The present disclosure relates to an insulative packaging system and, more particularly, to an insulative packaging system utilizing a chopped fiber insulative pad incorporating antimicrobial and absorbtive powders.
This section provides background information related to the present disclosure which is not necessarily prior art.
The current technology provides paper mailers, lined with plastic bubble-wrap, or more expensive foam, or foam-lined boxes. These products are used primarily for shipping sensitive or fragile items, but suffer from the fact that they have extremely limited cushioning, no absorption properties, no antimicrobial properties, and practically no temperature-control value.
Foam, or foam-lined boxes are also used for shipping temperature-sensitive products such as medical samples, pharmaceuticals, chocolates, etc. These current products, in addition to being dramatically more expensive to purchase, warehouse, and ship (in-bound and outbound freight), are also more labor intensive, less user-and-environmentally friendly, and provide very limited protection during transit. Often these shipping containers utilize a significant amount of dry ice to maintain key low temperatures to prevent spoilage.
This section provides a general summary of the disclosure, and is not a comprehensive disclosure of its full scope or all of its features.
An insulative packing material is disclosed. The material contains a polymer film having an interior surface and lateral edges folded on itself to form a pocket having an opening and sealable by a flap. A textile pad having chopped fibers selected from the group polyester, nylon, acrylic, cotton, polypropylene, denim and combinations thereof is coupled to an interior surface being attached to the pad. The textile pad has powder antimicrobials while the polymer film has biodegradable enhancers added therein.
An insulative packaging system has a shipping container, a three layered polymer film laminate having an interior surface and lateral edges folded on itself to form a pocket having an opening and sealable by a flap, and a textile pad. The textile pad is disposed within the container and the polymer film and is formed of chopped fibers selected from the group polyester, nylon, acrylic, cotton, polypropylene, denim and combinations thereof. The textile pad further has microbial and super-absorbent powders disposed adjacent to an exterior surface of the textile paid or within.
Other and further objects of the present invention will be come apparent from the following detailed description of the invention when taken in conjunction with the appended drawings.
The drawings described herein are for illustrative purposes only of selected embodiments and not all possible implementations, and are not intended to limit the scope of the present disclosure.
Corresponding reference numerals indicate corresponding parts throughout the several views of the drawings.
Example embodiments will now be described more fully with reference to the accompanying drawings.
Referring now to the drawings, the mailer is shown in
The inner surface of the mailer 10 can be a non-petroleum based, biodegradable film or paper (substrate) 14 that is permeable. Sandwiched between the inner biodegradable film or paper (substrate) 14 and the outer film 12, and sealed on all sides, is a proprietary, biodegradable pad 16 made from re-cycled, purified, ground-up material to which super absorbent powders (for the absorption of spills), and antimicrobial powders (for the prevention of contamination in case of rupture for such products as blood or vaccines, etc.) have been added during manufacture. The antimicrobials are programmed to expire, after a pre-selected desired length of time, to allow for the eventual, natural, degradation/biodegradability of the mailer. The outer surface of the pad 16 is encompassed within the water-proof, biodegradable film or paper 12, sealed on two (or three) sides with film 14, which extends laterally coextensive with film 12. The film 14 is double-sealed with pressure-sensitive, biodegradable tape 18 (covered with a protective strip 34, at the top, for safety and to prevent tampering). Film 14 does not surround the pad 16 completely, but the end portions 40 extend around the pad 16 sufficiently to enable the end portions 40 to be sealed with the film 12, as indicated at 44.
As shown in
The pad 16, as duly noted, can be made from re-cycled, purified, ground-up material to which super absorbent powders (for the absorption of spills), and antimicrobial powders (for the prevention of contamination in case of rupture for such products as blood or vaccines, etc.) have been added during manufacture. The antimicrobials are programmed to expire, after a pre-selected desired length of time, to allow for the eventual, natural, degradation-biodegradability of the mailer.
As evident from the above description, the pad 16 is covered by the film 14 on the inside with film 14 extending laterally beyond the pad 16 to lie coextensive with the marginal edges of the film 12 so all marginal edges can be heat sealed together. Film 14 extends around the longitudinal extremities of the pad 16 so that the end portions 40 of the film 14 lie between the pad 16 and the outer film 12 when the pad 16 is located in the mailer 10. These portions 40 enable the film 14 to be heat sealed together with the film 12 around the mailer opening 24, thereby entrapping the pad 16. The portion of the opening 24 that lies with the flap 26 has pressure-sensitive, biodegradable tape 18 (covered with a protective strip 34) in order to seal the top edges of the inner film 14 together before the flap 26 is sealed to the front of the mailer 10.
The film is preferably a biodegradable polymer as defined by ASTM 1991, and is preferably biodegradable in 9 months to 5 years either anaerobically and aerobically. The film can be manufactured as a 3-layer construction. In this regard, each layer can be manufactured with a biodegradable additive from ECM Biofilms, Inc. of Painsville, Ohio 44077. Optionally, the inner and outer layer can be colored with colors such as white or silver. The inside layer can be laminated to the pad material using an adhesive or thermal bonding. The layered structure can be perforated and have an inner nylon core and low-density polyethylene skin. Optionally, this laminate structure can be formed using a molten material force fed through a die and subsequently cooled.
The insulative batt is manufactured from any of a wide variety of textile compositions comprising, for example, polyester, nylon, acrylic, cotton, polypropylene, denim etc., or combinations thereof, including both natural and man-made fibers. Randomly distributed textile and binder fibers having lengths between 1/16 inch to 1.5 inches and a denier of between 5 and 12 are used to form a textile batt, which is processed to form the insulative pad.
In one embodiment, two textile pads are bonded to a biodegradable polymer layer to form the textile insulative construction. The resulting pads may be used as an insulative layer within a shipping container that can be formed of a polymer, paper, or cardboard material. There are several ways to make the textile batt. In the first, the fiber batt can contain binder fibers. The fiber batt is heated in an oven and compressed to form an insulative pad. Optionally, the insulative pad can be formed using needle setting technology.
Optionally, several layers of enveloped textile pad can be used to form the construction. Each textile pad within the system may be of equal thickness, or may be of unequal thickness. It is envisioned the pad can have a thickness of about 1/16 of an inch or greater. The starting insulative pad may be split longitudinally to provide two, three or more partial thickness batts. Optionally, the fibers can include thermoplastic binder fibers and reinforcement fibers are laid randomly yet consistently in x-y-z axes. The reinforcement fibers are generally bound together by heating the binder fibers above their glass transition temperature. Typically, less than about 20% by weight binder fiber is used, and preferably about 15% binder fiber is used to form the insulative pad.
Thermoplastic binder fibers are provided having a weight of less than 0.2 pounds per square foot and, more particularly, preferably about 0.1875 pounds per square foot. The remaining reinforcement fiber is greater than 0.8 pounds per square foot, and preferably 1.0625 pounds per square foot. The binder fibers are preferably a mixture of thermoplastic polymers which consist of polyethylene/polyester or polypropylene/polyester or combinations thereof.
The insulative pad is formed by heating the textile batt in the oven to a temperature greater than about 350° F. and, more preferably, to a temperature of about 362° F. Such heating causes the binder fibers to melt and couple to the non-binder fibers, thus causing fibers to adhere to each other and solidify during cooling. Upon cooling, the binder fibers solidify and function to couple the non-binder reinforcement fibers together as, well as function as reinforcement themselves.
The insulative textile batt is compressed to form the insulative pad so it has a density of greater than about 10 pounds per cubic foot. For systems, the insulative pad preferably has a density of greater than about 10 pounds per cubic foot and, more preferably, about 13.3 pounds per cubic foot with a thickness of about ⅛ inch.
The insulating properties of the material are tested under ASTME90-97, ASTME413-87. The insulative pad preferably has a compression resistance at 25% of the original thickness of greater than about 20 psi and preferably about 23.2 psi, at 30% of greater than about 35.0 psi and preferably about 37.0 psi, and at 50% of greater than about 180 psi and preferably about 219 psi. Additionally, the compression set at a compression of 25% of the original thickness is less than 20%, and preferably about 18.8%, and the tensile strength is between about 60 and 80 pounds and, most preferably, about 78.4 pounds.
Phase-change materials (refrigerants/gel packs) used in the mailer can also biodegradable, making the entire shipping system cost-effective, environmentally-friendly, and socially-responsible.
The insulative properties of the mailer are roughly equivalent to one-half inch of foam, thus, allowing for the savings of second-day shipping as opposed to the cost of overnight priority freight/delivery charges as is required with current mailer technology.
The textile pad can serves six purposes: 1) insulation; 2) padding/cushioning; 3) absorption; 4) antimicrobial action; 5) biodegradability and; 6) cost efficiency (in terms of initial cost as opposed to a foam-lined box, set-up/fulfillment labor expenses, storage space, with attendant charges, and in-bound and out-bound freight charges).
The insulation properties of the mailer are roughly equivalent to one-half inch of foam, thus allowing for the savings of second-day shipping as opposed to the cost of overnight priority freight/delivery charges as is required with current mailer technology.
A specific example of a mailer according to the present invention is one that is 14.5 inches long, 10 inches wide, and has a 4.5 inch flap. The top opening is about 8.5 inches across and can be opened to about 5 inches, thereby facilitating loading.
Examples of the materials used for the mailer are as follows. Tri-extruded degradable sheeting can be used as a film. The film is manufactured as 37″ lay flat at 0.004 inches. Grass green, opaque tri-extruded degradable sheeting can be used for film 14. The sheeting is manufactured with a degradable additive in all layers. The film manufactured is 12″ lay flat at 0.0015 inches. For the film 12, a white opaque outside/silver-color inside tri-extruded degradable sheeting can be used. The sheeting is manufactured with a degradable additive in all layers. The film is manufactured as 12″ lay flat at 0.004 inches. The films are obtainable commercially from a variety of suppliers.
An example of the sealing tape 18 is BP-1052 SIS block co-polymer rubber, obtainable from DarTape Technologies Corporation. Biodegradable materials are commercially available from ECM Biofilms, Inc., Painesville, Ohio. Incorporation of at least 1% of the ECM Masterbatch pellets will assure biodegradation. Antimicrobial materials useable are Lurol AM-7 obtainable from Goulston Technologies, Inc. of Monroe, N.C. The pad 16 was made using new textile clippings mixed with commercially available antimicrobial and super-absorbent powders (such as carboxymethylcellulose), and then processed through a web forming operation to produce a pad or batten about 15 mm or 0.6 inches thick. Film 12 can be from about 2 mils thick to about 6 mils thick, and preferably about 4 mils thick. Film 14 can be from about 0.5 mils thick to about 5 mils thick, and preferably about 3 mils thick. Pad 16 can be from about 5 mm thick to about 25 mm thick, and preferably about 15 mm thick.
Optionally, the absorbent material can be incorporated into the batting material prior to the binding of the fibers. Optionally, the absorbent material can be sodium polyacrylate in the form of a white powder. The sodium polyacrylate can have a pH of 5.5-6.5, a melting point of >390° F., and a specific gravity of 0.4-0.7 g/ml.
Example embodiments are provided so that this disclosure will be thorough, and will fully convey the scope to those who are skilled in the art. Numerous specific details are set forth such as examples of specific components, devices, and methods to provide a thorough understanding of embodiments of the present disclosure. It will be apparent to those skilled in the art that specific details need not be employed, that example embodiments may be embodied in many different forms, and that neither should be construed to limit the scope of the disclosure. In some example embodiments, well-known processes, well-known device structures, and well-known technologies are not described in detail.
As shown in
The embodiment shown in
The terminology used herein is for the purpose of describing particular example embodiments only and is not intended to be limiting. As used herein, the singular forms “a,” “an,” and “the” may be intended to include the plural forms as well, unless the context clearly indicates otherwise. The terms “comprises,” “comprising,” “including,” and “having” are inclusive and therefore specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof. The method steps, processes, and operations described herein are not to be construed as necessarily requiring their performance in the particular order discussed or illustrated, unless specifically identified as an order of performance. It is also to be understood that additional or alternative steps may be employed.
When an element or layer is referred to as being “on,” “engaged to,” “connected to,” or “coupled to” another element or layer, it may be directly on, engaged, connected or coupled to the other element or layer, or intervening elements or layers may be present. In contrast, when an element is referred to as being “directly on,” “directly engaged to,” “directly connected to,” or “directly coupled to” another element or layer, there may be no intervening elements or layers present. Other words used to describe the relationship between elements should be interpreted in a like fashion (e.g., “between” versus “directly between,” “adjacent” versus “directly adjacent,” etc.). As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items.
Although the terms first, second, third, etc. may be used herein to describe various elements, components, regions, layers and/or sections, these elements, components, regions, layers and/or sections should not be limited by these terms. These terms may be only used to distinguish one element, component, region, layer or section from another region, layer or section. Terms such as “first,” “second,” and other numerical terms when used herein do not imply a sequence or order unless clearly indicated by the context. Thus, a first element, component, region, layer or section discussed below could be termed a second element, component, region, layer or section without departing from the teachings of the example embodiments.
Spatially relative terms, such as “inner,” “outer,” “beneath,” “below,” “lower,” “above,” “upper,” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. Spatially relative terms may be intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. For example, if the device in the Figures is turned over, elements described as “below” or “beneath” other elements or features would then be oriented “above” the other elements or features. Thus, the example term “below” can encompass both an orientation of above and below. The device may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein interpreted accordingly.
Although the invention has been described in terms of preferred embodiments, changes can be made which do not depart from the inventive concept. Such changes are deemed to fall within the purview of the appended claims. The foregoing description of the embodiments has been provided for purposes of illustration and description. It is not intended to be exhaustive or to limit the disclosure. Individual elements or features of a particular embodiment are generally not limited to that particular embodiment, but, where applicable, are interchangeable and can be used in a selected embodiment, even if not specifically shown or described. The same may also be varied in many ways. Such variations are not to be regarded as a departure from the disclosure, and all such modifications are intended to be included within the scope of the disclosure.
This application is a continuation-in-part of U.S. patent application Ser. No. 12/945,403, filed on Nov. 12, 2010, which is a continuation-in-part of International Patent Application No. PCT/US2009/043972, filed on May 14, 2009, which is a continuation-in-part of U.S. patent application Ser. No. 12/120,353, filed May 14, 2008. The contents of these applications are hereby incorporated by reference herein in their entirety.
Number | Date | Country | |
---|---|---|---|
Parent | 12945403 | Nov 2010 | US |
Child | 13158942 | US | |
Parent | PCT/US2009/043972 | May 2009 | US |
Child | 12945403 | US | |
Parent | 12120353 | May 2008 | US |
Child | PCT/US2009/043972 | US |