Claims
- 1. A stucco material for use in producing shell molds for investment casting, said stucco material consisting of solid granules having a particle size of 18 to 140 mesh and consisting of silica powder and an organic binder, said powder being bound together by said binder, said binder having the property that when heated to firing temperatures used in the investment casting process, will no longer bind said silica powder together and said stucco material having the property such that the linear thermal expansion of shell molds made therefrom is not more than 0.6 percent when the molds are heated from room temperature to 1800.degree. F.
- 2. The stucco material of claim 1 in which the organic binder is selected from the group consisting of polyvinyl acetate, polyvinyl alcohol, starch, and gelatin.
- 3. The stucco material of claim 1 having a particle size distribution of 18 to 50 mesh.
- 4. The stucco material of claim 1 having the following particle size distribution:
- ______________________________________U.S. Std. Screen % ON______________________________________18 mesh 020 mesh 5-2050 mesh 77-88Pan max 2______________________________________
- 5. The stucco material of claim 1 having the following particle size distribution:
- ______________________________________U.S. Std. Screen % ON______________________________________ 50 mesh Trace120 mesh 80-95140 mesh 5-20Pan max 2%______________________________________
- 6. The stucco material of claim 1 in which the organic binder is polyvinyl acetate.
- 7. A stucco material for use in producing shell molds for investment casting, said stucco material consisting of solid granules having a particle size of 18 to 140 mesh and produced from a mixture consisting essentially of silica powder, vinyl acetate emulsion, and water, said mixture having been pelletized, dried, crumbled, and sieved, to produce said stucco material.
- 8. The stucco material of claim 7 in which the relative amounts in said mixture are 5000 grams of silica powder, to at least 500 ml of vinyl acetate emulsion, and sufficient added water for pelletizing.
- 9. The stucco material of claim 7 having a grain size distribution of 18 to 50 mesh.
- 10. The stucco material of claim 7 having the following grain size distribution:
- ______________________________________U.S. Std. sieve % ON______________________________________ 50 Mesh Trace120 Mesh 80-95140 Mesh 5-20Pan 2 Max______________________________________
Parent Case Info
This is a continuation of co-pending application Ser. No. 431,338, filed on Sept. 30, 1982, now abandoned.