Patent Application
20140131192
The invention relates to a photocatalytic nanocomposite, a related method of making the photocatalytic nanocomposite, and a method of using the photocatalytic nanocomposite to covert carbon dioxide into methane.
Photocatalytic materials are drawing significant attention because of their potential for solving environmental and energy problems. Among these problems are finding ways to address the contributions of CO2 to global warming while still permitting increased energy consumption, as energy plays a critical role in the quality of life improvement and economic prosperity.
One potential avenue for reduction of greenhouse gases such as CO2 has been CO2 photoreduction using a photocatalyst in which CO2 is reduced to various less harmful products over the photocatalyst that is activated by UV radiation. To date, titanium dioxide (TiO2) is one of the most studied photocatalysts because it has shown the most efficient photocatalytic activity, highest stability, low cost, as well as low toxicity. In the photocatalytic reaction, electrons and holes are produced from TiO2 under UV irradiation. The electrons and holes subsequently interact with reactants (including CO2) to form the products.
However, CO2 photoreduction has only been performed using titanium dioxide (TiO2) with limited or qualified success. One of the problems in using unmodified TiO2 as a photocatalyst is that electron and hole recombination leads to low photoconversion efficiency. Although various modifications to the catalytic structure have been attempted, none of the modifications have created a commercially and industrially viable structure for CO2 photoreduction.
Hence, a continued need exists for a photocatalyst that improves the kinetics of a photoreduction reaction of CO2.
According to one aspect of the invention, a photocatalytic nanocomposite is provided that includes a reduced graphite oxide, a photocatalytic metal oxide in nanoparticle form, wherein the photocatalytic metal oxide in nanoparticle form is dispersed in the reduced graphite oxide. The photocatalytic metal oxide may be TiO2 and may be in a mixed phase form including rutile and anatase. The reduced graphite oxide may be a powder.
The photocatalytic nanocomposite may further include an ionic moiety attached to the reduced graphite oxide. The ionic moiety may comprise R1R2R3 in which R1 is NH, R2 is alkylene, and R3 is a cationic group. In some forms, R2 may be C1 to C5 alkylene, and R3 may be an imidazole ring protonated or substituted at a nitrogen atom. In one more specific form, R2 may be propylene and R3 may be an alkyl-substituted imidazole ring.
In some instances, the reduced graphite oxide may be an ionic liquid functionalized reduced graphite oxide formed by attaching a NH2-terminated ionic liquid to the reduced graphite oxide.
According to another aspect of the invention, a method of making a photocatalytic nanocomposite of this type is provided. The method of making a photocatalytic nanocomposite includes oxidizing graphite to form a reduced graphite oxide and mixing the reduced graphite oxide with TiO2 nanoparticles to form the photocatalytic nanocomposite. The reduced graphite oxide may be functionalized with a NH2-terminated ionic liquid to form an ionic liquid functionalized reduced graphite oxide before the step of mixing. The NH2-terminated ionic liquid may an imidazole such as, for example, a 1-butyl-3-methylimidazolium-based ionic liquid (e.g., 1-butyl-3-methylimidazolium chloride).
According to still another aspect of this invention a method of CO2 photoreduction is provided. The method of CO2 photoreduction includes contacting reactants of CO2 and H2O over a photocatalytic nanocomposite of the type described herein and reacting the CO2 and H2O over the photocatalytic nanocomposite to produce products including CH4. In some forms, the products may be substantially free of CO gas. In some forms, the CH4 may have a production rate in excess of 10 μmol/g catalyst-hr or in excess of 250 μmol/g catalyst-hr.
According to one specific example, an ionic liquid functionalized reduced graphite oxide (IL-RGO)/TiO2 nanocomposite was synthesized and used to reduce CO2 to a hydrocarbon in the presence of H2O vapor. IL-RGO was synthesized through chemically attaching the ionic liquid, 1-butyl-3-methylimidazolium chloride (C4mimCl), to a graphite oxide (GO) surface and simultaneously reducing GO to RGO in a basic reaction environment. As a comparison, reduced graphite oxide (RGO) was synthesized using the same procedure, but without adding the ionic liquid. The SEM image revealed that IL-RGO/TiO2 contained a homogeneous dispersion of graphite flakes with TiO2 nanoparticles. Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) was used to study the conversion of CO2 and H2O vapor over the IL-RGO/TiO2 catalyst. Under UV-Vis irradiation, two new peaks were detected in the infrared spectrum after just 40 seconds of irradiation. The intensities of these peaks continuously increased in subsequent spectra that were taken under longer irradiation time. The two peaks detected as products were characteristic of CH4. Background experiments that were conducted confirmed that CH4 was indeed generated from the reduction of CO2 over the IL-RGO/TiO2 catalyst surface. A CH4 production rate of 279 μmol/g catalyst-hr (as measured using DRIFTS) over a 55 minute period was calculated. These findings suggest the direct, selective formation of CH4 in the absence of CO.
These and still other advantages of the invention will be apparent from the detailed description and drawings. What follows is merely a description of some preferred embodiments of the present invention. To assess the full scope of the invention the claims should be looked to as these preferred embodiments are not intended to be the only embodiments within the scope of the claims.
Carbonaceous nanomaterials have unique properties and the potential to control the structural and electrical properties of photocatalysts. The presence of a carbon material such as carbon nanotubes (CNTs) or graphene might potentially reduce electron and hole recombination in the photocatalyst via transport of the electrons to the conductive carbon material. By improving the separation of the charges, recombination may be avoided thereby enhancing the photoconversion efficiency of TiO2. Indeed, to date some nanocarbon (for example, CNTs or graphene)/TiO2 composites have shown improved photocatalytic activity over TiO2 in various applications (for example, the photooxidation of environmental pollutants).
As compared to cylindrical CNTs, planar graphene may have a smaller electron transfer barrier. As a result, the electron-hole recombination may be less. Graphene is an atomic sheet of sp2-bonded carbon atoms that are arranged into a honeycomb structure. The high surface area of graphene may increase the adsorption of reactants and provide more active sites. Nearly 90% enhancement in photocurrent was seen for reduced graphene oxide described below, which serves as an electron collector and transporter in the graphene-TiO2 composite. A significant enhancement in the reaction rate for the degradation of methylene blue was observed using a P25 (Degussa)-graphene composite material in contrast with a bare P25 (Degussa) or a P25 (Degussa)-CNT material with the same carbon content. In addition, a decrease in charge transfer resistance of graphene/P25 (Degussa) sample was observed versus P25 (Degussa) alone.
Presently, there are only a few examples regarding the use of TiO2 nanocarbon materials for the conversion of carbon dioxide (CO2) and H2O vapor to fuels. Xia et al. synthesized multi-walled carbon nanotube (MWCNT) supported TIO2 and investigated its photocatalytic activity in the reduction of CO2 with H2O (Xia, X. H.; Jia, Z. H.; Yu, Y.; Liang, Y.; Wang, Z.; Ma, L. L., Preparation of multi-walled carbon nanotube supported TiO2 and its photocatalytic activity in the reduction of CO2 with H2O. Carbon 2007, 45, 717-721.). Sol-gel and hydrothermal methods were used to synthesize the MWCNT/TiO2 composite. Both syntheses methods led to the formation of C2H5OH, HCOOH and CH4. The total carbonaceous yields of the products were higher than the reported yields in the literature, which focused on using other materials to modify TiO2 rather than carbon (i.e., Cu doping, Cu—Fe co-doping TiO2/porous silica, TiO2 nanotube). This result suggests that carbon-containing TiO2 materials may be better than other materials in terms of enhancing CO2 photoconversion efficiency.
It appears there has been only one instance in which an externally mixed graphene/TiO2 material was applied to CO2 photoreduction. Liang, Y. T.; Vijayan, B. K.; Gray, K. A.; Hersam, M. C., Minimizing Graphene Defects Enhances Titania Nanocomposite-Based Photocatalytic Reduction of CO2 for Improved Solar Fuel Production. Nano Letters 2011, 11, 2865-2870. A solvent exfoliated graphene/P25 thin film and a thermally reduced graphite oxide/P25 thin film were used as the photocatalysts, and CH4 was the major product identified. The CH4 production rates of exfoliated graphene/P25 thin film and a thermally reduced graphite oxide/P25 thin film were 8.1 μmol/m2-hr and 1.8 μmol/m2-hr, respectively. The results indicate that TiO2/graphene may be selective towards CH4 production but provided low reaction rates.
In this disclosure, a novel synthesis method was used to create an improved graphene type carbon/TiO2 composite material for CO2 photoreduction, and the product of the CO2 photocatalytic reaction in the presence of water vapor was studied. Instead of adding TiO2 and the graphene type material separately, a nanocomposite material was formed. Graphene is a single atomic layer of sp2 carbon structure. In the disclosed method and resulting structure, carbon layers were separated by oxidizing natural graphite to form graphite oxide and subsequently functionalizing graphite oxide with a NH2-terminated ionic liquid. At the same time graphite oxide was reacted to form reduced graphite oxide (RGO) in a basic reaction environment. The high solubility of the ionic liquid in water makes it possible for an ionic liquid functionalized reduced graphite oxide (IL-RGO) to mix well with TiO2 nanoparticles in water. Moreover, the ionic liquid, which is functionalized to the RGO surface, may introduce surface charge to the RGO. The charge repulsion may help to further separate the graphite layers. The high surface area of the layer-separated graphite material may enhance the adsorption of the reactants, i.e. CO2 and H2O vapor, thus creating more reactive sites.
In addition, NH2-ionic liquid cations may significantly enhance the ability to attract CO2 via amine group-CO2 interactions. Therefore, the amine-functionalized ionic liquid may also enhance the adsorption of CO2. Previous experimental results indicate that the C4mimCl ionic liquid does not interact with alkanes. CH4 is a potential product of CO2 photoreduction using TiO2 or modified TiO2 catalyst. Therefore, the ionic liquid may be able to selectively adsorb the reactant, CO2, but quickly dissociate the potential product, CH4, thus promoting the photoreduction of CO2.
The IL-RGO/TiO2 nanocomposite was applied to reduce CO2 in the presence of H2O vapor. The products of CO2 photoreduction over the IL-RGO/TiO2 was compared with the product formation data that were reported in the literature using pristine TiO2 (P25) and other modified TiO2 in order to provide an initial examination of the selectivity towards different products.
In the examples provided below, the new method was used to synthesize a carbon/semiconductor composite material via attaching ionic liquid to graphite oxide surface to obtain the ionic liquid functionalized reduced graphite oxide (IL-RGO), and mixing it with TiO2 nanoparticles in solution. The successful synthesis of this material was confirmed by Raman spectra, XRD, XPS and SEM. Comparing RGO without functionalized ionic liquid, the IL-RGO layers were separated and IL-RGO flakes can be clearly seen in the SEM images. In addition, the SEM images showed that TiO2 nanoparticles are dispersed with IL-RGO flakes. The photoreduction of CO2 over IL-RGO/TiO2 in the presence of H2O vapor was investigated using Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS). CH4 was formed after just 40 seconds of UV-Vis irradiation over the catalyst of IL-RGO/TiO2. The IR features of CH4 increased as the irradiation time increased. However, no product was found for the photoreduction of commercial P25 under the same experimental conditions. Therefore, the presence of IL-RGO significantly enhances the photocatalytic activity of P25 due to the enhanced electron-hole separation. In addition, CH4 was found to be the only product for IL-RGO/TiO2.
The regeneration and reuse of IL-RGO/TiO2 catalyst for CO2 photoreduction was also investigated. The regenerated catalyst can produce almost identical amount of CH4 at the same irradiation times. A CH4 production rate of 279 μmol/g catalyst-hr over a 55 minute period was calculated.
The following examples are presented for illustrative purposes only, and are not intended to limit the scope of the present invention in any way.
Synthesis of the ionic liquid reduced graphite oxide/TiO2 (IL-RGO/TiO2) composite involved three basic steps: synthesis of graphite oxide, functionalization and reduction of the graphite oxide in order to make the material more conductive, and addition of the TiO2 to allow for photoactivity.
Graphite Oxide (GO) was synthesized from natural graphite powder (325 mesh, Alfa Aesar) by the method of Hummers and Offeman (Hummers, W. S.; Offeman, R. E., Preparation of Graphitic Oxide. Journal of the American Chemical Society 1958, 80, 1339-1339). Prior to synthesis using Hummers and Offeman's method, the graphite powder was pre-oxidized. Otherwise, incompletely oxidized graphene-core/GO-shell particles were observed in the final product. The pre-oxidation procedure followed the method of Kovtyukhova et al. (Kovtyukhova, N. I.; Ollivier, P. J.; Martin, B. R.; Mallouk, T. E.; Chizhik, S. A.; Buzaneva, E. V.; Gorchinskiy, A. D., Layer-by-layer assembly of ultrathin composite films from micron-sized graphite oxide sheets and polycations. Chemistry of Materials 1999, 11, 771-778.) Briefly, the pre-oxidation process used concentrated H2SO4, K2S2O8 and P2O5 to oxidize the graphite powder. The resultant product was subsequently thermally isolated and allowed to cool to room temperature. After cooling, the product was diluted and washed with distilled water until the water's pH became neutral. The product was dried in air at ambient temperature overnight and subjected to oxidation by Hummers and Offeman's method. The pre-oxidized graphite powder was further oxidized using 0° C. concentrated H2SO4 and KMnO4. The reaction was terminated by the addition of a large amount of distilled water and 30% H2O2 solution. The mixture was centrifuged with 1:10 HCl solution to remove metal ions. Also, additional distilled water washing was done to the mixture until a neutral pH was achieved. The mixture was dark brown in color. The GO was added to distilled water and sonicated for 15 minutes to separate the GO layers. Finally, the GO sample was obtained by centrifugation of the GO solution at 5000 rpm for 30 minutes.
It is observed that this oxidation step may help to prevent the graphite from aggregating during mixing, as might occur when using natural graphite flakes. This is evidenced by SEM images in the results below in which the flakes remain separated.
The overall reaction for the synthesis of IL-RGO is presented in
First, 3-chloropropylamine hydrochloride (Sigma Aldrich, 98%) and 1-methylimidazole (Sigma Aldrich, 99%) were added to ethanol (Sigma Aldrich, ≧99.5%). The mixture was then refluxed under nitrogen for 24 hours. The resulting turbid mixture was purified by re-crystallization from ethanol and ethyl acetate as anti-solvent. Finally, the resulting ionic liquid was dried under N2 at 60° C. overnight.
The C4mimCl functionalized RGO synthesis is based on an epoxide ring-opening reaction between GO and NH2—C4mimCl. NH2—C4mimCl was added into a GO dispersed solution. The salt effect of the GO sheet occurred due to the presence of the ionic liquid. The epoxide ring-opening reaction can be catalyzed by a base. Therefore, KOH was added into the turbid mixture solution. The solution was subjected to ultrasonication for 30 minutes. Lastly, the homogeneous solution was vigorously stirred at 80° C. for 24 hours. The resulting solution was washed using ethanol and distilled water several times until the pH was neutral. The resulting solution was subjected to the IL-RGO/TiO2 nanocomposite material synthesis process. The IL-RGO solution was dried at room temperature for IL-RGO material characterization. For comparison, RGO was synthesized using the same procedure, but without adding the NH2—C4mimC;.
TiO2 nanoparticles (Evonik P25) were mixed with distilled water and 1-Butyl-3-methylimidazolium tetrafluoroborate (C4mimBF4, Sigma Aldrich, 98%) (H2O:C4mimBF4=9:1 by volume) to make a TiO2 suspension. Before making the IL-RGO/TiO2 composite, the IL-RGO solution was ultrasonicated for 30 minutes and stirred for 1 hour. Later, the IL-RGO solution was added to the TiO2 suspension and vigorously stirred for one hour. The mass percentage of IL-RGO was 3.5% of the composite material. The IL-RGO/TiO2 mixture was washed until the pH became neutral. Then the mixture was ultrsonicated for 30 minutes and dried at 80° C. overnight. Eventually, the sample was ground to powder for use in the CO2 conversion experiments. For comparison, the RGO/TiO2 was synthesized using the same procedure.
Raman spectra of GO and IL-RGO were collected using a custom built Raman spectrometer in a 180° geometry. The sample was excited using a 100 mW compass 532 nm laser. The data were collected using an Acton 300i spectrograph and a back thinned Princeton Instruments liquid nitrogen cooled CCD detector. The spectral resolution was 3.5 cm−1. X-ray Diffraction (XRD) data were collected with a high resolution X-ray diffractometer (PANALYTICAL X′PERT PRO) using Cu-Kα radiations and an X′celerator detector. Scanning electron microscopy (SEM) was performed using an XL30 ESEM-FEG. X-ray photoelectron spectroscopy (XPS) was performed using a VG ESCALAB 220i-XL aluminum-Kα (1486.6 eV) X-ray source.
The Raman spectra of GO and IL-RGO are shown in
X-ray spectroscopy (XPS) was used to characterize the chemical composition of the material. The XPS spectra are presented in
The atomic concentration ratio of carbon to oxygen (C/O) determined using the XPS data of GO was 0.8, while the C/O ratio for IL-RGO determined using the XPS data was 1.4. The atomic concentration of the C—N peak shown in
High resolution XPS spectra of C1s in GO and IL-RGO are shown in
Turning now to
The scanning electron micrographs (SEM) of IL-RGO/TiO2 and RGO/TiO2 are shown in
The experiments on the photoreduction of CO2 were carried out using a Nicolet 6700 Fourier transform infrared (FTIR) spectrometer equipped with a Praying Mantis diffuse reflectance accessory (Harrick Sci. Corp., Model DRP-M-07) and a 316 stainless steel high temperature reaction chamber (Harrick Sci. Corp., Model HVC-DRP-4), a mercury cadmium telluride (MCT) detector and a KBr beam splitter. The chamber dome has two KBr windows and a quartz window. The quartz window was used for visual observation while the KBr windows were used to permit entry and exit of the infrared beam.
The IL-RGO/TiO2 or pristine Degussa P25 powders were placed in the sample compartment of the reaction chamber, and the dome was mounted and sealed with an O-ring. The reaction chamber has an inlet for introducing gas to the sample and an outlet for gas exhaust. The chamber was purged with N2 before introducing the CO2 and H2O vapor reactant gases. The H2O vapor was obtained by flowing N2 through an impinger containing distilled water. CO2 mixed with humidified N2 was introduced to the reaction chamber. Mass flow controllers (Omega Engineering, Inc.) were used to control the flow of CO2 and N2. The inlet mixing ratio of CO2 is 10% by volume. An IR spectrum was obtained after the CO2/humidified N2 mixture flowed over the photocatalyst, in order to check that CO2 and H2O vapor were absorbed to the surface of the catalyst. The inlet and outlet of the chamber were sealed, and subsequent spectra were taken in a batch mode of operation.
A series of background experiments were conducted in order to characterize the system and to ensure the absence of product formation, even in the presence of the catalytic surface. The sample with CO2 and humidified N2 was kept in the dark for 30 minutes. IR spectra were obtained during the 30 minutes dark period to examine whether products formed in the absence of light. In addition, a background experiment with the catalyst and humidified N2 but without CO2 was performed under UV-Visible light irradiation in order to determine whether there was product formation in the absence of CO2. After performing the background experiments, the catalyst (IL-RGO/TiO2 or P25) was placed in the chamber with CO2 and humidified N2. UV-Visible light, produced from a deuterium-halogen light source (Ocean Optics DH-2000-BAL, wavelength=210-1500 nm), was used to activate the catalyst. An optical fiber cable was used to introduce the light to the sample surface through the quartz window of the chamber. Several IR spectra at different irradiation times were acquired over a total irradiation time of 60 minutes. Each spectrum was acquired using 4 cm−1 resolution and 32 scans.
To attempt to quantify the amount of product formed, standard samples of product (diluted by N2) were admitted to the DRIFTS reaction cell to generate a calibration curve. The gas was allowed to equilibrate with the surface, a spectrum was obtained, and the surface was subsequently purged with N2 in between each admission of product. Spectra were acquired during the N2 purge to ensure that the product was completely desorbed from the surface and removed from the chamber. A surface adsorbed product calibration curve was generated and used to attempt to quantify the amount of product formed during the CO2 photoreduction experiment over IL-RGO/TiO2.
The CO2 photoreduction using IL-RGO/TiO2 catalyst in the presence of H2O vapor was performed twice using fresh and regenerated catalyst samples. Initially, fresh IL-RGO/TiO2 was used for CO2 photoreduction. After 30 minute UV-Visible irradiation, the sample was regenerated by cleaning the catalyst surface using pure N2. IR spectra of the catalytic surface were obtained to ensure that the reactants (CO2 and H2O vapor), and the CH4 product formed in the previous run were completely dissociated from the catalyst surface and removed from the reaction chamber. Then, the reactants with the same concentrations were admitted to the reaction chamber and the photoreduction experiment was performed again.
In the background experiments, no new peaks were observed in the IR spectra of IL-RGO/TiO2 with CO2 and humidified N2 in the dark over 30 minutes. When IL-RGO/TiO2 and humidified N2 (in the absence of CO2) were irradiated for 30 minutes using UV-Vis light, no new peaks were detected in the IR spectra. Experiments were also performed for bare P25 with CO2 and humidified N2. Even after 60 minutes of UV-V is irradiation, no new peak formation was detected in the IR spectra.
The IL-RGO/TiO2 composite material was applied to the photoreduction of CO2 in the presence of H2O vapor. IR spectra of the IL-RGO/TiO2 surface before and after UV-Visible irradiation were obtained and are shown in
The major challenge in CO2 photoreduction is that the recombination of electron and hole generated from TiO2 is very fast. Thus, there is a significant decrease in the photocatalytic efficiency of TiO2. P25, which is the mixed phases of TiO2 with approximately 75% anatase and approximately 25% rutile, is expected to have better electron and hole separation than a single phase of TiO2 due to the different positions of the conduction and valence bands of the anatase and rutile phases such as is illustrated in
Electron paramagnetic resonance (EPR) studies by Gray and co-workers indicated that photogenerated electrons actually migrated from rutile to lower energy anatase trapping sites, consequently enhancing electron-hole separation. See, for example: Hurum, D. C.; Agrios, A. G.; Gray, K. A.; Rajh, T.; Thurnauer, M. C., Explaining the enhanced photocatalytic activity of Degussa P25 mixed-phase TiO2 using EPR. Journal of Physical Chemistry B 2003, 107, 4545-4549; Hurum, D. C.; Gray, K. A.; Rajh, T.; Thurnauer, M. C., Recombination pathways in the Degussa P25 formulation of TiO2: Surface versus lattice mechanisms. Journal of Physical Chemistry B 2005, 109, 977-980; and Hurum, D. C.; Agrios, A. G.; Crist, S. E.; Gray, K. A.; Rajh, T.; Thurnauer, M. C., Probing reaction mechanisms in mixed phase TiO2 by EPR. Journal of Electron Spectroscopy and Related Phenomena 2006, 150, 155-163.
However, when P25 was used in the CO2 photoreduction experiments, no product was observed under the DRIFTS experimental conditions. Therefore, the commercial P25 was still not effective enough for the photoreduction of CO2 with H2O vapor. Nevertheless, it was found that the presence of IL-RGO significantly enhances the photoactivity of P25 which is likely due to the improved electron-hole separation via electron transport from the TiO2 to the IL-RGO.
The production of CO is frequently reported in the literature as the major product for CO2 photoreduction studies using TiO2-based nanoparticles. The IR feature of CO is expected to appear in the 2000-2270 cm−1 frequency range. Notably, the lack of CO features in
Additionally, in the literature, there are different proposed mechanisms for CH4 formation in CO2 photoreduction using TiO2-based photocatalysts. The selectivity of the products, for example CO or CH4, may be due to differences in the numbers of electrons that are produced by the catalyst and separated from the holes. As reported for photochemical reduction of CO2, the reaction mechanism for CO production requires four electrons, while eight electrons are needed for CH4 production. The selective formation of CH4 that is reported herein suggests that more electrons are available from the IL-RGO/TiO2 material as compared to the catalysts used in published studies that have CO as the major product of CO2 photoreduction. This further confirms that the presence of IL-RGO helps to separate electron and hole pairs. The selective production of CH4 is very valuable in the application of the catalyst in CO2 photoreduction because CO, as a synthesis gas, cannot be used as a fuel directly whereas CH4 is an energy-rich fuel.
In
Although the present invention has been described in detail with reference to certain embodiments, one skilled in the art will appreciate that the present invention can be practiced by other than the described embodiments, which have been presented for purposes of illustration and not of limitation. Therefore, the scope of the invention should not be limited to the description of the embodiments contained herein. For example, it is contemplated that another application for this material or other materials made by similar processes may exist in Field Effect Transistors.
This application claims the priority benefit of U.S. provisional patent application No. 61/724,578 entitled “Ionic Liquid Functionalized Reduced Graphite Oxide/TiO2 Nanocomposite for Conversion of CO2 to CH4” filed on Nov. 9, 2012, the contents of which are incorporated by reference as if set forth in its entirety herein for all purposes.
The invention was made with government support under 1253443 awarded by the National Science Foundation. The United States government has certain rights in the invention.