Patent Grant
9708214
A high temperature resistant inorganic fiber that is useful as a thermal, electrical, or acoustical insulating material, and which has a use temperature of 1260° C. and greater is provided. The high temperature resistant inorganic fiber is easily manufacturable, exhibits low shrinkage after exposure to the use temperature, retains good mechanical strength after continued exposure to the use temperature, and exhibits low biopersistence in physiological fluids.
The insulation material industry has determined that it is desirable to utilize fibers in thermal, electrical and acoustical insulating applications, which are not durable in physiological fluids, that is, fiber compositions which exhibit a low biopersistence in physiological fluids.
While candidate materials have been proposed, the use temperature limit of these materials have not been high enough to accommodate many of the applications to which high temperature resistant fibers are applied. For example, such low biopersistence fibers exhibit high shrinkage at use temperatures and/or reduced mechanical strength when exposed to use temperatures ranging from 1000° C. to 1400° C. as compared to the performance of refractory ceramic fibers.
The high temperature resistant, low biopersistence fibers should exhibit minimal shrinkage at expected exposure temperatures, and after prolonged or continuous exposure to the expected use temperatures, in order to provide effective thermal protection to the article being insulated.
In addition to temperature resistance as expressed by shrinkage characteristics that are important in fibers that are used in insulation, it is also required that the low biopersistence fibers have mechanical strength characteristics during and following exposure to the expected use or service temperature, that will permit the fiber to maintain its structural integrity and insulating characteristics in use.
One characteristic of the mechanical integrity of a fiber is its after service friability. The more friable a fiber, that is, the more easily it is crushed or crumbled to a powder, the less mechanical integrity it possesses. In general, inorganic fibers that exhibit both high temperature resistance and low biopersistence in physiological fluids also exhibit a high degree of after service friability. This results in a brittle fiber lacking the strength or mechanical integrity after exposure to the service temperature to be able to provide the necessary structure to accomplish its insulating purpose. Other measures of mechanical integrity of fibers include compressive strength and compression recovery.
It is desirable to produce an improved inorganic fiber composition that is readily manufacturable from a fiberizable melt of desired ingredients, which exhibits low biopersistence in physiological fluids, low shrinkage during and after exposure to use temperatures of 1260° C. and greater, such as 1400° C. and greater, and, which exhibits low brittleness after exposure to the expected use temperatures, and which maintains mechanical integrity after exposure to use temperatures of 1260° C. and greater, such as 1400° C. and greater.
Provided is a high temperature resistant alkaline-earth silicate fiber exhibiting improved thermal stability when the inorganic fiber is exposed to elevated temperatures of 1000° C. to 1500° C. It has been found that the inclusion of suitable amount of lithium oxide to an alkaline-earth silicate inorganic fiber reduces fiber shrinkage and enhances mechanical strength beyond that of alkaline earth silicate fibers without the presence of the lithium oxide addition. The fiber exhibits low biopersistence in physiological solutions, reduced linear shrinkage, and improved mechanical strength after exposure to expected use temperatures.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, and up to about 1 weight percent lithium oxide.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, calcia, and up to about 1 weight percent lithium oxide.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, calcia, and up to about 1 weight percent lithium oxide.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, lithium oxide and a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, calcia, lithium oxide, and a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, calcia, lithium oxide, and a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, lithium oxide, and alumina as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, calcia, lithium oxide, and alumina as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, calcia, lithium oxide, and alumina as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, lithium oxide, and boria as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, calcia, lithium oxide, and boria as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, calcia, lithium oxide, and boria as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, lithium oxide, and a mixture of alumina and boria as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, calcia, lithium oxide, and a mixture of alumina and boria as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, calcia, lithium oxide, and mixture of alumina and boria as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, zirconia, lithium oxide, and a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, zirconia, lithium oxide, and alumina as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, zirconia, lithium oxide, and boria as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain embodiments, the inorganic fiber comprises the fiberization product of silica, magnesia, zirconia, lithium oxide, and a mixture of alumina and boria as a viscosity modifier. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and lithium oxide. Lithium oxide may be included in an amount up to about 1 weight percent.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.3 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.25 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.2 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.175 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.15 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.1 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.075 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.05 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.01 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.005 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide, and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier it present is may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide, and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.175 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, a greater than 0 to about 0.25 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.175 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide and from 0 to about 11 weight percent zirconia.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.175 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide, from 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and up to about 1 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.3 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.25 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.2 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.175 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.15 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.1 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.075 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.01 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.005 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present is may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.175 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.075 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.175 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and up to about 1 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.3 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.25 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.2 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.15 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.1 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.075 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.05 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.01 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.005 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and up to about 1 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.3 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.25 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.2 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.15 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.1 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.075 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.05 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.01 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.005 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and up to about 1 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.3 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.25 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.2 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.15 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.1 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.075 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.05 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.01 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.005 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide, and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, and up to about 1 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.3 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.25 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.2 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.15 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.1 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.075 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.05 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.3 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.25 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.2 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.15 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.1 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.075 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.05 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present is may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.43 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.3 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.3 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.25 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.25 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.2 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.2 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.15 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.15 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.1 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.1 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.075 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.075 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.05 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.05 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, greater than 0 to about 0.01 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 81 weight percent silica, about 19 to about 22 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 79 to about 81 weight percent silica, about 19 to about 21 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia, and a viscosity modifier. According to certain illustrative embodiments, the inorganic fiber comprises the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, greater than 0 to about 0.005 weight percent lithium oxide, greater than 0 to about 11 weight percent zirconia and a viscosity modifier. The viscosity modifier can be selected from alumina, boria, and mixtures of alumina and boria. When a viscosity modifier is present it may include greater than 0 to about 2 weight percent alumina, or greater than 0 to about 1 weight percent boria, or a mixture of greater than 0 to about 2 weight percent alumina and greater than 0 to about 1 weight percent boria.
According to further illustrative embodiments, the inorganic fiber may comprise the fiberization product of silica in any of the range disclosed herein, magnesia in any of the ranges disclosed herein, optionally calcia in any of the ranges disclosed herein, optionally zirconia in any of the range disclosed herein, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to further illustrative embodiments, the inorganic fiber may comprise the fiberization product from about 65 to about 86 weight percent silica, from about 14 to about 35 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to further illustrative embodiments, the inorganic fiber may comprise the fiberization product from about 70 to about 80 weight percent silica, from about 20 to about 30 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to further illustrative embodiments, the inorganic fiber may comprise the fiberization product from about 75 to about 80 weight percent silica, from about 20 to about 25 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to further illustrative embodiments, the inorganic fiber may comprise the fiberization product from about 76 to about 80 weight percent silica, from about 20 to about 24 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to further illustrative embodiments, the inorganic fiber may comprise the fiberization product from about 77 to about 80 weight percent silica, from about 20 to about 23 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to further illustrative embodiments, the inorganic fiber may comprise the fiberization product from about 78 to about 80 weight percent silica, from about 20 to about 22 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to further illustrative embodiments, the inorganic fiber may comprise the fiberization product from about 78 to about 81 weight percent silica, from about 19 to about 22 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to further illustrative embodiments, the inorganic fiber may comprise the fiberization product from about 79 to about 81 weight percent silica, from about 19 to about 21 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to any of the above illustrative embodiments, the inorganic fiber contains 1 weight percent or less calcia. According to any of the above illustrative embodiments, the inorganic fiber contains 0.5 weight percent or less calcia. According to any of the above illustrative embodiments, the inorganic fiber contains 0.3 weight percent or less calcia.
According to any of the above embodiments, provided is a high temperature resistant inorganic fiber which exhibits a linear shrinkage of 5% or less when exposed a use temperature of 1260° C. and greater for 24 hours, and which maintains mechanical integrity after exposure to the use temperature, and which exhibits low biopersistence in physiological fluids.
According to any of the above embodiments, provided is a high temperature resistant inorganic fiber which exhibits a linear shrinkage of 5% or less when exposed a use temperature of 1260° C. and greater for 168 hours, and which maintains mechanical integrity after exposure to the use temperature, and which exhibits low biopersistence in physiological fluids.
According to any of the above embodiments, the high temperature resistant inorganic fiber exhibits a linear shrinkage of 4% or less when exposed a use temperature of 1260° C. and greater for 24 hours, maintains mechanical integrity after exposure to the use temperature, and which exhibits low biopersistence in physiological fluids.
According to any of the above embodiments, the high temperature resistant inorganic fiber exhibits a linear shrinkage of 4% or less when exposed a use temperature of 1260° C. and greater for 168 hours, maintains mechanical integrity after exposure to the use temperature, and which exhibits low biopersistence in physiological fluids.
According to any of the above embodiments, provided is a high temperature resistant inorganic fiber which exhibits a linear shrinkage of 5% or less when exposed a use temperature of 1400° C. or greater for 24 horns, and which maintains mechanical integrity after exposure to the use temperature, and which exhibits low biopersistence in physiological fluids.
According to any of the above embodiments, provided is a high temperature resistant inorganic fiber which exhibits a linear shrinkage of 5% or less when exposed a use temperature of 1400° C. or greater for 168, and which maintains mechanical integrity after exposure to the use temperature, and which exhibits low biopersistence in physiological fluids.
According to any of the above embodiments, the high temperature resistant inorganic fiber exhibits a linear shrinkage of 4% or less when exposed a use temperature of 1400° C. or greater for 24 hours, and which maintains mechanical integrity after exposure to the use temperature, and exhibit low biopersistence in physiological fluids.
According to any of the above embodiments, the high temperature resistant inorganic fiber exhibits a linear shrinkage of 4% or less when exposed a use temperature of 1400° C. or greater for 168 hours, and which maintains mechanical integrity after exposure to the use temperature, and exhibit low biopersistence in physiological fluids.
According to any of the above embodiments, provided is a method for preparing a high temperature resistant inorganic fiber having a use temperature of 1260° C. or greater, which maintains mechanical integrity after exposure to the use temperature, and which exhibits low biopersistence in physiological fluids.
According to any of the above embodiments, provided is a method for preparing a high temperature resistant inorganic fiber having a use temperature of 1400° C. or greater, which maintains mechanical integrity after exposure to the use temperature, and which exhibits low biopersistence in physiological fluids.
The method for preparing the fiber comprises forming a melt with ingredients comprising either (i) silica and magnesia, or (ii) silica and calcia, or (iii) silica, magnesia and calcia, lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
The method for preparing the fiber comprises forming a melt with ingredients comprising either (i) silica and magnesia, or (ii) silica and calcia, or (iii) silica, magnesia and calcia, and up to about 1 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt. The method for preparing the fiber comprises forming a melt with ingredients comprising either (i) silica and magnesia, or (ii) silica and calcia, or (iii) silica, magnesia and calcia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 65 to about 86 weight percent silica, from about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 70 to about 80 weight percent silica, from about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 75 to about 80 weight percent silica, from about 20 to about 25 weight percent magnesia, and up to about 1 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt. According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 75 to about 80 weight percent silica, from about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 76 to about 80 weight percent silica, from about 20 to about 24 weight percent magnesia, and up to about 1 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt. According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 76 to about 80 weight percent silica, from about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 77 to about 80 weight percent silica, from about 20 to about 23 weight percent magnesia, and up to about 1 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt. According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 77 to about 80 weight percent silica, from about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 78 to about 80 weight percent silica, from about 20 to about 22 weight percent magnesia, and up to about 1 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt. According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 78 to about 80 weight percent silica, from about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising silica in any of the range disclosed herein, magnesia in any of the ranges disclosed herein, optionally calcia in any of the ranges disclosed herein, optionally zirconia in any of the range disclosed herein, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 65 to about 86 weight percent silica, from about 14 to about 35 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 70 to about 80 weight percent silica, from about 20 to about 30 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 75 to about 80 weight percent silica, from about 20 to about 25 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 76 to about 80 weight percent silica, from about 20 to about 24 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 77 to about 80 weight percent silica, from about 20 to about 23 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 78 to about 80 weight percent silica, from about 20 to about 22 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 78 to about 81 weight percent silica, from about 19 to about 22 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method for preparing the fiber comprises forming a melt with ingredients comprising from about 79 to about 81 weight percent silica, from about 19 to about 21 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
Without limitation, the viscosity modifier that is added to the melt of ingredients to prepare the inorganic fiber may be selected from alumina, boria, and mixtures of alumina and boria. The viscosity modifier is included in the melt of ingredients in an amount effective render the melt fiberizable.
Also provided is a method of thermally insulating an article with fibrous insulation prepared from a plurality of the presently disclosed high temperature resistant low biopersistent inorganic fibers of any of the above disclosed illustrative embodiments. The method includes disposing on, in, near or around the article to be thermally insulated, a thermal insulation material comprising a plurality of the inorganic fibers comprising the fiberization product of either (i) silica and magnesia, or (ii) silica and calcia, or (iii) silica, magnesia and calcium, and greater than 0 to about 1 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier, wherein the fiberization product comprises any one of the above-disclosed fiberization products.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 65 to about 86 weight percent silica, from about 14 to about 36 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 70 to about 80 weight percent silica, from about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 75 to about 80 weight percent silica, from about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 76 to about 80 weight percent silica, from about 20 to about 24 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 77 to about 80 weight percent silica, from about 20 to about 23 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 78 to about 80 weight percent silica, from about 20 to about 22 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide, optionally greater than 0 to 11 weight percent zirconia, and optionally a viscosity modifier; and producing fibers from the melt.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of silica in any of the range disclosed herein, magnesia in any of the ranges disclosed herein, optionally calcia in any of the ranges disclosed herein, optionally zirconia in any of the range disclosed herein, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 65 to about 86 weight percent silica, from about 14 to about 35 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 70 to about 80 weight percent silica, from about 20 to about 30 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 75 to about 80 weight percent silica, from about 20 to about 25 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 76 to about 80 weight percent silica, from about 20 to about 24 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 77 to about 80 weight percent silica, from about 20 to about 23 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 78 to about 80 weight percent silica, from about 20 to about 22 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 78 to about 81 weight percent silica, from about 19 to about 22 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
According to certain illustrative embodiments, the method of thermally insulating an article with fibrous insulation comprising a plurality fibers comprising the fiberization product of from about 79 to about 81 weight percent silica, from about 19 to about 21 weight percent magnesia, optionally calcia in any of the ranges disclosed herein, optionally from greater than 0 to about 11 weight percent zirconia, optionally a viscosity modifier in any of the ranges disclosed herein, and lithium oxide in any one of the following ranges: (i) greater than 0 to about 0.05 weight percent, (ii) greater than 0 to about 0.045 weight percent, (iii) about 0.002 to about 0.04 weight percent, (iv) from about 0.005 to about 0.04 weight percent, (v) from about 0.01 to about 0.04 weight percent, (vi) from about 0.02 to about 0.04 weight percent, (vii) from about 0.03 to about 0.04 weight percent, or (viii) from about 0.035 to about 0.04 weight percent.
Also provided is an inorganic fiber containing article comprising at least one of bulk fiber, blankets, blocks, boards, caulking compositions, cement compositions, coatings, felts, mats, moldable compositions, modules, papers, pumpable compositions, putty compositions, sheets, tamping mixtures, vacuum cast shapes, vacuum cast forms, or woven textiles (for example, braids, cloths, fabrics, ropes, tapes, sleeving, wicking).
In order for a glass composition to be a viable candidate for producing a satisfactory high temperature resistant fiber product, the fiber to be produced must be manufacturable, sufficiently soluble (ie, having low biopersistence) in physiological fluids, and capable of surviving high temperatures with minimal shrinkage and minimal loss of mechanical integrity during exposure to the high service temperatures.
The present inorganic fiber exhibits low biopersistence in physiological fluids. By “low biopersistence” in physiological fluids, it is meant that the inorganic fiber at least partially dissolves in such fluids, such as simulated lung fluid, during in vitro tests.
Biopersistence may be tested by measuring the rate at which mass is lost from the fiber (ng/cm2-hr) under conditions which simulate the temperature and chemical conditions found in the human lung. This test consists of exposing approximately 0.1 g of de-shotted fiber to 50 ml of simulated lung fluid (SLF) for 6 hours. The entire test system is maintained at 37° C., to simulate the temperature of the human body.
After the SLF has been exposed to the fiber, it is collected and analyzed for glass constituents using Inductively Coupled Plasma Spectroscopy. A “blank” SLF sample is also measured and used to correct for elements present in the SLF. Once this data has been obtained, it is possible to calculate the rate at which the fiber has lost mass over the time interval of the study. The fibers are significantly less biopersistent than normal refractory ceramic fiber in simulated lung fluid.
“Viscosity” refers to the ability of a glass melt to resist flow or shear stress. The viscosity-temperature relationship is critical in determining whether it is possible to fiberize a given glass composition. An optimum viscosity curve would have a low viscosity (5-50 poise) at the fiberization temperature and would gradually increase as the temperature decreased. If the melt is not sufficiently viscous (i.e. too thin) at the fiberization temperature, the result is a short, thin fiber, with a high proportion of unfiberized material (shot). If the melt is too viscous at the fiberization temperature, the resulting fiber will be extremely coarse (high diameter) and short.
Viscosity is dependent upon melt chemistry, which is also affected by elements or compounds that act as viscosity modifiers. Viscosity modifiers permit fibers to be blown or spun from the fiber melt. It is desirable, however, that such viscosity modifiers, either by type or amount, do not adversely impact the solubility, shrink resistance, or mechanical strength of the blown or spun fiber.
One approach to testing whether a fiber of a defined composition can be readily manufactured at an acceptable quality level is to determine whether the viscosity curve of the experimental chemistry matches that of a known product which can be easily fiberized. Viscosity-temperature profiles may be measured on a viscometer, capable of operating at elevated temperatures. In addition, an adequate viscosity profile may be inferred by routine experimentation, examining the quality of fiber (index, diameter, length) produced. The shape of the viscosity vs. temperature curve for a glass composition is representative of the ease with which a melt will fiberize and thus, of the quality of the resulting fiber (affecting, for example, the fiber's shot content, fiber diameter, and fiber length). Glasses generally have low viscosity at high temperatures. As temperature decreases, the viscosity increases. The value of the viscosity at a given temperature will vary as a function of the composition, as will the overall steepness of the viscosity vs. temperature curve. The present fiber melt composition possesses a viscosity profile of a readily manufacturable fiber.
Linear shrinkage of an inorganic fiber is a good measure of a fiber's dimensional stability at high temperatures or of its performance at a particular continuous service or use temperature. Fibers are tested for shrinkage by forming them into a mat and needle punching the mat together into a blanket of approximately 4-10 pounds per cubic foot density and a thickness of about 1 inch. Such pads are cut into 3 inch×5 inch pieces and platinum pins are inserted into the face of the material. The separation distance of these pins is then carefully measured and recorded. The pad is then placed into a furnace, ramped to temperature and held at the temperature for a fixed period of time. After heating, the pin separation is again measured to determine the linear shrinkage that pad has experienced.
In one such test, the length and width of the fiber pieces were carefully measured, and the pad was placed in a furnace and brought to a temperature of 1260 or 1400° C. for 24 or 168 hours. After cooling, the lateral dimensions were measured and the linear shrinkage was determined by comparing “before” and “after” measurements. If the fiber is available in blanket form, measurements may be made directly on the blanket without the need to form a pad.
Mechanical integrity is also an important property since the fiber must support its own weight in any application and must also be able to resist abrasion due to moving air or gas. Indications of fiber integrity and mechanical strength are provided by visual and tactile observations, as well as mechanical measurement of these properties of after-service temperature exposed fibers. The ability of the fiber to maintain its integrity after exposure to the use temperature may also be measured mechanically by testing for compression strength and compression recovery. These tests measure, respectively, how easily the pad may be deformed and the amount of resiliency (or compression recovery) the pad exhibits after a compression of 50%. Visual and tactile observations indicate that the present inorganic fiber remains intact and maintains its form after exposure to a use temperature of at least 1260 or 1400° C.
According to certain embodiments, the low shrinkage, high temperature resistant inorganic fiber comprises the fiberization product of a melt containing magnesia and silica as the primary constituents. The low biopersistent inorganic fibers are made by standard glass and ceramic fiber manufacturing methods. Raw materials, such as silica, any suitable source of magnesia such as enstatite, forsterite, magnesia, magnesite, calcined magnesite, magnesium zirconate, periclase, steatite, or talc. Lithium may be included in the fiber melt as LiCO3. If zirconia is included in the fiber melt, any suitable source of zirconia such as baddeleyite, magnesium zirconate, zircon or zirconia, are introduced into a suitable furnace where they are melted and blown using a fiberization nozzle, or spun, either in a batch or a continuous mode.
An inorganic fiber comprising the fiberization product of magnesia and silica is referred to as a “magnesium-silicate” fiber. An inorganic fiber comprising the fiberization product of calcia, magnesia and silica is referred to as a “calcia-magnesium-silicate”fiber. An inorganic fiber comprising the fiberization product of calcia and silica is referred to as a “calcium-silicate” fiber. The low shrinkage, high temperature resistant inorganic fiber also comprises and a lithium oxide-bearing raw material component as part of the fiber melt chemistry.
According to certain embodiments, the present inorganic fiber has an average diameter of greater than 2 microns. According to certain embodiments, the present inorganic fiber has an average diameter of greater than 2 microns to about 7.5 microns. According to certain embodiments, the present inorganic fiber has an average diameter of about 3.5 to about 7 microns.
According to any one of the illustrative fiberization products disclosed above, the inorganic fiber exhibits low shrinkage and good mechanical strength at temperatures from about 1100° C. to about 1500° C. and low biopersistence.
According to any one of the illustrative fiberization products disclosed above, the inorganic fiber present exhibits low shrinkage and good mechanical strength at temperatures from about 1260° C. to about 1500° C. and low biopersistence.
According to any one of the illustrative fiberization products disclosed above, the inorganic fiber exhibits low shrinkage and good mechanical strength at temperatures from about 1260° C. to about 1400° C. and low biopersistence.
According to any one of the illustrative fiberization products disclosed above, the inorganic fiber exhibits low shrinkage and good mechanical strength at temperatures from about 1400° C. to about 1500° C. and low biopersistence.
The magnesium-silicate fibers containing intended additions of lithium oxide exhibit a linear shrinkage after exposure to a service temperature of 1400° C. for 24 hours of 10 percent or less. In other embodiments, the magnesium-silicate fibers containing intended additions of lithium oxide exhibit a linear shrinkage after exposure to a service temperature of 1400° C. for 24 hours of 5 percent or less. In other embodiments, the magnesium-silicate fibers containing intended additions of lithium oxide a linear shrinkage after exposure to a service temperature of 1400° C. for 24 hours of 4 percent or less.
The inorganic fibers containing intended additions of lithium oxide are useful for thermal insulating applications at continuous service or operating temperatures of at least 1260° C. and greater. According to certain embodiments, the fibers containing lithium oxide are useful for thermal insulating applications at continuous service or operating temperatures of at least 1400° C. and it has been found that the magnesium-silicate fibers containing the lithium oxide additions do not melt until they are exposed to a temperature of 1500° C. or greater.
The inorganic fibers may be prepared by fiber blowing or fiber spinning techniques. A suitable fiber blowing technique includes the steps of mixing the starting raw materials containing magnesia, silica, lithium oxide, viscosity modifier, and optional zirconia together to form a material mixture of ingredients, introducing the material mixture of ingredients into a suitable vessel or container, melting the material mixture of ingredients for discharge through a suitable nozzle, and blowing a high pressure gas onto the discharged flow of molten material mixture of ingredients to form the fibers.
A suitable fiber spinning technique includes the steps of mixing the starting raw materials together to form a material mixture of ingredients, introducing the material mixture of ingredients into a suitable vessel or container, melting the material mixture of ingredients for discharge through a suitable nozzle onto spinning wheels. The molten stream then cascades over the wheels, coating the wheels and being thrown off through centripetal forces, thereby forming fibers.
In some embodiments, the fiber is produced from a melt of raw materials by subjecting the molten stream to a jet of high pressure/high velocity air or by pouring the melt onto rapidly spinning wheels and spinning fiber centrifugally. The lithium oxide is provided as an additive to the melt, and a suitable source of the lithium oxide raw material is simply added at the proper amount to the raw materials being melted.
The addition of lithium oxide as a component of the raw materials which are fiberized results in a decrease of linear shrinkage of the resulting fiber after exposure to the use temperature. The lithium oxide may also be provided as either a continuous or discontinuous coating on the outer surfaces of the inorganic fibers.
In addition to the lithium oxide-bearing compounds, the viscosity of the material melt of ingredients may optionally be controlled by the presence of viscosity modifiers, in an amount sufficient to provide the fiberization required for the desired applications. The viscosity modifiers may be present in the raw materials which supply the main components of the melt, or may, at least in part, be separately added. Desired particle size of the raw materials is determined by furnacing conditions, including furnace size (SEF), pour rate, melt temperature, residence time, and the like.
The fiber may be manufactured with existing fiberization technology and formed into multiple thermal insulation product forms, including but not limited to bulk fibers, fiber-containing blankets, boards, papers, felts, mats, blocks, modules, coatings, cements, moldable compositions, pumpable compositions, putties, ropes, braids, wicking, textiles (such as cloths, tapes, sleeving, string, yarns, etc. . . . ), vacuum cast shapes and composites. The fiber may be used in combination with conventional materials utilized in the production of fiber-containing blankets, vacuum cast shapes and composites, as a substitute for conventional refractory ceramic fibers. The fiber may be used alone or in combination with other materials, such as binders and the like, in the production of fiber-containing paper and felt.
The fiber may be easily melted by standard glass furnacing methods, fiberized by standard RCF fiberization equipment, and is soluble in simulated body fluids.
A method of insulating an article using a thermal insulation containing the disclosed inorganic fibers is also provided. The method of insulating an article includes disposing on, in, near, or around the article to be insulated, a thermal insulation material that contains the inorganic fibers containing an intended lithium oxide addition.
The high temperature resistant inorganic fibers are readily manufacturable from a melt having a viscosity suitable for blowing or spinning fiber, are non-durable in physiological fluids, exhibit good mechanical strength up to the service temperature, exhibit excellent linear shrinkage up to 1400° C. and above and improved viscosity for fiberization.
The following examples are set forth to describe illustrative embodiments of the inorganic fibers containing lithium oxide addition in further detail and to illustrate the methods of preparing the inorganic fibers, preparing thermal insulating articles containing the fibers and using the fibers as thermal insulation. However, the examples should not be construed as limiting the fiber, the fiber containing articles, or the processes of making or using the fibers as thermal insulation in any manner.
Linear Shrinkage
A shrinkage pad was prepared by needling a fiber mat using a bank of felting needles. A 3 inch×5 inch test piece was cut from the pad and was used in the shrinkage testing. The length and width of the test pad was carefully measured. The test pad was then placed into a furnace and brought to a temperature of 1400° C. for 24 hours. After heating for 24 hours, the test pad was removed from the test furnace and cooled. After cooling, the length and width of the test pad were measured again. The linear shrinkage of the test pad was determined by comparing the “before” and “after” dimensional measurements.
A second shrinkage pad was prepared in a manner similar to that disclosed for the first shrinkage pad. However, the second shrinkage pad was placed in a furnace and brought to a temperature of 1260° C. for 24 hours. After heating for 24 hours, the test pad was removed from the test furnace and cooled. After cooling, the length and width of the test pad were measured again. The linear shrinkage of the test pad was determined by comparing the “before” and “after” dimensional measurements.
Compression Recovery
The ability of the inorganic fibers to retain mechanical strength after exposure to a use temperature was evaluated by a compression recovery test. Compression recovery is a measure of the mechanical performance of an inorganic fiber in response to the exposure of the fiber to a desired use temperature for a given period of time. Compression recovery is measured by firing test pads manufactured from the inorganic fiber material to the test temperature for the selected period of time. The fired test pads are thereafter compressed to half of their original thickness and allowed to rebound. The amount of rebound is measured as percent recovery of the compressed thickness of the pad. Compression recovery was measured after exposure to use temperatures of 1260° C. for 24 hours and 168 hours, and 1400° C. for 24 hours and 168 hours. According to certain illustrative embodiments, the test pads manufactured from the inorganic fibers exhibit a compression recovery of at least 10 percent.
Fiber Dissolution
The inorganic fiber is non-durable or non-biopersistent in physiological fluids. By “non-durable” or “non-biopersistent” in physiological fluids it is meant that the inorganic fiber at least partially dissolves or decomposes in such fluids, such as simulated lung fluid, during in vitro tests described herein.
The biopersistence test measures the rate at which mass is lost from the fiber (ng/cm2-hr) under conditions which simulate the temperature and chemical conditions found in the human lung. In particular, the fibers exhibit low biopersistence in Simulated Lung Fluid at a pH of 7.4.
To measure the dissolution rate of fibers in simulated lung fluid, approximately 0.1 g of fiber is placed into a 50 ml centrifuge tube containing simulated lung fluid which has been warmed to 37° C. This is then placed into a shaking incubator for 6 hours and agitated at 100 cycles per minute. At the conclusion of the test, the tube is centrifuged and the solution is poured into a 60 ml syringe. The solution is then forced through a 0.45 μm filter to remove any particulate and tested for glass constituents using Inductively Coupled Plasma Spectroscopy analysis. This test may be conducted using either a near-neutral pH solution or an acidic solution. Although no specific dissolution rate standards exist, fibers with dissolution values in excess of 100 ng/cm2 hr are considered indicative of a non-biopersistent fiber.
Table I shows fiber melt chemistries for various comparative and inventive fiber samples.
Table II shows the green thickness (inches) blankets prepared from the fibers of Table I:
Table IIIa-1 and IIIa-2 show the green and fired densities (pcf) of blankets prepared from fibers of Table I. Table Mb shows the diameters, fiber index, green density, green thickness and initial tensile strength of fibers of Table I.
Table IV shows the results for shrinkage for the fibers after exposure to 1260° C. and 1400° C. for 24 and 168 hours.
Table IV shows that a magnesium-silicate inorganic fiber composition including a synergistic combination of lithium oxide as a component of the fiberization product results in lower linear shrinkage at both 1260° C. and 1400° C. as compared to magnesium-silicate inorganic fiber without the intended and lithium oxide addition.
Table V shows the results compression recovery after exposure to 1260° C. and 1400° C. for 24 and 168 hours, and solubility for the fibers of Table I:
Table V shows that a magnesium-silicate inorganic fiber composition including an intended addition of lithium oxide as a component of the fiberization product results in an improvement in compression recovery at both 1260° C. and 1400° C. as compared to magnesium-silicate inorganic fiber without the intended and lithium oxide addition. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1260° C. for 24 hours of greater than about 30%. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1260° C. for 24 hours of greater than about 40%. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1260° C. for 24 hours of greater than about 50%. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1260° C. for 168 hours of greater than about 10%. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1260° C. for 168 hours of greater than about 20%. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1260° C. for 168 hours of greater than about 30%. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1400° C. for 24 hours of greater than about 30%. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1400° C. for 24 hours of greater than about 25%. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1400° C. for 24 hours of greater than about 20%. The magnesium-silicate inorganic fiber composition including lithium oxide as a component of the fiberization product exhibits a compression recovery after exposure to 1400° C. for 24 hours of greater than about 10%.
Table VI shows the results compressive strength after exposure to 1260° C. for 24 and 168 and 1400° C. for 24 hours for the fibers of Table I:
While the inorganic fiber, thermal insulation, methods of preparing the inorganic fiber, and method of insulating articles using the thermal insulation have been described in connection with various embodiments, it is to be understood that other similar embodiments may be used or modifications and additions may be made to the described embodiments for performing the same function. Furthermore, the various illustrative embodiments may be combined to produce the desired results. Therefore, the inorganic fiber, thermal insulation, methods of preparing the inorganic fiber, and method of insulating articles using the thermal insulation should not be limited to any single embodiment, but rather construed in breadth and scope in accordance with the recitation of the appended claims. It will be understood that the embodiments described herein are merely exemplary, and that one skilled in the art may make variations and modifications without departing from the spirit and scope of the invention. All such variations and modifications are intended to be included within the scope of the invention as described hereinabove. Further, all embodiments disclosed are not necessarily in the alternative, as various embodiments of the invention may be combined to provide the desired result.
This application claims the benefit of the filing date under 35 U.S.C. §119(e) of U.S. Provisional Application Patent Ser. No. 62/025,142 filed on Jul. 16, 2014, which is incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1759919 | Singer | May 1930 | A |
| 2051279 | Thorndyke | Aug 1936 | A |
| 2335220 | Edwards | Nov 1943 | A |
| 2576312 | Minnick | Nov 1951 | A |
| 2690393 | McGarvey | Sep 1954 | A |
| 2693668 | Slayter | Nov 1954 | A |
| 2699415 | Nachtman | Jan 1955 | A |
| 2710261 | McMullen | Jun 1955 | A |
| 2876120 | Machlan | Mar 1959 | A |
| 2877124 | Welsh | Mar 1959 | A |
| 3112184 | Hollenbach | Nov 1963 | A |
| 3166428 | Thomas | Jan 1965 | A |
| 3348994 | Rees et al. | Oct 1967 | A |
| 3380818 | Smith | Apr 1968 | A |
| 3383275 | Croop et al. | May 1968 | A |
| 3402055 | Harris et al. | Sep 1968 | A |
| 3455731 | Nielsen et al. | Jul 1969 | A |
| 3458329 | Owens et al. | Jul 1969 | A |
| 3459568 | Rinehart | Aug 1969 | A |
| 3469729 | Grekila et al. | Sep 1969 | A |
| 3597179 | Simmons | Aug 1971 | A |
| 3687850 | Gagin | Aug 1972 | A |
| 3783092 | Majumdar | Jan 1974 | A |
| 3785836 | Bacon | Jan 1974 | A |
| 3788885 | Birchall et al. | Jan 1974 | A |
| 3799836 | Rogers et al. | Mar 1974 | A |
| 3804608 | Gaskell et al. | Apr 1974 | A |
| 3804646 | Dumbaugh, Jr. | Apr 1974 | A |
| 3811901 | Bacon | May 1974 | A |
| 3854986 | Chvalovsky et al. | Dec 1974 | A |
| 3887386 | Majumdar | Jun 1975 | A |
| 3899342 | Birchall et al. | Aug 1975 | A |
| 3900329 | Grubb et al. | Aug 1975 | A |
| 3904424 | Aoki et al. | Sep 1975 | A |
| 3985935 | Brodmann | Oct 1976 | A |
| 3992498 | Morton et al. | Nov 1976 | A |
| 4002482 | Coenen | Jan 1977 | A |
| 4011651 | Bradbury et al. | Mar 1977 | A |
| 4036654 | Yale et al. | Jul 1977 | A |
| 4037015 | Koike et al. | Jul 1977 | A |
| 4078939 | Schwochow | Mar 1978 | A |
| 4102692 | Schartau et al. | Jul 1978 | A |
| 4104355 | Dunn et al. | Aug 1978 | A |
| 4118239 | Gagin et al. | Oct 1978 | A |
| 4194914 | Moriya et al. | Mar 1980 | A |
| 4243421 | Kume | Jan 1981 | A |
| 4303722 | Pilgrim | Dec 1981 | A |
| 4317575 | Cavicchio et al. | Mar 1982 | A |
| 4330628 | Cockram et al. | May 1982 | A |
| 4345430 | Pallo et al. | Aug 1982 | A |
| 4358500 | George et al. | Nov 1982 | A |
| 4363878 | Yamamoto et al. | Dec 1982 | A |
| 4366251 | Rapp | Dec 1982 | A |
| 4375493 | George et al. | Mar 1983 | A |
| 4379111 | Smith et al. | Apr 1983 | A |
| 4382104 | Smith et al. | May 1983 | A |
| 4387180 | Jen et al. | Jun 1983 | A |
| 4396661 | George et al. | Aug 1983 | A |
| 4428999 | George et al. | Jan 1984 | A |
| 4461840 | Massol | Jul 1984 | A |
| 4492722 | Ritter, II et al. | Jan 1985 | A |
| 4507355 | George et al. | Mar 1985 | A |
| 4542106 | Sproull | Sep 1985 | A |
| 4547403 | Smith | Oct 1985 | A |
| 4558015 | Ekdahl et al. | Dec 1985 | A |
| 4563219 | George et al. | Jan 1986 | A |
| 4604097 | Graves et al. | Aug 1986 | A |
| 4613577 | Tagai et al. | Sep 1986 | A |
| 4615988 | Le Moigne et al. | Oct 1986 | A |
| 4659610 | George et al. | Apr 1987 | A |
| 4673594 | Smith | Jun 1987 | A |
| 4735857 | Tagai et al. | Apr 1988 | A |
| 4737192 | Smith | Apr 1988 | A |
| 4778499 | Beaver | Oct 1988 | A |
| 4820573 | Tagai et al. | Apr 1989 | A |
| 4830989 | Trivedi et al. | May 1989 | A |
| 4867779 | Meunier et al. | Sep 1989 | A |
| 4882302 | Horiuchi et al. | Nov 1989 | A |
| 4933307 | Marshall et al. | Jun 1990 | A |
| 5037470 | Matzen et al. | Aug 1991 | A |
| 5055428 | Porter | Oct 1991 | A |
| 5064785 | Kawamoto et al. | Nov 1991 | A |
| 5108957 | Cohen et al. | Apr 1992 | A |
| 5145734 | Ito et al. | Sep 1992 | A |
| 5221558 | Sonuparlak et al. | Jun 1993 | A |
| 5223336 | Griffith et al. | Jun 1993 | A |
| 5250488 | Thelohan et al. | Oct 1993 | A |
| 5284807 | Komori et al. | Feb 1994 | A |
| 5312806 | Mogensen | May 1994 | A |
| 5332699 | Olds et al. | Jul 1994 | A |
| 5346575 | Griffith et al. | Sep 1994 | A |
| 5346868 | Eschner | Sep 1994 | A |
| 5371050 | Belitskus et al. | Dec 1994 | A |
| 5384188 | Lebold et al. | Jan 1995 | A |
| 5389716 | Graves | Feb 1995 | A |
| 5401693 | Bauer et al. | Mar 1995 | A |
| 5420087 | Wieland et al. | May 1995 | A |
| 5480676 | Sonuparlak et al. | Jan 1996 | A |
| 5486232 | Griffith et al. | Jan 1996 | A |
| 5552213 | Eschner | Sep 1996 | A |
| 5569629 | TenEyck et al. | Oct 1996 | A |
| 5576252 | Rapp et al. | Nov 1996 | A |
| 5580532 | Robinson et al. | Dec 1996 | A |
| 5583080 | Guldberg et al. | Dec 1996 | A |
| 5585312 | TenEyck et al. | Dec 1996 | A |
| 5591516 | Jaco et al. | Jan 1997 | A |
| 5603887 | Eschner | Feb 1997 | A |
| RE35557 | Thelohan et al. | Jul 1997 | E |
| 5714421 | Olds et al. | Feb 1998 | A |
| 5811360 | Jubb | Sep 1998 | A |
| 5821183 | Jubb | Oct 1998 | A |
| 5843854 | Karppinen et al. | Dec 1998 | A |
| 5858465 | Hunt et al. | Jan 1999 | A |
| 5874375 | Zoitos | Feb 1999 | A |
| 5928075 | Miya et al. | Jul 1999 | A |
| 5932500 | Jensen et al. | Aug 1999 | A |
| 5935886 | Jensen et al. | Aug 1999 | A |
| 5955389 | Jubb | Sep 1999 | A |
| 5962354 | Fyles et al. | Oct 1999 | A |
| 5968648 | Rapp et al. | Oct 1999 | A |
| 5994247 | Jubb et al. | Nov 1999 | A |
| 5998315 | Jubb | Dec 1999 | A |
| 6013592 | Merrill et al. | Jan 2000 | A |
| 6025288 | Zoitos et al. | Feb 2000 | A |
| 6030910 | Zoitos et al. | Feb 2000 | A |
| 6036762 | Sambasivan | Mar 2000 | A |
| 6037284 | Holstein et al. | Mar 2000 | A |
| 6037288 | Robinson et al. | Mar 2000 | A |
| 6043170 | Steinkopf et al. | Mar 2000 | A |
| 6156683 | Grove-Rasmussen et al. | Dec 2000 | A |
| 6180546 | Jubb et al. | Jan 2001 | B1 |
| 6284684 | Vignesoult et al. | Sep 2001 | B1 |
| 6309994 | Marra et al. | Oct 2001 | B1 |
| 6313050 | De Meringo et al. | Nov 2001 | B1 |
| 6346494 | Jensen et al. | Feb 2002 | B1 |
| 6358872 | Karppinen et al. | Mar 2002 | B1 |
| 6458436 | Hansen et al. | Oct 2002 | B1 |
| 6461415 | Sambasivan et al. | Oct 2002 | B1 |
| 6517906 | Economy et al. | Feb 2003 | B1 |
| 6551951 | Fay et al. | Apr 2003 | B1 |
| 6652950 | Barney et al. | Nov 2003 | B2 |
| 6716407 | Davis et al. | Apr 2004 | B2 |
| 6855298 | Teneyck | Feb 2005 | B2 |
| 6861381 | Jubb et al. | Mar 2005 | B1 |
| 6897173 | Bernard et al. | May 2005 | B2 |
| 6953757 | Zoitos et al. | Oct 2005 | B2 |
| 7153796 | Jubb et al. | Dec 2006 | B2 |
| 7160824 | Zguris et al. | Jan 2007 | B2 |
| 7259118 | Jubb et al. | Aug 2007 | B2 |
| 7468336 | Zoitos et al. | Dec 2008 | B2 |
| 7468337 | Zoitos et al. | Dec 2008 | B2 |
| 7470641 | Jubb et al. | Dec 2008 | B2 |
| 7550118 | Merry | Jun 2009 | B2 |
| 7567817 | Liu et al. | Jul 2009 | B2 |
| 7638447 | Bernard et al. | Dec 2009 | B2 |
| 7651965 | Jubb et al. | Jan 2010 | B2 |
| 7704902 | Maquin et al. | Apr 2010 | B2 |
| 7709027 | Fechner et al. | May 2010 | B2 |
| 7781043 | Nakayama et al. | Aug 2010 | B2 |
| 7781372 | Liu et al. | Aug 2010 | B2 |
| 7803729 | Keller et al. | Sep 2010 | B2 |
| 7875566 | Freeman et al. | Jan 2011 | B2 |
| 7887917 | Zoitos et al. | Feb 2011 | B2 |
| 7897255 | Liu et al. | Mar 2011 | B2 |
| 8026190 | Keller et al. | Sep 2011 | B2 |
| 8147952 | Iwamoto et al. | Apr 2012 | B2 |
| 8163377 | Wainwright et al. | Apr 2012 | B2 |
| 8551897 | Zoitos et al. | Oct 2013 | B2 |
| 8877102 | Bernard et al. | Nov 2014 | B2 |
| 20020022567 | Li et al. | Feb 2002 | A1 |
| 20020032116 | Jubb et al. | Mar 2002 | A1 |
| 20020107133 | Troczynski et al. | Aug 2002 | A1 |
| 20030015003 | Fisler et al. | Jan 2003 | A1 |
| 20030049329 | Lee et al. | Mar 2003 | A1 |
| 20030138673 | Sambasivan et al. | Jul 2003 | A1 |
| 20030162019 | Zoitos et al. | Aug 2003 | A1 |
| 20040011245 | Sambasivan et al. | Jan 2004 | A1 |
| 20040092379 | Lewis | May 2004 | A1 |
| 20050032620 | Zoitos et al. | Feb 2005 | A1 |
| 20050079970 | Otaki et al. | Apr 2005 | A1 |
| 20050085369 | Jensen | Apr 2005 | A1 |
| 20050268656 | Raichel et al. | Dec 2005 | A1 |
| 20060094583 | Freeman | May 2006 | A1 |
| 20060211562 | Fisler | Sep 2006 | A1 |
| 20070020454 | Zoitos et al. | Jan 2007 | A1 |
| 20080191179 | Bernard et al. | Aug 2008 | A1 |
| 20090053510 | Jubb | Feb 2009 | A1 |
| 20090130937 | Wainwright et al. | May 2009 | A1 |
| 20100093510 | Tanaka et al. | Apr 2010 | A1 |
| 20100184581 | Berthereau et al. | Jul 2010 | A1 |
| 20100209306 | Kunze et al. | Aug 2010 | A1 |
| 20100298110 | Richter et al. | Nov 2010 | A1 |
| 20110118102 | Zoitos et al. | May 2011 | A1 |
| 20110172077 | Lewis | Jul 2011 | A1 |
| 20130225025 | McGinnis | Aug 2013 | A1 |
| 20130333594 | Berthereau et al. | Dec 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 1 271 785 | Jul 1990 | CA |
| 2017344 | Nov 1990 | CA |
| 2043699 | Dec 1991 | CA |
| 0 074 655 | Mar 1983 | EP |
| 0132078 | Jan 1985 | EP |
| 0 142 715 | May 1985 | EP |
| 0 146 398 | Jun 1985 | EP |
| 0 155 550 | Sep 1985 | EP |
| 0 178 688 | Apr 1986 | EP |
| 0 178 689 | Apr 1986 | EP |
| 0 186 128 | Jul 1986 | EP |
| 0 302 465 | Feb 1989 | EP |
| 0 417 493 | Mar 1991 | EP |
| 0 427 873 | May 1991 | EP |
| 0 539 342 | Apr 1993 | EP |
| 0 834 489 | Apr 1998 | EP |
| 1 086 936 | Mar 2001 | EP |
| 1 323 687 | Jul 2003 | EP |
| 1 908 737 | Apr 2008 | EP |
| 2662687 | Dec 1991 | FR |
| 520247 | Apr 1940 | GB |
| 1 360 197 | Jul 1974 | GB |
| 1 360 198 | Jul 1974 | GB |
| 1 360 199 | Jul 1974 | GB |
| 1 360 200 | Jul 1974 | GB |
| 2 200 129 | Jul 1988 | GB |
| 2 383 793 | Jul 2003 | GB |
| 06-272116 | Oct 2006 | JP |
| 07-033546 | Feb 2007 | JP |
| 07-303011 | Nov 2007 | JP |
| 10-2004-0013846 | Feb 2004 | KR |
| 10-2010-0084917 | Jul 2010 | KR |
| WO 8502393 | Jun 1985 | WO |
| WO 8502394 | Jun 1985 | WO |
| WO 8705007 | Aug 1987 | WO |
| WO 8912032 | Dec 1989 | WO |
| WO 9002713 | Mar 1990 | WO |
| WO 9207801 | May 1992 | WO |
| WO 9209536 | Jun 1992 | WO |
| WO 9315028 | Aug 1993 | WO |
| WO 9415883 | Jul 1994 | WO |
| WO 9532926 | Dec 1995 | WO |
| WO 9605147 | Feb 1996 | WO |
| 9716386 | May 1997 | WO |
| WO 9832606 | Jul 1998 | WO |
| WO 9851981 | Nov 1998 | WO |
| WO 0216263 | Feb 2002 | WO |
| WO 03031368 | Apr 2003 | WO |
| WO 03050054 | Jun 2003 | WO |
| WO 03059835 | Jul 2003 | WO |
| 2006048610 | May 2006 | WO |
| WO 2007005836 | Jan 2007 | WO |
| Entry |
|---|
| Shelby, J.E., Introduction to Glass Science and Technology, 1997, The Royal Society of Chemistry, p. 109. |
| Wallenburger, et al. “Inviscid melt spinning: As-spun crystalline alumina fibers”, J. Mater. Res., vol. 5, No. 11, Nov. 1990. |
| Shyu, Jiin-Jyh and Wu, Jenn-Ming, Effect of TiO2 addition on the nucleation of apatite in an MgO—CaO—SiO—P2O5 glass, Journal of Materials Science Letters, vol. 10, 1991. |
| International Search Report for PCT/US2014/072027, mailed on Mar. 31, 2015. |
| International Written Opinion for PCT/ US2014/072027, mailed on Mar. 31, 2015. |
| U.S. Appl. No. 14/581,039 to Zhao, et al., filed Dec. 23, 2014. |
| U.S. Appl. No. 14/580,268 to Zhao, et al., filed Dec. 23, 2014. |
| Third party observations filed on corresponding PCT application WO2016/010580. |
| Number | Date | Country | |
|---|---|---|---|
| 20160017519 A1 | Jan 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62025142 | Jul 2014 | US |