Inorganic composition, process of preparation and method of use

Abstract

A coagulant which is the reaction product of a trivalent metal salt, excluding chromium salts, an acid phosphorous compound and an aluminum hydroxy chloride, and a process for preparing such coagulant. This coagulant may be effectively used to remove suspended solids and various impurities in most water treatment applications.

Description

BACKGROUND OF THE INVENTION

[0002] The present invention relates generally to coagulants for water treatment applications. In general, coagulants are utilized to remove suspended solid particles from aqueous systems.

[0003] Coagulants typically fall into the general category of inorganic (trivalent, divalent metal salts) or organic (water soluble polyelectrolytes). Examples of widely used inorganic coagulants are aluminum sulfate Al2 (SO4)3, aluminum chloride AlCl3, aluminum chlorohydrate Al2 (OH)5Cl, ferric chloride FeCl3, ferric sulfate Fe2 (SO4)3, and calcium chloride. Examples of commonly used water soluble or solution polyelectrolytes are p-DMDAAC (polydimethyl diallyl ammonium chloride) and Epi-DMA polyamine.

[0004] Many inorganic coagulants are compatible with solution cationic polyelectrolytes and can be combined to form stable combinations. In recent years, many different blend formulations of an inorganic coagulant with a high charge solution cationic polyelectrolyte have been patented and of an inorganic coagulant with a high charge solution cationic polyelectrolyte have been patented and marketed. An example of an inorganic coagulant/polymer blend might be: 5 parts of a standard 28° Baumé AlCl3 solution mixed-with 1 part of Epi-DMA polyamine. More examples, limits, and ranges are explained in U.S. Pat. Nos. 4,746,457, 4,800,039, and 5,035,808 to Calgon Corporation, and further in U.S. Pat. Nos. 2,862,880, 3,285,849, 3,472,767, 3,489,681, 3,617,569, 4,137,165, 4,450,092, 4,582,627, 4,610,801, and 4,655,934, the disclosures of which are incorporated herein by reference in their entirety. Normally, these compositions are physical blends of an inorganic trivalent metal salt solution and a water soluble polymer solution, which is a simple mixture of the components where both components retain their original identity or chemical composition, but provide utility and advantages-such as:

[0005] 1. a synergy of adding the inorganic and polymeric coagulants simultaneously as a blend; and

[0006] 2. ease of use—using one product instead of two (thereby eliminating feed systems, equipment, and handling).

[0007] Wastewater treatment systems typically require the use of trivalent metal salts, a polymer or a combination of both in the coagulation process. Both ferric coagulants such as FeCl3 blends and aluminum coagulants such as alum or Al2(OH)5Cl blends are often used for these processes. Both the ferric and aluminum coagulants provide different desirable properties. However, these coagulants are normally incompatible with each other.

[0008] It was thus desired in the art to develop a single coagulant which would combine the desirable properties of ferric and aluminum coagulants.

SUMMARY OF THE INVENTION

[0009] The present invention comprises a composition that is the reaction product of a trivalent metal salt, excluding chromium salts, an acid phosphorous compound and an aluminum hydroxy chloride, and a process for preparing the same.

[0010] The method of use according to the present invention comprises adding this reaction product in an effective amount to the solution to be treated. The composition of the present invention is an excellent and unique coagulant for most water treatment applications.

[0011] As used herein, the phrase “effective amount” refers to that amount of the claimed reaction product which is helpful to at least partially treat (coagulate) the impurities in the wastewater or system being treated.

BRIEF DESCRIPTION OF THE DRAWINGS

[0012] The above composition will become more apparent when reference is made to the following detailed description, taken in conjunction with the appended figures, in which:

[0013] FIG. 1 is an Al-27 NMR spectrum of monoaluminum phosphate;

[0014] FIG. 2 is an Al-27 NMR spectrum of aluminum chlorohydrate; and

[0015] FIG. 3 is an Al-27 NMR spectrum of the reaction mixture of iron(III) chloride, monoaluminum phosphate and aluminum chlorohydrate.

[0016] These figures are discussed in detail below.

DETAILED DESCRIPTION OF THE INVENTION

[0017] The present invention was discovered when the inventors were attempting to obtain the desirable properties of FeCl3 blends and Al(OH)5Cl blends by mixing these two inorganics and then combining the resultant mixture with a cationic polyelectolyte and other ingredients. However, they discovered that mixtures of trivalent metal salts such as FeCl3 and aluminum hydroxy chlorides such as Al2(OH)5Cl are incompatible and all attempts to combine such mixtures ended in a gelled/solidified reaction product which was not usable.

[0018] It was unexpectedly discovered that FeCl3 solution and Al2(OH)5Cl solution can be stabilized and combined through the use of a third ingredient, monoaluminum phosphate. The inventors have discovered a method of combining these previously incompatible coagulants and creating a stable, complex ion coordination compound that exhibits increased efficacy as a coagulant for industrial and municipal water treatment.

[0019] A composition, and process for preparing the same, has been discovered by the inventors comprising the reaction product of a trivalent metal salt other than chrominum salts, an aluminum hydroxy chloride, and an acid phosphorous compound which acts as a stabilizing compound.

[0020] The preferred process of preparing the present invention is the addition of the acid phosphorous compound (stabilizer) to the trivalent metal salt, soon followed by the addition of the aluminum hydroxy chloride. A small exotherm results from the addition of the acid phosphorous compound (stabilizer) to the trivalent metal salt. A larger and more vigorous exotherm results from the subsequent addition of the aluminum hydroxy chloride. Based upon this exotherm, as well as color changes and partial precipitation (and re-dissolution), it is believed that the components are reacting and a new compound is formed. Although the order of addition of these compounds to form the new compound may be altered, the above order of addition is preferred. If the trivalent metal salt and the aluminum hydroxy chloride are combined without the acid phosphorous compound, a slurry will be formed which will generally solidify in less than an hour. In order to create a stable final product, if this order of addition is utilized, the acid phosphorous compound should be added to this mixture prior to solidification, or preferably within 40 minutes. However, reconstitution after solidification is possible by the addition of the acid phosphorous compound. The least preferred order of addition is when the acid phosphorous compound is alone first mixed with the aluminum hydroxy chloride, because a solid mass will be formed almost instantaneously. However, this solid mass can be reconstituted by the addition of FeCl3. For these reasons, the above noted order of addition is preferred.

[0021] This new resultant compound is stable and appears to be different in composition from the compounds used in the preparation process. The conclusion that a new compound is formed is supported by FIGS. 1-3 which illustrate Al-27 NMR spectra for a compound formed from the reaction of the volume formula 10 FeCl3 (about 40% active raw material in water), 3 monoaluminum phosphate (Al(H2PO4)3.XH2O) (about 50 wt % in water), and 5 Al(OH)5Cl (about 50 wt % in water). Commerciably available FeCl3 solution is 38 to 42% active raw material in water. Commercially available monoaluminum phosphate and Al(OH)5Cl are both 50 wt % in water, plus or minus 1 to 2%.

[0022] The combination of a peak's shape and position yield structural information in NMR spectroscopy. The position is based upon a relative marker to a selected standard material and is measured in ppm shifts in frequency. The standard reference material used in these spectra was aluminum oxide (Al2O3) at 0 ppm. The shape of the peak (singlet, doublet, etc.) is dependent upon the nuclei's interaction with neighboring atoms. The combination of peak position and shape is a function of the nuclei's environment, and thus, its structure.

[0023] FIG. 1 is an Al-27 NMR spectrum of monoaluminum phosphate. This spectrum shows a single band centered at ca. −77.7 ppm relative to the standard. The width of the peak is indicative of the structure in solution.

[0024] FIG. 2 is an Al-27 NMR spectrum of aluminum chlorohydrate (Al2(OH)5Cl). This spectrum shows a very broad set of peaks centered at ca. −57.8 and −68.6 ppm with the former peak being the much stronger band. This spectrum shows two peaks which are overlapped. There are also two significantly smaller peaks on either side of these two major bands which are probably minor impurities. This material is known to be polymeric in nature. In general, the higher the molecular weight of a material the more broad the peaks become.

[0025] FIG. 3 is an Al-27 NMR spectrum of the reaction mixture of the present invention. This spectrum shows the product of the claimed reaction mixture of iron(III) chloride, monoaluminum phosphate and aluminum chlorohydrate according to the current reaction, using the concentrations and parts per volume of these three compounds in the preferred embodiment. In FIG. 3, the aluminum NMR peak is a very much sharper singlet and is shifted to a position at ca. −26.2 ppm relative to the standard. These changes indicate that a reaction has taken place, that the two component raw materials (iron(III) chloride and aluminum chlorohydrate) are most likely limiting reagents in this reaction, and that the structure of the final product is simpler than the aluminum chlorohydrate precursor. The aluminum exists in a single type of chemical environment, hence the rationale for the proposed structure of a new compound.

[0026] The molecular formula of this preferred embodiment, which is the subject of FIG. 3 is:

Iron(III) salt of [Aln(OH)a(H2PO4)b(Cl)c(H2O)d]3n−a−b−c

[0027] where a+b+c>3n

[0028] This new composition is the product of a Lewis/Acid Base type reaction in which a stable, complex ion coordination compound is formed as follows:

[0029] A+B→“intermediate” (4° C. temperature rise observed) “intermediate”+C→new compound (20° C. temperature rise observed)

where:                           (% Active Basis)
A = Iron Chloride                17.5%-20%
B = Phosphoric Acid, Aluminum Salt (3:1) 8%-10%
C = Aluminum Chloride, Basic     11.0%-13%

[0030] A typical structure of this new compound of the preferred embodiment is represented below where the H2O, Cl, OH and H2PO4 ligands can vary in number, as well as in their position on the metal ion in the coordination complex. The nature of the bond between each ligand and the central metal atom is coordinate covalent. 1

[0031] The preferred embodiment of the present invention composition, by volume, is:

[0032] 10 FeCl3 (aqueous solution about 40% active raw material in water)

[0033] 3 Monoaluminum phosphate (Al(H2PO4)3.XH2O) (about 50 wt % in water)

[0034] 5 Al2(OH)5Cl (about 50 wt % in water)

[0035] 1 CaCl2 (30% solution)

[0036] 2 Ca-250 (Epi-DMA polyamine) (50 wt % in water)

[0037] Multiple experiments involving the modification of the volume of the above ingredients in the preferred embodiment have been performed. It has been determined that although the above noted volumes provide the preferred combination, these ratios may be altered while still maintaining a stable reaction product and the desired coagulation properties to varying degrees. It has been determined that (using the concentrations set forth above) the volume of the FeCl3 component may be varied from 3 to 30 parts, the monoaluminum phosphate may be varied from 0.5 to 10 parts, and the Al2(OH)5Cl may be increased to as high as 20 parts. However, the upper limit of the Al2(OH)5Cl volume appears to be 20 because precipitation begins to occur at this level. Although the quality of the resultant compounds varied proportionally with the deviation from the preferred embodiment, the resultant compounds provided stable reaction produces. Further tests have performed varying the combinations of different trivalent metal salts, acid phosphorous compounds and aluminum hydroxy chlorides, as well as the volumes of each such component. The Example below demonstrates the results or selected tests on volume and component variations.

[0038] The volumetric ratios set forth above for components of the preferred embodiment are also applicable to the various claimed combinations of the other trivalent metal salts, acid phosphorous compounds and aluminum hydroxy chlorides. It is known by one skilled in the art that these various compounds can be obtained in varying concentrations. In order to obtain the most preferred ratio of components of various substitute components of varying concentration, one must obtain the same ratio of molar amounts of ferric, phosphate or phosphite and aluminum as that of the preferred embodiment above. For example, phosphoric acid is commercially available in about 85 wt % in water as compared to about 50 wt % of monoaluminum phosphate. Thus a component of different concentration can be used if the correct molar ratio is obtained.

[0039] It appears that the calcium chloride and CA-250 components are present only as a physical blend with the compound which is the result of the reaction. The resulting blend of the reaction product and the CaCl2 and CA-250 (Epi-DMA polyamine) is a “sweep-floc” which functions as a coagulant and a flocculent and, as noted above, could be useful in many water treatment processes. Other standard additives can also be mixed with the reaction product.

[0040] In place of the CA-250 (Epi-DMA polyamine), p-DMDAAC may be utilized under certain circumstances in the physical blend with the subject reaction product. The p-DMDAAC may be utilized when the trivalent metal salt FeCl3 (in the preferred embodiment) is diluted by 10 to 40% with water prior to the addition of the acid phosphorous compound and the aluminum hydroxy chloride. In order to utilize p-DMDAAC with the already prepared reaction product of the preferred embodiment, the entire reaction product must be diluted by 10 to 40% with water prior to the addition of p-DMDAAC. If phosphoric acid is substituted for the monoaluminum phosphate of the preferred embodiment, dilution of either FeCl3 or the entire reaction product should be by 10 to 80% with water, otherwise precipitation will occur.

[0041] Tests have also been performed involving the variance of the amounts of CaCl2 and the amount of the CA-250 (Epi-DMA polyamine). The volumes of these compounds have been varied both together and on an independent basis. The variance of these two components appears to have a negligible effect on the formulation.

[0042] As noted above, although the preferred embodiment utilizes FeCl3 as the trivalent metal salt, monoaluminum phosphate as the acid phosphorous compound, and Al2(OH)5Cl as the aluminum hydroxy chloride, substitutions may be made for each of these compounds while still resulting in a stable, effective reaction product.

[0043] The preferred trivalent metal salts are those of Group 8. The more preferred trivalent metal salts are metal halides. However, the most preferred trivalent metal salts are ferric, such as FeCl3, Fe2(SO4)3, FeBr3 and Fe(NO3)3. Additionally, blends of the foregoing may be utilized. Ferric halide is more preferred, while ferric chloride is most preferred. The preferred anions of the salt are chloride and halide. Sulfate is a less preferred anion of the salt. Nitrate may also be employed as an anion for the salt.

[0044] The preferred acid phosphorous compounds of the present invention are selected from the group consisting of acid phosphites (including phosphorous acid), acid phosphates (including phosphoric acid), and phosphonic acid. Acid phosphorous compounds having the following formula may be utilized:

MnHxPOq

[0045] Where:

[0046] M=cation such as a metal or ammonium

[0047] n=0 to 2

[0048] x=1 to 3

[0049] q=3 or 4

[0050] For example, the following acid phosphorous compounds may be utilized: monoaluminum phosphate (Al(H2PO4)3.XH2O), phosphoric acid (H3PO4), phosphorous acid (H3PO3), sodium phosphate monobasic (NaH2PO4), sodium phosphate dibasic (Na2HPO4), HEDP ((CH3C(OH) (PO3H2)), vinyl phosphonic acid (H2C═CHP(O) (OH)2), dimethyl phosphite ((CH3O2)P2(O)H), (NH4)2HPO4, NH4H2PO4, potassium phosphate monobasic (KH2PO4), and K2HPO4. The more preferred acid phosphorous compounds are those which are non-organic due to their lower cost.

[0051] The aluminum hydroxy chloride compounds which may be used in the formulation of the composition of the present invention are those of the general formula Al2(OH)yClz, where y=0.1 to 5 and z=1 to 5.9 The more preferred are those where y=1 to 5 and z=1 to 5. The most preferred are those where y=1.8 to 5 and z=1 to 4.2.

[0052] In preparing the claimed reaction product, AlCl3 can be utilized as the trivalent metal salt and combined with Al2(OH)5Cl and a stabilizer (acid phosphorous compound). An exotherm will occur and a reaction product will be formed. AlCl3 can also be utilized as a substitute for the aluminum hydroxy chloride component and combined with FeCl3 and a stabilizer. However, in this circumstance, a reaction product is not formed and a blend is achieved. Nevertheless, this blend exhibits good coagulation properties.

[0053] Experiments have also been performed where the CaCl2 compound has been substituted with MgCl2 and BaCl2 without resulting serious detriment to the performance of the resultant mixture with the reaction product. The CA-250 (Epi-DMA polyamine) may also be substituted with other Epi-DMA polyamines. CA-250 is preferred because of its relative low to medium molecular weight. CA-250 is a commercial polyamine product sold by Calgon Corporation.

[0054] This resultant new compound has been demonstrated to be an excellent and unique coagulant for most water treatment applications including E-coat waste treatment, water-borne paint waste coagulation, oily waste and solvent-borne paint detackification. It is also exhibits utility in general wastewater treatment, municipal wastewater treatment, metals removal from water, paper making waste water, water containing chemical compounds, water containing organic compounds, water containing biological compounds, poultry processing waste, ink containing solutions, raw water clarification (such as municipal drinking water and industrial purification), oil/water separation, water containing suspended solids, color removal (colored solutions), waste clay slurry, coal waste, mineral processing water, oily waste, water containing suspended solids, water containing paint solids and others. The resultant new compound has also been demonstrated to remove metals from water, including heavy metals such as lead and nickel. E-coat waste is the wastewater generated from electrolytic primer coating.

[0055] The method of using the new compound for coagulation in these various systems consists of adding the new compound to the system in an effective amount.

[0056] This new compound also may be utilized for enhanced coagulation. Enhanced coagulation is the reduction of total organic contaminants (TOC). The reduction of organic contaminants in drinking water is desirable to minimize formation of chlorinated hydrocarbons formed during the chlorination process.

[0057] The most preferred method for producing the claimed reaction product entails the following steps:

[0058] 1. At ambient temperature, add 3 parts by volume monoaluminum phosphate solution (about 50 wt % in water) to 10 parts by volume FeCl3 aqueous solution (about 40% active raw material in water). During the addition of the monoaluminum phosphate solution to the FeCl3 solution, some reaction will take place. There may be some partial precipitations and color changes—and striations in the solutions. However, when the reaction is complete, everything is in solution and it appears stable.

[0059] 2. Next, the 5 parts by volume aluminum chlorohydrate solution (about 50 wt % in water) is added to the mixture of FeCl3 and monoaluminum phosphate (and further reaction takes place). The resultant solution goes through a violent exotherm. The solution becomes hot, and the solution becomes homogeneous. When the solution cools down, it remains compatible and homogeneous.

[0060] 3. Preferably, 1 part by volume CaCl2 (30% solution) and 2 parts per volume of a polymer, such as CA-250 (Epi-DMA polyamine 50 wt %) are then added. The CaCl2 is added for hardness and the polymer to enhance coagulation and to begin flocculation (to help form the pin floc). There appears to be no further reaction when the CaCl2 and the polymer are added.

[0061] As noted above, it will be apparent to one skilled in the art that this process may be duplicated utilizing the other trivalent metal salts, acid phosphorous compounds, and aluminum hydroxy chlorides herein claimed, if the same noted molar ratios are utilized.

EXAMPLE

[0062] The following example is included to further describe and demonstrate the invention in greater detail. This example is not intended to limit the scope of the invention in any way. This example, and the tables included therein, demonstrate the performance of the claimed invention, including the preferred embodiment and other claimed reaction products formed from various Group 8 trivalent metal salts, acid phosphorous compounds and aluminum hydroxy chloride components, on the treatment of E-coat waste. Also included are entries illustrating the effectiveness of treating E-coat waste with only a trivalent metal salt and only an aluminum hydroxy compound.

[0063] The following test procedure was used to compile the results contained in the following tables.

[0064] Dilution of Product:

[0065] 1. 2.5 gms of the selected coagulant and/or reaction product was weighed and placed into a B-cup.

[0066] 2. 7.5 gms of deionized water was placed into the same B-cup and mixed until uniform.

[0067] Test Procedure:

[0068] 1. 495 mls of deionized water was added to a glass jar (a Graduated cylinder was used).

[0069] 2. The glass jar was placed on a gang stirrer and mixed at 100 rpm.

[0070] 3. 5 mls of neat E-coat waste was added to the water.

[0071] 4. 0.6 mls of the selected coagulant and/or reaction product solution (300 ppm) was added to the glass jar.

[0072] 5. The solution was mixed at 100 rpm for 15 seconds.

[0073] 6. The pH was lowered to 2.9 using stock H2SO4 (10 gm H2SO4+190 gm DiH2O).

[0074] 7. The number of drops of stock H2SO4 used to lower the pH was recorded.

[0075] 8. The solution was mixed at 100 rpm for 15 seconds.

[0076] 9. The pH was increased to 8.5 using a soda ash solution (20 gm soda ash +80 gm DiH2O).

[0077] 10. The number of drops of soda ash solution used to increase the pH was recorded.

[0078] 11. The solution was mixed at 100 rpm for 15 seconds.

[0079] 12. 2 mls of flocculent—Pol EZ 8736 or Pol EZ 7736 [0.5% product] which are commercially available high molecular weight polymers sold by Calgon Corporation—was placed in a syringe and added by the following method:

[0080] a) the tip of the syringe was placed below the surface of the solution at approximately the top of the vortex;

[0081] b) the flocculent was added and timed for exactly 10 seconds;

[0082] c) after the ten second period ended, the agitation was turned down to 50-60 rpm;

[0083] d) the floc was allowed to develop for 30 seconds; and

[0084] e) the agitation was then turned off.

[0085] 13. The floc was then allowed to settle for 10 minutes.

[0086] 14. The floc size and the appearance of the solution was then recorded (visual inspection only).

[0087] 15. 20 mls of the solution was removed with a syringe for a turbidity reading.

[0088] 16. The turbidity reading in NTU (nephelometric turbidity units) was recorded.

[0089] 17. The agitation was then turned on and the motion speed was slowly increased to ≦50 rpm.

[0090] 18. The solution was mixed for 30 seconds and the percentage of detackification was recorded.

[0091] 19. The motor speed was then increased to 100 rpm and the solution was mixed for 30 seconds.

[0092] 20. The percentage of detackification was then recorded (if detackification of 100% was recorded at 50 rpm, no reading was necessary at 100 rpm and therefore was not taken).

[0093] Unless otherwise noted, this procedure was utilized to obtain the results set forth in the tables below. Flocculation refers to the settling of suspended solid particles in the solution. Turbidity as used herein is defined as the cloudiness of the solution casued by suspended particles.

Table 1

[0094] This table illustrates the performance of the preferred embodiment, 10 FeCl3, 3 (Al(H2PO4)3.XH2O) and 5 Al2(OH)5Cl, 1 CaCl2 and 2 Ca-250, in the concentrations set forth above, as 3930-93. In 3982-84A, the (Al(H2PO4)3.XH2O) was substituted with HEDP in the same molar ratio. In 3982-86A and 3982-87, the (Al(H2PO4)3.XH2O) has been likewise substituted with vinyl phosphonic acid and dimethyl phosphite, respectively.

TABLE 1
	3930-93		3982-86A
	Preferred	3982-84A	Vinyl Phosphonic	3982-87
Description	embodiment	HEDP	acid	Dimethyl Phosphite
Product Dilution	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/
(Deionized water/product)	2.5 gms	2.5 gms	2.5 gms	2.5 gms
Appearance	medium amber	med-dk amber	yellow	very pale blue
Use Concentration	0.60 mls/	0.60 mls/	0.60 mls/	0.06 mls/
(mls/ppm)	300 ppm	300 ppm	300 ppm	300 ppm
E-coat Composition	495 mls/	495 mls/	495 mls/	495 mls/
	5 mls	5 mls	5 mls	5 mls
pH to 2.9	30 drops	29 drops	34 drops	31 drops
pH to 8.5	45 drops	50 drops	52 drops	40 drops
Floc size/appearance	large/hazy	med fluffy/	large/lt. haze	med-lg/sl haze
		sl haze
Turbidity	93.3	54.2	39.6	72.4
Detackification	good	fair	fair-good	bad
50 rpm:	100%	50&	65%	0%
100 rpm:		100%	100%	60%

Table 2

[0095] This table likewise illustrates how the performance of the preferred embodiment is effected by changes in the type and amount of the acid phosphorous compound utilized. The composition of the preferred embodiment remained constant for each trial, except: in 3982-79A, a lower volume of (Al(H2PO4)3.XH2O) (“MAP”) was utilized; in 3982-79B, a lower volume of H3PO4 was substituted for the MAP; in 3982-79C, H3PO4 was substituted for the MAP in the same volume; and in 3982-80G, NaH2PO4 was substituted for the MAP in the same volume.

TABLE 2
	3930-93
	Preferred	3982-79A	3982-79B	3982-79C	3982-80A	3982-80G
Description	Embodiment	Low MAP	Low H3PO4	Std H3PO4	Std H3PO3	Std NAH2PO4
Product Dilution	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms
Deionized
water/product
Appearance	good/med amber	good/dk amber	good/dk amber	good/yellow	good/dk amber	good/dk amber
Use Concentation	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm
(mls/ppm)
E-coat Composition	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls
Deionized water/
e-coat waste
pH to 2.9	27 drops	25 drops	24 drops	25 drops	23 drops	24 drops
pH to 8.5	60 drops	60 drops	60 drops	60 drops	60 drops	60 drops
Floc	very lg/sl haze	lg. tight/very sl.	very lg./hazy	lg. loose/sl.	med. loose/almost	lg. loose/sl. haze
size/appearance		haz		haze	clear
Turbidity	90/88	67	72	68	31	44.7
Detackification	Good	Good	Good	Good	Good	Good
50 rpm:	90%	100%	100%	100%	90%	100%
100 rpm:	100%				100%

Table 3

[0096] Tables 3 and 4 illustrate the effect of altering the use concentration of the preferred embodiment. The numbers included under the heading “Description” refer to the volumes 10 FeCl3, 3 (Al(H2PO4)3.XH2O), 5 Al2(OH5)Cl, 1 Cacl2 and 2 Ca-250, of the component concentrations of each set forth above.

TABLE 3
	#1	#2	#3	#4	#5
	Preferred	Preferred	Preferred	Preferred	Preferred	#6
	Embodiment	Embodiment	Embodiment	Embodiment	Embodiment	Preferred Embodiment
Description	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2
Product	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms
Dilution
Deionized
water/
product
Appearance	amber	amber	amber	amber	amber	amber
Use	0.0 mls/0 ppm	0.04 mls/20 ppm	0.10 mls/50 ppm	0.20 mls/100 ppm	1.00 mls/500 ppm	2.00 mls/1000 ppm
Concentation
(mls/ppm)
E-coat	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls
Composition
Deionized
water/
e-coat waste
pH to 2.9	n/a	n/a	n/a	n/a	n/a	n/a
pH to 8.5	n/a	n/a	n/a	n/a	n/a	n/a
Floc	tacky	tacky	tacky	tacky	hard floc/clear	spongy floc
size/appearance
Turbidity	58.5	49.9	48.2	34.1	14.8	32.9
Detackification	Bad	Bad	Bad	Bad	Good	Good
100 rpm:	0%	0%	0%	0%	100%	100%

[0097]

TABLE 4
	#1	#2	#3	#4	#5	#6
	Preferred	Preferred	Preferred	Preferred	Preferred	Preferred
	Embodiment	Embodiment	Embodiment	Embodiment	Embodiment	Embodiment
Description	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2	10 + 3 + 5 + 1 + 2
Product Dilution	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms
Deionized
water/product
Appearance	amber	amber	amber	amber	amber	amber
Use Concentation	0.40 mls/200 ppm	0.60 mls/300 ppm	0.80 mls/400 ppm	1.00 mls/500 ppm	1.20 mls/600 ppm	1.40 mls/700 ppm
(mls/ppm)
E-coat Composition	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls
Deionized water/
e-coat waste
pH to 2.9	n/a	n/a	n/a	n/a	n/a	n/a
pH to 8.5	n/a	n/a	n/a	n/a	n/a	n/a
Floc	sl tacky	sl tacky	sl tacky	fluffy	fluffy	fluffy
size/appearance
Turbidity	80.6	62.1	63.9	41.6	39.0	39.9
Detackification	Fair	Good	Good	Good	Good	Good
50 rpm:	>50%	95%	100%	100%	100%	100%

Table 5

[0098] Table 5 provides a comparative example of the testing of the preferred embodiment 3920-93, compared to the performance of the individual components thereof. Nos. 1 through 5 are demonstrative of the use of the individual component alone noted after the heading “Description”.

TABLE 5
	3930-93			#3
	Preferred	#1	#2	50% Al2OH5Cl	#4	#5
Description	Embodiment	40% FeCl3 sol.	50% MAP sol.	sol.	30% CaCl2 sol.	50% CA-250 sol.
Product Dilution	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms
Deionized
water/product
Appearance	med amber	yellow	water	water	water	water white/clear
			white/clear	white/clear	white/clear
Use Concentation	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm
(mls/ppm)
E-coat	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls
Composition
Deionized water/
e-coat waste
pH to 2.9	41 drops	38 drops	44 drops	46 drops	50 drops	50 drops
pH to 8.5	64 drops	64 drops	66 drops	68 drops	69 drops	70 drops
Floc size/appearance	lg-vig/slight	extra lg/very	lg/hazy	fine/very hazy	very fine/turbid	jelly/turbid
	haze	hazy
Turbidity	76	146	138	181	275	296
Detackification	Good	Bad	Very Bad 0%	Fair	None	None
50 rpm:	100%	0%	20%	20%	0%	0%
100 rpm:	100%	40%		75%	0%	0%

Table 6

[0099] Table 6 demonstrates the effect of varying the volume composition of components of the preferred embodiment and the effect of the complete omission of the Al2OH5Cl component. The ratios noted in this table utilize the concentrations of each component set forth above.

TABLE 6
						#6
		#2	#3	#4	#5	Fe3 + MAP +
	#1	FeCl3 + MAP +	Fe3 + MAP +	Fe3 + MAP +	Fe3 + MAP +	Al2OH5Cl +
Description	FeCl3 + MAP	Al2OH5Cl	Al2OH5Cl	Al2OH5Cl	Al2OH5Cl + CaCl2	CaCl2 + CA250
Ratio (mls)	10 + 3	10 + 3 + 5	15 + 3 + 5	10 + 3 + 10	10 + 3 + 5 + 1	10 + 3 + 5 + 1 + 2
Product Dilution	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms	7.5 gms/2.5 gms
Deionized
water/product
Appearance	yellow	amber	amber	very dark amber	amber	amber
Use Concentation	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm	0.60 mls/300 ppm
(mls/ppm)
E-coat	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls	495 mls/5 mls
Composition
Deionized water/
e-coat waste
pH to 2.9	34 drops	38 drops	36 drops	40 drops	37 drops	37 drops
pH to 8.5	60 drops	61 drops	63 drops	64 drops	61 drops	62 drops
Floc	lg. fluffy/hazy	lg. sl. fluffy/	lg. fluffy/hazy	lg. fluffy/hazy	large/hazy	large/hazy
size/appearance		very hazy
Turbidity	144	95	103	139	99.3	80
Detackification	Very bad	Good	Fair	Bad	Good	Good
50 rpm:	0%	75%	50%	20%	100%	100%
100 rpm:	20%	95%	75%	50%

Table 7

[0100] Table 7 sets forth the results of tests performed utilizing various aluminum hydroxy chlorides as substitutes for Al2OH5Cl in the preferred embodiment. These aluminum hydroxy chlorides are:

Aluminum
hydroxy		%	%	%
chloride	FORMULA	BASICITY	SOLIDS	Al2O3
A	Al2(OH)5Cl	83	50	23.5
Preferred
embodiment
B	Al2(OH)3Cl2(SO4)0.5	50	30	10
C	Al2(OH)1.3Cl4.2	30	33	8
D	Al2(OH)3Cl2(SO4)0.5	70	50	15
E	Al2(OH)3Cl3	50	33	10
F	Ferrous Chloride	—	28	—
	(FeCl2)
G	Al2(OH)2Cl4	30	40	—
H	Al2(OH)3Cl3	55	40	—
I	Al2(OH)3SO4SiO3	−35	−35	—

[0101]

TABLE 7
	Preferred
Description	Embodiment	C	D	E	H	G	B	I	F
Product	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/
Dilution	2.5 gms	2.5 gms	2.5 gms	2.5 gms	2.5 gms	2.5 gms	2.5 gms	2.5 gms	2.5 gms
Deionized
water/
product
Appearance	lt amber	lt amber	lt. amber	yellow	yellow	yellow	yellow	yellow	yellow
Use	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/
Concentation	300 ppm	300 ppm	300 ppm	300 ppm	300 ppm	300 ppm	300 ppm	300 ppm	300 ppm
(mls/ppm)
E-coat	495 mls/	495 mls/	495 mls/	495 mls/	495 mls/	495 mls/	495 mls/	495 mls/	495 mls/
Composition	5 mls	5 mls	5 mls	5 mls	5 mls	5 mls	5 mls	5 mls	5 mls
Deionized
water/
e-coat
waste
pH to 2.9	46 drops	37 drops	41 drops	38 drops	39 drops	39 drops	38 drops	38 drops	35 drops
pH to 8.5	105 drops	105 drops	131 drops	120 drops	106 drops	92 drops	100 drops	106 drops	106 drops
Floc	lg.	lg.	lg.	lg.	lg.	lg.	lg.	lg.	lg.
size/appear-	fluffy/	fluffy/	fluffy/	fluffy/	fluffy/	fluffy/	fluffy/	fluffy/	fluffy/
ance	clear	sl haze	sl haze	sl haze	sl haze	sl haze	sl haze	sl haze	sl haze
Turbidity	18.5	35.7	29.0	34.9	52.4	35.3	33.4	36.6	53.9
Detackifica-	good	good	good	good	fair-good	fair-good	fair-good	good	fair-good
tion
50 rpm:	90%-95%	100%	90%	85%-90%	80-85%	80-85%	80-85%	85%	80-85%
100 rpm:	100%		100%	100%	100%	100%	100%	100%	100%

Table 8

[0102] Table 8 illustrates the performance of the preferred embodiment compared to the performance when substitutions of various components are made in the same volume and concentration. The second column shows the effect of the substitution of FeBr3 for FeCl3. 4023-8A, 4023-8C and 4023-8E show the results of the substitution of the noted phosphorous compound for MAP. 4023-13A and 4023-13A show the results of the substitution of the noted component for CaCl2.

TABLE 8
	Preferred
Description	Embodiment	FeBr3	NH4HPO4	KH2PO4	Na2HPO4	MgCl2	BaCl2
Product Dilution	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/	7.5 gms/
Deionized water/	2.5 gms	2.5 gms	2.5 gms	2.5 gms	2.5 gms	2.5 gms	2.5 gms
product
Appearance	med lt	very lt	reddish	dk	dk	med lt	med lt amber
	amber	amber		reddish	reddish	amber
Use Concentation	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/	0.60 mls/
(mls/ppm)	300 ppm	300 ppm	300 ppm	300 ppm	300 ppm	300 ppm	300 ppm
E-coat Composition	495 mls/	495 mls/	495 mls/	495 mls/	495 mls/	495 mls/	495 mls/
Deionized water/	5 mls	5 mls	5 mls	5 mls	5 mls	5 mls	5 mls
e-coat waste
pH to 2.9	38 drops	31 drops	42 drops	40 drops	49 drops	40 drops	48 drops
pH to 8.5	94 drops	25 drops	94 drops	103 drops	105 drops	92 drops	107 drops
Floc	lg.	lg.	lg.	lg.	lg.	med	med fluffy/
size/appearance	fluffy/	fluffy/	fluffy/	fluffy/	fluffy/	fluffy/	hazy
	clear	sl cloudy	sl haze	hazy	hazy	clear
Turbidity	30	70	23.8	29.3	34.6	28.8	40.1
Detackification	good	good	good	fair	fair	good	fair-good
50 rpm:
100 rpm:	80%	85%	90%	50%	75%	90%	80%
	100%	99%	100%	100%	100%	100%	100%

Claims

1. A composition comprising the reaction product of a trivalent metal salt other than chromium salts, an acid phosphorous compound, and an aluminum hydroxy chloride.

2. The composition of claim 1 wherein the trivalent metal salt is a Group 8 trivalent metal salt.

3. The composition of claim 2 wherein the trivalent metal salt is a ferric metal salt.

4. The composition of claim 3 wherein the trivalent metal salt is a ferric halide.

5. The composition of claim 3 wherein the trivalent metal salt is selected from the group consisting of FeCl3, Fe(SO4)3, FeBr3 and Fe(NO3)3, and mixtures thereof.

6. The composition of claim 2 wherein the trivalent metal salt is a blend of one or more Group 8 trivalent metal salts.

7. The composition of claim 2 wherein the acid phosphorous compound is selected from the group consisting of acid phosphites, acid phosphates and phosphonic acid.

8. The composition of claim 7 wherein the acid phosphite is phosphorous acid and the acid phosphate is phosphoric acid.

9. The composition of claim 7 wherein the acid phosphorous compound is selected from the group of (Al(H2PO4)3.XH2O), H3PO4, H3PO3, NaH2PO4, Na2HPO4, CH3C(OH) (PO3H2) H2C═CHP(O) (OH)2, (CH3O2)P2(O)H, (NH4)2HPO4, NH4H2PO4, K2HPO4 and KH2PO4.

10. The composition of claim 7 wherein the acid phosphorous compound is of the formula MnHxPOq, where M=a cation such as a metal or ammonium, n=0 to 2, x=1 to 3, and q=3 or 4.

11. The composition of claim 2 wherein the aluminum hydroxy chloride is of the chemical formula Al2(OH)yClz where y=0.1 to 5 and z=1 to 5.9.

12. The composition of claim 11 wherein y=1.8 to 5 and z=1 to 4.2.

13. The composition of claim 2 wherein the trivalent metal salt is selected from the group of FeCl3, Fe(SO4)3, FeBr3 and Fe(NO3)3, the acid phosphorous compound is selected from the group (Al(H2PO4)3.XH2O), H3PO4, H3PO3, NaH2PO4, Na2HPO4, (NH)2HPO4, NH4H2PO4, K2HPO4 and KH2PO4, and the aluminum hydroxy chloride is of the chemical formula Al2(OH)yClz where y=1.8 to 5 and z=1 to 4.2.

14. The composition of claim 13 wherein the trivalent metal salt is FeCl3, the acid phosphorous compound is (Al(H2PO4)3.XH2O), and the aluminum hydroxy chloride is Al2(OH)5Cl.

15. The composition of claim 14 wherein the volume of FeCl3 (about 40% active raw material in water) is 3 to 30 parts, the volume of (Al(H2PO4)3.XH2O) (about 50 wt % in water) is 0.5 to 10 parts, and the volume of Al2(OH)5Cl (about 50 wt % in water) is 5 to 20 parts.

16. The composition of claim 15 wherein the volume of FeCl3 is 10 parts, the volume of (Al(H2PO4)3.XH2O) is 3 parts, and the volume of Al2(OH)5Cl is 5 parts.

17. The composition of claim 2 wherein AlCl3 is utilized as the trivalent metal salt.

18. A composition having an aluminum-27 NMR peak at ca. −26.2 ppm relative to aluminum oxide at 0 ppm.

19. The composition of claim 18 wherein the composition is reaction product of iron(III) chloride, monoaluminum phosphate and aluminum chlorohydrate.

20. A blend comprising the product of AlCl3, FeCl3 and an acid phosphorous compound.

21. The blend of claim 20 wherein the acid phosphorous compound is (Al(H2PO4)3.XH2O).

22. The composition of claim 2 further comprising the addition of CaCl2 and EPI-DMA polyamine.

23. The composition of claim 2 further comprising the addition of p-DMDAAC.

24. A composition comprising the reaction product of a trivalent metal salt other than chromium salts, an acid phosphorous compound, and an aluminum hydroxy chloride, where: a. the trivalent metal salt is one or more of the group of FeCl3, Fe(SO4)3, FeBr3 and Fe(NO)3; b. the acid phosphorous compound is selected from the group consisting of (Al(H2PO4)3.XH2O), H3PO4, H3PO3, NaH2PO4 Na2HPO4, CH3C(OH) (PO3H2), H2C═CHP(O) (OH)2, (CH3O2)P2(O)H, (NH4)2HPO4, NH4H2PO4, K2HPO4 and KH2PO4; and c. the aluminum hydroxy chloride is one of the formula Al2(OH)yClz where y=1.8 to 5 and z=1 to 4.2.

25. The composition of claim 24 wherein the trivalent metal salt is FeCl3, the acid phosphorous compound is (Al(H2PO4)3.XH2O), and the aluminum hydroxy chloride is Al2(OH)5Cl.

26. The composition of claim 23 wherein the trivalent metal salt is FeCl3 (about 40% active raw material in water) in a volume of 10 parts, the acid phosphorous compound is (Al(H2PO4)3.XH2O) (about 50 wt % in water) in a volume of 3 parts, the aluminum hydroxy chloride is Al2(OH)5Cl (about 50 wt % in water) in a volume of 5 parts, and: (a) the FeCl3 is diluted by 10 to 40% prior to the preparation of the composition and the subsequent addition of p-DMDAAC; or (b) the composition is diluted by 10 to 40% prior to the addition of the p-DMDAAC.

27. The composition of claim 23 wherein the trivalent metal salt is FeCl3 (about 40% active raw material in water) in a volume of 10 parts, the acid phosphorous compound is phosphoric acid (about 85 wt % in water) in a volume of 3 parts, the aluminum hydroxy chloride is Al2(OH)5Cl (about 50 wt % in water) in a volume of 5 parts, and: (a) the FeCl3 is diluted by 10 to 80% prior to the preparation of the composition and the subsequent addition of the p-DMDAAC; or (b) the composition is diluted by 10 to 80% prior to the addition of the p-DMDAAC.

28. A process for the production of a reaction product comprising blending an aqueous solution of a Group 8 trivalent metal salt, an acid phosphorous compound and an aluminum hydroxy chloride.

29. The process of claim 28 wherein the trivalent metal salt is first blended with the acid phosphorous compound, and the aluminum hydroxy chloride is subsequently added thereto.

30. The process of claim 28 wherein the trivalent metal salt is first blended with the aluminum hydroxy chloride, and the acid phosphorous compound is subsequently added thereto.

31. The process of claim 28 wherein the trivalent metal salt is selected from the group consisting of FeCl3, Fe(SO4)3, FeBr3, and Fe(NO3) and mixtures thereof.

32. The process of claim 28 wherein the acid phosphorous compound is selected from the group consisting of (Al(H2PO4)3.XH2O), H3PO4, H3PO3, NaH2PO4, Na2HPO4, CH3C(OH) (PO3H2), H2C═CHP(O) (OH)2, (CH3O2)P2(O)H, (NH4)2HPO4, NH4HPO4, NH4H2PO4, K2HPO4 and KH2PO4.

33. The process of claim 28 wherein the aluminum hydroxy chloride is one of the formula Al2(OH)yClz where y=0.1 to 5 and z=1 to 5.9.

34. The process of claim 33 wherein y=1.8 to 5 and z=1 to 4.2.

35. The process of claim 28 further comprising the addition of CaCl2 and Epi-DMA polyamine.

36. The process of claim 28 further comprising the addition of p-DMDAAC.

37. The process of claim 36 wherein the trivalent metal salt is FeCl3 (about 40% active raw material in water) in a volume of 10 parts, and the acid phosphorous compound is (Al(H2PO4)3.XH2O) (about 50 wt % in water) in a volume of 3 parts, the aluminum hydroxy chloride is Al2(OH)5Cl (about 50 wt % in water) in a volume of 5 parts, and: (a) the FeCl3 is diluted by 10 to 40% prior to the preparation of the composition and the subsequent addition of p-DMDAAC; or (b) the composition is diluted by 10 to 40% prior to the addition of the p-DMDAAC.

38. The process of claim 36 wherein the trivalent metal salt is FeCl3 (about 40% active raw material in water) in a volume of 10 parts, and the acid phosphorous compound is phosphoric acid (about 85 wt % in water) in a volume of 3 parts, the aluminum hydroxy chloride is Al2(OH)5Cl (about 50 wt % in water) in a volume of 5 parts, and: (a) the FeCl3 is diluted by 10 to 80% prior to the preparation of the composition and the subsequent addition of the p-DMDAAC; or (b) the composition is diluted by 10 to 80% prior to the addition of the p-DMDAAC.

39. A composition of matter comprising the product produced according to the process of claim 28.

40. A process for treating a solution comprising contacting the solution with an effective amount of the composition of claim 2.

41. A process for treating a solution comprising contacting the solution with an effective amount of the product produced according to the process of claim 28.

42. The process of claim 40 wherein the solution is selected from the group consisting of general wastewater, municipal wastewater, wastewater containing metals, papermaking wastewater, water containing organic compounds, water containing chemical compounds, water containing biological compounds, poultry processing waste, ink containing solutions, raw surface water, oil/water mixtures, colored solutions, coal waste, mineral processing water, oily waste, raw municipal drinking water, water containing suspended solids, water containing paint solids, electrolytic primer coating wastewater and industrial wastewater.

43. The process of claim 41 wherein the solution is selected from the group consisting of general wastewater, municipal wastewater, wastewater containing metals, papermaking wastewater, water containing organic compounds, water containing chemical compounds, water containing biological compounds, poultry processing waste, ink containing solutions, raw surface water, oil/water mixtures, colored solutions, coal waste, mineral processing water, oily waste, raw municipal drinking water, water containing suspended solids, water containing paint solids, electrolytic primer coating wastewater and industrial wastewater.

44. The process of claim 40 wherein the product is utilized in enhanced coagulation to reduce at least a portion of the total organic contaminants.

45. The process of claim 41 wherein the product is utilized in enhanced coagulation to reduce at least a portion of the total organic contaminants.