This invention concerns interfacing to electronic circuits or systems, such as integrated circuits, operating at low temperature using complementary metal-oxide semiconductor (CMOS) technology. Low temperature in this case refers to cryogenic temperatures, in particular but not exclusively to the 4.2 K region. Ultra-low temperatures here refers to the sub 1 K range, usually accessed using dilution refrigerator systems.
Electronic components in general, such as bipolar transistors will not work at low temperatures, below about 70 K.
Complementary metal-oxide semiconductor, technology (CMOS) was originally developed for room-temperature low-power applications.
Although much domestic and commercial electronics operate at room temperature (300 K) there are an important and growing number of applications which require lower temperatures.
It has been known for some decades that metal-oxide-semiconductor field-effect transistors (MOSFETs) can operate at low-temperatures. For example, the integer quantum Hall effect was discovered by von Klitzing [4] in 1980, from the effects of an external magnetic field on the two-dimensional electron system (2DES) of a MOSFET at 4.2 K.
Additionally, there has been some reported work in characterizing silicon MOSFETs at temperatures ≦4.2 K, such as the demonstration of an operational amplifier fabricated by a commercial process which is was able to operate at 4.2 K [5]. Also there has been work done on modeling the behavior of MOSFETs in the sub-100 mK [6] and 4.2 K [7] temperature regions. There have been demonstrations of the operation of MOSFETs integrated with single-electron transistors (SETs) [8], [9] at 4.2 K, and other demonstrations of the effects of CMOS processing steps, namely using lightly-doped drains (LDDs) and Vt-adjust implantation, on the drain current kink effect of NMOS FETs at 4.2 K [10]. Others have integrated commercial CMOS processes with superconducting technologies [11-13], which has led them to characterize those MOSFETs at 4.2 K. However, it is quite commonly documented that MOSFET channels may freeze-out at cryogenic temperatures [11], [12] rendering them unsuitable for use for control of quantum circuits. Additionally, it is not usually practical to produce CMOS circuits of even modest complexity in a research laboratory; but only in a commercial foundry.
The invention is an electronic circuit or system (including an integrated circuit) operating at low temperatures and ultra-low temperatures, and comprising controller (for writing and manipulation) or observer (for readout and measurement) circuits, or both, fabricated from ultra-thin silicon-on-insulator (SOI) CMOS technology.
The controller and observer circuits may be fabricated, in particular, using SOI-CMOS field-effect transistor (FET) technology.
The controller and observer circuits may employ CMOS circuits. As a result the invention is able to exploit the following properties of SOI-CMOSFET technology:
The inherent unity-gain frequency (ft) which is due to the short channel length and lower parasitics of SOI devices, and which can be employed to generate rapid pulse edge transition times (tr˜ft−1) and also high bandwidth (in the range 10-100 GHz, or above) for amplification.
The high pulse-voltage swing (±500 mV) is available in MOS technology. Ultra-low power operation is due to the low parasitics of SOI devices. In addition there is high capacitive drivability and scalability available in this technology. These features provide important advantages, particularly for qubit control, relative to other competing technologies such as RSFQ [3] which can only produce pulse-voltage swings of ˜10 mV.
Further advantages are large scale integration, and wide commercial availability. In fact, it has been found that the invention can be designed and built using a suitable SOI-CMOS process that was developed particularly for radio-frequency (RF) applications developed at a commercial foundry.
In a practical embodiment many SOI-CMOS circuits, that is tens, hundreds or even thousands, may be fabricated on a single integrated circuit using the foundry process.
The SOI-CMOS circuits of the invention may be fabricated on the same integrated circuit as other circuit elements, including the circuits or systems being controlled or observed. The invention may therefore comprise a single integrated circuit having both the control and readout circuit elements, as well as the circuit elements being controlled or observed.
Alternatively, the SOI-CMOS circuits of the invention may be on a separate integrated circuit, and possibly in a different temperature environment, from the circuit or system being controlled or observed.
The SOI-CMOS circuits of the invention, because of their high unity-gain frequency (ft), may be used to generate voltage or current pulses with rapid pulse-edge transition times, or generalized voltage or current waveforms with high temporal control. Such high-bandwidth waveform generators may be used to control other circuits or systems that require low temperatures for their operation. Because the SOI-CMOS circuits of the invention can operate at low temperatures, it is possible for them to be conveniently interfaced with the circuits or systems being controlled, with minimal corruption or distortion of the controlling voltage or current waveform.
The SOI-CMOS circuits of the invention, because of their high unity-gain frequency (ft), may be also used as high-bandwidth, voltage or current amplifiers. Such high-bandwidth amplifiers may be used to observe (i.e. measure) other circuits or systems that require low or ultra-low temperatures for their operation. Because the SOI-CMOS circuits of the invention can operate at low temperatures, it is possible for them to be conveniently interfaced with the circuits or systems being observed (measured), with a high signal-to-noise ratio and without losing high-frequency information.
An example where the controller and observer circuits of the invention would be particularly useful is to provide a stable steady-state voltage or current waveform suitable to control quantum bits, for instance to place and maintain a quantum bit (qubit) in a quantum-coherent superposition of |0 and |1
states. This is because most qubits require low temperatures for their operation.
In addition the controller circuits of the invention are able to provide duty-cycle (dwell time) controlled rapid single-shot pulses suitable for qubit control.
As a result the other electronic circuits or systems, those being controlled and observed, may include quantum processors, and the controller and observer circuits may be used for initialization, control (writing and manipulation) and observation (readout and measurement) of quantum bits (qubits) in a quantum computer.
Further, the controller and observer circuit components of the invention have been found to operate at ultra-low temperatures, that is, in the sub-100 mK range.
As a result the other electronic circuits or systems, those being controlled and observed, may include silicon-based quantum bits, for instance those involving spin or charge qubits, and the controller and observer circuits may be used at low temperatures or ultra-low temperatures for initialization, control (writing and manipulation) and observation (readout and measurement) of quantum bits (qubits) in a quantum computer. The controller and observer circuitry may be fabricated on the same integrated circuit as the quantum processor. Alternatively, the controller and observer circuits may be fabricated on a separate integrated circuit from the quantum processor, and may be operated in the same, or at a different, temperature from the quantum processor, with appropriate low-temperature interfacing between the two.
An example of the invention will be described with reference to the accompanying drawings, in which:
This example concerns the control and readout for a silicon (Si) based quantum computer. A quantum binary digit (qubit) is the fundamental computational element of the quantum computer. The solid-state qubit can be either a spin qubit [1], or a charge qubit [2]. In this example we consider a silicon charge qubit, however, we note that silicon spin-based qubits are expected to have much longer quantum coherence times and would be the preferred choice in most cases.
A buried donor charge qubit is shown in =|L
and |1
=|R
. Finally, a SET facilitates initialization and readout of the qubit.
The charge qubit requires the integration of a controller and observer circuit for input-process-output operations: the former to write and manipulate the initial states of the qubits, and the latter to read their final states.
System 20 involves conventional room temperature (300 K) control 22 and read-out 24 systems. These room temperature systems are connected to systems at low (4.2 K) or ultra-low temperatures (sub-100 mK) in conventional fashion using insulated pipelines as indicated at 26 and 28. In the low temperature environment controller circuits 30 are operable to initialize qubits in a quantum processor 32. Observer circuits 34 are able to readout the qubit states after processing.
Both the controller and observer circuits are fabricated from ultra-thin silicon-on-insulator (SOI) using CMOS technology. The circuits provide duty cycle, that is dwell time, controlled rapid single-shot pulses and therefore involve fast pulse generators, or voltage latches, among other circuit elements. For instance, digital state machines, digital to analogue converters, amplifiers, analog-to-digital converters and signal conditioning circuits such as SET interfaces.
The integrated controller-qubit-observer (CQO) circuit system (quantum computer) can be implemented either as a modular or monolithic design. The quantum processor containing the qubits must operate at sub-100 mK temperatures, to ensure quantum phase coherence times long enough for feasible qubits. In this example the controller and observer circuits are fabricated of silicon-on-insulator (SOI) complementary metal-oxide-semiconductor (CMOS) field-effect transistor (FET) technology.
A typical control signal to use for qubit control is a duty-cycle (dwell time) controlled rapid single-shot pulse.
The utility of the invention will be demonstrated with reference to a description of experimental work with reference to the following drawings, in which:
The proof that an integrated controller-qubit-observer (CQO) circuit system (quantum processor) can be built is achieved by characterizing SOI MOSFETs in the sub-100 mK temperature region where the integrated CQO circuit will be operating during qubit control and readout. Before going further Table 1 defines the variables that will be used.
The cryogenic operability of selected commercially available SOI thin-Si CMOS technologies, will now be described. In particular, the experimental characterization of SOI NMOS and PMOS FETs from the Peregrine Semiconductor Corporation (PSC) ultra-thin silicon (UTSi) silicon-on-sapphire (SOS) processes; the processes and devices that have been investigated are shown in Table 2.
The results show that SOI CMOS can be used for the specific purpose of qubit controller and observer circuit design for a quantum processor. The results also show that SOI CMOS can be used for other ultra-low temperature and ultra-low power applications as well.
The experimental setup used to obtain the direct current (DC) response characterization of NMOS and PMOS devices at room temperature (300 K), liquid helium temperature (4.2 K), and sub-100 mK temperature (30 mK) is shown in
The experimental setup 10 involves a power supply 12 and ammeter 14 to read measurements, as well as a DC ramp generator 16 to provide input voltage to the gate, all located at room temperature 300 K. The test chip 20 contains NMOS 22 and PMOS 24 devices which are able to be directly coupled to the power source 16 and measurement probes 14. The supply polarity is selected accordingly, and in
During the NMOS (PMOS) device measurement, the terminals of the PMOS (NMOS) device are pulled-down to ground. This approach enables alternatively measuring the devices in situ in the same temperature cycle for consistency. The DC measurement results of the NMOS and PMOS devices from the 500 nm process are shown in
The DC measurement results of the NMOS and PMOS devices from the 250 nm process are shown in
The DC I(V) measurements were performed using a 4.2 K station for 300 K and 4.2 K measurements, and a dilution refrigerator for 30 mK measurements.
The 4.2 K measurements were performed by cycling the devices through 300 K-4.2 K-300 K to ensure that the devices survived the temperature cycling, however this was not done for the sub-100 mK measurements as the ultra-low temperature effects were deduced to have occurred at a higher temperature than 4.2 K.
The devices produced reproducible and identical 300 K characteristics after temperature cycling, hence the results in
In addition measurements were made from a n+-diffusion resistor of the 500 nm process, using the above setup, with W/L=50/10 the measurement results of which are shown in
DC response measurements show that the PSC MOSFETs designed and fabricated for higher temperature (218-348 K) operation, can operate at the sub-100 mK region, subject to their particular PSC design and fabrication techniques; more importantly these results show that PSC 500 nm and 250 nm SOS processes are suitable commercial foundry processes for our purposes.
The room temperature characteristics of the 500 nm and 250 nm processes are shown in
The devices show favorable DC responses for FET-based control circuit design, apart from V, increases in ID(VGS), short-channel effects (SCEs) appearing earlier in their ID(VDS) curves as shown in
The increased threshold voltage (Vt) at 4.2 K and <100 mK temperatures may be due to carrier freeze-out in the channel region of the NMOS and PMOS devices, thus requiring a higher gate drive voltage to produce carriers in the channel material.
Vt(VDS) modulation: The modulation of Vt with increasing VDS may be due to the LDDs (drain extensions) freezing-out thus requiring a higher transverse electric field produced by VDS to produce proportionally higher carrier injection into the channel.
Transconductance (gm) increase: The increased DC currents and transconductance in both NMOS and PMOS devices at 30 mK, and 4.2 K relative to 300 K are most likely be due to lower thermal scattering thus higher mobility along the current paths (channel and ohmic contacts) in the devices.
Non-linearity in triode (ohmic) region for low VDS: This could be due to the ohmic contacts freezing-out producing higher contact tunnel barriers for carriers to propagate through thus producing some non-linearity. This effect may have been observed previously, at 300 K, in silicon short-channel MOSFETs with metal-silicide drain contacts at 300 K [14], and the proposed explanation is the presence of surface carriers at the source contact region of the channel that screen the effective gate-induced electric field thus reducing carrier injection into the channel from the source [14]. Perhaps in our devices at cryogenic temperatures, these surface states freeze-out producing a similar effect at low VDS, but are relieved at higher VDS. These surface states could raise the barrier at the ohmic contacts at ultra-low temperatures thus forming a Schottky contact. This could be the reason for the non-linear [15] ohmic region characteristic on the ID(VDS) behavior.
This ohmic region non-linearity is less pronounced in the 250 nm devices than in the 500 nm devices at 4.2 K and at 30 mK. The devices, of course, do not exhibit such behavior at 300 K as they are designed for that temperature region.
SCEs: In these devices, SCEs occur at relatively lower VGS bias at 30 mK and 4.2 K than at 300 K. So these effects are not clearly visible for VGS>1.6 V in our data in
The SCEs, in our devices, are most likely due to the higher electric field required to inject carriers into the channel at cryogenic temperatures thus causing the depletion regions of the contacts to approach each other.
The experimental setup used to obtain the transient response characterization of PMOS devices at room temperature (300 K), liquid helium temperature (4.2 K), and sub-100 mK temperature (30 mK) is shown in
The experimental setup 50 involves a high bandwidth DSO 52 including a voltmeter 54 for readout, and a voltage source 56. A pulse generator 58 was used to drive the gate 60 of the PMOS test chip 62.
This approach allowed estimation of the ft of the devices without having to use a y-parameter frequency analyzer, as it is not possible to immerse such equipment or their probes into a helium (He) Dewar or dilution refrigerator. The relation tr˜ft−1, where tr is the rise time, is used to estimate the ft of the devices from the transient response measurements.
This setup also allows us to investigate changes in the pulse shape, if any, due to the ultra-low-temperature-effects (non-linearities), revealed in the DC characterization (shown in
As mentioned above, a controller circuit has to produce fast pulses. Thus transient response of NMOS and PMOS devices provides information about the behavior of the devices at cryogenic temperatures, during ultra-high speed switching.
Due to the maximum effective power dissipation limit of the dilution refrigerator (100 μW), the I(V) data for 30 mK of both 500 nm and 250 nm processes were limited to the range VGS=VDS=[−1, 1] V and ID=[−0.1, 0.1] mA.
The PMOS measurements revealed a ft˜(100 ps)−1=10 GHz, which was proximal to the quoted value, from PSC, of 20 GHz. The transient response characteristics which were obtain for square-wave functions (emulating step inputs) also showed that the step response of the device is not affected by the non-linearity in the ohmic region and early SCEs in the saturation region of the MOSFETs either at 300 K or at 4.2 K. However we are not certain about both the design of the device and its particular effects on the transient response behavior of the device, we have observed. Hence we emphasize that while our interpretation of the observed results is speculative, the purpose of the transient response measurements at 300 K, and 4.2 K were to ascertain whether the devices would be affected by the deviation of the device characteristics at 4.2 K from those at 300 K.
The underdamped (ringing) behavior at the transition edges was due to a combination of parasitic inductance in the bonding wire and reflections in the lines. The bonding wire inductance was estimated to be about 5 nH for 5 mm of bonding wire which can produce the ringing in transient response as shown in
We found that the on-state and off-state responses of the PMOS were similar with almost identical ringing and reflections occurring except during switching. So we have shown the difference (subtraction) between the on- and off-states performed to extract what we believe is the device characteristics.
Our characterization of PSC 500 nm and 250 nm SOS CMOS FETs has confirmed the suitability of the technology for designing the quantum controller and observe circuits.
We have investigated NMOS and PMOS devices from both processes and characterized them for DC response at 300 K, 4.2 K, and 30 mK, and transient response at 300 K, and 4.2 K. We have shown that the devices operate favorable at these ultra-low temperatures with some changes to their characteristics such as a non-linearity in the ohmic region of both NMOS and PMOS in both processes, earlier SCEs such as HCE in the saturation region, and increased transconductance leading to slightly higher current gain.
We conclude that the PSC 500 nm and 250 mm UTSi SOS processes are suitable for use for applications that require ultra-low power or ultra-low temperature operation.
Further examples of the invention will now be described with reference to the following drawings, in which:
Referring now to
a is the schematic diagram for the layout of
Although the invention has been described with reference to particular MOSFETs with proven low temperature operability, it will be appreciated that many other MOSFET devices may be used in the invention.
Further, although the invention has been described with reference to application to the control of quantum computers, it will be appreciated that it could be applied in other ways. For instance in research requiring time-resolved applications and high-bandwidth signal amplification, such as fundamental semiconductor or pulsed physics, excitons, etc.
It will also be appreciated that an all digital integrated circuit can be fabricated.