The present disclosure generally relates to investment casting mold components and processes utilizing these components. The mold made in accordance with the present invention includes integrated ceramic filaments between the core and shell of the mold that can be utilized to form holes, i.e., effusion cooling holes, in the cast component made from these molds as well as cast external features that were incapable of being cast due to limitations on conventional techniques involving wax.
Many modern engines and next generation turbine engines require components and parts having intricate and complex geometries, which require new types of materials and manufacturing techniques. Conventional techniques for manufacturing engine parts and components involve the laborious process of investment or lost-wax casting. One example of investment casting involves the manufacture of a typical rotor blade used in a gas turbine engine. A turbine blade typically includes hollow airfoils that have radial channels extending along the span of a blade having at least one or more inlets for receiving pressurized cooling air during operation in the engine. The various cooling passages in a blade typically include a serpentine channel disposed in the middle of the airfoil between the leading and trailing edges. The airfoil typically includes inlets extending through the blade for receiving pressurized cooling air, which include local features such as short turbulator ribs or pins for increasing the heat transfer between the heated sidewalls of the airfoil and the internal cooling air.
The manufacture of these turbine blades, typically from high strength, superalloy metal materials, involves numerous steps shown in
The cast turbine blade may then undergo additional post-casting modifications, such as but not limited to drilling of suitable rows of film cooling holes through the sidewalls of the airfoil as desired for providing outlets for the internally channeled cooling air which then forms a protective cooling air film or blanket over the external surface of the airfoil during operation in the gas turbine engine. After the turbine blade is removed from the ceramic mold, the ball chute 203 of the ceramic core 200 forms a passageway that is later brazed shut to provide the desired pathway of air through the internal voids of the cast turbine blade. However, these post-casting modifications are limited and given the ever increasing complexity of turbine engines and the recognized efficiencies of certain cooling circuits inside turbine blades, more complicated and intricate internal geometries are required. While investment casting is capable of manufacturing these parts, positional precision and intricate internal geometries become more complex to manufacture using these conventional manufacturing processes. Accordingly, it is desired to provide an improved casting method for three dimensional components having intricate internal voids.
Methods for using 3-D printing to produce a ceramic core-shell mold are described in U.S. Pat. No. 8,851,151 assigned to Rolls-Royce Corporation. The methods for making the molds include powder bed ceramic processes such as disclosed U.S. Pat. No. 5,387,380 assigned to Massachusetts Institute of Technology, and selective laser activation (SLA) such as disclosed in U.S. Pat. No. 5,256,340 assigned to 3D Systems, Inc. The ceramic core-shell molds according to the '151 patent are limited by the printing resolution capabilities of these processes. As shown in
There remains a need to prepare ceramic core-shell molds produced using higher resolution methods that are capable of providing fine detail cast features in the end-product of the casting process.
The following presents a simplified summary of one or more aspects of the present disclosure in order to provide a basic understanding of such aspects. This summary is not an extensive overview of all contemplated aspects and is intended to neither identify key or critical elements of all aspects nor delineate the scope of any or all aspects. Its purpose is to present some concepts of one or more aspects in a simplified form as a prelude to the more detailed description that is presented later.
In one aspect, the present disclosure is directed to a method for fabricating a ceramic mold, comprising: (a) contacting a cured portion of a workpiece with a liquid ceramic photopolymer; (b) irradiating a portion of the liquid ceramic photopolymer adjacent to the cured portion through a window contacting the liquid ceramic photopolymer; (c) removing the workpiece from the uncured liquid ceramic photopolymer; and (d) repeating steps (a)-(c) until a ceramic mold is formed, the ceramic mold comprising: (1) a core portion and a shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of a cast component upon casting and removal of the ceramic mold, and (2) a plurality of inward protrusions protruding inward from the shell into the at least one cavity, wherein each inward protrusion defines a groove in the cast component upon removal of the mold. In some aspects, the method comprises, after step (d), a step (e) comprising pouring a liquid metal into a casting mold and solidifying the liquid metal to form the cast component. In some aspects, the method comprises, after step (e), a step (f) comprising removing the mold from the cast component. In some aspects, removing the mold from the cast component comprises a combination of mechanical force and chemical leaching. In some aspects, the cast component is adapted to fit with a second cast component by linking a groove in the cast component with a complementary tongue in the second cast component.
In another aspect, the present disclosure is directed to a first single crystal metal turbine blade or stator having one or more grooves and/or tongues on one or more surfaces of the first turbine blade or stator, the one or more grooves and/or tongues adapted to fit with one or more complementary tongues and/or grooves on an object. In some aspects, the object is a second turbine blade or stator. In some aspects, the grooves are seal slots adapted to contain seals to restrict cooling flow from the first turbine blade or stator to a second turbine blade or stator. In some aspects, the seal slots are located on a blade or stator platform or on a fore or aft skirt. In some aspects, the seal slots are located on a pressure side of the respective turbine blade or stator. In some aspects, the seal slots are located on a suction side of the respective turbine blade or stator. In some aspects, the turbine blade or stator has a platform with a first lateral end and a second lateral end opposed to the first lateral end, wherein the tongue is placed into the first lateral end and the groove is placed into the second lateral end.
These and other aspects of the invention will become more fully understood upon a review of the detailed description, which follows.
The detailed description set forth below in connection with the appended drawings is intended as a description of various configurations and is not intended to represent the only configurations in which the concepts described herein may be practiced. The detailed description includes specific details for the purpose of providing a thorough understanding of various concepts. However, it will be apparent to those skilled in the art that these concepts may be practiced without these specific details. For example, the present invention provides a preferred method for making cast metal parts, and preferably those cast metal parts used in the manufacture of j et aircraft engines. Specifically, the production of single crystal, nickel-based superalloy cast parts such as combustors, turbine blades, vanes, and shroud components can be advantageously produced in accordance with this invention. However, other cast metal components may be prepared using the techniques and integrated ceramic molds of the present invention.
The present inventors recognized that prior processes known for making integrated core-shell molds lacked the fine resolution capability necessary to print filaments extending between the core and shell portion of the mold of sufficiently small size and quantity to result in effusion cooling holes in the finished turbine blade. In the case of earlier powder bed processes, such as disclosed in U.S. Pat. No. 5,387,380 assigned to Massachusetts Institute of Technology, the action of the powder bed recoater arm precludes formation of sufficiently fine filaments extending between the core and shell to provide an effusion cooling hole pattern in the cast part. Other known techniques such as selective laser activation (SLA) such as disclosed in U.S. Pat. No. 5,256,340 assigned to 3D Systems, Inc. that employ a top-down irradiation technique may be utilized in producing an integrated core-shell mold in accordance with the present invention. However, the available printing resolution of these systems significantly limit the ability to make filaments of sufficiently small size to serve as effective cooling holes in the cast final product. In particular, these prior processes and systems known for making integrated core-shell molds are unable to make cooling holes in a cast final product having one or more outer portions or overhangs, specifically in locations that are proximal to these outer portions or overhangs.
The present inventors have found that the integrated core-shell mold of the present invention can be manufactured using direct light processing (DLP). DLP differs from the above discussed powder bed and SLA processes in that the light curing of the polymer occurs through a window at the bottom of a resin tank that projects light upon a build platform that is raised as the process is conducted. With DLP an entire layer of cured polymer is produced simultaneously, and the need to scan a pattern using a laser is eliminated. Further, the polymerization occurs between the underlying window and the last cured layer of the object being built. The underlying window provides support allowing thin filaments of material to be produced without the need for a separate support structure. In other words, producing a thin filament of material bridging two portions of the build object is difficult and was typically avoided in the prior art. For example, the '151 patent discussed above in the background section of this application used vertical plate structures connected with short cylinders, the length of which was on the order of their diameter. Staggered vertical cavities are necessitated by the fact that the powder bed and SLA techniques disclosed in the '151 patent require vertically supported ceramic structures and the techniques are incapable of reliably producing filaments. In addition, the available resolution within a powder bed is on the order of ⅛″ (3.2 mm), or 0.025 mm layer thickness for binder-jetting, making the production of traditional cooling holes impracticable. For example, round cooling holes generally have a diameter of less than 2 mm corresponding to a cooling hole area below 3.2 mm2. Production of a hole of such dimensions requires a resolution far below the size of the actual hole given the need to produce the hole from several voxels. This resolution is simply not available in a powder bed process. Similarly, stereolithography is limited in its ability to produce such filaments due to lack of support and resolution problems associated with laser scattering. But the fact that DLP exposes the entire length of the filament and supports it between the window and the build plate enables producing sufficiently thin filaments spanning the entire length between the core and shell to form a ceramic object having the desired cooling hole pattern. Although powder bed and SLA may be used to produce filaments, their ability to produce sufficiently fine filaments as discussed above is limited.
One suitable DLP process is disclosed in U.S. Pat. No. 9,079,357 assigned to Ivoclar Vivadent AG and Technische Universitat Wien, as well as WO 2010/045950 A1 and US 2011/0310370, each of which are hereby incorporated by reference and discussed below with reference to
Opposite the exposure unit 410, a production platform 412 is provided above the tank 404; it is supported by a lifting mechanism (not shown) so that it is held in a height-adjustable way over the tank bottom 406 in the region above the exposure unit 410. The production platform 412 may likewise be transparent or translucent in order that light can be shone in by a further exposure unit above the production platform in such a way that, at least when forming the first layer on the lower side of the production platform 412, it can also be exposed from above so that the layer cured first on the production platform adheres thereto with even greater reliability.
The tank 404 contains a filling of highly viscous photopolymerizable material 420. The material level of the filling is much higher than the thickness of the layers which are intended to be defined for position-selective exposure. In order to define a layer of photopolymerizable material, the following procedure is adopted. The production platform 412 is lowered by the lifting mechanism in a controlled way so that (before the first exposure step) its lower side is immersed in the filling of photopolymerizable material 420 and approaches the tank bottom 406 to such an extent that precisely the desired layer thickness A (see
These steps are subsequently repeated several times, the distance from the lower side of the layer 422 formed last to the tank bottom 406 respectively being set to the desired layer thickness A and the next layer thereupon being cured position-selectively in the desired way.
After the production platform 412 has been raised following an exposure step, there is a material deficit in the exposed region as indicated in
In order to replenish the exposure region with photopolymerizable material, an elongate mixing element 432 is moved through the filling of photopolymerizable material 420 in the tank. In the exemplary embodiment represented in
The movement of the elongate mixing element 432 relative to the tank may firstly, with a stationary tank 404, be carried out by a linear drive which moves the support arms 430 along the guide slots 434 in order to achieve the desired movement of the elongate mixing element 432 through the exposed region between the production platform 412 and the exposure unit 410. As shown in
Other alternative methods of DLP may be used to prepare the integrated core-shell molds of the present invention. For example, the tank may be positioned on a rotatable platform. When the workpiece is withdrawn from the viscous polymer between successive build steps, the tank may be rotated relative to the platform and light source to provide a fresh layer of viscous polymer in which to dip the build platform for building the successive layers.
Ceramic molds produced according to the present disclosure may contain at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of a cast component upon casting and removal of the ceramic mold, and a plurality of filaments joining the core and shell and defining a plurality of holes in the cast component defined by the core portion and an outer surface of the cast component upon removal of the mold. The cavity and filaments may be of any shape and size, depending on the desired shape of the cast component and any holes therein. The filaments and resulting holes may be linear or non-linear, and may be of any length, cross-sectional area, and/or diameter. In addition, the diameter and/or cross-sectional area of each of the plurality of filaments may change along its length. In some aspects, the cross-sectional area of each of the plurality of filaments ranges from 0.01 to 2 mm2, or any subrange contained therein. In addition, the plurality of filaments may be arranged in any pattern on the outer surface of the cast component and on the core portion, so as to produce any desired pattern of cooling holes.
The length of the filament is dictated by the thickness of the cast component, e.g., turbine blade or stator vane wall thickness, and the angle at which the cooling hole is disposed relative to the surface of the cast component. In some aspects, the filament lengths range from 0.5 to 5 mm, such as between 0.7 to 1 mm, such as about 0.9 mm. A cooling hole may be disposed at any angle relative to the surface of the cast component. In some aspects, the angle at which a cooling hole is disposed is at an angle other than 90° from the surface, such as approximately 5 to 35° relative to the surface, such as less than 20°, such as between 10 to 20°, such as approximately 12°, or such as 5° to 15°. It should be appreciated that the methods of casting according to the present invention allow for formation of cooling holes having a lower angle relative to the surface of the cast component than currently available using conventional machining techniques.
The specific shape of a cooling hole made in accordance with the present invention is determined by the shape of the filament connecting the core to the shell portion of the mold. Because the process for making filaments allows complete control over the dimensions of the filament, the present invention can be used to make any shape cooling hole. Moreover, a single cast object may be provided with several kinds of cooling hole designs. The following describes several non-limiting examples for cooling hole designs that may be used in accordance with the present invention. One key characteristic of the cooling holes of the present invention is that they may be provided with a non-line-of-sight shape. In practice, cooling holes drilled through a completed turbine blade using electro discharge machining (EDM) were limited to cooling holes that were generally shaped to have a line of sight through the cast metal object. This is because the EDM apparatus has a generally linear shape and operates by drilling through outer surface of the cast object to reach the core cavity. It is generally not possible to drill from the core cavity side of the cast object because the core cavity is inaccessible. In some aspects of the present disclosure, the filaments or holes are non-linear.
The present invention relates also to methods of making cast metal objects, in particular single crystal turbine blades and stators used in jet aircraft engines that have non-linear cooling holes such as the exemplary design shown in U.S. patent application Ser. No. 15/377,787, titled “INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH NON-LINEAR HOLES” with attorney docket number 037216.00041/285064, and filed Dec. 13, 2016 (“the '787 application”), which is incorporated by reference herein in its entirety. The method begins with the production of the ceramic mold using DLP. The DLP process involves a repetition of steps of (a) contacting a cured portion of a workpiece with a liquid ceramic photopolymer; (b) irradiating a portion of the liquid ceramic photopolymer adjacent to the cured portion through a window contacting the liquid ceramic photopolymer; and (c) removing the workpiece from the uncured liquid ceramic photopolymer. The steps (a)-(c) are repeated until the ceramic mold is formed. After the mold is formed, liquid metal may then be poured into the casting mold and solidified to form the cast component. The ceramic mold is then removed from the cast component using, for example, combination of mechanical removal of the outer shell and leaching of the inner ceramic core.
The specific geometry of the non-linear cooling hole filaments may be varied based on the needs for specific effusion cooling hole pattern to be placed in the turbine blade or stator. For example, the direction of the hole may be opposite that shown in the '787 application with holes aligned toward the top of the turbine blade. The filament may have a curvature that forms an “S” shaped hole upon removal of the mold. Alternatively, the holes may be aligned horizontally along the turbine blade such that they project inward or alternatively outward of the page. Given the flexibility possible for DLP processing, there are no limitations on the shape of the cooling hole. A few alternative exemplary cooling hole geometries are shown in the '787 application.
After leaching, the resulting holes in the turbine blade from the core print filaments may be brazed shut if desired. Otherwise the holes left by the core print filaments may be incorporated into the design of the internal cooling passages. Alternatively, cooling hole filaments may be provided to connect the tip plenum core to the shell in a sufficient quantity to hold the tip plenum core in place during the metal casting step. After printing the core-shell mold structures in accordance with the invention, the core-shell mold may be cured and/or fired depending upon the requirements of the ceramic core photopolymer material. Molten metal may be poured into the mold to form a cast object in the shape and having the features provided by the integrated core-shell mold. In the case of a turbine blade, the molten metal is preferably a superalloy metal that formed into a single crystal superalloy turbine blade using techniques known to be used with conventional investment casting molds.
The methods of the present disclosure may be used to produce objects of any shape or size, including various components for use in turbine engines.
In some aspects, the cavity is shaped so as to define a secondary surface of the cast component contained beneath the outer surface of the cast component. In such aspects, the core of the core-shell mold contains an inner core (beneath the secondary surface) and an outer core (between the secondary and outer surfaces). In other aspects, the core is a single core. In some aspects, a plurality of filaments may join the inner core and the outer core and define a plurality of holes in the cast component defined in the inner core and the secondary surface upon removal of the mold. The plurality of filaments or holes in the secondary surface may be similar in some aspects to the plurality of filaments in the outer surface.
In addition, the core (whether a single core or an inner core and an outer core) may be of any size or of any size relative to the thickness of the cast metal component. In some aspects, the core thickness is larger than the cast metal component thickness, and upon removal of the ceramic mold the larger thickness core creates a reservoir within the cast metal component. The reservoir may be of any size or shape and may contain one or more holes connecting it to the outer surface of the part.
In other aspects, the ceramic mold may contain one or more incomplete filaments, i.e., inward protrusions from the shell into the cavity that do not join a ceramic core. Upon casting of the cast metal component and removal of the ceramic mold, each of the one or more inward protrusions may define a respective groove in the cast metal component.
The groove or tongue from the cast metal component may be of any size and/or shape relative to the cast metal component. In some aspects, the inward protrusion 1242 has at least one dimension with a cross-section that is less than the corresponding dimension in the cast metal component 1244. In some aspects, the groove or tongue from the cast metal component may be adapted to fit with a complementary tongue or groove, respectively, in another component. As used herein, a tongue or groove in a first component that is “complementary” to a groove or tongue, respectively, in a second component is one that fits or interlocks with the groove or tongue in the second component similarly to, e.g., puzzle pieces.
In an aspect, the present invention relates to the core-shell mold structures of the present invention incorporated or combined with features of other core-shell molds produced in a similar manner. The following patent applications include disclosure of these various aspects and their use:
U.S. patent application Ser. No. 15/377,728, titled “INTEGRATED CASTING CORE-SHELL STRUCTURE” with attorney docket number 037216.00036/284976, and filed Dec. 13, 2016;
U.S. patent application Ser. No. 15/377,711, titled “INTEGRATED CASTING CORE-SHELL STRUCTURE WITH FLOATING TIP PLENUM” with attorney docket number 037216.00037/284997, and filed Dec. 13, 2016;
U.S. patent application Ser. No. 15/377,796, titled “MULTI-PIECE INTEGRATED CORE-SHELL STRUCTURE FOR MAKING CAST COMPONENT” with attorney docket number 037216.00033/284909, and filed Dec. 13, 2016;
U.S. patent application Ser. No. 15/377,746, titled “MULTI-PIECE INTEGRATED CORE-SHELL STRUCTURE WITH STANDOFF AND/OR BUMPER FOR MAKING CAST COMPONENT” with attorney docket number 037216.00042/284909A, and filed Dec. 13, 2016;
U.S. patent application Ser. No. 15/377,763, titled “INTEGRATED CASTING CORE SHELL STRUCTURE WITH PRINTED TUBES FOR MAKING CAST COMPONENT” with attorney docket number 037216.00032/284917, and filed Dec. 13, 2016;
U.S. patent application Ser. No. 15/377,759, titled “INTEGRATED CASTING CORE-SHELL STRUCTURE AND FILTER FOR MAKING CAST COMPONENT” with attorney docket number 037216.00039/285021, and filed Dec. 13, 2016;
U.S. patent application Ser. No. 15/377,787, titled “INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH NON-LINEAR HOLES” with attorney docket number 037216.00041/285064, and filed Dec. 13, 2016;
U.S. patent application Ser. No. 15/377,766, titled “INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT HAVING THIN ROOT COMPONENTS” with attorney docket number 037216.00053/285064B, and filed Dec. 13, 2016.
U.S. patent application Ser. No. 15/377,783, titled “INTEGRATED CASTING CORE-SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH COOLING HOLES IN INACCESSIBLE LOCATIONS” with attorney docket number 037216.00055/285064A, and filed Dec. 13, 2016.
The disclosure of each of these application are incorporated herein in their entirety to the extent they disclose additional aspects of core-shell molds and methods of making that can be used in conjunction with the core-shell molds disclosed herein.
This written description uses examples to disclose the invention, including the preferred embodiments, and also to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal language of the claims. Aspects from the various embodiments described, as well as other known equivalents for each such aspect, can be mixed and matched by one of ordinary skill in the art to construct additional embodiments and techniques in accordance with principles of this application.
This application is a divisional of U.S. application Ser. No. 15/887,601 filed on Feb. 2, 2018, titled “INTEGRATED CASTING-CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH NOVEL COOLING HOLE ARCHITECTURE”, which is herein incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15887601 | Feb 2018 | US |
| Child | 17350376 | US |