Patent Application
20060079402
This present invention relates to an intermetallic superconductor and an alloy superconductor which can be utilized in superconducting electronics such as a large scale electric power transmission system, a superconductive power storage system, a high performance Josephson device and a high frequency or electronic device, and which especially are high in superconducting transition temperature, are easy to manufacture, excel in malleability and ductility, and yet are altogether new. The invention also relates to a method of making such a novel superconductor.
Superconductors are known to include a superconductor made of a simple metal, a superconductor made of a compound, and a superconductor made of composite oxides.
A simple metal superconductor may contain a simple metal such Pb and Nb but is known to lack utility because it is low in superconducting transition temperature.
Known as intermetallic compound superconductors include those having a A15 type crystallographic structure of intermetallic compounds as represented by Nb3Ge, Nb3Ga, Nb3Al and Nb3Sn, and those having a chevrel type crystallographic structure of intermetallic compounds as represented by PbMo6S8. Intermetallic compound superconductors having an AlB2 type crystallographic structure of intermetallic compounds as represented by NbB2 are also known which, however, are also known to be extremely low in superconducting transition temperature (Tc=0.62 K, see Journal of the Less-Common Metals, 67 (1979), 249-255). These intermetallic compound superconductors include one with Nb3Ge which is relatively high in superconducting transition temperature (=about 23 K), but commonly have the disadvantage that they are weak in distortion and are fragile.
Known as a composite oxide superconductor include La group oxide superconductors as represented by composition La2−xBaxCuO4, Y group oxide superconductors as represented by composition Y1Ba2Cu3O7−x, Bi group oxide superconductors as represented by composition Bi2Sr2Can−1CunO2n+2, T1 group superconductors as represented by composition T12Ba2Can−1CunO2n+2, and Hg group oxide superconductors as represented by Hg1Ba1CaCu1O6+x. These composite oxide superconductors are high in superconducting transition temperature and indeed include those which have their superconducting transition temperatures reaching as high as 150 K. The composite oxide superconductor has a perovskite structure made up of a lamination of an octahedral, pyramidal or planar superconducting layer of CuO2, and a block layer (dissimilar in crystallographic structure to the superconducting layer) made of an atom or atoms such as La, Ca, Y, Bi or Hg and oxygen. As such the extreme complexity of the crystallographic structure of a composite oxide superconductor makes it difficult to conduct its production in a large volume and with good reproducibly. In addition, the superconductor being a composite oxide is naturally poor in both malleability and ductility, and is hard to use as a superconducting electric cable or wire.
A well known alloy superconductor is a Nb—Ti alloy, which is excellent in malleability and ductility and hence has been used to form superconducting electric cables or wires and superconducting magnets. However, an alloy conductor is as low in superconducting transition temperature as, e.g., about 9 K with the Nb—Ti alloy, and hence improvements in them are being sought.
It is accordingly an object of the present invention to provide an intermetallic compound that is high in superconducting transition temperature. It is also an object of the present invention to provide an alloy superconductor that is high in superconducting transition temperature and also excels in malleability and ductility. It is further an object of the present invention to provide methods of making them reproducibly and at a relative low cost of manufacture.
First, it is summarily stated how the inventors arrived at the present invention. It is generally thought that a superconductor made to contain a light element has its superconducting transition temperature raised. It was forecast that boron which is a light element and whose crystal is a semiconductor may be combined with another or other elements to develop superconductivity with a high probability. While among compounds of various transition metallic elements with boron, TiB2 taking the AlB2 crystallographic structure was found to be extremely low in electrical resistance, it did not exhibit superconductivity. After various three-element combinations were tried, it was confirmed that a combination of magnesium, a transition metal and boron developed a superconductivity which was, however, extremely low. Then, a trial of composing these elements in various altered proportions revealed that a stronger superconductivity is obtainable with a compound of magnesium and boron without containing a transition metallic element. However, since compounds were initially tested which contained magnesium much larger in amount than boron, powder X-ray diffraction measurements made observable only diffraction lines based on the crystallographic structure of the magnesium crystal, leading to the assumption that the genesis of the superconductivity might be an alloy in which boron is solid-dissolved into magnesium. Then, however, experiments conducted while varying the proportions of magnesium and boron little by little have finally revealed that the intermetallic compound of MgB exhibits a very high superconducting transition temperature at composition proportions of Mg1B2 where a strong superconductivity is also observed. Upon the confirmation that this is the essential of the superconduction, the present invention has been arrived at.
Accordingly, the first object mentioned above is attained in accordance with the present invention by an intermetallic compound superconductor characterized in that it is made of magnesium (Mg) and boron (B).
The second object mentioned above is attained in accordance with the present invention by an alloy superconductor characterized in that it contains an intermetallic compound made of Mg and B and also contains one or more metallic elements.
The said intermetallic compound superconductor is characterized in that it has a composition represented by chemical composition formula: Mg1B2 and having a hexagonal AlB2 type crystallographic structure in which a Mg layer and a B layer alternately lie.
Also, the said alloy superconductor that contains an intermetallic compound made of Mg and B is characterized in that it is an alloy having a composition represented by composition formula: Mg1−xB2+y where 0<x<1, −2<y<0 and 0<y<2.
The intermetallic compound superconductor made up as mentioned above has a superconducting transition temperature (Tc) of 39 K, and is higher in superconducting transition temperature than any intermetallic compound superconductor so far known and indeed much higher in superconducting transition temperature than any known intermetallic compound superconductor having the AlB2 type crystallographic structure.
Also, the alloy superconductor made up as mentioned above has a superconducting transition temperature (Tc) of 39 K, and is higher in superconducting transition temperature than any alloy superconductor so far known and comes also higher in both malleability and ductility.
The intermetallic compound superconductor made of magnesium and boron as mentioned above can be used as a superconductor high in superconducting transition temperature (Tc) in superconducting electronics such as a high performance Josephson device and a high frequency or electronic device.
The alloy superconductor containing the intermetallic compound made up of magnesium and boron as mentioned above can be used as a superconductor high in superconducting transition temperature and also excellent in malleability and ductility for a superconducting electric wire or cable used in a superconducting electric powder transmission system, a superconducting electric powder storage system or the like and also in a superconducting electronic component such as a high performance Josephson device and a high frequency or electronic device.
The present invention further provides a method of making an intermetallic compound superconductor, which method is characterized in that it comprises the steps of: mixing a Mg containing powder and a B containing powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=½, shaping the said mixture powder into the form of a pellet, and heating the said pellet in an inert gas to form the intermetallic compound superconductor.
An alternative method of manufacture of an intermetallic compound superconductor in accordance with the present invention may comprise the steps of: mixing a Mg containing powder and a B containing powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=½, shaping the said mixture powder into the form of a pellet, and heating the said pellet in a vacuum to form the intermetallic compound superconductor.
An alternative method of manufacture of an intermetallic compound superconductor in accordance with the present invention may comprise the steps of: mixing a Mg containing powder and a B containing powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=½, shaping the said mixture powder into the form of a pellet, and heating the said pellet in a pressurized inert gas to form the intermetallic compound superconductor.
An alternative method of manufacture of an intermetallic compound superconductor in accordance with the present invention may comprise the steps of: mixing a Mg containing powder and a B containing powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=½, shaping the said mixture powder into the form of a pellet, and pressing and heating or hot-pressing the said pellet to form the intermetallic compound superconductor.
The present invention also provides a method of making an alloy superconductor, characterized in that it comprises the steps of: mixing a Mg containing powder and a B containing powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=(1−x)/(2+y) where 0<x<1, −2<y<0 and 0<y<2, shaping the said mixture powder into the form of a pellet, and heating the said pellet in an inert gas to form the alloy superconductor.
An alternative method of manufacture of an alloy superconductor in accordance with the present invention may comprise the steps of: mixing a Mg containing powder and a B containing powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=(1−x)/(2+y) where 0<x<1, −2<y<0 and 0<y<2, shaping the said mixture powder into the form of a pellet, and heating the said pellet in a vacuum to form the alloy superconductor.
An alternative method of manufacture of an alloy superconductor in accordance with the present invention may comprise the steps of: mixing a Mg containing powder and a B containing powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=(1−x)/(2+y) where 0<x<1, −2<y<0 and 0<y<2, shaping the said mixture powder into the form of a pellet, and heating the said pellet in a pressurized inert gas to form the alloy superconductor.
An alternative method of manufacture of an alloy superconductor in accordance with the present invention may comprise the steps of: mixing a Mg containing powder and a B containing powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=(1−x)/(2+y) where 0<x<1, −2<y<0 and 0<y<2, shaping the said mixture powder into the form of a pellet, and pressing and heating or hot pressing the said pellet to form the alloy superconductor.
In the method of manufacture of an intermetallic compound superconductor mentioned above, the said pellet is preferably heated in the said inert gas at a temperature of 700 to 2000° C. for a period of several seconds or more.
In the method of manufacture of an intermetallic compound superconductor mentioned above, the said pellet is preferably heated in the vacuum under a pressure of 2×10−2 Pa or less at a temperature of 650 to 1100° C. for a period of several minutes or more.
In the method of manufacture of an intermetallic compound superconductor mentioned above, the said pellet is also preferably heated in the said inert gas under a pressure of 1 to 200 MPa at a temperature of 600 to 1100° C. for a period of several minutes or more.
In the method of manufacture of an intermetallic compound superconductor mentioned above, the said pellet is also preferably pressed and heated or hot pressed under a pressure of 0.1 to 6 GPa at a temperature of 700 to 1400° C. for a period of several minutes or more.
In the method of manufacture of an alloy superconductor mentioned above, the said pellet is advantageously heated in the said inert gas at a temperature of 700 to 2000° C. for a period of several seconds or more.
In the method of manufacture of an alloy superconductor mentioned above, the said pellet is advantageously heated in the vacuum under a pressure of 2×10−2 Pa or less at a temperature of 650 to 1100° C. for a period of several minutes or more.
In the method of manufacture of an alloy superconductor mentioned above, the said pellet is advantageously heated in the said inert gas under a pressure of 1 to 200 MPa at a temperature of 600 to 1100° C. for a period of several minutes or more.
In the method of manufacture of an alloy superconductor mentioned above, the said pellet is advantageously pressed and heated or hot pressed under a pressure of 0.1 to 6 GPa at a temperature of 700 to 1400° C. for a period of several minutes or more.
The method of making an intermetallic compound superconductor mentioned above permits an intermetallic compound superconductor composed of magnesium (Mg) and boron (B) in accordance with the present invention to be manufactured reproducibly and easily.
The method of making an alloy superconductor mentioned above permits an alloy superconductor containing the above-mentioned intermetallic compound in accordance with the present invention to be manufactured reproducibly and easily.
The present invention will better be understood from the following detailed description and the drawings attached hereto showing certain illustrative forms of embodiment of the present invention. In this connection, it should be noted that such forms of embodiment illustrated in the accompanying drawings hereof are intended in no way to limit the present invention but to facilitate an explanation and understanding thereof. In the drawings:
FIGS. 2(a) and 2(b) are a side and a plan view, respectively, of the crystallographic structure of the intermetallic compound made of magnesium and boron in accordance with the present invention;
Hereinafter, the present invention will be described in detail with reference to suitable forms of embodiment thereof illustrated in the drawing figures.
Mention is first made of the crystallographic structure of an intermetallic compound made of magnesium and boron according to the present invention.
As shown in
From the powder X-ray diffraction measurement pattern shown in
As is apparent from
Mention is next made of the superconducting characteristics of the intermetallic compound superconductor made of magnesium and boron in accordance with the present invention.
From
While the superconducting transition temperature is usually defined in terms of both Tconset and Tczero, the intermetallic compound superconductor according to the present invention has Tconset=39 K and Tczero=38 K.
Mention is next made of a result of measurements of the magnetic susceptibility of the intermetallic compound according to the present invention.
As is apparent from
In
Mention is next made of an alloy superconductor containing the intermetallic compound made of magnesium and boron in accordance with the present invention.
In
Mention is next made of the superconducting properties of an alloy superconductor containing the intermetallic compound made of magnesium and boron.
Mention is next made of a result of measurements conducted of the magnetic susceptibility of alloy superconductor according to the present invention.
As is apparent from
Mention is next made of methods of making an intermetallic compound superconductor made of magnesium and boron, and alloy superconductor containing the intermetallic compound made of magnesium and boron, in accordance with the present invention.
In the methods of making according to the present invention to be described below, which of intermetallic compound superconductor and alloy superconductor is coming out depends on the compositional proportions of Mg and B in feedstock powders to be mixed together. Thus, if feedstock powders are mixed together to contain magnesium and boron at a compositional ratio of Mg/B=½, then the entire powder mixture makes up a single phase intermetallic compound superconductor of the hexagonal AlB2 type crystallographic structure expressed by composition formula: Mg1B2.
On the other hand, if feedstock powders are mixed together to contain magnesium and boron at a compositional ratio of Mg/B=(1−x)/(2+y) where 0<x<1, −2<y<0 and 0<y<2, then there comes out an alloy superconductor containing the intermetallic compound mentioned above. Here, the compositional ratio can be varied to meet with an application purpose. For example, making Mg larger in compositional proportion may produce a superconducting electric cable. For Mg feedstock powder, use may be made of Mg powder or MgO powder. And, for B feedstock powder, use may be made of B powder.
In making an intermetallic compound superconductor or a powder conductor, several methods are available.
In a first method, a Mg powder and a B powder are mixed together in an agitating apparatus to form a powder mixture, which is then shaped into a pellet form, which in turn is heated in an inert gas atmosphere at a temperature of 700 to 2000° C. for a period of several seconds or more by using any known heating means such as arc heating, plasma-arc heating or high-frequency melting. This method permits forming either superconductor with ease.
In a second method, a Mg powder and a B powder are mixed together in the agitating apparatus to form a powder mixture, which is then shaped into a pellet form, which in turn is heated in a vacuum under a pressure of 2×10−2 Pa or less at a temperature of 650 to 1100° C. for a period of several minutes or more. This method permits forming either superconductor with ease.
In a third method, a Mg powder and a B powder are mixed together in the agitating apparatus to form a powder mixture, which is then shaped into a pellet form, which in turn is placed in a HIP (hot isostatic pressing) apparatus (made by, e.g., company Kobe Seiko, high temperature, high pressure atmosphere furnace) charged with an inert gas and is heated therein under an inert gas pressure of 1 to 200 MPa at a temperature of 600 to 1100° C. for a period of several minutes or more. This method permits forming either superconductor with ease.
In a fourth method, Mg powder and B powder are mixed together in the agitating apparatus to form a powder mixture, which is then shaped into a pellet form, which in turn is placed in a cubic anvil pressing or like pressing apparatus and is heated therein under a pressure of 0.1 to 6 GPa at a temperature of 700 to 1400° C. (hot pressed) for a period of several minutes or more. This method permits forming either superconductor with ease. High pressure is required to facilitate joining grain boundaries together while high temperature is needed to grow superconducting phase.
It should be noted here that an intermetallic compound superconductor and an alloy superconductor according to the present invention are not limited in form to a polycrystalline sintered body as above but may in form be a polycrystalline bulk body, large single crystal, or a thin film.
Using a conventional bulk body fabricating apparatus such as a forging or a superhigh-pressure pressing and heating synthetic apparatus permits an intermetallic compound superconductor in the form of a polycrystalline bulk body to be made that is light in weight, high in hardness and excels in corrosion resistance.
Also, a large single-crystal intermetallic compound superconductor is obtainable by using a known single-crystal growth process such as recrystallization, simple lifting, floating zone melting or fluxing, with the use of a suitable crucible in a controlled atmosphere.
Further, a thin-film intermetallic compound superconductor is obtainable by chemical gas-phase vapor deposition using a gas phase source containing magnesium and boron at compositional ratio of Mg/B=½, or by sputtering with the use of a target material as a sputtering source containing magnesium and boron at compositional ratio of Mg/B=½. Also, for the substrate on which to form a thin-film intermetallic compound superconductor, use may be a metal substrate formed of, e.g., Cu, or a ceramic substrate, and may be a composite substrate having a ceramic deposited on a metal substrate. Such substrates may selectively be used to meet with a particular use or application.
A superconducting alloy that excels in malleability and ductility is obtainable by making larger in Mg and B proportions the amount of Mg that excels in malleability and ductility, or by compounding upon addition of another metal or metals that excels in malleability and ductility. Such a superconducting alloy can be worked by rolling or extrusion into a ultra-thin multi-core superconducting cable, a thin superconducting wire, or a superconducting alloy wire or cable.
As can be appreciated from the foregoing description, the present invention provides an intermetallic compound superconductor that is high in superconducting transition temperature and is easy to make and hence is extremely useful when applied to superconducting electronics such as a high performance Josephson device, a high frequency or electronic device.
The present invention also provides an alloy superconductor containing the intermetallic compound, which is high in superconducting transition temperature, excels in malleability and ductility and is easy to make, and hence is extremely useful when applied to a large scale superconducting cable system, a superconducting electric power storage system, a high performance Josephson device, a high frequency or electronic device.
Further, using the method of making an intermetallic compound superconductor or an alloy superconductor containing such an intermetallic compound permits the intermetallic superconductor or the alloy superconductor containing such an intermetallic compound to be manufactured with an extremely high reproducibility, with ease, and at a reasonable cost.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2001-1948 | Jan 2001 | JP | national |
This application is a divisional application of prior application Ser. No. 10/220,272 filed Sep. 9, 2002, which is a §371 of international application No. PCT/JP01/06383 filed Jul. 24, 2001.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10220272 | Sep 2002 | US |
| Child | 11202335 | Aug 2005 | US |