20200139347
Agarose is a linear polysaccharide polymer made up of repeating units of agarobiose, which is a disaccharide formed of D-galactose and 3,6-anhydro-L-galactopyranose. Agarose is one of the two principal components of agar and is purified from agar by removing agar's other component, agaropectin. Agarose is frequently used in molecular biology for the separation of large molecules, especially DNA, by electrophoresis.
This disclosure relates to gels containing irradiated agarose and compositions containing irradiated agarose, as well as related methods of production and use. In some embodiments, a method of forming a composition containing irradiated agarose is disclosed and the method includes irradiating an agarose in dry form to produce an irradiated agarose, dissolving the irradiated agarose in a solvent to form a solution containing irradiated agarose, and gelling the solution containing irradiated agarose to form a gel containing irradiated agarose. The agarose may be irradiated in dry form with at least 5 kilograys (kGy) of radiation or with at least 40 kilograys (kGy) of radiation, in some embodiments. In these and other embodiments, water may be used as the solvent and the solution may contain between 3% and 10% irradiated agarose by weight. The solution may be gelled by chemical cross-linking or cooling, in some embodiments. The gel containing irradiated agarose may have an agarose concentration of at least 3% or at least 5%, in select embodiments. In these and other embodiments, the gel containing irradiated agarose may have a gel strength of less than 2,000 gm/cm2. The gel containing irradiated agarose need not be irradiated while in gel form. The gel containing irradiated agarose may be administered to a patient, for example via injection. In some embodiments, the gel may be fractured prior to being administered.
This disclosure relates to irradiated agarose compositions for dermal filling and other related applications. Gamma radiation has previously been used to sterilize various compositions and devices. However, in contrast to using gamma radiation as a terminal (end of process) sterilization step, the present disclosure describes methods and compositions in which agarose is irradiated in dry form and then subsequently prepared for insertion into the body. As described in more detail below, gels and other articles formed from the disclosed irradiated agarose may be used for any purpose, including cosmetic, reconstructive, and/or therapeutic applications.
Irradiating an agarose in gel form can negatively impact the gel and lessen its shelf life. However, irradiating an agarose in dry form (prior to forming a gel) can advantageously avoid the negative effects of irradiating the gel and may also positively impact the properties of a gel formed from the irradiated agarose. For example, a gel containing agarose that was irradiated in dry form may have modified elastic modulus (G′) and viscous modulus (G″) rheological properties as well as a lower gel strength as compared to a gel containing agarose that has not been irradiated.
As will be appreciated, a “dry” agarose or an agarose “in dry form” may refer to various types of agarose structures. For example, a dry agarose may take the form of a solid, particles, powder, thread, film, and/or matrix. The agarose in dry form that is irradiated may be, for example, in the form of a powder as commonly supplied commercially, or in the form of a dehydrated or partially dehydrated gel, or in the form of an agarose precipitated from a glycol, or some combination thereof. Suitable precipitation techniques are known to those skilled in the art.
The agarose in dry form that is irradiated may be modified (i.e., derivatized) or unmodified. As will be understood by those skilled in the art, modified or derivatized agarose may have slightly or significantly different properties as opposed to unmodified agarose (e.g., gel strength, melting/gelling point, molecular weight, viscosity, etc.). As used herein, the term “agarose” refers to a compound based on the following polymeric structure:
The agarose used in the disclosed methods and compositions may be commercially obtained or prepared by a user. The disclosed agarose may, in some embodiments, include one or more crude, purified, derivatized or modified agars or agaroses. For example, in certain embodiments, the agarose is selected from agarose, purified agarose, modified agarose, and/or derivatized agarose. The agarose may also be used as mixtures with other compatible polymers and additives such as agar, carrageenan, chitosan, alginate, gelatin, hyaluronic acid, and/or collagen. In select embodiments, the agarose is unmodified or modified agarose, and/or derivatized agarose. In certain embodiments, the agarose is Gracilaria-derived agarose. Gracilaria-derived agarose has a higher methoxy content than agarose derived from other sources (e.g., Gelidium). Agaroses from other seaweeds, for example, Pterocladia or Gelidiella may also be used as the disclosed agarose.
The agarose in dry form may be irradiated using any suitable technique, such as processes that employ gamma radiation, x-ray or beta radiation (e.g., electron beam “e-beam” processing). Numerous types of irradiating devices are known in the art and may be used to irradiate agarose in dry form in accordance with the disclosed methods. The agarose in dry form may be irradiated with any suitable amount of radiation, depending on the desired specifications of the resulting irradiated agarose. For example, in some embodiments, the agarose may be dosed with at least 5 kilograys (kGy), 10 kGy, 20 kGy, 30 kGy, 40 kGy, 50 kGy, 60 kGy, 70 kGy, 80 kGy, 90 kGy, 100 kGy, or more. In select embodiments, the agarose is irradiated with between 10 and 100 kGy, between 20 and 80 kGy, or between 40 and 60 kGy. The gel strength and viscosity of the resulting agarose may be tailored by simply adjusting the irradiation dosage of the agarose in dry form.
Among other possible effects, irradiating an agarose in dry form may, in some cases, reduce its molecular weight. Without wishing to be bound by theory, irradiating an agarose in dry form may cleave molecular bonds of the agarose structure, thereby reducing the total molecular weight of the agarose. Additionally, in some embodiments, irradiating an agarose in dry form may reduce viscosity and/or gel strength of the resulting agarose. In select embodiments, irradiating an agarose in dry form may reduce the viscosity of the resulting agarose by at least 5%, 10%, 20%, 30%, 40%, 50%, or more. In these and other embodiments, irradiating the agarose in dry form may reduce the gel strength of the resulting agarose gel by at least 5%, 10%, 20%, 30%, 40%, 50%, or more. For example, in some embodiments, irradiating the agarose in dry form may reduce the gel strength of the resulting agarose gel to less than 10%, 20%, 40% or less than 80% of the gel strength of a gel made with the un-irradiated agarose. If a high enough radiation dose is applied to the agarose in dry form, the resulting agarose may not even gel at all. Such an agarose could be useful in applications by itself or in combination with gelled agarose.
Method 200 of
Method 200 of
Method 200 of
Method 200 of
In some embodiments, the disclosed agarose gel compositions are administered to a patient at concentrations of at least 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, or 10% by weight. In these and other embodiments, the gel made from irradiated agarose may be mixed with other types of agaroses (e.g., agaroses having a different melting point and/or gel strength than the gel formed from agarose irradiated in dry form). Agarose compositions having varying properties can be produced by mixing agaroses prepared according to different techniques (e.g., agaroses irradiated in dry form with different dosings, or agarose irradiated in dry form mixed with agarose that was not irradiated in dry form).
Although method 200 outlines possible steps for producing and using a gel made from irradiated agarose, other methods of production and use are also possible. For example, agarose irradiated in dry form may be utilized by simply exposing it to water. Depending on the form of the irradiated agarose, when exposed to water, it may form a gel, or it may swell or rehydrate to some extent, or both. In some such embodiments, the agarose may be irradiated in dry form as a film, powder, thread, or matrix and may then be applied to a patient without further substantive processing.
In a first experimental example, two 3.5% agarose gels (3.5 grams agarose in 100 ml H2O) were made. The first gel (#1) was made with P.F.G.E agarose Scientific) that had not been exposed to gamma irradiation. The second gel (#2) was made with P.F.G.E agarose (IBI Scientific) that had been exposed to 25 kGy gamma irradiation. Gel #1 had a gel strength of 5200 gm/cm2 and gel #2 had a gel strength of 1920 gm/cm2.
In a second experimental example, two 1 ml syringes were fitted with 180 mesh screens such that the contents of the syringe needed to pass through the screen on delivery. The first syringe (#1) was loaded with a 3.5% solution of un-irradiated P.F.G.E agarose and the second syringe (#2) was loaded with a solution of 3.5% P.F.G.E agarose made with agarose powder that had been exposed to 25 kGy gamma irradiation. The solution in both syringes was allowed to cool and form a gel.
It was impossible to force the gel from syringe #1 through the 180 mesh. The plunger of the syringe bent before enough pressure could be applied to express the gel through the screen. The gel in syringe #2 could be easily expressed through the 180 mesh screen requiring a force of less than 20 Newton on the plunger.
The disclosed techniques and compositions may provide numerous advantages over alternative preparation and sterilization procedures. Notably, irradiating an agarose while in dry form as opposed to in gel form may result in unique properties of the resulting agarose. Specifically, an agarose having reduced molecular weight, reduced gel strength, and/or reduced viscosity may be obtained by irradiating the agarose in dry form. Additionally, agarose gels prepared according to the disclosed methods may also have improved tactile effects in the body. For example, the disclosed agarose gels (formed from agarose irradiated in dry form) may be less brittle and softer than conventional agarose gels. Due to the nature of the presently disclosed agarose gels, agarose gels with higher agarose concentrations may be appropriate for administration to a patient, which may increase the overall residence time in the body and may also increase the time needed before follow-up procedures to replenish gel that is consumed by the body.
The features and advantages described herein are not all-inclusive and, in particular, many additional features and advantages will be apparent to one of ordinary skill in the art in view of the present disclosure. Persons skilled in the relevant art can appreciate that many modifications and variations are possible in light of the above disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| PCT/US19/58042 | Oct 2019 | US | national |
This application claims priority from U.S. Provisional Application Ser. No. 62/754,813, titled “Irradiated Agarose, Compositions Thereof, and Related Methods” filed Nov. 2, 2018, the contents of which are incorporated by reference herein.
| Number | Date | Country | |
|---|---|---|---|
| 62754813 | Nov 2018 | US |