Patent Application
20240278974
The present disclosure relates to polymeric materials that can be formed to produce a container, and in particular, polymeric materials that insulate. More particularly, the present disclosure relates to polymer-based formulations that can be formed to produce a multi-layer sheet.
A multi-layer sheet in accordance with the present disclosure includes a film layer and an insulative cellular non-aromatic polymeric material. In illustrative embodiments, a blend of polymeric resins and cell-forming agents is extruded or otherwise formed to produce the insulated cellular non-aromatic polymeric material.
In illustrative embodiments, a polymeric-lamination layer couples together the film layer and the insulative cellular non-aromatic polymeric material. The multi-layer sheet may be formed by an extrusion lamination procedure that extrudes the polymer-lamination layer onto the insulative cellular non-aromatic polymeric material.
In some illustrative embodiments, the polymeric-lamination layer comprises a polypropylene, a polyethylene, or a mixture thereof. In some embodiments, the polymeric-lamination layer is substantially free of an adhesive.
In some illustrative embodiments, the insulative cellular non-aromatic polymeric material, the polymeric-lamination layer, or both comprise regrind. In some embodiments, regrind is blend of materials recaptured from the steps in forming the multi-layer sheet. In some illustrative embodiments, regrind is substantially free of an adhesive.
In some illustrative embodiments, the multi-layer sheet may have a tear resistance in a machine direction of at least about 75 gf according to ASTM D1922-93. In some illustrative embodiments, the multi-layer sheet has a puncture resistance of at least about 6,000 gf.
Additional features of the present disclosure will become apparent to those skilled in the art upon consideration of illustrative embodiments exemplifying the best mode of carrying out the disclosure as presently perceived.
The detailed description particularly refers to the accompanying figures in which:
An insulative cup 10 in accordance with the present disclosure may be formed from a multi-layer sheet 80 as shown in
Multi-layer sheet 80 is used to form insulative cup 10 as shown in
Multi-layer sheet 80 formed during cup-manufacturing process 100 may provide beneficial properties relative to a multi-layer sheet where an adhesive is used in place of polymeric-lamination layer 54. As an example, multi-layer sheet 80 may have improved rigidity. In addition, using polymeric-lamination layer 54 to couple insulative cellular non-aromatic polymeric material 82 to printed film layer 70 avoids the use of an adhesive. Illustratively, the presence of adhesive in multi-layer sheet 80 may inhibit the use of recaptured multi-layer sheet 80 as use in regrind for insulative cellular non-aromatic polymeric material 82, if present.
Multi-layer sheet 80 includes insulative cellular non-aromatic polymeric material 82, polymeric-lamination layer 54, and printed film layer 70, as shown in
A second embodiment of a multi-layer sheet 2080 is shown in
In some embodiments, multi-layer sheet 80 has a puncture resistance, as measured in max load for either a ¼″ probe or a ⅛″ probe. In some embodiments, the puncture resistance for multi-layer sheet 80 (max load) is at least about 1,000 gf, at least about 3,000 gf, at least about 6,000 gf, at least about 8,000 gf, at least about 9,000 gf, or at least about 9,500 gf. In some embodiments, the puncture resistance for multi-layer sheet 80 (max load) is less than about 20,000 gf, less than about 18,000 gf, less than about 12,000 gf, or less than about 10,000 gf. In some embodiments, the puncture resistance for multi-layer sheet 80 (max load) is in a range of about 1,000 gf to about 20,000 gf, about 1,000 gf to about 18,000 gf, about 1,000 gf to about 12,000 gf, about 3,000 gf to about 12,000 gf, about 6,000 gf to about 12,000 gf, about 7,000 gf to about 12,000 gf, about 7,000 gf to about 11,000 gf, about 8,000 gf to about 11,000 gf, about 8,000 gf to about 10,000 gf, or about 9,000 gf to about 10,000 gf.
In some embodiments, multi-layer sheet 80 or insulative cellular non-aromatic polymeric material 82 has a thermal conductivity at 21° C. In some embodiments, the thermal conductivity at 21° C. is at least about 0.05 W/m-K or at least about 0.052 W/m-K. In some embodiments, the thermal conductivity at 21° C. is less than about 0.06 W/m-K, less than about 0.057 W/m-K, less than about 0.056 W/m-K, or less than about 0.053 W/m-K. In some embodiments, multi-layer sheet 80 or insulative cellular non-aromatic polymeric material 82 has a thermal conductivity at 21° C. in a range of about 0.05 W/m-K to about 0.06 W/m-K, about 0.05 W/m-K to about 0.059 W/m-K, about 0.052 W/m-K to about 0.059 W/m-K, or about 0.054 W/m-K to about 0.057 W/m-K.
In some embodiments, multi-layer sheet 80 or insulative cellular non-aromatic polymeric material 82 has a thermal conductivity at 93° C. In some embodiments, the thermal conductivity at 93° C. is at least about 0.061 W/m-K or at least about 0.062 W/m-K. In some embodiments, the thermal conductivity at 93° C. is less than about 0.065 W/m-K, less than about 0.064 W/m-K, or less than about 0.0642 W/m-K. In some embodiments, multi-layer sheet 80 or insulative cellular non-aromatic polymeric material 82 has a thermal conductivity at 93° C. in a range of about 0.061 W/m-K to about 0.065 W/m-K, about 0.063 W/m-K to about 0.065 W/m-K, about 0.063 W/m-K to about 0.0645 W/m-K.
In some embodiments, multi-layer sheet 80 or insulative cellular non-aromatic polymeric material 82 was tested using the Elmendorf test method described in ASTM D1922-93. In some embodiments, the Elmendorf Arm machine direction (MD) for the insulative cellular non-aromatic polymeric material 82 is at least about 500 g. In some embodiments, the Elmendorf Arm MD for multi-layer sheet 80 is at least about 1500 g. In some embodiments, the Elmendorf Arm MD for cup 10 is at least about 1500 g. In some embodiments, the Elmendorf Arm TD for insulative cellular non-aromatic polymeric material 82 is at least about 500 g. In some embodiments, the Elmendorf Arm TD for multi-layer sheet 80 is at least about 1500 g. In some embodiments, the Elmendorf Arm TD for cup 10 is at least about 1500 g.
It is within the scope of the present disclosure that the density of the multi-layer sheet be up to about 0.25 g/cm3, up to about 0.2 g/cm3, up to about 0.18 g/cm3, up to about 0.16 g/cm3, up to about 0.14 g/cm3, up to about 0.13 g/cm3, or up to about 0.12 g/cm3. In some embodiments, the density of the multi-layer sheet is less than about 0.2 g/cm3, less than about 0.18 g/cm3, less than about 0.16 g/cm3, less than about 0.15 g/cm3, less than about 0.14 g/cm3, or less than about 0.13 g/cm3. The density of the multi-layer sheet may be about 0.01 g/cm3, about 0.03 g/cm3, about 0.05 g/cm3, about 0.06 g/cm3, about 0.07 g/cm3, about 0.08 g/cm3, about 0.09 g/cm3, about 0.1 g/cm3, about 0.11 g/cm3, about 0.12 g/cm3, about 0.13 g/cm3, about 0.14 g/cm3, about 0.15 g/cm3, about 0.16 g/cm3, about 0.18 g/cm3, about 0.2 g/cm3, or about 0.25 g/cm3. In a set of ranges, the density of the multi-layer sheet is one of the following ranges: about 0.01 g/cm3 to about 0.2 g/cm3, about 0.05 g/cm3 to about 0.19 g/cm3, about 0.05 g/cm3 to about 0.18 g/cm3, about 0.05 g/cm3 to about 0.17 g/cm3, about 0.1 g/cm3 to about 0.17 g/cm3, about 0.11 g/cm3 to about 0.17 g/cm3, or about 0.12 g/cm3 to about 0.16 g/cm3.
In some embodiments, multi-layer sheet 80 or insulative cellular non-aromatic polymeric material 82 was tested using the Elmendorf test method described in ASTM D1922-93. In some embodiments, the Elmendorf Tear MD for the multi-layer sheet 80 or insulative cellular non-aromatic polymeric material 82 is at least about 75 gf. In some embodiments, the Elmendorf Tear MD for the multi-layer sheet 80 or insulative cellular non-aromatic polymeric material 82 is less than about 350 gf. In some embodiments, the Elmendorf Tear MD for the multi-layer sheet 80 is at least about 65 gf. In some embodiments, the Elmendorf Tear MD for multi-layer sheet 80 is less than about 700 gf. In some embodiments, the Elmendorf Tear MD for multi-layer sheet 80 is at least about 125 gf, at least about 200 gf, at least about 300 gf, or at least about 400 gf. In some embodiments, the Elmendorf Tear MD for multi-layer sheet 80 is less than about 700 gf, less than about 600 gf, less than about 500 gf. In some embodiments, the Elmendorf Tear MD for multi-layer sheet 80 is in a range of about 200 gf to about 700 gf, about 200 gf to about 600 gf, about 200 gf to about 500 gf, or about 300 gf to about 500 gf.
In some embodiments, the Elmendorf Tear transverse direction (TD) for multi-layer sheet 80 is at least about 10 gf, at least about 50 gf, or at least about 125 gf. In some embodiments, the Elmendorf Tear TD for insulative cellular non-aromatic polymeric material 82 is less than about 450 gf. In some embodiments, the Elmendorf Tear TD for multi-layer sheet 80 is at least about 65 gf, at least about 100 gf, or at least about 200 gf. In some embodiments, the Elmendorf Tear TD for multi-layer sheet 80 is less than about 600 gf. In some embodiments, the Elmendorf Tear TD for multi-layer sheet 80 is at least about 200 gf, at least about 300 gf, or at least about 400 gf. In some embodiments, the Elmendorf Tear TD for multi-layer sheet 80 is less than about 700 gf, less than about 650 gf, or less than about 550 gf. In some embodiments, the Elmendorf Tear TD of cup 10 is about 200 gf to about 700 gf, about 200 gf to about 600 gf, or about 300 gf to about 600 gf.
Insulative cellular non-aromatic polymeric material 82 is configured in accordance with the present disclosure to provide means for enabling localized plastic deformation in at least one selected region of body 11 (e.g., side wall 18, rolled brim 16, floor mount, and a floor-retaining flange included in floor mount to provide (1) a plastically deformed first material segment having a first density in a first portion of the selected region of body 11 and (2) a second material segment having a relatively lower second density in an adjacent second portion of the selected region of body 11. In illustrative embodiments, the first material segment is thinner than the second material segment.
One aspect of the present disclosure provides a formulation for manufacturing an insulative cellular non-aromatic polymeric material 82. As referred to herein, an insulative cellular non-aromatic polymeric material 82 refers to an extruded structure having cells formed therein and has desirable insulative properties at given thicknesses. Another aspect of the present disclosure provides a polymeric formulation for manufacturing an extruded structure of insulative cellular non-aromatic polymeric material. Still another aspect of the present disclosure provides an extrudate comprising an insulative cellular non-aromatic polymeric material. A further aspect of the present invention provides multi-layer sheet 80 comprising insulative cellular non-aromatic polymeric material 82.
Illustratively, each of insulative cellular non-aromatic polymeric material 82, polymeric-lamination layer 54, and film layer 56 comprise a polymeric material. The polymeric material for each of insulative cellular non-aromatic polymeric material 82, polymeric-lamination layer 54, and film layer 56 can be made, for example, by extruding a formulation. It should be understood that many of the ranges described herein for the formulation apply with equal weight to the extruded polymeric material, except that in some examples the chemical nucleating agent will decompose upon heating. The decomposition of the chemical nucleating agent could cause the relative weight percentages of the remaining components to increase slightly.
As an example, a polymeric formulation for forming insulative cellular non-aromatic polymeric material 82 comprises a base resin blend comprising at least one high melt strength polypropylene and a polypropylene copolymer or homopolymer (or both). In some embodiments, the formulation may comprise cell-forming agents including a chemical nucleating agent, a physical nucleating agent, a physical blowing agent such as carbon dioxide, or a combination thereof. As a further example, insulative cellular non-aromatic polymeric material 82 further comprises a slip agent. As an example, at least one polypropylene resin may have a broadly distributed unimodal (not bimodal) molecular weight distribution.
A material-forming process uses a polymeric formulation in accordance with the present disclosure to produce a strip 82 of insulative cellular non-aromatic polymeric material as shown in
In exemplary embodiments, a polymeric formulation comprises a base resin blend comprising at least two materials. In some embodiments, the base resin blend comprises a first polymer and a second polymer. In some embodiments, the first polymer is a polypropylene. In some embodiments, the second polymer is a polypropylene. In some embodiments, the first polymer is a polypropylene and the second polymer is a polypropylene. In one exemplary embodiment, a first or second polypropylene polymer comprises a high melt strength polypropylene that has long chain branching. In one exemplary embodiment, the first or second polypropylene polymer also has non-uniform dispersity. In some embodiments, the first polypropylene polymer is a polypropylene homopolymer. In some embodiments, the second polypropylene is a polypropylene homopolymer. In some embodiments, the base resin blend comprises a first polypropylene homopolymer and a second polypropylene homopolymer.
In some embodiments, the base resin blend further comprises a third material. In some embodiments, the base resin blend comprises at least two high melt-strength polypropylenes. In some embodiments, the base resin blend comprises a first high melt-strength polypropylene, a second high melt-strength polypropylene, and a polypropylene copolymer. In some embodiments, the polypropylene copolymer is a high-crystallinity copolymer. In some embodiments, the first high melt-strength polypropylene is Amppleo® 1025MA from Braskem. In some embodiments, the second high melt-strength polypropylene is MFX6 from JPP. In some embodiments, the polypropylene copolymer is TI215OC available from Braskem.
Some illustrative examples of high melt strength polypropylene have long chain branching. Illustratively, long chain branching occurs by the replacement of a substituent, e.g., a hydrogen atom, on a monomer subunit, by another covalently bonded chain of that polymer, or, in the case of a graft copolymer, by a chain of another type. For example, chain transfer reactions during polymerization could cause branching of the polymer. Long chain branching is branching with side polymer chain lengths longer than the average critical entanglement distance of a linear polymer chain. Long chain branching is generally understood to include polymer chains with at least 20 carbon atoms depending on specific monomer structure used for polymerization. Another example of branching is by crosslinking of the polymer after polymerization is complete. Some long chain branch polymers are formed without crosslinking. Polymer chain branching can have a significant impact on material properties. Originally known as the polydispersity index, dispersity is the measured term used to characterize the degree of polymerization. For example, free radical polymerization produces free radical monomer subunits that attach to other free radical monomers subunits to produce distributions of polymer chain lengths and polymer chain weights. Different types of polymerization reactions such as living polymerization, step polymerization, and free radical polymerization produce different dispersity values due to specific reaction mechanisms. Dispersity is determined as the ratio of weight average molecular weight to number average molecular weight. Uniform dispersity is generally understood to be a value near or equal to 1. Non-uniform dispersity is generally understood to be a value greater than 2. Final selection of a polypropylene material may take into account the properties of the end material, the additional materials needed during formulation, as well as the conditions during the extrusion process. In exemplary embodiments, high melt strength polypropylenes may be materials that can hold a gas (as discussed hereinbelow), produce desirable cell size, have desirable surface smoothness, and have an acceptable odor level (if any).
Another illustrative example of a suitable polypropylene that may be included in the base resin blend is DAPLOY™ WB140 homopolymer (available from Borealis A/S), a high melt strength structural isomeric modified polypropylene homopolymer (melt strength=36 cN, as tested per ISO 16790, which is incorporated by reference herein, melting temperature=325.4° F. (163° C.) using ISO 11357, which is incorporated by reference herein).
Borealis DAPLOY™ WB140 properties (as described in a Borealis product brochure):
Other polypropylene polymers having suitable melt strength, branching, and melting temperature may also be used. Several base resins may be used and mixed together.
In some embodiments, the base resin blend comprises a polymer that may be, for example, a polymer with sufficient crystallinity. The polymer may also be, for example, a polymer with sufficient crystallinity and melt strength. In exemplary embodiments, the polymer may be at least one crystalline polypropylene homopolymer, a crystalline polypropylene copolymer, an impact polypropylene copolymer, mixtures thereof, or the like. One illustrative example is a high crystalline polypropylene homopolymer, available as F020HC from Braskem. Another illustrative example is an impact polypropylene copolymer commercially available as PRO-FAX SC204™ (available from LyondellBasell Industries Holdings, B.V.). Another illustrative example is Homo PP-INSPIRE 222, available from Braskem. Another illustrative example is the commercially available polymer known as PP 527K, available from Sabic. Another illustrative example is a polymer commercially available as XA-11477-48-1 from LyondellBasell Industries Holdings, B.V. Another illustrative example is TI215OC from Braskem. In one aspect the polypropylene polymer may have a high degree of crystallinity, i.e., the content of the crystalline phase exceeds 51% (as tested using differential scanning calorimetry) at 10° C./min cooling rate. In exemplary embodiments, several different polymers may be used and mixed together.
In some exemplary embodiments, the base resin blend may comprise polyethylene. In exemplary embodiments, the base resin blend may comprise low-density polyethylene, linear low-density polyethylene, high-density polyethylene, ethylene-vinyl acetate copolymers, ethylene-ethylacrylate copolymers, ethylene-acrylic acid copolymers, polymethylmethacrylate mixtures of at least two of the foregoing and the like. The use of non-polypropylene materials may affect recyclability, insulation, microwavability, impact resistance, or other properties, as discussed further hereinbelow.
It is within the scope of the present disclosure to select an amount of base resin blend of the polymeric formulation to be one of the following values: about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, about 86%, about 87%, about 88%, about 89%, about 90%, about 91%, about 92%, about 93%, about 94%, about 95%, about 96%, about 97%, about 98%, about 99%, about 99.5%, and about 99.9% by weight of the polymeric formulation. It is within the present disclosure for the amount of base resin blend in the polymeric formulation to fall within one of many different ranges. In a first set of ranges, the range of base resin blend of the polymeric formulation is one of the following ranges: about 40% to about 99.9%, about 70% to about 99.9%, about 80% to about 99.9%, about 85% to about 99.9%, about 90% to about 99.9%, about 95% to about 99.9%, about 98% to about 99.9%, and about 99% to about 99.9% by weight of the polymeric formulation. In a second set of ranges, the range of base resin blend in the polymeric formulation is one of the following ranges: about 85% to about 99%, about 85% to about 98%, about 85% to about 95%, and about 85% to about 90% by weight of the polymeric formulation. In a third set of ranges, the range of base resin blend of the polymeric formulation is one of the following ranges: about 40% to about 99%, about 40% to about 95%, about 40% to about 85%, about 45% to about 85%, about 40% to about 80%, about 50% to about 80%, about 55% to about 80%, and about 60% to about 80% by weight of the polymeric formulation. Each of these values and ranges is embodied in the Examples. As defined hereinbefore, the base resin blend may comprise any suitable polymeric material. In addition, the ranges disclosed herein for the formulation apply with equal weight to the ranges for the polymeric material.
In illustrative embodiments, the base resin blend comprises a polypropylene. In some embodiments, the base resin blend comprises a first polymer and a second polymer. In some embodiments, the base resin blend comprises a first polymer, a second polymer, and a third polymer. In some embodiments, the first polymer is a first polypropylene. In some embodiments, the polypropylene is a first polypropylene homopolymer. In some embodiments, the first polypropylene homopolymer is DAPLOY™ WB140 homopolymer (available from Borealis A/S). In some embodiments, the first polypropylene homopolymer is Braskem Amppleo® 1025 MA. It is within the scope of the present disclosure to select an amount of the first polymer of the base resin blend to be one of the following values: about 30%, about 35%, about 40%, about 41%, about 42%, about 43%, about 44%, about 45%, about 50%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 81%, about 82%, about 83%, about 84%, about 85%, about 86%, about 87%, about 88%, about 89%, about 90%, about 91%, about 92%, about 93%, about 94%, about 95%, about 96%, about 97%, or about 99% by weight of the base resin blend. It is within the present disclosure for the amount of the first polymer of the base resin blend to fall within one of many different ranges. In a first set of ranges, the range of first polymer in the base resin blend is one of the following ranges: about 30% to about 99%, about 40% to about 99%, about 50% to about 99%, about 60% to about 99%, about 70% to about 99%, about 80% to about 99%, or about 85% to about 99.9% by weight of the base resin blend. In a second set of ranges, the range of first polymer in the base resin blend is one of the following ranges: about 40% to about 97%, about 40% to about 95%, about 40% to about 92%, or about 40% to about 90% by weight of the base resin blend. In a third set of ranges, the range of first polymer in the base resin blend is one of the following ranges: about 40% to about 95%, about 40% to about 90%, about 40% to about 80%, about 40% to about 70%, about 45% to about 70%, about 45% to about 60%, about 50% to about 95%, about 60% to about 95%, about 65% to about 95%, about 65% to about 92%, about 70% to about 92%, about 75% to about 92%, or about 80% to about 92% by weight of the base resin blend.
In illustrative embodiments, the base resin blend includes a second polymer. In some embodiments, the second polymer is a polyethylene. In some embodiments, the second polymer is a polypropylene. In some embodiments, the second polypropylene is a second polypropylene homopolymer. In some embodiments, the second polypropylene is a second polypropylene copolymer. In some embodiments, the second polypropylene is a second high melt-strength polypropylene. It is within the scope of the present disclosure to select an amount of the second polymer of the base resin blend to be one of the following values: about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 11%, about 12%, about 13%, about 14%, about 15%, about 20%, about 25%, about 30%, about 35%, about 36%, about 37%, about 38%, about 39%, about 40%, about 41%, about 42%, about 43%, about 44%, about 45%, about 50%, or about 60% by weight of the base resin blend. It is within the present disclosure for an amount of the second polymer of the base resin blend to fall within one of many different ranges. In a first set of ranges, the range of base resin is one of the following ranges: about 1% to about 60%, about 1% to about 50%, about 1% to about 40%, about 1% to about 30%, about 1% to about 25%, about 1% to about 20%, about 1% to about 15%, about 1% to about 10%, or about 1% to about 5% by weight of the base resin blend. In a second set of ranges, the range of the second polymer of the base resin blend is one of the following ranges: about 1% to about 50%, about 10% to about 60%, about 15% to about 60%, about 20% to about 60%, about 30% to about 60%, about 35% to about 60%, or about 40% to about 60% by weight of the base resin blend. In a third set of ranges, the range of second polymer of the base resin blend is one of the following ranges: about 2% to about 60%, about 2% to about 50%, about 10% to about 50%, about 15% to about 50%, about 20% to about 50%, about 25% to about 50%, about 25% to about 45%, about 2% to about 40%, about 2% to about 30%, about 4% to about 30%, about 4% to about 25%, about 4% to about 20%, about 5% to about 20%, about 5% to about 20%, or about 5% to about 15% by weight of the base resin blend. In an embodiment, the base resin blend lacks a second polymer. In a particular embodiment, a second polypropylene can be a high crystalline polypropylene homopolymer, such as F020HC (available from Braskem) or PP 527K (available from Sabic). In some embodiments, the second polypropylene is MFX6 available from JPP. In an embodiment, a polymeric material lacks a secondary polymer.
In illustrative embodiments, the base resin blend includes a third polymer. In some embodiments, the third polymer is a polyethylene. In some embodiments, the third polymer is a polypropylene. In some embodiments, the third polypropylene is a polypropylene homopolymer. In some embodiments, the third polypropylene is a polypropylene copolymer. In some embodiments, the third polypropylene is a high crystallinity polypropylene copolymer. It is within the scope of the present disclosure to select an amount of the third polymer of the base resin blend to be one of the following values: about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 11%, about 12%, about 13%, about 14%, about 15%, about 20%, about 25%, about 30%, or about 35% by weight of the base resin blend. It is within the present disclosure for an amount of the third polymer of the base resin blend to fall within one of many different ranges. In a first set of ranges, the range of base resin is one of the following ranges: about 1% to about 35%, about 1% to about 30%, about 1% to about 25%, about 1% to about 20%, about 1% to about 15%, about 1% to about 10%, or about 1% to about 8% by weight of the base resin blend. In a second set of ranges, the range of the third polymer of the base resin blend is one of the following ranges: about 2% to about 35%, about 3% to about 35%, about 4% to about 35%, about 5% to about 35%, about 6% to about 35%, about 7% to about 35%, or about 8% to about 35% by weight of the base resin blend. In a third set of ranges, the range of third polymer of the base resin blend is one of the following ranges: about 1% to about 25%, about 2% to about 25%, about 2% to about 20%, about 3% to about 20%, about 4% to about 20%, about 4% to about 15%, about 5% to about 15%, or about 5% to about 10% by weight of the base resin blend. In an embodiment, the base resin blend lacks a third polymer. In a particular embodiment, the third polymer can be a high crystalline polypropylene. In some embodiments, the high crystalline homopolymer is F020HC (available from Braskem) or PP 527K (available from Sabic). In some embodiments, the high crystalline polypropylene is a copolymer, such as TI215OC from Braskem.
In some embodiments, the polymeric formulation comprises regrind. Regrind may be formed by recovering the excess material, sometimes called a blank-carrier sheet 94, produced during a blank forming step 500, as shown in
In some embodiments, regrind comprises ink. In some embodiments, the ink is from ink layer 66. In some embodiments, regrind is substantially free of ink. In some embodiments, the regrind comprises polypropylene, polyethylene, a physical nucleating agent, a slip agent, or a combination thereof. Illustratively, regrind is substantially free of an adhesive. In some embodiments, regrind is substantially free of an epoxy. In some embodiments, regrind comprises polypropylene, polyethylene, and bi-axially oriented polypropylene (BOPP).
As described above, in some embodiments, regrind is substantially free of an adhesive. Illustratively, adhesives may present issues when included in regrind used in materials that contact food products. Illustrative adhesives include epoxies, urethanes, acrylates, maleimides or any suitable alternative. In some embodiments, regrind substantially free of an adhesive may be reincorporated back into insulative cellular non-aromatic polymeric material 82. Accordingly, the process as suggested in
It was also surprisingly found that including regrind into the formulation for insulative cellular non-aromatic polymeric material 82 had minimal negative effects on performance. As shown below in the Examples, regrind has lower melt strength that virgin resin. In particular, regrind had an average load at break of less than about 0.1 N. In some embodiments, the average load at break of the regrind may be less than 0.3 N, less than about 0.2 N, or less than about 0.1 N. In contrast, the tested virgin materials had an average load at break of at least 0.4 N. In some embodiments, the virgin materials may have an average load at break of at least 0.35 N, at least about 0.4 N, or at least about 0.45 N. Illustratively, a ratio of the average load at break for the virgin material compared to the regrind may be at about 1:1, about 2:1, about 3:1, about 4:1, or about 5:1. Accordingly, maintaining the properties of the foam when substituting regrind for virgin resin allows for improved efficiency and minimizes waste.
It is within the scope of the present disclosure to select an amount of regrind to be up to about 5%, up to about 10%, up to about 15%, up to about 20%, up to about 25%, up to about 30%, up to about 35%, up to about 40%, up to about 45%, up to about 50%, up to about 55%, up to about 60%, up to about 65%, up to about 75%, up to about 85%, or up to about 95% by weight of the polymeric formulation. The percentage by weight of regrind in the polymeric formulation may be about 0%, about 0.5%, about 1%, about 3%, about 4%, about 5%, about 7%, about 10%, about 15%, about 20%, about 21%, about 22%, about 23%, about 24%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, about 90%, or about 95% by weight of the polymeric formulation. In a first set of ranges, the range of a regrind in the polymeric formulation is one of the following ranges: about 0.5% to about 95%, about 3% to about 95%, about 5% to about 95%, about 10% to about 95%, about 15% to about 95%, about 20% to about 95%, about 25% to about 95%, about 30% to about 40% to about 95%, about 50% to about 95%, about 60% to about 95%, about 75% to about 95%, or about 85% to about 95% by weight of the polymeric formulation. In a second set of ranges, the range of regrind in the polymeric formulation is one of the following ranges: about 0.5% to about 90%, about 0.5% to about 85%, about 0.5% to about 75%, about 0.5% to about 60%, about 0.5% to about 50%, about 0.5% to about 45%, about 0.5% to about 40%, about 0.5% to about 35%, about 0.5% to about 30%, about 0.5% to about 25%, about 0.5% to about 20%, about 0.5% to about 15%, or about 0.5% to about 10% by weight of the polymeric formulation. In a third set of ranges, the range of regrind in the polymeric formulation is one of the following ranges: about 1% to about 90%, about 1% to about 85%, about 1% to about 75%, about 1% to about 50%, about 3% to about 50%, about 3% to about 45%, about 5% to about 45%, about 5% to about 40%, about 5% to about 35%, about 10% to about 40%, about 10% to about 35%, about 10% to about 45%, about 20% to about 45%, about 5% to about 40%, about 5% to about 30%, about 15% to about 30%, about 15% to about 25%, or about 30% to about 40% by weight of the polymeric formulation.
In some embodiments, one or more nucleating agents are used to provide and control nucleation sites to promote the formation of cells, bubbles, or voids in the molten resin during the extrusion process. A nucleating agent can be a chemical or physical material that provides sites, i.e., nucleation sites, for cells to form in a molten resin mixture. Nucleating agents may be physical agents or chemical agents. When a suitable temperature is reached, the nucleating agent acts to enable the formation of gas bubbles that create cells in the molten resin. In some embodiments, the polymeric formulation lacks a nucleating agent. In some embodiments, the polymeric formulation does not include a chemical nucleating agent, a physical nucleating agent, or both.
Suitable physical nucleating agents have a desirable particle size, aspect ratio, top-cut properties, shape, and surface compatibility. Examples include, but are not limited to, talc, CaCO3, mica, kaolin clay, chitin, aluminosilicates, graphite, cellulose, and mixtures of at least two of the foregoing. The nucleating agent may be blended with the base resin blend that is introduced into hopper 113. Alternatively, the nucleating agent may be added to the molten resin mixture in an extruder 111, 111A, 111B.
After decomposition, the chemical nucleating agent forms small gas cells, which further serve as nucleation sites for larger cell growth from physical blowing agents or other types thereof. An illustrative example of a chemical nucleating agent is citric acid or a citric acid-based material. One representative example is Hydrocerol® CF-40E™ (available from Clariant Corporation), which contains citric acid and a crystal nucleating agent. Another representative example is Hydrocerol® CF-05E™ (available from Clariant Corporation), which contains citric acid and a crystal nucleating agent. In illustrative embodiments, one or more catalysts or other reactants may be added to accelerate or facilitate the formation of cells.
As described herein, the polymeric formulation may comprise a physical nucleating agent, a chemical nucleating agent, or both. In some embodiments, the nucleating agent is up to about 1%, up to about 3%, up to about 5%, up to about 7%, or up to about 10% by weight of the polymeric formulation. It is within the scope of the present disclosure to select an amount of a nucleating agent to be one of the following values: about 0%, about 0.5%, about 1%, about 1.5%, about 2%, about 2.5%, about 3%, about 4%, and about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 12%, or about 14% by weight of the total formulation of the polymeric layer. It is also within the scope of the present disclosure for the weight percentage (w/w) of a nucleating agent to fall within one of many different ranges. In a first set of ranges, the weight percentage of a nucleating agent is one of the following ranges: about 0.1% to about 20% (w/w), about 0.25% to about 20%, about 0.5% to about 20%, about 0.75% to about 20%, about 1% to about 20%, about 1.5% to about 20%, about 2% to about 20%, about 2.5% to about 20%, about 3% to about 20%, about 4% to about 20%, about 4.5% to about 20%, and about 5% to about 20%. In a second set of ranges, the range of a nucleating agent is one of the following ranges: about 0.1% to about 10%, about 0.25% to about 10%, about 0.5% to about 10%, about 0.75% to about 10%, about 1% to about 10%, about 1.5% to about 10%, about 2% to about 10%, about 3% to about 10%, about 4% to about 10%, and about 5% to about 10% of the total formulation of the polymeric layer by weight percentage. In a third set of ranges, the range of a nucleating agent is one of the following ranges: about 0.1% to about 5%, about 0.25% to about 5%, about 0.5% to about 5%, about 0.75% to about 5%, about 1% to about 5%, about 1.5% to about 5%, about 2% to about 5%, about 2.5% to about 5%, about 3% to about 5%, about 3.5% to about 5%, about 4% to about 5%, and about 4.5% to about 5% of the total formulation of the polymeric layer by weight percentage. The nucleating agent may be up to about 5%, up to about 10%, up to about 15%, up to about 20% by weight of the polymeric formulation. In an embodiment, the polymeric formulation lacks a nucleating agent.
In certain exemplary embodiments, one or more blowing agents may be incorporated. Blowing agent may be either a physical or a chemical material (or a combination of materials) that acts to expand nucleation sites. Illustratively, nucleating agents and blowing agents may work together to control the size and or quality of the formed cell. The blowing agent acts to reduce density by forming cells in the molten resin. The blowing agent may be added to the molten resin mixture in an extruder through a physical blowing agent port.
In exemplary embodiments, physical blowing agents are typically gasses that are introduced as liquids under pressure into the molten resin via a port in the extruder as suggested in
Illustrative physical blowing agents include agents that are gasses. Representative examples of physical blowing agents include, but are not limited to, carbon dioxide, nitrogen, helium, argon, air, water vapor, pentane, butane, other alkane mixtures of the foregoing and the like. In some embodiments, a physical blowing agent can be selected from the group consisting of carbon dioxide, nitrogen, helium, argon, methane, pentane, butane, ethane, propane, n-butane, isobutene, n-pentane, isopentane, neopentane, methyl fluoride, perfluoromethane, ethyl fluoride, 1,1-difluoroethane, 1,1,1-trifluoroethane, 1,1,1,2-tetrafluoro-ethane, pentafluoroethane, perfluoroethane, 2,2-difluoropropane, 1,1,1-trifluoropropane, perfluoropropane, perfluorobutane, perfluorocyclobutane, methyl chloride, methylene chloride, ethyl chloride, 1,1,1-trichloroethane, 1,1-dichloro-1-fluoroethane, 1-chloro-1,1-difluoroethane, 1,1-dichloro-2,2,2-trifluoroethane, 1-chloro-1,2,2,2-tetrafluoroethane, trichloromonofluoromethane, dichlorodifluoromethane, trichlorotrifluoroethane, dichlorotetrafluoroethane, chloroheptafluoropropane, dichlorohexafluoropropane, methanol, ethanol, n-propanol, and isopropanol. In certain exemplary embodiments, a processing aid may be added to the formulation to enhance the solubility of the physical blowing agent. Alternatively, the physical blowing agent may be a hydrofluorocarbon, such as 1,1,1,2-tetrafluoroethane, also known as R134a, a hydrofluoroolefin, such as, but not limited to, 1,3,3,3-tetrafluoropropene, also known as HFO-1234ze, or other haloalkane or haloalkane refrigerant. Selection of the blowing agent may be made to consider environmental impact.
One example of a physical blowing agent is nitrogen (N2). The N2 is pumped as a supercritical fluid into the molten formulation via a port in the extruder. The molten material with the N2 in suspension then exits the extruder via a die where a pressure drop occurs. As the pressure drop happens, N2 moves out of suspension toward the nucleation sites where cells grow. Excess gas blows off after extrusion with the remaining gas trapped in the cells formed in the extrudate. Other suitable examples of physical blowing agents include, but are not limited to, carbon dioxide (CO2), helium, argon, air, pentane, butane, or other alkane mixtures of the foregoing and the like.
In an illustrative example, a physical blowing agent may be introduced at a rate of about 0.02 pounds per hour (lbs/h) to about 1.3 (lbs/h). In another illustrative example, the physical blowing agent may be introduced at a rate of about 0.03 (lbs/h) to about 1.25 (lbs/h). In another illustrative example, the physical blowing agent may be introduced at a rate of about 0.02 (lbs/h) to about 0.15 (lbs/h). In another illustrative example, the physical blowing agent may be introduced at a rate of about 0 (lbs/h) to about 0.15 (lbs/h). In another illustrative example, the physical blowing agent may be introduced at a rate of about 0.02 (lbs/h) to about 0.22 (lbs/h). In another illustrative example, the physical blowing agent may be introduced at a rate of about 0.02 (lbs/h) to about 0.25 (lbs/h). In still yet another illustrative example the physical blowing agent may be introduced at a rate of about 0.07 (lbs/h) to about 0.27 (lbs/h). In some embodiments, the physical blowing agent is used between about 0.01 lbs/h to about 0.2 lbs/h, about 0.01 lbs/h to about 0.17 lbs/h, about 0.01 lbs/h to about 0.15 lbs/h, about 0.01 lbs/h to about 0.1 lbs/h, about 0.05 lbs/h to about 0.2 lbs/h, about 0.05 lbs/h to about 0.17 lbs/h, about 0.05 lbs/h to about 0.15 lbs/h, about 0.05 lbs/h to about 0.1 lbs/h, about 0.1 lbs/h to about 0.2 lbs/h, about 0.1 lbs/h to about 0.17 lbs/h, or about 0.1 lbs/h to about 0.15 lbs/h.
In further embodiments, the physical blowing agent is measured in saturation percentage (%). In exemplary embodiments, physical blowing agent saturation can have a range that is about 0.1% to about 0.4%, about 0.1% to about 0.35%, about 0.1% to about 0.3%, about 0.1% to about 0.25%, 0.15% to about 0.4%, about 0.15% to about 0.35%, about 0.15% to about 0.3%, about 0.15% to about 0.25%, 0.2% to about 0.4%, about 0.2% to about 0.35%, about 0.2% to about 0.3%, or about 0.2% to about 0.25%.
Chemical blowing agents are materials that degrade or react to produce a gas. Chemical blowing agents may be endothermic or exothermic. Chemical blowing agents typically degrade at a certain temperature to decompose and release gas. In one aspect the chemical blowing agent may be one or more materials selected from the group consisting of azodicarbonamide, azodiisobutyro-nitrile, benzenesulfonyl hydrazide, 4,4-oxybenzene sulfonylsemicarbazide, p-toluene sulfonyl semi-carbazide, barium azodicarboxylate, N,N′-dimethyl-N,N′-dinitrosoterephthalamide, trihydrazino triazine, sodium bicarbonate, sodium carbonate, ammonium bicarbonate, ammonium carbonate, ammonium nitrite, N,N′-dinitrosopentamethylene tetramine, azobisisobutylonitrile, azocyclohexylnitrile, azodiaminobenzene, toluene sulfonyl hydrazide, p,p′-oxybis(benzene sulfonyl hydrazide), diphenyl sulfone-3,3′-disulfonyl hydrazide, calcium azide, 4,4′-diphenyl disulfonyl azide, and p-toluene sulfonyl azide. In some embodiments, the chemical blowing agent is Hydrocerol™ CF®-40E available from Clariant. In some embodiments, the chemical blowing agent is Ecocell® P available from the Polyfil Corporation.
The amount of a chemical blowing agent may be one of several different values or fall within one of several different ranges. It is within the scope of the present disclosure to select an amount of a chemical blowing agent to be one of the following values: about 0%, about 0.1%, about 0.2%, about 0.3%, about 0.4%, about 0.5%, about 0.75%, about 1%, about 1.5%, or about 2% of the total formulation of the polymeric layer by weight percentage. It is within the scope of the present disclosure for the amount of a chemical blowing agent in the formulation to fall within one of many different ranges. In a first set of ranges, the range of a chemical blowing agent is one of the following ranges: about 0% to about 5%, about 0.1% to about 5%, about 0.25% to about 5%, about 0.5% to about 5%, about 0.75% to about 5%, about 1% to about 5%, about 1.5% to about 5%, about 2% to about 5%, about 3% to about 5%, and about 4% to about 5% of the total formulation of the polymeric layer by weight percentage. In a second set of ranges, the range of a chemical blowing agent is one of the following ranges: about 0.1% to about 4%, about 0.1% to about 3%, about 0.1% to about 2%, and about 0.1% to about 1% of the total formulation by weight percentage. In a third set of ranges, the range of a chemical blowing agent is one of the following ranges: about 0.25% to about 4%, about 0.75% to about 4%, about 1% to about 4%, about 1.5% to about 4%, about 2% to about 4%, about 3% to about 4%, about 0% to about 3%, about 0.25% to about 3%, about 0.5% to about 3%, about 0.75% to about 3%, about 1% to about 3%, about 1.5%, to about 3%, about 2% to about 3%, about 0% to about 2%, about 0.25% to about 2%, about 0.5%, to about 2%, about 0.75% to about 2%, about 1% to about 2%, about 1.5% to about 2%, about 0% to about 1%, about 0.5% to about 1%, and about 0.75% to about 1% of the total formulation of the polymeric layer by weight percentage. In one aspect of the present disclosure, where a chemical blowing agent is used, the chemical blowing agent may be introduced into the material formulation that is added to the hopper.
In one aspect of the present disclosure, the chemical blowing agent may be a decomposable material that forms a gas upon decomposition. A representative example of such a material is citric acid or a citric-acid based material. In one exemplary aspect of the present disclosure, it may be possible to use a mixture of physical and chemical blowing agents.
In one aspect of the present disclosure, at least one slip agent may be incorporated into the resin mixture to aid in increasing production rates. Slip agent (also known as a process aid) is a term used to describe a general class of materials, which are added to a resin mixture and provide surface lubrication to the polymer during and after conversion. Slip agents may also reduce or eliminate die drool. Representative examples of slip agent materials include amides of fats or fatty acids, such as, but not limited to, erucamide and oleamide. In one exemplary aspect, amides from oleyl (single unsaturated C18) through erucyl (C22 single unsaturated) may be used. Other representative examples of slip agent materials include low molecular weight amides and fluoroelastomers. Combinations of two or more slip agents can be used. Slip agents may be provided in a master batch pellet form and blended with the resin formulation. One example of a slip agent that is commercially available as AMPACET™ 102109 Slip PE MB. Another example of a slip agent that is commercially available is AMAPACET™ 102823 Process Aid PE MB. In some embodiments, the insulative cellular non-aromatic polymeric material lacks a process aid.
The amount of a slip agent may be one of several different values or fall within one of several different ranges. It is within the scope of the present disclosure to select an amount of a slip agent to be one of the following values: about 0%, about 0.1%, about 0.2%, about 0.3%, about 0.4%, about 0.5%, 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, or about 10% of the total formulation of the polymeric layer by weight percentage. It is within the scope of the present disclosure for the amount of a slip agent in the formulation to fall within one of many different ranges. In a first set of ranges, the range of a slip agent is one of the following ranges: about 0% to about 10% (w/w), about 0.1% to about 50%, about 0.3% to about 10%, about 0.5% to about 10%, about 1% to about 10%, about 2% to about 10%, about 3% to about 10%, about 4% to about 10%, about 5% to about 10%, about 6% to about 10%, about 7% to about 10%, about 8% to about 10%, and about 9% to about 10% of the total formulation of the polymeric layer by weight percentage. In a second set of ranges, the range of a slip agent is one of the following ranges: about 0% to about 9%, about 0% to about 8%, about 0% to about 7%, about 0% to about 6%, about 0% to about 5%, about 0% to about 4%, about 0% to about 3%, about 0% to about 2%, about 0% to about 1%, and about 0% to about 0.5% of the total formulation of the polymeric layer by weight percentage. In a third set of ranges, the range of a slip agent is one of the following ranges: about 0.1% to about 5%, about 0.1% to about 3%, about 0.1% to about 2%, about 0.1% to about 1%, about 0.1% to about 0.5%, about 0.5% to about 5%, about 0.5% to about 4%, about 0.5% to about 3%, about 0.5%, to about 2%, about 1% to about 2%, about 1% to about 3%, about 1% to about 4%, about 1% to about 5%, about 2% to about 3%, about 2% to about 4%, and about 2% to about 5% of the total formulation by weight percentage. In an embodiment, the polymeric formulation lacks a slip agent.
One or more additional components and additives optionally may be incorporated, such as, but not limited to, anti-oxidants, impact modifiers, and colorants (such as, but not limited to, titanium dioxide). One example of a commercially available colorant is COLORTECH® blue-white colorant. Another example of a commercially available colorant is COLORTECH® J11 white colorant.
The amount of a colorant may be one of several different values or fall within one of several different ranges. It is within the scope of the present disclosure to select an amount of a colorant to be one of the following values: about 0%, about 0.1%, about 0.5%, about 0.6%, about 0.7%, about 0.8%, about 0.9%, about 1%, about 1.5%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, 1 about 0%, about 15%, or about 20% of the total formulation of the polymeric layer by weight percentage. It is within the scope of the present disclosure for the amount of a colorant in the formulation to fall within one of many different ranges. In a first set of ranges, the range of a colorant is one of the following ranges: about 0% to about 20% (w/w), about 0% to about 10%, about 0% to about 5%, and about 0% to about 4%. In a second set of ranges, the range of a colorant is one of the following ranges: about 0.1% to about 4%, about 0.25% to about 4%, about 0.5% to about 4%, about 0.75% to about 4%, about 1% to about 4%, about 1.5% to about 4%, about 2% to about 4%, about 2.5% to about 4%, and about 3% to about 4% of the total formulation of the polymeric layer by weight percentage. In a third set of ranges, the range of a colorant is one of the following ranges: about 0% to about 3%, about 0% to about 2.5%, about 0% to about 2.25%, about 0% to about 2%, about 0% to about 1.5%, about 0% to about 1%, about 0% to about 0.5%, about 0.1% to about 3.5%, about 0.1% to about 3%, about 0.1% to about 2.5%, about 0.1% to about 2%, about 0.1% to about 1.5%, about 0.1% to about 1%, about 1% to about 5%, about 1% to about 10%, about 1% to about 15%, about 1% to about 20%, and about 0.1% to about 0.5% of the total formulation by weight percentage. In an embodiment, the formulation lacks a colorant.
As described herein, a polymeric formulation, sometimes illustrated as polymeric formulation as in
The insulative cellular non-aromatic polymeric material that forms insulative cellular non-aromatic polymeric material strip 82 has a density that is generally lower than a non-foamed equivalent material. It is within the scope of the present disclosure that the density of the extruded insulative cellular non-aromatic material be up to about 0.25 g/cm3, up to about 0.2 g/cm3, up to about 0.18 g/cm3, up to about 0.16 g/cm3, up to about 0.14 g/cm3, up to about 0.13 g/cm3, or up to about 0.12 g/cm3. In some embodiments, the density of the polymeric material is less than about 0.2 g/cm3, less than about 0.18 g/cm3, less than about 0.16 g/cm3, less than about 0.15 g/cm3, less than about 0.14 g/cm3, or less than about 0.13 g/cm3. The density of the insulative-cellular non-aromatic polymeric material may be about 0.01 g/cm3, about 0.03 g/cm3, about 0.05 g/cm3, about 0.06 g/cm3, about 0.07 g/cm3, about 0.08 g/cm3, about 0.09 g/cm3, about 0.1 g/cm3, about 0.11 g/cm3, about 0.12 g/cm3, about 0.13 g/cm3, about 0.14 g/cm3, about 0.15 g/cm3, about 0.16 g/cm3, about 0.18 g/cm3, about 0.2 g/cm3, or about 0.25 g/cm3. In a first set of ranges, the density of the insulative cellular non-aromatic polymeric material is one of the following ranges: about 0.01 g/cm3 to about 0.2 g/cm3, about 0.05 g/cm3 to about 0.25 g/cm3, about 0.05 g/cm3 to about 0.2 g/cm3, about 0.05 g/cm3 to about 0.19 g/cm3, about 0.07 g/cm3 to about 0.2 g/cm3, about 0.08 g/cm3 to about 0.2 g/cm3, about 0.09 g/cm3 to about 0.2 g/cm3, about 0.1 g/cm3 to about 0.2 g/cm3, about 0.11 g/cm3 to about 0.2 g/cm3, or about 0.12 g/cm3 to about 0.2 g/cm3. In a second set of ranges, the density of the insulative cellular non-aromatic polymeric material is one of the following ranges: about 0.06 g/cm3 to about 0.25 g/cm3, about 0.06 g/cm3 to about 0.2 g/cm3, about 0.06 g/cm3 to about 0.18 g/cm3, about 0.06 g/cm3 to about 0.16 g/cm3, about 0.06 g/cm3 to about 0.14 g/cm3, or about 0.06 g/cm3 to about 0.12 g/cm3. In a third set of ranges, the density of the insulative cellular non-aromatic polymeric material is one of the following ranges: about 0.05 g/cm3 to about 0.2 g/cm3, about 0.05 g/cm3 to about 0.15 g/cm3, about 0.07 g/cm3 to about 0.15 g/cm3, about 0.09 g/cm3 to about 0.15 g/cm3, about 0.11 g/cm3 to about 0.15 g/cm3, about 0.08 g/cm3 to about 0.2 g/cm3, about 0.08 g/cm3 to about 0.18 g/cm3, about 0.08 g/cm3 to about 0.16 g/cm3, about 0.08 g/cm3 to about 0.14 g/cm3, about 0.09 g/cm3 to about 0.14 g/cm3, about 0.09 g/cm3 to about 0.13 g/cm3, about 0.1 g/cm3 to about 0.14 g/cm3, or about 0.1 g/cm3 to about 0.12 g/cm3.
The insulative cellular non-aromatic polymeric material that forms insulative cellular non-aromatic polymeric material strip 82 has a thickness that is generally greater than a non-foamed equivalent material. It is within the scope of the present disclosure that the thickness of the extruded insulative cellular non-aromatic material be less than about 0.254 centimeter (about 0.1 inches), less than about 0.203 centimeter (about 0.08 inches), less than about 0.178 centimeter (about 0.07 inches), or less than about 0.152 centimeter (about 0.06 inches). In some embodiments, the thickness of the insulative cellular non-aromatic polymeric material is at least 0.0254 centimeter (0.01 inches), at least 0.0762 centimeter (0.03 inches) or higher, or at least 0.102 centimeter (0.04 inches).
Illustratively, the insulative cellular non-aromatic polymeric material is a polymeric material comprising cells. In illustrative embodiments, the cell morphology of an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure is a function of formulation and process conditions, which conditions have an effect on the quality of an article, such as an insulative container, formed therewith. In particular, the effects of such conditions on cell density and cell dimensional attributes, and ultimately on crease/wrinkle resistance, results in a wrinkle-resistance prediction model based on power law regression.
In illustrative embodiments, the cell aspect ratio of an extruded sheet of insulative cellular polypropylene-based material in accordance with the present disclosure has an effect on the wrinkle resistance of that material during mechanical convolution. Parameters such as cell density and aspect ratio contribute to the control limits that result in a wrinkle-resistance model for the extruded sheet.
Direct evidence of polymer cell structure is provided by microscopy studies. There is a close relationship between the regularity of molecular structure and malleability. Cell morphology describes polymer cell density, cell structure, cell wall thickness, cell shape, and cell size distribution of cells. Polymer cell structures may have the same general shape and appearance, being composed predominantly of oval cells, and the same lognormal cell distribution, but possess a different cell aspect ratio and cell wall thickness. Illustratively, cell aspect ratio is the ratio between lengths of the ovular polymer cells to widths of the ovular polymer cells. In some embodiments, the cell aspect ratio of the insulative cellular non-aromatic polymeric material is at least 0.5, at least 1, at least 1.1, at least 1.2, at least 1.5, at least 1.7, or at least 2. In some embodiments, the cell aspect ratio of the cells of the insulative cellular non-aromatic polymeric material is less than 7, less than 6, less than 4, less than 3.5, less than 3, less than 2.5, or less than 2. In some embodiments, the aspect ratio of the cells of the insulative cellular non-aromatic polymeric material is selected from a range of 0.5 to about 4, about 1 to about 4, about 1 to about 3.5, about 1 to about 3, or about 1 to about 2.
Illustratively, the polymer cells can have a cell aspect ratio in the machine direction (MD) and in the cross direction (CD). As confirmed by microscopy, in one exemplary embodiment the average cell dimensions in a machine direction (machine or along the web direction) of an extruded strip 82 of insulative cellular non-aromatic polymeric material were about 0.0362 inches (0.92 mm) in width by about 0.0106 inches (0.27 mm) in height. As a result, a machine direction cell size aspect ratio is about 3.5. The average cell dimensions in a cross direction (cross-web or transverse direction) was about 0.0205 inches (0.52 mm) in width and about 0.0106 inches (0.27 mm) in height. As a result, a cross-direction aspect ratio is 1.94. In one exemplary embodiment, it was found that for the strip to withstand a compressive force during cup forming, one desirable average cell aspect ratio was between about 1.0 and about 3.0. In one exemplary embodiment, one desirable average cell aspect ratio was between about 1.0 and about 2.0. In another exemplary embodiment, the average cell aspect ratio is between about 2 and about 3. In another exemplary embodiment, a desirable average cell aspect ratio in the cross direction was about 0.5 to about 4. In another exemplary embodiment, a desirable average cell aspect ratio in the machine direction was about 1 to about 7.
In some embodiments, the polymeric material has a certain percentage of closed cells, sometimes called a closed cell performance. In some embodiments, the percentage of closed cells is up to about 100%. In some embodiments, the percentage of closed cells is at least about 20%, at least 40%, at least 60%, at least 70%, or at least 80%. In some embodiments, the percentage of closed cells is about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 81%, about 82%, about 83%, about 84%, about 85%, about 86%, about 87%, about 88%, about 90%, about 95%, or about 99%. In some embodiments, the percentage of closed cells is about 20% to about 100%, about 30% to about 100%, about 35% to about 95%, about 40% to about 95%, about 50% to about 95%, about 55% to about 95%, about 65% to about 95%, about 70% to about 95%, about 80% to about 95%, or about 80% to about 90%.
The insulative cellular non-aromatic polymeric material may have a certain number of cells per unit area. In some embodiments, the insulative-cellular non-aromatic polymeric materials in accordance with the present disclosure may have a cell density of about 1×105 to about 2.5×106 cells/in3. In some embodiments, the cell density is at least 1×105 cells/in3, at least 2×105 cells/in3, at least 3×105 cells/in3, at least 5×105 cells/in3, or at least 6×105 cells/in3. In some embodiments, the cell density falls within a range of about 1×105 cells/in3 to about 2.5×106 cells/in3, about 2×105 cells/in3 to about 2.5×106 cells/in3, about 4×105 cells/in3 to about 2.5×106 cells/in3, about 4×105 cells/in3 to about 1.5×106 cells/in3, about 5×105 cells/in3 to about 1.5×106 cells/in3, about 5×105 cells/in3 to about 1×106 cells/in3, or about 6×105 cells/in3 to about 1×106 cells/in3.
The ratio of machine direction to cross direction cell length is used as a measure of anisotropy of the extruded strip. In exemplary embodiments, a strip of insulative cellular non-aromatic polymeric material may be bi-axially oriented, with a coefficient of anisotropy ranging between about 1.5 and about 3. In one exemplary embodiment, the coefficient of anisotropy was about 1.8.
If the circumference of the cup is aligned with machine direction of extruded strip 82 with a cell aspect ratio exceeding about 3.0, deep creases with a depth exceeding about 200 microns are typically formed on inside surface of the cup making it unusable. Unexpectedly, it was found, in one exemplary embodiment, that if the circumference of the cup was aligned can be characterized by cell aspect ratio below about 2.0, no deep creases were formed inside of the cup, indicating that the cross direction of extruded strip 82 was more resistant to compression forces during cup formation.
The formulation and insulative cellular non-aromatic polymeric material of the present disclosure satisfies a long-felt need for a material that can be formed into an article, such as a cup, that includes many if not all of the features of insulative performance, ready for recyclability, puncture resistance, frangibility resistance, microwavability, regrindability, and other features as discussed herein. Others have failed to provide a material that achieves combinations of these features as reflected in the appended claims. This failure is a result of the features being associated with competitive design choices. As an example, others have created materials and structures therefrom that based on design choices are insulated but suffer from poor puncture resistance, inability to effectively be recyclable, inability to be used reground, and lack microwavability. In comparison, the formulations and materials disclosed herein overcome the failures of others by using an insulative cellular non-aromatic polymeric material. Reference is hereby made to U.S. application Ser. No. 13/491,007 filed Jun. 7, 2012, and entitled INSULATED CONTAINER for disclosure relating to articles, such as cups, formed from such insulative cellular non-aromatic polymeric materials, which application is hereby incorporated in its entirety herein.
Reference is hereby made to U.S. application Ser. No. 14/462,073 filed Aug. 18, 2014, and entitled POLYMERIC MATERIAL FOR AN INSULATED CONTAINER for disclosure relating to insulative cellular non-aromatic polymeric materials, which application is hereby incorporated in its entirety herein
In some illustrative embodiments, polymeric-lamination layer 54 extends between and interconnects film layer 56 and insulative cellular non-aromatic polymeric material 82 as shown in
In some embodiments, polymeric-lamination layer 54 is substantially free of an adhesive. In some embodiments, polymeric-lamination layer 54 is substantially free of an epoxy. In some embodiments, polymeric-lamination layer 54 is substantially free of ink. In some other embodiments, polymeric-lamination layer 54 comprises ink. In some embodiments, polymeric-lamination layer 54 comprises regrind, a polypropylene, a polyethylene, a colorant, or a mixture or combination thereof. In some embodiments, polymeric-lamination layer 54 consists of regrind.
Polymeric-lamination layer 54 is formed by extruding a polymeric formulation. It is within the scope of the present disclosure for the polymeric formulation to have a melt flow index at 230° C. of at least 5 g/10 min, at least 10 g/10 min, at least 15 g/10 min, at least 20 g/10 min, or at least 25 g/10 min. It is within the scope of the present disclosure to prepare a formulation that has a melt flow rate at 230° C. in a range of about 5 g/10 min to about 55 g/10 min, about 15 g/10 min to about 55 g/10 min, about 35 g/10 min to about 55 g/10 min, about 5 g/10 min to about 45 g/10 min, about 5 g/10 min to about 35 g/10 min, about 10 g/10 min to about 35 g/10 min, about 15 g/10 min to about 35 g/10 min, or about 20 g/10 min to about 35 g/10 min.
Polymeric-lamination layer 54 extends between and interconnects strip 82 of insulative cellular non-aromatic polymeric material and film layer 56 as shown in
In some embodiments, the polymeric formulation for polymeric-lamination layer 54 comprises a polypropylene. In some embodiments, the polypropylene is a polypropylene homopolymer. In some embodiments, the polypropylene is virgin material. In some embodiments, the polypropylene homopolymer is ExxonMobil™ PP3155. In some embodiments, the polypropylene is Flint Hills P9H8M-015. In some embodiments, the melt mass-flow rate at 230° C. as measured using ASTM D1238 for the polypropylene is at least 25 g/10 min, at least 30 g/10 min, or at least 35 g/10 min. In some embodiments, the melt mass-flow rate at 230° C. for the polypropylene is less than 60 g/10 min, less than 50 g/10 min, less than about 45 g/10 min, or less than about 40 g/10 min. In some embodiments, the melt mass-flow rate is in a range of about 25 g/10 min to about 50 g/10 min, about 25 g/10 min to about 40 g/10 min, or about 30 g/10 min to about 40 g/10 min. In some embodiments, the melt mass-flow rate at 230° C. is about 36 g/10 min. In some embodiments, the melt mass-flow rate is in a range of about 25 g/10 min to about 60 g/10 min, about 30 g/10 min to about 60 g/10 min, or about 40 g/10 min to about 60 g/10 min. In some embodiments, the melt mass-flow rate at 230° C. is about 53 g/10 min.
It is within the scope of the present disclosure to select an amount of the polypropylene of the polymeric formulation for forming polymeric-lamination layer 54 to be up to about 40%, up to about 50%, up to about 60%, up to about 70%, up to about 75%, up to about 80%, up to about 85%, up to about 90%, or up to about 95% by weight of the polymeric formulation. It is within the scope of the present disclosure to select an amount of the polypropylene of the polymeric formulation for forming polymeric-lamination layer 54 to be one of the following values: about 10%, about 20%, about 30%, about 40%, about 42%, about 43%, about 44%, about 45%, about 46%, about 47%, about 48%, about 49%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 81%, about 82%, about 83%, about 84%, about 85%, about 86%, about 87%, about 88%, about 89%, about 90%, about 91%, about 92%, about 93%, about 94%, about 95%, about 96%, about 97%, or about 99% by weight of the polymeric formulation. It is within the present disclosure for the amount of the polypropylene of the polypropylene of the polymeric formulation for forming polymeric-lamination layer 54 to fall within one of many different ranges. In a first set of ranges, the range of first polymer in the base resin blend is one of the following ranges: about 40% to about 99%, about 60% to about 99%, about 70% to about 99%, about 75% to about 99%, or about 80% to about 99% by weight of the polymeric formulation. In a second set of ranges, the of the polypropylene of the polymeric formulation for forming polymeric-lamination layer 54 is one of the following ranges: about 40% to about 97%, about 40% to about 95%, about 40% to about 92%, about 40% to about 90%, about 40% to about 70%, about 40% to about 60%, or about 40% to about 50%, by weight of the base resin blend. In a third set of ranges, the polypropylene of the polymeric formulation for forming polymeric-lamination layer 54 is one of the following ranges: about 50% to about 99%, about 50% to about 95%, about 60% to about 95%, about 65% to about 95%, about 65% to about 90%, about 70% to about 90%, about 75% to about 90%, or about 75% to about 85% by weight of the polymeric formulation.
In some embodiments, the polymeric formulation for polymeric-lamination layer 54 comprises a polyethylene. In some embodiments, the polyethylene is a low-density polyethylene. In some embodiments, the low-density polyethylene is Dow™ 4012 low-density polyethylene. In some embodiments, the melt mass-flow rate at 190° C. as measured using ASTM D1238 for the polyethylene is at least 5 g/10 min, at least 10 g/10 min, or at least 12 g/10 min. In some embodiments, the melt mass-flow rate at 190° C. for the polyethylene is less than 30 g/10 min, less than about 25 g/10 min, or less than about 20 g/10 min. In some embodiments, the melt mass-flow rate for the polyethylene is in a range of about 5 g/10 min to about 30 g/10 min, about 5 g/10 min to about 25 g/10 min, or about 5 g/10 min to about 20 g/10 min. In some embodiments, the melt mass-flow rate for the polyethylene at 190° C. is about 12 g/10 min. In some embodiments, the polymeric formulation for polymeric-lamination layer 54 is substantially free of polyethylene.
It is within the scope of the present disclosure to select an amount of the polyethylene of the polymeric formulation for forming polymeric-lamination layer 54 to be up to about 60%, up to about 50%, up to about 40%, up to about 35%, up to about 30%, up to about 25%, up to about 20%, or up to about 15% by weight of the polymeric formulation. It is within the scope of the present disclosure to select an amount of the polyethylene of the polymeric formulation for forming polymeric-lamination layer 54 to be one of the following values: about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 11%, about 12%, about 13%, about 14%, about 15%, about 16%, about 17%, about 18%, about 19%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, or about 60% by weight of the polymeric formulation. It is within the present disclosure for the amount of the polyethylene of the polymeric formulation for forming polymeric-lamination layer 54 to fall within one of many different ranges. In a first set of ranges, the range of the polyethylene of the polymeric formulation for forming polymeric-lamination layer 54 is one of the following ranges: about 1% to about 60%, about 3% to about 60%, about 3% to about 60%, about 5% to about 60%, or about 10% to about 60% by weight of the polymeric formulation. In a second set of ranges, the range of the polyethylene of the polymeric formulation for forming polymeric-lamination layer 54 is one of the following ranges: about 1% to about 55%, about 1% to about 50%, about 1% to about 40%, about 1% to about 30%, or about 10% to about 20% by weight of the polymeric formulation. In a third set of ranges, the range of the polyethylene of the polymeric formulation for forming polymeric-lamination layer 54 is one of the following ranges: about 2% to about 60%, about 2% to about 50%, about 2 to about 40%, about 2% to about 30%, about 5% to about 30%, about 5% to about 25%, about 10% to about 25%, or about 10% to about 20% by weight of the polymeric formulation.
In some embodiments, the polymeric formulation for forming polymeric-lamination layer 54 comprises a colorant. The colorant in the polymeric formulation for forming polymeric-lamination layer 54 can be up to about 25%, up to about 20%, up to about 15%, up to about 10%, or up to about 5% by weight of the polymeric formulation. It is within the scope of the present disclosure to select an amount of the colorant of the polymeric formulation for forming polymeric-lamination layer 54 to be one of the following values: about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 11%, about 12%, about 13%, about 14%, about 15%, about 20%, or about 25% by weight of the polymeric formulation. It is within the present disclosure for the amount of the colorant of the polymeric formulation for forming polymeric-lamination layer 54 to fall within one of many different ranges. In a set of ranges, the range of the colorant of the polymeric formulation for forming polymeric-lamination layer 54 is one of the following ranges: about 1% to about 25%, about 1% to about 15%, about 3% to about 15%, about 3% to about 10%, about 5% to about 15%, or about 5% to about 13% by weight of the polymeric formulation.
In some embodiments, the polymeric formulation for forming polymeric-lamination layer 54 comprises regrind. The regrind in the polymeric formulation for forming polymeric-lamination layer 54 can be up to about 25%, up to about 45%, up to about 60%, up to about 80%, up to about 90%, or up to about 99% by weight of the polymeric formulation. It is within the scope of the present disclosure to select an amount of regrind of the polymeric formulation for forming polymeric-lamination layer 54 to be one of the following values: about 1%, about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 41%, about 42%, about 43%, about 44%, about 45%, about 46%, about 47%, about 48%, about 49%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, about 90%, about 95%, or about 99% by weight of the polymeric formulation. It is within the present disclosure for the amount of regrind of the polymeric formulation for forming polymeric-lamination layer 54 to fall within one of many different ranges. In a set of ranges, the range of regrind of the polymeric formulation for forming polymeric-lamination layer 54 is one of the following ranges: about 1% to about 99%, about 5% to about 99%, about 5% to about 75%, about 15% to about 75%, about 20% to about 70%, about 25% to about 70%, about 25% to about 60%, about 35% to about 60% or about 35% to about 55% by weight of the polymeric formulation. In some embodiments, the ratio of regrind and virgin polymeric resin is about 1:1.
Film layer 56 is laminated onto polymeric-lamination layer 54 as shown in
As shown in
In some embodiments, printed film layer 70 is arranged to form an outer surface 2106 and strip 82 of insulative cellular non-aromatic polymeric material forms an inner surface 2108 as shown in
A cup-manufacturing process 100 comprising a process for forming multi-layer sheet 80 in accordance with the present disclosure is shown, for example, in
Cup-manufacturing process 100 may optionally include each of an extruding stage 300, a laminating stage 400, a blank forming stage 500, a cup-forming stage 700, and a regrinding stage 800, as shown in
Extruding or strip-forming stage 300 provides strip of insulative cellular non-aromatic polymeric material 82 as suggested in
Strip-forming stage 300 incorporates a blender 310 for material blending of the polymeric formulations, as shown in
In one example, an annular die 312 is used to form a tube of expanded polymeric material. A cooling can nose 314 uses air to promote the formation of bubbles, as shown in
A gas, such as, but not limited to, carbon dioxide, nitrogen, other relatively inert gas, a mixture of gasses or the like, is introduced into the molten resin mixture to expand the polypropylene and reduce density by forming cells in the molten polypropylene. R134a or other haloalkane refrigerant may be used with the gas. In one aspect of the present disclosure, the cells formed in the insulative cellular non-aromatic polymeric material may have an average size in a range of about 0.010 to about 0.030 inches.
Printed film layer 70 formed and provided by film forming stage 900, as shown in
Film-layer printing stage 920 uses a printer 64 to print ink layer 66 on film layer 56 to provide printed film layer 70 as shown in
During laminating stage 400, a polymeric-lamination layer 54 is extruded at the junction of strip of insulative cellular non-aromatic polymeric material 82 and printed film layer 70 to form multi-layer sheet 80 as suggested in
In some embodiments, laminating stage 400 orients 412 strip of insulative cellular non-aromatic polymeric material 82 prior to lamination as shown in
Blank forming stage 500 cuts body blanks 92 from multi-layer sheet as shown in
Cup-bottom forming stage 600 forms cup bottom 20, which is combined with blank 92 to form cup 10, as suggested in
Cup-forming process 700 forms cup 10 out of body blank 92 and cup bottom 20 as shown in
Regrinding stage 800 recaptures and processes excess material from extruding stage, laminating stage 400, blank forming stage 500, cup-bottom forming stage 600, cup-forming stage 700, or a combination thereof, to form regrind used for the polymeric formulations in accordance with the present disclosure, as shown in
Insulative cellular non-aromatic material is used during cup-manufacturing process 100 to make insulative cup 10 as suggested in
In some exemplary embodiments, the cell has a length in the cross or transverse direction and a length in the machine direction. In some embodiments, the cell length in the cross direction is up to about 60 mils. In some embodiments, the cell length in the machine direction is up to about 50 mils.
In some exemplary embodiments, the cell has a width in the cross or transverse direction and a width in the machine direction. In some embodiments, the cell width in the cross direction up to about 30 mils. In some embodiments, the cell width in the machine direction is up to about 25 mils.
The ratio of machine direction to cross direction cell length is used as a measure of anisotropy of the extruded strip. In exemplary embodiments, a strip of insulative cellular non-aromatic polymeric material may be bi-axially oriented, with a coefficient of anisotropy ranging between about 1.5 and about 3. In one exemplary embodiment, the coefficient of anisotropy was about 1.8.
In some exemplary embodiments, the polymeric material has a percentage crystallinity at 5° C./min, 10° C./min or 15° C./min. In some exemplary embodiments, the percentage crystallinity at 5° C./min is at least about 15%. In some exemplary embodiments, the percentage crystallinity at 5° C./min is up to about 50%. In some exemplary embodiments, the percentage crystallinity at 10° C./min is at least about 10%. In some exemplary embodiments, the percentage crystallinity at 10° C./min is up to about 60%. In some exemplary embodiments, the percentage crystallinity at 15° C./min is at least about 15%. In some exemplary embodiments, the percentage crystallinity at 15° C./min is up to about 55%.
In some exemplary embodiments, the polymeric material has a crystallization temperature measured at a rate of 5° C./min, 10° C./min or 15° C./min. In some exemplary embodiments, the crystallization temperature measured at 5° C./min is at least about 120° C., at least about 125° C., or at least about 130° C. In some exemplary embodiments, the crystallization temperature measured at 5° C./min is up to about 140° C. or up to about 135° C. In some exemplary embodiments, the crystallization temperature measured at 10° C./min is at least about 115° C., at least about 120° C., or at least about 125° C. In some exemplary embodiments, the crystallization temperature measured at 10° C./min is up to about 140° C. or up to about 135° C. In some exemplary embodiments, the crystallization temperature measured at 15° C./min is at least about 110° C., at least about 115° C., or at least about 120° C. In some exemplary embodiments, the crystallization temperature measured at 15° C./min is up to about 135° C. or up to about 130° C.
In some exemplary embodiments, the polymeric material has an impact strength as measured by dart drop (ASTM D1709). In some embodiments, the dart drop performance is at least about 50 g, at least about 75 g, or at least about 125 g. In some embodiments, the dart drop performance is up to about 225 g, up to about 200 g, or up to about 190 g.
In some exemplary embodiments, the polymeric material has an impact strength as measured by dart impact. In some embodiments, the dart impact performance is at least about 1 inch. In some embodiments, the dart impact performance is less than about 2.2 inches.
In some embodiments, the polymeric material, a laminated material comprising the polymeric material, or the cup formed of the laminated material were tested using the Elmendorf test method described in ASTM D1922-93. In some embodiments, the Elmendorf Arm MD for the polymeric material is at least about 500 g. In some embodiments, the Elmendorf Arm MD for the laminated material is at least about 1500 g. In some embodiments, the Elmendorf Arm MD for the cup is at least about 1500 g. In some embodiments, the Elmendorf Arm TD for the polymeric material is at least about 500 g. In some embodiments, the Elmendorf Arm TD for the laminated material is at least about 1500 g. In some embodiments, the Elmendorf Arm TD for the cup is at least about 1500 g.
In some embodiments, the polymeric material, a laminated material comprising the polymeric material, or the cup formed of the laminated material were tested using the Elmendorf test method described in ASTM D1922-93. In some embodiments, the Elmendorf Tear MD for the polymeric material is at least about 75 gf. In some embodiments, the Elmendorf Tear MD for the polymeric material is less than about 350 gf. In some embodiments, the Elmendorf Tear MD for the laminated material is at least about 65 gf. In some embodiments, the Elmendorf Tear MD for the laminated material is less than about 700 gf. In some embodiments, the Elmendorf Tear MD for the cup is at least about 125 gf. In some embodiments, the Elmendorf Tear MD for the cup is less than about 500 gf.
In some embodiments, the Elmendorf Tear TD for the polymeric material is at least about 10 gf, at least about 50 gf, or at least about 125 gf. In some embodiments, the Elmendorf Tear TD for the polymeric material is less than about 450 gf. In some embodiments, the Elmendorf Tear TD for the laminated material is at least about 65 gf, at least about 100 gf, or at least about 200 gf. In some embodiments, the Elmendorf Tear TD for the laminated material is less than about 600 gf. In some embodiments, the Elmendorf Tear TD for the cup is at least about 200 gf. In some embodiments, the Elmendorf Tear TD for the cup is less than about 650 gf.
In some exemplary embodiments, a cup formed from the polymeric material can have a frangibility measurement measured when the cup is either hot or cold. In some embodiments, the cup has a frangibility of at least about 20 lbf when the cup is hot. In some embodiments, the cup has a frangibility less than about 60 lbf when the cup is hot. In some embodiments, the cup has a frangibility of at least about 25 lbf when the cup is cold. In some embodiments, the cup has a frangibility less than about 55 lbf when the cup is cold.
In some embodiments, a cup formed from the polymeric material reaches a temperature when filled with hot liquid. In some embodiments, the hot fill temperature (max sidewall) is at least about 130° C. In some embodiments, the hot fill temperature (max sidewall) is less than about 170° C. In some embodiments, the hot fill temperature (min internal) is at least about 135° C. In some embodiments, the hot fill temperature (min internal) is less than about 160° C.
In some exemplary embodiments, the polymeric material has a melting crystallinity at 5° C./min, 10° C./min or 15° C./min. In some exemplary embodiments, the melting crystallinity at 5° C./min is at least about 20%. In some exemplary embodiments, the melting crystallinity at 5° C./min is up to about 60%. In some exemplary embodiments, the melting crystallinity at 10° C./min is at least about 10%. In some exemplary embodiments, the melting crystallinity at 10° C./min is up to about 60%. In some exemplary embodiments, the melting crystallinity at 15° C./min is at least about 15%. In some exemplary embodiments, the melting crystallinity at 15° C./min is up to about 65%.
In some embodiments, the polymeric material, a laminated sheet comprising the polymeric material, or a cup formed of the laminated sheet has a puncture resistance, as measured in inches for either a ¼″ probe or a ⅛″ probe. In some embodiments, the puncture resistance for the polymeric material, the laminated sheet, or the cup (elongation at peak load) is at least about 0.2 inches. In some embodiments, the puncture resistance for the polymeric material, the laminated sheet, or the cup (elongation at peak load) is less than about 0.75 inches.
In some embodiments, the polymeric material, a laminated sheet comprising the polymeric material, or a cup formed of the laminated sheet has a puncture resistance, as measured in max load for either a ¼″ probe or a ⅛″ probe. In some embodiments, the puncture resistance for the polymeric material, the laminated sheet, or the cup (max load) is at least about 1,000 gf, at least about 3,000 gf, at least about 6,000 gf, or at least about 8,000 gf. In some embodiments, the puncture resistance for the polymeric material, the laminated sheet, or the cup (max load) is less than about 20,000 gf, less than about 18,000 gf, less than about 12,000 gf, or less than about 1,000 gf.
In some embodiments, the cup has a rigidity as measured when the cup is filled with cold, room temperature, or hot water and if the cup comprises a lid coupled with the brim. In some exemplary embodiments, the cup has a cold fill lidded rigidity of at least about 1 kg-F. In some embodiments, the cup has a cold fill lidded rigidity of less than about 1.5 kg-F. In some exemplary embodiments, the cup has a cold fill unlidded rigidity of at least about 0.5 kg-F. In some embodiments, the cup has a cold fill unlidded rigidity of less than about 1.2 kg-F. In some exemplary embodiments, the cup has a hot fill lidded rigidity of at least about 0.35 kg-F. In some embodiments, the cup has a hot fill lidded rigidity of less than about 0.75 kg-F. In some exemplary embodiments, the cup has a hot fill unlidded rigidity of at least about 0.2 kg-F. In some embodiments, the cup has a hot fill unlidded rigidity of less than about 0.5 kg-F. In some exemplary embodiments, the cup has a room temperature fill lidded rigidity of at least about 0.6 kg-F. In some embodiments, the cup has a room temperature fill lidded rigidity of less than about 1.7 kg-F. In some exemplary embodiments, the cup has a room temperature fill unlidded rigidity of at least about 0.3 kg-F. In some embodiments, the cup has a room temperature fill unlidded rigidity of less than about 1 kg-F. In some exemplary embodiments, the cup has a room temperature unfilled lidded rigidity of at least about 0.6 kg-F. In some embodiments, the cup has a room temperature fill lidded rigidity of less than about 1.7 kg-F. In some exemplary embodiments, the cup has a room temperature unfilled unlidded rigidity of at least about 0.3 kg-F. In some embodiments, the cup has a room temperature fill unlidded rigidity of less than about 1 kg-F.
In some exemplary embodiments, the cup formed cup has a seam. In some embodiments, the seam thickness is at least about 0.0762 centimeter (about 0.03 inches). In some embodiments, the seam thickness is less than about 1.2 inches.
In some embodiments, the cup or the polymeric material has a thermal conductivity at 21° C. In some embodiments, the thermal conductivity at 21° C. is at least about 0.05 W/m-K or at least about 0.052 W/m-K. In some embodiments, the thermal conductivity at 21° C. is less than about 0.057 W/m-K or less than about 0.053 W/m-K.
In some embodiments, the cup or the polymeric material has a thermal conductivity at 93° C. In some embodiments, the thermal conductivity at 93° C. is at least about 0.061 W/m-K or at least about 0.062 W/m-K. In some embodiments, the thermal conductivity at 93° C. is less than about 0.065 W/m-K or less than about 0.064 W/m-K.
In some embodiments, the cup, when filled with a hot liquid has a time to cool from about 200° F. to about 140° F. In some embodiments, the time to cool is at least 3400 seconds. In some embodiments, the time to cool extended past the allotted measured time.
In some embodiments, the cup formed from the polymeric material has a top load measurement. In some embodiments, the top load is at least about 70 lbf, at least about 90 lbf, or at least about 115 lbf. In some embodiments, the top load is less than about 200 lbf, less than about 175 lbf, or less than about 150 lbf.
In some embodiments, a cup formed from the polymeric material has a weight. In some embodiments, the weight of the cup is at least about 9 g, at least about 10 g, or at least about 12 g. In some embodiments, the weight of the cup is less than about 15 g, less than about 14 g, or less than about 12 g.
Recyclability of articles formed from the insulative cellular non-aromatic polymeric material of the present disclosure minimizes the amount of disposable waste created. In comparison, beaded expanded polystyrene cups that break up into beads and thus ordinarily cannot easily be reused in a manufacturing process with the same material from which the article was formed. In addition, paper cups that typically have an extrusion coated plastic layer or a plastic lamination for liquid resistance ordinarily cannot be recycled because the different materials (paper, adhesive, film, plastic) normally cannot be practicably separated in commercial recycling operations.
A potential feature of a cup formed of the insulative cellular non-aromatic polymeric material according to one aspect of the present disclosure is that it possesses unexpected strength as measured by rigidity. Rigidity is a measurement done at room temperature and at an elevated temperature (e.g., by filling the cup with a hot liquid) and measuring the rigidity of the material. The strength of the cup material is important to reduce the potential for the cup being deformed by a user and the lid popping off or the lid or sidewall seal leaking.
A potential feature of a cup formed of the insulative cellular non-aromatic polymeric material according to the present disclosure is that the sleeve is resistant to puncture, such as by a straw, fork, spoon, fingernail, or the like, as measured by standard impact testing, as described hereinbelow. Test materials demonstrated substantially higher impact resistance when compared to a beaded expanded polystyrene cup. Accordingly, a cup formed one aspect as described herein can reduce the likelihood of puncture and leakage of hot liquid onto a user.
The insulative cellular non-aromatic polymeric material of the present disclosure may be formed into a strip, which can be wrapped around other structures. For example, a strip of the material according to one aspect of the present disclosure that can be used as a wrapping material may be formed and wrapped around a pipe, conduit, or other structure to provide improved insulation. The sheet or strip may have a layer of adhesive, such as a pressure sensitive adhesive, applied to one or both faces. The strip may be wound onto a roll. Optionally, the strip may have a release liner associated therewith to make unwinding the strip from the roll easier. The polymer formulation may be adapted to provide the requisite flexibility to form a wrap or windable strip, for example, by using one or more polypropylene or other polyolefin materials that have sufficient flexibility to enable the extruded sheet to be flexible enough to be wound onto a roll. The insulative cellular non-aromatic polymeric material may be formed into a sleeve that can be inserted over a cup to provide additional insulation.
In exemplary embodiments, sheets formed from the insulative cellular non-aromatic polymeric material of the present disclosure may be cut at the die or be flaked and used as a bulk insulator.
The formulation and insulative cellular non-aromatic polymeric material of the present disclosure satisfies a long-felt need for a material that can be formed into an article, such as a cup, that includes many if not all of the features of insulative performance, ready for recyclability, regrindability, puncture resistance, frangibility resistance, microwavability and other features as discussed herein. Others have failed to provide a material that achieves combinations of these features as reflected in the appended claims. This failure is a result of the features being associated with competitive design choices. As an example, others have created materials and structures therefrom that based on design choices are insulated but suffer from poor puncture resistance, inability to effectively be recyclable, and lack microwavability. In comparison, the formulations and materials disclosed herein overcome the failures of others by using an insulative cellular non-aromatic polymeric material.
The material of the present disclosure may also be formed into a deformable sheet, which can be wrapped around other structures. For example, a sheet of the present material may be formed and wrapped around a pipe, conduit, or other structure to provide improved insulation.
Aromatic molecules typically display enhanced hydrophobicity when compared to non-aromatic molecules. As a result, it would be expected that changing from a polystyrene-based insulative cellular polymeric material to a polypropylene-based insulative cellular polymeric material would result in a change in hydrophobicity with a concomitant, but not necessarily predictable or desirable, change in surface adsorption properties of the resulting material. In addition, by virtue of the hydrocarbon chain in polystyrene, wherein alternating carbon centers are attached to phenyl groups, neighboring phenyl groups can engage in so-called pi-stacking, which is a mechanism contributing to the high intramolecular strength of polystyrene and other aromatic polymers. No similar mechanism is available for non-aromatic polymers such as polypropylene. Moreover, notwithstanding similar chemical reactivity and chemical resistance properties of polystyrene and polypropylene, polystyrene can be either thermosetting or thermoplastic when manufactured whereas polypropylene is exclusively thermoplastic. As a result, to the extent that surface adsorption properties, manufacturing options, and strength properties similar to those of polystyrene are sought, likely alternatives to polystyrene-based insulative cellular polymeric materials would be found in another aromatic polymer rather than in a non-aromatic polymer.
In some embodiments, the multi-layer sheet consists of the film layer, the insulative cellular non-aromatic polymeric layer, and the polymeric-lamination layer. In some embodiments, the multi-layer sheet consists of the film layer, the insulative cellular non-aromatic polymeric layer, the polymeric-lamination layer, and an ink layer printed onto the film layer to locate the film layer between the ink layer and the polymeric-lamination layer.
In some embodiments, the polymeric-lamination layer consists of regrind, polypropylene, polyethylene, and a colorant. In some embodiments, the polymeric-lamination layer consists essentially of regrind, polypropylene, and polyethylene.
Reference is hereby made to U.S. application Ser. No. 13/526,444 filed Jun. 18, 2012, and entitled PROCESS FOR FORMING AN INSULATED CONTAINER HAVING ARTWORK and U.S. application Ser. No. 13/526,454 filed Jun. 18, 2012, and entitled PROCESS FOR FORMING AN INSULATED CONTAINER HAVING ARTWORK for disclosures relating to processes relating to cup formation, film compositions and printing, and insulative cellular non-aromatic polymeric materials, which applications are hereby incorporated in their entirety herein
Reference is hereby made to U.S. application Ser. No. 13/491,007 filed Jun. 7, 2012, and entitled INSULATED CONTAINER for disclosure relating to insulative containers, which application is hereby incorporated in its entirety herein.
The following examples are set forth for purposes of illustration only. Parts and percentages appearing in such examples are by weight unless otherwise stipulated. All ASTM, ISO, and other standard test method cited or referred to in this disclosure are incorporated by reference in their entirety.
A base resin blend comprised DAPLOY™ WB140 polypropylene homopolymer (available from Borealis A/S) and F020HC high crystallinity polypropylene homopolymer, available from Braskem. The base resin blend was blended with: Hydrocerol® CF-40E™ as a chemical blowing agent (CBA), talc as a physical nucleation agent, CO2 as a physical blowing agent, a slip agent, and Ampacet blue-white as a colorant. The colorant can be added to the base resin or to the secondary resin and may be done prior to mixing of the two resins. Percentages were:
The formulation was added to an extruder hopper. The extruder heated the formulation to form a molten resin mixture. CO2 was added to the molten resin mixture to expand the resin and reduce density. The formed mixture was extruded through a die head into a strip.
A polymeric-lamination layer comprised Dow 4012 LDPE and ExxonMobil™ 3155 PP3155. The two resins were blended with J11 as the colorant. Percentages by weight were:
The formulation was added to an extruder hopper. The extruder heated the formulation to form a molten resin mixture. The molten mixture was between the film (Jindal Films Bicor™ 18 LPX-2) and the insulative cellular non-aromatic polymeric material described above to form the multi-layer sheet. Blanks were cut from the multi-layer sheet and used to form cups in accordance with the present disclosure.
The properties insulative cellular non-aromatic material of Example 1 were evaluated according to procedures known in the art and are shown in Table 1.
The properties of the multi-layer sheet formed according to Example 1 are shown below in Table 2.
A base resin blend comprised Braskem Amppleo® 1025MA, JPP MFX6 PP Resin, and Braskem TI215OC. The base resin blend was blended with regrind and a chemical blowing agent. The chemical blowing agent was Ecocell® P. Percentages were about:
The formulation was added to an extruder hopper. The extruder heated the formulation to form a molten resin mixture. The molten mixture was extruded between the extruded insulative cellular non-aromatic polymeric material and the film, as suggested in
A polymeric-lamination layer comprised reground insulative cellular-nonaromatic polymeric material and Flint Hills P9H8M-015 Polypropylene. The two resins were blended with Colortech E-1274 Blue White as the colorant.
Percentages by weight were about:
The formulation was added to an extruder hopper. The extruder heated the formulation to form a molten resin mixture. The molten mixture was extruded between the extruded insulative cellular non-aromatic polymeric material and the film, as suggested in
The resulting composite material had properties according to Table 3.
An example of the regrinding process is described in the Figures. Amppleo® 1025MA from Braskem, Daploy™ WB140 HMS from Borealis, Waymax MFX6 from JPP, and regrind material were tested for melt elasticity. Briefly, the resins were extruded using an extruder having a wheel position about 114 mm below the die, ambient wheel temperature, a barrel diameter of 12 mm, a die entry angle of about 180°, a 2 mm die diameter, a 30 mm die length, with a 6 minute preheat time and a 200° C. barrel temperature. The experiments were repeated in triplicate. The results are shown in Table 4.
Polymeric material for forming the cup bottom was prepared as follows. A base resin blend comprised a high melt strength polypropylene, a polypropylene homopolymer, and a polypropylene elastomer. The base resin blend was blended with regrind, a chemical blowing agent, an antioxidant, and a nucleating agent. Percentages were:
The formulation was added to an extruder hopper. The extruder heated the formulation to form a molten resin mixture. CO2 was added to the molten resin mixture to expand the resin at a rate of 11.8 lbs/hr. The formed mixture was extruded through a die head into a strip.
Although only a number of exemplary embodiments have been described in detail above, those skilled in the art will readily appreciate that many modifications are possible in the exemplary embodiments without materially departing from the novel teachings and advantages. Accordingly, all such modifications are intended to be included within the scope of this disclosure as defined in the following claims.
As used in the specification and the appended claims, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Ranges may be expressed herein as from “about” one particular value, and/or to “about” another particular value. When such a range is expressed, another embodiment includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another embodiment. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint.
“Optional” or “optionally” means that the subsequently described event or circumstance may or may not occur, and that the description includes instances where said event or circumstance occurs and instances where it does not.
Throughout the description and claims of this specification, the word “comprise” and variations of the word, such as “comprising” and “comprises,” means “including but not limited to,” and is not intended to exclude, for example, other additives, components, integers or steps. “Exemplary” means “an example of” and is not intended to convey an indication of a preferred or ideal embodiment. “Such as” is not used in a restrictive sense, but for explanatory purposes.
Disclosed are components that can be used to perform the disclosed methods, equipment, and systems. These and other components are disclosed herein, and it is understood that when combinations, subsets, interactions, groups, etc. of these components are disclosed while specific reference of each various individual and collective combinations and permutation of these may not be explicitly disclosed, each is specifically contemplated and described herein, for all methods, equipment, and systems. This applies to all aspects of this application including, but not limited to, steps in disclosed methods. Thus, if there are a variety of additional steps that can be performed it is understood that each of these additional steps can be performed with any specific embodiment or combination of embodiments of the disclosed methods.
It will be apparent to those skilled in the art that various modifications and variations can be made without departing from the scope or spirit of the present disclosure. Other embodiments will be apparent to those skilled in the art from consideration of the specification and practice disclosed herein. It is intended that the specification and examples be considered as exemplary only.
It should further be noted that any publications and brochures referred to herein are incorporated by reference in their entirety.
This application is a continuation of U.S. application Ser. No. 18/406,730, filed Jan. 8, 2024, which is a continuation of U.S. application Ser. No. 17/528,650, filed Nov. 17, 2021, which is a continuation of U.S. application Ser. No. 16/058,126, filed Aug. 8, 2018, which claims priority under 35 U.S.C. § 119(e) to U.S. Provisional Application No. 62/542,324, filed Aug. 8, 2017, each of which is expressly incorporated by reference herein.
| Number | Date | Country | |
|---|---|---|---|
| 62542324 | Aug 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 18406730 | Jan 2024 | US |
| Child | 18639437 | US | |
| Parent | 17528650 | Nov 2021 | US |
| Child | 18406730 | US | |
| Parent | 16058126 | Aug 2018 | US |
| Child | 17528650 | US |