Claims
- 1. A method of making a flexible, porous, separator for an alkaline EMF cell comprising the steps of:
- dissolving in a solvent a thermoplastic rubber of the type made up of chains of 3-blocks wherein the middle block is an elastomer and each end block is thermoplastic;
- mixing a first filler material inert to said alkaline electrolyte and a second-pore forming filler material reactive with said alkaline electrolyte;
- combining the filler materials and the dissolved thermoplastic rubber to form a slurry;
- coating said slurry on a flexible non-metallic substrate; and
- drying said coating.
- 2. The method of claim 1 wherein a polyester selected from the group of esters consisting of hydroxyethyl and hydroxypropyl esters of adipic and azelaic acids is added to the dissolved thermoplastic rubber.
- 3. The method of claim 1 wherein epoxidized soyabean oil is added to the dissolved thermoplastic rubber.
- 4. The method of claim 1 wherein said elastomer is ethylene-butylene rubber.
- 5. The method of claim 1 wherein said slurry includes between 50-80 volume percent of said thermoplastic rubber.
- 6. The method of claim 1 wherein said slurry coating is from about 10 to about 20 mils thick.
- 7. The method of claim 1 wherein said slurry is comprised of parts by weight: 40-50 of rubber based resin; sufficient solvent to dissolve the resin; and 10 to 100 of calcium silicate.
- 8. The method of claim 7 and including by parts weight: 10 to 100 of at least one inert filler; 2-20 of silica and 10-100 of alumina.
- 9. The method of claim 8 and including by parts weight: 20-50 of a plasticizer selected from the group of esters consisting of hydroxyethyl and hydroxypropyl esters of adipic and azeliac acids.
- 10. The method of claim 8 and including by parts weight: 20-50 of epoxidized soyabean oil.
- 11. The method of claim 1 wherein said substrate is paper.
- 12. The method of claim 1 wherein said solvent is a chlorinated hydrocarbon solvent.
- 13. The method of claim 12 wherein said solvent is chloroform.
- 14. The method of claim 1 wherein said first inert filler is lead titanate and said second pore-forming filler is calcium silicate.
- 15. The method of claim 14 wherein said calcium silicate is less than 50% by volume of the total filler material.
- 16. The method of claim 15 wherein the total filler material is between 25% and less than 50% by volume of said slurry, excluding the solvent.
- 17. The method of claim 1 wherein said thermoplastic rubber is polystyrene.
ORIGIN OF THE INVENTION
This invention was made by an employee of the United States Government and may be manufactured or used by or for the Government of the United States without the payment of any royalties thereon or therefor.
US Referenced Citations (8)