1. Field of the Invention
The present invention relates to a novel inkjet recording method and inkjet recording apparatus.
2. Description of Related Art
An inkjet recording mode is one for recording images and texts by flying minute droplets of ink to adhere onto a recording medium by various operation principles, and has advantages such as relatively high speed, low noise and easiness of multiple coloration. In the above inkjet recording mode, various improvements have been performed in various fields such as an ink, inkjet recording medium and inkjet recording apparatus, and at present, the mode has become rapidly popular for various fields such as various printers, facsimiles and computer terminals. In particular, recently high-quality picture technology in the printer has been improved, and its level has come at a picture quality of photograph.
As the inkjet recording apparatus used in the inkjet recording mode, for enhancing a printing speed, those where multiple ink jet openings (nozzle sections) and ink liquid paths are integrated as a recording head where multiple recording elements are integrated/arrayed (hereinafter also referred to as a multihead) are used. Additionally, as the inkjet recording apparatus for corresponding to coloration, those where multiple recording heads composed of the above configuration are comprised are frequently used. In that case, it is general that the recording heads which ejaculate inks of respective colors are disposed in parallel with a main scanning direction.
Here, when a color image picture is printed, differently from those where only characters are printed in a black-and-white printer, various factors such as color density, gradation and uniformity are important to obtain high-quality pictures. In particular, with respect to the uniformity, slight dispersion of nozzle units which occurs in difference of multihead fabrication steps influences jetting amounts and jetting directions of inks at respective nozzles, and becomes a cause which finally deteriorates image quality as uneven density of a printed image. Also, speed variation at a main scanning of a carriage where heads are loaded, variation of sub scanning paper feeding amount of the medium, and variation of a distance between a medium surface and a nozzle face on the medium cause deterioration of the image.
For the above problems, a so-called multi-pass recording method has been proposed where image deterioration due to the dispersion of respective nozzles and various variations is reduced by scanning multiple times the recording head having multiple nozzle sections onto the same recording area on the inkjet recording medium and forming an image according to a complementary thinning-out pattern. As a mask used in this case, as described in JP-Tokukaisho-60-107975A, the method of using a complementary pattern with a constant thinning-out rate of a certain rule is the commonest.
However, as described below, when using such a regular mask, conversely uneven colors, stripe unevenness and white spots sometimes remarkably appear, and thus, the method of using a mask pattern without regularity has been proposed as an improving countermeasure of this. By forming an image thinned out of this thinning-out pattern without regularity, it is possible to prevent the uneven density and uneven colors produced due to a synergistic effect of regularity of the image and regularity of the mask, and realize high-quality picture and high speed printing to some extent (for example, refer to JP-Tokukaihei-7-52390A, JP-Tokukai-2002-96461A, and JPTokukai-2002-144552A.).
Whereas, the present applicant has found that when a certain inks and a recording medium is used, and in particular when high-quality printing such as silver halide photograph is required, sufficient image quality is not obtained only by the proposed thinning-out printing method. This is illustrated below.
The inks used in the inkjet recoding mode are broadly divided into dye inks where color materials are dissolved in solvents and dispersion inks where color materials, mainly pigments are dispersed in solvents. The dye dissolves in the solvents and is in a molecular state or a cluster state, which makes its absorption spectrum sharp, and develops clear color with high purity. Additionally, there is no particle pattern due to particles and no scattered light and reflected light occur, therefore it is possible to obtain an inkjet image with high translucent feeling and clear color phase. The dye has a property excellent in scratch/abrasion resistance because no color material particle is present on the surface of media. The dye, however, has drawbacks of poor light resistance because dye molecules tend to break by photochemical reaction. The reduction in dye molecular number directly reflects upon a color density. It is an actual state that the inkjet recording image using the dye inks is the high image quality but the poor image stability against light, and the technology which is superior to silver halide photographs in the light of stability has not appeared yet.
As the method for solving this problem, pigment inks where the pigments with good light resistance are used as colorants have been used for the intended use where the high light stability is required.
In case of using such a pigment, increase of an ink adhesive amount generates aggregation of pigment and causes the problem that a color image with high quality and definition cannot be obtained. To solve such a problem, it is possible to apply a method for forming a color image by using an ink set in which special colors, such as red and violet, is added to inks of yellow, magenta, cyan and black (for example, see JP-Tokukai-2003-266913A).
However, when an inkjet image recording according to the thinning-put pattern without regularity is performed using the pigment inks, a dot position formed at each scanning has no regularity. Therefore, the case where the ink droplets of cyan, magenta, yellow and black are adjacently printed on the inkjet recording medium at the same scanning becomes frequent. As a result, the respective ink droplets are mixed one another, aggregation of pigment particles is caused, and a phenomenon called bronzing which is hardly caused in the dye inks occurs. A problem that the color image cannot be accurately reproduced occurs.
In particular, in order to form the image at high definition like a silver halide photograph, when the inkjet recording medium having a micro-porous layer containing inorganic fine particles with a mean particle size of 100 nm or less is used, an absorption speed of inks is fast and the aggregation of pigment particles present on the recording medium occurs more easily. Besides, it has been found that due to using the mask pattern without regularity, a probability that different color dots are adjacently printed becomes high, and the formation of image at high definition becomes difficult because the pigment particles having different color tone are mixed on the recording medium.
This is because when using the regular thinning-out pattern, the position of each ink formed on the recording medium at one scanning can be finely controlled and mixture of the dots can be effectively inhibited whereas it is difficult to perform such a control in the case without regularity. When a printing rate per scanning by the thinning-out is low, even if using the mask without regularity, the probability that the dots adjacently formed on the recording medium becomes low, and thus, the problem in image quality is reduced.
The present invention has been made in the light of the above problems.
The above object of the invention is accomplished by the following configurations.
In accordance with the first aspect of the present invention, sn inkjet recording method comprising the step of: forming a color image with color inks on the recording medium by while scanning a recording head multiple times on a same recording area of the recording medium, forming a thinned-out image according to an thinning-out pattern without regularity in each scanning, the recording head having a plurality of nozzle sections for jetting the color inks, wherein a nozzle pitch of the recording head is from 10 to 50 μm, the color inks comprise cyan, magenta, yellow and black inks and at least one special color ink, the color inks contain pigments, at least one organic solvent with high boiling point and water, a dot formed by jetting the color inks from the recording head has a size of 10 to 50 μm on the recording medium, the recording medium has a transferred amount at 0.04 seconds of absorption time by Bristow method of 10 ml/m2 or more, the recording medium comprises a micro-porous layer containing inorganic fine particles having a mean particle size of 15 to 100 nm and a hydrophilic binder; and a 20-degree specular gloss of the recording medium according to JIS-Z-8741 is 20 to 45%.
In accordance with the second aspect of the present invention, an inkjet recording apparatus for forming a color image by jetting color inks on a recording medium, comprising: a recording head having a plurality of nozzle sections to jet the color inks, the nozzle sections being arrayed at a pitch of 10 to 50 μm; a scanning section to make the recording head scan multiple times on one recording area of the recording medium; and a control section to allow the recording head to jet the color inks from the plurality of nozzle sections so that a thinned-out image according to a thinning-out pattern without regularity in each scanning is formed on the recording medium, wherein the color inks comprise cyan, magenta, yellow and black inks and at least one special color ink, the color inks contains pigments, at least one organic solvent with high boiling point and water, a dot formed by jetting the color inks from the recording head has a size of 10 to 50 μm on the recording medium, the recording medium has a transferred amount at 0.04 seconds of absorption time by Bristow method is 10 ml/m2 or more, and the recording medium has a micro-porous layer containing inorganic fine particles having a mean particle size of 15 to 100 nm and a hydrophilic binder, and a 20-degree specular gloss of the recording medium according to JIS-Z-8741 is 20 to 45%.
The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus are not intended as a definition of the limits of the present invention, and wherein:
Hereinafter, the best modes for carrying out the invention are illustrated in detail, but the invention is not limited thereto.
First, a inkjet printer to which the inkjet recording method of the invention can be applied is illustrated in reference to
As is shown in the figure, an image forming section 2 where inks are jetted onto a recording medium to form an image is installed in the inkjet printer 1. In this image forming section 2, a platen 21 which supports a back face (face opposite to a side of a recorded face) of a recording medium in a given range by its upper face is nearly horizontally arranged. A guiding member 25 which extends along a scanning direction X over the platen 21, for moving a carriage as scanning member 23 which scans in the scanning direction X is installed in the image forming section 2.
In the carriage 23, recording head 22 which jet the inks on the recording medium and a linear encoder sensor 27 which reads an optical pattern of a linear scale 26 where the optical pattern extends along the scanning direction X and is arranged in its longitudinal direction with 300 dpi cycle to output as clock signals are loaded. Meanwhile, dpi referred to in the invention represents a dot number per 2.54 cm. In the present embodiment, printing operation is performed by dividing this encoder signal, for example, by a printing resolution of 1200 dpi. A moving direction of the carriage 23 is changed by a rotation direction of a driving motor for the carriage, and the carriage 23 is moved back and forth in the scanning direction X by this. At the image formation, the carriage 23 moves forth, back or back and forth when the recording medium stops. A moving speed at that time is, for example, 705 mm/sec at the highest speed.
Next, the recording heads 22 are illustrated in reference to
The recording head 22 may be a piezo mode or a thermal mode, but is preferably the thermal mode in terms of arranging the nozzles at high density, and the recording heads of thermal mode are used in the present embodiment. This recording head 22 is arranged such that a recording face of the recording medium fed on the platen 21 is faced to a nozzle face 222 at the image recording where the nozzles 221 of the recording heads 22 are formed.
As shown in
The ink is supplied to each recording head passing through a tube for piping from a cartridge for recording ink which is not shown in the figure. Four recording heads 22 are disposed side by side along the scanning direction, and are used for 4 color inks of cyan (C), magenta (M), yellow (Y) and black (K) and 3 special color inks, and respectively. In the present Examples, 7 type inks of C, M, Y and K and 3 special colors are used as the recording inks, but the effects of the invention are the same even in the inkjet printer which records 9 colors or more, for example, 8 colors of dark and light C, M, Y and K using light colors and 3 special colors. In
Next, a control section of the inkjet printer 1 is illustrated in reference to
As shown in
The control section 100 controls feeding of the recording medium, scanning of the carriage 23 and ink jetting of the recording head 22, and the like. As is shown in
The printer driver 203 comprises a rasterizer 204 which converts the image data dealt in the application program 201 into image gradation data including color information of dot units, a color gradation compensation module 205 which compensates the image gradation data in accordance with color density property and gradation property of the inkjet printer 1, and a halftone module 206 which produces the image data of so-called halftone where a density at a certain area is expressed by the presence or absence of the recording inks at dot units from the image data after the color compensation. A module 207 which performs the thinning-out mask processing can be also incorporated in this printer driver. In that case, a mask setting can be changed depending on a type of the recording medium used for the printing, and thus more flexible control is possible than the processing in the printer. When the mask processing circuit 108 is used, the processing at the module 207 is not performed. Conversely, when the mask processing is performed at the module 207, the processing at the mask processing circuit 108 the is not performed. Also, it is possible to download a mask pattern every printing from the image forming apparatus 200.
Next, multi-pass inkjet recording method is illustrated. As mentioned above, in the inkjet image recording, particularly when a color image picture is formed, various factors such as color density, gradation and uniformity are required. In particular, with respect to the uniformity, slight unevenness of nozzle units which occurs in difference at multihead fabricating influences jetting amounts and jetting directions of inks at respective nozzles, or strip-shaped unevenness occurs due to mechanical accuracy at movement of the recording medium, and as a result, becomes a cause which finally deteriorates image quality as uneven density of a printed image. Thus, in the present embodiment, to solve such problems, the color image is formed using the multi-pass inkjet recording method where the recording heads 22 are scanned multiple times onto the same recording area of the inkjet recording medium.
As the multi-pass ink jet recording method, it is possible to use the method, for example, in JP-Tokukaisho-60-107975A. That method is illustrated by
This method shows the multihead 1101 is scanned three times to complete a printing area shown in
When using such a recording method, even if using the same one as the multihead shown in
When such recording is performed, the image data are divided to offset one another of the certain alignment in the first scanning and the second scanning. Typically, as shown in
Accordingly, in a unit printing area (here 4 pixel unit), the printing is completed by the first scanning where staggered grids are printed and the second scanning where inverse staggered grids are printed.
This way, the recording area of 4 pixel unit every one scanning is completed by alternately performing the paper feeding of 4 pixel unit and the recording of the staggered or inverse staggered pattern in sequence. As illustrated above, it is possible to obtain high-quality image which uneven density is alleviated by completing the printing by the different two types of nozzles in the same area.
However, even when such multi-pass recording is performed, the above uneven density is not sometimes dissolved at all and new uneven density is sometimes affirmed particularly in halftone depending on duties. Such phenomena are illustrated below.
Typically, the image data to be recorded in a certain area, which the printer receives, have been already arrayed regularly. In the side of the recording apparatus, a definite amount of those data is stocked in buffer, new mask (image alignment pattern) of the staggered or inverse staggered pattern is given as is already illustrated, and the printing of that pixels is performed only when both the image data and pattern of the mask become an ON state.
In
However, as is shown in
When such a phenomenon occurs, the printing of all image data is terminated in the first scanning (1840) and the recording is not performed in the second scanning (1850) at all. Thus, all printing data are printed by the same nozzles. Therefore, the influences of nozzle dispersion are directly reflected upon the uneven density, and original purposes of the above division recording method are not accomplished.
When the thinning-out printing is performed using a specified mask pattern, the printing data and the mask pattern have sometimes the same cycle. An amplitude due to an allocation of the printing pixels and non-printing pixels on the mask pattern and an amplitude of the printing data are overlapped and vibrate sympathetically. Dot alignments of the image formed by this has a pattern with a certain orientation. Typically, this phenomenon is called a moire. This is easily remarkable and easily recognized by users when the images using the same mask pattern are in multiple lines. This moire heavily depends on periodicity of the mask pattern.
In addition to the above problems, the following problems occur when bidirectional printing is performed.
In such a state, when the image at duty of 100% is bidirectionally printed using the staggered thinning-out mask, a jetted dot state becomes one like
Such total displacement of jetted positions at the bidirectional printing occurs not only due to partial lows and highs of the face of the recording medium as shown in
Due to the adverse effects described above, sufficient image quality is not always obtained with respect to the uneven density in the multi-pass recording using the regular thinning-out pattern which has been conventionally performed to compensate the variation of nozzles and the like. These adverse effects for the uneven density has the periodicity where unevenness alternately appears at a certain width of printing area, and thus it facilitates human visual sensation which recognizes as the uneven density.
The present inventors have found that the above issues occur when the regular mask pattern is used. Thus, in the present embodiment, the above problems are solved by performing the multi-pass recording using a thinning-out pattern without regularity, which defines an array of non-record pixel locations and record pixel locations, instead of using the regular mask pattern. As the thinning-out pattern without regularity, for example, it is possible to use a random pattern of a given size prepared using random numbers. Specifically, for example, as described in JP-3176182B, multiple random mask patterns with a given size where non-recording pixels and recording pixels are randomly arrayed are produced, the produced random mask patterns can be used as masks for thinning out recording data as thinning-out patterns for each recording area.
By forming the printed image in accordance with such random mask patterns, to have pattern cycles on the thinning-out alignment can be inhibited, that is, the adverse effect of uneven density in the formed image which occurs in the conventional multi-pass recording method using the regular masks can be overcome by eliminating the periodicity of uneven density.
Also, in place of the random mask using such random numbers, a dot allocation pattern with so-called blue noise property may be used as the thinning-out pattern without regularity. This pattern has been developed for quantization processing of halftone. When a dither processing is performed using this pattern, there are characteristics that less low frequency component is contained in the produced dots and the image where a particle feel is reduced is obtained.
In order to perform the image formation according to the thinning-out pattern without regularity, the method is not limited to the method using the random mask using random numbers or the dot allocation pattern with the blue noise property, and the other similar patterns for forming the thinned-out image of the thinning-out pattern without regularity can be used.
Next, with respect to the method of performing the multi-pass recording using the masks without regularity as the above, the case where 4 scanning printing is performed using the dot allocation pattern with the blue noise property as the mask is illustrated below in reference to
In an actual figuration of the nozzles of the recording head 22 used for the recording, as shown in
Hereinafter, to simplify the illustration of the multi-pass recording, the nozzles were 16 per color, this was divided into 4 to make a nozzle number per divided area 4, and a mask size corresponding to it was made 4×16. The divided areas corresponding to this are shown as 501 to 504 in
In each scanning, a thinning-out mask pattern with about 25% duty, thus, the mask pattern where a printing acceptable rate is about 25% is set for the printing data for each divided area, and a 100% image is made by scanning 4 times. A1 to A4 which are examples of the 4×16 mask patterns used for this are shown in
For the printing data 800 (hatching portions indicate that there are the printing data) shown in
Print is performed as follows.
In the first printing area on a print image, the mask pattern A1 is set for the divided area 504 of the recording head 22 and the recording is performed in the first scanning. Subsequently, in the second scanning, in the first printing area, the mask pattern A2 is used for the divided area 503 of the recording head 22, and in the second printing area, the print is performed using the mask pattern B1, of which the group is different from that of the mask pattern used in the first printing area, for the divided area 504 of the recording head 22.
Further, in the third scanning, the print is performed using the mask pattern A3 for the divided area 502 of the recording head in the first printing area, the mask pattern B2 for the divided area 503 of the recording head in the second printing area, and the mask pattern C1, of which the group is different from those of the mask patterns A3 and B2, for the divided area 504 of the recording head in the third printing area.
And in the fourth scanning, the print is performed using the mask pattern A4 for the divided area 501 of the recording head in the first printing area, the mask pattern B3 for the divided area 502 of the recording head in the second printing area, the mask pattern C2 for the divided area 503 of the recording head in the third printing area, and the mask pattern D1, of which the group is different from those of the mask patterns A4, B3 and C2, for the divided area 504 of the recording head in the fourth printing area. At that time, in the first printing area, total four times of scanning are performed using 4 mask patterns, A1, A2, A3 and A4, and the image print for this area is completed.
By the same procedure, the image formation is made using mask patterns B1, B2, B3 and B4 in the second printing area, using mask patterns C1, C2, C3 and C4 in the third printing area, and using mask patterns D1, D2, D3 and D4 in the fourth printing area. Subsequently, the printing is continued by repeatedly making use of the printing using mask patterns A1, A2, A3 and A4 in the fifth printing area and mask patterns B1, B2, B3 and B4 in the sixth printing area, and the patterns of these 4 groups.
Also, as is shown in
This way, when the blue noise property is given to the dot pattern itself formed by one scanning, there are effects that occurrence of the repeated pattern and particulate deterioration are reduced compared to the case using the patterns produced by the random numbers. This is described in, for example, Tokukai2002-96461.
If the acceptable printing rate of the mask is changed, the mask after change can be easily obtained by changing the values of these 0 to 255 depending on a printing rate. For example if making two pairs of 40% and 10% masks, the masks could be made by making the pixels corresponding to 0 to 102, 103 to 127, 128 to 230 and 231 to 255 the printing acceptable pixels, respectively. Examples of such masks are shown in
The reference numeral 305 is a register connected to CPU 103 through CPU data bus, for storing the mask patterns, 306 is a selector for selecting a digit position of the mask pattern, 307 is a selector for selecting a line position of the mask pattern, and 311 is a counter for managing the digit position.
In a transfer circuit shown in
A mask register 305 is configured by four mask registers, A, B, C and D, mask patterns written by the CPU 103 are housed. Each mask register stores the mask pattern of vertical 16 bits and horizontal 16 bits. A selector 306 selects mask pattern data corresponding to a digit position by making a value of a column counter 111 a selection signal. Also, the selector 307 selects mask pattern data corresponding to a line position by making a value of a transfer counter 304 a selection signal. The masks are applied to the transfer data using the AND gate 303 by the mask pattern data selected by the selectors 306 and 307.
These data are used for injection control of each nozzle of the recording head 22, and an injection is performed by synchronizing with timing signals produced from encoder signals. Hereinafter, these operations are performed in conformity with printing resolution toward to a width direction of the recording medium. In this embodiment, a mask size is 16 in a horizontal direction, and thus, the same mask pattern is repeatedly used every 16 pixels, but it is also possible to make the size in the horizontal direction of the mask the same size as the width of the recording medium. As the present embodiment, it is possible to reduce a capacity of the register which memorizes the masks by repeatedly using the same mask pattern.
In the inkjet recording method and the inkjet recording apparatus of the present embodiment, it is one of characteristics that a nozzle pitch of the recording head is from 10 to 50 μm. If the nozzle pitch is 50 μm or less, when jetted ink droplets are printed side by side one another, the distance between the droplets becomes short, and thus a problem of bronzing by adjacent dots one another easily occurs. Therefore, effects by applying the invention to the case that the nozzle pitch is 50 μm or less are great. This reason is that dot sizes on the recording medium is expanded approximately twice as large as the size of nozzle used ordinarily, and a dot jetted position on the recording medium is displaced from the proper position to be jetted at by unevenness of angles in jetting from the nozzle.
Besides, by making the nozzle pitch short such as 50 μm or less, even when multiple nozzles which exceed 500 nozzles per recording head are made, it is possible to keep an entire recording head length short. This can suppress jetted ink out of the position on the recording medium attributed to a change of a flying distance of the ink droplet from the nozzle in a recording head length direction due to a slope between the recording medium surface and the nozzle face, and thus it is possible to retain high printing accuracy. By making the nozzle pitch 10 μm or more, it is possible to suppress disturbance in fabrication aptitude, and consequently, it is possible to suppress the jetted ink out of the position, make it suppress to cause an overlap of dots due to shortening of dot intervals in the recording head length direction, and suppress the problem such as bronzing.
The nozzle pitch referred to here is a separation distance of mutual nozzles in the nozzle group arranged nearly in a line. As
Thus, in the invention, when the distance between the most separate nozzle rows (distance between N1 and Nn, i.e., in the case of three rows, the distance between the first row and the third row) of multiple rows (n rows such as N1, N2 . . . Nn) of the nozzle groups is 4 mm or less, the nozzle pitch is 1/n of the pitch in each row, whereas when the distance is more than 4 mm, the nozzle pitch is the pitch in each row because it is preferable to consider influences for aggregation.
In the inkjet recording method of the invention, it is preferred that a printing acceptable rate by the thinning-out pattern is from 15 to 35%. Here, in the invention, the printing acceptable rate is a rate of dot number where jetting of the ink is acceptable in one main scanning based on total dot number in the pattern when using the thinning-out pattern.
When the printing is performed using multiple thinning-out patterns different in printing acceptable rate in one image, the image quality of the image after the printing is frequently attributed to the thinning-out pattern with high printing acceptable rate. Therefore, in the invention, when the multiple thinning-out patterns different in printing acceptable rate are used in one image, the acceptable rate of the thinning-out pattern with the highest printing acceptable rate in the thinning-out patterns used in one image is the printing acceptable rate.
By making the printing acceptable rate by the thinning-out pattern 15% or more, the probability that the jetted ink droplets are printed side by side one another becomes high, and therefore the effects obtained by applying the properties of the inks, the medium and the recording method of the invention are great. Thus, by applying the invention, the high-quality images with less bronzing can be obtained. On the other hand, by making the printing acceptable rate 35% or less, in the portions where adhering liquid amounts are large such as red, blue and dark grey, the high quality images can be obtained.
It is preferred that a dot size formed by the color ink jetted from the recording head is from 10 to 50 μm on the recording medium. By making the dot size formed by the color ink 10 μm or more, it is possible to maintain a printing efficiency at a certain level or more, and accurately control an ink droplet size. Also, by making it 50 μm or less, it is possible to suppress the bronzing due to the ink droplets one another printed side by side, and obtain the images at high definition.
In the present invention, at least one special color ink is used together with basic color inks of yellow, magenta, cyan and black. A special color ink is an ink having a color between one color of basic colors (cyan, magenta and yellow) and another color of the basic colors, and for example, means an ink of red, green, violet, orange, blue or the like. By using the special color ink together with basic color inks of yellow, magenta, cyan and black, it is possible to reduce the amount of inks to be jetted. As a result, it is possible to prevent aggregation of pigment particles which are comprised in jetted ink and realize a color image with high quality and high definition in which decrease of gloss, bronzing, and color turbidity are suppressed.
In case of using such a special color, there are more kinds of ink than ordinary printing with CMYK inks. No method for separating input image data (RGB, CMYK or the like) into respective colors is established as a common belief, and technical know-how depending on inks to be used is required. As for this, color separation in accordance with a special color to be used is made possible by using the art enclosed in JP-Tokukai-2000-32284A by the present applicant, or the like. According to this art, it is possible to use the color gamut extended by a special color ink most effectively and also secure continuity of color calorimetrically.
In addition to this, alternatively, such a method as described in JP-2711081B can generate special color version of data. According to the method, data value for a blue ink is generated from data values of cyan and magenta. It is possible to perform ink amount control, such as reducing the total ink amount by cutting down data value for cyan and magenta depending on the data, and reducing roughness by using light-colored cyan and magenta without a special color in highlight part.
Next, the color inks according to the invention are illustrated.
The color inks of the invention contain pigments, at least one organic solvent with high boiling point and water, and additionally it is preferred that a surface tension of the color inks is from 30 to 50 mN/m and the pigments are dispersed by a polymeric dispersant.
As the pigments which can be used for the invention, it is possible to use chromatic organic or chromatic inorganic pigments known in the art. For example, azo pigments such as azo lake, insoluble azo pigments, condensed azo pigments and chelate azo pigments, polycyclic pigments such as phthalocyanine pigments, perylene pigments, anthraquinone pigments, quinacridone pigments, dioxazine pigments, thioindigo pigments, isoindolinone pigments and quinophthalone pigments, dye lakes such as basic dye lake and acid dye lake, organic pigments such as nitro pigments, nitroso pigments, aniline black and daylight fluorescent pigments, and inorganic pigments such as carbon black are included but the invention is not limited thereto.
Specific organic pigments are exemplified below.
As the pigments for magenta, for example, C.I. Pigment Red 2, C.I. Pigment Red 3, C.I. Pigment Red 5, C.I. Pigment Red 6, C.I. Pigment Red 7, C.I. Pigment Red 15, C.I. Pigment Red 16, C.I. Pigment Red 48:1, C.I. Pigment Red 53:1, C.I. Pigment Red 57:1, C.I. Pigment Red 122, C.I. Pigment Red 123, C.I. Pigment Red 139, C.I. Pigment Red 144, C.I. Pigment Red 166, C.I. Pigment Red 202, C.I. Pigment Red 222, C.I. Pigment Violet 19 and the like are included.
As the pigments for red, for example, C.I. Pigment Red 17, C.I. Pigment Red 49:2, C.I. Pigment Red 112, C.I. Pigment Red 149, C.I. Pigment Red 177, C.I. Pigment Red 178, C.I. Pigment Red 188, C.I. Pigment Red 255, C.I. Pigment Red 264 and the like are included.
As the pigments for yellow, for example, C.I. Pigment Orange 31, C.I. Pigment Yellow 12, C.I. Pigment Yellow 13, C.I. Pigment Yellow 14, C.I. Pigment Yellow 15, C.I. Pigment Yellow 17, C.I. Pigment Yellow 74, C.I. Pigment Yellow 93, C.I. Pigment Yellow 94, C.I. Pigment Yellow 128, C.I. Pigment Yellow 138 and the like are included.
As the pigments for orange, for example, C.I. Pigment Orange 36, C.I. Pigment Orange 43, C.I. Pigment Orange 61 and the like are included.
As the pigments for cyan, for example, C.I. Pigment Blue 15, C.I. Pigment Blue 15:2, C.I. Pigment Blue 15:3, C.I. Pigment Blue 16 and the like are included.
As the pigments for green, for example, C.I. Pigment Green 7, C.I. Pigment Green 36 and the like are included.
As the pigments for blue, for example, C.I. Pigment Blue 60, C.I. Pigment Violet 23 and the like are included.
As the pigment for black, for example, C.I. Pigment Black 1, C.I. Pigment Black 6, C.I. Pigment Black 7 and the like are included.
As methods for dispersing the pigments, it is possible to use various dispersing machines such as a ball mill, sand mill, attritor, roll mill, agitator, Henschel mixer, colloid mill, ultrasonic homogenizer, pearl mill, wet type jet mill and paint shaker. Also it is preferable to use a centrifuging machine and a filter for the purpose of eliminating crude particles of a pigment dispersion.
In the ink of the invention, it is one of the characteristics to use a polymeric dispersant for the dispersion of the pigments. The polymeric dispersant of the invention is not particularly limited, and a water-soluble resin or a water-insoluble resin is used. As these polymeric molecules, it is possible to include polymers made up of a single monomer or copolymers made up of two or more monomers selected from styrene, styrene derivatives, vinylnaphthalene derivatives, acrylic acid, acrylate derivatives, methacrylic acid, methacrylate derivatives, maleic acid, maleate derivatives, itaconic acid, itaconate derivatives, fumaric acid and fumarate derivatives, and salts thereof. Also, it is possible to use water-soluble polymeric molecules such as polyvinyl alcohol, polyvinyl pyrrolidone, cellulose derivatives, gelatin, and polyethyleneglycol.
It is preferred that these polymers have both a hydrophilic moiety and a hydrophobic moiety. The hydrophilic moiety has a function to stabilize the dispersion in water which is a major component of the ink, whereas the hydrophobic moiety has a function to enhance adhesion onto pigment surfaces. Among others, acryl type polymeric dispersants are preferably used in terms of the characteristics such as easiness of molecular structure design and easiness to obtain a performance as the dispersant. The acryl type polymeric dispersant is referred to the polymeric dispersant containing an acryl type monomer at least at 30 mol % or more.
As such an acryl type polumeric dispersant, polymers made up of the hydrophobic monomer and hydrophilic monomer shown below, or copolymers made up of two or more of the monomers, and salts thereof are preferable. The hydrophobic monomers include but are not limited to, for example, styrene, α-methylstyrene, methyl methacrylate (MMA), ethyl methacrylate (EMA), propyl methacrylate, n-butyl methacrylate (BMA or NBMA), hexyl methacrylate, 2-ethylhexyl methacrylate (EHMA), octyl methacrylate, lauryl methacrylate (LMA), stearyl methacrylate, phenyl methacrylate, hydroxyethyl methacrylate (HEMA), hydroxypropyl methacrylate, 2-ethoxyethyl methacrylate, methacrylonitrile, 2-trimethylsiloxyethyl methacrylate, glycidyl methacrylate (GMA), p-tolyl methacrylate, sorbyl methacrylate, methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, hexyl acrylate, 2-ethylhexyl acrylate, octyl acrylate, lauryl acrylate, stearyl acrylate, phenyl acrylate, hydroxyethyl acrylate, hydroxypropyl acrylate, acrylonitrile, 2-trimethylsiloxyethyl acrylate, glycidyl acrylate, p-tolyl acrylate, sorbyl acrylate, benzyl acrylate, benzyl methacrylate, 2-phenylethyl methacrylate and the like.
As the hydrophobic monomer, styrene, methyl methacrylate, butyl methacrylate, 2-ethylhexyl methacrylate, benzyl methacrylate, 2-phenylethyl methacrylate, or benzyl acrylate is particularly preferable.
The hydrophilic monomers include, but are not limited to, for example, methacrylic acid (MAA), acrylic acid, maleic acid, dimethylaminoethyl methacrylate (DMAEMA), diethylaminoethyl methacrylate, tert-butylaminoethyl methacrylate, dimethylaminoethyl acrylate, diethylaminoethyl acrylate, dimethylaminopropyl methacrylamide, methacrylamide, acrylamide, dimethyl acrylamide and the like.
As the hydrophilic monomer, methacrylic acid, acrylic acid or dimethylaminoethyl methacrylate is preferable.
A polymeric molecule containing an acid is manufactured directly from an unsaturated acid or manufactured from a blocked monomer having a blocking group which can be eliminated after polymerization. As examples of the blocked monomer which produces acrylic acid or methacrylic acid after eliminating the blocking group, trimethylsilyl methacrylate (TMS-MAA), trimethylsilyl acrylate, 1-butoxyethyl methacrylate, 1-ethoxyethyl methacrylate, 1-butoxyethyl acrylate, 1-ethoxyethyl acrylate, 2-tetrahydropyranyl acrylate, 2-tetrahydropyranyl methacrylate and the like are included.
Structures of these polymers include random polymer or random copolymer, block copolymer, branched polymer or copolymer, graft polymer or copolymer. Among others, the block copolymer and the branched copolymer are preferable for the object of the invention because the design and control of the hydrophilic and hydrophobic moieties are easy.
The block polymers include structures such as AB, BAB and ABC types (here, A, B and C schematically represent high molecular blocks different in structure one another), but there is no restriction of the structure so long as the block moiety is present. Particularly, the block polymer having a hydrophobic block and a hydrophilic block or having a balanced block size which contributes to dispersion stability is preferable. A functional group can be incorporated in the hydrophobic block (block to which a coloring agent is bound) thereby improving the dispersion stability, and thus a specific interaction between the dispersant and the coloring agent is further enforced.
These polymers can be synthesized by conventionally known in the art, and can be synthesized particularly by the methods disclosed in the specification of U.S. Pat. Nos. 5,085,698, 5,221,334, 5,272,201, 5,519,085 and 6,117,921, and the examples in JP-Tokukaihei-10-279873A, 11-269418A, JP-Tokukai-2001-115065A, 2001-139849A, 2001-247796A and 2003-260348A.
As the hydrophobic monomers which can be used for the block copolymer, for example, it is possible to include the same monomers as the hydrophobic monomers which can be used for the acryl type polymeric dispersant.
As the hydrophobic monomers, methyl methacrylate, butyl methacrylate, 2-ethylhexyl methacrylate, benzyl methacrylate, 2-phenylethyl methacrylate, or benzyl acrylate is particularly preferable. As the hydrophobic high molecular block, the polymer made up of the above single monomer or the copolymer block made up of two or more monomers is preferable.
As the hydrophilic monomers which can be used for the block copolymer, for example, it is possible to include the same monomers as the hydrophilic monomers which can be used for the acryl type polymeric dispersant.
The hydrophilic monomer is preferably methacrylic acid, acrylic acid or dimethylaminoethyl methacrylate, and as the hydrophilic polymer high molecular block, the polymer made up of the above single monomer or homopolymer and copolymer made up of two or more of the monomers are preferable.
As the monomers which can be used for the branched polymer or copolymer and the graft polymer or copolymer, it is possible to use those included as the monomers which can be used for the above block copolymer. The branched polymer or copolymer and the graft polymer or copolymer can be easily synthesized by using a macromer having a polymerizable functional group at one end, for example, silicone macromer, styrene type macromer, polyester type macromer, polyurethane type macromer or polyalkylether macromer. As examples of the above macromer, styrene macromers AS-6 and AN-6 supplied from Toagosei Co., Ltd., silicone macromers FM-0711 and FM-0721 supplied from Chisso Corporation, polyethyleneglycol and polyethyleneglycol methacrylate and the like are included.
A weight average molecular weight of these polymeric molecules is preferably in the range of 1,000 to 30,000, and more preferably in the range of 1,500 to 15,000. An acid value is preferably in the range of 10 to 500, and more preferably in the range of 50 to 250.
In the ink of the invention, a pigment dispersant known in the art, for example, surfactants such as higher fatty acid salts, alkyl sulfate salts, alkyl ester sulfate salts, alkyl sulfonate salts, sulfosuccinate salts, naphthalene sulfonate salts, alkyl phosphate salts, polyoxyalkylenealkylether phosphate salts, polyoxyalkylenealkylphenyl ether, polyoxyethylenepolyoxypropyleneglycol, glycerin ester, sorbitan ester, polyoxyethylene fatty acid amide and amine oxide may be combined along with the above polymeric dispersant.
In the aqueous ink of the invention, a volume average particle size of a pigment dispersion is preferably from 20 to 200 nm in terms of obtaining preferable color tone, high print density or good gloss, and more preferably from 40 to 140 nm in terms of additionally improving light resistance.
In the invention, the volume average particle size of the pigment dispersion can be obtained by a commercially available particle size measuring instrument using a light scattering method, electrophoresis, a laser Doppler method and the like, and as a specific particle size measuring instrument, for example, it is possible to include Zetasizer 1000HS supplied from Malvern Instruments.
The water-soluble organic solvents which can be used in the invention specifically include alcohols (e.g., methanol, ethanol, propanol, isopropanol, butanol, isobutanol, secondary butanol, tertiary butanol, pentanol, hexanol, cyclohexanol, benzyl alcohol, etc.), polyvalent alcohols (e.g., ethyleneglycol, diethyleneglycol, triethyleneglycol, polyethyleneglycol, propyleneglycol, dipropyleneglycol, polypropyleneglycol, butyleneglycol, hexanediol, pentanediol, glycerin, hexanetriol, thiodiglycol, etc.), polyvalent alcohol ethers (e.g., ethyleneglycol monomethylether, ethyleneglycol monoethylether, ethyleneglycol monobutylether, ethyleneglycol monophenylether, diethyleneglycol monomethylether, diethyleneglycol monoethylether, diethyleneglycol monobutylether, diethyleneglycol dimethylether, propyleneglycol monomethylether, propyleneglycol monobutylether, ethyleneglycol monomethylether acetate, triethyleneglycol monomethylether, triethyleneglycol monoethylether, triethyleneglycol monobutylether, triethyleneglycol dimethylether, dipropyleneglycol monopropylether, tripropyleneglycol dimethylether, etc.), amines (e.g., ethanolamine, diethanolamine, triethanolamine, N-methyldiethanolamine, N-ethyldiethanolamine, morpholine, N-ethylmorpholine, ethylenediamine, diethylenediamine, triethylenetetramine, tetraethylenepentamine, polyethyleneimine, pentamethyldiethylenetriamine, tetramethylpropylenediamine, etc.), amides (e.g., formamide, N-N-dimethylformamide, N,N-dimethylacetamide, etc.), heterocycles (e.g., 2-pyrrolidone, N-methyl-2-pyrrolidone, N-cyclohexyl-2-pyrrolidone, 2-oxazolidone, 3-dimethyl-2-imidazolidinone, etc.), sulfoxides (e.g., dimethylsulfoxide, etc.), sulfones (e.g., sulforane, etc.), sulfonate salts (e.g., sodium 1-butylsulfonate salt, etc.), acetonitrile, acetone, and the like.
It is also preferred that the respective colored inks according to the invention contain urea or an urea derivative. By containing urea or the urea derivative in the respective colored inks according to the invention, it is preferable because it is possible to inhibit aggregation of the pigment particles in the jetted ink liquid drops on the recording medium and consequently improve glossiness and texture. It is preferred that this urea or urea derivative has appropriately strong interaction for expressing objective effects by the interaction such as hydrogen bonds. As such compounds, urea, thiourea, and urea derivatives substituted with lower alkyl group (e.g., methylurea, dimethylurea, butylurea, ethyleneurea, phenylurea, etc.) are preferable, and particularly urea and ethyleneurea are preferable.
In the respective colored inks according to the invention, it is preferred in the light of being capable of obtaining the images with favorable output stability and high density having preferable gloss that a content of urea is from 1 to 20% by mass.
In the ink according to the invention, pH is preferably 7.0 or above, and more preferably from 8.0 to 10.0. By making the above pH, the image where injection stability is good and print density is high and having a preferable gloss can be obtained, and thus it is preferable. As a pH adjuster used for the color ink according to the invention, for example, various organic amine such as monoethanolamine, diethanolamine and triethanolamine, inorganic alkali agents such as hydroxide of alkali metal such as sodium hydroxide, lithium hydroxide and potassium hydroxide, organic acids and mineral acids.
It is preferable that a surface tension of the ink according to the invention is from 30 to 50 mN/m. When the surface tension of the ink becomes less than 30 mN/m, a absorption speed to the recording medium becomes fast and aggregation by pigment particles one another occurs resulting in occurrence of bronzing and reduction of gloss and scratch/abrasion resistance. When the surface tension exceeds 50 mN/m, color turbidity due to long retention of jetted ink droplets on the medium occurs, and it becomes impossible to obtain the image at high definition.
For the surface tension, it is possible to adjust to the desired surface tension by appropriately conditioning types and addition amounts using the various water-soluble organic solvents described above and various surfactants described below.
The method of measuring the surface tension is described in general reference books of surface chemistry and colloid chemistry, for example, Shin Jikken Kagaku Kouza, Vol. 18 (Surface and Colloid) edited by the Chemical Society of Japan and published by Maruzen Co., Ltd.: pages 68 to 117 can be referred, and specifically, it can be obtained by a ring method (DuNouy method) or a plate method (Wilhelmy method).
As one of ways to accomplish the above surface tension, various surfactants can be used. Various surfactants which can be used in the invention are not particularly limited, and for example, include anionic surfactants such as dialkyl sulfosuccinate salts, alkylnaphthalene sulfonate salts and fatty acid salts, nonionic surfactants such as polyoxyethylene alkylethers, polyoxyethylene alkylallylethers, acetyleneglycols, block copolymer of polyoxyethylene and polyoxypropylene, and cationic surfactants such as alkylamine salts, and quaternary ammonium salts. Particularly, the anionic surfactants and the nonionic surfactants can be preferably used.
In the invention, it is preferred that acetylene type surfactant is used as the surfactant in terms of being capable of obtaining the image where the injection stability is good with high print density, having preferable gloss and which is excellent in uniformity.
The acetylene type surfactant is not particularly limited, for example, includes acetylene glycols and acetylene alcohols, is more preferably the surfactant having acetylene group and alkylene oxide chain, and for example, can include Surfynol 465 (supplied from Nisshin Chemical Industry Co., Ltd.).
In the ink of the invention, in addition to the above illustration, if necessary, various additives known in the art, for example, a viscosity adjuster, specific resistance adjuster, film forming agent, ultraviolet ray absorbent, anti-oxidant, anti-color fading agent, antimicrobials and fungicides, anti-rusting agent and the like can be used for the purpose of the injection stability, compatibility of the recording head 22 and ink cartridge, storage stability, image permanence, and the other performance improvement. For example, as these additives it is possible to include oil droplet fine particles such as liquid paraffin, dioctyl phthalate, tricresyl phosphate and silicon oil, the ultraviolet ray absorbents described in JP-Tokukaisho-57-74193A, JP-Tokukaisho-57-87988A and JP-Tokukaisho-62-261476A, the anti-color fading agents described in JP-Tokukaisho-57-74192A, 57-87989A, 60-72785A, 61-146591A, JP-Tokukaihei-1-95091A and 3-13376A, the fluorescent brightening agents described in JP-Tokukaisho-59-42993A, 59-52689A, 62-280069A, 61-242871A and JP-Tokukaihei-4-219266A, and the like.
Then, the recording medium of the invention is illustrated.
Generally, as an ink absorbing layer, there are a swelling type and a micro-porous type by broadly dividing. As the swelling type, a water-soluble binder, for example, gelatin, polyvinyl alcohol, polyvinyl pyrrolidone, polyethylene oxide and the like is applied alone or in combination, and this is made the ink absorbing layer. However, in the invention, in order to adapt to continuous high speed print, the recording medium where an ink absorption speed is high is more suitable, and thus from this point, the inkjet recording medium having the ink absorbing layer of the micro-porous type is used.
In the recording medium having the ink absorbing layer of the micro-porous type (also referred to as a micro-porous layer) of the invention, it is one of the characteristics that a transferred amount at 0.04 seconds of absorption time by Bristow method is 10 ml/m2 or more, and it is preferably 10 ml/m2 or more and 30 ml/m2 or less. When the transferred amount is less than 10 ml/m2, the ink absorption speed on the recording medium is reduced, color turbidity occurs when the jetted ink droplets are printed side by side, and it becomes impossible to obtain the image at high definition.
In the recording medium of the invention, the method to accomplish the transferred amount defined above is not particularly limited, and the transferred amount can be used by appropriately conditioning a thickness of the micro-porous layer, a mean particle size of inorganic fine particles (F) which configure the micro-porous layer, a type of a hydrophilic binder (B), a ratio (F/B) of the inorganic fine particles to the hydrophilic binder (B), a type of a support used and the like.
Bristow method referred to in the invention is the method of measuring liquid absorption behavior of paper and plate paper in a short time. Particularly, according to J. TAPPI paper pulp test method No. 51-87, a method of testing absorbability of the paper or plate paper (Bristow method), the measurement is performed, and the absorption is represented by the transferred amount (ml/m2) at 0.04 sec of the absorption time. In the above method, purified water (ion-exchange water) is used for the measurement. However, in order to make determination of a measurement area easy, in the invention, the measurement is performed using an aqueous solution of 2% C.I. Acid Red 52.
One example of specific measurement method is illustrated below.
As the method of measuring the transferred amount, after leaving the recording medium under an atmosphere of 25° C. and 50% RH for 12 hours or more, the measurement is performed using a Bristow testing machine II type (press mode) which is a liquid dynamic absorbability testing machine supplied from Kumagai Rikikogyo Co., Ltd. The aqueous solution of 2% C.I. Acid Red 52 is used for the measurement as mentioned above to enhance measurement accuracy, and the transferred amount can be obtained by measuring an area stained on the recording medium after a defined contact time.
As for a recording medium according to the present invention, it is a characteristic that the 20-degree specular gloss according to JIS-Z-8741 is 20 to 45%.
The 20-degree specular gloss is a 20-degree specular gloss value (%) measured according to the method provided in JIS-Z-8741. A specular gloss correlates with the smoothness of a surface of recording media. A smoother surface has a higher specular gloss value. Therefore in case of a 20-degree specular gloss less than 20%, the smoothness of the surface of recording media is inadequate and forming a pigment image thereon leads to decreasing gloss of the image as a whole. Increase of the amount of adhered pigment cause increase of the specular gloss. In this case, if a white background part (surface of recording media) with no pigment adhered has a specular gloss less than 20%, gloss difference between the image part and the no-image part becomes larger and only the image part stands out in bold relief.
Meanwhile, when trying to manufacture the recording medium where the 20-degree specular gloss exceeds-45%, numerous energy is required to make the surface smooth, and it becomes unrealistic. Furthermore, when the surface is made smooth such that the 20-degree specular gloss exceeds 45%, the micro-porous layer of the recording medium is crushed, the absorption speed and the absorption capacity are reduced consequently leading to color turbidity at the image formation, and it becomes impossible to obtain the image with high definition. Thus, by making the 20-degree specular gloss between 20% and 45%, it is possible to inhibit a phenomenon where only the image section stands out in bold relief, which is unique for the image formed by the pigment inks, and improve depth feel of the whole image. Also, it is possible to form the image with high definition without causing the color turbidity. As a result, it becomes possible to obtain the images which come near the silver salt photographs.
The 20-degree specular gloss according to the invention can be measured using, for example, precision glossmeters GM-26D, True Gloss GM-26DPRO and a variable angle glossmeter GM-3D (supplied from Murakami Color Research Laboratory), variable angle glossmeters VGS-10001DP, VG-2000 (supplied from Nippon Denshoku Industries Co., Ltd.), a digital variable angle glossmeter (supplied from Suga Test Instruments Co., Ltd.) and the like.
In the recording medium according to the invention, a way for realizing the 20 degree specular gloss value (%) within the scope defined in the invention is not particularly limited, but, for example, the desired 20 degree specular gloss value (%) can be obtained by the method of previously giving a smoothing treatment to a support surface and forming an ink absorption layer thereon, the method of installing the ink absorption layer on the smooth support where boric acid has been previously impregnated, the method of installing a polymer fine particle layer on an ink absorption layer surface and smoothing by treatment with heat and pressure, the method of installing a gloss layer made up of inorganic fine particles and a binder on the ink absorption layer surface, the method of applying the ink absorption layer and subsequently performing the smoothing treatment such as a calendar treatment, and the like. For example, in the case of surface smoothing by a specular roll, it is preferable to perform typically at about 20 to 100° C. with a line pressure of 0.5 to 4 kN/cm, at a feeding velocity of 10 to 500 m/min as a calendar condition and dry at about 20 to 100° C. for about 0.1 to 10 min.
Hereinafter, respective constituent factors of the inkjet recording medium of the invention are illustrated.
Conventionally, various methods of forming micro-pores in a membrane have been known, for example, the method of forming micro-pores by applying a uniform coating solution containing two or more polymeric molecules onto a support and causing phase separation of these polymeric molecules in a drying process, the method of making micro-pores by applying a coating solution containing solid fine particles and a hydrophilic or hydrophobic resin onto a support, after drying, immersing an inkjet recording medium in water or a liquid containing an appropriate organic solvent, and dissolving the solid fine particles, the method of forming micro-pores in a membrane by applying a coating solution containing a compound having a nature which foams at the membrane formation, and subsequently foaming this compound in a drying process, the method of forming micro-pores in porous fine particles and between fine particles by applying a coating solution containing porous solid fine particles and a hydrophilic binder on a support, the method of forming micro-pores between solid fine particles by applying a coating solution containing solid fine particles or fine particle oil droplets having a volume nearly equal to or more than that of a hydrophilic binder and the hydrophilic binder on a support, and the like have been known.
The micro-porous layer of the invention indicates an ink receiving layer with a void rate of 25 to 75%, and preferably the void rate of 30 to 70%, mainly formed from the inorganic fine particles and a small amount of the hydrophilic binder.
In the invention, it is the characteristics that the micro-porous layer is formed by containing the inorganic fine particles with a mean particle size of 15 to 100 nm, and preferably the mean particle size is from 20 to 80 nm. When the mean particle size exceeds 100 nm, deterioration of surface gloss of a coating occurs.
As the inorganic fine particles used for the above purpose, it is possible to include white inorganic pigments such as calcium carbonate light, calcium carbonate heavy, magnesium carbonate, kaolin, clay, talc, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide, zinc hydroxide, zinc sulfide, zinc carbonate, hydrotalcite, aluminium silicate, diatomite, calcium silicate, magnesium silicate, synthetic amorphous silica, colloidal silica, alumina, colloidal alumina, pseudoboehmite, aluminium hydroxide, lithopone and magnesium hydroxide.
The mean particle size of the inorganic fine particles in the invention is obtained as the simple mean value (number mean) by observing cross sections and surfaces of the micro-porous layer in the recording medium by an electron microscope and randomly measuring the particle size of 1,000 particles. Here, the particle size of individual particle is a diameter when a circle equal to a projection area thereof is supposed. As the inorganic fine particle, it is preferable to use silica or alumina.
As the silica which can be used in the invention, silica synthesized by a usual wet method, colloidal silica or silica synthesized by a vapor phase method or the like is preferably used, and as the silica preferably used in the invention, colloidal silica or fine particle silica synthesized by the vapor phase method is preferable. Among others, the fine particle silica synthesized by the vapor phase method has a characteristics that a so-called soft aggregation structure is formed by coexisting with the hydrophilic binder to give a high void rate. Further this fine particle silica when it is added to a cationic polymer molecule used for the purpose of immobilizing colorants, rough and large aggregation is difficult to be formed, and thus it is preferable.
Alumina or alumina hydrate which can be used in the invention may be crystalline or amorphous, and it is possible to use those with any shape such as undefined shaped particles, spherical particles and needle particles. Among others, the alumina hydrate having a plate shape where an average aspect ratio is from 1 to 4 is preferable. There are those having a fibrous shape and those having a plate shape in the alumina hydrate. When the fibrous alumina hydrate is used, it is prone to orientate in parallel with a substrate surface at the application, and thus formed micropores become small. On the contrary, in the case of the plate alumina hydrate, tendency to orientate to a certain direction by the application is small, and a relatively large void rate can be obtained.
As the hydrophilic binder which can be used in the micro-porous layer of the invention, for example, polyvinyl alcohol, gelatin, polyethylene oxide, polyvinyl pyrrolidone, polyacrylic acid, polyacrylamide, polyurethane, dextran, dextrin, carrageenan (κ, ι, λ, etc.) agar, pullulan, water-soluble polyvinyl butyral, hydroxyethylcellulose, carboxymethylcellulose, and the like are included. It is possible to combine two or more of these water-soluble binders, but polyvinyl-alcohol or derivatives thereof are particularly preferable in terms of relatively small moisture absorption property of the binder, smaller curl of the medium and being high binder performance by the use of a small amount with excellent crack and velation.
As polyvinyl alcohol preferably used in the invention, modified polyvinyl alcohol such as polyvinyl alcohol where the end is modified with cation, and anion modified polyvinyl alcohol having anionic group are included in addition to common polyvinyl alcohol obtained by hydrolyzing polyvinyl acetate.
As polyvinyl alcohol obtained by hydrolyzing polyvinyl acetate, those with an average polymerization degree of 300 or more are preferably used, and particularly those with an average polymerization degree of 1,000 to 5,000 are preferably used. A saponification degree is preferably from 70 to 100%, and particularly preferably 80 to 99.8%.
The cation modified polyvinyl alcohol is, for example, the polyvinyl alcohol having primary to tertiary amino groups and quaternary amino groups in a backbone or side chains as described in JP-Tokukaisho-61-10483A, and this is obtained by saponifying a copolymer of an ethylenic unsaturated monomer having cationic group and vinyl acetate.
As the ethylenic unsaturated monomer having cationic group, for example, trimethyl-(2-acrylamide-2,2-dimethylethyl)ammonium chloride, trimethyl-(3-acrylamide-3,3-dimethylpropyl)ammonium chloride, N-vinylimidazole, N-methylvinylimidazole, N-(3-dimethylaminopropyl)methacrylamide, hydroxyethyltrimethylammonium chloride, trimethyl-(3-methacrylamidepropyl)ammonium chloride and the like are included.
A percentage of cation modified group-containing monomer of the cation modified polyvinyl alcohol is from 0.1 to 10 mol %, and preferably from 0.2 to 5 mol % based on vinyl acetate.
As anion modified polyvinyl alcohol, for example, polyvinyl alcohol having anionic group described in JP-Tokukaihei-1-206088A, copolymers of vinyl alcohol and a vinyl compound having water-soluble group described in JP-Tokukaisho-61-237681A and 63-307979, and modified polyvinyl alcohol having water-soluble group described in JP-Tokukaihei-7-285265A are included.
As nonionic modified polyvinyl alcohol, for example, polyvinyl alcohol derivatives where polyalkyleneoxide group is added to a part of vinyl alcohol described in JP-Tokukaihei-7-9758A, block copolymer of a vinyl compound having hydrophobic group and vinyl alcohol described in JP-Tokukaihei-8-25795A, and the like are included.
Polyvinyl alcohol can be also used in combination with two or more depending on difference in polymerization degree and modification type. Particularly when polyvinyl alcohol with a polymerization degree of 2,000 or more, is used, if it is precedently added at 0.05 to 10% by mass, preferably from 0.1 to 5% by mass based on the inorganic fine particles and then polyvinyl alcohol with a polymerization degree of 2,000 or more is added, there is no remarkable thickening and it is preferable.
A ratio of the inorganic fine particles to the hydrophilic binder in the micro-porous layer is preferably from 2 to 20 at a mass ratio. When the mass ratio is 2 times or more, a porous membrane with sufficient void rate is obtained, a sufficient void capacity is easily obtained, micro-pores are not occupied by swelling of retainable hydrophilic binder at the inkjet recording, and thus it becomes a factor capable of retaining a high ink absorption speed. On the other hand, if this ratio is 20 times or less, when the micro-porous layer is formed by applying a thick membrane, it becomes difficult to cause cracks. The particularly preferable ratio of the inorganic fine particles to the hydrophilic binder is from 2.5 to 12 times, and most preferably it is from 3 to 10 times.
It is preferred that a total amount of the micro-pores (void capacity) in the micro-porous layer is 16 ml or more per m2 of the recording medium. By making the void capacity 16 ml/m2 or more, even when an ink amount becomes large, it is possible to make an ink absorbability good, and thus it is possible to improve the image quality and suppress reduction of drying.
The upper limit of the void capacity is preferably not more than 25 ml/m2. Though the more micro-pores lead to increase of the absorption speed and absorption capacity, on the contrary, at the same time, it becomes more delicate to an external force. Trying to the increase thickness for this has a problem that a crack is easily generated in production. Though it is possible to increase the absorption speed and absorption capacity by increasing the void rate without changing the thickness, it becomes also delicate to generation of crack. Whereas there are various studies to overcome the problem, in the present circumstance, a thickness or a void rate with the absorption speed per unit area more than 25 ml/m2 causes much generation of minute crack. As a result, it becomes impossible to form a high-quality image. Therefore it is preferable that a recording medium having a micro-porous layer is designed and produced in such a way that the recording medium has a thickness or a void rate with an absorption capacity per unit area not more than 25 ml/m2.
The void capacity in the invention indicates a saturated water absorption amount obtained by Bristow method. When the transferred amount obtained by Bristow method is plotted versus a square root of the absorption time, a line with a certain slope is obtained. This represents changes of absorption amounts of the recording medium versus the absorption time. When the ink (here, referred to the aqueous solution of 2% C.I. acid red 52) is absorbed to fill up the void capacity, there becomes no room, and thus the slope is 0. The water absorption amount at that time is the saturated water absorption amount, and is considered as a value which represents the void capacity. In the case of the recording medium having an absorbable support preferably used in the invention, it sometimes represents the absorption of the support in addition to the ink absorption by the ink absorbing layer. In the recording medium used in the invention, the absorption speed of the ink in the ink absorbing layer is overwhelmingly much faster than that in the support, and thus, even when the absorption by the support is measured, a curve has double slopes and discrimination of both is easy.
The void rate referred to in the invention indicates the rate of a total volume of the voids in a volume of the micro-porous layer. The void capacity obtained by the above Bristow method can be used as it is for the total volume of the voids. The volume of the micro-porous layer can be obtained as the volume per m2 of the recording medium by measuring the dried membrane thickness. The aimed void rate can be obtained as a ratio of both volumes by calculation. The total volume of the voids can be easily obtained by the saturated transferred amount and the water absorption amount measurement by Bristow method.
For the above micro-porous layer, various additives can be used in addition to the inorganic fine particles and the binder. Among others, a cationic polymeric molecule, hardener, urea or a derivative thereof plays important roles in terms of improving bleeding resistance, bronzing resistance, and scratch/abrasion resistance.
Examples of the cationic polymer molecules include polyethyleneimine, polyallylamine, polyvinylamine, dicyandiamidepolyalkylenepolyamine condensates, polyalkylenepolyaminedicyandiamide ammonium condensates, dicyandiamideformaline condensates, epichlorohydrin/dialkylamine addition polymers, diallyldimethylammonium chloride polymers, diallyldimethylammonium chloride/SO2 copolymers, polyvinylimidazole, vinylpyrrolidone/vinylimidazole copolymers, polyvinylpyridine, polyamidine, chitosan, cationized starch, vinylbenzyltrimethylammonium chloride polymers, (2-methacroyloxyethyl)trimethylammonium chloride polymers, dimethylaminoethyl methacrylate polymers, and the like.
Cationic polymeric molecules described in Kagaku Kogyo Jiho (Aug. 15 and 25, 1998) and polymeric molecular dye fixing agents described in “Kobunshi Yakuzai Nyumon” published by Sanyo Chemical Industries Ltd. are included as the examples.
In the recording medium according to the invention, it is preferable to add the hardener of the water-soluble binder which forms the micro-porous layer.
The hardener which can be used for a hard membrane of the water-soluble binder which forms the micro-porous layer in the invention is not particularly limited so long as it performs a hardening reaction with the water-soluble binder. Boric acid and salts thereof are preferable, but the other known in the art can be also used. Generally it is the compound having groups capable of reacting with the water-soluble binder or the compound which facilitates a reaction of different groups one another which the water-soluble binder has, and is appropriately used depending on the type of water-soluble binder. Specific examples of the hardener include epoxy type hardeners (diglycidylethylether, ethyleneglycol diglycidylether, 1,4-butanediol diglycidylether, 6-diglycidylcyclohexane, N,N-diglycidyl-4-glycidyloxyaniline, sorbitol polyglycidylether, etc.), aldehyde type hardeners (formaldehyde, glyoxazol, etc.), active halogen type hardeners (2,4-dichloro-4-hydroxy-1,3,5-s-triadine, etc.), active vinyl type compounds (1,3,5-trisacryloyl-hexahydro-s-triadine, bisvinylsulfonylmethylether, etc.), aluminium alum, and the like.
Boric acid and salts thereof are referred to oxyacids where boron atom is a central atom and salts thereof, and specifically, ortho-boric acid, diboric acid, metaboric acid, tetraboric acid, pentaboric acid and octaboric acid and salts thereof are included.
Boric acid having boron atoms and the salts thereof as the hardeners may be used as an aqueous solution thereof alone or in mixture with two or more. Particularly preferable is a mixed aqueous solution of boric acid and borax. Aqueous solutions of boric acid and borax are each added only by relatively diluted aqueous solutions, but it is possible to make a thick aqueous solution by mixing the both, and concentrate the coating solution. Besides there is an advantage that pH of the added aqueous solutions can be controlled relatively freely. A total use amount of the above hardener is preferably from 1 to 600 mg per g of the above water-soluble binder.
It is possible to add polyvalent metal ions to the recording medium according to the invention. The polyvalent metal ion is not particularly limited so long as it is bivalent or more metal ion, and preferable polyvalent ions include aluminium ion, zirconium ion, titanium ion and the like. These polyvalent metal ions can be contained in the micro-porous layer in a water-soluble or water-insoluble salt form.
These polyvalent metal ions may be used alone or in combination with different two or more. The compound comprising the polyvalent metal ions may be added to a coating solution which forms the micro-porous layer or supplied to the micro-porous layer by an over coat method after once applying the micro-porous layer, particularly after once applying and drying the micro-porous layer. As the former, when the compound comprising the polyvalent metal ions is added to the coating solution which forms the ink absorbing layer, it is possible to use the method of adding by uniformly dissolving in water or an organic solvent or a mix solvent thereof or the method of adding by dispersing into fine particles by a wet pulverizing method of a sand mill, an emulsifying dispersion method and the like. When the micro-porous layer is made up of multiple layers, they may be added to the coating solution for only one layer or can be added to the coating solutions for two or more layer or all constitutive layers. As the latter, when they are added by the over coat method after once forming the micro-porous layer, it is preferred that the compound comprising the polyvalent metal ions is uniformly dissolved in the solvent, and subsequently supplied to the micro-porous layer.
These polyvalent metal ions are used in the range of about 0.05 to 20 mmol, and preferably from 0.1 to 10 mmol per m2 of the recording medium.
To the micro-porous layer according to the invention, various additives other than the above can be added. For example, it is possible to contain various additives known in the art such as polystyrene, polyacrylate esters, polymethacrylate esters, polyacrylamides, polyethylene, polypropylene, polyvinyl chloride, polyvinylidene chloride, or copolymers thereof, urea resins, or organic latex fine particles of melamine resins, various cationic or nonionic surfactants, ultraviolet ray absorbents described in JP-Tokukaisho-57-74193A, 57-87988A and 62-261476A, anti-color fading agents described in JP-Tokukaisho-57-74192A, 57-87989A, 60-71785A, 61-146591A, JP-Tokukaihei-1-95091A and 3-13376A, fluorescent brightening agents described in JP-Tokukaisho-59-42993A, 59-52689A, 62-280069A, 61-242871A and JP-Tokukaihei-4-219266A, pH adjusters such as sulfuric acid, phosphoric acid, citric acid sodium hydroxide, potassium hydroxide and potassium carbonate, ant-foaming agent, preservative, thickening agent, anti-electrostatic agent and matting agent.
Both an absorbable support and non-absorbable support can be used as the support of the recording medium according to the invention. In terms of exerting objective effects of the invention with no obstacle, for example, it is preferable to use the absorbable support which is a paper support such as plain paper, baryta paper, art paper, coated paper and cast-coated paper.
The absorbable support of the invention can include, for example, sheet, plate and the like having common paper, synthetic paper, fabrics, wood materials and the like, and particularly the paper is the most preferable because it is excellent in absorbability of the substrate itself and cost. The paper support is illustrated below.
As basic materials of the paper support, it is possible to use those where a major basic material is wood pulps such as chemical pulps such as LBKP and NBKP, mechanical pulps such as GP, CGP, RMP, TMP, CTMP, CMP and PGW, and used paper pulps such as DIP, and it is preferable to use hardwood pulps. As the hardwood pulps, kraft pulp, sulfate pulp, chemithermomechanical pulp, chemimechanical pulp and the like may be used alone or in combination with several types. If necessary, paper making is performed by using synthetic pulp such as polypropylene or synthetic fibers such as nylon and polyester in addition to the wood pulps.
In terms of improving whiteness degree, it is preferred that a bleaching treatment by peroxide and the like is given to the pulp which is a basic material. It is preferred that the bleaching treatment is given after digesting the pulp, subsequent chlorine treatment, alkali treatment or extraction, hypochlorite bleaching, chlorine dioxide bleaching, and multistage bleaching by combination thereof, further if necessary reduction bleaching by hydrosulfite and sodium borohydride. More preferably, peroxide bleaching treatment in alkali could be given as the final pulp bleaching treatment after the pulp bleaching treatments known in the art after digesting the pulp, but the alkali treatment or extraction or purification may be further given.
Various additives conventionally known in the art such as a sizing agent, pigments, paper power enhancer, fixing agents, fluorescent brightening agent, wet paper power agent and cationizing agent can be added to the paper support if necessary. As the sizing agent, the sizing agents such as a higher fatty acid, alkylketene dimer, rosin, paraffin wax, alkenylsuccinic acid and petroleum resin emulsion can be added if necessary. The pigments include calcium carbonate, talc, titanium oxide, urea resin fine particles and the like, the paper power enhancers include starch, polyacrylamide, polyvinyl alcohol and the like, and the fixing agents include sulfate band and cationic polymeric molecule electrolytes, but they are not limited thereto.
The paper support can be manufactured by mixing the above fiber substances such as wood pulps and various additives and using various paper making machines such as a fourdrinier machine, cylinder machine and twin wire paper making machine. If necessary, it is also possible to give a size press treatment by starch, polyvinyl alcohol and the like, various coating treatments and calendar treatment in the paper making stage or after the paper making.
A paper density is generally from 0.7 to 1.2 g/cm3 (JIS-P-8118). A base paper stiffness is preferably from 20 to 200 g under the condition defined in JIS-P-8143.
A paper pH is preferably from 5 to 9 when measured a hot water extraction method defined in JIS-P-8113.
In the invention, for the purpose of increasing an adhesion strength of the support and the ink receiving layer, it is possible to give corona discharge treatment, undercoating treatment and application of an intermediate layer prior to the application of the ink receiving layer.
Next, the method of manufacturing the inkjet recording medium of the invention is illustrated.
As the method of manufacturing the inkjet recording medium of the invention, it is possible to manufacture by appropriately selecting an application mode from the application modes known in the art and applying and drying respective constituent layers comprising the ink absorbing layer onto the support separately or simultaneously. As the application mode, for example, a roll coating method, rod bar coating method, air knife coating method, spray coating method, curtain application method, or a slide bead application method using a hopper described in U.S. Pat. Nos. 2,761,419 and 2,761,791, an extrusion coat method and the like are preferably used.
As a viscosity when a simultaneous overlaying application is performed, in the case of using the slide bead application mode, it is preferably in the range of 5 to 100 mPa·s, and more preferably from 10 to 70 mPa·s. In the case of using the curtain application mode, it is preferably in the range of 5 to 1200 mPa·s, and more preferably from 25 to 500 mPa·s.
The viscosity of the coating solution at 15° C. is preferably 100 mPa·s or more, more preferably from 100 to 30,000 mPa·s, still preferably from 3,000 to 30,000 mPa·s, and most preferably from 10,000 to 30,000 mPa·s.
As the applying and drying methods, it is preferred that the coating solution is heated to 30° C. or above, the simultaneous overlaying application is performed, subsequently a temperature of a formed coating film is once cooled to 1 to 15° C., and the drying is performed at 10° C. or above. More preferably, a drying condition is that the drying is performed at the condition in the range of a wet bulb temperature of 5 to 50° C. and a membrane surface temperature of 10 to 50° C. Cooling immediately after the application is preferably performed by a horizontal set mode in terms of formed coating film uniformity.
Hereinafter, the present invention is specifically illustrated by referring to Examples, but the invention is not limited thereto.
<<Manufacture of Recording Medium™>>
[Manufacture of Recording Medium 1]
[Manufacture of Support]
Base paper was made by preparing a slurry solution containing 1 part of polyacrylamide, 4 parts of ash (talc), 2 parts of cationized starch, 0.5 parts of polyamide epichlorohydrin resin and various addition amounts of alkylketene dimer (sizing agent) for 100 parts of wood pulp (LBKP/NBSP=50/50) and using a fourdrinier machine such that a weighing is 170 g/m2. A support which was an absorbable support having a smooth surface was made by giving a super calendar treatment to this base paper. Additionally an aqueous solution of 3% boric acid was applied and dried by a roll coater and a support 1 impregnated with 0.1 g/m2 of boric acid was manufactured.
After giving corona discharge to this support 1, a hardener-containing gelatin undercoating layer was applied at 0.04 g/m2 in terms of a solid content, and on a back face, a styrene/acryl type emulsion containing silica fine particles (matting agent) having a mean particle size of 1 μm and a small amount of a cationic polymeric molecule (conducting agent) was applied such that a dried film thickness is about 0.5 μm.
[Preparation of Coating Solution for Ink Absorbing Layer]
A coating solution for an ink absorbing layer (micro-porous layer) was prepared according to the following procedure.
[Preparation of Titanium Oxide Dispersion]
Titanium oxide (20 kg) (W-10 supplied from Ishihara Sangyo Co., Ltd.) having a mean particle size of 0.25 μm was added to 90 L of an aqueous solution at pH 7.5 containing 150 g of sodium tripolyphosphate, 500 g of polyvinyl alcohol (PVA235 supplied from Kuraray Co., Ltd.), 150 g of cationic polymeric molecule P-1 (refer to the following Chemical formula) and 10 g of anti-foaming agent SN 381 supplied from San nobuko KK, dispersed by a high pressure homogenizer (Sanwa Industries Co., Ltd.), and subsequently a total amount was filled up to 100 L to yield a uniform titanium oxide dispersion.
A total amount was filled up to 100 L with purified water.
As inorganic fine particles, 50 kg of silica fine particles (mean primary particle size: about 35 nm) were prepared, the above additives were added thereto, and subsequently the dispersion was performed by a dispersion method described in Example 5 of JP-Tokukai-2002-47454A to yield a silica dispersion 1.
1: Anti-color fading agent (AF-1) HO—N(C2H4SO3Na)2
2: UVITEX NFW LIQUID supplied from Ciba Specialty Chemicals Inc.
(Preparation of Silica Dispersion 2)
A silica dispersion 2 was prepared as is the case with the preparation of the above silica dispersion 1, except that the cationic polymeric molecule P-1 was changed to a cationic polymeric molecule P-2 (refer to the following Chemical formula).
(Preparation of Coating Solution)
Respective coating solutions of the first, second, third and fourth layers were prepared by the following procedures.
<Coating Solution for First Layer>
The following additives were sequentially added to 610 ml of the silica dispersion 1 at 40° C. with stirring.
A total amount was filled up to 1000 ml with purified water.
<Coating Solution for Second Layer>
The following additives were sequentially added to 630 ml of the silica dispersion 1 at 40° C. with stirring.
A total amount was filled up to 1000 ml with purified water.
<Coating Solution for Third Layer>
The following additives were sequentially added to 650 ml of the silica dispersion 2 at 40° C. with stirring.
A total amount was filled up to 1000 ml with purified water.
<Coating Solution for Fourth Layer>
The following additives were sequentially added to 650 ml of the silica dispersion 2 at 40° C. with stirring.
A total amount was filled up to 1000 ml with purified water.
The two step filtration of the respective coating solutions prepared as above was performed with a 20 μm filter capable of collecting.
All of the above coating solution exhibited viscosity property of 30 to 80 mPa·s at 40° C. and 30,000 to 100,000 mPa·s at 15° C.
(Application)
The respective coating solutions obtained in this way were simultaneously applied on an upper side of the above support made above to arrange in order of the first layer (35 μm), the second layer (45 μm), the third layer (45 μm) and the fourth layer (40 μm). A number in a parenthesis indicates a wet film thickness. The application was simultaneously performed at an application width of about 1.5 m at an application speed of 100 m/min using each coating solution at 40° C. and using a 4-layer type curtain coater, and then was calendered by a specular roll.
Immediately after the application, cooling was performed in a cooling zone retained at 8° C. for 20 sec, and subsequently drying was performed by blowing respective drying winds at 20 to 30° C. and a relative humidity of 20% or less for 30 sec, at 60° C. and a relative humidity of 20% or less for 120 sec, and at 55° C. and a relative humidity of 20% or less for 60 sec. Then the surface was calendered, and additionally, a recording medium 1 was obtained by performing air conditioning in an air conditioning zone at 23° C. and relative humidity of 40 to 60%, and rolling up in a roll shape. The obtained recording medium 1 was then stored in a roll shape at 40° C. for 5 days with being humidified, and subsequently cut into a given size. As a result of measuring by the method described below, the void rate of the recording medium was 55%. Also as a result of measuring by the method described below, the transferred amount at 0.04 seconds of absorption time by Bristow method was 16 ml/m2. According to JIS-Z-8741, the 20-degree specular gloss on the side of an ink absorbing layer provided surface was measured by a digital variable angle glossmeter (supplied from Suga Test Instruments Co., Ltd.), and consequently it was 24%.
[Manufacture of Recording Medium 2]
A recording medium 2 where the transferred amount at 0.04 seconds of absorption time by Bristow method was 8 ml/m2 was made by changing the support 1 to the following support 2 and appropriately changing a constituent ratio (F/B) of silica fine particles (F) to polyvinyl alcohol (B) in the respective ink absorbing layers in the manufacture of the above recording medium 1.
(Manufacture of Support 2)
Base paper was made by preparing a slurry solution containing 1 part of polyacrylamide, 4 parts of ash (talc), 2 parts of cationized starch, 0.5 parts of polyamide epichlorohydrin resin and various addition amount of alkylketene dimer (sizing agent) for 100 parts of wood pulp (LBKP/NBSP=50/50) and using a fourdrinier machine such that a weighing is 170 g/m2. After giving a calendar treatment to this base paper, a low density polyethylene resin with a density of 0.92 containing 7% anatase type titanium oxide and a small amount of a color tone adjuster was coated on a single side of the base paper by a melting extrusion coating method such that a thickness is 28 μm at 320° C. Immediately after the melting extrusion application, various fine particle typing treatments was given to the surface of polyethylene by pressing/cooling a cooling roll having various regular concavoconvex height. Difference of the typing was made by conditioning the density and the concavoconvex height.
Then, a support 2 which was non-absorbable support was made by coating a melted matter where high density polyethylene with a density of 0.96 and low density polyethylene with a density of 0.92 were mixed at 70/30 on an opposite side face similarly by the melting extrusion coating method such that a thickness was 32 μm.
After giving corona discharge to a face side of the layer containing titanium oxide of this support 2, a hardener-containing gelatin undercoating layer was applied at 0.04 g/m2 in terms of a solid content, and on a back face, a styrene/acryl type emulsion containing silica fine particles (matting agent) having a mean particle size of 1 μm and a small amount of a cationic polymeric molecule (conducting agent) was applied such that a dried film thickness was about 0.5 μm.
[Manufacture of Recording Medium 3]
A recording medium 3 where the transferred amount at 0.04 seconds of absorption time by Bristow method was 20 ml/m2 was made by appropriately changing a constituent ratio (F/B) of silica fine particles to polyvinyl alcohol in the respective ink absorbing layers in the manufacture of the above recording medium 2.
[Manufacture of Recording Medium 4]
A recording medium 4 where the transferred amount at 0.04 seconds of absorption time by Bristow method was 11 ml/m2 was made by appropriately changing a constituent ratio (F/B) of silica fine particles to polyvinyl alcohol in the respective ink absorbing layers in the manufacture of the above recording medium 1. The void rate was measured by the method described below, and it was 35%
[Manufacture of Recording Medium 5]
Hydrochloric acid at 1 mol/L was added to the above dispersion to adjust pH to 4, and this was stirred at 95° C. for 2 hours. Then, an aqueous solution of sodium hydroxide at 1 mol/L was added to adjust pH to 10, and further stirred for 8 hours. After stirring, the solution was cooled to room temperature, pH was adjusted to 7 to 8, desalting treatment was given, and further acetic acid was added to deflocculate. After concentrating until a solid content became 17%, an aqueous solution of 9% polyvinyl alcohol (PVA117 supplied from Kuraray Co., Ltd.) was mixed such that a solid content ratio of alumina to polyvinyl alcohol was 10:1 at a weight ratio, and stirred to yield a coating solution.
The coating solution prepared as the above was filtrated with a 20 μl filter capable of collecting. This coating solution was applied onto a supercalendered baryta layer of a substrate (whiteness degree: 89%) by a die coater such that a dried film thickness was 30 g/m2. Note that the substrate was coated with an aqueous boric acid solution and dried in advance in such a way that the boric acid content is 0.5 g/m2. An applying speed at that time was 50 m/min and the drying was performed at a temperature of 150° C. to make a recording medium 5.
The mean particle size of the alumina particles in the recording medium 5 was 30 nm. The transferred amount at 0.04 seconds of absorption time by Bristow method was 22 ml/m2, and the void rate was 55%
[Manufacture of Recording Media 6 to 8]
Recording media 6 to 8 were made as was the case with the manufacture of the recording medium 1, except that the silica particles (mean particle size: about 35 nm) used for the preparation of the respective ink absorbing layer coating solutions were changed to silica particles with mean particle size described in Table 1. The transferred amounts and the void rates of these recording media were as was shown in Table 1.
[Manufacture of Recording Medium 9]
A recording medium 9 was made as was the case with the manufacture of the recording medium 1, except that boric acid and borax used for the preparation of the respective ink absorbing layer coating solutions were removed.
[Manufacture of Recording Media 10 and 11]
Recording media 10 and 11 were made as was the case with the manufacture of the recording medium 1, except that the void rates of the ink absorbing layer were 25% and 75%, respectively by appropriately changing the constituent ratio (F/B) of the silica fine particles to polyvinyl alcohol in the respective ink absorbing layers. The void rates in these recording media were as was shown in Tables 1 and 2.
[Manufacture of Recording Media 12 to 15]
Recording media 12 to 15 were made as was the case with the manufacture of the recording medium 1, except that processing temperatures and linear preasures in calendering just after application and drying were changed appropriately so that the 20-degree specular glosss were 18%, 22%, 42% and 47%, respectively.
<<Preparation of Inks>>
[Preparation of Color Ink Set 1]
(Preparation of Pigment Dispersion)
<Preparation of Yellow Pigment Dispersion 1>
Anthranilic acid (1.5 g) was added to 10 g of a hydrochloric acid solution (6 mol/L), subsequently cooled to 5° C., 1.8 g of sodium nitrite was added, and stirred. Powder of C.I. Pigment Yellow-74 (5 g) was added thereto, a liquid temperature was raised to 80° C. with stirring, heating was continued until production of nitrogen gas stopped, and cooled. Then, acetone was added, and a yellow dispersion 1 was yielded by filtrating pigment particles, washing with ion-exchange water, subsequently adding ion-exchange water, performing respective operations of ion exchange, ultrafiltration and centrifugation and adjusting with ion-exchange water such that a pigment content was 20% by mass.
<Preparation of Magenta Pigment Dispersion 1>
Anthranilic acid (1.5 g) was added to 10 g of a hydrochloric acid solution (6 mol/L), subsequently cooled to 5° C., 1.8 g of sodium nitrite was added, and stirred. Powder of C.I. Pigment Red 122 (5 g) was added thereto, a liquid temperature was raised to 80° C. with stirring, heating was continued until production of nitrogen gas stopped, and cooled. Then, acetone was added, and a magenta dispersion 1 was yielded by filtrating pigment particles, washing with ion-exchange water, subsequently adding ion-exchange water, performing respective operations of ion exchange, ultrafiltration and centrifugation and adjusting with ion-exchange water such that a pigment content was 25% by mass.
<Preparation of Cyan Pigment Dispersion 1>
Anthranilic acid (1.5 g) was added to 10 g of a hydrochloric acid solution (6 mol/L), subsequently cooled to 5° C., 1.8 g of sodium nitrite was added, and stirred. Powder of C.I. Pigment Blue 15:3 (5 g) was added thereto, a liquid temperature was raised to 80° C. with stirring, heating was continued until production of nitrogen gas stopped, and cooled. Then, acetone was added, and a cyan dispersion 1 was yielded by filtrating pigment particles, washing with ion-exchange water, subsequently adding ion-exchange water, performing respective operations of ion exchange, ultrafiltration and centrifugation and adjusting with ion-exchange water such that a pigment content was 25% by mass.
<Preparation of Black Pigment Dispersion 1>
Anthranilic acid (1.5 g) was added to 10 g of a hydrochloric acid solution (6 mol/L), subsequently cooled to 5° C., 1.8 g of sodium nitrite was added, and stirred. Powder of Carbon black (5 g) was added thereto, a liquid temperature was raised to 80° C. with stirring, heating was continued until production of nitrogen gas stopped, and cooled. Then, acetone was added, and a black dispersion 1 was yielded by filtrating pigment particles, washing with ion-exchange water, subsequently adding ion-exchange water, performing respective operations of ion exchange, ultrafiltration and centrifugation and adjusting with ion-exchange water such that a pigment content was 20% by mass.
<Preparation of Blue Pigment Dispersion 1>
Anthranilic acid (1.5 g) was added to 10 g of a hydrochloric acid solution (6 mol/L), subsequently cooled to 5° C., 1.8 g of sodium nitrite was added, and stirred. Powder of C.I. Pigment Violet 23 (5 g) was added thereto, a liquid temperature was raised to 80° C. with stirring, heating was continued until production of nitrogen gas stopped, and cooled. Then, acetone was added, and a blue dispersion 1 was yielded by filtrating pigment particles, washing with ion-exchange water, subsequently adding ion-exchange water, performing respective operations of ion exchange, ultrafiltration and centrifugation and adjusting with ion-exchange water such that a pigment content was 20% by mass.
<Preparation of Red Pigment Dispersion 1>
Anthranilic acid (1.5 g) was added to 10 g of a hydrochloric acid solution (6 mol/L), subsequently cooled to 5° C., 1.8 g of sodium nitrite was added, and stirred. Powder of C.I. Pigment Red 177 (5 g) was added thereto, a liquid temperature was raised to 80° C. with stirring, heating was continued until production of nitrogen gas stopped, and cooled. Then, acetone was added, and a red dispersion 1 was yielded by filtrating pigment particles, washing with ion-exchange water, subsequently adding ion-exchange water, performing respective operations of ion exchange, ultrafiltration and centrifugation and adjusting with ion-exchange water such that a pigment content was 25% by mass.
[Preparation of Color Ink Set]
Using the respective pigment dispersions prepared above, a color ink set 1 composed of a yellow ink 1, a magenta ink 1, a cyan ink 1 and a black ink 1 was prepared.
The surfactant was added such that the surface tension was 38 mN/m and a quantity was adjusted with ion-exchange water such that a total quantity was 100% by mass. A yellow ink 1 was prepared by mixing the above compositions, stirring and filtrating with a 1 μm filter. A mean particle size of pigments in the ink was 131 nm.
The surfactant was added such that the surface tension was 38 mN/m and a quantity was adjusted with ion-exchange water such that a total quantity was 100% by mass. A magenta ink 1 was prepared by mixing the above compositions, stirring and filtrating with a 1 μm filter. A mean particle size of pigments in the ink was 129 nm.
The surfactant was added such that the surface tension was 38 mN/m and a quantity was adjusted with ion-exchange water such that a total quantity was 100% by mass. A cyan ink 1 was prepared by mixing the above compositions, stirring and filtrating with a 1 μm filter. A mean particle size of pigments in the ink was 104 nm.
The surfactant was added such that the surface tension was 38 mN/m and a quantity was adjusted with ion-exchange water such that a total quantity was 100% by mass. A black ink 1 was prepared by mixing the above compositions, stirring and filtrating with a 1 μm filter. A mean particle size of pigments in the ink was 98 nm.
The surfactant was added such that the surface tension was 38 mN/m and a quantity was adjusted with ion-exchange water such that a total quantity was 100% by mass. A blue ink 1 was prepared by mixing the above compositions, stirring and filtrating with a 1 μm filter. A mean particle size of pigments in the ink was 129 nm.
The surfactant was added such that the surface tension was 38 mN/m and a quantity was adjusted with ion-exchange water such that a total quantity was 100% by mass. A red ink 1 was prepared by mixing the above compositions, stirring and filtrating with a 1 μm filter. A mean particle size of pigments in the ink was 123 nm.
[Preparation of Color Ink Set 2]
A color ink set 2 was made up of basic inks (yellow ink 1, magenta ink 1, cyan ink 1 and black ink 1) as is the case with the above preparation of the ink set 1 except the blue ink 1 and the red ink 1 which were special color inks.
[Preparation of Color Ink Set 3]
<Preparation of Green Pigment Dispersion 1>
Anthranilic acid (1.5 g) was added to 10 g of a hydrochloric acid solution (6 mol/L), subsequently cooled to 5° C., 1.8 g of sodium nitrite was added, and stirred. Powder of C.I. Pigment Green 7 (5 g) was added thereto, a liquid temperature was raised to 80° C. with stirring, heating was continued until production of nitrogen gas stopped, and cooled. Then, acetone was added, and a green dispersion 1 was yielded by filtrating pigment particles, washing with ion-exchange water, subsequently adding ion-exchange water, performing respective operations of ion exchange, ultrafiltration and centrifugation and adjusting with ion-exchange water such that a pigment content was 25% by mass.
The surfactant was added such that the surface tension was 38 mN/m and a quantity was adjusted with ion-exchange water such that a total quantity was 100% by mass. A green ink 1 was prepared by mixing the above compositions, stirring and filtrating with a 1 μm filter. A mean particle size of pigments in the ink was 104 nm.
[Preparation of Color Ink Set 3]
A color ink set 3 was made up as is the case the above preparation of the ink set 1 except using of the green ink 1 instead of the blue ink 1 and the red ink 1 which were special color inks.
[Preparation of Ink Set 4]
(Preparation of Pigment Dispersion)
The above additives were mixed and dispersed using a horizontal type bead mill (System Zeta mill supplied from Ashizawa Finetech Ltd.) in which zirconia beads of 0.3 mm were filled at a volume rate of 60% to yield a yellow pigment dispersion 2. A mean particle size of the obtained yellow pigments was 112 nm.
The above additives were mixed and dispersed using a horizontal type bead mill (System Zeta mill supplied from Ashizawa Finetech Ltd.) in which zirconia beads of 0.3 mm were filled at a volume rate of 60% to yield a magenta pigment dispersion 2. A mean particle size of the obtained magenta pigments was 105 nm.
The above additives were mixed and dispersed using a horizontal type bead mill (System Zeta mill supplied from Ashizawa Finetech Ltd.) in which zirconia beads of 0.3 mm were filled at a volume rate of 60% to yield a cyan pigment dispersion 2. A mean particle size of the obtained cyan pigments was 87 nm.
The above additives were mixed and dispersed using a horizontal type bead mill (System Zeta mill supplied from Ashizawa Finetech Ltd.) in which zirconia beads of 0.3 mm were filled at a volume rate of 60% to yield a black pigment dispersion 2. A mean particle size of the obtained black pigments was 75 nm
The above additives were mixed and dispersed using a horizontal type bead mill (System Zeta mill supplied from Ashizawa Finetech Ltd.) in which zirconia beads of 0.3 mm were filled at a volume rate of 60% to yield a blue pigment dispersion 2. A mean particle size of the obtained cyan pigments was 107 nm
The above additives were mixed and dispersed using a horizontal type bead mill (System Zeta mill supplied from Ashizawa Finetech Ltd.) in which zirconia beads of 0.3 mm were filled at a volume rate of 60% to yield a red pigment dispersion 2. A mean particle size of the obtained magenta pigments was 98 nm.
Each polymeric dispersant used for each of the above-described pigment disperions was prepared according to the following method.
[Preparation of Polymeric Dispersant]
<Preparation of Polymeric Dispersant SA-1>
A 3 L four-necked flask was equipped with a three one motor, a thermometer, a nitrogen charging tube and a dropping funnel with a drying tube. With running dried nitrogen gas, tetrahydrofuran (780.0 g) and p-xylene (3.6 g) were charged into this. With stirring, tetrabutylammonium m-benzoate (solution at 1 mol/L, 3.2 ml) was added, and further 1,1-bis(trimethylsiloxy)-2-methylpropene (144.0 g) was added.
Next, tetrabutylammonium m-benzoate (solution at 1 mol/L, 3.2 ml) was dripped from the dropping funnel over 130 min with stirring. After dripping, a mixture of benzyl methacrylate (272.6 g) and trimethylsilyl methacrylate (489.8 g) was dripped from the dropping funnel over 40 min with stirring. After stirring for 30 min, benzyl methacrylate (545.4 g) was dripped from the dropping funnel over 30 min with stirring.
After stirring as it was for 240 min, absolute methanol (216 g) was added and stirred. The dropping funnel was changed to Liebig condenser, an entire vessel was heated, and a fraction of distillate at a boiling point of 55° C. or below was eliminated. Distillation was further continued, at the time point when the boiling point was 76° C., 2-propanol (900 g) was added, and heating and distillation were further continued. Heating was continued until a solvent at a total amount of 1,440 g was run out to yield a solution 1 of an aimed block copolymer (BzMA//BzMA/MAA=5//2.5/5). A part was dried, a molecular weight and an acid value were measured, and they were 1,500 and 70, respectively.
This solution 1 was neutralized by adding N,N-dimethylethanolamine to yield an aimed polymeric dispersant SA-1.
[Preparation of Polymeric Dispersant SA-2]
A polymeric dispersant SA-2 was prepared as was the case with the preparation of the polymeric dispersant SA-1, except that neutralization was performed using potassium hydroxide in place of N,N-dimethylethanolamine.
(Preparation of Pigment Ink Set)
A color ink set 4 was prepared as was the case with the above preparation of the ink set 1, except that the yellow pigment dispersion 2, the magenta pigment dispersion 2, the cyan pigment dispersion 2, the black pigment dispersion 2, the blue pigment dispersion 2 and the red pigment dispersion 2 which were prepared above were used instead of the yellow pigment dispersion 1, the magenta pigment dispersion 1, the cyan pigment dispersion 1, the black pigment dispersion 1, the blue pigment dispersion 1 and the red pigment dispersion 1.
[Preparation of Ink Set 5]
An ink set 5 was prepared as was the case with the above preparation of the ink set 3, except that the cyan ink 2 was changed to the cyan ink 3 prepared according to the following procedure.
(Preparation of Pigment Dispersion)
The above additives were mixed and kneaded 20 times using a three roll mill. The obtained paste was added into ion-exchange water (200 g), stirred thoroughly, and subsequently methylethylketone and water were distilled off using a rotary evaporator such that the solid content was 20% to yield a cyan pigment dispersion 2.
The polymeric dispersant SA-3 used for the above-described cyan pigment disperion 3 was prepared according to the following method.
[Preparation of Polymeric Dispersant SA-3]
A 1 L four-necked flask was equipped with a three one motor, a thermometer, a reflux tube with a nitrogen charging tube and a dropping funnel. With running dried nitrogen gas, the following monomer mixture 1 was charged into this, and a temperature was raised to 65° C.
Next, the following monomer mixture 2 was dripped over 2.5 hours with stirring. Further, a mix solution of azobisdimethylvaleronitrile (0.8 g) and methylethylketone (22 ml) was dripped over 0.5 hours. Azobisdimethylvaleronitrile (0.8 g) was added and further heated and stirred for one hour.
After completion of the reaction, methylethylketone (450 ml) was added to yield a solution of a polymeric dispersant SA-3 with solid content of 50%. A part was dried, a molecular weight and an acid value were measured, and they were 15,000 and 55, respectively.
The surfactant was added such that the surface tension was 38 mN/m and a quantity was adjusted with ion-exchange water such that a total quantity was 100% by mass. A cyan ink 3 was prepared by mixing the above compositions, stirring and filtrating with a 1 μm filter. A mean particle size of pigments in the ink was 98 nm.
[Preparation of Ink Set 6]
(Preparation of Pigment Dispersion)
A yellow pigment dispersion 3, a magenta pigment dispersion 3, a cyan pigment dispersion 4, a black pigment dispersion 3, a blue pigment dispersion 3 and a red pigment dispersion 3 were prepared as is the case with the above preparation of the yellow pigment dispersion 2, the magenta pigment dispersion 2, the cyan pigment dispersion 2, the black pigment dispersion 2, the blue pigment dispersion 2 and the red pigment dispersion 2 except that sodium naphthalenesulfonate was used instead of the polymeric dispersants SA-1 and SA-2.
(Preparation of Color Ink Set]
A color ink set 6 was prepared as was the case with the above preparation of the ink set 1, except that the yellow pigment dispersion 3, the magenta pigment dispersion 3, the cyan pigment dispersion 4, the black pigment dispersion 3, the blue pigment dispersion 3 and the red pigment dispersion 3 which were prepared above were used instead of the yellow pigment dispersion 1, the magenta pigment dispersion 1, the cyan pigment dispersion 1, the black pigment dispersion 1, the blue pigment dispersion 1 and the red pigment dispersion 1.
[Preparation of Ink Sets 7 to 9]
Ink sets 7 to 9 were prepared as was the case with the above preparation of the ink set 1, except that the surface tension of the respective color inks was made 28 mN/m, 48 mN/m, and 55 mN/m, respectively by appropriately conditioning the addition amounts of the polymeric dispersants used for the preparation of the respective pigment dispersions and the surfactant used for the preparation of the ink.
[Preparation of Ink Set 10]
An ink set 10 was prepared as was the case with the above preparation of the ink set 1, except that 5% by mass of ethylene urea was added to each color ink.
<<Measurement of Property Values of Recording Media and Inks>>
[Recording Medium: Measurement of Transferred Amount]
The transferred amount at 0.04 seconds of absorption time by Bristow method was measured in each recording medium made above according to the following method.
As the method of measuring the transferred amount, after leaving the recording medium under an atmosphere at 25° C. and 50% RH for 12 hours or more, the measurement was performed using a Bristow testing machine II type (press mode) which was a liquid dynamic absorbability testing machine supplied from Kumagai Rikikogyo Co., Ltd. The aqueous solution of 2% C.I. acid red 52 was used for the measurement and the transferred amount can be obtained by measuring an area stained with magenta on the recording medium after 0.04 seconds of absorption time.
[Calculation of Void Rate]
The void rate of each recording medium made above was calculated by calculation from a void capacity obtained from Bristow method and a total volume of the micro-porous layer obtained from a dried film thickness.
[Ink Set: Measurement of Surface Tension]
For the surface tension of the ink which composes the ink set, a surface tension value (mN/m) at an ink temperature of 25° C. was measured by a platinum plate method using a tensiometer (CBVP-Z supplied from Kyowa Interface Science Co., Ltd.)
[20-Degree Specular Gloss]
The 20-degree specular gloss on the side of an ink absorbing layer application surface of each recording medium was measured by using the digital variable angle glossmeter (supplied from Suga Test Instruments Co., Ltd.) according to JIS-Z-8741.
<<Printing Methods>>
[Printing Method 1]
Each ink set prepared above was set in an on-demand type inkjet printer with a maximum recording density main scanning 1200× sub scanning 1200 dpi having thermal type heads which arrange two rows with 1 mm distance of nozzle rows and enable to effectively form 256 dots with 1200 dpi pitch by arraying the nozzles in two rows with a shift of 21.2 μm in a sub scanning direction, where a nozzle pore size was 15 μm, a driving frequency was 20 kHz, an amount of an ink droplet was 3 pl, a dot size after jetted on the recording medium was 35 μm, a nozzle number in one row was 128 and a nozzle pitch was 42.3 μm and one-pass printing was performed without using the thinning-out pattern. Here, dpi referred to represents a dot number per 2.54 cm. The image data were extracted by the method described in paragraph numbers [0038] to [0059] of JP-Tokukaihei-2000-32284A.
Relationship between the image data and ink amount to be used in this case is shown in
In
[Printing Method 2]
Each ink set prepared above was set in an on-demand type inkjet printer with a maximum recording density main scanning 1200× sub scanning 1200 dpi having thermal type heads which arrange two rows with 1 mm distance of nozzle rows and enable to effectively form 256 dots with 1200 dpi pitch by arraying nozzles in two rows with a shift of 21.2 μm in a sub scanning direction where a nozzle pore size was 15 μm, a driving frequency was 20 kHz, an amount of an ink droplet was 3 pl, a dot size after jetted on the recording medium was 35 μm, a nozzle number in one row was 128 and a nozzle pitch was 42.3 μm, and the formation of thinned-out image was performed by four-pass printing using the regular thinning-out pattern at a printing acceptable rate of 25%. The masks used are shown in
[Printing Method 3]
Each ink set prepared above was set in an on-demand type inkjet printer with a maximum recording density main scanning 1200× sub scanning 1200 dpi having thermal type heads which arrange two rows with 1 mm distance of nozzle rows and enable to effectively form 256 dots with 1200 dpi pitch by arraying nozzles in two rows with a shift of 21.2 μm in a sub scanning direction where a nozzle pore size was 15 μm, a driving frequency was 20 kHz, an amount of an ink droplet was 3 pl, a dot size after jetted on the recording medium was 35 μm, a nozzle number in one row was 128 and a nozzle pitch was 42.3 μm, and the formation of thinned-out image was performed by four-pass printing using the thinning-out pattern without regularity at a printing acceptable rate of 25%. The masks used are shown in
[Printing Method 4]
A printing method 4 was performed as was the case with the above printing method 3, except that effectively heads of 2400 dpi were made to make printing resolution of the maximum recording density main scanning 2400× sub scanning 2400 dpi by appropriately changing the nozzle pore size to make the ink droplet (about 0.75 pl) such that the dot size after jetted on the recording medium was 15 μm, making the nozzle pitch of one row 21.2 μm and making the shift between the two rows 10.6 μm. The method for extracting image data was along with the printing method 1.
[Printing Method 5]
A printing method 5 was performed as was the case with the above printing method 3, except that the nozzle pore size was appropriately changed such that the ink droplet amount was about 5 pl which corresponded to the dot size of 40 μm after jetted on the recording medium. The image data were precedently conditioned such that an ink adhesive amounts on the medium were nearly identical to those in the printing method 3. The method for extracting image data was along with the printing method 1.
[Printing Method 6]
A printing method 6 was performed as was the case with the above printing method 3, except that the nozzle pore size was appropriately changed such that the ink droplet amount was about 14 pl which corresponded to the dot size of 60 μm after jetted on the recording medium. The image data were precedently conditioned such that an ink adhesive amounts on the medium were nearly identical to those in the printing method 3. The method for extracting image data was along with the printing method 1.
[Printing Method 7]
A printing method 7 was performed as was the case with the above printing method 3, except that the heads were changed to the heads where the nozzle pitch is 15 μm and 256 nozzles were arranged in one row to make the maximum recording density main scanning 850× sub scanning 1690 dpi. The sub scanning resolution corresponded to the head nozzle pitch, and the main scanning resolution was changed depending on this such that the ink adhesive amounts on the medium were nearly identical to those in the printing method 3. The method for extracting image data was along with the printing method 1.
[Printing Method 8]
A printing method 8 was performed as was the case with the above printing method 3, except changing to the maximum recording density main scanning 1570× sub scanning 920 dpi by changing to the nozzle heads where the nozzle groups where 256 nozzles were arranged in one row with a nozzle pitch of 55 μm were separated by 2 cm, two rows for each color were arranged with a shift of 27.5 μm in the subscanning direction, and 512 nozzles per color were arranged. In this case, the nozzle pitch is 55 μm. The sub scanning resolution corresponded to the dot pitch on the medium, and the main scanning resolution was changed depending on this such that the ink adhesive amounts on the medium were nearly identical to those in the printing method 3. The method for extracting image data was along with the printing method 1.
[Printing Method 9]
A printing method 9 was performed as was the case with the above printing method 3, except changing the printing acceptable rate to a repeat of four types of 40%, 40%, 10% and 10% (thus the printing acceptable rate was 40%). The method for extracting image data was along with the printing method 1.
[Printing Method 10]
A printing method 10 was performed as was the case with the above printing method 3, except changing to the maximum recording density main scanning 1200× sub scanning 1200 dpi by changing to the nozzle heads where the nozzle groups where 256 nozzles were arranged in one row with a nozzle pitch of 42.3 μm were separated by 2 cm, two rows for each color were arranged with a shift of 21.2 μm in the subscanning direction, and 512 nozzles per color were arranged. In this case, the nozzle pitch is 42.3 μm. The method for extracting image data was along with the printing method 1.
<<Formation of Inkjet Recording Image>>
Solid image printing of the respective colors of yellow, magenta, cyan, green, red, blue and black was performed by combining the above printing method, the recording medium and the ink set made above as described in Tables 1, 2 and 3 to make the images 1 to 42, and the obtained images were evaluated as follows.
<<Evaluation of Inkjet Recording Image>>
[Evaluation of Gloss Difference]
Images of High Definition Color Digital Standard Image Data “N5 Bicycle” (published in December, 1995) published by Japan Standards Association obtained by combining the above (printing method, recording medium and inks) were visually observed, and the image quality was evaluated according to the following criteria.
A: No difference is felt between the gloss of a clock section with high image density and a color chart section and the gross of a peripheral white background section, and the clock and the color chart are looked evenly without standing out in bold relief from the periphery.
B: Some difference is felt between the gloss of the clock section with high image density and the color chart section and the gross of the peripheral white background section, but the clock and the color chart are looked evenly without standing out in bold relief from the periphery.
C: Difference is felt between glosses of the clock section with high image density and the color chart section and the gross of the peripheral white background section, and further the clock and the color chart somewhat stand out in bold relief, but practically no problem.
D: Large gloss difference is felt between the gloss of the clock section with high image density and the color chart section and the gloss of the peripheral white background section, and further the clock and the color chart stand out in bold relief from the periphery.
[Evaluation of Image Quality]
Images of High Definition Color Digital Standard Image Data “N5 Bicycle” (published in December, 1995) published by Japan Standards Association obtained by combining the above (printing method, recording medium and inks) were visually observed, and the image quality was evaluated according to the following criteria.
A: No occurrence of color turbidity and an image with extremely high definition is obtained.
B: Occurrence of slight color turbidity and an image with high definition is obtained.
C: Occurrence of rather turbid color and an image with rather less distinction, but practically no problem.
D: Obvious color turbidity is observed and an image lacks distinction.
[Evaluation of Depth Feeling]
Images of High Definition Color Digital Standard Image Data “N2 Cafeteria” (published in December, 1995) published by Japan Standards Association obtained by combining the above (printing method, recording medium and inks) were visually observed, and depth feeling was evaluated according to the following criteria.
A: An image from which deep depth feeling is felt and which comes near a silver salt photographic image.
B: An image from which depth feeling is felt and which slightly comes near the silver salt photographic image.
C: An image which slightly lacks the depth feeling but is in the practically acceptable range.
D: An image which obviously lacks the depth feeling and is off from practical use.
[Evaluation of Scratch/Abrasion Resistance]
For the cyan solid image made above, back and forth abrasion was performed 10 times on the surface with an office eraser (MONO supplied from Tombow Pencil Co., Ltd.), and the presence or absence of occurrence of stain on the printed portion was visually determined.
A: No stain on the printed portion is observed
B: Slight stain on the printed portion is observed
C: Stain on the printed portion is clearly observed but no problem in practical use
D: Density reduction is clearly observed on the printed portion
The results obtained above are shown in Table 4.
As is obvious from the results in Table 4, it is shown that the good printing efficiency is obtained, the obtained images are excellent in bronzing resistance, gloss, scratch/abrasion resistance and image uniformity, and the images at high definition are obtained in the inkjet recording method comprising the combination of the recording heads, inks and the recording medium defined in the invention compared to Comparative Examples.
According to the present embodiment, even when the color image is formed by printing the pigment inks on the inkjet recording medium according to the thinning-out pattern without regularity, it is possible to provide the inkjet recording method and the inkjet recording apparatus by which the image at high definition with bronzing resistance and no color turbidity where gloss and scratch/abrasion resistance are improved is obtained.
Number | Date | Country | Kind |
---|---|---|---|
2004-212426 | Jul 2004 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
5102731 | Takimoto et al. | Apr 1992 | A |
5818474 | Takahashi et al. | Oct 1998 | A |
6601939 | Fujita et al. | Aug 2003 | B2 |
6669318 | Ushiroda | Dec 2003 | B2 |
6811837 | Iwasa et al. | Nov 2004 | B2 |
20040092621 | Kataoka et al. | May 2004 | A1 |
Number | Date | Country |
---|---|---|
7-52390 | Feb 1995 | JP |
2002-96461 | Apr 2002 | JP |
2002-144552 | May 2002 | JP |
2003-266913 | Sep 2003 | JP |
Number | Date | Country | |
---|---|---|---|
20060017759 A1 | Jan 2006 | US |