The instant invention relates to a process for upgrading heavy oils, in which the feed is pretreated to partially reduce impurities, nitrogen, carbon residuum, asphaltnenes, metals, and sulfur, then is contacted with a slurry catalyst composition in a series of upflow reactors.
There is an increased interest at this time in the processing of heavy oils, due to larger worldwide demand for petroleum products. Canada and Venezuela are sources of heavy oils. Processes which result in complete conversion of heavy oil feeds to useful products are of particular interest.
The following patents, which are incorporated by reference, are directed to the preparation of highly active slurry catalyst compositions and their use in processes for upgrading heavy oil:
U.S. Ser. No. 10/938,202 is directed to the preparation of a catalyst composition suitable for the hydroconversion of heavy oils. The catalyst composition is prepared by a series of steps, involving mixing a Group VIB metal oxide and aqueous ammonia to form an aqueous mixture, and sulfiding the mixture to form a slurry. The slurry is then promoted with a Group VIII metal. Subsequent steps involve mixing the slurry with a hydrocarbon oil and combining the resulting mixture with hydrogen gas and a second hydrocarbon oil having a lower viscosity than the first oil. An active catalyst composition is thereby formed.
U.S. Ser. No. 10/938,003 is directed to the preparation of a slurry catalyst composition. The slurry catalyst composition is prepared in a series of steps, involving mixing a Group VIB metal oxide and aqueous ammonia to form an aqueous mixture and sulfiding the mixture to form a slurry. The slurry is then promoted with a Group VIII metal. Subsequent steps involve mixing the slurry with a hydrocarbon oil, and combining the resulting mixture with hydrogen gas (under conditions which maintain the water in a liquid phase) to produce the active slurry catalyst.
U.S. Ser. No. 10/938,438 is directed to a process employing slurry catalyst compositions in the upgrading of heavy oils. The slurry catalyst composition is not permitted to settle, which would result in possible deactivation. The slurry is recycled to an upgrading reactor for repeated use and products require no further separation procedures for catalyst removal.
U.S. Ser. No. 10/938,200 is directed to a process for upgrading heavy oils using a slurry composition. The slurry composition is prepared in a series of steps, involving mixing a Group VIB metal oxide with aqueous ammonia to form an aqueous mixture and sulfiding the mixture to form a slurry. The slurry is then promoted with a Group VIII metal compound. Subsequent steps involve mixing the slurry with a hydrocarbon oil, and combining the resulting mixture with hydrogen gas (under conditions which maintain the water in a liquid phase) to produce the active slurry catalyst.
U.S. Ser. No. 10/938,269 is directed to a process for upgrading heavy oils using a slurry composition. The slurry composition is prepared by a series of steps, involving mixing a Group VIB metal oxide and aqueous ammonia to form an aqueous mixture, and sulfiding the mixture to form a slurry. The slurry is then promoted with a Group VIII metal. Subsequent steps involve mixing the slurry with a hydrocarbon oil and combining the resulting mixture with hydrogen gas and a second hydrocarbon oil having a lower viscosity than the first oil. An active catalyst composition is thereby formed.
A process for the hydroconversion of heavy oils with a slurry, said process employing at least two upflow reactors in series with a separator in between each reactor, said process comprising the following steps:
The slurry upgrading step of this invention converts nearly 98% of a typical feed, vacuum residue to lighter products (in the boiling range below 1000 F). Due to large quantities of impurities such as sulfur, nitrogen, metals, Conradson carbon and asphaltenes in straight run vacuum residuum, the slurry conversion reactor requires a very high severity. High severity includes high pressure, large reactors, high fresh catalyst make-up rate and relatively high spent catalyst bleed rate. Downstream hydroprocessing is often required to achieve appropriate product qualities, but it may be avoided or minimized may be avoided by in-line, integrated pre-treatment of the feed prior to slurry hydroprocessing as in the instant invention.
In-line pretreating of feed to slurry hydrocracking will reduce overall capital expeditures for the slurry hydrocracking processes of this invention. It will also improve product qualities and produce more valuable products.
The FIGURE depicts a process scheme of this invention which employs a fixed bed preatreating reactor upstream of three reactors employing a catalyst slurry, within the same process loop.
The instant invention is directed to a process for catalyst activated slurry hydrocracking with upstream in-line pretreating, as depicted in the FIGURE. Stream 1 comprises a heavy feed, such as vacuum residuum. This feed enters furnace 80 where it is heated, exiting in stream 4. Stream 4 combines with a hydrogen containing gas (stream 2) resulting in a mixture (stream 101). Stream 101 enters the top of the pretreater reactor 100. The pretreater is either a fixed bed hydrotreating unit or a deasphalting unit. In a deasphalting unit, solvent generally flows countercurrent to the feed. Deasphalting is not depicted. Stream 102 leaves the bottom of the pretreater and proceeds to hot high pressure separator 110, which is preferably a flash drum. Product and hydrogen is removed overhead as a vapor stream, stream 103. Stream 103 joins with stream 22. Unconverted material exits the bottoms flash drum 110 as liquid stream 104. Stream 104 combines with stream 106. Stream 106 is composed of recycle slurry catalyst (stream 19) as well as make-up slurry catalyst (stream 3). Streams 104 and 106 combine to form stream 107.
Stream 107 enters the bottoms of upflow reactor 10, which is preferably a liquid recirculating reactor. Stream 5, a vapor stream exits the reactor overhead and comprises slurry, products, hydrogen and unconverted material. Stream 5 passes to hot high pressure separator 40, which is preferably a flash drum. Product and hydrogen is removed overhead in a vapor stream as stream 6. Liquid stream 7 is removed through the bottom of the flash drum. Stream 7 contains slurry in combination with unconverted oil.
Stream 7 is combined with a gaseous stream comprising hydrogen (stream 15) to create stream 25. Stream 25 enters the bottom of second reactor 20. Stream 8, a vapor stream comprising slurry, products, hydrogen and unconverted material, passes overhead from reactor 20 to separator 50, preferably a flash drum. Products and hydrogen are removed overhead as vapor stream 9. Liquid stream 11 is removed through the bottom of the flash drum. Stream 11 contains slurry in combination with unconverted oil.
Stream 11 is combined with a gaseous stream comprising hydrogen (stream 16) to create stream 26. Stream 26 enters the bottom of second reactor 30. Vapor stream 12 passes overhead from reactor 30 to hot high pressure separator 60, preferably a flash drum. Product and hydrogen is removed overhead as vapor stream 13. Stream 17 is removed through the bottom of the flash drum 60. Liquid stream 17 contains slurry in combination with unconverted oil. A portion of this stream may be drawn off through stream 18.
Overhead vapor streams 6, 9 and 13 create stream 14, which passes to lean oil contactor 70. Stream 22, containing a lean oil such as vacuum gas oil, enters the top portion of lean oil contactor 70 and flows downward (1) removing any possible entrained catalyst and (2) reducing heavy materials(high boiling range oil including small amounts of vacuum residue). Product and hydrogen (stream 21) exits lean oil contactor 70 as vapor overhead, while liquid stream 19 exits at the bottom. Stream 21 combines with product stream 103 to form stream 22, which is sent to hydrofinishing.
Stream 19 comprises a mixture of slurry and unconverted oil. Stream 19 is combined with stream 17, which also comprises a mixture of slurry and unconverted oil. Fresh slurry is added in stream 3, and stream 106 is created. Stream 106 is combined with the feed to first reactor 10 (stream 104) to create stream 107.
The heavy product fraction is hydrofinished to eliminate any remaining olefins. The hydrofinisher further refines products from the slurry upgrader to high quality products by removing impurities and stabilizing the products. Greater than 99 wt % sulfur and nitrogen removal may be achieved. Reactor effluent is cooled by means of heat recovery and sent to the product recovery section as in any conventional hydroprocessing unit.
Conditions for pretreating hydrocarbons are well known to those of skill in the art. Pretreating may involve hydrotreating or deasphalting. Hydrotreating is a well-known form of feed pretreatment, and usually occurs in fixed bed hydrotreating reactors having one or more beds. Hydrotreating is generally disclosed in U.S. Pat. No. 6,890,423 and is discussed in Gary and Handwerk, Petroleum Refining (2nd ed. 1984). Typical hydrotreating conditions vary over a wide range. In general, the overall LHSV is about 0.25 to 2.0, preferably about 0.5 to 1.0. The hydrogen partial pressure is greater than 200 psia, preferably ranging from about 500 psia to about 2000 psia. Hydrogen recirculation rates are typically greater than 50 SCF/Bbl, and are preferably between 1000 and 5000 SCF/Bbl. Temperatures range from about 300[deg] F. to about 750[deg] F., preferably ranging from 450[deg] F. to 600[deg] F. Catalysts useful in hydrotreating operations are well known in the art. Suitable catalysts include noble metals from Group VIIIA (according to the 1975 rules of the International Union of Pure and Applied Chemistry), such as platinum or palladium on an alumina or siliceous matrix, and unsulfided Group VIIIA and Group VIB, such as nickel-molybdenum or nickel-tin on an alumina or siliceous matrix. The non-noble metal (such as nickel-molybdenum) hydrogenation metals are usually present in the final catalyst composition as oxides, or more preferably or possibly, as sulfides when such compounds are readily formed from the particular metal involved. Preferred non-noble metal catalyst compositions contain in excess of about 5 weight percent, preferably about 5 to about 40 weight percent molybdenum and/or tungsten, and at least about 0.5, and generally about 1 to about 15 weight percent of nickel and/or cobalt determined as the corresponding oxides. The noble metal (such as platinum) catalyst may contain in excess of 0.01 percent metal, preferably between 0.1 and 1.0 percent metal. Combinations of noble metals may also be used, such as mixtures of platinum and palladium.
Pretreating may alternately employ deasphalting, if the feed to be employed contains asphalt. Deasphalting is usually accomplished by the use of propane as a solvent, although other solvents may include lower-boiling paraffinic hydrocarbons such as ethane, butane or pentane. Deasphalting techniques are well known in the refining arts, but are discussed in the text Petroleum Refining. Deasphalting is disclosed generally in patents such as U.S. Pat. Nos. 6,264,826 and 5993,644.
Alternate embodiments for the slurry reactor system, which are not pictured, include a series of reactors in which one or more of the reactors contains internal separation means, rather than an external separator or flash drum following the reactor.
The process for the preparation of the catalyst slurry composition used in this invention is set forth in U.S. Ser. No. 10/938003 and U.S. Ser. No. 10/938202 and is incorporated by reference. The catalyst composition is useful for but not limited to hydrogenation upgrading processes such as thermal hydrocracking, hydrotreating, hydrodesulphurization, hydrodenitrification, and hydrodemetalization.