydrate42.2OO2.14; 1.75;1.13; 2.328 ATrisodiumtrithiocya-43.7OO2.20; 1.80;nurate nonahydrate1.12; 2.368 BTrisodiumtrithiocya-44.6OO2.20; 1.79;nurate nonahydrate1.14; 2.339 ATrisodium44.3OXOX2.12; 1.61;methylenediaminetetra-1.12; 2.41acetate hydrate9 BTrisodium47.1OXOX2.11; 1.52;methylenediaminetetra-1.13; 2.38acetate hydrate10 ADiammonium44.3OO2.08; 1.61;ethylenediaminetetra-1.12; 2.33acetate hydrate10 BDiammonium47.1OXOX2.07; 1.44;ethylenediaminetetra-1.13; 2.32acetate hydrateO - no coalescence or bleed between the color blocks red/green (200%) OX - slight coalescence or bleed

[0059]

6

TABLE 6

Printing and gloss properties

(Canon S800 Printer) (Embodiment I)

Color density

Gloss

cyan/magenta/

Example
% 60°
Coalescence
Bleed
yellow/black

V1
FS in-house standard
40
O
O
2.57; 1.88;

1.10; 2.34

RV
OEM Standard Canon
52
O
O
2.41; 1.83;

PR101

1.11; 2.22

V4 A
N-vinyl acetamide
38.5
O
O
2.36; 1.74;

1.07; 2.03

V4 B
N-vinyl acetamide
38.1
O
O
2.32; 1.75;

1.06; 1.97

V5 A
Ethylenediaminetetra-
43.1
O
O
2.46; 1.82;

acetic acid

1.13; 2.09

V5 B
Ethylenediaminetetra-
43.3
O
O
1.98; 1.76;

acetic acid

1.15; 2.01

1 A
Na acrylate
43.7
O
O
2.19; 1.73;

1.11; 1.79

1 B
Na acrylate
38.2
O
O
2.14; 1.74;

1.11; 1.68

2 A
Na vinyl sulphonate
40.3
O
O
2.19; 1.72;

1.10; 1.72

2 B
Na vinyl sulphonate
40.9
O
O
2.20; 1.74;

1.12; 1.75

3 A
Na acetate
41.6
O
O
2.09; 1.64;

1.14; 1.83

3 B
Na acetate
43.1
O
O
2.10; 1.67;

1.17; 1.79

5 A
Na thiosulphate
39.8
O
O
2.15; 1.70;

pentahydrate

1.14; 1.85

5 B
Na thiosulphate
42.2
O
O
2.13; 1.69;

pentahydrate

1.12; 1.83

6
Li thiocyanate

O
O
2.38; 1.76;

1.11; 2.30

7
Na citrate dihydrate
42.2
O
O
2.19; 1.74;

1.15; 1.94

8 A
Trisodiumtrithiocyanu-
43.7
O
O
2.25; 1.65;

rate nonahydrate

1.14; 1.90

8 B
Trisodiumtrithiocyanu-
44.6
O
O
2.28; 1.69;

rate nonahydrate

1.14; 1.92

9 A
Trisodiummethylenedia
44.3
O
O
2.34; 1.80;

minetetraacetate

1.11; 1.96

hydrate

9 B
Trisodiummethylenedia
47.1
OX
OX
2.22; 1.84;

minetetraacetate

1.12; 1.85

hydrate

10 A
Diammoniumethylenedia
44.3
OX
OX
2.36; 1.81;

minetetraacetate

1.13; 1.91

hydrate

10 B
Diammoniumethylenedia
47.1
OX
OX
2.24; 1.84;

minetetraacetate

1.14; 1.82

hydrate

[0060]

7

TABLE 7

Resistance to ozone (Embodiment I)

Epson 870
Canon S 800

Example
% ΔE total
% ΔE cyan
% ΔE total
% ΔE cyan

V1
100
100
100
100

V2Epson
71
61
—
—

V3Canon
—
—
110
105

V4
100
100
96
92

V5
105
101
107
100

1 A
17
3
14
18

1 B
8
2
8
10.5

2 A
60
59
60
65

2 B
52
52
45
48

3 A
40
31
77
18

3 B
30
26
14
10.5

4 A
67
63.9
—
—

4 B
55
48.5
—
—

5 A
33
41
35
37

5 B
6
2
10
10

6
27.5
39
15
17

7
72
66
77
75

8 A
70
54
50
67

8 B
62
7
24
20

9 A
71
51
67
71

9 B
24
18
22
33

10 A
72
70
77
62

10 B
25
18
28.5
22

[0061]

8

TABLE 8

Print and gloss properties

(Epson 870 printer) Embodiment II)

Gloss

Color density

%

cyan/magenta/

Example
60°
Coalescence
Bleed
yellow/black

R1
FS in-house
45.5
O
O
1.98; 1.35;

standard

1.07; 2.41

11
Na acrylate
39
O
O
1.61; 1.17;

1.03; 1.83

12
Na vinyl sulphonate
37.5
O
O
1.61; 1.17;

1.03; 1.83

13A
Na acetate
38.2
O
O
2.16; 1.73;

1.08; 2.23

13B
Na acetate
35.3
O
O
2.10; 1.67;

1.07; 2.22

14A
Na thiosulphate
19
O
O
1.92; 1.62;

pentahydrate

1.05; 2.01

14B
Na thiosulphate
22.5
O
O
1.87; 1.59;

pentahydrate

1.05; 1.96

15
Disodium fumarate
30.3
O
O
1.65; 1.18;

1.07; 1.85

[0062]

9

TABLE 9

Resistance to ozone (Embodiment II)

(Epson 870 Printer).

% E

Example
% ΔE total
% ΔE cyan

R1
100
100

11
43
51

12
80
81

13A
69
75

13B
58
60

14A
57
53

14B
53
62

15
59
68

[0063] As seen in Tables 7 and 9, a noticeable improvement in the resistance to ozone can be achieved by means of the compounds used according to the invention.

Ink-jet recording sheet with improved ozone resistance

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

US Classifications

International Classifications

Abstract

Description

Claims

Priority Claims (1)