Patent Grant
8785058
The present disclosure relates to the fields of biological fuel cells and nanomaterial technology.
Research to develop biological fuel cells (“biofuel cells”) dates back to the 1960s. The working principle is similar to that of conventional chemical fuel cells; however, biofuel cells typically avoid the use of expensive noble metals as catalysts like platinum and ruthenium. Rather, biofuel cells use biocatalysts such as enzymes, or even whole organisms, to catalyze the conversion of chemical energy into electricity.
A basic biofuel cell can generally operate in two ways. It can use biological catalysts—enzymes extracted from biological systems—to oxidize fuel molecules at the anode and to enhance oxygen reduction at the cathode of the biofuel cell. Alternatively, whole microbial cells can be used to supply the biofuel cells with the fuel. In both cases the main scientific problem is the electrical coupling of the biological components of the system with the fuel cell's electrodes. Molecules known as electron-transfer mediators can provide efficient transport of electrons between the biological components, enzymes or microbial cells, and the electrodes of the biofuel cell.
Nanomaterials and Single Wall Nanotubes (“SWNTs”)
There has been interest in nanomaterials, more specifically carbon nanotubes (“CNTs”), since their discovery by Iijima in 1991, partly because of their structural and electronic properties. Single wall carbon nanotubes (“SWNTs”) are the fundamental form of carbon nanotubes with electronic properties that emerge due to their one dimensionality. A SWNT comprises a single hexagonal layer of carbon atoms (a graphene sheet) that has been rolled up to form a seamless cylinder.
SWNTs have no functional groups and are consequently quite inert. Limited reactivity arises due to the curvature-induced stress from the non-planer sp2 carbons and the misaligned π orbitals. While there is a wealth of literature on the derivatization of the SWNTs, two general approaches appear to be 1,3-dipolar cycloaddition, and the oxidation of some of the atoms at the tube ends or on the tube wall, and then substitution of the functionality thus formed (—F, —OH, —COOH). At this point, a variety of synthetic organic reactions can be carried out. An example of the former approach is a reaction with azomethine. The latter approach, on the other hand, requires a more aggressive oxidation, such as, refluxing with HNO3, ozonation, or reaction with solid KOH.
Solubility, in both water and organic solvents, is an issue in the functionalization of nanomaterials. One disadvantage of many nanomaterials is their limited solubility in common solvents. Solubility of nanomaterials, specifically carbon nanotubes, in water would allow chemical derivatization and manipulation of the nanotubes to be facilitated simply and less expensively.
Efforts have been made to make carbon nanotubes stably dispersed or soluble in water and in organic solvents, but to date the solubilities observed have been relatively low—typical values at room temperature range from 0.06 to 0.08 mg of SWNT per milliliter of solvent. Different strategies have been employed to achieve dispersion including shortening the SWNTs as well as prolonged and vigorous acid treatment. Dispersion of full-length nanotubes has mostly been achieved by non-covalent wrapping of water-soluble macromolecules on the nanotubes.
Much of the effort aimed at SWNT functionalization has involved the use of conventional chemical techniques, such as refluxing and sonication. Many of these reactions need to be carried out over a long period of time. For example, for carboxylation, the reaction mixture was typically refluxed in conc. HNO3 for 10 to 50 hrs. Further functionalization, such as, diimide-activated amidation and 1,3-dipolar cycloaddition may require additional days of reaction time. The functionalization of carbon nanotubes by conventional chemical processing is a tedious and time-consuming process. Consequently, there is a need to develop techniques for rapid chemical functionalization of carbon nanotubes.
Microwaves
Microwaves are electromagnetic radiation in the 0.3-300 GHz frequency range (corresponding to 0.1-100 cm wavelength). To avoid interference with communication networks, all microwave heaters (domestic or scientific) are designed to work at either 2.45 GHz or 0.9 GHz, of which, the former is more prevalent. According to Planck's law, the energy at this wavelength is 0.3 cal/mol, and is therefore insufficient for molecular excitation, thus most of the energy is used in substrate heat-up. The mechanism of microwave heating is different from that of conventional heating, where heat is transferred by conduction, convection or radiation. In microwave heating, electromagnetic energy is transformed into heat through ionic conduction and the friction due to rapid reorientation of the dipoles under microwave radiation. The larger the dipole moment of a molecule, the more vigorous is the oscillation in the microwave field, consequently more heating. This type of heating is fast, has no inertia, and is in-situ without heating the surroundings.
Chemistry under microwave radiation is known to be quite different, fast and efficient (Gedye et al., Tetrahedron Lett., 27 (1986) 279; Giguere et al., Tetrahedron Lett., 27 (1986) 4945; Loupy et al., Chimie, 7 (2004) 103-112). It also reduces the need for solvents, thus it is eco-friendly. Some of the reported advantages are rapid reactions under controlled temperature and pressure (especially in a closed system), higher purity products achieved due to short residence times at higher temperatures, and better yields even at very short residence times. Another factor is that during dipolar polarization under microwave radiation, the activation parameters are modified. For example, it has been reported by Lewis that during imidization of polyamic acid, the activation energy reduced from 105 to 57 KJ/mol. (Lewis et al., J. Polym. Sci., 30A (1992) 1647) (All referenced cited in this paragraph are herein incorporated by reference in their entirety).
Composites
Investigations have been conducted on the SWNT based composites by both theoretical and experimental means. These prior art approaches involve, among other things, dispersion, melt mixing, milling, covalent grafting or in-situ growing of SWNTs in different polymer or ceramic matrices to achieve the certain composite. The results, however, conflict among studies wherein some studies revealed that the introduction of SWNTs in polymer clearly enhances both the physical and mechanical properties while others showed that the carbon nanotube contributed no mechanical improvement to the composites.
The ineffective utilization of nanotubes as reinforcement in composites is normally suffered from two factors, non-uniform dispersion of carbon nanotubes in a matrix and poor interfacial bonding between them. The latter one consequently will result in low efficiency of load transfer across the nanotube/matrix interface, and the pull-out of carbon nanotubes from the matrix can be observed when the composites are under extension.
The observed ineffective utilization of carbon nanotubes as the reinforcing material in many of these composites has been attributed to the non-uniform dispersion of carbon nanotubes, and the poor interfacial adhesion to the matrix. For example, the latter results in ineffective load transfer across the nanotube/matrix interface, and the “pullout” of carbon nanotubes has been observed when the composite is under strain. One issue has been the high temperature and reactivity of some of the current methodologies, which can destroy and/or damage the carbon nanotubes.
A non-compartmental biofuel cell including glucose oxidase (GOx) for the anode or oxidizing electrode is known in the art. This non-compartmental biofuel cell uses glucose oxidase (GOx) in the anode, which results in an oxygen-insensitive anode system that could react directly in the bloodstream. Katz et al., A non-compartmentalized glucose|O2 biofuel cell by bioengineered electrode surfaces, J. Electroanalytical Chem. 479 (1999) 64-68. Katz's method utilizes a gold plate on which an enzyme complex of GOx, plus an electron transfer mediator, coupled with a maleimide monolayer is constructed.
Another type of biofuel cell is a biofuel cell cathode, described in Minteer's U.S. Patent Application Publication, 2005/0095466. This biofuel cell consists of an organic cathode made of a catalytic enzyme, an electron transfer mediator, and a metallic electrode. This conventional biofuel cell technology, utilizes an electron transfer mediator like a protein or protein by-product combined with an electrode, which is preferably metallic.
Carbon nanotubes have been used in the prior art by Cai as replacements for electron transfer mediators. Cai at al., Direct electron transfer of glucose oxidase promoted by carbon nanotubes, Anal. Biochem. 332 (2004) 75-83. Cai discusses transfer electrons (electricity) from complex enzymes like GOx. Due to the complexity of the enzymes, it is difficult to immobilize them on the carbon nanotube surface while still retaining their chemical properties. Their complexity also makes access to the reaction centers within these enzymes difficult. Cai attempts to address these issues through the modification of a carbon nanotube to absorb GOx. Cai's modifications entail placing free-floating carbon nanotubes in a suspension. Additionally, Cai uses a surfactant to disperse the carbon nanotubes into the solvent in order to combine it with GOx.
Choi US Patent Application 2005/0118494 discloses a specific process in which one can build a biofuel cell anode or cathode by layering either metal or carbon nanotube to construct a vertical array of nanowires (such as gold wires of nanometers in width) or carbon nanotubes perpendicular to a conductive base. Choi discloses that with the Langmuir-Blodgett lift-off (“LB”) process, one can coat the resulting structure with glucose oxidase and other enzymes. Choi discloses building the multiple-layered electrode base with a gold or titanium base over some other non-metallic conductor.
To date it has not been possible to fabricate practical biological fuels and/or biological fuel cells. Current biofuel cells fabricated using presently available technologies suffer from low power densities and short lifetimes. This is due to, among other things, the long-term chemical fragility of the enzymes, cost of electron mediator compounds, the need of complex organic structures for electron transfer, inefficient micro-fluidics and cross-over of fuel through the polymer electrolyte membranes. These and other needs are addressed and/or overcome by the present disclosure.
The present disclosure provides for a biofuel cell system including an anode electrically coupled to a cathode, an electrolyte in electrical communication with the anode and the cathode, a first nanomaterial on a first substrate, the first nanomaterial on the first substrate having at least one first enzyme immobilized with respect to the first nanomaterial as the anode, a second nanomaterial on a second substrate, with the second nanomaterial on the second substrate having at least one second enzyme immobilized with respect to the second nanomaterial as the cathode.
The present disclosure also provides for a biofuel cell system, wherein at least one of the first and second nanomaterial is selected from the group consisting of single wall carbon nanotubes (SWNTs), multiwall carbon nanotubes (MWNTs), carbon nanohorns, fullerenes, nano onions, nanocomposites and combinations thereof.
The present disclosure also provides for a biofuel cell system, wherein the at least one first enzyme is immobilized with respect to the first nanomaterial by an electrochemical process; and wherein the at least one second enzyme is immobilized with respect to the second nanomaterial by an electrochemical process. In an alternative embodiment, the present disclosure also provides for a biofuel cell system, wherein the at least one first enzyme is immobilized with respect to the first nanomaterial by a microwave-assisted process; and wherein the at least one second enzyme is immobilized with respect to the second nanomaterial by a microwave-assisted process.
The present disclosure also provides for a biofuel cell system, wherein the at least one first enzyme immobilized with respect to the first nanomaterial as the anode includes glucose oxidase (GOx); and wherein the at least one second enzyme immobilized with respect to the second nanomaterial as the cathode includes bilirubin oxidase (BOD). In one embodiment, the electrolyte includes 100 mM β-D-glucose in pH 7 phosphate buffer. In an alternative embodiment, present disclosure provides for a biofuel cell system, wherein the at least one first enzyme immobilized with respect to the first nanomaterial as the anode includes glucose oxidase (GOx); and wherein the at least one second enzyme immobilized with respect to the second nanomaterial as the cathode includes laccase.
The present disclosure also provides for a biofuel cell system, wherein the first and second substrates are silicon. In an alternative embodiment, the first and second substrates are porous silicon. In another embodiment, the first and second substrates are polymeric substrates. In another embodiment, the first and second substrates are nanotube membranes.
The present disclosure also provides for a biofuel cell system, wherein the first and second nanomaterials are vertically oriented on the first and second substrates.
The present disclosure also provides for a biofuel cell system, wherein at least one micro-fluidic channel is located on the first substrate, and wherein at least one micro-fluidic channel is located on the second substrate. In one embodiment, the at least one micro-fluidic channel located on the first substrate suctionally communicates with the first nanomaterial, and the at least one micro-fluidic channel located on the second substrate suctionally communicates with the second nanomaterial.
The present disclosure also provides for a biofuel cell system further including at least two fullerene molecules, wherein at least one fullerene molecule is chemically tethered to the first nanomaterial, and wherein at least one fullerene molecule is chemically tethered to the second nanomaterial.
The present disclosure also provides for a biofuel cell system further including a porous polymer, and wherein the electrolyte is immobilized in the pores of the porous polymer. In one embodiment, the porous polymer is poly-tetrafluoroethylene (PTFE). In another embodiment, the biofuel cell system further includes a porous polymer, wherein the electrolyte is immobilized in the pores of the porous polymer, and wherein the biofuel cell system is utilized as an implanted device.
The present disclosure also provides for a biofuel cell system further including a bio-compatible polymer, wherein the bio-compatible polymer encompasses the biofuel cell system. In one embodiment, the biofuel cell system further includes a bio-compatible polymer, wherein the bio-compatible polymer encompasses the biofuel cell system, and wherein the biofuel cell system is utilized as an implanted device.
The present disclosure also provides for a method for producing a nanomaterial substrate system including: providing nanomaterial on a substrate, utilizing a catalyst deposition step to deposit catalyst/promoter precursor on the substrate, utilizing a chemical vapor deposition (“CVD”) step, and immobilizing at least one enzyme to the nanomaterial. In one embodiment, the nanomaterial is selected from the group consisting of single wall carbon nanotubes (SWNTs), multiwall carbon nanotubes (MWNTs), carbon nanohorns, fullerenes, nano onions, nanocomposites and combinations thereof.
The present disclosure also provides for a method for producing a nanomaterial substrate system, wherein the substrate is silicon. In another embodiment, the substrate is porous silicon. In another embodiment, the substrate is a polymeric substrate. In another embodiment, the substrate is a nanotube membrane.
The present disclosure also provides for a method for producing a nanomaterial substrate system, wherein the nanomaterial is vertically oriented on the substrate.
The present disclosure also provides for a method for producing a nanomaterial substrate system, wherein the catalyst/promoter precursor is deposited on the substrate with a dip coating technique. In another embodiment, the catalyst/promoter precursor is deposited on the substrate with a spin coating technique.
The present disclosure also provides for a method for producing a nanomaterial substrate system, wherein the chemical vapor deposition (“CVD”) step includes ethanol chemical vapor deposition.
The present disclosure also provides for a method for producing a nanomaterial substrate system, wherein the at least one enzyme includes β-NAD (nicotinamide adenine dinucleotide) synthetase.
The present disclosure also provides for a method for producing a nanomaterial substrate system, further including the step of utilizing the nanomaterial substrate system as a biosensor.
The present disclosure also provides for a method for producing a nanomaterial substrate system, further including the step of utilizing the nanomaterial substrate system as an enzymatic sensing electrode in a biofuel cell.
The present disclosure also provides for a method for producing a nanomaterial substrate system, further including the step of utilizing the nanomaterial substrate system as a glucose biosensor in a biofuel cell consisting of a platinum electrode, wherein the nanomaterial includes SWNTs and the at least one enzyme includes glucose oxidase (GOx).
The present disclosure also provides for an electrode including a nanomaterial vertically oriented on a substrate, having at least one enzyme immobilized with respect to the nanomaterial. In one embodiment, the nanomaterial is selected from the group consisting of single wall carbon nanotubes (SWNTs), multiwall carbon nanotubes (MWNTs), carbon nanohorns, fullerenes, nano onions, nanocomposites and combinations thereof.
The present disclosure also provides for an electrode, wherein the at least one enzyme is immobilized with respect to the nanomaterial by an electrochemical process. In another embodiment, the at least one enzyme is immobilized with respect to the nanomaterial by a microwave-assisted process.
The present disclosure also provides for an electrode, wherein the substrate is selected from the group consisting of silicon, porous silicon, polymeric substrates, and nanotube membranes. In another embodiment, at least one micro-fluidic channel is located on the substrate. In another embodiment, the at least one micro-fluidic channel located on the substrate suctionally communicates with the nanomaterial.
The present disclosure also provides for an electrode, wherein the electrode is utilized as an enzymatic sensor in a biofuel cell. In another embodiment, the electrode is utilized as a nanoelectrode in an electrochemical cell. In another embodiment, the electrode is utilized as a biosensor. In another embodiment, the electrode is utilized in a biofuel cell.
To assist those of ordinary skill in the relevant art in making and using the subject matter hereof, reference is made to the appended drawings, wherein:
The present disclosure provides for a method of forming, producing or manufacturing functionalized and soluble nanomaterials, most specifically carbon nanotubes on a substrate, which can be used in the production or manufacture of biofuel cells. In one embodiment, the substrate is a doped silicon wafer. In another embodiment, the substrate is a gold-coated polymeric substrate. In another embodiment, the substrate is a free-standing nanotube membrane.
One embodiment of the present disclosure provides for the coupling of biofuel cells with a nanomaterial, wherein the nanomaterial supports catalytic enzymes. In one embodiment, carbon nanotubes are used to support catalytic enzymes. This integrated biofuel cell eliminates the need for expensive electron-transfer mediators, and can also function as a biosensor.
Another embodiment of this disclosure utilizes microwaves to couple or bond enzymes to the nanotubes to give efficient fuel cell and biosensor performance, thereby permitting non-compartmentalized biofuel cell and biosensor performance without the use of membranes.
Another embodiment of the present disclosure provides for the construction of a biofuel cell, wherein the application of a microwave process, and/or an electrochemical technique, is used to develop a biofuel cell having nanomaterial/enzyme-based electrodes on a substrate. In one embodiment, the substrate is an electrochemically fabricated porous silicon wafer platform. This embodiment provides efficient microfluidics at low cost. Another embodiment of the biofuel cell involves the growth of vertically-aligned SWNTs on etched porous silicon membranes having nano- and micro-scale hierarchies of fluidic channels, which can be used as-prepared, or alternatively transferred by contact removal techniques to flexible polymeric substrates.
Another embodiment provides for the application of a microwave process, and/or an electrochemical technique, to build a biofuel cell with nanomaterial/enzyme-based electrodes on flat and porous silicon wafers. In an alternative embodiment, the nanomaterial/enzyme-based electrodes are contact-transferred to conductive plastic substrates having micro-machined channels. These channels enable nanoscale fluidic transport of the biofuel (glucose, for example), oxidizer (oxygen, for example) and reaction products (primarily water, for example) at the electrodes.
In another embodiment of the present disclosure, a series of micro-wells and microfluidic channels on the substrate facilitate the holding of nanotubes in place on the substrate using suction. In one embodiment, these micro-wells and micro-fluidic channels are located on the substrate, which could include, but is not limited to, a doped silicon wafer. In another embodiment, these micro-wells and micro-fluidic channels are created by an electrochemical etching process.
Another embodiment of the present disclosure provides for a composite of nanomaterial grown on a substrate, coupled to tethered or bonded enzymes, to fabricate direct electron transfer electrodes. In another embodiment, this disclosure provides for a bio-inorganic composite of vertically oriented single wall carbon nanotubes grown directly on conductive silicon wafers, coupled to tethered or covalently bonded enzymes resulting from a rapid microwave process, which makes it possible to fabricate chemically stable, direct electron transfer electrodes. This composite overcomes non-uniform dispersion of SWNTs in the matrix and poor interfacial bonding. Accordingly, this bio-inorganic composite is a candidate for structural reinforcements in the fabrication of high strength, light weight, and high performance composites.
Another embodiment of this disclosure provides for a biofuel cell which uses enzymes immobilized on nanomaterials as electrodes. In one embodiment, this disclosure provides for a biofuel cell which uses specific enzymes immobilized on the molecular-scale tips of oriented single walled carbon nanotubes (“SWNTs”) as electrodes. This construction permits quasi-one-dimensional ballistic conductivity of single wall carbon nanotubes in combination with their colossal molecular to nanoscale surface areas, which enhances biofuel cell performance. Additionally the high-rate direct electron transfer eliminates the need for an electron mediator.
Another embodiment of the present disclosure provides for an open, non-compartmentalized integrated biofuel cell that utilizes specific enzymes, such as, for example, glucose oxidase (GOx) and bilirubin oxidase (BOD), immobilized and stabilized by tethering on the molecular-scale tips of SWNTs as the anode and cathode. In one embodiment the anode could consist of GOx functionalized, oriented SWNTs on silicon and the cathode could consist of oriented SWNTs on silicon, and functionalized with BOD. These anode and cathode enzymes are immobilized and stabilized by tethering on the molecular-scale tips of SWNTs. Immobilization involves, for example, bonding the enzymes to the nanotubes. The one-dimensional ballistic electrical conductivity of the carbon nanotubes enables high rate direct electron transfer, which eliminates the need for expensive and sometimes unstable compounds or biochemically engineered enzymes needed for electron transfer.
Alternatively, the electron transfer in nanomaterials is achieved by chemical tethering the structurally compatible fullerene molecules to the nanomaterial. In another embodiment, the electron transfer in SWNTs is achieved by chemical tethering the structurally compatible fullerene C60 molecules to the nanotube walls. C60 has a highly delocalized, three-dimensional electronic structure, which is very suitable for efficient electron transfer because the uptake and release of electrons results in minimal structural and property changes. Moreover, the covalently bonded tethering of the enzymes allows for non-compartmentalized operation without the need for proton exchange membranes.
Another embodiment of the present disclosure provides for an implanted device system, wherein the electrolyte is immobilized in the pores of a porous polymer, such as, for example, poly-tetrafluoroethylene (PTFE). In another embodiment of an implanted device system, the biofuel cell is wrapped in a bio-compatible polymer. In one embodiment, the implanted device system includes leads connecting to a biomedical device.
The present disclosure includes the application and method of forming, producing or manufacturing rapidly functionalized and highly soluble nanomaterials, more specifically carbon nanotubes, as well as a microwave process and the composites/composite building methods, discussed in U.S. Non-Provisional Utility patent application Ser. No. 11/374,499 filed Mar. 13, 2006 which claimed the benefit of U.S. Provisional Application No. 60/660,802 filed Mar. 11, 2005; U.S. Provisional Application No. 60/767,564 filed Jan. 10, 2006; and U.S. Provisional Application No. 60/767,565 filed Jan. 10, 2006, all of which are herein incorporated in their entirety. These processes are incorporated into at least one embodiment of the present disclosure. In an alternative embodiment, this disclosure also provides for an electrochemical technique, to produce a biofuel cell.
The present disclosure also provides a method for producing a nanomaterial-substrate system. In one embodiment, a method for growing nanomaterials on a substrate and attaching at least one enzyme to the nanomaterial is disclosed. For example, this nanomaterial-substrate system may be used in a biofuel cell system or as a biosensor. In one embodiment, the substrate is a gold-coated polymeric substrate. In another embodiment, the substrate is a free standing nanotube membrane.
In another embodiment, the present disclosure provides for the growth on thin films of vertically aligned SWNTs on silicon wafers using a chemical vapor deposition (“CVD”) process with ethanol as the carbon source and densely deposited bimetallic cobalt/molybdenum as catalyst. In one embodiment, glucose oxidase (GOx) and bilirubin oxidase (BOD) enzymes dissolved in a buffer are reacted with the nanotube tips by a rapid microwave process. In an alternative embodiment, GOx and BOD enzymes dissolved in a buffer are reacted with the nanotube tips by an electrochemical reaction.
In another embodiment of the present disclosure, the assembly of a non-compartmentalized glucose/air biofuel cell with SWNT/GOx as anode and SWNT/BOD as cathode in an electrolyte comprised of 100 mM β-D-glucose in pH 7 phosphate buffer is disclosed.
The present disclosure also provides for a biofuel cell that may be utilized as a biosensor. In one embodiment, the biofuel cell may be utilized as a glucose biosensor consisting of a SWNT/GOx sensing electrode. In one embodiment, the biofuel cell may be utilized as a glucose biosensor consisting of a platinum electrode.
Microwave Induced Functionalization of Highly Water-Dispersible Carbon Nanotubes
The functionalization of the nanomaterial, specifically carbon nanotubes, serves several functions. Materials such as carbon nanotubes are inert and do not mix and blend easily in most matrices. They are not soluble either, so they can not be processed easily either in, for example, thin films or polymer composites. Functionalization allows the chemical structure of the nanotubes to be modified, and other functional groups, including, but not limited to, polymers, ceramics, biological molecules such as enzymes and other appropriate chemical moeties to be attached.
For the purposes of this application “nanomaterials” can include, but is not limited to, single wall nanotubes (SWNTs), multiwall nanotubes (MWNTs), nanohorns, fullerenes, nano onions and nanocomposites. These nanomaterials also include but are not limited to carbon based nanomaterials such as carbon nanotubes and carbon SWNTs.
In another embodiment, the functionalization may be covalent bonding to the nanotube, or noncovalent adsorption or wrapping. By putting appropriate functionalities, the nanotubes may be rendered soluble in, for example, aqueous, organic, polar, nonpolar, hydrogen bonding, ionic liquids, and other solvents so that they can be processed easily. For example, polymer or ceramic precursors or the like may also be reacted with the nanotubes to form composites, or biological molecules may be attached for drug delivery, sensing or other functions.
The current disclosure provides for, in one embodiment, a rapid and environmentally friendly, microwave induced method, to prepare highly water-dispersible carbon nanotubes. In one embodiment, microwave-assisted functionalization of SWNTs in a mixture of acidic components can be utilized to generate water-dispersible nanotubes. In a further embodiment, microwave-assisted functionalization of SWNTs in a mixture of nitric and sulfuric acids can be utilized to synthesize highly water-dispersible nanotubes with stable concentrations as high as 10 mg/ml in approximately three minutes. The microwave processing time depends on the diameter of the starting SWNTs employed.
In one embodiment, the starting SWNTs were prepared by the high pressure carbon monoxide (HiPCO) chemical vapor deposition process, as described in Nikolaev, P.; Bronikowski, M. J.; Bradley, R. K.; Rohmund, E.; Colbert, D. T.; Smith, K. A.; Smalley, R. E. Chem. Phys. Lett. 1999, 313, 91 and Bronikowski, M. J.; Willis, P. A.; Colbert, D. T.; Smith, K. A.; Smalley, R. E. J. Vac. Sci. Technol. 2001, A19, 1800, which herein are incorporated by reference. The original or starting SWNTs were not soluble (or dispersible) in de-ionized (DI) water, or alcohol even after prolonged sonication. Suspensions were formed where the SWNTs quickly agglomerated and settled down to the bottom of the container. This embodiment could occur in approximately three minutes.
In one embodiment, the experiments resulting in functionalization and stable dispersion were carried out in a CEM Model 205 microwave oven with a 100 ml closed-vessel reaction chamber lined with Teflon PFA®, and connected to a 0˜200 psi pressure control system. The microwave system could be programmed to operate at different pressures, power levels and time periods. For this embodiment 200 psi pressure and 900 Watts of power were used.
In one reaction of this embodiment, 10 to 20 mg of as-received, pure SWNTs were added to 20 ml of a 1:1 mixture of 70% nitric acid and 97% sulfuric acid aqueous solutions in the reaction chamber. The microwave power was set at 50% of a total of 900 Watts, and the pressure was set at 20 psi. The reaction vessel was then subjected to microwave radiation for 1, 2, 3, 5, 10 and 20 minutes. Functionalization of the SWNTs as determined by FTIR spectroscopy and the dispersion of SWNTs were not observed when the SWNT-acid mixture was not subjected to microwave radiation. Under these conditions three minutes of microwave irradiation was found to be the optimum time for the reaction however by way of example only, the reaction could be conducted in a range of approximately three to fifteen minutes.
At the three minute reaction time, under the described conditions, a large fraction of the SWNTs dispersed in the acid mixture with minimal loss of nanotubes due to microwave-induced oxidation occurred. The mixture was then diluted with DI water, filtered through a 10 μm polytetrafluoroethylene (PTFE) filter paper, and the filtrate was transferred to a dialysis bag with nominal molecular weight cut off of 12,000-14,000 daltons. The bag was placed in a beaker containing DI water. The DI water was continually replaced until the pH of the filtrate in the bag reached 7. The filtrate was then removed and concentrated in a vacuum evaporator. The functionalized solid SWNT residue obtained from the evaporator was dried overnight at room temperature in vacuum and used for quantitative solubility testing, and for the characterization measurements discussed below.
Field emission scanning electron microscope (SEM) images were taken using a LEO 1530 electron microscope, and transmission electron microscope (TEM) images were recorded using a TOPCON 200 kV ultra-high resolution microscope. The SEM images were obtained on microwaved SWNTs deposited on a conducting silicon wafer from a concentrated aqueous solution of the nanotubes, while the TEM images were obtained on thin films deposited on TEM grids from a dilute methanol solution of the microwaved SWNTs.
The infrared and Raman spectra were recorded using a Perkin Elmer FTIR spectrometer and a Horiba/Jovin Yvon Lab Ram system with 632.8 nm excitation, respectively. FTIR measurements were made on thin films deposited from a methanol solution of SWNTs on a single crystal sodium chloride plate. The Raman spectra were measured on aqueous solutions of the microwaved SWNTs and on the functionalized SWNT solids. The thermogravimetric analyses (TGA) were performed using a Universal V3.7A instrument on pristine and microwave functionalized SWNTs.
Laser light scattering particle size measurements on aqueous solutions of microwave functionalized SWNTs were performed with a Beckman Coulter N4 Plus Submicron Particle Size Analyzer, which has an effective detection range from 3 to 800 nm. Sheet electrical conductivities along SWNT membrane surfaces, which all have an area of 2.54×2.54 cm2, were measured. The free standing SWNT membranes were self-assembled, washed, dried and removed after slow vacuum filtration of dispersions and suspensions of the nanotubes in water through PTFE filter paper. Two silver pads deposited on the membrane were used as the electrical contacts. The average membrane thicknesses were measured using a micrometer.
The acid-functionalized SWNTs obtained after microwave treatment were highly dispersible in DI water and ethanol under ambient conditions. Dispersed concentration of 10 and 2.5 mg per milliliter (ml) were obtained in water and anhydrous alcohol respectively. A significantly higher concentration up to 20 mg per ml was obtained in acidified water. The dispersions showed no indication of SWNT precipitation after prolonged standing (months) under ambient conditions. Photographs of typical aqueous dispersions of different concentrations of the microwave functionalized SWNTs are shown in
Laser light scattering particle size measurements at detection angles of 62.2 and 90 degrees of the aqueous dispersions of microwave functionalized SWNTs were compared with measurements made on an aqueous suspension of pristine SWNTs. The suspension prepared by sonication of 0.01 weight % SWNTs (0.1 mg per ml) and 0.5 weight % of the surfactant Triton X-100 showed particle sizes ranging from 100 to 600 nm with a maxima at 300 nm. In contrast, a 0.5 mg/ml aqueous dispersion of microwave functionalized SWNTs (
SEM images of the microwave functionalized SWNT bundles are shown in
In order to characterize the electronic states of the microwave functionalized SWNTs, visible-near infrared (vis-NIR) absorption spectra of aqueous dispersions and of a suspension of pristine SWNTs in dimethylformamide were measured. The spectra are shown in
The effect of thermal treatment on the functionalized SWNTs was studied by thermogravimetric analysis (TGA) measurements and compared with pristine SWNTs. The heating was carried out under dry nitrogen at a heating rate of 10° C. per minute from 30° to 500° C. The TGA traces (shown in
The conductivity of membranes fabricated from both pristine SWNTs and microwave treated SWNTs were measured and compared. The pristine SWNT membrane was made from an aqueous SWNT suspension in a surfactant (Triton-X 100). The surfactant was removed by washing with DI water and methanol, and annealing at 700° C. under argon for one hour. The membrane made from microwave treated SWNTs was fabricated in two steps. In the first step, 150 mg of pristine SWNTs was added to 30 ml of the acid mixture described above, and microwaved for 3 minutes. The acids were removed by filtration and washing with DI water. Then, the SWNTs collected were suspended in water by sonication in a water bath in the absence of a surfactant, and a membrane was deposited by filtering through a PTFE filter paper (0.5 μm pore size).
Part of the membrane made from microwave treated SWNTs was also annealed at 700° C. under argon for one hour. Both the annealed and unannealed microwaved SWNT membranes along with the annealed pristine SWNT membrane were used for the conductivity measurements. The measurement set-up is schematically shown as the inset in
It was also observed that aqueous dispersions of microwave functionalized SWNTs were electrically conductive with an ionic conductivity in DI water of 215.8 μS relative to that of 1.5 μS for pure DI water. This raises the possibility for electrical manipulation (such as, electrodeposition of thin films) of the SWNTs from a solution phase. Another interesting observation was that the microwave functionalized SWNTs showed very low concentrations of left over iron from the starting catalyst as determined by ferromagnetic magnetic resonance (FMR) spectroscopy, which is extremely sensitive to the presence of magnetic particles. The starting HiPCO-prepared SWNTs showed a strong FMR signal indicating the presence of a significant concentration of the iron catalyst. The low residual concentration may be due to small amounts of iron, which remained trapped in the interstitial sites of the thin SWNT bundles.
For this embodiment, it can be concluded that microwave treatment of a suspension of starting SWNTs in a 1:1 mixture of 70% nitric acid and 97% sulfuric acid in water was found to form carboxylated and acid sulfonated SWNTs with relatively high dispersivity in DI water and ethanol. Elemental analysis indicated that every third and tenth carbon atoms on the SWNT structure were carboxylated and sulfonated, respectively. Some reduction in average length of the nanotubes, sidewall disordering, and extensive debundling due to functionalization, were also observed. Thermogravimetric measurements to 500° C. showed the loss of the functional groups, suggesting that structural order on the sidewalls can be restored by thermal treatment. The loss in electrical conductivity after microwave treatment can be fully recovered after high temperature annealing in argon. The results also indicate the removal of a large fraction of the iron catalyst particles during the microwave treatment. The very high dispersivity in polar solvents will enable SWNTs to be more easily processed during, for example, chemical and biochemical reactions, physical blending, and thin film/nanocomposite formation. Moreover, their alignment during deposition as a thin film from aqueous suspension will allow the fabrication of a variety of nanoscale device architectures and aligned nanocomposite structures.
Nanomaterial Substrate System
The present disclosure also provides a method for producing a nanomaterial-substrate system. In one embodiment, a method for growing nanomaterials on a substrate and attaching at least one enzyme to the nanomaterial is disclosed. The nanomaterial-substrate system may be used in a biofuel cell system or as a biosensor, for example. In one embodiment, a method for producing a nanomaterial-substrate system includes providing nanomaterial on a substrate, utilizing a catalyst deposition step to deposit catalyst/promoter precursor on the substrate, utilizing a chemical vapor deposition step, and then attaching at least one enzyme to the nanomaterial is disclosed.
In the following examples, the nanomaterials were grown using two different catalyst deposition methods, followed by ethanol chemical vapor deposition (“CVD”).
In one embodiment, a method for growing individual, vertically aligned SWNTs on silicon and attaching at least one enzyme to the tube ends of the SWNTs is disclosed. In one embodiment, thin films of vertically aligned individual SWNTs were deposited on silicon using a CVD process. Oriented SWNT growth was achieved with two methods of catalyst precursor self-assembly followed by ethanol CVD. Using the silicon substrate as the working electrode in an electrochemical cell and the enzyme β-NAD (nicotinamide adenine dinucleotide) synthetase dissolved in a buffered electrolyte solution, the enzyme was attached at the nanotube ends. Enzyme immobilization on the 1 to 2 nm diameter tube ends of the individual SWNTs allows for dense packing of the enzyme and utilization of the electrode as an enzymatic sensor in a biofuel cell configuration.
In one embodiment, bimetallic cobalt (Co): molybdenum (Mo) with 1:1 or 1.6:1 in atomic weight ratio was used as catalyst/promoter for the growth of SWNTs. The catalyst/promoter precursors were deposited by dip or spin coating techniques. The dip-coating precursor was prepared by suspending and sonicating a mixture of Co and Mo acetates in chloroform containing 0.02 wt % of metals to total solution. The dip coating process involved immersing a silicon wafer in the mixture and slowly pulling it out after 5 to 10 minutes.
The spin-coating precursor was prepared using different amounts (between 0.02 to 0.1 wt %) of metal to total solution with varying amounts of poly-vinylpyrollidone (PVP) in 90% ethanol. To prepare the catalyst/promoter precursor solution, cobalt nitrate and ammonium heptamolybdate were first dissolved in water. PVP was then added and dissolved in the clear cobalt nitrate and molybdate solution. After that, nine times of ethanol to water in volume ratio was added to the solution. The solution obtained was then spin-coated onto a Si wafer at a spinning speed of 3000 rpm. After removing the PVP polymer by heating in air to 800° C. at a heating rate of 5° C./min. and holding at 800° C. for 2 hours, the catalyst/promoter-coated substrate was transferred to the CVD system for SWNT growth.
The same SWNT growth conditions were employed for both dip- and spin-coated catalyst/promoter precursors. The CVD process involved decomposition and reduction of the catalyst/promoter precursors under flowing hydrogen (100 sccm flow rate at 1 atm.) at 800° C. followed by SWNT growth for 20 min. at the same temperature using ethanol transported by argon (300 sccm flow rate at 1 atm) as the carbon source.
Electrochemical functionalization with the enzyme, β-NAD (nicotinamide adenine dinucleotide) synthetase was carried out in a three-electrode cell, with 0.1 M of KCl used as the electrolyte. In this embodiment, the reaction was carried out in 80 ml of pH 7 phosphate buffer (40 mM) with 50 mg of the enzyme. A Si wafer with oriented SWNTs was used as the working electrode, with a platinum wire as counter electrode and a saturated calomel electrode (SCE) as reference electrode. Cyclic voltammetry (CV) was carried out at a scan rate of 50 mV/s in the range between −1V to 1V using a computer-controlled Elchema PS-205B potentiostat-galvanostat. After reaction, the SWNT electrode was rinsed with distilled water and dried in air.
The transmission electron microscope (TEM) images were obtained using a 200 kV High Resolution Transmission Electron Microscope. Scanning electron microscopy (SEM) was carried out using a LEO 1530 instrument and Raman spectroscopy using a Horiba/Jobin Yvon LabRaman system with 632.8 nm laser excitation.
For this embodiment, ethanol was chosen as the carbon source due to the fact that the OH radicals formed on decomposition removes amorphous carbon and thus reduces the formation of carbon soot during the growth process. 0.02 wt % each of Co and Mo in chloroform was found to be the best dip-coating catalyst/promoter precursor composition for the growth of vertically oriented SWNTs.
A high degree of vertical orientation of SWNTs on Si was obtained with 0.05 wt % each of Mo and Co together with 1 wt % of PVP in 90% ethanol of catalyst/promoter precursors.
Raman spectra taken from the aligned SWNT samples using 632.8 nm excitation were consistent with the formation of SWNTs using both catalyst/promoter deposition methods.
Parameters, such as, for example, catalyst/promoter particle density, size, location and reactivity are variables for the formation of well-aligned, vertically grown SWNTs. Immobilization by the polymer PVP leads to uniform, nanometer size catalyst/promoter particles (
A Si substrate with oriented SWNTs obtained from the dip-coating catalyst/promoter was used to electrochemically react with the enzyme, β-NAD synthetase. The reaction was carried out as discussed in the experimental section for 10 scan cycles between −1 V to +1 V. The CV curve was reproducible for each scan.
a shows a typical SEM image from the enzyme functionalized SWNT films. The bottom half of the image, which is lighter than the top half, is from the enzyme functionalized SWNTs. The enzyme appears to be uniformly attached to the oriented nanotube ends. However, some enzyme aggregation was also found in some spots, as shown in the higher magnification image in
The demonstration of electrochemical tethering of a FAD-based enzyme to densely packed and vertically aligned largely individual SWNTs on a silicon chip opens up the possibility of using such a platform for nanoscale biosensing—an application involving nanoscale electronics. One embodiment uses the SWNT-enzyme on silicon as an enzymatic sensing electrode in a biofuel cell configuration. An alternative embodiment uses the fabricated SWNT-enzyme platform as a working nanoelectrode in an electrochemical cell. This embodiment provides for monitoring changes in the cyclic voltammogram to detect biological agents that interact specifically with selected enzymes.
An Open, Non-Compartmentalized Biofuel Cell
In another embodiment, the present disclosure also provides for the coupling of biofuel cells with a nanomaterial, wherein the nanomaterial supports catalytic enzymes. In one embodiment, biofuel cells are coupled with nanotechnology wherein individual carbon nanotubes are used to support catalytic enzymes. This integrated biofuel cell eliminates the need for expensive electron-transfer mediators, and may also function as a biosensor.
In another embodiment, a nanotechnology biofuel cell is created by the application of microwaves to rapidly couple or bond selected enzymes to the nanotubes to give efficient fuel cell and biosensor performance. This combination facilitates non-compartmentalized biofuel cell and biosensor performance without the use of ion-exchange membranes.
In another embodiment, a nanotechnology-based biofuel cell is constructed on an electrochemically fabricated porous silicon wafer platform. This embodiment allows efficient micro- and nano-scale fluidics at low cost.
Another embodiment provides for a biofuel cell that uses specific enzymes immobilized on the molecular-scale tips of oriented single walled carbon nanotubes as electrodes. This construction permits quasi-one-dimensional ballistic conductivity of single wall carbon nanotubes in combination with their colossal molecular to nanoscale surface areas, which enhances biofuel cell performance. Additionally the high rate direct electron transfer eliminates the need for an electron mediator and concomitantly leads to enzyme stability.
In one embodiment, the open, non-compartmentalized integrated biofuel cell utilizes specific enzymes, such as, for example, GOx and BOD, immobilized and stabilized by tethering on the molecular-scale tips of SWNTs as the anode and cathode. In this embodiment, the anode could consist of, for example, GOx functionalized, oriented SWNTs on silicon and the cathode could consist of, for example, oriented SWNTs on silicon, and functionalized with BOD. These anode and cathode enzymes are immobilized and stabilized by tethering on the molecular-scale tips of SWNTs. Immobilization involves bonding the enzymes to the nanotubes.
For this embodiment, where the anode consists of GOx functionalized, oriented SWNTs on silicon and the cathode consists of oriented SWNTs on silicon functionalized with BOD, a basic phosphate buffer was used as liquid electrolyte.
Without the addition of biofuel oxidant between the two electrodes, an observed maximum current of 40 nA (1 cm2 working area) and an observed maximum open circuit voltage of 280 mV were noted. After the addition of β-D-glucose, the output increased to about 80 nA current and 480 mV open circuit voltage, indicating direct transfer fuel cell action via the aligned nanotubes. It is noteworthy that sizable fuel cell performance was achieved without the use of an electron transfer layer. A fuel cell polarization curve (not shown) for such a cell shows that about 1 micro-watt of power can be extracted from the cell comparable to that obtained from lithium iodine batteries currently in use with cardiac pacemakers. An initial demonstration of glucose detection has also been performed with the oriented SWNT/enzyme electrodes functioning as the sensing element.
In accordance with this embodiment, the growth of SWNTs, whose individual diameters are in the 1-2 nm range within bundles or ropes, in a perpendicularly aligned manner on silicon substrates has been achieved and is shown in
After applying the low power microwave method described previously, the resulting electrodes were tested in a non-compartmentalized biofuel cell shown schematically in
The embodiments generated as a result of the presently disclosed microwave method, illustrate the high “ballistic” conductivity of electrons within the one-dimensional structure of the nanotubes which direct the electron transfer without requiring expensive complex electron-transfer mediators.
Additionally, in one embodiment, GOx provides efficient biocatalyzed oxidation of glucose that is unaffected by oxygen, enabling the anode to operate in the presence of oxygen. Thus, in one embodiment, the biofuel cell uses O2 as an oxidizer and glucose as a fuel without the need for compartmentalization.
In another embodiment, since the biofuel cell is non-compartmentalized, it can be used for both in vitro and ex vitro applications. For example, the biofuel cell configuration allows the construction of an in vitro electrical energy generation device utilizing glucose as fuel and O2 from the blood stream as oxidizer. Such in vitro electrical energy generation devices may be power sources for implantable devices, including, but not limited to, pacemakers or insulin pumps. However, more efficiency can be achieved via the use of thin Nafion® polymer electrolyte membranes to compartmentalize the cell for ex vitro or external applications, and the use of porous silicon wafers with electrochemically etched channels (
Another embodiment of this disclosure is the use of a biofuel cell as a biosensor. Biofuel cells can also operate as biosensors (
Another embodiment provides for the fabrication and characterization of a membrane-free, direct electron transfer glucose oxidation and oxygen reduction enzymatic biofuel cell. This disclosure provides for a bioelectrode design comprised of a porous silicon (“p-Si”) current collecting flow-field platform on which either single-walled or multiwalled carbon nanotubes (“SWNTs” and “MWNTs”, respectively) were grown and then functionalized with carboxylic groups. Anodic and cathodic enzymes: glucose oxidase (GOx) and laccase, respectively, were then electrochemically immobilized on the nanotube sidewalls and tips. Membrane-free biofuel cells consisting of p-Si/SWNTs or p-Si/MWNTs electrodes with immobilized GOx and laccase were studied with 4 mM glucose in pH 7 buffer solution as fuel and oxygen as oxidant.
One embodiment provides for the electrodeposition technique of directly immobilizing GOx and laccase onto the p-Si/CNT electrodes after initially acid-treating the electrodes to form carboxylic groups at the CNT tips and defects on the sidewalls. Cyclic voltammetry was used to monitor the redox reactions between the enzymes and the CNTs indicating immobilization via covalent interaction between the carboxylic group and the amine linkage on the enzyme.
Membrane-less CNT-based biofuel cells were set up and tested. Two types of cells: p-Si/SWNTs/GOx|p-Si/SWNTs/laccase and p-Si/MWNTs/GOx|p-Si/MWNTs/laccase, were assembled and their electrical characteristics were determined.
Pristine (111) n-doped silicon wafers (resistivity, ˜0.005 Ω-cm, ˜1 cm2 in area) were used to fabricate porous Si by an anodic etch in HF/ethanol 1:1 (v/v) solution. Electrochemical etching was performed by controlling the current density at 200 mA/cm2 for 30 minutes. The wafers with a black porous layer were then removed and washed extensively with deionized water to remove HF.
SWNT membranes were prepared using pre-synthesized SWNTs obtained from Carbon Nanotechnologies Inc. The SWNT solids were suspended in water to which 0.5 volume % surfactant Triton X was added. The suspension was sonicated for 15 minutes and then vacuum filtered through Teflon-coated filter paper with average pore sizes of 0.1 μm. A self-assembled sheet of SWNTs was left on the filter paper, which was peeled off after drying in air.
Both single and multiwall carbon nanotubes were grown on the porous silicon wafers by chemical vapor deposition (“CVD”) using ethanol as the carbon source and argon as the carrier gas at an elevated temperature of 700° C. for 10 minutes. Prior to CNT growth, catalyst cobalt and promoter (molybdenum) precursor solutions were deposited on p-Si by spin coating at 2000 rpm for 40 seconds. The solutions were prepared using 0.05 wt % and 0.075 wt % of Co [from cobalt (II) nitrate] and Mo (from heptamolybdate tetrahydrate) to 1 wt % of polyvinyl pyrollidone (PVP) in 90% ethanol. Either SWNTs or MWNTs can be formed depending on the average size of the Ni/Mo particles produced. A combination of SEM imaging and Raman spectral characterization was used to characterize the nature of the CNTs produced.
The CNTs on p-Si substrates were functionalized with carboxylic groups by sonication in concentrated HNO3 for 5 minutes followed by washing with distilled water for 10 minutes at room temperature. Enzyme electrochemical immobilization reactions were performed with a computer-controlled Elchema PS 205B Potentiostat/Galvanostat system using a three electrode cell, which included the p-Si/CNTs working electrode, Pt counter electrode and a saturated calomel electrode (SCE) as the reference electrode. Cyclic voltammetry (CV) was used to demonstrate reduction-oxidation reactions. The working electrolyte solution used was 1 mg/ml of enzyme (GOx for anode and laccase for cathode for the p-Si based electrodes) in pH 7 phosphate buffer solution. The potential was swept from −1.0 V to 1.0 V and then back to −1 V.
The CNT membranes used as combined platform and electrode, were carboxyl group functionalized by sonication in nitric acid for 5 minutes followed by washing in de-ionized water for 10 minutes. GOx and Bilirubin Oxidase (BOD) enzymes were electrochemically immobilized on the membranes to form the biofuel cell anode and cathode respectively, as described for the p-Si based electrodes.
Two sets of electrodes: p-Si/MWNTs/GOx|p-Si/MWNTs/laccase and p-Si/SWNTs/GOx|p-Si/SWNTs/laccase were assembled to form membrane-less biofuel cells in order to evaluate their current-voltage and power output performance. In addition, a similar cell using a SWNT membrane was fabricated with the following configuration: SWNT membrane/GOx|SWNTmembrane/BOD. The current-voltage output of the biofuel cells were obtained at various resistive loads at a concentration of 4 mM glucose in pH 7.0 phosphate buffer with constant stirring and bubbling of air into the cell. The 1 cm by 1 cm anode and cathode electrodes were positioned 5 mm apart in the cells.
The cyclic voltammograms for GOx and laccase immobilization on both p-Si/MWNTs and p-Si/SWNTs substrates obtained according to the procedure described above showed well-defined redox peaks indicating enzyme immobilization and attachment (
The linear relationship of the peak current with the scan rate (inserted plots in
From the CV curves for p-Si/MWNTs/laccase and p-Si/SWNTs/laccase, it can be seen that the peak currents increased along with increase of scan rate, while ΔEp values were reduced (
All the CV curves indicated the existence of direct electron transfer between the p-Si/CNT electrode/platform system and the enzymes, but the direct electron transfer rates were lower than those for the reversible reaction. The peak currents increased and shifted with increasing scan rates resulting in a large separation potential ΔEp and asymmetry of the redox peaks in the curves, suggesting that the carboxyl-amine coupling reaction between the CNTs and enzyme occurs simultaneously with the electron transfer reaction. This may be due to the fact that chemical reaction occurs during potential sweeping resulting in slower kinetics of the electrochemical reaction. Equilibrium is therefore not established rapidly enough (in comparison to the voltage scan rate), giving rise to smaller peaks in the reverse scans. In addition, the p-Si substrate experiences a temperature of 700° C. in air for a short period during catalyst formation for CNT growth. This is likely to produce an oxide layer with poor interfacial conductivity, which would reduce the electron transport efficiency.
The two sets of electrodes discussed above: p-Si/MWNTs/GOx|p-Si/MWNTs/laccase and p-Si/SWNTs/GOx|p-Si/SWNTs/laccase were configured as biofuel cells according to the schematic shown in
The current-voltage data for the biofuel cells at different external loads are shown in
The extractable power from the biofuel cell (P=VcellIcell) is controlled by the cell voltage (Vcell) and cell current (Icell). The power (P) from the biofuel cells for different external loads is shown in
The present disclosure provides for the fabrication of direct electron transfer GOx and laccase-based biocatalysts on p-Si/CNT substrates using a direct electrochemical immobilization and attachment technique. Both directly grown SWNTs and MWNTs were used as direct electron transfer mediators. The cyclic voltammetry data showed that the p-Si/SWNT electrode provided better electron transfer efficiency compared to the p-Si/MWNT electrode. The method presented here can be extended to immobilize and electrochemically attach other enzymes. Membrane-less biofuel cells for two sets of electrodes: p-Si/MWNTs/GOx|p-Si/MWNTs/laccase and p-Si/SWNTs/GOx|p-Si/SWNTs/laccase were assembled and their performance was investigated. The electrical power generated by the p-Si/SWNTs/GOx|p-Si/SWNTs/laccase biofuel was higher than that of the p-Si/MWNTs/GOx|p-Si/MWNTs/laccase biofuel cell by three orders of magnitude.
In another embodiment, a SWNT membrane/GOx|SWNTmembrane/BOD biofuel cell using a highly conducting SWNT membrane functioning both as electrode and platform was constructed. The current-voltage behavior of such a cell is shown in
There are many advantageous properties and/or characteristics of the present disclosure. The advantageous properties and/or characteristics of the present disclosure include, but are not limited to the following. It should be noted that not every embodiment of the present disclosure contains all of the properties and/or characteristics listed below:
One advantage of the present disclosure is that biological fuel cells are engineered on a molecular scale. These biofuel cells are small and light weight because they convert the fuel and oxidants to benign byproducts with the generation of electricity, and they use concentrated sources of chemical energy from the blood stream, as opposed to battery powered devices.
In addition, biofuel cells provide a continuously renewable, tailored power source because the biological fuel cells are fueled by chemicals within the body itself. Accordingly, the biofuel cells can operate for long durations without the need for maintenance requiring surgical procedures, as are currently required with battery operated technologies, which is increasingly important with the trend towards the use of implantable electrical devices. An example of how this can be achieved is in an open, non-compartmentalized integrated biofuel cell that utilizes specific enzymes, such as GOx and BOD, immobilized and stabilized by tethering on the molecular-scale tips of SWNTs as the anode and cathode.
Another advantage is that the biofuel cell is non-compartmentalized. For example, this biofuel cell configuration allows the construction of an in vitro electrical energy generation device utilizing glucose as fuel and O2 from the blood stream as oxidizer. Such in vitro electrical energy generation devices may be power sources for implantable devices, including, but not limited to, pacemakers or insulin pumps. This biofuel cell configuration also permits ex vitro or external applications. For example, the biofuel cell efficiency can for ex vitro or external applications be achieved via the use of thin Nafion polymer electrolyte membranes to compartmentalize the cell and the use of porous silicon wafers with electrochemically etched channels.
Another advantage stems from the molecular scale and non-compartmentalized nature of the biofuel cell, which allows for versatility of use in a range of applications including, but not limited to: targeted drug delivery, physiological monitoring and control, synthetic organs, prostheses, and other advanced medical device concepts. Examples of the latter include, but is not limited to, pacemakers, insulin pumps, glucose and pressure sensors, and bionic devices for stimulating the brain and spinal cord. Biofuel cells could also power external devices attached to the skin, such as, for example, patches and intravenous devices for drug delivery.
Another advantage is a reduction of cost. An embodiment of the present disclosure provides a high “ballistic” conductivity of electrons within the one-dimensional structure of the nanotubes. This directs the electron transfer without requiring expensive and complex electron-transfer mediators. Previous fuel cells used expensive noble metals as catalysts, for example, platinum and ruthenium or the like. However, the presently disclosed biofuel cell uses biocatalysts such as, for example, enzymes, or even whole organisms, to catalyze the conversion of chemical energy into electricity.
Another advantage is that the biofuel cells typically operate at temperatures compatible with living organisms. Unlike battery powered devices which can harm surrounding tissues by resultant temperature increases, typically biofuel cells are compatible for use in living biological entities without harming tissues from the biofuel cell's operation.
High energy efficiency and stability are additional advantages of the presently disclosed enzymatic biofuel cells. An embodiment of the disclosed biofuel cell has efficient micro- and nano-scale fluidics due to the micro-channels. Additionally there is no cross-over of fuel across a polymer electrolyte membrane because in non-compartmentalized operation oxidation and reduction will be permitted to occur only on the anode and cathode, respectively. Also, the use of carbon nanotubes on which the enzymes are attached enable the enzymes to be more hardy and less fragile because the carbon nanotubes do not chemically interfere with immobilized enzymes as occurs with methods currently known in the art that use Nafion® membrane, thereby ensuring longer enzyme life. Accordingly this provides for higher power densities combined with extended lifetimes.
Nanomaterials and SWNTs have a more preferable alignment during deposition from solution due to the presently disclosed method. Carbon nanotubes maintain a specific geometry, cultivated on a silicon electrode platform as opposed to free-floating suspension. This geometry and alignment eases the complexity of the enzymes, while still retaining their chemical properties. Using carbon nanotubes with a specific geometry also makes access to the reaction centers within these enzymes simpler thereby facilitating and improving performance of the biofuel cell.
An embodiment of the presently disclosed biofuel cell also has the advantage of improved fluidics due to the use of the porous silicon base with nano-sized channels.
Enhanced applicability of carbon nanotubes in various applications is another advantage that arises from the functionalization of the carbon nanotubes. Since carbon nanotubes are naturally inert and do not mix and blend easily in most matrices, functionalization allows modification thereby increasing the uses of previously inert entities. Functionalization may also lead to more efficient purification/separation techniques, such as, for example, those based on chirality, or, the separation of metallic SWNTs from semi-conducting ones. More importantly, functionalization leads to the development of new classes of material with specificity for different physical and chemical properties.
Ease of processing is an advantage directly related to solubility, in both water and organic solvents, which results from the functionalization of the carbon nanotubes.
Rapid functionalization is another advantage. When practicing one of the disclosed methods of synthesis, the microwave-induced reaction occurs in a matter of seconds or minutes and can generate a high purity product with high, yield. This is advantageous because it makes the overall process cost effective. The reaction speed is partially due to rapid heating and even superheating at a molecular level. Side reactions are also eliminated as the bulk does not need to be heated.
Another advantage of an embodiment of the presently disclosed method of synthesis is that it induces a relatively low temperature microwave-induced reaction to soluble nanomaterials. The presently disclosed method of synthesis has the ability to operate at a low temperature, due in part to in-situ heating at the reaction site. This is advantageous because it leads to fast reaction kinetics and reactions that would not otherwise be possible.
The microwave process also provides the added benefit of being able to allow carbon nanotubes to immobilize enzymes quickly without the use of membranes which increases the efficiency of the biofuel cell and biosensor performance.
Microwave induced reactions as a means of nanotube functionalization and water-dispersion are also important from the standpoint of process development and scale-up. The ease of creating functionalized soluble nanomaterials increases production of nanomaterials at a reduced price, thereby enabling sufficient quantities to be produced for use in commercial goods as well as production at a cost that can be tolerated by consumer markets. Additionally the method in general reduces reaction time by orders of magnitude and provides high yield, thus adding to its cost effectiveness.
Another advantage to this method is that the synthesis, production and use are environmentally safer as it requires less energy and chemicals such as solvents. Specifically, the microwave process reduces the need for solvents.
Applicant has attempted to disclose all embodiments and applications of the disclosed subject matter that could be reasonably foreseen. However, there may be unforeseeable, insubstantial modifications that remain as equivalents. While the present invention has been described in conjunction with specific, exemplary embodiments thereof, it is evident that many alterations, modifications, and variations will be apparent to those skilled in the art in light of the foregoing description without departing from the spirit or scope of the present disclosure. Accordingly, the present disclosure is intended to embrace all such alterations, modifications, and variations of the above detailed description.
This application claims the benefit of U.S. Provisional Application No. 60/790,333 filed Apr. 7, 2006, all of which is herein incorporated in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 6515325 | Farnworth et al. | Feb 2003 | B1 |
| 6566704 | Choi et al. | May 2003 | B2 |
| 6616497 | Choi et al. | Sep 2003 | B1 |
| 6830981 | Lee et al. | Dec 2004 | B2 |
| 6838297 | Iwasaki et al. | Jan 2005 | B2 |
| 6858891 | Farnworth et al. | Feb 2005 | B2 |
| 6933222 | Dubin et al. | Aug 2005 | B2 |
| 6995046 | Rueckes et al. | Feb 2006 | B2 |
| 7045421 | Rueckes et al. | May 2006 | B2 |
| 7081385 | Farnworth et al. | Jul 2006 | B2 |
| 7091096 | Balasubramanian et al. | Aug 2006 | B2 |
| 7132714 | Bae et al. | Nov 2006 | B2 |
| 7135773 | Furukawa et al. | Nov 2006 | B2 |
| 7211844 | Furukawa et al. | May 2007 | B2 |
| 7652418 | Choi et al. | Jan 2010 | B2 |
| 20050095466 | Minteer et al. | May 2005 | A1 |
| 20050118494 | Choi | Jun 2005 | A1 |
| 20050156203 | Bae et al. | Jul 2005 | A1 |
| 20060154126 | Ritts et al. | Jul 2006 | A1 |
| 20060169972 | Furukawa et al. | Aug 2006 | A1 |
| 20060233694 | Sandhu et al. | Oct 2006 | A1 |
| 20060249388 | Chang et al. | Nov 2006 | A1 |
| 20060286023 | Huang | Dec 2006 | A1 |
| 20070056852 | Kubo et al. | Mar 2007 | A1 |
| 20070287034 | Minteer et al. | Dec 2007 | A1 |
| 20080044721 | Heller et al. | Feb 2008 | A1 |
| Number | Date | Country |
|---|---|---|
| 2001312953 | Nov 2001 | JP |
| 2006111498 | Apr 2006 | JP |
| WO 03081687 | Oct 2003 | WO |
| Entry |
|---|
| Gedye et al., The Use of Microwave Ovens for Rapid. Organic Synthesis, Tetrahedron Letters, vol. 27, No. 3, pp. 279-282 (1986). |
| Giguere et al., Application of Commercial Microwave Ovens to Organic Synthesis, Tetrahedron Letters, vol. 27, No. 41, pp. 4945-4948, (1986). |
| Loupy et al., Solvent-Free Microwave Organic Synthesis As an Efficient Procedure for Green Chemistry, C. R. Chimie, vol. 7 (2004) pp. 103-112. |
| Lewis et al., Accelerated Imidization Reactions Using Microwave Radiation, Journal of Polymer Science, 30 (1992) pp. 1647-1653. |
| Katz et al., A Non-Compartmentalized Glucose | O2 Biofuel Cell by Bioengineered Electrode Surfaces, Journal of Electroanalytical Chemistry, vol. 479 (1999), pp. 64-68. |
| Cai at al., Direct Electron Transfer of Glucose Oxidase Promoted by Carbon Nanotubes, Analytical Biochemistry, vol. 332, (2004), pp. 75-83. |
| A. P. Graham et al., “Towards the Integration of Carbon Nanotubes in Microelectronics,” Diamond and Related Materials 13 (2004) 1296-1300. |
| Choi, W. B. et al, “Carbon Nanotube for Nanoelectronics”, IEEE NANO 2003, San Francisco, CA, 2003. |
| D. A. Kurnosov, et al., “Influence of the Interelectrode Distance in Electrophoretic Cold Cathode Fabrication on the Emission Uniformity,” Applied Surface Science 215 (2003) pp. 232-236. |
| G. S. Duesberg et al., “Growth of Isolated Carbon Nanotubes with Lithographically Defined Diameter and Location,” Nano Letters, 2003. vol. 3, No. 2, pp. 257-259. |
| S. Duesberg et al., “Ways Towards the Scaleable Integration of Carbon Nanotubes into Silicon Based Technology,” Diamond and Related Materials 13 (2004) pp. 354-361. |
| H. Kim et al., “Parallel Patterning of Nanoparticles via Electrodynamic Focusing of Charged Aerosols,” Nature Nanotechnology, vol. 1, Nov. 2006, pp. 117-121. |
| H. Ma, et al., “Electron Field Emission Properties of Carbon Nanotubes-Deposited Flexible Film,”Applied Surface Science 251 (2005) pp. 258-261. |
| J. Bae et al, “Field Emission Properties of Carbon Nanotubes Deposited by Electrophoresis,” Physica B 323 (2002), pp. 168-170. |
| J. Hahn et al., “Fabrication of Clean Carbon Nanotube Field Emitters,” Applied Physics Letters 88,113101 (2006). |
| K. Yamoto et al., “Orientation and Purification of Carbon Nanotubes Using AC Electrophoresis,” J. Phys. D: Appl. Phys. 31 (1998), pp. L34-L36. |
| Merkulov et al., “Alignment Mechanism of Carbon Nanofibers Produced by Plasma-Enhanced Chemical-Vapor Deposition,” Applied Physics Letters, vol. 79, No. 18, Oct. 29, 2001, pp. 2970-2972. |
| W. B. Choi et al., “Electrophoresis Deposition of Carbon Nanotubes for Triode-Type Field Emission Display,” Applied Physics Letters, vol. 78, No. 11, Mar. 12, 2001, pp. 1547-1549. |
| W. B. Choi, “Ultrahigh-Density Nanotransistors by Using Selectively Grown Vertical Carbon Nanotubes,” Applied Physics Letters, vol. 79, No. 22, Nov. 26, 2001, pp. 3696-3698. |
| W. Hoenlein et al., “Carbon Nanotubes for Microelectronics: Status and Future Prospects,” Materials Science and Engineering C23 (2003) pp. 663-669. |
| Y. Lin et al., Glucose Biosensors Based on Carbon Nanotube Nanoelectrode Ensembles, 4 Nano Lett. 191-195 (2004). |
| Number | Date | Country | |
|---|---|---|---|
| 20080160384 A1 | Jul 2008 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60790333 | Apr 2006 | US |