Patent Grant
10962698
The present invention relates to an inorganic polarizing plate.
Polarizing plates configured to pass only light or waves polarized in a specific direction are used in, for example, liquid crystal displays.
As the polarizing plates, often used are polarizing films obtained by adsorbing iodine compounds to polyvinyl alcohol (PVA) films and subjecting the films to stretch orientation to develop a dichroic property for absorption of visible light. The polarizing films are interposed between transparent films of, for example, triacetyl cellulose (TAC) in order to secure mechanical strength, heat resistance, and humidity resistance, and further have hard coatings on the transparent films for protection from, for example, scratches and stain adhesion.
Of light components incident to the polarizing films, polarized light components that do not pass through the polarizing films are absorbed in the polarizing films and radiated to the outside of the polarizing films as heat. Therefore, when the polarizing films are irradiated with strong light, there is a problem that the temperatures of the polarizing films rise due to heat generation to degrade the polarizing property. The cause of this problem is essentially the heat resistance of the organic materials. Therefore, fundamental resolution of this problem is difficult.
Hence, as polarizing plates that can be used at places where the polarizing plates are required to have a high heat resistance, wire grid polarizing plates formed completely of inorganic materials are being studied. The wire grid polarizing plates have structures in which wire grids of fine metal wires having cycles equal to or shorter than the wavelengths of light are formed on the surfaces of the substrates (see, e.g., PTL 1).
In regard of the wire grid polarizing plates, liquid stains that adhere to the grid peripheral ends diffuse in the concaves in the wire grids due to capillary actions caused by the convexes and concaves in the grid structures, to degrade the optical properties of the wire grid polarizing plates.
Hence, the following polarizer is proposed (see, e.g., PTL 2). The polarizer has a first surface that is bordered at a peripheral portion, and includes a standard region and a rib-corrected region. The standard region has ribs having standard properties. The standard region is configured to polarize incident light. The rib-corrected region is provided between at least a portion of the standard region and the peripheral portion and along at least a portion of the peripheral portion of the substrate. The rib-corrected region has corrected ribs that are corrected to have properties different from the standard properties such that the capillary action in the rib-corrected region becomes substantially smaller than the capillary action in the standard region.
With a difference in the level of the capillary action between the corrected ribs and the ribs, this polarizer is intended to prevent intrusion of liquid stains into the ribs.
However, this proposed technique needs to produce the ribs and the corrected ribs, leading to a complicated production process. In addition, because the corrected ribs also have a capillary action, there is a problem that intrusion of liquid stains into the ribs through the corrected ribs cannot completely be prevented.
The present invention aims to solve the various problems in the related art and achieve the object described below. That is, the present invention has an object to provide an inorganic polarizing plate that does not need a complicated production process and can suppress degradation of optical properties due to liquid stains that adhere to peripheral ends.
Means for solving the above problems are as follows.
<1> An inorganic polarizing plate, including in an order of reciting:
a substrate transparent to light in a bandwidth used;
a first dielectric layer;
a plurality of linear metal layers;
a plurality of linear second dielectric layers; and
a plurality of linear light absorbing layers,
wherein the plurality of linear metal layers are arranged on the first dielectric layer in a manner that the plurality of linear metal layers are spaced at intervals shorter than a wavelength of the light,
wherein the plurality of linear second dielectric layers are arranged on the plurality of linear metal layers, respectively,
wherein the plurality of linear light absorbing layers are arranged on the plurality of linear second dielectric layers, respectively, and
wherein the inorganic polarizing plate includes a water repelling layer at peripheral ends of the inorganic polarizing plate, the peripheral ends being peripheral ends at which longer-direction ends of the linear metal layers are present, the water repelling layer covering longer-direction ends of the linear metal layers, the linear second dielectric layers, and the linear light absorbing layers.
<2> The inorganic polarizing plate according to <1>, including
a third dielectric layer on facing side surfaces of the plurality of linear metal layers and on a surface of the first dielectric layer between the plurality of linear metal layers.
<3> The inorganic polarizing plate according to <1> or <2>,
wherein a material of the linear metal layers is any one selected from the group consisting of Al, Ag, Cu, Mo, Cr, Ti, Ni, W, Fe, Si, Ge, Te, and an alloy of 2 or more thereof.
<4> The inorganic polarizing plate according to any one of <1> to <3>,
wherein a material of the first dielectric layer and the linear second dielectric layers is any one of SiO2 and Al2O3.
<5> The inorganic polarizing plate according to any one of <1> to <4>,
wherein a material of the linear light absorbing layers is any one selected from the group consisting of Ta, Al, Ag, Cu, Mo, Cr, Ti, W, Ni, Fe, Sn, Si, and an alloy of 2 or more thereof.
<6> The inorganic polarizing plate according to any one of <1> to <5>,
wherein a water contact angle of the water repelling layer is 90° or greater.
<7> The inorganic polarizing plate according to any one of <1> to <6>,
wherein a material of the water repelling layer is an organopolysilazane.
<8> The inorganic polarizing plate according to any one of <1> to <7>,
wherein a material of the substrate is any one selected from the group consisting of glass, quartz crystal, and sapphire.
The present invention can solve the various problems in the related art, achieve the object described above, and provide an inorganic polarizing plate that does not need a complicated production process and can suppress degradation of optical properties due to liquid stains that adhere to peripheral ends.
(Inorganic Polarizing Plate)
An inorganic polarizing plate of the present invention includes at least a substrate, a first dielectric layer, a plurality of linear metal layers, a plurality of linear second dielectric layers, and a plurality of linear light absorbing layers in the order of reciting.
The inorganic polarizing plate includes a water repelling layer at peripheral ends of the inorganic polarizing plate, where the peripheral ends are peripheral ends at which the longer-direction ends of the linear metal layers are present.
The water repelling layer covers the longer-direction ends of the linear metal layers, the linear second dielectric layers, and the linear light absorbing layers.
The inorganic polarizing plate is a so-called wire grid polarizing plate.
The present inventors have found that an inorganic polarizing plate that includes at least a substrate, a first dielectric layer, a plurality of linear metal layers, a plurality of linear second dielectric layers, and a plurality of linear light absorbing layers in the order of reciting does not need a complicated production process, and has a good polarizing property. As a result of earnest studies in order to suppress degradation of optical properties due to liquid stains that adhere to peripheral ends, the present inventors have found that the inorganic polarizing plate that includes a water repelling layer at peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers are present such that the water repelling layer covers the longer-direction ends of the linear metal layers, the linear second dielectric layers, and the linear light absorbing layers can suppress degradation of optical properties due to liquid stains that adhere to the peripheral ends. The present invention has been completed in this way.
<Substrate>
The material, shape, size, and structure of the substrate are not particularly limited and may be appropriately selected depending on the intended purpose so long as the substrate is transparent to light in a bandwidth used.
The light in a bandwidth used is not particularly limited and may be appropriately selected depending on the intended purpose. Examples of the light include visible light. Examples of the visible light include light of from 380 nm through 810 nm.
Transparency to the light in the bandwidth used does not mean a 100% transmittance. Therefore, the substrate needs only to be transparent in the range in which the inorganic polarizing plate serves its function.
The material of the substrate is not particularly limited and may be appropriately selected depending on the intended purpose. Preferable examples of the material of the substrate include glass, quartz crystal, and sapphire. Glass is more preferable in terms of costs and transmittance.
Furthermore, a material having a refractive index of from 1.1 through 2.2 is preferable as the material of the substrate.
The average thickness of the substrate is not particularly limited, may be appropriately selected depending on the intended purpose, and is preferably from 300 μm through 1,000 μm.
<First Dielectric Layer>
The first dielectric layer is formed on the substrate.
The material of the first dielectric layer is not particularly limited and may be appropriately selected depending on the intended purpose. Examples of the material of the first dielectric layer include SiO2, Al2O3, and MgF2. Among these materials, SiO2 and Al2O3 are preferable.
The average thickness of the first dielectric layer is not particularly limited, may be appropriately selected depending on the intended purpose, and is preferably from 1 nm through 105 nm and more preferably from 35 nm through 105 nm in order to increase an interference effect.
The average thickness can be obtained by, for example, observation with a scanning electron microscope and observation with a transmission electron microscope. For example, thickness is measured at arbitrary 10 positions and the average thickness is obtained from the arithmetic mean of the measurements.
<Plurality of Linear Metal Layers>
In the inorganic polarizing plate, the plurality of linear metal layers are arranged on the first dielectric layer in a manner that the linear metal layers are spaced at intervals shorter than the wavelength of the light.
The material of the linear metal layers is not particularly limited and may be appropriately selected depending on the intended purpose. Preferable examples of the material of the linear metal layers in terms of pattern formation and optical properties include Al, Ag, Cu, Mo, Cr, Ti, Ni, W, Fe, Si, Ge, Te, and an alloy of 2 or more thereof.
The cross-sectional shape of the linear metal layers in a cross section taken orthogonally to the longer direction of the linear metal layers is not particularly limited and may be appropriately selected depending on the intended purpose. Examples of the cross-sectional shape of the linear metal layers include rectangles and trapezoids.
The average thickness of the linear metal layers is not particularly limited, may be appropriately selected depending on the intended purpose, and is preferably from 20 nm through 400 nm in terms of a polarizing property.
It is preferable that the average thickness of the linear metal layers be 50% or greater of the total of the average thickness of the linear metal layers, the average thickness of the second dielectric layers, and the average thickness of the linear light absorbing layers.
In the present specification, the average thickness of the linear metal layers is the arithmetic mean of heights of the metal layers in a cross-section taken orthogonally to the longer direction of the linear metal layers. The average thickness can be obtained by, for example, observation with a scanning electron microscope and observation with a transmission electron microscope. For example, the height is measured at arbitrary 10 positions and the average thickness is obtained from the arithmetic mean of the measurements.
The average width of the linear metal layers is not particularly limited, may be appropriately selected depending on the intended purpose, and is preferably from 20% through 60% of the average interval between the plurality of linear metal layers in terms of a polarizing property and process stability.
The average width of the linear metal layers can be obtained by, for example, observation with a scanning electron microscope and observation with a transmission electron microscope. For example, the width of 4 linear metal layers is measured at their arbitrary positions, and the average width is obtained from the arithmetic mean of the measurements. Note that the width is measured at the top level of the linear metal layers.
The average interval between the plurality of linear metal layers is not particularly limited, may be appropriately selected depending on the intended purpose, and is preferably from 100 nm through 200 nm in terms of ease of production and stability.
The average interval can be obtained by, for example, observation with a scanning electron microscope and observation with a transmission electron microscope. For example, the interval (pitch) of the linear metal layers is measured at arbitrary 4 positions, and the average interval is obtained from the arithmetic mean of the measurements. Note that the interval (pitch) is the distance measured for adjoining 2 linear metal layers, between a top edge of one of the linear metal layers at the other linear metal layer side and a top edge of the other of the linear metal layers at the side opposite to the one linear metal layer side.
<Plurality of Linear Second Dielectric Layers>
The plurality of linear second dielectric layers are arranged on the plurality of linear metal layers, respectively.
The material of the linear second dielectric layers is not particularly limited and may be appropriately selected depending on the intended purpose. Examples of the material of the linear second dielectric layers include SiO2, Al2O3, and MgF2. Among these materials, SiO2 and Al2O3 are preferable.
The cross-sectional shape of the linear second dielectric layers in a cross section taken orthogonally to the longer direction of the linear second dielectric layers is not particularly limited and may be appropriately selected depending on the intended purpose. Examples of the cross-sectional shape of the linear second dielectric layers include rectangles and trapezoids.
The average thickness of the linear second dielectric layers is not particularly limited, may be appropriately selected depending on the intended purpose, and is preferably from 1 nm through 100 nm and more preferably from 3 nm through 80 nm in order to increase an interference effect.
The average thickness of the linear second dielectric layers can be obtained in the same manner as for obtaining the average thickness of the linear metal layers.
<Plurality of Linear Light Absorbing Layers>
The plurality of linear light absorbing layers are arranged on the plurality of linear second dielectric layers, respectively.
The linear light absorbing layers have a light absorbing function.
The light absorbing function means a function of attenuating a polarized wave (TE wave (S wave)) having an electric field component parallel with the grid formed in the inorganic polarizing plate. The linear light absorbing layers allow transmission therethrough of a polarized wave (TM wave (P wave)) having an electric field component perpendicular to the grid.
The material of the linear light absorbing layers is not particularly limited and may be appropriately selected depending on the intended purpose so long as the linear light absorbing layers have the light absorbing function. Examples of the material of the linear light absorbing layers include metals, semiconductors, and metal-containing semiconductors. Among these materials, any one of Ta, Al, Ag, Cu, Mo, Cr, Ti, W, Ni, Fe, Sn, Si, and an alloy of 2 or more thereof is preferable in terms of optical properties.
The linear light absorbing layers may have a single-layer structure or a multi-layer structure. For example, the linear light absorbing layers may include a single layer formed of a metal-containing semiconductor or include 2 layers formed of a metal or a semiconductor, and a metal-containing semiconductor.
The linear light absorbing layers having a 2-layer structure formed of a metal or a semiconductor and a metal-containing semiconductor can suppress reflection, improve transmittance, and increase contrast.
The average thickness of the linear light absorbing layers is not particularly limited, may be appropriately selected depending on the intended purpose, and is preferably from 1 nm through 100 nm, more preferably from 5 nm through 80 nm, and particularly preferably from 10 nm through 50 nm.
The average thickness of the linear light absorbing layers can be obtained in the same manner as for obtaining the average thickness of the linear metal layers.
<Water Repelling Layer>
The water repelling layer is formed at peripheral ends of the inorganic polarizing plate at which the longer direction ends of the linear metal layers are present. The water repelling layer covers the longer-direction ends of the linear metal layers, the linear second dielectric layers, and the linear light absorbing layers.
In the inorganic polarizing plate, the water repelling layer may also be formed at other portions in addition to the peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers are present.
With the water repelling layer for covering the longer-direction ends of the linear metal layers, the linear second dielectric layers, and the linear light absorbing layers provided at the peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers are present, the inorganic polarizing plate can prevent liquid stains from intruding from the longer-direction ends of the linear metal layers into between the linear metal layers (between grid portions of the wire grid) and further from diffusing in the wire grid due to a capillary action. As a result, the inorganic polarizing plate can suppress degradation of optical properties due to the liquid stains that adhere to the peripheral ends.
The inorganic polarizing plate can prevent liquid stains from intruding into between the linear metal layers (between grid portions of the wire grid) and further from diffusing in the wire grid due to a capillary action with the water repelling layer. Therefore, there is no need for producing corrected ribs and ribs as in the invention described in JP-A No. 2013-218294. Hence, the inorganic polarizing plate does not need a complicated production process.
The water repelling layer is not particularly limited and may be appropriately selected depending on the intended purpose so long as the water-repelling layer has water repellency, but it is preferable that a water contact angle of the water-repelling layer be 90° or greater. The water contact angle can be measured with, for example, a contact angle mater using pure water.
The material of the water repelling layer is not particularly limited and may be appropriately selected depending on the intended purpose so long as water repellency can be obtained. An organopolysilazane is preferable because of an excellent heat resistance.
The average thickness of the water repelling layer is not particularly limited and may be appropriately selected depending on the intended purpose.
<Other Members>
Examples of the other members include a third dielectric layer.
<<Third Dielectric Layer>>
The third dielectric layer is arranged on facing side surfaces of 2 linear meatal layers.
The third dielectric layer is arranged on the surface of the first dielectric layer between 2 linear metal layers.
With the third dielectric layer, the inorganic polarizing plate can be improved in resistance such as heat resistance and humidity resistance.
The material of the third dielectric layer is not particularly limited and may be appropriately selected depending on the intended purpose. Examples of the material of the third dielectric layer include SiO2, Al2O3, and MgF2. Among these materials, SiO2 and Al2O3 are preferable.
The average thickness of the third dielectric layer is not particularly limited, may be appropriately selected depending on the intended purpose, and is preferably from 1 nm through 100 nm and more preferably from 3 nm through 80 nm.
An example of the inorganic polarizing plate of the present invention will be described with reference to the drawings.
The inorganic polarizing plate of
The plurality of linear metal layers 3 are arranged on the first dielectric layer 2 in a manner that the linear metal layers 3 are spaced at intervals shorter than the wavelength of light.
The plurality of linear second dielectric layers 4 are arranged on the plurality of linear metal layers 3, respectively.
The plurality of linear light absorbing layers 5 are arranged on the plurality of linear second dielectric layers 4, respectively.
The inorganic polarizing plate includes a water repelling layer 6 at peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers 3 are present. The water repelling layer 6 covers the longer-direction ends of the linear metal layers 3, the linear second dielectric layers 4, and the linear light absorbing layers 5.
At the peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers 3 are present, the water repelling layer 6 needs not cover the longer-direction ends of the linear metal layers 3, the linear second dielectric layers 4, and the linear light absorbing layers 5 that are positioned at both ends of sides of the inorganic polarizing plate defining the peripheral ends as illustrated in
Needless to say, at the peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers 3 are present, the water repelling layer 6 may cover also both ends of the sides of the inorganic polarizing plate defining the peripheral ends as illustrated in
At the peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers 3 are present, the water repelling layer 6 may cover a part of the substrate 1 as illustrated in
At the peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers 3 are present, the water repelling layer 6 may cover the first dielectric layer as illustrated in
On the top surface of the inorganic polarizing plate having the side surface illustrated in
Also on the top surface of the inorganic polarizing plate having the side surface illustrated in
<Method for Producing Inorganic Polarizing Plate>
Next, an example of a method for producing the inorganic polarizing plate of the present invention will be described with reference to
First, a substrate 1 is prepared (
Next, a first dielectric layer 2 is formed on the substrate 1 (
Next, a metal layer 3′ is formed on the first dielectric layer 2 (
Next, a second dielectric layer 4′ is formed on the metal layer 3′ (
Next, a light absorbing layer 5′ is formed on the second dielectric layer 4′ (
Next, a resist layer 11′ is formed on the light absorbing layer 5′ (
Next, the resist layer 11′ is exposed to light and developed, to form a resist pattern 11 (
Next, etching is performed using the resist pattern 11 as a mask, to form linear metal layers 3, linear second dielectric layers 4, and linear light absorbing layers 5 (
Next, optionally, the resultant is cut into a desired size with a scribing apparatus.
Next, a water repelling layer 6 for covering the longer-direction ends of the linear metal layers 3, the linear second dielectric layers 4, and the linear light absorbing layers 5 is formed at peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers 3 are present (
In the way described above, the inorganic polarizing plate is produced.
Next, another example of the method for producing the inorganic polarizing plate of the present invention will be described with reference to
The method is the same as in
Next, optionally, the resultant is cut into a desired size with a scribing apparatus.
Next, a third dielectric layer 7 is formed on the exposed portions of the first dielectric layer 2, on the side surfaces of the linear metal layers 3, on the side surfaces of the linear second dielectric layers 4, and on the side surfaces and top surfaces of the linear light absorbing layers 5 (
Next, a water repelling layer 6 for covering the longer-direction ends of the linear metal layers 3, the linear second dielectric layers 4, and the linear light absorbing layers 5 is formed at peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers 3 are present (
In the way described above, the inorganic polarizing plate is produced.
Next, another example of the method for producing the inorganic polarizing plate of the present invention will be described with reference
First, a first dielectric layer 2, a metal layer, and a resist layer are formed in the order of reciting on a substrate 1 prepared. Subsequently, the resultant is exposed to light and developed, to form a resist pattern. Next, etching is performed using the resist pattern as a mask, to process the metal layer into desired linear metal layers 3 (
Next, optionally, the resultant is cut into a desired size with a scribing apparatus.
Next, a dielectric layer is formed on the exposed portions of the first dielectric layer 2 and on the side surfaces and top surfaces of the linear metal layers 3 (
Next, linear light absorbing layers 5 are formed on the linear second dielectric layers 4 (
Next, a water repelling layer 6 for covering the longer-direction ends of the linear metal layers 3, the linear second dielectric layers 4, and the linear light absorbing layers 5 is formed at peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers 3 are present (
In the way described above, the inorganic polarizing plate is produced.
<Water Repelling Layer>
Next, the water repelling layer will be described in more detail.
The height H (m) of liquid level rise in
T represents surface tension (N/m). ρ represents density (kg/m3). g represents gravitational acceleration (m/s2). d represents tube size (m). θ represents contact angle (°).
In
Fully sealed: a state that the medium that has intruded into a void fills the void to the full of the grid height
50% sealed: a state that the medium that has intruded into a void fills the void to 50% of the grid height.
25% sealed: a state that the medium that has intruded into a void fills the void to 25% of the grid height.
From
The water repelling layer can be formed with a water repellent agent having a water contact angle of 90° or greater. In this case, for example, the sides of the inorganic polarizing plate at which the grid is opened is impregnated with the water repellent agent. Further, with combination of a dipping tank and a lifting mechanism, water repelling layers can be formed on many inorganic polarizing plates at a time.
When a water repellent agent having a super water repellency is used, the water contact angle of the water repellent agent is 125° or greater as illustrated in
Examples of the position at which the water repelling layer is formed include the positions illustrated in
As illustrated in
In order to confirm that a capillary action is prevented, there is a method of attaching, for example, sebum on the peripheral ends of the inorganic polarizing plate at which the longer-direction ends of the linear metal layers are present and observing the state of intrusion of, for example, the sebum in the grid grooves. For example, sebum is attached on the longer-direction ends of the linear metal layers of the inorganic polarizing plate of the present invention including a water repelling layer having a water contact angle of 90° or greater, and the inorganic polarizing plate is left to stand at normal temperature in a state that the inorganic polarizing plate is stood upright with the peripheral end on which the sebum is attached facing downward. A capillary action at the portion on which the sebum is attached is observed with an optical microscope, to observe temporal changes.
When the inorganic polarizing plate is used in a projector, the temperature of the inorganic polarizing plate will be elevated to 150° C. or higher due to photothermal generation because light of the projector will be passing through the inorganic polarizing plate for a long time. It can be assumed that the components of the water repellent agent forming the water repelling layer may volatize in a high-temperature environment at a high temperature of 250° C. due to thermal decomposition, to lower the water contact angle to 30° or less, and the water repelling layer may lose its property. However, although light of a projector heats the inorganic polarizing plate at the same time as it passes through the center of the inorganic polarizing plate, the temperature at the peripheral ends of the inorganic polarizing plate does not rise to 250° C. Therefore, the water repelling layer will not lose its property.
The water contact angle at the central portion of the inorganic polarizing plate lowered at every 100 hours along with the cumulative irradiation time. On the other hand, the contact angle at the peripheral ends of the inorganic polarizing plate that were not on the light path was kept to 135° or greater. Therefore, it was possible to maintain a water contact angle effective for a capillary action. As a result of confirming this effect by a capillary action test, as illustrated in
The material forming the water repelling layer is preferably an organopolysilazane. The organopolysilazane can form a water repelling layer having a water contact angle of 90° or greater, and has an excellent heat resistance. The organopolysilazane having an excellent heat resistance can suppress degradation of water repellency due to heat generation on the light path, which is the drawback with the use of a typical water repellent agent.
The inorganic polarizing plate of the present invention does not need a complicated production process and can suppress degradation of optical properties due to liquid stains that adhere to the peripheral ends. Therefore, the inorganic polarizing plate of the present invention can be suitably used in projectors.
| Number | Date | Country | Kind |
|---|---|---|---|
| JP2015-002536 | Jan 2015 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2016/050371 | 1/7/2016 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2016/111333 | 7/14/2016 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20030072079 | Silverstein | Apr 2003 | A1 |
| 20070285777 | Toyoshima | Dec 2007 | A1 |
| 20080166549 | Shieh | Jul 2008 | A1 |
| 20100103517 | Davis | Apr 2010 | A1 |
| 20130250411 | Bangerter | Sep 2013 | A1 |
| 20130250412 | Aota | Sep 2013 | A1 |
| 20130286358 | Takahashi | Oct 2013 | A1 |
| 20140063467 | Takahashi | Mar 2014 | A1 |
| 20140234640 | Kohno | Aug 2014 | A1 |
| 20140287242 | Cleymans | Sep 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 103323900 | Sep 2013 | CN |
| 103323901 | Sep 2013 | CN |
| 2008216956 | Sep 2008 | JP |
| 2010210829 | Sep 2010 | JP |
| Entry |
|---|
| The State Intellectual Property Office of People's Republic of China, Second Chinese Office Action issued in corresponding Chinese Application No. 201680004442.0, dated Oct. 21, 2019. |
| Office Action issued in corresponding Chinese Application No. 20168000044420, dated Feb. 19, 2019 with English Translation. |
| Number | Date | Country | |
|---|---|---|---|
| 20180267221 A1 | Sep 2018 | US |